WO2012132935A1 - Procédé de fabrication d'un verre de protection pour dispositif électronique, verre de protection pour dispositif électronique, plaque en verre pour verre de protection utilisé dans des dispositifs électroniques, et procédé de fabrication d'un module de détection de type à effleurement - Google Patents

Procédé de fabrication d'un verre de protection pour dispositif électronique, verre de protection pour dispositif électronique, plaque en verre pour verre de protection utilisé dans des dispositifs électroniques, et procédé de fabrication d'un module de détection de type à effleurement Download PDF

Info

Publication number
WO2012132935A1
WO2012132935A1 PCT/JP2012/056704 JP2012056704W WO2012132935A1 WO 2012132935 A1 WO2012132935 A1 WO 2012132935A1 JP 2012056704 W JP2012056704 W JP 2012056704W WO 2012132935 A1 WO2012132935 A1 WO 2012132935A1
Authority
WO
WIPO (PCT)
Prior art keywords
printing
glass substrate
protective film
cover glass
glass
Prior art date
Application number
PCT/JP2012/056704
Other languages
English (en)
Japanese (ja)
Inventor
下川　貢一
Original Assignee
Hoya株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hoya株式会社 filed Critical Hoya株式会社
Priority to CN201280016451.3A priority Critical patent/CN103619773B/zh
Publication of WO2012132935A1 publication Critical patent/WO2012132935A1/fr

Abstract

Cette invention concerne un procédé de fabrication d'un verre de protection qui est utilisé dans les dispositifs électroniques et comprend une étape d'impression pour effectuer une impression sur une surface d'un substrat en verre pour verre de protection, et comprend également une étape de formation d'un film protecteur sur toute la surface du substrat en verre pour verre de protection et une étape de modification de la surface du film protecteur correspondant au moins à la région qui doit être imprimée afin de permettre l'impression, avant l'étape d'impression. Dans l'étape d'impression, l'impression est effectuée sur une région se situant dans la région qui a été modifiée.
PCT/JP2012/056704 2011-03-31 2012-03-15 Procédé de fabrication d'un verre de protection pour dispositif électronique, verre de protection pour dispositif électronique, plaque en verre pour verre de protection utilisé dans des dispositifs électroniques, et procédé de fabrication d'un module de détection de type à effleurement WO2012132935A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN201280016451.3A CN103619773B (zh) 2011-03-31 2012-03-15 电子设备用覆盖玻璃的制造方法、电子设备用覆盖玻璃、用于电子设备的覆盖玻璃用玻璃基板、以及触摸传感器模块的制造方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2011-077483 2011-03-31
JP2011077483 2011-03-31
JP2012-034121 2012-02-20
JP2012034121A JP5454969B2 (ja) 2011-03-31 2012-02-20 電子機器用カバーガラスの製造方法、及びタッチセンサモジュールの製造方法

Publications (1)

Publication Number Publication Date
WO2012132935A1 true WO2012132935A1 (fr) 2012-10-04

Family

ID=46930670

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/056704 WO2012132935A1 (fr) 2011-03-31 2012-03-15 Procédé de fabrication d'un verre de protection pour dispositif électronique, verre de protection pour dispositif électronique, plaque en verre pour verre de protection utilisé dans des dispositifs électroniques, et procédé de fabrication d'un module de détection de type à effleurement

Country Status (4)

Country Link
JP (1) JP5454969B2 (fr)
CN (1) CN103619773B (fr)
TW (1) TWI524168B (fr)
WO (1) WO2012132935A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013089178A1 (fr) * 2011-12-13 2013-06-20 Hoya株式会社 Verre de recouvrement pour instrument électronique, procédé pour le fabriquer et procédé de fabrication d'un module à capteur tactile
CN108268820A (zh) * 2016-12-30 2018-07-10 南昌欧菲光学技术有限公司 电子装置、玻璃盖板及其制作方法
US20200369562A1 (en) * 2017-11-30 2020-11-26 Saint-Gobain Glass France Method for producing a printed, coated panel
US11524916B2 (en) 2017-11-30 2022-12-13 Saint-Gobain Glass France Method for producing a printed, coated panel

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103434289B (zh) * 2013-08-27 2016-07-27 江西合力泰科技有限公司 一种防止玻璃盖板脏污的印刷工艺
CN107922256B (zh) * 2015-08-10 2021-07-27 Ａｇｃ株式会社 带防污层的玻璃板
WO2019235160A1 (fr) * 2018-06-04 2019-12-12 株式会社カネカ Stratifié de verre, son procédé de production et panneau avant de dispositif d'affichage utilisant celui-ci
CN108863103A (zh) * 2018-08-31 2018-11-23 嘉善银升玻璃有限公司 一种防油污玻璃的加工方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6259922U (fr) * 1985-10-04 1987-04-14
JPH11322367A (ja) * 1998-05-14 1999-11-24 Asahi Glass Co Ltd フラットパネルディスプレイ用ガラス基板およびその製造方法
JP2001192237A (ja) * 1999-10-29 2001-07-17 Nippon Electric Glass Co Ltd ガラス物品とその製造方法及び物品表面の清浄化方法
WO2009099615A1 (fr) * 2008-02-05 2009-08-13 Corning Incorporated Article en verre résistant à l'endommagement destiné à être utilisé comme cache de verre dans des dispositifs électroniques
JP2011006288A (ja) * 2009-06-26 2011-01-13 Panasonic Corp ガラス基板の刻印方法およびそれを用いたフラットパネルディスプレイの製造方法

