WO2012023545A1 - Matériau pour élément électroluminescent organique, composition contenant ledit matériau, film formé en utilisant ladite composition, et élément électroluminescent organique - Google Patents

Matériau pour élément électroluminescent organique, composition contenant ledit matériau, film formé en utilisant ladite composition, et élément électroluminescent organique Download PDF

Info

Publication number
WO2012023545A1
WO2012023545A1 PCT/JP2011/068530 JP2011068530W WO2012023545A1 WO 2012023545 A1 WO2012023545 A1 WO 2012023545A1 JP 2011068530 W JP2011068530 W JP 2011068530W WO 2012023545 A1 WO2012023545 A1 WO 2012023545A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
organic electroluminescent
electroluminescent element
layer
organic
Prior art date
Application number
PCT/JP2011/068530
Other languages
English (en)
Japanese (ja)
Inventor
早 高田
直之 林
浩二 高久
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Publication of WO2012023545A1 publication Critical patent/WO2012023545A1/fr

Abstract

L'invention concerne un élément électroluminescent organique dont la durabilité lors de l'excitation à haute température est améliorée et qui permet de réduire les irrégularités de luminance dans le plan et d'éviter la diminution de luminance initiale. L'invention concerne également un matériau pour élément électroluminescent organique qui est préparé en introduisant un groupe thermiquement réactif dans un précurseur préalablement purifié par sublimation. Le précurseur est un composé portant une fraction de liaison hydrogène, et l'introduction du groupe thermiquement réactif consiste à introduire un groupe polymérisable dans la fraction de liaison hydrogène dans le composé portant ladite fraction. La fraction de liaison hydrogène dans le précurseur se situe dans une arylamine primaire ou secondaire. Le matériau pour élément électroluminescent organique répond à la formule générale (1) dans laquelle les R1 représentent indépendamment un substituant, P1 représente un groupe vinyle, acryle, méthacryle, époxy ou oxétane, les l représentent indépendamment un entier valant 0-5, l' représente un entier valant 0-4, et m3 représente un entier égal à 0 ou plus, les R1 pouvant former conjointement une liaison pour constituer ainsi un noyau condensé qui peut porter un substituant.
PCT/JP2011/068530 2010-08-17 2011-08-15 Matériau pour élément électroluminescent organique, composition contenant ledit matériau, film formé en utilisant ladite composition, et élément électroluminescent organique WO2012023545A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010-182647 2010-08-17
JP2010182647A JP2012043912A (ja) 2010-08-17 2010-08-17 有機電界発光素子用材料、該有機電界発光素子用材料を含む組成物、並びに、該組成物により形成された膜、及び有機電界発光素子

Publications (1)

Publication Number Publication Date
WO2012023545A1 true WO2012023545A1 (fr) 2012-02-23

Family

ID=45605198

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/068530 WO2012023545A1 (fr) 2010-08-17 2011-08-15 Matériau pour élément électroluminescent organique, composition contenant ledit matériau, film formé en utilisant ladite composition, et élément électroluminescent organique

Country Status (2)

Country Link
JP (1) JP2012043912A (fr)
WO (1) WO2012023545A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015039723A1 (fr) * 2013-09-17 2015-03-26 Merck Patent Gmbh Complexes d'iridium phényl-pyridine polycyclique et dérivés pour oled desdits complexes
CN109627175A (zh) * 2017-10-09 2019-04-16 北京夏禾科技有限公司 可交联氘代的电荷传输化合物，包含该化合物的有机电致发光器件及溶液配方
CN111655707A (zh) * 2018-05-14 2020-09-11 株式会社Lg化学 化合物及包含其的有机发光器件

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115572284A (zh) * 2014-09-25 2023-01-06 三星显示有限公司 可交联主体材料
KR102250691B1 (ko) * 2014-10-06 2021-05-13 덕산네오룩스 주식회사 유기전기 소자용 화합물, 이를 이용한 유기전기소자 및 그 전자 장치
KR102336027B1 (ko) * 2015-03-27 2021-12-07 덕산네오룩스 주식회사 유기전기 소자용 화합물, 이를 이용한 유기전기소자 및 그 전자 장치
KR102336029B1 (ko) * 2015-03-27 2021-12-07 덕산네오룩스 주식회사 유기전기 소자용 화합물, 이를 이용한 유기전기소자 및 그 전자 장치
CN110832658A (zh) * 2017-07-04 2020-02-21 日立化成株式会社 有机电子材料及有机电子元件
JP6457161B1 (ja) * 2017-09-14 2019-01-23 住友化学株式会社 液状組成物の製造方法
US11046886B2 (en) 2017-09-14 2021-06-29 Sumitomo Chemical Company, Limited Method for producing liquid composition
EP3780118A4 (fr) 2018-04-03 2021-06-02 FUJIFILM Corporation Élément semi-conducteur organique, composition, procédé de purification de composé et application associée
KR102206819B1 (ko) * 2018-05-14 2021-01-22 주식회사 엘지화학 화합물 및 이를 포함하는 유기 발광 소자
KR102443861B1 (ko) * 2018-05-24 2022-09-15 주식회사 엘지화학 유기 발광 소자

