WO2007111138A1 - 光学用粘着剤、粘着剤付き光学フィルムおよび画像表示装置 - Google Patents

光学用粘着剤、粘着剤付き光学フィルムおよび画像表示装置 Download PDF

Info

Publication number
WO2007111138A1
WO2007111138A1 PCT/JP2007/055112 JP2007055112W WO2007111138A1 WO 2007111138 A1 WO2007111138 A1 WO 2007111138A1 JP 2007055112 W JP2007055112 W JP 2007055112W WO 2007111138 A1 WO2007111138 A1 WO 2007111138A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
meth
optical
sensitive adhesive
adhesive
Prior art date
Application number
PCT/JP2007/055112
Other languages
English (en)
French (fr)
Inventor
Shinichi Inoue
Masayuki Satake
Kohei Yano
Original Assignee
Nitto Denko Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corporation filed Critical Nitto Denko Corporation
Priority to US12/293,936 priority Critical patent/US9321942B2/en
Publication of WO2007111138A1 publication Critical patent/WO2007111138A1/ja

Abstract

　粘着剤付き光学フィルム等に用いられる、アクリル系共重合体からなる光学用粘着剤であって、表示画面の周辺部分に表示ムラが生じにくい光学用粘着剤を提供すること。アルキル（メタ）アクリレート（ａ１）およびＮ‐（２‐ヒドロキシエチル）（メタ）アクリルアミド（ａ２）を、モノマー単位として含有するアクリル系共重合体を含有することを特徴とする光学用粘着剤。

Description

明 細 書
光学用粘着剤、粘着剤付き光学フィルムおよび画像表示装置
技術分野
[0001] 本発明は、光学用粘着剤およびこれを用いた粘着剤付き光学フィルムに関する。
当該光学用粘着剤、粘着剤付き光学フィルムは、液晶表示装置、有機 EL表示装置 、 PDP等の画像表示装置に好適に用いられる。前記光学フィルムとしては、偏光板、 位相差板、光学補償フィルム、輝度向上フィルム、さらにはこれらが積層されているも のなどがあげられる。
背景技術
[0002] 液晶表示装置は、その画像形成方式から液晶セルの両側に偏光素子を配置する ことが必要不可欠であり、一般的には偏光板が貼着されている。また液晶パネルに は偏光板の他に、ディスプレイの表示品位を向上させるために様々な光学素子が用 いられるようになってきている。例えば、着色防止としての位相差板、液晶ディスプレ ィの視野角を改善するための視野角拡大フィルム、さらにはディスプレイのコントラス トを高めるための輝度向上フィルム等が用いられる。これらのフィルムは総称して光学 フィルムと呼ばれる。
[0003] 前記光学フィルムを液晶セルに貼着する際には、通常、粘着剤が使用される。また 、光学フィルムと液晶セル、または光学フィルム間の接着は、通常、光の損失を低減 するため、それぞれの材料は粘着剤を用いて密着されている。このような場合に、光 学フィルムを固着させるのに乾燥工程を必要としな 、こと等のメリットを有することから
、粘着剤は、光学フィルムの片側に予め粘着剤層として設けられた粘着剤付き光学 フィルムが一般的に用いられる。
[0004] 上記粘着剤付き光学フィルムに用いる粘着剤としては、その優れた接着性、透明性 等のためにアクリル系ポリマーをベースポリマーとするアクリル系粘着剤が多用されて いる。また、アクリル系粘着剤の架橋方法は、イソシァネート系架橋剤を用いたものが 多ぐ主としてアクリル系ポリマーに共重合した官能性モノマーとの結合を利用したも のである。 [0005] 前記光学フィルムを液晶セルに貼り合わせた液晶パネルは、液晶表示装置に搭載 されて用いられる。液晶表示装置は、電卓にはじまり、時計やテレビ、モニターなどに 利用されている。液晶表示装置は、加熱や加湿条件下等の様々な条件下におかれ るため、かかる環境下においても、表示品位を損なわない高耐久性が要求されてい る。
[0006] しかし、液晶表示装置を、加熱や加湿条件下にお!/、た場合には、液晶パネルの周 辺部に表示ムラが生じ、表示不良が起きることがある。この周辺部の表示ムラは、特 に、偏光板に視野角拡大フィルムを積層した光学フィルムを使用した場合に顕著に みられることがあった。
[0007] 前記周辺部の表示ムラを改善するために、粘着剤付き光学フィルムに用いる粘着 剤として、可塑剤やオリゴマー成分を含有する粘着剤組成物を用いることが提案され ている (特許文献 1、特許文献 2参照)。しかし、これらの粘着剤組成物は、長時間の 加熱試験において、可塑剤やオリゴマー成分等の添加剤自体が析出して外観不良 や粘着剤が劣化する問題があった。
特許文献 1 :特開平 9 87593号公報
特許文献 2：特開平 10— 279907号公報
発明の開示
発明が解決しょうとする課題
[0008] 本発明は、粘着剤付き光学フィルム等に用いられる、アクリル系共重合体からなる 光学用粘着剤であって、表示画面の周辺部分に表示ムラが生じにく!、光学用粘着 剤を提供することを目的とする。
[0009] また本発明は、前記光学用粘着剤を用いた粘着剤付き光学フィルムを提供するこ とを目的とする。さら〖こは、前記粘着剤付き光学フィルムを用いた画像表示装置を提 供することを目的とする。
課題を解決するための手段
[0010] 本発明者らは前記課題を解決すべく鋭意検討を重ねた結果、下記光学用粘着剤 等を見出し、本発明を完成するに至った。
[0011] すなわち本発明は、アルキル (メタ）アタリレート（al)および N- (2-ヒドロキシェチル ) (メタ)アクリルアミド (a2)を、モノマー単位として含有するアクリル系共重合体、なら びに架橋剤を含有することを特徴とする光学用粘着剤、に関する。
[0012] 前記光学用粘着剤において、 N- (2-ヒドロキシェチル）（メタ）アクリルアミド (a2)の 割合は、アルキル (メタ）アタリレート（al) 100重量部に対して、 0. 01〜： LOO重量部 であることが好ましい。
[0013] 前記光学用粘着剤において、モノマー単位として、さらに、前記 (al)および (a2)を 除ぐモノマー（a3)を、アルキル (メタ）アタリレート（al) 100重量部に対して、 50重量 部以下含有することができる。
[0014] 前記光学用粘着剤にぉ 、て、モノマー（a3)は、カルボキシル基を含有するモノマ 一であることが好ましい。また、モノマー（a3)は、窒素含有ビュルモノマーが好ましい
[0015] また本発明は、光学フィルムの少なくとも一方の面に粘着剤層が積層されている粘 着剤付き光学フィルムであって、