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN201169571Y (zh) * 2008-01-31 2008-12-24 谷崧精密工业股份有限公司 玻璃面板结构
US20090258187A1 (en) * 2008-04-10 2009-10-15 Michael Donavon Brady Protective coating for glass manufacturing and processing into articles
CN201345096Y (zh) * 2008-12-16 2009-11-11 柯涵钰 透明基板的图案化透明导电薄膜及触控面板

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6259922U (fr) * 1985-10-04 1987-04-14
JPH11322367A (ja) * 1998-05-14 1999-11-24 Asahi Glass Co Ltd フラットパネルディスプレイ用ガラス基板およびその製造方法
JP2001192237A (ja) * 1999-10-29 2001-07-17 Nippon Electric Glass Co Ltd ガラス物品とその製造方法及び物品表面の清浄化方法
WO2009099615A1 (fr) * 2008-02-05 2009-08-13 Corning Incorporated Article en verre résistant à l'endommagement destiné à être utilisé comme cache de verre dans des dispositifs électroniques
JP2011006288A (ja) * 2009-06-26 2011-01-13 Panasonic Corp ガラス基板の刻印方法およびそれを用いたフラットパネルディスプレイの製造方法

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013089178A1 (fr) * 2011-12-13 2013-06-20 Hoya株式会社 Verre de recouvrement pour instrument électronique, procédé pour le fabriquer et procédé de fabrication d'un module à capteur tactile
JP5270810B1 (ja) * 2011-12-13 2013-08-21 Ｈｏｙａ株式会社 電子機器用カバーガラス及びその製造方法、並びにタッチセンサモジュールの製造方法
CN103974919A (zh) * 2011-12-13 2014-08-06 Hoya株式会社 电子设备用盖板玻璃及其制造方法、以及触摸传感器模块的制造方法
CN103974919B (zh) * 2011-12-13 2016-07-06 Hoya株式会社 电子设备用盖板玻璃及其制造方法、以及触摸传感器模块的制造方法
CN108268820A (zh) * 2016-12-30 2018-07-10 南昌欧菲光学技术有限公司 电子装置、玻璃盖板及其制作方法
US20200369562A1 (en) * 2017-11-30 2020-11-26 Saint-Gobain Glass France Method for producing a printed, coated panel
US11524916B2 (en) 2017-11-30 2022-12-13 Saint-Gobain Glass France Method for producing a printed, coated panel
US11548812B2 (en) * 2017-11-30 2023-01-10 Saint-Gobain Glass France Method for producing a printed, coated panel

Also Published As

Publication number Publication date
CN103619773A (zh) 2014-03-05
CN103619773B (zh) 2016-02-17
JP5454969B2 (ja) 2014-03-26
TWI524168B (zh) 2016-03-01
JP2012214360A (ja) 2012-11-08
TW201245937A (en) 2012-11-16

Similar Documents

Publication Publication Date Title
JP5454969B2 (ja) 電子機器用カバーガラスの製造方法、及びタッチセンサモジュールの製造方法
JP5654072B2 (ja) 携帯型電子機器用カバーガラスのガラス基板の製造方法
JP6313391B2 (ja) ガラス基板、電子機器用カバーガラス、及びガラス基板の製造方法
JP6024873B2 (ja) トラックパッド用カバーガラス及びその製造方法
JP5270810B1 (ja) 電子機器用カバーガラス及びその製造方法、並びにタッチセンサモジュールの製造方法
US20130330515A1 (en) Method of processing cover glass
JP2016167078A5 (fr)
WO2013100067A1 (fr) Lamelle couvre-objet pour dispositif électronique, son procédé de fabrication, et module de capteur tactile pour dispositif électronique
JP2012088946A (ja) タッチパネルの製造方法およびその方法により製造された加飾カバーガラス一体型タッチパネル
JP5705040B2 (ja) 携帯機器用カバーガラスの製造方法
JP2014125399A (ja) タッチパネル形成用強化ガラス基板の製造方法
JP2013006745A (ja) 携帯機器用カバーガラスの製造方法
JP2015197784A (ja) カバーガラス一体型タッチパネルセンサー基板および表示装置
TW201413532A (zh) 觸控面板製造方法
JP5564522B2 (ja) 電子機器用カバーガラスの製造方法、及びタッチセンサモジュールの製造方法
JP2015079436A (ja) ガラス基板の切断方法およびこれを用いたタッチパネルセンサー基板の製造方法、タッチパネルセンサー基板
JP2016006573A (ja) カバーガラス一体型タッチパネルセンサー基板及びカバーガラス
JP2014047108A (ja) 電子機器用カバーガラスの製造方法、及びタッチセンサモジュールの製造方法
JP2014047109A (ja) 電子機器用カバーガラスの製造方法、及びタッチセンサモジュールの製造方法
JP5345225B2 (ja) 携帯機器用カバーガラスの製造方法
JP5701703B2 (ja) 携帯機器用カバーガラスの製造方法
JP5351364B2 (ja) 携帯機器用カバーガラス及びその製造方法
JP2014009132A (ja) ガラス基板ホルダ、及び電子機器用カバーガラスのガラス基板の製造方法
CN105405742B (zh) 一种基板处理方法
JP6279271B2 (ja) 電子機器用カバーガラスのガラス基板の製造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201280016451.3

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12763186

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12763186

Country of ref document: EP

Kind code of ref document: A1