WO2007072944A1 - 太陽電池用封止膜及びこの封止膜を用いた太陽電池 - Google Patents
太陽電池用封止膜及びこの封止膜を用いた太陽電池 Download PDFInfo
- Publication number
- WO2007072944A1 WO2007072944A1 PCT/JP2006/325617 JP2006325617W WO2007072944A1 WO 2007072944 A1 WO2007072944 A1 WO 2007072944A1 JP 2006325617 W JP2006325617 W JP 2006325617W WO 2007072944 A1 WO2007072944 A1 WO 2007072944A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solar cell
- sealing film
- mass
- ethylene
- acetate copolymer
- Prior art date
Abstract
耐熱性、耐光性の向上した太陽電池用封止膜及びこの封止膜を有する太陽電池を提供すること。
エチレン／酢酸ビニル共重合体及び有機過酸化物を含む太陽電池用封止膜において、
該有機過酸化物として、特定のパーオキシエステルを使用し、且つ黄変防止のために、ジヒドロキシジメトキシベンゾフェノン系紫外線吸収剤を使用し、ヒンダードアミン系光安定剤を実質的に使用しないことを特徴とする太陽電池用封止膜；及びエチレン／酢酸ビニル共重合体及び有機過酸化物を含む太陽電池用封止膜において、該有機過酸化物として、特定のジアルキルパーオキサイドを使用し、且つ黄変防止のために、ジヒドロキシジメトキシベンゾフェノン系紫外線吸収剤を使用し、モノヒドロキシアルコキシベンゾフェノン系紫外線吸収剤を実質的に使用しないことを特徴とする太陽電池用封止膜；及びこの封止膜を有する太陽電池。
Description
明 細 書
太陽電池用封止膜及びこの封止膜を用いた太陽電池
技術分野
[0001] 本発明は、エチレン 酢酸ビニル共重合体を主成分とする太陽電池用封止膜及 びこの封止膜を用いた太陽電池に関し、特に黄変防止性に優れた太陽電池用封止 膜及び太陽電池に関する。
背景技術
[0002] 近年、資源の有効利用や環境汚染の防止等の面から、太陽光を直接電気工ネル ギ一に変換する太陽電池が注目され、開発が進められている。
[0003] 太陽電池は、一般に、図 1に示すように、表面側透明保護部材としてのガラス基板 1 と裏面側保護部材 (バックカバー） 2との間に EVA (エチレン 酢酸ビニル共重合体） フィルムの封止膜 3A, 3Bにより、シリコン発電素子等の太陽電池用セル 4を封止した 構成とされている。なお、以下において、セルに対して受光面側に配置する封止膜を 「表面側封止膜」と称し、セルの後方側に配置する封止膜を「裏面側封止膜」と称す
[0004] このような太陽電池は、ガラス基板 1、表面側封止用 EVAフィルム 3A、シリコン発 電素子 4、裏面側封止用 EVAフィルム 3B及びバックカバー 2をこの順で積層し、カロ 熱加圧して、 EVAを架橋硬化させて接着一体化することにより製造される。
[0005] 上記太陽電池においては、太陽電池に入射した光をできるだけ効率よく太陽電池 用セル内に取り込めるようにすることが発電効率の向上の点から強く望まれている。 従って、封止用 EVAフィルムは、できるだけ高い透明性を有し、入射した太陽光を吸 収したり、反射したりすることが無ぐ太陽光のほとんどを透過させるものが望ましい。 さらに太陽電池を長期に使用した場合に、光、熱の影響により、封止用 EVAフィルム が黄変して、太陽光の透過率が低下する現象が見られること、及びその黄変による 外観不良が問題となっている。
