WO2013039233A1 - Matériau permettant de protéger une cellule photovoltaïque - Google Patents

Matériau permettant de protéger une cellule photovoltaïque Download PDF

Info

Publication number
WO2013039233A1
WO2013039233A1 PCT/JP2012/073727 JP2012073727W WO2013039233A1 WO 2013039233 A1 WO2013039233 A1 WO 2013039233A1 JP 2012073727 W JP2012073727 W JP 2012073727W WO 2013039233 A1 WO2013039233 A1 WO 2013039233A1
Authority
WO
WIPO (PCT)
Prior art keywords
solar cell
protective material
film
layer
pressure
Prior art date
Application number
PCT/JP2012/073727
Other languages
English (en)
Japanese (ja)
Inventor
治 赤池
直哉 二宮
由美 満倉
雅秀 小西
畠山　研一
Original Assignee
三菱樹脂株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱樹脂株式会社 filed Critical 三菱樹脂株式会社
Priority claimed from JP2012203036A external-priority patent/JP6007037B2/ja
Priority claimed from JP2012203027A external-priority patent/JP2013084929A/ja
Priority claimed from JP2012203025A external-priority patent/JP2013084928A/ja
Priority claimed from JP2012203031A external-priority patent/JP2013077818A/ja
Priority claimed from JP2012203034A external-priority patent/JP2013123036A/ja
Publication of WO2013039233A1 publication Critical patent/WO2013039233A1/fr

Abstract

La présente invention a trait à un matériau permettant de protéger une cellule photovoltaïque, qui est constitué d'un film de fluororésine, d'une couche adhésive (i) qui comprend un adhésif (i) et d'un film de résine qui est doté d'une couche d'oxyde métallique, stratifiés dans l'ordre mentionné. Un matériau de base du film de résine qui est doté d'une couche d'oxyde métallique est pourvu d'une épaisseur inférieure ou égale à 30 μm, l'épaisseur de la couche adhésive (i) est de 13 à 45 μm et le module d'élasticité de stockage à la traction de la couche adhésive (i) à 100 °C, avec une fréquence de 10 Hz et une distorsion de 0,1 %, est de 5,0×104 à 5,0×105 Pa.
PCT/JP2012/073727 2011-09-16 2012-09-14 Matériau permettant de protéger une cellule photovoltaïque WO2013039233A1 (fr)

Applications Claiming Priority (20)

Application Number Priority Date Filing Date Title
JP2011203160 2011-09-16
JP2011-203160 2011-09-16
JP2011-209406 2011-09-26
JP2011-209402 2011-09-26
JP2011209406 2011-09-26
JP2011209402 2011-09-26
JP2011245857 2011-11-09
JP2011-245857 2011-11-09
JP2012-183096 2012-08-22
JP2012183096 2012-08-22
JP2012-203036 2012-09-14
JP2012-203034 2012-09-14
JP2012-203025 2012-09-14
JP2012-203031 2012-09-14
JP2012203036A JP6007037B2 (ja) 2012-08-22 2012-09-14 積層防湿フィルム、太陽電池用保護材、及び太陽電池
JP2012203027A JP2013084929A (ja) 2011-09-26 2012-09-14 太陽電池用保護材
JP2012203025A JP2013084928A (ja) 2011-09-26 2012-09-14 太陽電池用保護材
JP2012203031A JP2013077818A (ja) 2011-09-16 2012-09-14 太陽電池用保護材
JP2012-203027 2012-09-14
JP2012203034A JP2013123036A (ja) 2011-11-09 2012-09-14 太陽電池用保護材

Publications (1)

Publication Number Publication Date
WO2013039233A1 true WO2013039233A1 (fr) 2013-03-21

Family

ID=47883449

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/JP2012/073728 WO2013039234A1 (fr) 2011-09-16 2012-09-14 Matériau de protection de cellule solaire
PCT/JP2012/073727 WO2013039233A1 (fr) 2011-09-16 2012-09-14 Matériau permettant de protéger une cellule photovoltaïque

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/073728 WO2013039234A1 (fr) 2011-09-16 2012-09-14 Matériau de protection de cellule solaire

Country Status (1)