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11292829A (ja) * 1998-04-13 1999-10-26 Chemiprokasei Kaisha Ltd 有機エレクトロルミネッセント素子
JP2005519429A (ja) * 2002-03-04 2005-06-30 シーディーティー オックスフォード リミテッド 燐光体組成物及びそれを含む有機発光装置
JP2007506237A (ja) * 2003-09-17 2007-03-15 凸版印刷株式会社 Ｅｌ素子
WO2009063757A1 (fr) * 2007-11-14 2009-05-22 Konica Minolta Holdings, Inc. Matériau de dispositif électroluminescent organique, dispositif électroluminescent organique, procédé de fabrication d'un dispositif électroluminescent organique, dispositif d'affichage et dispositif d'éclairage

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004327454A (ja) * 1998-12-28 2004-11-18 Idemitsu Kosan Co Ltd 有機エレクトロルミネッセンス素子
KR20070114713A (ko) * 2004-12-30 2007-12-04 이 아이 듀폰 디 네모아 앤드 캄파니 전하 수송 물질
JP5470706B2 (ja) * 2007-01-25 2014-04-16 三菱化学株式会社 正孔輸送材料、該正孔輸送材料を重合させてなる高分子化合物、有機電界発光素子用組成物および有機電界発光素子

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11292829A (ja) * 1998-04-13 1999-10-26 Chemiprokasei Kaisha Ltd 有機エレクトロルミネッセント素子
JP2005519429A (ja) * 2002-03-04 2005-06-30 シーディーティー オックスフォード リミテッド 燐光体組成物及びそれを含む有機発光装置
JP2007506237A (ja) * 2003-09-17 2007-03-15 凸版印刷株式会社 Ｅｌ素子
WO2009063757A1 (fr) * 2007-11-14 2009-05-22 Konica Minolta Holdings, Inc. Matériau de dispositif électroluminescent organique, dispositif électroluminescent organique, procédé de fabrication d'un dispositif électroluminescent organique, dispositif d'affichage et dispositif d'éclairage

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015039723A1 (fr) * 2013-09-17 2015-03-26 Merck Patent Gmbh Complexes d'iridium phényl-pyridine polycyclique et dérivés pour oled desdits complexes
CN105555792A (zh) * 2013-09-17 2016-05-04 默克专利有限公司 用于oled的多环苯基吡啶铱络合物及其衍生物
CN109627175A (zh) * 2017-10-09 2019-04-16 北京夏禾科技有限公司 可交联氘代的电荷传输化合物，包含该化合物的有机电致发光器件及溶液配方
CN111655707A (zh) * 2018-05-14 2020-09-11 株式会社Lg化学 化合物及包含其的有机发光器件
CN111655707B (zh) * 2018-05-14 2023-06-23 株式会社Lg化学 化合物及包含其的有机发光器件

Also Published As

Publication number Publication date
JP2012043912A (ja) 2012-03-01

Similar Documents

Publication Publication Date Title
WO2012023545A1 (fr) Matériau pour élément électroluminescent organique, composition contenant ledit matériau, film formé en utilisant ladite composition, et élément électroluminescent organique
JP6616351B2 (ja) ジアリールアミノフェニルカルバゾール化合物を用いた第二正孔輸送層
JP6468723B2 (ja) 含窒素多環芳香族をアクセプターとして含むドナー−アクセプター化合物
TWI498411B (zh) 有機電激發光元件
JP2014208642A (ja) 架橋可能なイオンドーパント
JP2013543864A (ja) リン光物質
TW201211201A (en) Organic electroluminescent element
JP4691611B1 (ja) 有機電界発光素子
JP7069947B2 (ja) １，３，５－トリアジン化合物、該化合物を含有する組成物、及び有機電界発光素子製造方法
JP2011049511A (ja) 有機電界発光素子
JP2011091356A (ja) 有機電界発光素子
JP7409428B2 (ja) イリジウム錯体化合物の製造方法
TWI532719B (zh) 電荷輸送材料及有機電激發光元件
JP5591052B2 (ja) 有機電界発光素子
JP5557624B2 (ja) 組成物、並びに、該組成物を用いた膜、電荷輸送層、有機電界発光素子、及び電荷輸送層の形成方法
JP5476234B2 (ja) 有機電界発光素子用材料、有機電界発光素子、及び有機電界発光素子の製造方法
TWI532720B (zh) 有機電激發光元件
WO2012002399A1 (fr) Matière d'élément électroluminescent organique, élément électroluminescent organique et procédé de production pour un élément électroluminescent organique
JP2015193632A (ja) 有機電界発光素子用材料、該有機電界発光素子用材料を含む組成物、並びに、該組成物により形成された膜、及び有機電界発光素子
TWI507394B (zh) 有機電激發光元件
JP6059193B2 (ja) 有機電界発光素子、表示装置、照明装置、及び有機電界発光素子の製造方法。
Lorente Sánchez Synthesis of side-chain polystyrenes for all organic solution processed OLEDs
JP5642011B2 (ja) 有機電界発光素子の作製方法
KR20200034519A (ko) 신규한 공중합체 및 이를 포함하는 유기 발광 소자

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11818186

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11818186

Country of ref document: EP

Kind code of ref document: A1