WO2013073505A1 - Composition d'auto-organisation pour la formation de motif et procédé de formation de motif - Google Patents

Composition d'auto-organisation pour la formation de motif et procédé de formation de motif Download PDF

Info

Publication number
WO2013073505A1
WO2013073505A1 PCT/JP2012/079308 JP2012079308W WO2013073505A1 WO 2013073505 A1 WO2013073505 A1 WO 2013073505A1 JP 2012079308 W JP2012079308 W JP 2012079308W WO 2013073505 A1 WO2013073505 A1 WO 2013073505A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
self
pattern
pattern formation
polymer
Prior art date
Application number
PCT/JP2012/079308
Other languages
English (en)
Japanese (ja)
Inventor
信也 峯岸
祐司 浪江
永井　智樹
曽根　卓男
Original Assignee
Jsr株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jsr株式会社 filed Critical Jsr株式会社
Publication of WO2013073505A1 publication Critical patent/WO2013073505A1/fr

Abstract

L'invention concerne une composition d'auto-organisation pour la formation d'un motif comprenant [A] un polymère avec un groupe contenant un hétéroatome (α) sur au moins une extrémité de la chaîne principale et [B] un polysiloxane. L'hétéroatome est de préférence au moins une sorte sélectionnée dans le groupe constitué d'atomes d'oxygène, d'atomes d'azote, d'atomes de soufre, d'atomes de phosphore, d'atomes d'étain et d'atomes de silicium. Le groupe (α) est de préférence représenté par la formule (1). Le polymère [A] est de préférence un polymère de styrène. (1)
PCT/JP2012/079308 2011-11-14 2012-11-12 Composition d'auto-organisation pour la formation de motif et procédé de formation de motif WO2013073505A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011248549 2011-11-14
JP2011-248549 2011-11-14

Publications (1)

Publication Number Publication Date
WO2013073505A1 true WO2013073505A1 (fr) 2013-05-23

Family

ID=48429563

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/079308 WO2013073505A1 (fr) 2011-11-14 2012-11-12 Composition d'auto-organisation pour la formation de motif et procédé de formation de motif

Country Status (3)

Country Link
JP (1) JPWO2013073505A1 (fr)
TW (1) TW201323508A (fr)
WO (1) WO2013073505A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013146600A1 (fr) * 2012-03-27 2013-10-03 日産化学工業株式会社 Composition filmogène de sous-couche pour films auto-assemblés
KR20150014008A (ko) * 2013-07-25 2015-02-06 에스케이하이닉스 주식회사 반도체 소자 제조 방법
WO2015041208A1 (fr) * 2013-09-19 2015-03-26 日産化学工業株式会社 Composition pour la formation d'un film de sous-couche pour un film à auto-assemblage comprenant une structure polycyclique aliphatique
JP2016108436A (ja) * 2014-12-05 2016-06-20 東京応化工業株式会社 下地剤、及び相分離構造を含む構造体の製造方法
JP2017505709A (ja) * 2014-01-16 2017-02-23 ブルーワー サイエンス アイ エヌ シー． 誘導自己組織化用高χブロックコポリマー
US10504726B2 (en) 2013-07-25 2019-12-10 SK Hynix Inc. Nano-scale structures

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6023010B2 (ja) * 2013-06-26 2016-11-09 東京エレクトロン株式会社 基板処理方法、プログラム、コンピュータ記憶媒体及び基板処理システム
KR102308953B1 (ko) * 2017-03-10 2021-10-05 주식회사 엘지화학 패턴화 기판의 제조 방법

