Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K11/00—Luminescent, e.g. electroluminescent, chemiluminescent materials
  • C09K11/08—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials
  • C09K11/0883—Arsenides; Nitrides; Phosphides
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K11/00—Luminescent, e.g. electroluminescent, chemiluminescent materials
  • C09K11/08—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials
  • C09K11/77—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials containing rare earth metals
  • C09K11/7715—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials containing rare earth metals containing cerium
  • C09K11/77218—Silicon Aluminium Nitrides or Silicon Aluminium Oxynitrides
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K11/00—Luminescent, e.g. electroluminescent, chemiluminescent materials
  • C09K11/08—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials
  • C09K11/77—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials containing rare earth metals
  • C09K11/7728—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials containing rare earth metals containing europium
  • C09K11/77348—Silicon Aluminium Nitrides or Silicon Aluminium Oxynitrides
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K11/00—Luminescent, e.g. electroluminescent, chemiluminescent materials
  • C09K11/08—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials
  • C09K11/77—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials containing rare earth metals
  • C09K11/7783—Luminescent, e.g. electroluminescent, chemiluminescent materials containing inorganic luminescent materials containing rare earth metals containing two or more rare earth metals one of which being europium
  • C09K11/77928—Silicon Aluminium Nitrides or Silicon Aluminium Oxynitrides
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
  • H01L2224/00—Indexing scheme for arrangements for connecting or disconnecting semiconductor or solid-state bodies and methods related thereto as covered by H01L24/00
  • H01L2224/01—Means for bonding being attached to, or being formed on, the surface to be connected, e.g. chip-to-package, die-attach, "first-level" interconnects; Manufacturing methods related thereto
  • H01L2224/42—Wire connectors; Manufacturing methods related thereto
  • H01L2224/47—Structure, shape, material or disposition of the wire connectors after the connecting process
  • H01L2224/48—Structure, shape, material or disposition of the wire connectors after the connecting process of an individual wire connector
  • H01L2224/4805—Shape
  • H01L2224/4809—Loop shape
  • H01L2224/48091—Arched
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
  • H01L2224/00—Indexing scheme for arrangements for connecting or disconnecting semiconductor or solid-state bodies and methods related thereto as covered by H01L24/00
  • H01L2224/01—Means for bonding being attached to, or being formed on, the surface to be connected, e.g. chip-to-package, die-attach, "first-level" interconnects; Manufacturing methods related thereto
  • H01L2224/42—Wire connectors; Manufacturing methods related thereto
  • H01L2224/47—Structure, shape, material or disposition of the wire connectors after the connecting process
  • H01L2224/48—Structure, shape, material or disposition of the wire connectors after the connecting process of an individual wire connector
  • H01L2224/481—Disposition
  • H01L2224/48151—Connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive
  • H01L2224/48221—Connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive the body and the item being stacked
  • H01L2224/48245—Connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive the body and the item being stacked the item being metallic
  • H01L2224/48247—Connecting between a semiconductor or solid-state body and an item not being a semiconductor or solid-state body, e.g. chip-to-substrate, chip-to-passive the body and the item being stacked the item being metallic connecting the wire to a bond pad of the item
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01L—SEMICONDUCTOR DEVICES NOT COVERED BY CLASS H10
  • H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
  • H01L2924/15—Details of package parts other than the semiconductor or other solid state devices to be connected
  • H01L2924/181—Encapsulation
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10H—INORGANIC LIGHT-EMITTING SEMICONDUCTOR DEVICES HAVING POTENTIAL BARRIERS
  • H10H20/00—Individual inorganic light-emitting semiconductor devices having potential barriers, e.g. light-emitting diodes [LED]
  • H10H20/80—Constructional details
  • H10H20/85—Packages
  • H10H20/851—Wavelength conversion means
  • H10H20/8511—Wavelength conversion means characterised by their material, e.g. binder
  • H10H20/8512—Wavelength conversion materials
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10H—INORGANIC LIGHT-EMITTING SEMICONDUCTOR DEVICES HAVING POTENTIAL BARRIERS
  • H10H20/00—Individual inorganic light-emitting semiconductor devices having potential barriers, e.g. light-emitting diodes [LED]
  • H10H20/80—Constructional details
  • H10H20/85—Packages
  • H10H20/851—Wavelength conversion means
  • H10H20/8515—Wavelength conversion means not being in contact with the bodies
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K50/00—Organic light-emitting devices
  • H10K50/10—OLEDs or polymer light-emitting diodes [PLED]
  • H10K50/11—OLEDs or polymer light-emitting diodes [PLED] characterised by the electroluminescent [EL] layers
  • H10K50/125—OLEDs or polymer light-emitting diodes [PLED] characterised by the electroluminescent [EL] layers specially adapted for multicolour light emission, e.g. for emitting white light