前記粘着剤層は、前記光学用粘着剤により形成されていることを特徴とする粘着剤 付き光学フィルム、に関する。
[0016] 前記粘着剤付き光学フィルムにお 、て、光学フィルムとしては、例えば、偏光板お よび Zまたは位相差板があげられる。
[0017] また本発明は、前記粘着剤付き光学フィルムが用いられて!/ヽることを特徴とする画 像表示装置、に関する。
発明の効果
[0018] 上記本発明は、光学用粘着剤のベースポリマーに用いるアクリル系共重合体の共 重合成分として、主成分である、アルキル (メタ）アタリレート（al)にカ卩えて、 N- (2-ヒ ドロキシェチル）（メタ）アクリルアミド（a2)を用いている。かかる、 N- (2-ヒドロキシェ チル）（メタ)アクリルアミド (a2)の作用により、前記光学用粘着剤を、粘着剤付き光学 フィルムに適用した場合に、表示画面の周辺部分の表示ムラを抑えることができる。 また、本発明の光学用粘着剤は、ベースポリマーのモノマー単位として、前記 (a2) 成分を用いることにより、表示ムラを抑えているため、ベースポリマーに加えて、可塑 剤等の添加剤を用いた粘着剤のように、添加剤自体が析出して外観不良や粘着剤 が劣化することはない。特に、本発明の光学用粘着剤は、粘着剤付き光学フィルム の光学フィルムとして、偏光板に視野角拡大フィルムを積層したものを用いた場合に おける、表示ムラを抑えるうえで好適である。
発明を実施するための最良の形態
[0019] 本発明の光学用粘着剤は、ベースポリマーとして、アルキル (メタ)アタリレート（al) および N- (2-ヒドロキシェチル）（メタ）アクリルアミド（a2)を、モノマー単位として含有 するアクリル系共重合体を含有する。なお、（メタ)アタリレートはアタリレートおよび Z またはメタタリレートをいい、本発明の (メタ）とは同様の意味であり、（メタ）アクリルアミ ドは、アクリルアミドおよび/またはメタクリルアミドを示す。
[0020] アクリル系共重合体は、アルキル (メタ）アタリレート（al)の単位を主成分とする。ァ ルキル (メタ）アタリレート（al)のアルキル基の炭素数は 1〜18程度、好ましくは炭素 数 1〜9であり、アルキル基は直鎖、分岐鎖のいずれでもよい。アルキル (メタ）アタリ レートの具体例としては、例えば、メチル (メタ)アタリレート、ェチル (メタ)アタリレート 、プロピル (メタ）アタリレート、イソプロピル (メタ）アタリレート、 n—ブチル (メタ）アタリレ ート、イソブチル (メタ）アタリレート、ペンチル (メタ）アタリレート、へキシル (メタ）アタリ レート、 2—ェチルへキシル (メタ）アタリレート、 n—ォクチル (メタ）アタリレート、イソォ クチル (メタ)アタリレート、デシル (メタ)アタリレート、ドデシル (メタ)アタリレート、ラウリ ル (メタ）アタリレート、ステアリル (メタ）アタリレート、シクロへキシル (メタ）アタリレート、 などを挙げることができる。これらは単独でまたは組み合わせて使用することができる 。これらアルキル基の平均炭素数は 4〜 12であるのが好ましい。
[0021] アクリル系共重合体における、 N- (2-ヒドロキシェチル）（メタ）アクリルアミド（a2)の 割合は、アルキル (メタ）アタリレート（al) 100重量部に対して 0. 01〜： LOO重量部の 範囲で用いることが好ましい。前記 (a2)成分が、 0. 01重量部未満の場合には、ヒド ロキシ基が、架橋剤との架橋反応点して有効に機能せず、本発明の粘着剤により形 成される粘着剤層が架橋不足になるおそれがある。一方、前記 (a2)成分が、 100重 量部を超える場合には、アクリル系共重合体のガラス転移温度 (Tg)が上昇し、粘着 剤として必要な柔軟性が損なわれるおそれがあり好ましくない。かかる観点から、前 記 (a2)成分の割合は、前記 (al)成分 100重量部に対して、 0. 05〜30重量部、さ らに 0. 07〜5重量部用いることが好ましい。
[0022] また、アクリル系共重合体は、モノマー単位として、さらに、前記 (al)成分および (a 2)成分を除ぐモノマー (a3)成分を、含有することができる。
[0023] 前記 (a3)成分としては、例えば、 2 ヒドロキシェチル (メタ)アタリレート、 2 ヒドロ キシプロピル (メタ）アタリレート、 4—ヒドロキシブチル (メタ）アタリレート、 6—ヒドロキシ へキシル (メタ）アタリレート、 8 ヒドロキシォクチル (メタ）アタリレート、 10 ヒドロキシ デシル (メタ）アタリレート、 12 ヒドロキシラウリル (メタ）アタリレートや（4 ヒドロキシメ チルシクロへキシル) メチルアタリレートなどの前記（a2)成分以外のヒドロキシル基 含有モノマー； (メタ)アクリル酸、カルボキシェチル (メタ)アタリレート、カルボキシペン チル (メタ)アタリレート、ィタコン酸、マレイン酸、フマール酸、クロトン酸などのカルボ キシル基含有モノマー；無水マレイン酸、無水ィタコン酸などの酸無水物基含有モノ マー；アクリル酸の力プロラタトン付カ卩物；スチレンスルホン酸ゃァリルスルホン酸、 2 - (メタ）アクリルアミドー 2—メチルプロパンスルホン酸、（メタ）アクリルアミドプロパン スルホン酸、スルホプロピル (メタ）アタリレート、（メタ）アタリロイルォキシナフタレンス ルホン酸などのスルホン酸基含有モノマー； 2—ヒドロキシェチルアタリロイルホスフエ ートなどの燐酸基含有モノマーなどがあげられる。
[0024] また、前記 (a3)成分としては、前記 (a2)成分以外の窒素含有ビュルモノマーがあ げられる。例えば、マレイミド、 N シクロへキシノレマレイミド、 N フエ-ノレマレイミド； N—アタリロイルモルホリン；（メタ）アクリルアミド、 N, N ジメチル (メタ）アクリルアミド 、 N, N ジェチル (メタ）アクリルアミド、 N へキシル (メタ）アクリルアミド、 N—メチル (メタ）アクリルアミド、 N ブチル (メタ）アクリルアミド、 N ブチル (メタ）アクリルアミド や N—メチロール (メタ）アクリルアミド、 N—メチロールプロパン (メタ）アクリルアミドな どの（N 置換)アミド系モノマー；アミノエチル (メタ）アタリレート、ァミノプロピル (メタ )アタリレート、 N, N ジメチルアミノエチル (メタ）アタリレート、 t ブチルアミノエチル (メタ）アタリレート、 3— (3—ピリ-ジル）プロピル (メタ）アタリレートなどのアルキルアミ ノアルキル (メタ）アタリレート系モノマー；メトキシェチル (メタ）アタリレート、エトキシェ チル (メタ）アタリレートなどのアルコキシアルキル (メタ）アタリレート系モノマー； N— ( メタ）アタリロイルォキシメチレンスクシンイミドゃ N— (メタ）アタリロイル一 6—ォキシへ キサメチレンスクシンイミド、 N— (メタ）アタリロイルー 8—ォキシオタタメチレンスクシン イミド、 N—アタリロイルモルホリンなどのスクシンイミド系モノマーなども改質目的のモ ノマ一例としてあげられる。
