Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
  • C09D5/20—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes for coatings strippable as coherent films, e.g. temporary coatings strippable as coherent films
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B08—CLEANING
  • B08B—CLEANING IN GENERAL; PREVENTION OF FOULING IN GENERAL
  • B08B7/00—Cleaning by methods not provided for in a single other subclass or a single group in this subclass
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B08—CLEANING
  • B08B—CLEANING IN GENERAL; PREVENTION OF FOULING IN GENERAL
  • B08B7/00—Cleaning by methods not provided for in a single other subclass or a single group in this subclass
  • B08B7/0014—Cleaning by methods not provided for in a single other subclass or a single group in this subclass by incorporation in a layer which is removed with the contaminants
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
  • C09D5/04—Thixotropic paints
• • C—CHEMISTRY; METALLURGY
  • C11—ANIMAL OR VEGETABLE OILS, FATS, FATTY SUBSTANCES OR WAXES; FATTY ACIDS THEREFROM; DETERGENTS; CANDLES
  • C11D—DETERGENT COMPOSITIONS; USE OF SINGLE SUBSTANCES AS DETERGENTS; SOAP OR SOAP-MAKING; RESIN SOAPS; RECOVERY OF GLYCEROL
  • C11D11/00—Special methods for preparing compositions containing mixtures of detergents
• • C—CHEMISTRY; METALLURGY
  • C11—ANIMAL OR VEGETABLE OILS, FATS, FATTY SUBSTANCES OR WAXES; FATTY ACIDS THEREFROM; DETERGENTS; CANDLES
  • C11D—DETERGENT COMPOSITIONS; USE OF SINGLE SUBSTANCES AS DETERGENTS; SOAP OR SOAP-MAKING; RESIN SOAPS; RECOVERY OF GLYCEROL
  • C11D3/00—Other compounding ingredients of detergent compositions covered in group C11D1/00
  • C11D3/16—Organic compounds
  • C11D3/37—Polymers
• • G—PHYSICS
  • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
  • G21F—PROTECTION AGAINST X-RADIATION, GAMMA RADIATION, CORPUSCULAR RADIATION OR PARTICLE BOMBARDMENT; TREATING RADIOACTIVELY CONTAMINATED MATERIAL; DECONTAMINATION ARRANGEMENTS THEREFOR
  • G21F9/00—Treating radioactively contaminated material; Decontamination arrangements therefor
  • G21F9/001—Decontamination of contaminated objects, apparatus, clothes, food; Preventing contamination thereof
  • G21F9/002—Decontamination of the surface of objects with chemical or electrochemical processes
• • G—PHYSICS
  • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
  • G21F—PROTECTION AGAINST X-RADIATION, GAMMA RADIATION, CORPUSCULAR RADIATION OR PARTICLE BOMBARDMENT; TREATING RADIOACTIVELY CONTAMINATED MATERIAL; DECONTAMINATION ARRANGEMENTS THEREFOR
  • G21F9/00—Treating radioactively contaminated material; Decontamination arrangements therefor
  • G21F9/001—Decontamination of contaminated objects, apparatus, clothes, food; Preventing contamination thereof
  • G21F9/005—Decontamination of the surface of objects by ablation
• • C—CHEMISTRY; METALLURGY
  • C11—ANIMAL OR VEGETABLE OILS, FATS, FATTY SUBSTANCES OR WAXES; FATTY ACIDS THEREFROM; DETERGENTS; CANDLES
  • C11D—DETERGENT COMPOSITIONS; USE OF SINGLE SUBSTANCES AS DETERGENTS; SOAP OR SOAP-MAKING; RESIN SOAPS; RECOVERY OF GLYCEROL
  • C11D2111/00—Cleaning compositions characterised by the objects to be cleaned; Cleaning compositions characterised by non-standard cleaning or washing processes
  • C11D2111/10—Objects to be cleaned
  • C11D2111/14—Hard surfaces
  • C11D2111/24—Mineral surfaces, e.g. stones, frescoes, plasters, walls or concretes
• • C—CHEMISTRY; METALLURGY
  • C11—ANIMAL OR VEGETABLE OILS, FATS, FATTY SUBSTANCES OR WAXES; FATTY ACIDS THEREFROM; DETERGENTS; CANDLES
  • C11D—DETERGENT COMPOSITIONS; USE OF SINGLE SUBSTANCES AS DETERGENTS; SOAP OR SOAP-MAKING; RESIN SOAPS; RECOVERY OF GLYCEROL
  • C11D2111/00—Cleaning compositions characterised by the objects to be cleaned; Cleaning compositions characterised by non-standard cleaning or washing processes
  • C11D2111/40—Specific cleaning or washing processes
  • C11D2111/42—Application of foam or a temporary coating on the surface to be cleaned

Definitions

• TITLE METHOD FOR PROTECTING SUBSTRATES AND REMOVING
• This invention relates to coating compositions for protecting substrates and for removing contaminants from such substrates. More particularly, this invention relates to sacrificial barrier coatings which may be used to protect a wide variety of substrate from a wide variety of contaminants, including graffiti, as well as radioactive contaminants (e.g., Iodine 131 , Technitium 99m, etc.), dirt or soil, toxins, and the like.
