WO2012122735A1 - 一种含铬轻烃燃烧催化剂及制备方法 - Google Patents

一种含铬轻烃燃烧催化剂及制备方法 Download PDF

Info

Publication number
WO2012122735A1
WO2012122735A1 PCT/CN2011/074137 CN2011074137W WO2012122735A1 WO 2012122735 A1 WO2012122735 A1 WO 2012122735A1 CN 2011074137 W CN2011074137 W CN 2011074137W WO 2012122735 A1 WO2012122735 A1 WO 2012122735A1
Authority
WO
WIPO (PCT)
Prior art keywords
chromium
catalyst
light hydrocarbon
crcl
hours
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2011/074137
Other languages
English (en)
French (fr)
Inventor
张永春
苑兴洲
张鲁湘
陈少云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian University of Technology
Original Assignee
Dalian University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian University of Technology filed Critical Dalian University of Technology
Publication of WO2012122735A1 publication Critical patent/WO2012122735A1/zh
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Description

一种含铬轻烃燃烧催化剂及制备方法 技术领域
本发明属于催化剂技术领域，涉及到一种含铬轻烃燃烧催化剂及制备方法。
背景技术
随着人类社会的发展和世界各国工业化进程的加快，地球上化石燃料资源 的不断减少，环境污染日益加重，能源和环保问题已受到各国政府的高度重视。石化燃料的燃烧一直是世界能源工业的支柱，但传统的火焰燃烧方式燃烧效率低下、尾气中污染物含量高。轻烃催化燃烧被视为一条高效、低排放的燃烧路线，成为各国科研与工程技术人员关注的重要课题。
在轻烃的低碳烷烃中，以甲烷碳链最短，碳氢键最强，所以甲烷的燃烧温度决定了低碳烷烃整体的燃烧温度。催化燃烧催化剂分为以下几种：
贵金属催化剂一般采用 Al2O3 、 ZrO2 和 SnO2 作为载体，添加稀土元素 (La 、 Ce 等 ) 以提高催化剂的活性和稳定性，这一催化剂体系的主要缺点在于成本高、耐热性、抗烧结能力差。 Stefania 等于 2009 年在 Journal of catalysis 上报道 Pd 负载于 Ce-Zr 复合氧化物催化剂，在 350 ℃ 起燃， 410 ℃ 完全燃烧。
钙钛矿催化剂通式为 ABO3 ， A 为较大的阳离子为十二面体结构，多采用稀土元素，而较小的 B 为阳离子为六配位，多采用过渡金属元素。 La 被作为最常用的 A 位元素， B 位取代对其反应活性影响更明显。对于取代元素和取代量都有较多的研究报道，普遍认为 B 位元素对催化剂的氧化还原性能影响显著，致使其反应性能差别突出。 L Fabbrini 等利用火焰水解法 ( Flame hydrolysis ， FH ) 制备 La0.9Ce0.1CoO3+δ 粉末 ， 并将 Al2O3 与 La2O3 作为第二载体分别涂覆到堇青石基体上 ， 样品表现出良好的催化活性 ， 440 ℃ 时甲烷转化率可达到 50% 。
六铝酸盐催化剂通式为 AAl12O19( 或 AO·6A12O3) ，其中 A 位通常为碱金属或碱土金属，从热稳定性、低挥发性、机械强度及抗热震性能几方面考虑是最理想的甲烷高温燃烧催化剂体系，这种材料的活性较贵金属和钙铁矿材料低。 Moon Hee Han 等在 Catal. Today 报道用 γ-Al2O3 粉末上浸渍 La 、 Mn 制备六铝酸盐 ， 直接挤出成型制备整体型催化剂 。 实验表明 ： 整体型催化剂比相应的粉末活性高 ， 调节晶格中 La ， Mn 的比例能改善催化剂热稳定性 。 除了以上介绍的常见氧化物外，还有如烧绿石、水滑石等结构的氧化物对全氧化也有较好的反应活性。
中国专利 CN 101293201 B 所涉及的甲烷燃烧催化剂，采用溶胶凝胶法制备出钙钛矿 LaMn0.8O3 和烧绿石 La2Sn2O7 共存的复合氧化物催化剂，具有较好的热稳定性和反应活性，合成方法简单而成本较低廉，但是比表面积小而影响反应活性不能提高；中国专利 CN 1326607 C 所涉及的甲烷燃烧催化剂，采用共沉淀法，水热合成法和溶胶凝胶法制备过渡金属取代六铝酸盐催化剂，活性组分可以为铁、钴、镍、铜等取代六铝酸盐，该催化剂在高温下较稳定，且有较高的比表面积，但催化活性相对较低。与上两种催化剂相比较，我们合成的催化剂具有更大的催化剂比表面积，更高的反应活性，更低的起燃温度和更简便的合成方法。
 技术问题
本发明的目的是提供一种含铬轻烃燃烧催化剂及制备方法。通过用浸渍法和等体积浸渍法，制备一种含铬负载型催化剂，提高催化剂的性能，解决的技术问题是在较低温度下实现轻烃的起燃和完全燃烧。
