Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/052—Li-accumulators
  • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/05—Accumulators with non-aqueous electrolyte
  • H01M10/058—Construction or manufacture
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/42—Methods or arrangements for servicing or maintenance of secondary cells or secondary half-cells
  • H01M10/52—Removing gases inside the secondary cell, e.g. by absorption
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/116—Primary casings; Jackets or wrappings characterised by the material
  • H01M50/121—Organic material
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/131—Primary casings; Jackets or wrappings characterised by physical properties, e.g. gas permeability, size or heat resistance
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/131—Primary casings; Jackets or wrappings characterised by physical properties, e.g. gas permeability, size or heat resistance
  • H01M50/133—Thickness
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M10/00—Secondary cells; Manufacture thereof
  • H01M10/42—Methods or arrangements for servicing or maintenance of secondary cells or secondary half-cells
  • H01M10/4235—Safety or regulating additives or arrangements in electrodes, separators or electrolyte
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
  • H01M50/10—Primary casings; Jackets or wrappings
  • H01M50/116—Primary casings; Jackets or wrappings characterised by the material
  • H01M50/124—Primary casings; Jackets or wrappings characterised by the material having a layered structure
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/10—Energy storage using batteries
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
  • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
  • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Definitions

• the present invention relates to rechargeable lithium batteries containing means capable of sorbing the harmful substances generated by these batteries during their use.
• Rechargeable lithium batteries are used in several electronic devices thanks to their greater capacity and power and energy density. Recent developments of these batteries that have further improved their performances allow their use also in hybrid or totally electric vehicles. Rechargeable lithium batteries and their operation principle are widely known.
• a lithium battery comprises two electrodes (anode and cathode) spaced apart by means of a separator and immersed in an electrolyte.
• the oxidation reaction occurs on the anode and allows to release electrons into the electric circuit, whereas the reduction reaction occurs on the cathode and allows to reintroduce electrons into the battery through the electric circuit.
• the electrolyte has the purpose of completing the electric circuit of the battery by allowing the ions transportation from one electrode to the other, whereas the separator has the function of preventing a short-circuit between cathode and anode.
• lithium batteries are essentially comprised of an airtight container inside which are arranged electrodes (anode and cathode) immersed or impregnated with special electrolytic solutions and spaced apart by means of a separator, and electrical contacts communicating a portion of these electrodes with the outside of the battery.
• a 20 ⁇ m thick aluminum sheet is typically coated with oxides such as LiCoO 2 , LiNiO 2 , LiMn 2 O 4 , LiFePO 4 , also mixed oxides of Ni and Co according to the formula LiCo x Nii_ x O 2 may be employed for this purpose.
• oxides such as LiCoO 2 , LiNiO 2 , LiMn 2 O 4 , LiFePO 4 , also mixed oxides of Ni and Co according to the formula LiCo x Nii_ x O 2 may be employed for this purpose.
• the anode is typically made of a copper sheet coated with graphite. In the rest of the description of the invention anode and cathode will no longer be distinguished, but these elements will be generically identified with the term electrode.
• electrolytic solutions these are typically formed of an organic solvent and a ionic salt.
• lithium hexafluorophosphate LiPF 6
• solvents mostly used are propylene carbonate (PC), dimethyl carbonate (DMC), diethyl carbonate (DEC), ethyl carbonate (EC) and dimethyl ethane (DME) alone, or more commonly a mixture of two or more components chosen among these.
• the separator is generally made of a porous polymeric material that is permeable to lithium ions.
• Harmful substances being often in a gaseous form, may be generated inside lithium batteries during their use, which may damage the batteries even in an irreparable manner. Another possible source of harmful substances may be due to the desorption of some materials used inside the battery. More details about the mechanisms generating harmful species inside lithium batteries may be found in the article "Gas generation mechanism due to electrolyte decomposition in commercial lithium-ion cell", by Kumai et. al. published in 1999 on the Journal of Power Sources, pages 715-719, and in the article "In situ study on CO 2 evolution at lithium-ion battery cathodes", by Vetter et al., published in 2006 on the Journal of Power Sources, pages 277-281.
• Carbon dioxide (CO 2 ), carbon monoxide (CO), saturated and unsaturated hydrocarbons, oxygen (O 2 ) and hydrofluoric acid (HF) are among the most harmful gaseous species, whereas water (H 2 O), which is another very harmful species, is typically present in liquid phase dissolved in the electrolytic solution. CO 2 too may be present in liquid phase, although the major risks associated to its presence inside the battery are due to its gaseous phase.
• getter materials are used for the manufacturing of composite barriers, i.e. their function is to prevent impurities from entering the electrochemical cell rather than sorbing the gases present or generated therein.
• patent application US 2007/0042264 mentions the presence of barrier layers for the sorption of H 2 O in the area where the battery is sealed, while in this document the presence of getter materials in lithium batteries is said to be useful without describing the methods for introducing these materials inside the electrochemical device.