[0025] さらに、前記（a3)成分としては、酢酸ビニル、プロピオン酸ビュル、 N—ビニルピロ リドン、メチルビニルピロリドン、ビニルピリジン、ビニルピペリドン、ビニルピリミジン、ビ -ルピペラジン、ビュルピラジン、ビュルピロール、ビュルイミダゾール、ビュルォキサ ゾール、ビュルモルホリン、 N—ビ-ルカルボン酸アミド類、スチレン、 α—メチルスチ レン、 Ν—ビ-ルカプロラタタムなどのビュル系モノマー；アクリロニトリル、メタタリロニ トリルなどの-トリル系モノマー；グリシジル (メタ）アタリレートなどのエポキシ基含有ァ クリル系モノマー；ポリエチレングリコール（メタ）アタリレート、ポリプロピレングリコール (メタ）アタリレート、メトキシエチレングリコール (メタ）アタリレート、メトキシポリプロピレ ングリコール (メタ）アタリレートなどのグリコール系アクリルエステルモノマー；テトラヒド 口フルフリル (メタ）アタリレート、フッ素 (メタ）アタリレート、シリコーン (メタ）アタリレート 、 2—メトキシェチルアタリレート、ベンジル (メタ）アタリレート、フエノキシェチル (メタ） アタリレート、などの（メタ）アタリレート系モノマーなども使用することができる。
[0026] 前記 (a3)成分は、ベースポリマーを改質するために、任意に用いることができる。
前記 (a3)成分は、 1種または 2種以上を用いることができる。前記 (a3)成分の割合 は、アルキル (メタ)アタリレート (al) 100重量部に対して、 50重量部以下、さらには 3 0重量部以下、さらには 20重量部以下とするのが好ましい。前記 (a3)成分の割合が 、 50重量部を超えると粘着剤としての柔軟性を損なうおそれがある点で好ましくな ヽ
[0027] 前記 (a3)成分としては、接着性が良好である点から、カルボキシル基を含有するモ ノマー、特にアクリル酸の使用が好適に用いられる。カルボキシル基を含有するモノ マーを用いる場合、その割合は、アルキル (メタ)アタリレート（al) 100重量部に対し て、 0. 1〜： LO重量部程度、好ましく 0. 5〜8重量部、さらに好ましくは 1〜6重量部で ある。
[0028] 前記 (a3)成分としては、表示画面の周辺部分の表示ムラを抑える点から、窒素含 有ビュルモノマー、特に、 N—アタリロイルモルホリンや、 N, N—ジメチル (メタ）アタリ ルアミド等の (N—置換)アミド系モノマーが好適に用いられる。窒素含有ビュルモノ マーを用いる場合、その割合は、アルキル (メタ)アタリレート（al) 100重量部に対し て、 0. 1〜： L0重量部程度、好ましく 0. 5〜8重量部、さらに好ましくは 1〜6重量部で ある。窒素含有ビュルモノマーは、カルボキシル基を含有するモノマーと併用し、好 適に用いられる。
[0029] アクリル系共重合体の平均分子量は特に制限されないが、重量平均分子量は、 50 万〜 250万程度であるのが好ましい。前記アクリル系共重合体の製造は、各種公知 の手法により製造でき、たとえば、バルタ重合法、溶液重合法、懸濁重合法等のラジ カル重合法を適宜選択できる。ラジカル重合開始剤としては、ァゾ系、過酸化物系の 各種公知のものを使用できる。反応温度は通常 50〜80°C程度、反応時間は 1〜8 時間とされる。また、前記製造法の中でも溶液重合法が好ましぐアクリル系共重合 体の溶媒としては一般に酢酸ェチル、トルエン等が用いられる。溶液濃度は通常 20 〜80重量％程度とされる。またアクリル系共重合体は、水系のェマルジヨンとして得 ることがでさる。
[0030] また本発明の光学用粘着剤は、ベースポリマーである前記アクリル系共重合体に 加えて、架橋剤を含有する。架橋剤により、光学フィルムとの密着性や耐久性を向上 でき、また高温での信頼性や粘着剤自体の形状の保持を図ることができる。架橋剤と しては、イソシァネート系、エポキシ系、過酸化物系、金属キレート系、ォキサゾリン系 などを適宜に使用可能である。これら架橋剤は 1種を、または 2種以上を組み合わせ て用いることができる。架橋剤としては、ヒドロキシル基と反応性を示す官能基を含有 する架橋剤が好適であり、特に、イソシァネート系架橋剤が好適である。
[0031] イソシァネート系架橋剤は、イソシァネートイ匕合物が用いられる。イソシァネートイ匕合 物としては、トリレンジイソシァネート、クロルフエ-レンジイソシアナート、へキサメチレ ンジイソシアナート、テトラメチレンジイソシアナート、イソホロンジイソシァネート、キシ リレンジイソシァネート、ジフエ-ルメタンジイソシァネート、水添されたジフエ-ルメタ ンジイソシァネートなどのイソシァネートモノマー及びこれらイソシァネートモノマーを トリメチロールプロパンなどと付カ卩したァダクト系イソシァネートイ匕合物；イソシァヌレー ト化物、ビュレット型化合物、さらには公知のポリエーテルポリオールやポリエステル ポリオール、アクリルポリオール、ポリブタジエンポリオール、ポリイソプレンポリオール などを付加反応させたウレタンプレボリマー型のイソシァネートなどが挙げられる。
[0032] エポキシ系架橋剤としては、例えば、ビスフエノール Aェピクロルヒドリン型のェポキ シ榭脂があげられる。また、エポキシ系架橋剤としては、例えば、エチレングリコール ジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、グリセリンジグ リシジルエーテル、グリセリントリグリシジルエーテル、 1, 6 へキサンジオールジグリ シジルエーテル、トリメチロールプロパントリグリシジルエーテル、ジグリシジルァ二リン 、 N, N, Ν' , Ν， 一テトラグリシジノレー m キシリレンジァミン、 1, 3 ビス（N, N ジ グリシジルアミノメチル）シクロへキサン、 N, N, Ν' , Ν， 一テトラグリシジルァミノフエ ニルメタン、トリグリシジノレイソシァヌレート、 m— Ν, N ジグリシジノレアミノフエニノレグ リシジルエーテル、 N, N ジグリシジルトルイジン、及び N, N ジグリシジルァ二リン などが挙げられる。
[0033] 過酸ィ匕物系架橋剤としては、各種過酸ィ匕物が用いられる。過酸ィ匕物としては、ジ（2 -ェチルへキシル）パーォキシジカーボネート、ジ（4-t-ブチルシクロへキシル）パー ォキシジカーボネート、ジ -sec-ブチルパーォキシジカーボネート、 t ブチルパーォ キシネオデカノエート、 t-へキシルバーォキシピバレート、 t-ブチノレパーォキシピバレ ート、ジラウロイルパーォキシド、ジ -n-オタタノィルパーォキシド、 1, 1, 3, 3-テトラメ チルブチルパーォキシイソブチレート、 1, 1, 3, 3-テトラメチルブチルパーォキシ 2- ェチルへキサノエート、ジ（4-メチルベンゾィル）パーォキシド、ジベンゾィルバーオ キシド、 t-ブチルパーォキシイソブチレート、などが挙げられる。これらのなかでも、特 に架橋反応効率に優れる、ジ（4十ブチルシクロへキシル)パーォキシジカルボネー ト、ジラウロイルパーォキシド、ジベンゾィルパーォキシドが好ましく用いられる。
[0034] 架橋剤の使用量は、アクリル系共重合体 (A) 100重量部に対して、 10重量部以下 、好ましくは 0. 01〜5重量部、さらに好ましくは 0. 02〜3重量部である。架橋剤の使 用割合が、 10重量部を超えると架橋が進みすぎて接着性が低下するおそれがある 点で好ましくない。
[0035] さら〖こは、本発明の光学用粘着剤には、必要に応じて、粘着付与剤、可塑剤、ガラ ス繊維、ガラスビーズ、金属粉、その他の無機粉末等力もなる充填剤、顔料、着色剤 、充填剤、酸化防止剤、紫外線吸収剤、シランカップリング剤等を、また本発明の目 的を逸脱しな 、範囲で各種の添加剤を適宜に使用することもできる。また微粒子を含 有して光拡散性を示す粘着剤層などとしても良い。