技术解决方案
本发明的技术方案是：
本发明所述的含铬轻烃燃烧催化剂包括下述质量分数的组分： Al2O3:Cr2O3:CeO 2= A ： B ： C 或 Al2O3:CrCl3:CeO2= A ： B ： C , 其 A ： B 的范围在 1/0.05~1/0.5 之间， C 的范围在 1~5% 之间， Al2O3 : 65~95% （ W/W% ） , Cr2O3 ： 5~50% （ W/W% ） ,CrCl3 ： 5~50% （ W/W% ）， CeO2 ： 0~5% （ W/W% ） 。
本发明催化剂的制备采用过量浸渍法，等体积浸渍法，包括以下步骤：
步骤（ 1 ）：将硝酸铬、硝酸铈溶解在水中，得到浓度为 0.4~10mol/L 的溶液，其中硝酸铬可由氯化铬代替 ;
步骤（ 2 ）：将步骤（ 1 ）所述的溶液滴加到 Al2O3 上，搅拌 10-20 分钟，于 25 ℃ 下在空气中 静置 2-6 小时；
步骤（ 3 ）：将步骤（ 2 ）所得的催化剂前驱体在 70-110℃ 下干燥 12-24 小时，然后降温至 25 ℃ ，再以升温速率 1-2℃/min 升温至 500-800℃ 焙烧 4-6 小时，然后自然降温至
25 ℃ ，研磨、压片、破碎、筛分，即得所需催化剂。
 有益效果
本发明的效果和益处是所述方法制备的一种含铬轻烃燃烧催化剂，具有很 好的轻烃催化燃烧活性、稳定性高、制备工艺简单、原料易得、成本低廉、环境污染小。
附图说明
图1是不同前躯体制备甲烷燃烧催化剂的反应活性图。
图 2 是 不同 CrCl3 负载量甲烷燃烧催化剂的反应活性图。
图 3 是 30 wt.%CrCl3 负载量甲烷燃烧催化剂XRD谱图。
图 4 是 50 wt.%CrCl3 负载量甲烷燃烧催化剂XRD谱图。
 本发明的最佳实施方式
实施例1
称取 3.6189g 的 Cr(NO3)3·9H2O 在 25 ℃ 下溶于3.2 ml 去离子水中，将 Cr(NO3)3 水溶液滴加入4g纳米 γ-Al2O3 中，形成等体积浸渍，在 25 ℃ 下静置3 h ，70℃过夜， 110℃普通干燥3 h ，研磨，马弗炉中500℃焙烧4h得到 Cr(NO3)3/γ-Al2O3 催化剂。
 本发明的实施方式
实施例2
称取2.8148g的 CrCl3·6H2O 在 25 ℃ 下溶于 3.5ml 去离子水中，将 CrCl3 水溶液滴加入 4g 纳米 γ-Al2O3 中，形成等体积浸渍，在 25 ℃ 下静置3 h ，70℃过夜， 110℃普通干燥3 h ，研磨，马弗炉中500℃焙烧4h得到 CrCl3/γ-Al2O3 催化剂。
实施例3
称取0.5259g-5.259g的 CrCl3·6H2O 溶于 2.5-5ml 去离子水，将氯化铬水溶液滴加入3g纳米 γ-Al2O3 中，室温静置3 h ，放入真空干燥箱，70℃真空干燥过夜，110℃普通干燥3 h ，研磨，马弗炉中 500 ℃ 焙烧4 h 得到5 %-50%CrCl3/γ-Al2O3 催化剂。
实施例4
称取 3.6189g 的 Cr(NO3)3·9H2O 和 0.1109-0.5545g 的 Ce(NO3)3·9H2O 在 25 ℃ 下溶于3.2 ml 去离子水中，将 Cr(NO3)3 水溶液滴加入4g纳米 γ-Al2O3 中，形成等体积浸渍，在 25 ℃ 下静置3 h ，70℃过夜， 110℃普通干燥3 h ，研磨，马弗炉中500℃焙烧4h得到 Cr(NO3)3/γ-Al2O3 催化剂。
由图1.-图4.可以看出：
以氯化铬为前躯体，催化剂催化活性高；不同负载量中30 wt.%负载量催化剂的催化活性最高；50 wt.%负载量的 XRD 谱图中出现了明显的 CrCl3 晶体衍射峰，证明表面形成了 CrCl3 晶体聚集，降低了表面 CrCl3 分散性，降低了活性。
附表 1. 催化剂催化性能
催化剂： CrCl3/γ-Al2O3 、 Cr2O3/γ-Al2O3
反应条件 ： 在甲烷，氧气，氮气体积比例2:8:90，空速12000 ml/h·g
甲烷转化率 （ % ） 10% 20% 50% 90% 99%
CrCl3/γ-Al2O3 337.1 360.2 398.2 443.0 466.8
Cr2O3/γ-Al2O3 344.6 367.0 405.4 451.2 483.1
附表 2. 催化剂催化性能
不同 CrCl3 负载量催化剂：300 mg
反应条件：在甲烷，氧气，氮气体积比例2:8:90，空速12000 ml/h·g
不同 CrCl3 负载量（wt.%） 5% 10% 20% 30% 50%
甲烷转化率达到 10% 时的温度 （℃） 409.9 376.9 350.0 336.4 345.9
甲烷转化率达到 90% 时的温度 （℃） 534.8 492.0 458.5 444.6 469.2
附表 3. 催化剂催化性能
Ce 改性 CrCl3 负载量催化剂：300 mg
反应条件：在轻烃（甲烷 73.54%，乙烷 9.73%，丙烷 7.57%，乙烯4.72% 丙烯 4.34%），氧气，氮气体积比例2:8:90，空速12000 ml/h·g
转化率 （ % ） 甲烷 乙烷 乙烯 丙烷和丙烯
198.7 （℃） 0 0 0 0
243.5 （℃） 0 0 16.2 37.2
291.4 （℃） 1.7 86.2 100 100
341.2 （℃） 34.9 100 100 100
390.1 （℃） 89.9 100 100 100
工业实用性
序列表自由内容