• sacrificial barrier coatings which may be used to protect a wide variety of substrate from a wide variety of contaminants, including graffiti, as well as radioactive contaminants (e.g., Iodine 131 , Technitium 99m, etc.), dirt or soil, toxins, and the like.
• Graffiti is a common problem encountered in areas of access to the general public. Moreover, generally, unwanted markings on surfaces can occur almost anywhere. For example, walls in homes may be marked accidentally or by children, and in the workplace walls and other surfaces may be marked inadvertently or unavoidably for any of a number of reasons. Graffiti is often in the form of paint, such as spray paint, but graffiti and other markings may be applied by markers, chalk, crayons, and other writing fluids. As used herein, the term "graffiti" will be used to refer broadly to unwanted markings, whether consisting of paint, other unwanted markings, scuff marks, and the like.
• Barrier coatings may be used to combat contaminant materials such as graffiti. These coatings may be divided into two categories: sacrificial and non- sacrificial. With both types of barrier coatings, the coatings prevent the contaminant from reaching the substrate, making the contaminant easy to remove. With a sacrificial barrier coating, as the name implies, at least a portion of the barrier coating is "sacrificed" during clean up. Clean up may involve, for example, washing, wiping, scrubbing, spraying and/or rinsing. After clean up, another coat of the sacrificial coating may be applied. Non-sacrificial barrier coatings, by contrast, do not involve removal of the coating and do not require recoating after the contaminant material has been removed. Non-sacrificial barrier coatings typically involve the use of coatings based on aliphatic urethane compounds, rubber silicone-based compounds, or waterbome polyurethanes.
• This invention relates to a method employing a sacrificial barrier coating for protecting a substrate from damage due to various contaminants.
• the inventive method comprises: applying a coating composition to the substrate, the coating composition comprising water, a water-soluble film forming polymer, a wetting agent and a thixotropic additive; dehydrating the coating composition and/or crosslinking the polymer to form a sacrificial barrier coating; depositing a contaminant material on the barrier coating; and removing the barrier coating and the contaminant material from the substrate.
• the barrier coating and the contaminant material may be removed by any number of traditional methods including washing, wiping, scrubbing, spraying and/or rinsing.
• the contaminant material may comprise any undesirable contaminant, including graffiti, as well as radioactive contaminants (e.g., Iodine 131 , Technitium 99m, etc.), dirt or soil, toxins, and the like.
• water-soluble refers to a material that is soluble in water at a temperature of 20 0 C to the extent of at least about 5 grams of the material per liter of water.
• water-soluble may also refer to a material that forms an emulsion in water.
• sacrificial barrier coating refers to a coating that is applied to a substrate to protect the substrate from contamination, and is at least partially removed, and in one embodiment completely removed, during clean up to remove the contaminant.
• the coating composition may comprise water, at least one water-soluble film forming polymer, at least one wetting agent, and at least one thixotropic additive.
• the polymer may comprise repeating units derived from vinyl alcohol and/or meth(acrylic) acid.
• the polymer may comprise vinyl alcohol, a copolymer of vinyl alcohol, or a mixture thereof.
• copolymer may be used herein to refer to a polymer with two or more different repeating units including copolymers, terpolymers, and the like.
• the polymer may comprise an atactic polyvinyl alcohol. These polymers may have a semicrystalline character and a strong tendency to exhibit both inter- molecular and intra-molecular hydrogen bonds.
• the polymer may comprise repeating units represented by the formula -CH 2 -
• the alkyl group may contain from 1 to about 6 carbon atoms, and in one embodiment from 1 to about 2 carbon atoms.
• the number of repeating units represented by the formula -CH 2 -CH(OCOR)- may be in the range from about
• ester groups may be substituted by acetaldehyde or butyraldehyde acetals.
• the polymer may comprise a polyvinyl alcohol/vinyl acetate) structure.
• the polymer may be in the form of a vinyl alcohol copolymer which also contains hydroxyl groups in the form of 1 ,2-glycols, such as copolymer units derived from 1 ,2- dihydroxyethylene.
• the copolymer may contain up to about 20 mole % of such units, and in one embodiment up to about 10 mole % of such units.
• the polymer may comprise a copolymer containing repeating units derived from vinyl alcohol and/or (meth)acrylic acid, and repeating units derived from one or more of vinyl acetate, ethylene, propylene, acrylic acid, methacrylic acid, acrylamide, methacrylamide, dimethacrylamide, hydroxyethylmethacrylate, methyl methacrylate, methyl acrylate, ethyl acrylate, vinyl pyrrolidone, hydroxyethylacrylate, allyl alcohol, and the like.