• the possible use of barrier layers made of getter materials inside lithium batteries is also described in patent application WO 2005/067645 and in patent application US 2006/0286448.
• the solutions of the prior art can prevent or slow down the ingress of harmful substances inside the battery, but they are not efficient as to the sorption of the harmful substances generated or present inside the same battery.
• the present invention relates to a rechargeable lithium battery being able to overcome the problems still present in the prior art, and it particularly consists in a rechargeable lithium battery comprising an airtight container, electrodes immersed in an electrolytic solution, said electrodes being spaced apart by means of one or more separators, electrical contacts connected to the electrodes and a means for sorbing harmful substances, characterized in that said means for sorbing harmful substances comprises a polymeric housing being permeable to said harmful substances but impermeable to the electrolyte and containing one or more getter materials for the sorption of said harmful substances.
• figure 1 shows a means for the sorption of harmful substances in rechargeable lithium batteries according to the present invention
• figure 2 shows another embodiment of a means for the sorption of harmful substances in rechargeable lithium batteries of the invention
• figure 3 shows a sectional (broken) view of a rechargeable lithium battery comprising a permeable polymeric container containing getter materials
• figure 4 shows an alternative embodiment of the rechargeable lithium battery shown in figure 3
• figure 5 shows a longitudinal-sectional view of a rechargeable lithium battery having a different shape and comprising a permeable polymeric housing containing getter materials
• figure 6 shows a cross-sectional view of a preferred embodiment of the rechargeable lithium battery shown in figure 5.
• Figure 1 shows a means 10 for the sorption of harmful substances, comprised of two polymeric sheets 11 and 12 welded to each other and defining a cavity 13 containing powders of one or more getter materials 14.
• At least one and preferably both the materials forming the polymeric sheets 11, 12 are permeable to the harmful substances but impermeable to the electrolyte, thus accomplishing a protective action with respect to the getter material.
• the thickness of the polymeric sheets 11, 12 is a very important parameter for carrying out the invention, as it is necessary that these sheets are thin in order to allow an effective permeation of the harmful substances, but at the same time the sheets must be thick enough to prevent them from breaking and to avoid the consequent loss of getter material. In order to satisfy these contrasting requirements it has been determined that the thickness of the polymeric sheets is comprised between 2 and 50 ⁇ m and preferably between 5 and 15 ⁇ m. In a preferred embodiment the two polymeric sheets have the same thickness.
• Means for the sorption of harmful substances for the use in rechargeable lithium batteries having a structure similar to that described in figure 1 might also be obtained by using a single polymeric sheet folded on itself along a line, thus forming one side of the means and being welded along the other side or the other sides in order to form a closed cavity completely similar to cavity 13. Moreover by doing so the previously described preferred embodiment is obtained, i.e. sheets 11 and 12 have the same thickness and the same permeability.
• the means for sorbing the harmful substances is arranged along one of the inner walls of the rechargeable lithium battery, it is possible to use a higher thickness for the sheet contacting said wall, as there is no permeation of harmful substances along the contact surface between the getter system and the battery wall.
• the getter materials contained in the polymeric housing are preferably in the form of powders, with a size comprised between 10 and 60 ⁇ m. It also possible that the getter material is used in the form of pills formed of compressed powders. Such an embodiment is useful when a larger amount of getter material must be introduced into the battery.
• Figure 2 shows a system 20 for the sorption of harmful substances, wherein two different getter materials 22, 22' are introduced in the form of pills enclosed in a cylindrical housing 21 made of a polymeric material permeable to the harmful substances.
• a variation of the system of figure 2 is a single pill formed of getter material powders enclosed in a (generically cylindrical) polymeric housing, permeable to the harmful substances, in direct contact with the surface of the pill; a similar sorbing means (not shown in the drawings) can find application in batteries of suitable shape, e.g. button-like batteries.
• Getter materials in permeable polymeric housings used in other applications and fields are known and described for instance in patents US 4,830643, US 5,743,942 and US 6,428,612.
• suitable materials for carrying out the invention are polyolefms, in particular polyethylenes, and more in particular low density polyethylene (LDPE), polypropylene (PP), polystyrene and thermoplastic olefins (TPE), or fluorinated polymers such as polytetrafluorethylene (PTFE).
• LDPE low density polyethylene
• PP polypropylene
• TPE thermoplastic olefins
• fluorinated polymers such as polytetrafluorethylene (PTFE).
• EVA ethyl- vinyl-acetate
• the getter materials employed in the means for removing harmful substances are of various types, depending on the harmful substances to be removed from the battery.
• the nature of these substances, for each type of lithium battery, may be determined through preliminary tests carried out on batteries being not provided with means for the removal of harmful substances.
• the harmful substance is H 2 O it is possible to use oxides of alkaline-earth metals (preferred oxides of this type are magnesium and calcium oxides), boron oxide or zeolites of various nature.
• suitable getter materials for carrying out the invention are carbon molecular sieves (CMS), hydroxides of alkaline and alkaline-earth metals (lithium and sodium in particular), lithium salts like LiXO y , with X chosen among zirconium, iron, nickel, titanium, silicon and y comprised between 2 and 4.
