WO2009096552A1 - Photorécepteur électrophotographique, dispositif de formation d'image le comprenant et procédé de fabrication de photorécepteur électrophotographique - Google Patents

Photorécepteur électrophotographique, dispositif de formation d'image le comprenant et procédé de fabrication de photorécepteur électrophotographique Download PDF

Info

Publication number
WO2009096552A1
WO2009096552A1 PCT/JP2009/051637 JP2009051637W WO2009096552A1 WO 2009096552 A1 WO2009096552 A1 WO 2009096552A1 JP 2009051637 W JP2009051637 W JP 2009051637W WO 2009096552 A1 WO2009096552 A1 WO 2009096552A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
sionb
photosensitive member
electrophotographic photosensitive
less
Prior art date
Application number
PCT/JP2009/051637
Other languages
English (en)
Japanese (ja)
Inventor
Hiroyuki Nakashima
Original Assignee
Kyocera Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kyocera Corporation filed Critical Kyocera Corporation
Priority to JP2009551620A priority Critical patent/JP5436227B2/ja
Publication of WO2009096552A1 publication Critical patent/WO2009096552A1/fr

Abstract

L'invention concerne un photorécepteur électrophotographique (2) présentant un substrat conducteur (20) et une couche de revêtement (21) qui recouvre le substrat conducteur (20). Le revêtement (21) est constitué d'une couche photoréceptrice (22), d'une couche résistante à la pression (23) conçue entre le substrat cylindrique (20) et la couche photoréceptrice (22), et d'une couche contenant du SiONB (24) conçue entre le substrat cylindrique (20) et la couche résistante à la pression (23). L'épaisseur de la couche contenant du SiONB est, par exemple, comprise entre 0,15 μm et 1,05 μm.
PCT/JP2009/051637 2008-01-31 2009-01-30 Photorécepteur électrophotographique, dispositif de formation d'image le comprenant et procédé de fabrication de photorécepteur électrophotographique WO2009096552A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2009551620A JP5436227B2 (ja) 2008-01-31 2009-01-30 電子写真感光体、これを備えた画像形成装置および電子写真感光体の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2008022130 2008-01-31
JP2008-022130 2008-01-31

Publications (1)

Publication Number Publication Date
WO2009096552A1 true WO2009096552A1 (fr) 2009-08-06

Family

ID=40912895

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/051637 WO2009096552A1 (fr) 2008-01-31 2009-01-30 Photorécepteur électrophotographique, dispositif de formation d'image le comprenant et procédé de fabrication de photorécepteur électrophotographique

Country Status (2)

Country Link
JP (1) JP5436227B2 (fr)
WO (1) WO2009096552A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59119358A (ja) * 1982-12-27 1984-07-10 Toshiba Corp 電子写真感光体
JPS62269147A (ja) * 1986-05-16 1987-11-21 Canon Inc 光受容部材
JPS62276559A (ja) * 1986-05-26 1987-12-01 Canon Inc 光受容部材
JPH0283549A (ja) * 1988-09-20 1990-03-23 Sanyo Electric Co Ltd 静電潜像担持体

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59119358A (ja) * 1982-12-27 1984-07-10 Toshiba Corp 電子写真感光体
JPS62269147A (ja) * 1986-05-16 1987-11-21 Canon Inc 光受容部材
JPS62276559A (ja) * 1986-05-26 1987-12-01 Canon Inc 光受容部材
JPH0283549A (ja) * 1988-09-20 1990-03-23 Sanyo Electric Co Ltd 静電潜像担持体

Also Published As

Publication number Publication date
JPWO2009096552A1 (ja) 2011-05-26
JP5436227B2 (ja) 2014-03-05

Similar Documents

Publication Publication Date Title
JP4499785B2 (ja) 電子写真感光体およびこれを備えた画像形成装置
JP4404942B2 (ja) 画像形成装置
JP4242893B2 (ja) 電子写真感光体およびこれを備えた画像形成装置
US8055156B2 (en) Image-forming apparatus which can eliminate static electricity
US8137878B2 (en) Electrophotographic photoreceptor, method for manufacturing the same, and image-forming apparatus using same
JP4776674B2 (ja) 電子写真感光体および画像形成装置
JP2004077650A (ja) 電子写真装置
JP4436823B2 (ja) 画像形成装置
WO2009104466A1 (fr) Photorécepteur électrophotographique et dispositif de formation d'image équipé de celui-ci
JP4242890B2 (ja) 電子写真感光体、これの製造方法および画像形成装置
JP4996684B2 (ja) 電子写真感光体およびその製造方法、並びに画像形成装置
JP5436227B2 (ja) 電子写真感光体、これを備えた画像形成装置および電子写真感光体の製造方法
US7672612B2 (en) Electrophotographic photosensitive member, and image forming apparatus using same
JP2002149029A (ja) 画像形成方法、画像形成装置、及び感光体
JP4283331B2 (ja) 画像形成装置
JP5311830B2 (ja) 電子写真装置
JP4273131B2 (ja) 電子写真感光体およびこれを備えた画像形成装置
WO2020022385A1 (fr) Photorécepteur électrophotographique et dispositif de formation d'image
JP2007293280A (ja) 電子写真感光体およびこれを備えた画像形成装置
JP4249751B2 (ja) 画像形成装置
JPWO2009028448A1 (ja) 電子写真感光体および該電子写真感光体を備える画像形成装置
JP2019144476A (ja) 電子写真感光体およびこれを備える画像形成装置
JP2009036932A (ja) 電子写真感光体およびこれを備えた画像形成装置
JPH11212286A (ja) 電子写真感光体
JP2009014777A (ja) 電子写真感光体の検査方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09706164

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2009551620

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09706164

Country of ref document: EP

Kind code of ref document: A1