[0036] 本発明の粘着剤付き光学フィルムは、光学フィルムの少なくとも一方の面に、前記 光学用粘着剤により、粘着剤層を形成したものである。なお、前記粘着剤層は光学フ イルムの片面を設けて 、てもよく、光学フィルムの両面に有して 、てもよ 、。
[0037] 粘着剤層の形成法は、特に制限されず、前記光学フィルム上に粘着剤溶液を流延 方式や塗工方式等の適宜な展開方式で塗布し乾燥する方法、粘着剤層を設けた離 型シートにより転写する方法等があげられる。塗布法は、リバースコーティング、ダラ ビアコーティング等のロールコーティング法、スピンコーティング法、スクリーンコーテ イング法、フアウンテンコーティング法、デイツビング法、スプレー法などを採用できる。 粘着剤溶液を塗布後、乾燥工程で溶剤や水を揮発することで所定の厚みの粘着剤 層を得る。
[0038] 粘着剤層の厚さは、使用目的や接着力などに応じて適宜に決定でき、一般的には 、 1〜500 μ mであり、好ましくは 1〜50 μ mである。さらには 1〜40 μ mが好ましく、 さらいは 5〜30 /ζ πιが好ましぐ特に 10〜25 /ζ πι力 S好ましい。 1 mより薄いと耐久 性が悪くなり、厚くなると発泡などによる浮きや剥がれが生じやすく外観不良となりや すい。粘着剤層は、異なる組成又は種類等のものの重量層として偏光板や光学フィ ルムの片面又は両面に設けることもできる。また両面に設ける場合に、偏光板や光学 フィルムの表裏において異なる組成や種類や厚さの粘着層とすることもできる。
[0039] また、粘着剤層の形成は、 UV硬化性の粘着剤シロップを離型フィルム上に塗布し 、電子線や UV等の放射線を照射することで前記アクリル系共重合体を含有する粘 着剤層を形成できる。この際、粘着剤には、架橋剤を含有させていることから、高温 での信頼性や粘着剤自体の形状の保持を図ることができる。
[0040] なお、粘着剤層の架橋は、前記乾燥工程や UV照射工程で行うことができる他、乾 燥後に、加温状態や室温放置によるエージングにより、架橋が促進するような架橋形 態ち選択でさる。
[0041] 離型シートの構成材料としては、紙、ポリエチレン、ポリプロピレン、ポリエチレンテレ フタレート等の合成樹脂フィルム、ゴムシート、紙、布、不織布、ネット、発泡シートや 金属箔、それらのラミネート体等の適宜な薄葉体等があげられる。離型シートの表面 には、粘着剤層力ゝらの剥離性を高めるため、必要に応じてシリコーン処理、長鎖アル キル処理、フッ素処理などの低接着性の剥離処理が施されて!/、ても良!、。
[0042] 粘着剤層等の形成にあたり、層間密着性を向上させるために、光学フィルムには活 性ィ匕処理を施すことができる。活性ィ匕処理は各種方法を採用でき、コロナ放電処理、 プラズマ放電処理、グロ一放電処理、低圧 UV処理等の表面処理や、ケン化処理を 施すことができ、またカップリング剤等をアンカー層として形成することが可能である。
[0043] なお、本発明の粘着剤付き光学フィルムの光学フィルムや粘着剤層などの各層に は、例えば、サリチル酸エステル系化合物やべンゾフエノール系化合物、ベンゾトリア ゾール系化合物ゃシァノアクリレート系化合物、ニッケル錯塩系化合物等の紫外線 吸収剤で処理する方式などの方式により紫外線吸収能をもたせたものなどであって ちょい。
[0044] 光学フィルムと前記粘着剤層との間には前記以外のアンカーコ一ト層を有して!/ヽて もよい。本発明の粘着剤付き光学フィルムの粘着剤層と光学フィルムとの間の設けら れるアンカーコート層を形成する材料は特に限定されないが、粘着剤層と光学フィル ムのいずれにも良好な密着性を示し、凝集力に優れる皮膜を形成するものが望まし い。このような性質を示すものには、各種ポリマー類、金属酸化物のゾル、シリカゾル 等を使用できる。これらのなかでも特にポリマー類が好ましく用いられる。
[0045] 前記ポリマー類としては、ポリウレタン系榭脂、ポリエステル系榭脂、分子中にアミノ 基を含むポリマー類があげられる。ポリマー類の使用形態は溶剤可溶型、水分散型 、水溶解型のいずれでもよい。例えば、水溶性ポリウレタン、水溶性ポリエステル、水 溶性ポリアミド等や水分散性榭脂（エチレン—酢酸ビュル系ェマルジヨン、（メタ）ァク リル系ェマルジヨンなど）が挙げられる。また、水分散型は、ポリウレタン、ポリエステル 、ポリアミド等の各種の榭脂を乳化剤を用いてェマルジヨン化したものや、前記榭脂 中に、水分散性親水基のァ-オン基、カチオン基またはノ-オン基を導入して自己 乳化物としたもの等を用いることができる。またイオン高分子錯体を用いることができ る。 [0046] 力かるポリマー類は粘着剤層中のイソシァネート系化合物と反応性を有する官能基 を有するものが好ましい。前記ポリマー類としては、分子中にアミノ基を含むポリマー 類が好ましい。特に、末端に 1級アミノ基を有するものが好ましく用いられ、イソシァネ ート系化合物との反応により強固に密着することが確認されている。
[0047] 分子中にアミノ基を含むポリマー類としては、ポリエチレンィミン、ポリアリルァミン、 ポリビニルァミン、ポリビニルピリジン、ポリビニルピロリジン、ジメチルアミノエチルァク リレート等の含ァミノ基含有モノマーの重合体などをあげることができる。これらのなか でもポリエチレンィミンが好まし 、。
[0048] またアンカーコート層の形成にあたっては、アミノ基を含むポリマー類にカ卩えて、アミ ノ基を含むポリマー類と反応する化合物を混合して架橋して、アンカーコート層の強 度を向上させることができる。アミノ基を含むポリマー類と反応する化合物としては、ェ ポキシィ匕合物等を例示できる。
[0049] アンカーコート層を設ける場合には、前記光学フィルム上にアンカーコート層を形 成した後に、粘着剤層を形成する。たとえば、ポリエチレンイミン水溶液の如きアンカ 一成分の溶液を、コーティング法、デイツビング法、スプレー法などの塗工法を用いて 、塗布、乾燥し、アンカーコート層を形成させる。アンカーコート層の厚みとしては 10 〜5000nm程度、さらには 50〜500nmの範囲にあることが好ましい。アンカーコート 層の厚みが薄くなると、バルタとしての性質を有さず、十分な強度を示さなくなり、十 分な密着性が得られない場合がある。また、厚すぎると光学特性の低下を招くおそれ がある。
[0050] 粘着剤付き光学フィルムには、帯電防止性を付与するために、帯電防止剤を用い ることもできる。帯電防止剤は、各層に含有させることができ、また、別途、帯電防止 層を形成することができる。帯電防止剤としては、イオン性界面活性剤系；ポリア-リ ン、ポリチォフェン、ポリピロール、ポリキノキサリン等の導電ポリマー系；酸化スズ、酸 ィ匕アンチモン、酸化インジウム等の金属酸ィ匕物系などが挙げられるが、特に光学特 性、外観、帯電防止効果、および帯電防止効果の熱時、加湿時での安定性という観 点から、導電性ポリマー系が好ましく使用される。この中でも、ポリア-リン、ポリチォ フェンなどの水溶性導電性ポリマー、もしくは水分散性導電性ポリマーが特に好まし く使用される。これは、帯電防止層の形成材料として水溶性導電性ポリマーや水分 散性導電性ポリマーを用いた場合、塗布工程に際して有機溶剤による光学フィルム 基材の変質を抑える点で好まし 、。
[0051] 本発明の粘着剤付き光学フィルムに使用される光学フィルムとしては、液晶表示装 置等の画像表示装置の形成に用いられるものが使用され、その種類は特に制限され ない。たとえば、光学フィルムとしては偏光板があげられる。偏光板は偏光子の片面 または両面には透明保護フィルムを有するものが一般に用いられる。