• MOF Metal Organic Framework
• aminic groups such as aminic groups.
• cobalt (II, III) oxide Co 3 O 4 , copper (II) oxide CuO, or potassium permanganate KMnO 4 may be used, to be preferably used in combination with a CO 2 sorber.
• cobalt (II, III) oxide Co 3 O 4 , copper (II) oxide CuO, or potassium permanganate KMnO 4 may be used, to be preferably used in combination with a CO 2 sorber.
• oxidation catalysts such as Pt, Pd, Rh.
• the harmful substance is hydrogen in the gaseous phase
• ternary alloys among zirconium, cobalt and rare earths, sold by the applicant under the name St 787, or more generally non-evaporable getter alloys or unsaturated organic compounds may be used.
• the harmful substances are saturated or unsaturated hydrocarbons, referring in particular but not exclusively to methane, propylene, ethane and propane, activated carbons having a large specific surface area, carbon nanotubes, oxidizing compounds like KMnO 4 or combinations thereof may be used.
• ternary alloys among zirconium, vanadium and iron sold by the applicant under the name St 707 ternary alloys among zirconium, cobalt and rare earths, sold by the applicant under the name St 787, or more generally non-evaporable getter alloys.
• metals may be used, among which nickel, copper, iron or reduced or partially reduced metal oxides are preferred, among which iron, nickel, tin or copper oxides or combinations thereof are preferred.
• oxides in general may be used, with particular reference to basic oxides, among which oxides of alkaline or alkaline-earth metals are preferred. Among these oxides the use of magnesium oxide is even more preferred.
• the means for sorbing harmful substances suitable for the aims of the present invention may contain one or more getter materials depending on the harmful substance that must be removed from the battery.
• the expected composition of such substances produced during the operation of the battery may vary on the basis of the type of rechargeable battery and of its conditions of use, whereby it is possible to choose a mix of getter powders on the basis of the battery type in an optimum manner.
• the rechargeable lithium batteries of the present invention may be made by arranging the permeable housing containing the getter material along one side of the battery, in a region of the battery free from electrodes, e.g. as shown in figure 3.
• the structure of the rechargeable lithium battery 30 comprises a series of electrodes (in order not to jeopardize the understanding of the drawing only the two outermost electrodes 32, 32' have been illustrated) in the form of parallel metallic plates spaced apart by separators and immersed in an electrolytic solution (these members are not shown).
• the permeable polymeric housing 33 is arranged, containing the getter material for the sorption of harmful gases.
• the electrical contacts 34 and 34' communicate the electrodes with the outside of the airtight container 31 of the battery.
• Figure 3 shows a preferred embodiment of a rechargeable lithium battery 30.
• Figure 4 shows a rechargeable lithium battery 40 similar to the one described with reference to figure 3 (the members of figure 4 having the same numerals of those of figure 3 are equal to those previously described), wherein a portion 43 for containing the means for the sorption of harmful substances is added to the structure of the battery, the means 45 comprising a getter material.
• portion 43 containing the permeable polymeric housing containing in turn the getter material for the sorption of harmful substances forms a portion of the airtight container of the battery, which portion is free from the members of the battery (electrodes, contacts, separators) but communicates with the inside of the battery along one side. If the permeable polymeric housing does not occupy the whole available volume of portion 43, a portion of the remaining volume is filled by the electrolyte.
• the permeable housing containing the getter material may be inserted in the central portion of the rechargeable lithium battery, e.g. as shown in figure 5.
• battery 50 has a cylindrical shape and a longitudinal section thereof taken along its axis is shown.
• the battery comprises an airtight container 51 whose electrodes 52 are in the form of thin sheets wound to form a spiral and immersed in a liquid electrolyte. A sectional view of these sheets is shown by means of parallel vertical lines close to each other. The separator arranged between the electrodes is not shown.
• Electrical contacts 54, 54' communicate the electrodes with the outside of the airtight container (in figure 5 the electrical contacts have been drawn as members separated from the electrodes for the sake of clarity only).
• the means 55 for the sorption of the harmful substances, consisting of a permeable polymeric housing containing the getter material is arranged in the central portion of this battery.
• FIG. 6 Another preferred embodiment for this type of rechargeable lithium battery is shown in figure 6.
• the battery, 60 still has a cylindrical shape and its electrodes are in the form of a wound spiral 62.
• a portion 63 is provided, which serves for accommodating the means 65 for the sorption of harmful substances, being also in this case in the form of a permeable polymeric housing containing the getter material.
• This embodiment is particularly advantageous as there are no special geometrical limits due to the proximity of the means for the sorption of harmful substances to the electrical contacts.
• a separating grid (not shown) between the portions 43 and 63 accommodating the permeable polymeric housing and the electrodes, in order to prevent these latter from damaging the polymeric housing thus causing the loss of the getter material contained therein.
• a grid must be electrically inert, as contacting the different electrodes it must not cause short- circuits among them.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Materials Engineering (AREA)
• Secondary Cells (AREA)
• Solid-Sorbent Or Filter-Aiding Compositions (AREA)