• the copolymer may contain up to about 50 mole % of repeating units other than those of vinyl alcohol, and in one embodiment from about 1 to about 20 mole % of such repeating units other than vinyl alcohol.
• the polymer may have a hydrolysis level in the range from about 70% to about 100%, and in one embodiment from about 70% to about 99.3%, and in one embodiment in the range from 70% to about 95%, and in one embodiment from about 70% to about 90%, and in one embodiment from about 75% to about 90%, and in one embodiment from about 87% to about 89%.
• the polymer may comprise one or more poly(meth)acrylic acids (i.e. polyacrylic acid and/or polymethacrylic acid).
• Polyacrylic Acid 5100 from Hampton Research
• Poly(acrylic acid) which is a partial sodium salt, lightly crosslinked polymer available from Sigma Aldrich
• Poly(acrylic acid) from Polysciences, lnc (MW -90000 g/mol)
• Poly(Acrylic Acid) from Polysciences lnc (MW: ⁇ 100000 g/mol).
• Polymethacrylic acids that may be used may include those available under tradenames Poly(methacrylic acid solution salt) from Sigma Aldrich (MW: -429,000 to 549,000 g/mol), and Poly Methacrylic Acid (25087-26-7) from Polysciences lnc (MW: -100,000 g/mol).
• the polymer may have an average molecular weight in the range from about 5,000 to about 2,000,000 g/mol, and in one embodiment from about 10,000 to about 1 ,000,000 g/mol, and in one embodiment from about 10,000 to about 600,000 g/mol, and in one embodiment from about 10,000 g/mol to about 250,000 g/mol, and in one embodiment from about 30,000 g/mol to about 190,000 g/mol, and in one embodiment in the range from about 50,000 to about 150,000 g/mole, and in one embodiment in the range from about 85,000 to about 125,000 g/mole.
• the concentration of the polymer in the coating composition (before dehydrating) may be in the range from about 0.1 to about 50% by weight, and in one embodiment from about 1 to about 25% by weight, and in one embodiment in the range from about 2 to about 15% by weight, and in one embodiment in the range from about 2 to about 6% by weight.
• the coating composition may have a concentration of water (before dehydrating) in the range from about 40 to about 99.9% by weight, and in one embodiment from about 75 to about 99% by weight, and in one embodiment from about 90 to about 99% by weight.
• the water may be derived from any source.
• the water may comprise deionized or distilled water.
• the water may comprise tap water.
• the water may comprise sterile nanopure water.
• the wetting agent may comprise one or more compounds that reduce the surface tension of the coating composition to permit it to spread across or penetrate more easily the surface of a substrate.
• the wetting agent may comprise a silicone surfactant.
• the wetting agent may comprise one or more polysiloxanes, for example, one or more poly(dimethylsiloxanes).
• the wetting agent may comprise one or more polysiloxanes, dimethylpolysiloxanes, polyether modified dimethylpolysiloxanes, polyester modified dimethylpolysiloxanes, polymethylalkylsiloxanes, aralkyl modified polymethylalkylsiloxanes, alcohol alkoxylates, polyacrylates, polymeric fluorosurfactants, fluoro modified polyacrylates, or a mixture of two or more thereof.
• a wetting agent that may be used is Byk-345 which is a product of Chemie identified as polyether modified siloxane.
• the wetting agent may function as a leveling agent.
• the concentration of the wetting agent in the coating composition may be in the range from about 0.05 to about 10% by weight of the coating composition, and in one embodiment in the range from about 0.1 to about 5% by weight, and in one embodiment from about 0.1 to about 2% by weight, and in one embodiment in the range from about 0.2 to about 1% by weight.
• the thixotropic additive may comprise one or more compounds that enables the coating composition to thicken or stiffen in a relatively short period of time on standing at rest but, upon agitation or manipulation (e.g., brushing, rolling, spraying) to flow freely.
• the thixotropic additive may comprise fumed silica, treated fumed silica, clay, hectorite clay, organically modified hectorite clay, a thixotropic polymer, a pseudoplastic polymer, polyurethane, a polyhydroxycarboxylic acid amide, modified urea, urea modified polyurethane, or a mixture of two or more thereof.
• a thixotropic additive that may be used is Byk-420 which is a product of Chemie identified as a modified urea.
• the concentration of the thixotropic additive in the coating composition (before dehydrating) may be in the range from about 0.01 to about 10% by weight of the coating composition, and in one embodiment in the range from about 0.05 to about 5% by weight, and in one embodiment from about 0.1 to about 4% by weight, and in one embodiment in the range from about 0.5 to about 3.5% by weight.
• the coating composition may further comprise one or more pseudoplastic additives, rheology modifiers, anti-sagging agent, anti-settling agents, leveling agents, pH modifiers, defoamers, pigments, dyes, organic solvents, plasticizers, viscosity stabilizers, biocides, viricides, fungicides, humectants, crosslinkers, surfactants, colorants, UV stabilizers, or a mixture of two or more thereof.