[0052] 偏光子は、特に限定されず、各種のものを使用できる。偏光子としては、たとえば、 ポリビュルアルコール系フィルム、部分ホルマール化ポリビュルアルコール系フィル ム、エチレン ·酢酸ビュル共重合体系部分ケンィ匕フィルム等の親水性高分子フィルム に、ヨウ素や二色性染料の二色性物質を吸着させて一軸延伸したもの、ポリビニルァ ルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリェン系配向フィルム 等があげられる。これらの中でも、ポリビュルアルコール系フィルムとヨウ素などの二 色性物質力もなる偏光子が好適である。これらの偏光子の厚さは特に制限されない 力 一般的に 5〜80 μ m程度である。
[0053] ポリビニルアルコール系フィルムをヨウ素で染色し一軸延伸した偏光子は、たとえば 、ポリビニルアルコールをヨウ素の水溶液に浸漬することによって染色し、元長の 3〜 7倍に延伸することで作成することができる。必要に応じてホウ酸や硫酸亜鉛、塩ィ匕 亜鉛等を含んでいても良いヨウ化カリウムなどの水溶液に浸漬することもできる。さら に必要に応じて染色前にポリビニルアルコール系フィルムを水に浸漬して水洗しても よ 、。ポリビュルアルコール系フィルムを水洗することでポリビュルアルコール系フィ ルム表面の汚れやブロッキング防止剤を洗浄することができるほ力に、ポリビニルァ ルコール系フィルムを膨潤させることで染色のムラなどの不均一を防止する効果もあ る。延伸はヨウ素で染色した後に行っても良いし、染色しながら延伸しても良いし、ま た延伸して力 ヨウ素で染色しても良い。ホウ酸やヨウ化カリウムなどの水溶液や水浴 中でも延伸することができる。
[0054] 前記偏光子の片面または両面に設けられる透明保護フィルムを形成する材料とし ては、透明性、機械的強度、熱安定性、水分遮断性、等方性などに優れるものが好 ましい。例えば、ポリエチレンテレフタレートやポリエチレンナフタレート等のポリエス テノレ系ポリマー、ジァセチノレセノレロースやトリァセチノレセノレロース等のセノレロース系 ポリマー、ポリメチルメタタリレート等のアクリル系ポリマー、ポリスチレンやアタリ口-トリ ル 'スチレン共重合体 (AS榭脂）等のスチレン系ポリマー、ポリカーボネート系ポリマ 一などがあげられる。また、ポリエチレン、ポリプロピレン、シクロ系ないしはノルボルネ ン構造を有するポリオレフイン、エチレン ·プロピレン共重合体の如きポリオレフイン系 ポリマー、塩ィ匕ビュル系ポリマー、ナイロンや芳香族ポリアミド等のアミド系ポリマー、 イミド系ポリマー、スノレホン系ポリマー、ポリエーテノレスノレホン系ポリマー、ポリエーテ ノレエーテノレケトン系ポリマー、ポリフエ二レンスルフイド系ポリマー、ビニルアルコール 系ポリマー、塩化ビニリデン系ポリマー、ビニルブチラール系ポリマー、ァリレート系ポ リマー、ポリオキシメチレン系ポリマー、エポキシ系ポリマー、または前記ポリマーのブ レンド物なども前記透明保護フィルムを形成するポリマーの例としてあげられる。透明 保護フィルムは、アクリル系、ウレタン系、アクリルウレタン系、エポキシ系、シリコーン 系等の熱硬化型、紫外線硬化型の樹脂の硬化層として形成することもできる。
[0055] また、特開 2001— 343529号公報（WO01Z37007)に記載のポリマーフィルム、 たとえば、（A)側鎖に置換および Zまたは非置^ミド基を有する熱可塑性榭脂と、 (B)側鎖に置換および Zまたは非置換フ -ルならびに-トリル基を有する熱可塑 性榭脂を含有する榭脂組成物があげられる。具体例としてはイソブチレンと N—メチ ルマレイミドからなる交互共重合体とアクリロニトリル 'スチレン共重合体とを含有する 榭脂組成物のフィルムがあげられる。フィルムは榭脂組成物の混合押出品など力ゝらな るフィルムを用いることができる。
[0056] 保護フィルムの厚さは、適宜に決定しうるが、一般には強度や取扱性等の作業性、 薄膜性などの点より 1〜500 m程度である。特に、 5〜200 mが好ましい。
[0057] また、保護フィルムは、できるだけ色付きがな！、ことが好まし！/、。従って、 Rth= (nx
-nz) *d (ただし、 nxはフィルム平面内の遅相軸方向の屈折率、 nzはフィルム厚方 向の屈折率、 dはフィルム厚みである）で表されるフィルム厚み方向の位相差が 90 nm〜 + 75nmである保護フィルムが好ましく用いられる。力かる厚み方向の位相差 値 (Rth)が 90nm〜 + 75nmのものを使用することにより、保護フィルムに起因す る偏光板の着色 (光学的な着色）はほぼ解消することができる。厚み方向位相差 (Rt h)は、さらに好ましくは一 80nm〜 + 60nm、特に一 70nm〜+45nmが好ましい。
[0058] 保護フィルムとしては、偏光特性や耐久性などの点より、トリァセチルセルロース等 のセルロース系ポリマーが好まし 、。特にトリァセチルセルロースフィルムが好適であ る。また偏光子の寸法変化による応力を受けた場合にも位相差が生じにくい熱可塑 性飽和ノルボルネン系榭脂を使用することもできる。熱可塑性飽和ノルボルネン系榭 脂は、シクロォレフィンを主骨格となり、炭素 炭素二重結合を実質的に有しないも のである。熱可塑性飽和ノルボルネン系榭脂としては、日本ゼオン (株)製のゼォネッ ダス、ゼォノア、 JSR (株)製のアートン等があげられる。
[0059] なお、偏光子の両側に保護フィルムを設ける場合、その表裏で同じポリマー材料か らなる保護フィルムを用いても良ぐ異なるポリマー材料等力もなる保護フィルムを用 いても良い。
[0060] 前記偏光子と保護フィルムとは通常、水系接着剤等を介して密着して!/ヽる。水系接 着剤としては、イソシァネート系接着剤、ポリビュルアルコール系接着剤、ゼラチン系 接着剤、ビュル系ラテックス系、水系ポリウレタン、水系ポリエステル等を例示できる。
[0061] 前記透明保護フィルムの偏光子を接着させない面には、ハードコート層や反射防 止処理、ステイツキング防止や、拡散ないしアンチグレアを目的とした処理を施したも のであっても良い。
[0062] ハードコート処理は偏光板表面の傷付き防止などを目的に施されるものであり、例 えばアクリル系、シリコーン系などの適宜な紫外線硬化型榭脂による硬度や滑り特性 等に優れる硬化皮膜を透明保護フィルムの表面に付加する方式などにて形成するこ とができる。反射防止処理は偏光板表面での外光の反射防止を目的に施されるもの であり、従来に準じた反射防止膜などの形成により達成することができる。また、ステ イツキング防止処理は他の部材の隣接層との密着防止を目的に施される。
[0063] また、アンチグレア処理は偏光板の表面で外光が反射して偏光板透過光の視認を 阻害することの防止等を目的に施されるものであり、例えばサンドブラスト方式ゃェン ボス加工方式による粗面化方式や透明微粒子の配合方式などの適宜な方式にて透 明保護フィルムの表面に微細凹凸構造を付与することにより形成することができる。 前記表面微細凹凸構造の形成に含有させる微粒子としては、例えば平均粒径が 0. 5〜50 μ mのシリカ、アルミナ、チタ二了、ジルコユア、酸化スズ、酸化インジウム、酸 化カドミウム、酸ィ匕アンチモン等力もなる導電性の場合もある無機系微粒子、架橋又 は未架橋のポリマー等力もなる有機系微粒子 (ビーズを含む)などの透明微粒子が 用いられる。表面微細凹凸構造を形成する場合、微粒子の使用量は、表面微細凹 凸構造を形成する透明榭脂 100重量部に対して一般的に 2〜50重量部程度であり 、 5〜25重量部が好ましい。アンチグレア層は、偏光板透過光を拡散して視角などを 拡大するための拡散層 (視角拡大機能など)を兼ねるものであっても良い。