[0006] このような黄変防止のために、封止用 EVAフィルムには、各種の紫外線吸収剤、光 安定剤等が使用されている。例えば、特許文献 1 (特開平 7— 169986号公報)では
、有機過酸化物 (架橋剤）として、パーォキシエステル系の過酸ィ匕物である 2, 5 ジ メチル—2, 5—ジ (t—ブチルパーォキシ)へキサンを使用し、紫外線吸収剤としてモ ノヒドロキシアルコキシベンゾフエノン系の 2 ヒドロキシ一 4— n—オタトキシベンゾフ ヱノンが使用されている。また、特許文献 2 (特開 2000— 183381号公報）には、有 機酸化物として、 1, 1 ビス（t—ブチルパーォキシ）3, 3, 5 トリメチルシクロへキサ ンを用い、紫外線吸収剤として上記と同じ 2 ヒドロキシ一 4— n—オタトキシベンゾフ ヱノンが使用されている。
[0007] 特許文献 1 :特開平 7— 169986号公報
特許文献 2 :特開 2000— 183381号公報
発明の開示
発明が解決しょうとする課題
[0008] 本発明者の検討によると、従来一般的に使用されている紫外線吸収剤、或いは光 安定剤は、他の紫外線吸収剤と併用したときに、黄変防止に対してむしろ悪影響を 及ぼす場合があることが明らかとなった。本発明者がさらに研究を重ねたところ、使用 する有機過酸化物の種類により、上記悪影響を与える紫外線吸収剤等の種類が異 なることも見いだした。
[0009] 従って、本発明は、上記従来の問題点を解決し、耐光性、耐熱性の向上した太陽 電池用封止膜を提供することを目的とする。
[0010] また、本発明は、上記太陽電池用封止膜を用いた耐光性、耐熱性の向上した太陽 電池を提供することを目的とする。
課題を解決するための手段
[0011] 上記目的は、
エチレン z酢酸ビニル共重合体及び有機過酸化物 (架橋剤)を含む太陽電池用封 止膜において、
該有機過酸化物として、下記式 I：
[0012] [化 1]
O
SI
i_0 ~O~C ~0 ~ 2
[0013] [但し、 R1が炭素原子数 3〜5の分岐のアルキル基を表し、そして R2が炭素原子数 6 〜9の分岐のアルキル基を表す。 ]
で表されるパーォキシエステルを含み、且つ黄変防止のために、ジヒドロキシジメトキ シベンゾフエノン系紫外線吸収剤を含有し、ヒンダードアミン系光安定剤を実質的に 含有していないことを特徴とする太陽電池用封止膜;及び
エチレン Z酢酸ビニル共重合体及び有機過酸化物 (架橋剤)を含む太陽電池用封 止膜において、
該有機過酸化物として、下記式 II：
[0014] [化 2]
R3 R3
R5 0— 0—C - CH2 CH— 00— 0
R3 R3
[0015] [但し、 R3が、それぞれ独立して炭素原子数 1〜3のアルキル基を表し、 R4が炭素原 子数 3〜5の分岐のアルキル基を表し、そして R5が炭素原子数 3〜5の分岐のアルキ ル基を表す。 ]
で表されるジアルキルパーオキサイドを含み、且つ黄変防止のために、ジヒドロキシ ジメトキシベンゾフエノン系紫外線吸収剤を含有し、モノヒドロキシアルコキシベンゾフ ヱノン系紫外線吸収剤を実質的に含有していないことを特徴とする太陽電池用封止 膜により達成することができる。
[0016] 本発明の太陽電池用封止膜の好ましい態様を以下に列記する。
(1)式 Iにおいて、 R1が t—ブチルを表し、そして R2が 2—ェチルへキシル基を表す。
(2)上記ヒンダードアミン系光安定剤力 ビス（2, 2, 6, 6—テトラメチル— 4—ピペリ ジル)セバケートである。実質的に使用しない量とは、エチレン Z酢酸ビュル共重合
体 100質量部に対して 0. 1質量部未満 (特に 0. 01質量部未満)である。