• pseudoplastic additives rheology modifiers, anti-sagging agent, anti-settling agents, leveling agents, pH modifiers, defoamers, pigments, dyes, organic solvents, plasticizers, viscosity stabilizers, biocides, viricides, fungicides, humectants, crosslinkers, surfactants, colorants, UV stabilizers, or a mixture of two or more thereof.
• a single additive may provide two or more of the foregoing functions.
• Byk-420 may function as both a thixotropic additive and an anti-sagging additive.
• the defoamer may comprise a polysiloxane defoamer.
• the defoamer may comprise octyl alcohol, aluminum stearate, a sulfonated hydrocarbon, a silicone, or a mixture of two or more thereof.
• a defoamer that may be used is Byk-028 which is a product of Chemie identified as a mixture of foam destroying polysiloxanes and hydrophobic solids in polyglycol.
• the pH modifier may comprise an alkali metal hydroxide such as sodium hydroxide or potassium hydroxide.
• the pH modifier may compirse hydrochloric acid, acetic acid, phosphoric acid, citric acid, or a mixture of two or more thereof.
• the organic solvent may comprise one or more alcohols, for example, methanol, ethanol, propanol, isopropanol, butanol, one or more ketones, for example, acetone, one or more acetates, for example, methyl acetate, or a mixture of two or more thereof.
• the plasticizer may comprise ethylene glycol, polyethylene glycol, propylene glycol, polypropylene glycol, butane diol, polybutylene glycol, glycerine, or a mixture of two or more thereof.
• the viscosity stabilizer may comprise a mono or multifunctional hydroxyl compound. These may include methanol, ethanol, propanol, butanol, ethylene glycol, polyethylene glycol, propylene glycol, polyethylene glycol, propylene glycol, polypropylene glycol, butane diol, polybutylene glycol, glycerol, or a mixture of two or more thereof.
• the biocide, viricide or fungicide may comprise sodium hypochlorite, potassium hypochlorite, pH-amended sodium hypochlorite, quaternary ammonium chloride, pH-amended bleach (Clorox®), CASCADTM surface decontamination foam (AllenVanguard), DeconGreen (Edgewood Chemical Biological Center), DioxiGuard (Frontier Pharmaceutical), EasyDecon 200 (Envirofoam Technologies), Exterm-6 (ClorDiSys Solutions), Hl-Clean 605 (Howard Industries), HM-4100 (Biosafe) KlearWater (Disinfection Technology), Peridox (Clean Earth Technologies) Selectrocide (BioProcess Associates), EasyDECONTM 200 decontamination solution, or a mixture of two or more thereof.
• the biocides may include Kathon LX (a product of Rohm and Hass Company comprising 5-chloro-2-methyl-4-isothiazolin-3-one and 2-methyl-4-isothiazolin-3-one) or Dowacil 75 (a product of Dow Chemical identified as being 1-(3-chloroallyl)-3,5,7-triaza-1-azoniaadamantane chloride and described as being useful as a preservative for antimicrobial protection).
• Kathon LX a product of Rohm and Hass Company comprising 5-chloro-2-methyl-4-isothiazolin-3-one and 2-methyl-4-isothiazolin-3-one
• Dowacil 75 a product of Dow Chemical identified as being 1-(3-chloroallyl)-3,5,7-triaza-1-azoniaadamantane chloride and described as being useful as a preservative for antimicrobial protection.
• the crosslinker may comprise sodium tertraborate, glyoxal, Sunrez 700 (a product of Sequa Chemicals identified as cyclic urea/glyoxal/polyol condensate), Bacote-20 (a product of Hopton Technology identified as stabilized ammonium zirconium carbonate), Polycup-172 (a product of Hercules, Inc. identified as a polyamide-epichlorohydrin resin), or a mixture of two or more thereof.
• Sunrez 700 a product of Sequa Chemicals identified as cyclic urea/glyoxal/polyol condensate
• Bacote-20 a product of Hopton Technology identified as stabilized ammonium zirconium carbonate
• Polycup-172 a product of Hercules, Inc. identified as a polyamide-epichlorohydrin resin
• the humectant may comprise polyacrylic acid, polyacrylic acid salt, an acrylic acid copolymer, a polyacrylic acid salt copolymer, or a mixture of two or more thereof.
• the surfactant may comprise sodium dodecyl sulfate, sodium lauryl sulfate, cetyltrimethylammonium bromide, cetyltrimethyl ammonium chloride, hexadecyl trimethyl ammonium bromide, hexadecyl trimethyl ammonium chloride, or a mixture of two or more thereof.
• the colorant may comprise one or more dyes, pigments, and the like. These may include blue food coloring from McCormick and Company Inc., and/or
• the colorant may comprise one or more dyes that become fluorescent upon drying or in response to a change in pH.