[0064] なお、前記反射防止層、ステイツキング防止層、拡散層やアンチグレア層等は、透 明保護フィルムそのものに設けることができるほか、別途光学層として透明保護フィル ムとは別体のものとして設けることもできる。
[0065] また光学フィルムとしては、例えば反射板や反透過板、位相差板（1Z2や 1Z4等 の波長板を含む）、視角補償フィルム、輝度向上フィルムなどの液晶表示装置等の 形成に用いられることのある光学層となるものがあげられる。これらは単独で光学フィ ルムとして用いることができる他、前記偏光板に、実用に際して積層して、 1層または 2層以上用いることができる。
[0066] 特に、偏光板に更に反射板または半透過反射板が積層されてなる反射型偏光板 または半透過型偏光板、偏光板に更に位相差板が積層されてなる楕円偏光板また は円偏光板、偏光板に更に視角補償フィルムが積層されてなる広視野角偏光板、あ るいは偏光板に更に輝度向上フィルムが積層されてなる偏光板が好ましい。
[0067] 反射型偏光板は、偏光板に反射層を設けたもので、視認側 (表示側)からの入射光 を反射させて表示するタイプの液晶表示装置などを形成するためのものであり、バッ クライト等の光源の内蔵を省略できて液晶表示装置の薄型化を図りやすいなどの利 点を有する。反射型偏光板の形成は、必要に応じ透明保護層等を介して偏光板の 片面に金属等力 なる反射層を付設する方式などの適宜な方式にて行うことができ る。
[0068] 反射型偏光板の具体例としては、必要に応じマット処理した透明保護フィルムの片 面に、アルミニウム等の反射性金属からなる箔ゃ蒸着膜を付設して反射層を形成し たものなどがあげられる。また、前記透明保護フィルムに微粒子を含有させて表面微 細凹凸構造とし、その上に微細凹凸構造の反射層を有するものなどもあげられる。前 記した微細凹凸構造の反射層は、入射光を乱反射により拡散させて指向性やギラギ ラした見栄えを防止し、明暗のムラを抑制しうる利点などを有する。また微粒子含有 の保護フィルムは、入射光及びその反射光がそれを透過する際に拡散されて明暗ム ラをより抑制しうる利点なども有している。透明保護フィルムの表面微細凹凸構造を 反映させた微細凹凸構造の反射層の形成は、例えば真空蒸着方式、イオンプレー ティング方式、スパッタリング方式ゃメツキ方式などの適宜な方式で金属を透明保護 層の表面に直接付設する方法などにより行うことができる。
[0069] 反射板は前記の偏光板の透明保護フィルムに直接付与する方式に代えて、その透 明フィルムに準じた適宜なフィルムに反射層を設けてなる反射シートなどとして用いる こともできる。なお反射層は、通常、金属力 なるので、その反射面が透明保護フィル ムゃ偏光板等で被覆された状態の使用形態が、酸化による反射率の低下防止、ひ いては初期反射率の長期持続の点や、保護層の別途付設の回避の点などより好ま しい。
[0070] なお、半透過型偏光板は、上記にお!、て反射層で光を反射し、かつ透過するハー フミラー等の半透過型の反射層とすることにより得ることができる。半透過型偏光板は
、通常液晶セルの裏側に設けられ、液晶表示装置などを比較的明るい雰囲気で使 用する場合には、視認側 (表示側)からの入射光を反射させて画像を表示し、比較的 喑 、雰囲気にぉ 、ては、半透過型偏光板のバックサイドに内蔵されて 、るバックライ ト等の内蔵電源を使用して画像を表示するタイプの液晶表示装置などを形成できる
。すなわち、半透過型偏光板は、明るい雰囲気下では、ノ ックライト等の光源使用の エネルギーを節約でき、比較的喑 、雰囲気下にお ヽても内蔵電源を用いて使用でき るタイプの液晶表示装置などの形成に有用である。
[0071] 偏光板に更に位相差板が積層されてなる楕円偏光板または円偏光板について説 明する。直線偏光を楕円偏光または円偏光に変えたり、楕円偏光または円偏光を直 線偏光に変えたり、あるいは直線偏光の偏光方向を変える場合に、位相差板などが 用いられる。特に、直線偏光を円偏光に変えたり、円偏光を直線偏光に変える位相 差板としては、いわゆる 1Z4波長板（λ Ζ4板とも言う）が用いられる。 1Z2波長板（ λ Ζ2板とも言う）は、通常、直線偏光の偏光方向を変える場合に用いられる。
[0072] 楕円偏光板はスーパーツイストネマチック（STN)型液晶表示装置の液晶層の複屈 折により生じた着色 (青又は黄)を補償 (防止)して、前記着色のな!、白黒表示する場 合などに有効に用いられる。更に、三次元の屈折率を制御したものは、液晶表示装 置の画面を斜め方向から見た際に生じる着色も補償 (防止)することができて好まし い。円偏光板は、例えば画像がカラー表示になる反射型液晶表示装置の画像の色 調を整える場合などに有効に用いられ、また、反射防止の機能も有する。
[0073] 位相差板としては、高分子素材を一軸または二軸延伸処理してなる複屈折性フィ ルム、液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムにて支持したも のなどがあげられる。位相差板の厚さも特に制限されないが、 0. 5〜150 /ζ πι、0. 5 〜50 μ m程度が一般的である。
[0074] 高分子素材としては、たとえば、ポリビュルアルコール、ポリビュルブチラール、ポリ メチルビ二ノレエーテル、ポリヒドロキシェチノレアタリレート、ヒドロキシェチノレセルロース 、ヒドロキシプロピルセルロース、メチノレセノレロース、ポリカーボネート、ポリアリレート、 ポリスルホン、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエーテノレス ルホン、ポリフエ-レンスルファイド、ポリフエ-レンオキサイド、ポリアリルスルホン、ポ リアミド、ポリイミド、ポリオレフイン、ポリ塩化ビュル、セルロース系重合体、ノルボルネ ン系榭脂、またはこれらの二元系、三元系各種共重合体、グラフト共重合体、プレン ド物などがあげられる。これらの高分子素材は延伸等により配向物 (延伸フィルム）と なる。
[0075] 液晶ポリマーとしては、たとえば、液晶配向性を付与する共役性の直線状原子団（ メソゲン）がポリマーの主鎖や側鎖に導入された主鎖型や側鎖型の各種のものなどを あげられる。主鎖型の液晶ポリマーの具体例としては、屈曲性を付与するスぺーサー 部でメソゲン基を結合した構造の、例えばネマチック配向性のポリエステル系液晶性 ポリマー、ディスコティックポリマーゃコレステリックポリマーなどがあげられる。側鎖型 の液晶ポリマーの具体例としては、ポリシロキサン、ポリアタリレート、ポリメタタリレート 又はポリマロネートを主鎖骨格とし、側鎖として共役性の原子団からなるスぺーサー 部を介してネマチック配向付与性のパラ置換環状ィ匕合物単位力 なるメソゲン部を 有するものなどがあげられる。これらの液晶ポリマーは、たとえば、ガラス板上に形成 したポリイミドゃポリビュルアルコール等の薄膜の表面をラビング処理したもの、酸ィ匕 ケィ素を斜方蒸着したものなどの配向処理面上に液晶性ポリマーの溶液を展開して 熱処理することにより行われる。