Claims (4)

  1. 一种含铬轻烃燃烧催化剂，其特征在于：所述的含铬低碳烷烃燃烧催化剂包括下述质量分数的组分：
    Al2O3:Cr2O3 = 1/0.05~1/0.5 或 Al2O3:CrCl3 = 1/0.05~1/0.5 ；
    其中 Al2O3 质量分数是 65~95% （ W/W% ）； Cr2O3 质量分数是 5~50% （ W/W% ）； CrCl3 质量分数是 5~50% （ W/W% ）。
  2. 根据权利要求1所述的 一种含铬轻烃燃烧催化剂，其特征在于所述的一种含铬低碳烷烃燃烧催化剂还包括助催化剂 CeO2 ，其质量百分含量为
    0~5% 。
  3. 根据权利要求 1 或 2 所说的一种含铬轻烃燃烧催化剂，其特征在于所述的轻烃为烷烃、烯烃、炔烃、芳香烃。
  4. 权利要求 1 或 2 所述一种含铬轻烃燃烧催化剂的制备方法，其特征在于包括以下步骤：
    步骤（ 1 ）：将硝酸铬、硝酸铈溶解在水中，得到浓度为 0.4~10mol/L 的溶液，其中硝酸铬可由氯化铬代替 ;
    步骤（ 2 ）：将步骤（ 1 ）所述的溶液滴加到 Al2O3 上，搅拌 10-20 分钟，于 25 ℃下在空气中 静置 2-6 小时；
    步骤（ 3 ）：将步骤（ 2 ）所得的催化剂前驱体在 70-110 ℃ 下干燥 12-24 小时，然后降温至 25 ℃ ，再以升温速率 1-2 ℃ /min 升温至 500-800 ℃ 焙烧 4-6 小时，然后自然降温至 25 ℃ ，研磨、压片、破碎、筛分，即得所需催化剂。
    5. 权利要求 3 所述一种含铬轻烃燃烧催化剂的制备方法，其特征在于包括以下步骤：
    步骤（ 1 ）：将硝酸铬、硝酸铈溶解在水中，得到浓度为 0.4~10mol/L 的溶液，其中硝酸铬可由氯化铬代替 ;
    步骤（ 2 ）：将步骤（ 1 ）所述的溶液滴加到 Al2O3 上，搅拌 10-20 分钟，于 25 ℃下在空气中 静置 2-6 小时；
    步骤（ 3 ）：将步骤（ 2 ）所得的催化剂前驱体在 70-110 ℃ 下干燥 12-24 小时，然后降温至 25 ℃ ，再以升温速率 1-2 ℃ /min 升温至 500-800 ℃ 焙烧 4-6 小时，然后自然降温至 25 ℃
    ，研磨、压片、破碎、筛分，即得所需催化剂。
PCT/CN2011/074137 2011-03-17 2011-05-16 一种含铬轻烃燃烧催化剂及制备方法 Ceased WO2012122735A1 (zh)