(3)式 IIにおいて、 R3カ^チルを表し、そして R4及び R5力 ¾—ブチルを表す。
(4)上記モノヒドロキシアルコキシベンゾフエノン系紫外線吸収剤が 2—ヒドロキシ一 4 ーォクチルォキシベンゾフエノンである。実質的に使用しない量とは、エチレン Z酢 酸ビニル共重合体 100質量部に対して 0. 2質量部未満 (特に 0. 02質量部未満)で ある。
(5)ジヒドロキシジメトキシベンゾフエノン系紫外線吸収剤力 2, 2—ジヒドロキシー4 , 4ージメトキシベンゾフエノンである。
(6)ジヒドロキシジメトキシベンゾフエノン系紫外線吸収剤を、エチレン Z酢酸ビュル 共重合体 100質量部に対して 0. 01〜： L 0質量部含有している。上記有機過酸ィ匕 物を用いた際の黄変防止効果が優れて 、る。
(7)封止膜は、有機過酸化物を、エチレン Z酢酸ビニル共重合体 100質量部に対し て 0. 1〜5. 0質量部含有している。
(8)封止膜は、架橋助剤 (ラジカル重合性基を有する化合物）を、エチレン Z酢酸ビ -ル共重合体 100質量部に対して 0. 1〜5. 0質量部含有している。
(9)エチレン Z酢酸ビニル共重合体の酢酸ビニル単位が、エチレン酢酸ビニル共重 合体 100質量部に対して 20〜35質量％の範囲である。優れた透明性を示す。
[0017] さらに本発明は、
表面側透明保護部材と裏面側保護部材との間に封止膜を用いて太陽電池用セル を封止してなる太陽電池において、該太陽電池用セルと裏面側保護部材との間に介 在させる封止膜として上記の太陽電池用封止膜を用いて架橋一体化されていること を特徴とする太陽電池にもある。
発明の効果
[0018] 本発明の太陽電池用封止膜は、エチレン Z酢酸ビニル共重合体 (EVA)を主成分 とし、特定の有機過酸化物と特定の紫外線吸収剤を含み、且つ従来、一般的に使用 されてきた特定の紫外線吸収剤又は光安定剤を含まないものである。これにより、長 期使用した場合の黄変等の発生が顕著に抑えられ、向上した耐光性、耐熱性を有 する太陽電池用封止膜を得ることができる。
[0019] 従って、このような太陽電池用封止膜を有する太陽電池も耐光性、耐候性、耐熱性 が向上している。
図面の簡単な説明
[0020] [図 1]一般的な太陽電池を示す断面図である。
符号の説明
[0021] 1ガラス基板
2バックカバー
3A, 3B EVAフィルム
4シリコン発電素子
発明を実施するための最良の形態
[0022] 本発明の太陽電池用封止膜は、エチレン Z酢酸ビニル共重合体 (EVA)を主成分 とし、特定の有機過酸化物 (架橋剤)と特定の紫外線吸収剤を含み、且つ従来、一般 的に使用されてきた特定の紫外線吸収剤又は光安定剤を含んで!/ヽな ヽ。
[0023] 即ち、本発明の太陽電池用封止膜においては、有機過酸ィ匕物として、下記式 I：
[0024] [化 3] o
!1
i_0 -0~C ~0 ~R2
[0025] [但し、 R1が炭素原子数 3〜5の分岐のアルキル基を表し、そして R2が炭素原子数 6 〜9の分岐のアルキル基を表す。 ]
で表されるパーォキシエステルを使用した場合は、黄変防止のために、ジヒドロキシ ジメトキシベンゾフエノン系紫外線吸収剤を使用し、従来から一般的に使用されて ヽ るヒンダードアミン系光安定剤を実質的に使用しない。ヒンダードアミン系光安定剤は 、ラジカル補足剤であり、光に対する安定剤として開発されたものであるが、最近では 広い酸ィ匕防止機能を有するものとして知られている。このため本発明者が従来使用 されてきた光安定剤にっ ヽて再評価したところ、上記有機過酸化物との組合せでは 好ましくない結果が得られた。特に、ヒンダードアミン系光安定剤を上記ジヒドロキシ