Definitions

• the present exemplary embodiments relate to novel phosphor compositions. They find particular application in conjunction with converting LED-generated ultraviolet (UV) 1 violet or blue radiation into white light or other colored light for general illumination purposes. It should be appreciated, however, that the invention is also applicable to the conversion of radiation in Hg-based fluorescent lamps, in gas discharge lamps, as scintillating detector elements in computed tomography (CT) and positron emission tomography (PET), UV, violet and/or blue lasers, as well as other white or colored light sources for different applications.
• CT computed tomography
• PET positron emission tomography
• LEDs Light emitting diodes
• LEDs are semiconductor light emitters often used as a replacement for other light sources, such as incandescent lamps. They are particularly useful as display lights, warning lights and indicating lights or in other applications where colored light is desired. The color of light produced by an LED is dependent on the type of semiconductor material used in its manufacture.
• Colored semiconductor light emitting devices including light emitting diodes and lasers (both are generally referred to herein as LEDs), have been produced from Group IH-V alloys such as gallium nitride (GaN).
• Group IH-V alloys such as gallium nitride (GaN).
• GaN gallium nitride
• layers of the alloys are typically deposited epitaxially on a substrate, such as silicon carbide or sapphire, and may be doped with a variety of n and p type dopants to improve properties, such as light emission efficiency.
• GaN-based LEDs With reference to the GaN-based LEDs, light is generally emitted in the UV and/or blue range of the electromagnetic spectrum.
• LEDs have not been suitable for lighting uses where a bright white light is needed, due to the inherent color of the light produced by the LED.
• a phosphor is a luminescent material that absorbs radiation energy in a portion of the electromagnetic spectrum and emits energy in another portion of the electromagnetic spectrum.
• Phosphors of one important class are crystalline inorganic compounds of very high chemical purity and of controlled composition to which small quantities of other elements (called "activators”) have been added to convert them into efficient fluorescent materials. With the right combination of activators and host inorganic compounds, the color of the emission can be controlled. Most useful and well-known phosphors emit radiation in the visible portion of the electromagnetic spectrum in response to excitation by electromagnetic radiation outside the visible range.
• a combination of LED generated light and phosphor generated light may be used to produce white light.
• the most popular white LEDs are based on blue emitting GaInN chips.
• the " blue emitting chips are coated with a phosphor that converts some of the blue radiation to a complementary color, e.g. a yellow-green emission.
• the total of the light from the phosphor and the LED chip provides a color point with corresponding color coordinates (x and y) in the CIE 1931 chromaticity diagram and correlated color temperature (CCT), and its spectral distribution provides a color rendering capability, measured by the color rendering index (CRI).
• CCT color rendering index
• the CRI is commonly defined as a mean value for 8 standard color samples (R-i-e), usually referred to as the General Color Rendering Index and abbreviated as R a .
• One known white light emitting device comprises a blue light- emitting LED having a peak emission wavelength in the blue range (from about 440 nm to about 480 nm) combined with a phosphor, such as cerium doped yttrium aluminum garnet Y 3 AI 5 O- ⁇ Ce 3+ ("YAG").
• a phosphor such as cerium doped yttrium aluminum garnet Y 3 AI 5 O- ⁇ Ce 3+ ("YAG").
• YAG cerium doped yttrium aluminum garnet Y 3 AI 5 O- ⁇ Ce 3+
• the blue LED-YAG phosphor device described above typically produces a white light with a general color rendering index (R 3 ) of from about 70-82 with a tunable color temperature range of from about 4000K to 8000K.
• Typical general lighting applications require a higher CRl and lower CCT values than possible using the blue LED-YAG approach.
• a phosphor comprising Cai_ a - b Ce a Eu b AI 1+a Si 1-a N 3 , where 0 ⁇ a ⁇ 0.2, 0 ⁇ b ⁇ 0.2.
• a phosphor comprising Ca- I-0 . d Ce 0 Eu d AI 1-c (Mg ,Zn) 0 SiN 3 , where 0 ⁇ c ⁇ 0.2, 0 ⁇ d ⁇ 0.2.
• a phosphor comprising Ca-i -2e - fCee(Li,Na) e EufAlSiN3, where O ⁇ e ⁇ O.2, 0 ⁇ f ⁇ 0.2, e+f>0.
• a phosphor comprising Cai. g -h- iCeg(Li I Na) h Eu l Ali+g- h Sii -g+h N 3 where 0 ⁇ g ⁇ 0.2, 0 ⁇ h ⁇ 0.4, 0 ⁇ i ⁇ 0.2 ⁇ , g+i>0.
• a light emitting device including a semiconductor light source having a peak emission from about 250 to about