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11236416A (ja) * 1997-10-08 1999-08-31 Shin Etsu Chem Co Ltd ポリスチレン系高分子化合物及び化学増幅ポジ型レジスト材料並びにパターン形成方法
JP2003140350A (ja) * 2001-11-07 2003-05-14 Shin Etsu Chem Co Ltd 高分子化合物、レジスト材料及びパターン形成方法
JP2003255546A (ja) * 2001-12-28 2003-09-10 Fujitsu Ltd アルカリ可溶性シロキサン重合体、ポジ型レジスト組成物、レジストパターン及びその製造方法、並びに、電子回路装置及びその製造方法
JP2005126481A (ja) * 2003-10-21 2005-05-19 Nippon Steel Chem Co Ltd ブロック共重合体及びその製造方法
JP2005340720A (ja) * 2004-05-31 2005-12-08 Jsr Corp パターン形成方法及び半導体装置の製造方法
JP2007246600A (ja) * 2006-03-14 2007-09-27 Shin Etsu Chem Co Ltd 自己組織化高分子膜材料、自己組織化パターン、及びパターン形成方法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11236416A (ja) * 1997-10-08 1999-08-31 Shin Etsu Chem Co Ltd ポリスチレン系高分子化合物及び化学増幅ポジ型レジスト材料並びにパターン形成方法
JP2003140350A (ja) * 2001-11-07 2003-05-14 Shin Etsu Chem Co Ltd 高分子化合物、レジスト材料及びパターン形成方法
JP2003255546A (ja) * 2001-12-28 2003-09-10 Fujitsu Ltd アルカリ可溶性シロキサン重合体、ポジ型レジスト組成物、レジストパターン及びその製造方法、並びに、電子回路装置及びその製造方法
JP2005126481A (ja) * 2003-10-21 2005-05-19 Nippon Steel Chem Co Ltd ブロック共重合体及びその製造方法
JP2005340720A (ja) * 2004-05-31 2005-12-08 Jsr Corp パターン形成方法及び半導体装置の製造方法
JP2007246600A (ja) * 2006-03-14 2007-09-27 Shin Etsu Chem Co Ltd 自己組織化高分子膜材料、自己組織化パターン、及びパターン形成方法

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013146600A1 (fr) * 2012-03-27 2013-10-03 日産化学工業株式会社 Composition filmogène de sous-couche pour films auto-assemblés
US10000664B2 (en) 2012-03-27 2018-06-19 Nissan Chemical Industries, Ltd. Underlayer film-forming composition for self-assembled films
KR20150014008A (ko) * 2013-07-25 2015-02-06 에스케이하이닉스 주식회사 반도체 소자 제조 방법
US10504726B2 (en) 2013-07-25 2019-12-10 SK Hynix Inc. Nano-scale structures
KR102105196B1 (ko) * 2013-07-25 2020-04-29 에스케이하이닉스 주식회사 반도체 소자 제조 방법
WO2015041208A1 (fr) * 2013-09-19 2015-03-26 日産化学工業株式会社 Composition pour la formation d'un film de sous-couche pour un film à auto-assemblage comprenant une structure polycyclique aliphatique
US11674053B2 (en) 2013-09-19 2023-06-13 Nissan Chemical Industries, Ltd. Composition for forming underlayer film of self-assembled film including aliphatic polycyclic structure
JP2017505709A (ja) * 2014-01-16 2017-02-23 ブルーワー サイエンス アイ エヌ シー． 誘導自己組織化用高χブロックコポリマー
US10421878B2 (en) 2014-01-16 2019-09-24 Brewer Science, Inc. High-Chi block copolymers for directed self-assembly
JP2016108436A (ja) * 2014-12-05 2016-06-20 東京応化工業株式会社 下地剤、及び相分離構造を含む構造体の製造方法

Also Published As

Publication number Publication date
TW201323508A (zh) 2013-06-16
JPWO2013073505A1 (ja) 2015-04-02

Similar Documents

Publication Publication Date Title
WO2013073505A1 (fr) Composition d'auto-organisation pour la formation de motif et procédé de formation de motif
JP5835123B2 (ja) パターン形成用自己組織化組成物及びパターン形成方法
US20190241695A1 (en) Composition and pattern-forming method
US9738746B2 (en) Composition for pattern formation, pattern-forming method, and block copolymer
JP6394042B2 (ja) パターン形成用組成物及びパターン形成方法
WO2014003023A1 (fr) Composition pour former des motifs et procédé de formation de motifs
US20150252216A1 (en) Pattern-forming method and directed self-assembling composition
KR102393027B1 (ko) 패턴 형성용 조성물 및 패턴 형성 방법
JP7044976B2 (ja) パターン形成方法
US9557644B2 (en) Base film-forming composition, and directed self-assembly lithography method
WO2013146715A1 (fr) Procédé de formation de motif
JP6652721B2 (ja) パターン形成用組成物及びパターン形成方法
WO2014188806A1 (fr) Procédé de lithographie auto-organisé et composition de formation de film de sous-couche
WO2022049968A1 (fr) Composition filmogène à auto-organisation, et procédé de formation de motif
JP5907009B2 (ja) パターン形成方法
JP6788198B2 (ja) コンタクトホールパターンの形成方法及び組成物
JP2015139875A (ja) パターン形成用自己組織化組成物及びパターン形成方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12849777

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2013544262

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12849777

Country of ref document: EP

Kind code of ref document: A1