• the UV stabilizer may comprise one or more of a paraaminobenzoic acid (and derivatives), octyl cinnamate and its derivatives, benzophenone and its derivatives, ultrafine titanium dioxide powder and hindered amine/amide light stabilizers such as Ciba® CHIMASSORB® 944, Ciba® TINUVIN® 123, Ciba® TINUVIN® 622, Ciba® TINUVIN® 765, Ciba® TINUVIN® 770, Ciba® TINUVIN® P, Ciba®, TINUVIN® 213, Ciba® TINUVIN® 234, Ciba® TINUVIN® 326, Ciba® TINUVIN® 327, Ciba® TINUVIN® 328, Ciba® TINUVIN® 571 , Ciba® TINUVIN® B 75, and/or Ciba® TINUVIN® B 88.
• the concentration of each of the foregoing additives in the coating composition may be up to about 25% by weight, and in one embodiment up to about 10% by weight, and in one embodiment up to about 5% by weight, and in one embodiment up to about 2% by weight, and in one embodiment up to about 1 % by weight.
• the coating composition may have a broad range of viscosities and rheological properties which may allow the coating composition spread over the surface of a substrate and to allow for a variety of application methods including application via brush, roller, spray equipment, and the like.
• the Brookfield Viscosity of the coating composition (prior to dehydrating) may be in the range from about 5 to about 100,000 centipoise, and in one embodiment in the range from about 10 to about 25,000 centipoise measured at the rpm and spindle appropriate for the sample in the range of 0.3 - 200 rpm and spindles 1-4 at 25 0 C.
• the coating composition may have a sufficient viscosity to permit it to form a wet film on a horizontal and/or a non-horizontal substrate that upon dehydrating forms a solid matrix or film.
• the coating composition may have a pH in the range from about 4 to about 10, and in one embodiment in the range from about 4 to about 8.
• the inventive method may comprise applying the coating composition to a substrate and then dehydrating or drying the coating composition and/or crosslinking the polymer to form a sacrificial barrier coating.
• the coating composition may be applied to the substrate using conventional coating techniques, for example, brushing, rolling, spraying, spreading, smearing, and the like. Dehydration or drying may be enhanced using fans, dehumidifiers, a heat source, or a combination thereof.
• the barrier coating may remain applied to the substrate until the build up of contaminant material (e.g., graffiti) reaches the point where removal is desirable.
• the contaminant material along with at least part of the barrier coating, and in one embodiment all of the barrier coating, may then be removed from the substrate.
• the contaminant material and the barrier coating may be removed using conventional methods, for example, peeling, washing, wiping, scrubbing, spraying and/or rinsing. This may include applying composition comprising water (e.g., a cleaning solution comprising soap or detergent and water) to the contaminant and the barrier coating, and then removing the contaminant material and at least part of the barrier coating from the substrate.
• composition comprising water (e.g., a cleaning solution comprising soap or detergent and water)
• the contaminant material and the barrier coating may be removed by power washing at a temperature in the range from about 1O 0 C to about 100 0 C, and in one embodiment from about 5O 0 C to about 9O 0 C; and a pressure in the range from about 250 to about 5000 pounds per square inch (psi) (17.2 to 345 bars), and in one embodiment from about 500 to about 2500 psi (34.4 to 241.3 bars).
• the resulting barrier coating overlying the surface of the substrate may be transparent or colored, preferably transparent.
• the coating composition may be colored with one or more pigments, dyes, invisible dyes, and/or dyes that change color in response to a change in pH.
• the barrier coating may have a concentration of water in the range up to about 25% by weight, and in one embodiment up to about 15% by weight.
• the barrier coating may have a thickness in the range from about 0.25 to about 50 mils, and in one embodiment from about 0.2 to about 10 mils.
• the coating composition may be delivered to the point of use in the form of a concentrate containing a reduced concentration of water or in a rehydratable form such as a powder that may be rehyd rated at the time of use.
• the amount of the coating composition needed to adequately coat a substrate will be dependent on the nature of the surface of the substrate, with a greater quantity being needed to provide adequate coverage on more porous surfaces such as stucco, brick, cement and the like, and a smaller quantity being needed on smooth surfaces such as metal signs.
• the coat density may be in the range from about 100 to about 500 square feet per gallon for stucco, brick or similar porous surfaces, and from about 100 to about 1000 square feet per gallon for smooth surfaces. One or more coats may be applied.
• the barrier coating may be usable as a protective barrier as soon as it is dehydrated or dried, which may be within about 5 to about 180 minutes, depending on environmental conditions.
• the coating may form a transparent or colored shield or barrier layer over the underlying surface. Any contaminants, such as graffiti markings, deposited on the barrier coating may be prevented from contacting and marking the underlying surface. If a contaminant material such as graffiti is deposited on the barrier coating or if the coating becomes excessively soiled, the contaminant may be removed, together with at least part of the barrier coating, as described above. A new protective barrier coating may then be applied.