Priority Applications (9)

Applications Claiming Priority (2)

Publications (1)

Family

ID=39707961

Family Applications (1)

Country Status (11)

Cited By (10)

Families Citing this family (22)

Citations (10)

Family Cites Families (29)

• 2007
  • 2007-06-05 IT IT001147A patent/ITMI20071147A1/it unknown
• 2008
  • 2008-06-04 KR KR1020097027630A patent/KR101522638B1/ko active Active
  • 2008-06-04 CA CA002686346A patent/CA2686346A1/en not_active Abandoned
  • 2008-06-04 EP EP08760465.8A patent/EP2156508B1/en active Active
  • 2008-06-04 AU AU2008258579A patent/AU2008258579A1/en not_active Abandoned
  • 2008-06-04 BR BRPI0811237-1A2A patent/BRPI0811237A2/pt not_active Application Discontinuation
  • 2008-06-04 JP JP2010510776A patent/JP5559042B2/ja active Active
  • 2008-06-04 US US12/600,461 patent/US8460808B2/en active Active
  • 2008-06-04 CN CN2008800188954A patent/CN101682078B/zh active Active
  • 2008-06-04 WO PCT/EP2008/056882 patent/WO2008148781A1/en not_active Ceased
• 2009
  • 2009-11-26 IL IL202368A patent/IL202368A0/en unknown

Patent Citations (10)

Also Published As

Similar Documents

Legal Events