[0076] 位相差板は、例えば各種波長板や液晶層の複屈折による着色や視角等の補償を 目的としたものなどの使用目的に応じた適宜な位相差を有するものであって良ぐ 2 種以上の位相差板を積層して位相差等の光学特性を制御したものなどであっても良 い。
[0077] また、上記の楕円偏光板や反射型楕円偏光板は、偏光板又は反射型偏光板と位 相差板を適宜な組合せで積層したものである。カゝかる楕円偏光板等は、（反射型)偏 光板と位相差板の組合せとなるようにそれらを液晶表示装置の製造過程で順次別個 に積層することによつても形成しうる力 前記の如く予め楕円偏光板等の光学フィル ムとしたものは、品質の安定性や積層作業性等に優れて液晶表示装置などの製造 効率を向上させうる利点がある。
[0078] 視角補償フィルムは、液晶表示装置の画面を、画面に垂直でなくやや斜めの方向 力 見た場合でも、画像が比較的鮮明にみえるように視野角を広げるためのフィルム である。このような視角補償位相差板としては、例えば位相差板、液晶ポリマー等の 配向フィルムや透明基材上に液晶ポリマー等の配向層を支持したものなど力もなる。 通常の位相差板は、その面方向に一軸に延伸された複屈折を有するポリマーフィル ムが用いられるのに対し、視角補償フィルムとして用いられる位相差板には、面方向 に二軸に延伸された複屈折を有するポリマーフィルムと力、面方向に一軸に延伸され 厚さ方向にも延伸された厚さ方向の屈折率を制御した複屈折を有するポリマーや傾 斜配向フィルムのような二方向延伸フィルムなどが用いられる。傾斜配向フィルムとし ては、例えばポリマーフィルムに熱収縮フィルムを接着して加熱によるその収縮力の 作用下にポリマーフィルムを延伸処理又は Z及び収縮処理したものや、液晶ポリマ 一を斜め配向させたものなどがあげられる。位相差板の素材原料ポリマーは、先の位 相差板で説明したポリマーと同様のものが用いられ、液晶セルによる位相差に基づく 視認角の変化による着色等の防止や良視認の視野角の拡大などを目的とした適宜 なものを用いうる。
[0079] また、良視認の広い視野角を達成する点などより、液晶ポリマーの配向層、特にデ イスコティック液晶ポリマーの傾斜配向層からなる光学的異方性層をトリアセチルセル ロースフィルムにて支持した光学補償位相差板が好ましく用いうる。
[0080] 偏光板と輝度向上フィルムを貼り合せた偏光板は、通常液晶セルの裏側サイド〖こ 設けられて使用される。輝度向上フィルムは、液晶表示装置などのバックライトや裏 側からの反射などにより自然光が入射すると所定偏光軸の直線偏光または所定方向 の円偏光を反射し、他の光は透過する特性を示すもので、輝度向上フィルムを偏光 板と積層した偏光板は、バックライト等の光源からの光を入射させて所定偏光状態の 透過光を得ると共に、前記所定偏光状態以外の光は透過せずに反射される。この輝 度向上フィルム面で反射した光を更にその後ろ側に設けられた反射層等を介し反転 させて輝度向上フィルムに再入射させ、その一部又は全部を所定偏光状態の光とし て透過させて輝度向上フィルムを透過する光の増量を図ると共に、偏光子に吸収さ せにくい偏光を供給して液晶表示画像表示等に利用しうる光量の増大を図ることに より輝度を向上させうるものである。すなわち、輝度向上フィルムを使用せずに、バッ クライトなどで液晶セルの裏側カゝら偏光子を通して光を入射した場合には、偏光子の 偏光軸に一致していない偏光方向を有する光は、ほとんど偏光子に吸収されてしま い、偏光子を透過してこない。すなわち、用いた偏光子の特性よつても異なる力 お よそ 50%の光が偏光子に吸収されてしまい、その分、液晶画像表示等に利用しうる 光量が減少し、画像が暗くなる。輝度向上フィルムは、偏光子に吸収されるような偏 光方向を有する光を偏光子に入射させずに輝度向上フィルムで一反反射させ、更に その後ろ側に設けられた反射層等を介して反転させて輝度向上フィルムに再入射さ せることを繰り返し、この両者間で反射、反転している光の偏光方向が偏光子を通過 し得るような偏光方向になった偏光のみを、輝度向上フィルムは透過させて偏光子に 供給するので、バックライトなどの光を効率的に液晶表示装置の画像の表示に使用 でき、画面を明るくすることができる。
[0081] 輝度向上フィルムと上記反射層等の間に拡散板を設けることもできる。輝度向上フ イルムによって反射した偏光状態の光は上記反射層等に向かうが、設置された拡散 板は通過する光を均一に拡散すると同時に偏光状態を解消し、非偏光状態となる。 すなわち、自然光状態の光が反射層等に向力ぃ、反射層等を介して反射し、再び拡 散板を通過して輝度向上フィルムに再入射することを繰り返す。このように輝度向上 フィルムと上記反射層等の間に、偏光を元の自然光にもどす拡散板を設けることによ り表示画面の明るさを維持しつつ、同時に表示画面の明るさのむらを少なくし、均一 で明るい画面を提供することができる。力かる拡散板を設けることにより、初回の入射 光は反射の繰り返し回数が程よく増加し、拡散板の拡散機能と相俟って均一の明る V、表示画面を提供することができたものと考えられる。
[0082] 前記の輝度向上フィルムとしては、例えば誘電体の多層薄膜や屈折率異方性が相 違する薄膜フィルムの多層積層体の如き、所定偏光軸の直線偏光を透過して他の光 は反射する特性を示すもの、コレステリック液晶ポリマーの配向フィルムやその配向 液晶層をフィルム基材上に支持したものの如き、左回り又は右回りのいずれか一方 の円偏光を反射して他の光は透過する特性を示すものなどの適宜なものを用いうる。
[0083] 従って、前記した所定偏光軸の直線偏光を透過させるタイプの輝度向上フィルムで は、その透過光をそのまま偏光板に偏光軸を揃えて入射させることにより、偏光板に よる吸収ロスを抑制しつつ効率よく透過させることができる。一方、コレステリック液晶 層の如く円偏光を透過するタイプの輝度向上フィルムでは、そのまま偏光子に入射さ せることもできるが、吸収ロスを抑制する点よりその円偏光を、位相差板を介し直線偏 光化して偏光板に入射させることが好ましい。なお、その位相差板として 1Z4波長板 を用いることにより、円偏光を直線偏光に変換することができる。
[0084] 可視光域等の広い波長で 1Z4波長板として機能する位相差板は、例えば波長 55 Onmの淡色光に対して 1Z4波長板として機能する位相差板と他の位相差特性を示 す位相差層、例えば 1Z2波長板として機能する位相差層とを重畳する方式などによ り得ることができる。従って、偏光板と輝度向上フィルムの間に配置する位相差板は、 1層または 2層以上の位相差層力 なるものであってよい。
[0085] なお、コレステリック液晶層についても、反射波長が相違するものの組合せにして 2 層又は 3層以上重畳した配置構造とすることにより、可視光城等の広い波長範囲で 円偏光を反射するものを得ることができ、それに基づ 、て広 、波長範囲の透過円偏 光を得ることができる。
[0086] また、偏光板は、上記の偏光分離型偏光板の如ぐ偏光板と 2層又は 3層以上の光 学層とを積層したものからなっていても良い。従って、上記の反射型偏光板や半透過 型偏光板と位相差板を組み合わせた反射型楕円偏光板や半透過型楕円偏光板な どであっても良い。
[0087] ディスコティック液晶層を含む視野角拡大フィルム、コーティングで形成されたフィ ルム等の位相差機能を持つフィルムなど、特に周辺部にムラが出やす ヽ光学フィル ムに本発明の粘着剤が好ましく用いられる。