• the sacrificial barrier coating that is applied to a substrate pursuant to the inventive method may be water soluble or water soluble when contacted with a water based solution that contains additives that increase the water solubility of the barrier coating.
• the adhesion of the barrier coating to the substrate may be reduced when contacted with water or a water based solution containing additives that reduce the adhesion of the coating to the substrate.
• the sacrificial barrier coating may be sprayed from a traditional hand pump spray bottle or other spray apparatus. The coating may be sprayed on almost any surface including surfaces above urinals or on bathroom stalls known to be targets for contaminants such as graffiti. When the coating dries, it may act as a barrier coating protecting the substrate from contact with the contaminant.
• the coating When washed with water or a water based solution, the coating may dissolve and be removed thus also removing the contaminant.
• An example of a contaminant is the ink from a permanent marker.
• the ink When applied to a painted surface the ink may be difficult to remove requiring harsh scrubbing or solvents that may damage the painted surface. However, because the ink never touches the paint when the sacrificial barrier coating has been employed, the painted surface may be cleaned relatively easily and not be damaged during the cleaning process.
• the barrier coating and contaminant material may be removed by contacting the barrier coating and contaminant material with a treating composition comprising water, a water-soluble film forming polymer, a wetting agent and a thixotropic additive as described above.
• the treating composition may have the same formulation as the coating composition.
• the treating composition may be dehydrated to form a treating film, and the method may further comprise separating the barrier coating, contaminant material and treating film from the substrate.
• the barrier coating, contaminant material and treating film may be peeled from the substrate. This peeling may be accomplished in a single step.
• the coating composition may be used as a cleaning composition.
• a hand pump spray bottle can be used to apply the coating composition to a substrate that has a sacrificial barrier on it and graffiti written on the barrier coating.
• the graffiti may be removed by wiping it off in a traditional manner (e.g. traditional bathroom cleaner).
• a thin layer of the cleaning composition may be left behind that dries or dehydrates to form a layer of the sacrificial barrier coating. This may improve the ease of removal of contaminant materials such as graffiti in the future.
• the surface may also be sprayed an additional time with the coating composition leaving a thicker barrier coating and further improving the efficacy of the sacrificial barrier coating.
• the coating composition may include one or more crosslinkers.
• Sodium tetraborate as well as others as indicated above, may be used to crosslink polymers containing vinyl alcohol repeating units.
• Divalent or trivalent cations for example, calcium hydroxide or calcium oxide, may be used to crosslink polymers comprising repeating units derived from acrylic acid and/or methacrylic acid.
• the coating composition may be applied to a substrate at a pH below about 6.8, and after application as a coating, the pH may rise when in contact with the environment (or atmosphere). This may increase the crosslink density as the coating dehydrates or dries. Increasing the crosslink density may increase the stability of the coating in the presence of moisture such as in the exterior environment (outdoors).
• the coating may be removed using conventional methods such as washing, scrubbing, spraying, and the like. Removal of crosslinked barrier coatings may be facilitated by using a water solution with additives that destroy the crosslinks of the coatings.
• a water solution with additives that destroy the crosslinks of the coatings For example, an acidic solution with a pH below about 6.8, and in one embodiment below about 6.0, may be used.
• the acidic solution may be mixed with rinse water using, for example, a power washer attached to a city water outlet.
• the power washer may have attached to it, via a soap solution inlet, an inlet for a concentrated acid such as hydrochloric acid with a pH between about 0.0 and about 6.0.
• the acid solution may be mixed with the water when the power washer is in use, forming an aqueous solution with the desired pH.
• the crosslinks formed between, for example, a tetraborate anion and polyvinyl alcohol may be reduced, thus increasing the water solubility or water sensitivity of the barrier coating and thereby allowing for easier removal.
• Monovalent cations for example, sodium hydroxide or potassium hydroxide, may be used to increase the water solubility of un-neutralized or partially neutralized polymers comprising repeating units derived from acrylic acid and/or methacrylic acid as well as to reduce the crosslink density of the polymers that have been crosslinked with divalent or thvalent cations.
• the crosslinker may be used to decrease the barrier coating moisture sensitivity in outdoor environments and a water solution employing one or more additives may be used to increase the barrier coating moisture sensitivity during the cleaning process.
• Crosslinkers may be employed for interior and exterior applications.
• Example 1 The following examples are provided to further describe the invention. In these examples, as well as throughout the text, unless otherwise indicated, all parts and percentages are by weight.
• a jacketed one-liter reactor equipped with a thermocouple, condenser and stir motor is charged with 667.2g of distilled water, 4.2g of Byk-028, and 4.6g of 46% by weight NaOH.
• the resulting aqueous composition is agitated until the salts are dissolved followed by the addition of 169.6g of Celvol 523.