ジメトキシベンゾフエノン系紫外線吸収剤を併用したときに、顕著にその傾向があるこ とが明ら力となった。その機構については不明である。
[0026] 式 Iにおいて、 R1は、炭素原子数 3〜5の分岐のアルキル基、例えばイソプロピル、 t ーブチノレ、 iーブチノレ、 sec ブチノレ、イソペンチノレ、 tert ペンチノレ、ネオペンチノレ を表し、特に t ブチルが好ましぐそして R2が炭素原子数 6〜9の分岐のアルキル基 、例えば 1ーェチルブチル、 1 メチルヘプチル基、 1 メチルへキシル基、 1ーェチ ルへキシル基、 1 ェチルヘプチル基、 2—ェチルブチル、 2—メチルヘプチル基、 2 メチルへキシル基、 2—ェチルへキシル基、 2—ェチルへプチル基を表し、特に 2 ェチルへキシル基が好まし 、。
[0027] 上記ヒンダードアミン系光安定剤としては、ビス（2, 2, 6, 6—テトラメチルー 4ーピ ペリジル)セバケート [商品名の例：サノール LS770、三共化学 (株)製]が一般的で ある。この化合物を実質的に使用しない量とは、エチレン Z酢酸ビニル共重合体 10 0質量部に対して 0. 1質量部未満 (特に 0. 01質量部未満)である。
[0028] 黄変防止のために、本発明で使用されるジヒドロキシジメトキシベンゾフエノン系紫 外線吸収剤としては、例えば 2 ヒドロキシー4ーメトキシベンゾフエノン [商品名の例 ：ュピナ一ノレ 3040、 BASF社製]、 2, 2 ジヒドロキシ一 4, 4 ジメトキシベンゾフエ ノン [商品名の例：ュピナール 3049、 BASF社製]を挙げることができ、特に 2, 2— ジヒドロキシ 4, 4ージメトキシベンゾフエノンが好まし!/、。
[0029] また、本発明の太陽電池用封止膜においては、有機過酸ィ匕物として、下記式 II：
[0030] [化 4]
R3 R3
5-0-0-C-CH2-CH2~C-0-~0-R4
R3 R3
[0031] [但し、 R3が、それぞれ独立して炭素原子数 1〜3のアルキル基を表し、 R4が炭素原 子数 3〜5の分岐のアルキル基を表し、そして R5が炭素原子数 3〜5の分岐のアルキ ル基を表す。 ]
で表されるジアルキルパーオキサイドを使用した場合、黄変防止のために、ジヒドロキ
シジメトキシベンゾフエノン系紫外線吸収剤を使用し、モノヒドロキシアルコキシベンゾ フエノン系紫外線吸収剤を実質的に使用しな 、。モノヒドロキシアルコキシベンゾフエ ノン系紫外線吸収剤は、紫外線吸収剤として従来カゝら使用されているものであるが、 本発明者の紫外線吸収剤の再評価よれば、上記有機過酸化物との組合せでは好ま しくない結果が得られた。特に、モノヒドロキシアルコキシベンゾフエノン系紫外線吸 収剤を上記ジヒドロキシジメトキシベンゾフエノン系紫外線吸収剤と併用したときに、 顕著にその傾向があることが明ら力となった。
[0032] 式 IIにおいて、 R3が、それぞれ独立して炭素原子数 1〜3のアルキル基、例えばメ チル、ェチル、 i—プロピルを表し、 R4が炭素原子数 3〜5の分岐のアルキル基、例え ば i プロピル、 tーブチル、 iーブチル、 sec ブチル、イソペンチル、 tert ペンチ ル、ネオペンチルを表し、そして R5が炭素原子数 3〜5の分岐のアルキル基、例えば i プロピノレ、 tーブチノレ、 iーブチノレ、 sec ブチノレ、イソペンチノレ、 tert ペンチノレ、 ネオペンチルを表す。 R3は、全て同一であることが好ましぐ特にメチルが好ましい。 R4及び R5は、相互に同一であることが好ましぐ tーブチル、 iーブチル、 sec ブチル 、特に t ブチルが好ましい。