[0088] 偏光板に前記光学層を積層した光学フィルムは、液晶表示装置等の製造過程で 順次別個に積層する方式にても形成することができる力 予め積層して光学フィルム としたものは、品質の安定性や組立作業等に優れて!/、て液晶表示装置などの製造 工程を向上させうる利点がある。積層には粘着層等の適宜な接着手段を用いうる。前 記の偏光板と他の光学層の接着に際し、それらの光学軸は目的とする位相差特性な どに応じて適宜な配置角度とすることができる。
[0089] 本発明の粘着剤付き光学フィルムは液晶表示装置等の各種画像表示装置の形成 などに好ましく用いることができる。液晶表示装置の形成は、従来に準じて行いうる。 すなわち液晶表示装置は一般に、液晶セルと粘着剤付き光学フィルム、及び必要に 応じての照明システム等の構成部品を適宜に組み立てて駆動回路を組み込むことな どにより形成されるが、本発明においては本発明による粘着剤付き光学フィルムを用 いる点を除いて特に限定は無ぐ従来に準じうる。液晶セルについても、例えば TN 型や STN型、 π型などの任意なタイプなどの任意なタイプのものを用いうる。
[0090] 液晶セルの片側又は両側に粘着剤付き光学フィルムを配置した液晶表示装置や、 照明システムにバックライトある!/、は反射板を用いたものなどの適宜な液晶表示装置 を形成することができる。その場合、本発明による光学フィルムは液晶セルの片側又 は両側に設置することができる。両側に光学フィルムを設ける場合、それらは同じもの であっても良いし、異なるものであっても良い。さらに、液晶表示装置の形成に際して は、例えば拡散板、アンチグレア層、反射防止膜、保護板、プリズムアレイ、レンズァ レイシート、光拡散板、ノ ックライトなどの適宜な部品を適宜な位置に 1層又は 2層以 上配置することができる。
実施例
[0091] 以下に、実施例によって本発明を具体的に説明するが、本発明はこれら実施例に よって限定されるものではない。
[0092] 実施例 1
冷却管、撹拌羽、温度計が付属した 4つ口フラスコ中に、ブチルアタリレート 95重量 部、アクリル酸 4重量部、 N- (2-ヒドロキシェチル)アクリルアミド 1重量部および過酸 化ベンゾィル 0. 2重量部をトルエン 200重量部とともに加え、十分に窒素置換した後 、窒素気流下で撹拌しながら、約 60°Cで 8時間反応させ、重量平均分子量 180万（ GPCポリスチレン換算）のアクリル系共重合体の溶液を得た。このアクリル系共重合 体の溶液の固形分 100重量部に対して、イソシァネート系架橋剤（コロネート L, 日本 ポリウレタン社製)を固形分で 0. 5重量部加えて、粘着剤溶液を作成した。
[0093] 実施例 2〜12、比較例 1〜4
実施例 1において、モノマー成分の種類または配合量を、表 1に示すように変えた こと以外は実施例 1と同様にして、粘着剤溶液を作成した。
[0094] 実施例および比較例で得られた粘着剤溶液を、離型処理を施したポリエステルフィ ルム（厚さ 38 μ m)からなるセパレータ上に、乾燥後の粘着剤層の厚さが 20 μ mにな るように、リバースロールコート法により塗布し、 155°Cで 3分間加熱処理して、溶剤を 揮発させ、粘着剤層を得た。この粘着剤層を、視野角拡大フィルム付き偏光板（日東 電工製: NWF— LESEGタイプ）に積層して、粘着剤付き光学フィルムを作製した。 視野角拡大フィルム付き偏光板は、偏光板に、接着剤により視野角拡大フィルムとし て液晶層を積層したものであり、粘着剤層は、視野角拡大フィルム側表面に設けた。
[0095] 上記で得られた粘着剤付き光学フィルムについて、以下の評価を行った。結果を表
1に示す。
[0096] くムラ〉
粘着剤付き光学フィルムは、偏光板の吸収軸に対して 135° の角度で 17インチサ ィズに切り出したものを 2枚用意した。この粘着剤付き光学フィルムを、ガラス板の表 裏にクロス-コルになるようにラミネータにて貼り合せたのち、 50°C、 5atmで 15分間 のオートクレープ処理を行った。これを初期状態とした。次いで、 60°Cで、 24時間の 加熱処理を行った。これを加熱処理後の状態とした。初期状態および加熱処理後の 状態について、光学フィルムをバックライト上に置き、その周辺部のムラを、下記の基 準により、 目視で評価した。〇：周辺部にムラなし。 X：周辺部にムラあり。
[0097] <粘着力の測定 >
粘着剤付き光学フィルムを、位相差板 (JSR社製，ノルボルネン系フィルム、アート ン）に貼り合せた後、 25mm X I 50mmに裁断し、引張り試験機にて、剥離角度 90° 、剥離速度 300mmZminで粘着力を測定した。
[0098] [表 1]
Figure imgf000024_0001
[0099] 表 1中、 BA: n-ブチルアタリレート、 2EHA: 2—ェチルへキシルアタリレート、 HEA A:N- (2-ヒドロキシェチル）アクリルアミド、 AA:アクリル酸、 ACMO :N-アタリロイル モルホリン、 DMAA:N, N-ジメチルアクリルアミド、 HEA: 2-ヒドロキシェチルアタリ レート、を示す。
[0100] 実施例、比較例では、初期状態はいずれも、評価「〇」であり周辺部のムラはな力つ た。一方、実施例では、加熱処理後の状態も評価「〇」であった。しかし、比較例 1、 3 では HEAAを用いていないため、また比較例 2、 4では、 HEAAの代わりに、ヒドロキ シル基含有モノマーとして HEAを用いている力 加熱処理後の状態は、いずれも「 X」であり周辺部にムラが認められた。

Claims

請求の範囲
[1] アルキル (メタ）アタリレート（al)および N- (2-ヒドロキシェチル）（メタ）アクリルアミド
(a2)を、モノマー単位として含有するアクリル系共重合体、ならびに架橋剤を含有す ることを特徴とする光学用粘着剤。
[2] N- (2-ヒドロキシェチル）（メタ）アクリルアミド (a2)の割合力 アルキル (メタ）アタリレ ート（al) 100重量部に対して、 0. 01〜： L00重量部であることを特徴とする請求項 1 記載の光学用粘着剤。
[3] モノマー単位として、さらに、前記 (al)成分および (a2)成分を除ぐモノマー（a3) を、アルキル (メタ)アタリレート（al) 100重量部に対して、 50重量部以下含有するこ とを特徴とする請求項 1記載の光学用粘着剤。
[4] モノマー（a3)力 カルボキシル基を含有するモノマーであることを特徴とする請求 項 1記載の光学用粘着剤。
[5] モノマー（a3)が、窒素含有ビュルモノマーであることを特徴とする請求項 1記載の 光学用粘着剤。
[6] 光学フィルムの少なくとも一方の面に粘着剤層が積層されている粘着剤付き光学フ イルムであって、
前記粘着剤層は、請求項 1〜5のいずれかに記載の光学用粘着剤により形成され て!、ることを特徴とする粘着剤付き光学フィルム。
[7] 光学フィルムが偏光板および Zまたは位相差板であることを特徴とする請求項 6記 載の粘着剤付き光学フィルム。
[8] 請求項 6記載の粘着剤付き光学フィルムが用いられて ヽることを特徴とする画像表 示装置。
PCT/JP2007/055112 2006-03-27 2007-03-14 光学用粘着剤、粘着剤付き光学フィルムおよび画像表示装置 WO2007111138A1 (ja)