WO2013146589A1 - Élément d'affichage à cristaux liquides et son procédé de fabrication - Google Patents

Élément d'affichage à cristaux liquides et son procédé de fabrication Download PDF

Info

Publication number
WO2013146589A1
WO2013146589A1 PCT/JP2013/058303 JP2013058303W WO2013146589A1 WO 2013146589 A1 WO2013146589 A1 WO 2013146589A1 JP 2013058303 W JP2013058303 W JP 2013058303W WO 2013146589 A1 WO2013146589 A1 WO 2013146589A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
display element
crystal display
alignment film
group
Prior art date
Application number
PCT/JP2013/058303
Other languages
English (en)
Japanese (ja)
Inventor
達哉 名木
宏之 桜井
皇晶 筒井
Original Assignee
日産化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産化学工業株式会社 filed Critical 日産化学工業株式会社
Priority to KR1020147030401A priority Critical patent/KR20140139115A/ko
Priority to CN201380028338.1A priority patent/CN104335112A/zh
Publication of WO2013146589A1 publication Critical patent/WO2013146589A1/fr

Abstract

Un élément d'affichage à cristaux liquides (1) est configuré de manière à ce qu'un substrat TFT (2) et un substrat CF (3) pourvu d'une couche CF (7) prennent en sandwich une couche de cristaux liquides (4). Le substrat TFT (2) et le substrat CF (3) sont prévus avec un film d'alignement de cristaux liquides (12). Dans l'élément d'affichage à cristaux liquides (1), un matériau d'étanchéité (16) utilise une résine durcissable aux rayons UV, et même dans les régions dans lesquelles les pixels sont formés, les rayons UV pour durcir le matériau d'étanchéité (16) sont émis et prévus. L'élément d'affichage à cristaux liquides (1) est configuré à l'aide du film d'alignement de cristaux liquides (12) qui contient un film de polyimide synthétisé à partir d'un composé diamine d'une structure spécifique. Lorsque le matériau d'étanchéité (16) est durci, même si les régions dans lesquelles les pixels sont formés sont irradiées par des rayons UV, la dégradation de fonctionnalité est supprimée.
PCT/JP2013/058303 2012-03-30 2013-03-22 Élément d'affichage à cristaux liquides et son procédé de fabrication WO2013146589A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
KR1020147030401A KR20140139115A (ko) 2012-03-30 2013-03-22 액정 표시 소자 및 그 제조 방법
CN201380028338.1A CN104335112A (zh) 2012-03-30 2013-03-22 液晶显示元件及其制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012-081162 2012-03-30
JP2012081162 2012-03-30

Publications (1)

Publication Number Publication Date
WO2013146589A1 true WO2013146589A1 (fr) 2013-10-03

Family

ID=49259844

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/058303 WO2013146589A1 (fr) 2012-03-30 2013-03-22 Élément d'affichage à cristaux liquides et son procédé de fabrication

Country Status (5)

Country Link
JP (1) JPWO2013146589A1 (fr)
KR (1) KR20140139115A (fr)
CN (1) CN104335112A (fr)
TW (1) TWI499616B (fr)
WO (1) WO2013146589A1 (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106292046A (zh) * 2016-08-19 2017-01-04 京东方科技集团股份有限公司 一种显示面板及制作方法
WO2019013117A1 (fr) * 2017-07-14 2019-01-17 シャープ株式会社 Composition de matériau d'étanchéité, cellule à cristaux liquides et antenne de balayage
CN111072556A (zh) * 2019-12-31 2020-04-28 阜阳欣奕华材料科技有限公司 一种二胺化合物、其制备方法及应用

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06337425A (ja) * 1993-05-28 1994-12-06 Hitachi Chem Co Ltd 液晶配向膜用組成物、液晶配向膜の製造法、液晶配向膜、液晶挟持基板および液晶表示素子
JPH08122790A (ja) * 1994-10-20 1996-05-17 Japan Synthetic Rubber Co Ltd 液晶配向剤

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TW461980B (en) * 1997-04-30 2001-11-01 Nissan Chemical Ind Ltd Liquid crystal orientation processing agent
CN100537638C (zh) * 2004-04-28 2009-09-09 日产化学工业株式会社 液晶定向剂、使用了该定向剂的液晶定向膜及液晶显示元件
WO2009084665A1 (fr) * 2007-12-28 2009-07-09 Nissan Chemical Industries, Ltd. Agent d'alignement de cristaux liquides et dispositif d'affichage à cristaux liquides l'utilisant
JP5333454B2 (ja) * 2008-11-06 2013-11-06 日産化学工業株式会社 液晶配向処理剤

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06337425A (ja) * 1993-05-28 1994-12-06 Hitachi Chem Co Ltd 液晶配向膜用組成物、液晶配向膜の製造法、液晶配向膜、液晶挟持基板および液晶表示素子
JPH08122790A (ja) * 1994-10-20 1996-05-17 Japan Synthetic Rubber Co Ltd 液晶配向剤

Also Published As

Publication number Publication date
TWI499616B (zh) 2015-09-11
KR20140139115A (ko) 2014-12-04
JPWO2013146589A1 (ja) 2015-12-14
CN104335112A (zh) 2015-02-04
TW201345951A (zh) 2013-11-16

Similar Documents

Publication Publication Date Title
JP5257548B2 (ja) 液晶表示素子および液晶配向剤
WO2013125595A1 (fr) Composition, agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides
JP5930239B2 (ja) 組成物、液晶配向処理剤、液晶配向膜および液晶表示素子
WO2015152174A1 (fr) Agent d'alignement de cristaux liquides contenant un copolymère ester d'acide polyamique - acide polyamique, et film d'alignement de cristaux liquides utilisant l'agent d'alignement de cristaux liquides contenant un copolymère ester d'acide polyamique - acide polyamique
JP6331028B2 (ja) 液晶配向処理剤、液晶配向膜および液晶表示素子
WO2014133042A1 (fr) Polymère, agent de traitement servant à l'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
JP6052171B2 (ja) 組成物、液晶配向処理剤、液晶配向膜及び液晶表示素子
JP6079627B2 (ja) 組成物、液晶配向処理剤、液晶配向膜及び液晶表示素子
WO2014092126A1 (fr) Composition, agent de traitement d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
WO2014119682A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
US10761375B2 (en) Liquid crystal aligning agent, liquid crystal alignment film and liquid crystal display element
WO2015141598A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
JP5930238B2 (ja) 組成物、液晶配向処理剤、液晶配向膜および液晶表示素子
WO2013065755A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
WO2013146589A1 (fr) Élément d'affichage à cristaux liquides et son procédé de fabrication
JP6361887B6 (ja) 液晶配向膜の製造方法、液晶配向膜、液晶表示素子
JP7001063B2 (ja) 液晶配向剤、液晶配向膜、及び液晶表示素子
US11112654B2 (en) Liquid crystal display device
WO2019163904A1 (fr) Procédé de production d'un élément d'affichage à cristaux liquides
WO2018216664A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
WO2016125871A1 (fr) Agent d'orientation de cristaux liquides, film orienté de cristaux liquides, et élément d'affichage à cristaux liquides
WO2016140302A1 (fr) Précurseur de polyimide, et agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides comprenant un précurseur
JP6776897B2 (ja) 液晶配向剤、液晶配向膜、及び液晶表示素子
TW201823303A (zh) 液晶配向劑、液晶配向膜及液晶顯示元件

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13768813

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2014507822

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20147030401

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 13768813

Country of ref document: EP

Kind code of ref document: A1