• a phosphor blend including one or more of the phosphors as defined above and at least one additional phosphor, wherein the phosphor blend is capable of emitting light suitable for use in general illumination either alone or in combination with radiation emitted by a semiconductor light source radiationally coupled to the phosphor blend.
• FIGURE 1 is a schematic cross-sectional view of an illumination system in accordance with one embodiment of the present invention.
• FIGURE 2 is a schematic cross-sectional view of an illumination system in accordance with a second embodiment of the present invention.
• FIGURE 3 is a schematic cross-sectional view of an illumination system in accordance with a third embodiment of the present invention.
• FIGURE 4 is a cutaway side perspective view of an illumination system in accordance with a fourth embodiment of the present invention.
• FIGURE 5 is the emission spectrum of one present embodiment phosphor under 470 nm excitation.
• FIGURE 6 are the emission and absorption spectra of another present embodiment phosphor.
• FIGURE 7 are the emission spectra of various phosphors according to another embodiment.
• FIGURE 8 are the diffuse reflectance spectra of various phosphors according to another embodiment.
• FIGURE 9 is the simulated emission spectrum of an LED based lamp according to another present embodiment.
• Phosphors convert radiation (energy) to visible light. Different combinations of phosphors provide different colored light emissions. The colored light that originates from the phosphors provides a color temperature. Novel phosphor compositions are presented herein as well as their use in LED and other light sources.
• a phosphor conversion material (phosphor material) converts generated UV or blue radiation to a different wavelength visible light. The color of the generated visible light is dependent on the particular components of the phosphor material.
• the phosphor material may include only a single phosphor composition or two or more phosphors of basic color, for example a particular mix with one or more of a yellow and red phosphor to emit a desired color (tint) of light.
• the term "phosphor material" is intended to include both a single phosphor composition as well as a blend of two or more phosphor compositions.
• a luminescent material phosphor conversion material coated LED chip for providing white light.
• the phosphor material may be an individual phosphor or a phosphor blend of two or more phosphor compositions, including individual phosphors that convert radiation at a specified wavelength, for example radiation from about 250 to 550 nm as emitted by a UV to visible LED, into a different wavelength visible light.
• the visible light provided by the phosphor material (and LED chip- if emitting visible light) comprises a bright white light with high intensity and brightness.
• the light emitting assembly 10 comprises a semiconductor UV or visible radiation source, such as a light emitting diode (LED) chip 12 and leads 14 electrically attached to the LED chip.
• the leads 14 may comprise thin wires supported by a thicker lead frame(s) 16 or the. leads may comprise self supported electrodes and the lead frame may be omitted.
• the leads 14 provide current to the LED chip 12 and thus cause the LED chip 12 to emit radiation.
• the lamp may include any semiconductor visible or UV light source that is capable of producing white light when its emitted radiation is directed onto the phosphor.
• the preferred peak emission of the LED chip in the present invention will depend on the identity of the phosphors in the disclosed embodiments and may range from, e.g., 250 - 550 nm. In one preferred embodiment, however, the emission of the LED will be in the near UV to deep, blue region and have a peak wavelength in the range from about 350 to about 500 nm.
• the semiconductor light source comprises an LED doped with various impurities.
• the LED may comprise a semiconductor diode based on any suitable Hl-V, H-VI or IV-IV semiconductor layers and having a peak emission wavelength of about 250 to 550 nm.
• the LED may contain at least one semiconductor layer comprising GaN, ZnSe or SiC.
• Such LED semiconductors are known in the art.
• the radiation source is described herein as an LED for convenience.
• the term is meant to encompass all semiconductor radiation sources including, e.g., semiconductor laser diodes.
• semiconductor radiation sources including, e.g., semiconductor laser diodes.
• the general discussion of the exemplary structures of the invention discussed herein are directed toward inorganic LED based light sources, it should be understood that the LED chip may be replaced by an organic light emissive structure or other radiation source unless otherwise noted and that any reference to LED chip or semiconductor is merely representative of any appropriate radiation source.
• the LED chip 12 may be encapsulated within a shell 18, which encloses the LED chip and an encapsulant material 20.