• the mixture is heated to 85 0 C and held for 30 minutes, then cooled to 65 0 C. 48.3g of 95% ethanol is added followed by 25.4g BYK-420 in a drop-wise fashion.
• the formulation is then agitated for one hour at 65 0 C.
• a premix of 1.7g of Dowicil 75 and 121.1 g of distilled water is slowly added with strong agitation.
• the mixture is then filtered to yield Formulation A.
• a jacketed one-liter reactor equipped with a thermocouple, condenser and stir motor is charged with 667.2g of distilled water, 4.2g of Byk-028, and 4.6g of 46% by weight NaOH.
• the resulting aqueous composition is agitated until the salts are dissolved followed by the addition of 169.6g of water soluble polymer Celvol 508.
• Formulation C has a Brookfield viscosity of
• Formulation D A 100.Og aliquot of Formulation C is added to 400.Og of Dl water under medium agitation and stirred for 20 minutes to yield Formulation D.
• the substrates are prepared using 12 inch
• Formulations B and D are drawn down onto the horizontal panels using the following wire wound draw down bars:
• #20, #40, #80, and #200 to produce reproducible wet film thicknesses of the formulations.
• permanent marker Sharpie brand
• the panels are wetted with water and agitated with paper towels to determine the barrier properties of the dried formulations.
• the #20 wire bar 2.0 mil wet film thickness
• Formulation D has bleed through of the marker resulting in incomplete removal of the permanent marker.
• Formulation B produces complete removal of the permanent marker.
• a 96.Og aliquot of Formulation B is mixed with 4.Og of BYK 307 (product of Chemie identified as a high slip polyether modified dimethylpolysiloxane copolymer) under medium agitation for 10 minutes to form Formulation F.
• BYK 307 product of Chemie identified as a high slip polyether modified dimethylpolysiloxane copolymer
• a 96.Og aliquot of Formulation B is mixed with 4.0g of BYK 345 under medium agitation for 10 minutes to form Formulation G.
• Formulations B, E, F, and G are drawn down on horizontal panels (as in Example 2) to determine wet out efficacy of each formulation at equal film thicknesses and compared as barrier coatings against a permanent marker (Sharpie brand). Each formulation produces an effective barrier coating with Formulation G being more effective than B, E, or F based on overall quality of wet out and lack of marker seep through.
• Example 6 20.Og of Formulation A are mixed with 80.Og of distilled water and 0.1g of
• Formulation H 20.Og of Formulation H are mixed with 80.Og of distilled water and 0.5g of BYK 345 under medium agitation for 10-15 minutes to yield Formulation J.
• Formulations B, H, I, and J are drawn down on painted panels (as in Example 2) at 2.0 mil wet film thickness to determine the efficacy of each. After 24 hours, a Sharpie brand marker is drawn across the dried filmed and allowed to cure for 20 minutes. Water and paper towel agitation are used to remove the films from the painted substrate. Each formulation produces an effective barrier coating with Formulation I providing better barrier protection while still contributing to wet out. This is shown below.
• a 99.2g aliquot of Formulation B is added to 0.8g of Stanfax 1025 (an aqueous sodium lauryl sulfate solution supplied by Para Chem, Chemidex LLC, which is abbreviated herein as S125) by mixing under medium agitation for 10-15 minutes to yield Formulation K.
• Stanfax 1025 an aqueous sodium lauryl sulfate solution supplied by Para Chem, Chemidex LLC, which is abbreviated herein as S125
• Formulation B A 98.4g aliquot of Formulation B is added to 1.6g of S125 by mixing under medium agitation for 10-15 minutes to yield formulation L.
• Formulations K and L are compared against Formulation B at equal film thicknesses as barrier coatings against permanent marker on both semi gloss and flat horizontal substrates.
• Each formulation is evaluated for leveling and marker test results on a scale of 1-5 (with 1 being the best). The results are summarized in the following table.
• a jacketed one-liter reactor equipped with a thermocouple, condenser and stir motor is charged with 656.1g of distilled water, 4.2g of Byk-028, and 4.6g of 46% by weight NaOH.
• the resulting aqueous composition is agitated until the salts are dissolved followed by the addition of 166.7g of Celvol 523.
• the mixture is heated to
• a 20.Og aliquot of Formulation M is mixed with 79.4g of water under medium agitation for 10 minutes.
• 0.6g Cab-O-Sperse 2020K (a dispersed fumed silica rheological additive from Cabot Corporation) is slowly added with increased agitation over 5 minutes. Agitation is continued for 10 minutes to yield Formulation M.
• Formulation S A 20.Og aliquot of Formulation M is mixed with 72.6g of water under medium agitation for 10 minutes. Agitation is increase to high as 7.4g Cab-O-Sperse 2020K is slowly added with increased agitation over 5 minutes. Agitation is continued for 10 minutes to yield Formulation S.