Country Link
WO (2) WO2013039234A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015007181A (ja) * 2013-06-25 2015-01-15 日立化成株式会社 太陽電池用接続材料、これを用いた太陽電池モジュール及びその製造方法
WO2015008614A1 (fr) * 2013-07-17 2015-01-22 東レフィルム加工株式会社 Feuille de protection arrière pour module de cellule solaire
JP2016204461A (ja) * 2015-04-17 2016-12-08 富士フイルム株式会社 機能性フィルムおよび機能性フィルムの製造方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008204997A (ja) * 2007-02-16 2008-09-04 Toppan Printing Co Ltd 太陽電池用裏面保護シート
JP2009135457A (ja) * 2007-11-05 2009-06-18 Techno Polymer Co Ltd 太陽電池用バックシート
JP2009200385A (ja) * 2008-02-25 2009-09-03 Toppan Printing Co Ltd 太陽電池用保護シート及びこれを用いた太陽電池モジュール
JP2010027815A (ja) * 2008-07-18 2010-02-04 Daio Paper Corp 太陽電池モジュール用裏面保護シート
JP2010238790A (ja) * 2009-03-30 2010-10-21 Lintec Corp 太陽電池モジュール用保護シートおよびそれを用いてなる太陽電池モジュール
JP2010263193A (ja) * 2009-04-08 2010-11-18 Nippon Shokubai Co Ltd 太陽電池モジュール用バックシート

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3078936B2 (ja) * 1992-12-28 2000-08-21 キヤノン株式会社 太陽電池
JP5262044B2 (ja) * 2007-09-27 2013-08-14 凸版印刷株式会社 太陽電池裏面封止用シート及びこれを用いた太陽電池モジュール
JP4993504B2 (ja) * 2008-04-02 2012-08-08 三井・デュポンポリケミカル株式会社 太陽電池用積層体シート及びそれを用いた太陽電池モジュール
JP2010016286A (ja) * 2008-07-07 2010-01-21 Toppan Printing Co Ltd 太陽電池裏面封止用シート

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008204997A (ja) * 2007-02-16 2008-09-04 Toppan Printing Co Ltd 太陽電池用裏面保護シート
JP2009135457A (ja) * 2007-11-05 2009-06-18 Techno Polymer Co Ltd 太陽電池用バックシート
JP2009200385A (ja) * 2008-02-25 2009-09-03 Toppan Printing Co Ltd 太陽電池用保護シート及びこれを用いた太陽電池モジュール
JP2010027815A (ja) * 2008-07-18 2010-02-04 Daio Paper Corp 太陽電池モジュール用裏面保護シート
JP2010238790A (ja) * 2009-03-30 2010-10-21 Lintec Corp 太陽電池モジュール用保護シートおよびそれを用いてなる太陽電池モジュール
JP2010263193A (ja) * 2009-04-08 2010-11-18 Nippon Shokubai Co Ltd 太陽電池モジュール用バックシート

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015007181A (ja) * 2013-06-25 2015-01-15 日立化成株式会社 太陽電池用接続材料、これを用いた太陽電池モジュール及びその製造方法
WO2015008614A1 (fr) * 2013-07-17 2015-01-22 東レフィルム加工株式会社 Feuille de protection arrière pour module de cellule solaire
JP2016204461A (ja) * 2015-04-17 2016-12-08 富士フイルム株式会社 機能性フィルムおよび機能性フィルムの製造方法

Also Published As

Publication number Publication date
WO2013039234A1 (fr) 2013-03-21

Similar Documents

Publication Publication Date Title
JP5540840B2 (ja) 太陽電池裏面封止シート
WO2012124742A1 (fr) Film résistant à l'humidité stratifié
WO2012091122A1 (fr) Couche stratifiée imperméable à l'humidité
JP2010263193A (ja) 太陽電池モジュール用バックシート
JP2010238790A (ja) 太陽電池モジュール用保護シートおよびそれを用いてなる太陽電池モジュール
JP2012148560A (ja) 積層防湿フィルム
JP2014060390A (ja) 太陽電池用保護シート
JP5865739B2 (ja) 積層防湿フィルム
KR101350557B1 (ko) 태양전지 모듈용 백 시트 및 이를 포함하는 태양전지 모듈
JP6007037B2 (ja) 積層防湿フィルム、太陽電池用保護材、及び太陽電池
JP6135060B2 (ja) 太陽電池モジュール用裏面保護シート
JP2014041900A (ja) 太陽電池用保護材及び太陽電池
WO2013039233A1 (fr) Matériau permettant de protéger une cellule photovoltaïque
WO2013100108A1 (fr) Matériau protecteur pour cellules solaires
JP2012213937A (ja) 積層防湿シート
TW201315609A (zh) 太陽電池用保護材
JP2012148561A (ja) 積層防湿フィルム
JP2012214023A (ja) 積層防湿フィルム
JP2012244068A (ja) 太陽電池用保護材
JP2014058155A (ja) 積層シートの製造方法
JP5474171B1 (ja) 太陽電池用保護材
JP2013077818A (ja) 太陽電池用保護材
JP2013084929A (ja) 太陽電池用保護材
JP2012158154A (ja) 透明積層防湿フィルム
JP2013123036A (ja) 太陽電池用保護材

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12832567

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12832567

Country of ref document: EP

Kind code of ref document: A1