• the shell 18 may be, for example, glass or plastic.
• the LED 12 is substantially centered in the encapsulant 20.
• the encapsulant 20 is preferably an epoxy, plastic, , low temperature glass, polymer, thermoplastic, thermoset material, resin, silicone, or other type of. LED encapsulating material as is known in the art.
• the encapsulant 20 is a spin-on glass or some other high index of refraction material.
• the encapsulant material 20 is an epoxy or a polymer material, such as silicone.
• Both the shell 18 and the encapsulant 20 are preferably transparent or substantially optically transmissive with respect to the wavelength of light produced by the LED chip 12 and a phosphor material 22 (described below).
• the lamp 10 may only comprise an encapsulant material without an outer shell 18.
• the LED chip 12 may be supported, for example, by the lead frame 16, by the self supporting electrodes, the bottom of the shell 18, or by a pedestal (not shown) mounted to the shell or to the lead frame.
• the structure of the illumination system includes a phosphor material 22 radiationally coupled to the LED chip 12. Radiationally coupled means that the elements are associated with each other so radiation from one is transmitted to the other.
• This phosphor material 22 is deposited on the LED 12 by any appropriate method.
• a water based suspension of the phosphor(s) can be formed, and applied as a phosphor layer to the LED surface.
• a silicone slurry in which the phosphor particles are randomly suspended is placed around the LED.
• the phosphor material 22 may be coated over or directly on the light emitting surface of the LED chip 12 by coating and drying the phosphor suspension over the LED chip 12.
• Both the shell 18 and the encapsulant 20 should be transparent to allow light 24 to be transmitted through those elements.
• the median particle size of the phosphor material may be from about 1 to about 10 microns.
• FIG. 2 illustrates a second preferred structure of the . system according to the preferred aspect of the present invention.
• the structure of the embodiment of FlG. 2 is similar to that of FIG. 1 , except that the phosphor material 122 is interspersed within the encapsulant material 120, instead of being formed directly on the LED chip 112.
• the phosphor material (in the form of a powder) may be interspersed within a single region of the encapsulant material 120 or, more preferably, throughout the entire volume of the encapsulant material.
• Radiation 126 emitted by the LED chip 112 mixes with the light emitted by the phosphor material 122, and the mixed light appears as white light 124.
• a phosphor powder may be added to a polymer precursor, loaded around the LED chip 112, and then the polymer . precursor may be cured to solidify the polymer material.
• Other known phosphor interspersion methods may also be used, such as transfer loading. 6 045181
• FIG. 3 illustrates a third preferred structure of the system according to the preferred aspects of the present invention.
• the structure of the embodiment shown in FIG. 3 is similar to that of FIG. 1, except that the phosphor material 222 is coated onto a surface of the shell 218, instead of being formed over the LED chip 212.
• the phosphor material is preferably coated on the inside surface of the shell 218, although the phosphor may be coated on the outside surface of the shell, if desired.
• the phosphor material 222 may be coated on the entire surface of the shell or only a top portion of the surface of the shell.
• the radiation 226 emitted by the LED chip 212 mixes with the light emitted by the phosphor material 222, and the mixed light appears as white light 224.
• the structures of FIGS. 1-3 may be combined and the phosphor may be located in any two or all three locations or in any other suitable location, such as separately from the shell or integrated into the LED.
• the lamp 10 may also include a plurality of scattering particles (not shown), which are embedded in the encapsulant material.
• the scattering particles may comprise, for example, AI 2 O 3 particles such as alumina powder or TiO 2 particles.
• the scattering particles effectively scatter the coherent light emitted from the LED chip, preferably with a negligible amount of absorption.
• the LED chip 412 may be mounted in a reflective cup 430.
• the cup 430 may be made from or coated with a reflective material, such as alumina, titania, or other dielectric powder known in the art.
• a preferred reflective material is AI 2 O 3 .
• the remainder of the structure of the embodiment of FIG. 4 is the same as that of any of the previous Figures, and includes two leads 416, a conducting wire 432 electrically connecting the LED chip 412 with the second lead, and an encapsulant material 420.