• the viscosity of Formulation S and Formulation B are as follows (200 rpm , L1 spindle, 25 0 C, Thermo Haake 6 Plus Viscotester):
• a 20.Og aliquot of Formulation M is mixed with 72.6 of water under medium agitation for 10 minutes. Agitation is increased as 7.4g Cab-O-Sperse 4012K (a small particle silica emulsion from Cobot Corporation) are slowly added with increased agitation over 5 minutes. Agitation is continued for 10 minutes to yield
• Formulations containing the fumed silica Cab-O-Sperse show a matting effect when applied to surfaces thus creating a flat appearance, complimentary as a barrier coating to flat or dull surfaces.
• a 30.Og aliquot of Formulation A is mixed with 0.3g of BYK 345, 69.Og distilled water, 0.05g of McCormick blue food coloring, and 1.0g of glycerol (99+% pure, synthetic supplied by Acros Organics) for 15 minutes to yield formulation U.
• a 30.Og aliquot of Formulation A is mixed with 0.3g BYK 345, 65.Og distilled water, 0.05g McCormick blue food coloring, and 5.Og glycerol (99+% pure, synthetic) under medium agitation for 15 minutes to yield Formulation W.
• Formulations U, V and W are drawn down on cured Rustoleum semi gloss spray painted panels at 2 mil wet film thicknesses and allowed to dry for 24 hours.
• Krylon blue spray paint is sprayed across the coated panels.
• the formulations are tested for ease of spray paint removal after 24 and 72 hour increments
• Formulation W The pH of Formulation W is adjusted using hydrochloric acid to 6.0. To this mixture is added 0.25g sodium tetraborate under high agitation for 5 minutes to yield Formulation X. Formulation X is drawn down at 2.0 mil wet film thickness onto a 12 inch (30.5 cm) square mirror and tested for film strength by scoring with a probe.
• a jacketed one-liter reactor equipped with a thermocouple, condenser and stir motor is charged with 450.Og of distilled water. Under high agitation, 50.Og Kuraray
• Exceval AQ 4104 ethylene vinyl alcohol
• Formulation Y A 300 ml_, three necked round bottom flask is equipped with a condenser and placed in a water bath. The flask is charged with 41.8g of Formulation Y, 0.214g of BYK 028, 0.094g of 46% NaOH, and heated to 65 0 C under medium agitation by stir bar. 0.321 g of BYK 345 is added slowly to the mixture and the agitation is increased. 1.142g of 70% isopropanol are added to the mixture drop wise followed by 0.60Og of BYK 420. The mixture is stirred at 65 0 C for one hour. A premix of 0.0368g Dowicil 75 and 50.5g distilled water is added with strong agitation. The formulation is cooled to yield Formulation Z.
• Formulation I is sprayed (using a Zep commercial spray bottle) on a vertical painted wall (Behr brand semigloss washable indoor) and allowed to dry for 12 hours. Krylon blue spray paint is sprayed onto the barrier (dried Formulation I) and cured for 72 hours. A strip of duct tape is firmly applied across the spray paint and peeled, taking with it much of the dried Krylon spray paint. A water soaked coarse sponge is used to remove the remaining spray paint and sacrificial coating from the painted wall.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Life Sciences & Earth Sciences (AREA)
• Wood Science & Technology (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• General Engineering & Computer Science (AREA)
• Food Science & Technology (AREA)
• Physics & Mathematics (AREA)
• Materials Engineering (AREA)
• High Energy & Nuclear Physics (AREA)
• Oil, Petroleum & Natural Gas (AREA)
• General Chemical & Material Sciences (AREA)
• Electrochemistry (AREA)
• Paints Or Removers (AREA)
• Cleaning In General (AREA)
• Prevention Of Fouling (AREA)
• Cleaning By Liquid Or Steam (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Cleaning Or Drying Semiconductors (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (2)

Family

ID=39917157

Family Applications (1)

Country Status (9)

Cited By (5)

Families Citing this family (29)

Family Cites Families (44)

• 2008
  • 2008-06-19 KR KR1020097026466A patent/KR20100031683A/ko not_active Withdrawn
  • 2008-06-19 CN CN200880020701A patent/CN101730727A/zh active Pending
  • 2008-06-19 EP EP08795935A patent/EP2162498B1/en not_active Not-in-force
  • 2008-06-19 CA CA2696161A patent/CA2696161A1/en not_active Abandoned
  • 2008-06-19 WO PCT/US2008/067454 patent/WO2008157670A2/en not_active Ceased
  • 2008-06-19 JP JP2010513401A patent/JP5313242B2/ja not_active Expired - Fee Related
  • 2008-06-19 AT AT08795935T patent/ATE505517T1/de not_active IP Right Cessation
  • 2008-06-19 DE DE602008006189T patent/DE602008006189D1/de active Active
  • 2008-06-19 US US12/142,059 patent/US20080317949A1/en not_active Abandoned

Also Published As

Similar Documents

Legal Events