[0033] 上記モノヒドロキシアルコキシベンゾフエノン系紫外線吸収剤としては、例えば 2 ヒ ドロキシー4ーォクチルォキシベンゾフエノン、 2 ヒドロキシー4ーメトキシー5—スル ホベンゾフエノンを挙げることができ、 2 ヒドロキシ一 4—ォクチルォキシベンゾフエノ ン [商品名の例:スミソープ 130、住友ィ匕学 (株)製]が一般的であり、特に有効である 。この化合物を実質的に使用しない量とは、エチレン Z酢酸ビニル共重合体 100質 量部に対して 0. 2質量部未満 (特に 0. 02質量部未満)である。
[0034] ここで使用されるジヒドロキシジメトキシベンゾフエノン系紫外線吸収剤は前記の通り である。
[0035] 上記のように、本発明の太陽電池用封止膜は、退色による黄変等の発生が顕著に 抑えられており、向上した耐光性、耐熱性を得ることができる。
[0036] 本発明の太陽電池用封止膜は、例えば、上記構成を有する EVA榭脂組成物を常 法に従って成膜することにより、容易に製造することができる。
[0037] 得られる本発明の太陽電池用封止膜の厚さは、一般に 50 m〜 2mmの範囲にあ
る。
[0038] 次に、本発明の EVA榭脂組成物について説明する。
[0039] 本発明の EVA榭脂組成物に用いられる有機榭脂としては、エチレン Z酢酸ビュル 共重合体 (EVA)が使用される。さらに、ポリビュルァセタール系榭脂（例えば、ポリビ -ルホルマール、ポリビュルブチラール (PVB榭脂）、変性 PVB)、塩ィ匕ビュル榭脂 を副次的に使用することもできる。その場合、特に PVBが好ましい。
[0040] 上記 EVAは、酢酸ビニル含有率が、一般に 10〜40質量％であり、 10〜36質量 %、特に 10〜33質量0 /0、中でも 10〜28質量％であることが好ましい。この酢酸ビ- ル含有率が 40質量％を超えると、榭脂の粘性が低下し、封止時にガラス基板とバッ クカバーとの間から流れ出し易くなり好ましくない。さらに、粘着性が増大して、取扱 いが困難となる。酢酸ビニル含有率が 10質量％未満になると、加工性が低下し、得 られるフィルムが硬質になりすぎるため、脱気性が低下し、太陽電池作製時にセルに 損傷を与えやすくなる。
[0041] 本発明で用いられる EVAは、メルトフローレートが 0. 7〜40gZlO分、特に 1. 5〜
15gZ 10分であることが好ましい。
[0042] 本発明で用いる EVA榭脂組成物には、耐候性の向上のために有機過酸化物 (架 橋剤）を含有しており、これにより架橋構造が得られる。本発明では前記の特定の有 機過酸化物を含有している。しカゝしながら、副次的に他の有機過酸ィ匕物を含有しても 良い。
[0043] その有機過酸ィ匕物 (架橋剤）としては、一般に、 100°C以上でラジカルを発生する 有機過酸化物が用いられ、特に、配合時の安定性を考慮に入れれば、半減期 10時 間の分解温度が 70°C以上であるものが好ましい。このような有機過酸ィ匕物としては、 例えば 2, 5 ジメチルへキサン； 2, 5 ジハイド口パーオキサイド； 3 ジー tーブチ ルパーオキサイド； tージクミルパーオキサイド； 2, 5 ジメチルー 2, 5 ジ（tーブチ ルバーオキシ）へキシン；ジクミルパーオキサイド； a , α ， 一ビス（t ブチルパーォキ シイソプロピル）ベンゼン； n—ブチノレ 4, 4 ビス（t ブチノレパーォキシ）ブタン； 2 , 2 ビス (t ブチノレパーォキシ）ブタン； 1 , 1 ビス（t ブチノレパーォキシ）シクロ へキサン； 1, 1 ビス（t ブチルパーォキシ）3, 3, 5 トリメチルシクロへキサン； t—
ブチルパーォキシベンゾエート；ベンゾィルパーオキサイド等を用いることができる。
[0044] 有機過酸ィ匕物は、一般に EVA100重量部に対して一般に 5質量部以下、好ましく は 0. 1〜5質量部、特に 0. 1〜3質量部の範囲で使用される。