• the invention provides a novel phosphor composition, which may be used in the phosphor composition 22 in the above described LED light, wherein the composition is a phosphor composition having a formula Cai -a - b CeaEUbAli+ a Sii -a N3, where 0 ⁇ a ⁇ 0.2, 0 ⁇ b ⁇ 0.2.
• the phosphor comprises Cai- c - d Ce c Eu d Ali. c (Mg, Zn) 0 SiN 3, where 0 ⁇ c ⁇ 0.2, 0 ⁇ d ⁇ 0.2.
• the phosphor comprises Ca 1-2e - f Ce e (Li,Na) e EU f AISiN 3 , where O ⁇ e ⁇ O.2, 0 ⁇ f ⁇ 0.2, e+f>0.
• the phosphor comprises Cai -g-h- iCe g (Li J Na) h EUiAI 1+ g -h S! 1-g+h N 3 where 0 ⁇ g ⁇ 0.2, 0 ⁇ h ⁇ 0.4, 0 ⁇ i ⁇ 0.2, g+i>0.
• various phosphors are described herein in which different elements enclosed in parentheses and separated by commas, such as in the above Cai -c-d CecEudAli -c (Mg,Zn) c SiN 3 phosphor.
• this type of notation means that the phosphor can include any or all of those specified elements in the formulation in any ratio from 0 to 100%. That is, this type of notation, for the above phosphor for example, has the same meaning as qZn q ) c SiN 3 , wherein 0 ⁇ q ⁇ 1.
• Exemplary phosphors according to one or more of these embodiments include (Ca 0 .97Eu 0 .oiCeo.o2)(Alo.98Mgo.o2)SiN3,
• Figure 5 is the emission spectrum of (Cao. 97 Euo . oiCeo.o 2 )(Alo. 98 Mgo.o 2 )SiN 3 under 470 nm excitation.
• Figure 6 are the excitation and emission spectra of (Cao. 99 Ce 0 .oi)(Alo. 99 Mgo.oi)SiN 3 .
• the use of Ce 3+ as a dopant may increase the efficiency of the resulting lighting device when other phosphors are present.
• an LED lighting assembly including a phosphor composition comprising a blend of a phosphor from one of the above embodiments with one or more additional phosphors.
• These phosphors can be used either individually for single color lamps or in blends with other phosphors to generate white light for general illumination. These phosphors can be blended with suitable phosphors to produce a white light emitting device with CCTs ranging from 2500 to 10,000 K and CRIs ranging from 50- 99. Non-limiting examples of suitable phosphors for use with the present inventive phosphors in phosphor blends are listed below. [0049] The specific amounts of the individual phosphors used in the phosphor blend will depend upon the desired color temperature. The relative amounts of each phosphor in the phosphor blend can be described in terms of spectral weight. The spectral weight is the relative amount that each phosphor contributes to the overall emission spectrum of the device.
• the spectral weight amounts of all the individual phosphors and any residual bleed from the LED source should add up to 100%.
• the above described phosphor in the blend will have a spectral weight ranging from about 1 to 75%.
• suitable phosphors for use in the blend with the present phosphors include:
• a phosphor has two or more dopant ions (i.e. those ions following the colon in the above compositions), this is meant to mean that the phosphor has at least one (but not necessarily all) of those dopant ions within the material. That is, as understood by those skilled in the art, this type of notation means that the phosphor can include any or all of those specified ions as dopants in the formulation.
• the inventive phosphors can be used either alone to make single color light sources or in blends for white light sources.
• the phosphor composition is a blend of one or more of the above phosphors and one or more gap filling phosphors, such that the light emitted from the LED device is a white light.
• the ratio of each of the individual phosphors in the phosphor blend may vary depending on the characteristics of the desired light output.
• the relative proportions of the individual phosphors in the various embodiment phosphor blends may be adjusted such that when their emissions are blended and employed in an backlighting device, there is produced visible light of predetermined x and y values on the CIE chromaticity diagram.
• a white light is preferably produced. This white light may, for instance, may possess an x value in the range of about 0.30 to about 0.55, and a y value in the range of about 0.30 to about 0.55.
• the exact identity and amounts of each phosphor in the phosphor composition can be varied according to the needs of the end user.
• the above described phosphor composition may be produced using known solution or solid state reaction processes for the production of phosphors by combining, for example, elemental nitrides, oxides, carbonates and/or hydroxides as starting materials.
• Other starting materials may include nitrates, sulfates, acetates, citrates, or oxalates.
• coprecipitates of the rare earth 'oxides could be used as the starting materials for the RE elements.
• the starting materials are combined via a dry or wet blending process and fired in air or under a reducing atmosphere or in ammonia at from, e.g., 1000 to 1600 0 C.
• a fluxing agent may be added to the mixture before or during the step of mixing.
• This fluxing agent may be AIF 3 , NH 4 CI or any other conventional fluxing agent.
• a quantity of a fluxing agent of less than about 20, preferably less than about 10, percent by weight of the total weight of the mixture is generally adequate for fluxing purposes.
• the starting materials may be mixed together by any mechanical method including, but not limited to, stirring or blending in a high-speed blender or a ribbon blender.
• the starting materials may be combined and pulverized together in a bowl mill, a hammer mill, or a jet mill.
• the mixing may be carried out by wet milling especially when the mixture of the starting materials is to be made into a solution for subsequent precipitation. If the mixture is wet, it may be dried first before being fired under a reducing atmosphere at a temperature from about 900 0 C to about 1700 0 C 1 preferably from about 1100 0 C to about 160O 0 C, for a time sufficient to convert all of the mixture to the final composition.
• the firing may be conducted in a batchwise or continuous process, preferably with a stirring or mixing action to promote good gas-solid contact.
• the firing time depends on the quantity of the mixture to be fired, the rate of gas conducted through the firing equipment, and the quality of the gas-solid contact in the firing equipment. Typically, a firing time up to about 10 hours is adequate but for phase formation it is desirable to refire couple of times at the desired temperatures after grinding.
• the reducing atmosphere typically comprises a reducing gas such as hydrogen, carbon monoxide, ammonia or a combination thereof, optionally diluted with an inert gas, such as nitrogen, helium, etc., or a combination thereof.
• a typical firing atmosphere is 2% H 2 in nitrogen.
• the crucible containing the mixture may be packed in a second closed crucible containing high-purity carbon particles and fired in air so that the carbon particles react with the oxygen present in air, thereby, generating carbon monoxide for providing a reducing atmosphere.
• the phosphor layer 22 may also comprise from 0 up to about 5 % by weight (based on the total weight of the phosphors) of a pigment or other UV absorbent material capable of absorbing or reflecting UV radiation having a wavelength between 250 nm and 550 nm.
• Suitable pigments or filters include any of those known in the art that are capable of absorbing radiation generated between 250 nm and 550 nm.
• Such pigments include, for example, nickel titanate or praseodymium zirconate. The pigment is used in an amount effective to filter 10% to 100% of the radiation generated in any of the 250 nm to 550 nm range.
• Sample phosphors were made by mixing the following starting materials. A slight excess of Li 3 N (2% per mol of sample) was added to compensate for Li volatility at high temperatures. All samples were mixed using mortar and pestle and fired in uncovered Mo crucibles at 800 0 C for 2 hrs, then 1200 0 C for.3 hrs and finally at 1500 0 C for 5 hrs, all under 2% H 2 /N 2 atmosphere with a charcoal crucible in front of the sample.
• single phosphor lamps can be provided having CRi values greater than those achievable using YAG alone over a wide range of color temperatures.
• the use of the present oxynitride phosphors in LED blends can produce lamps with CRI values over 90, over the entire range of color temperatures of interest for general illumination (2500 K to 8000 K). In some blends, the CRI values may approach the theoretical maximum of 100.
• the phosphor composition described above may be used in additional applications besides LEDs.
• the material may be used as a phosphor in a Hg fluorescent lamp or fluorescent lamps based upon alternate discharges, in a cathode ray tube, in a plasma display device or in a. liquid crystal display (LCD).
• the material may also be used as a scintillator in an electromagnetic calorimeter, in a gamma ray camera, in a computed tomography scanner, as scintillator detector elements in a CT or PET system, or in a laser. ' These uses are meant to be merely • exemplary and not exhaustive.

Landscapes

• Chemical & Material Sciences (AREA)
• Inorganic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• Luminescent Compositions (AREA)

Priority Applications (2)

Applications Claiming Priority (2)

Publications (2)

Family

ID=38052620

Family Applications (1)

Country Status (4)

Cited By (6)

Families Citing this family (64)

Family Cites Families (31)

• 2005
  • 2005-11-22 US US11/285,024 patent/US7262439B2/en not_active Expired - Lifetime
• 2006
  • 2006-11-22 WO PCT/US2006/045181 patent/WO2007120216A2/en not_active Ceased
  • 2006-11-22 JP JP2008542432A patent/JP5503871B2/ja not_active Expired - Fee Related
  • 2006-11-22 DE DE112006003161.9T patent/DE112006003161B4/de active Active

Also Published As

Similar Documents

Legal Events