[0045] また、太陽電池の封止膜として、発電素子との接着力向上の目的で、 EVA榭脂に シランカップリング剤を添加することができる。この目的に使用されるシランカップリン グ剤としては公知のもの、例えば γ—クロ口プロピルトリメトキシシラン；ビュルトリクロ口 シラン；ビュルトリエトキシシラン；ビュル一トリス一（ メトキシエトキシ）シラン； γ - メタクリロキシプロピルトリメトキシシラン； /3 - (3, 4—エトキシシクロへキシル）ェチル トリメトキシシラン； γ—グリシドキシプロピルトリメトキシシラン；ビニルトリァセトキシシラ ン； γ—メルカプトプロピルトリメトキシシラン； γ—ァミノプロピルトリメトキシシラン； Ν — β— (アミノエチル） - γ—ァミノプロピルトリメトキシシラン等を挙げることができる。 これらのシランカップリング剤は、 EVA100質量部に対して 5質量部以下、好ましくは 0. 1〜2質量部で使用される。
[0046] さらに、 EVAのゲル分率を向上させ、耐久性を向上するために EVA榭脂に架橋助 剤 (官能基としてラジカル重合性基を有する化合物）を添加することができる。この目 的に供される架橋助剤としては、公知のものとしてトリァリルシアヌレート；トリアリルイソ シァヌレート等の 3官能の架橋助剤の他、（メタ）アクリルエステル (例、 NKエステル等 )の単官能又は 2官能の架橋助剤等も挙げることができる。これらの架橋助剤は、 EV A100質量部に対して一般に 10質量部以下、好ましくは 0. 1〜5質量部で使用され る。
[0047] また、 EVAの安定性を向上する目的でハイドロキノン；ノヽイドロキノンモノメチルェ 一テル; p べンゾキノン;メチルハイドロキノンなどを添加することができ、これらは、 EVA榭脂 100重量部に対して一般に 5質量部以下で使用される。
[0048] 本発明では、上記のように、 EVAと共に、特定の有機過酸化物と組み合わせて、 特定の紫外線吸収剤が使用される。し力しながら、必要に応じ、さらに上記以外の着 色剤、紫外線吸収剤、老化防止剤、変色防止剤等を添加することができる。着色剤 の例としては、金属酸化物、金属粉等の無機顔料、ァゾ系、フタロシアニン系、ァヂ 系、酸性又は塩基染料系レーキ等の有機顔料がある。紫外線吸収剤としては、 2 - (
2，ーヒドロキシー5—メチルフエ-ル）ベンゾトリアゾール等のベンゾトリアゾール系；フ ェ-ルサルシレート； p—t—ブチルフエ-ルサルシレート等のヒンダートフエノール系 がある。老化防止剤としては、アミン系；フエノール系；ビスフエ-ル系を挙げることが できる。
[0049] 上記本発明の EVA榭脂組成物を、例えば、押出成形、カレンダー成形等によりカロ 熱圧延することにより成膜することにより、常法に従い本発明の太陽電池用封止膜を 製造することができる。尚、加熱温度は、架橋剤が反応しない或いはほとんど反応し ない温度とすることが好ましい。例えば、 40〜70°Cが好ましい。
[0050] 本発明の太陽電池用封止膜を用いて太陽電池を製造するには、図 1に示すように ガラス基板 1、 EVAフィルム 3A、シリコン発電素子 4、 EVAフィルム 3B及びバック力 バー 2を積層するに当り、裏面側 EVAフィルム 3Bとして、本発明の封止膜を用い、ま た、表面側の EVAフィルム 3Aとしても本発明の封止膜を用いて積層し、積層体を常 法に従って、真空ラミネータで温度 120〜150°C、脱気時間 2〜15分、プレス圧力 0 . 5〜： LkgZcm2、プレス時間 8〜45分で加熱加圧圧着すれば良ぐこの加熱加圧時 に、 EVAフィルム 3A, 3Bが架橋して耐光性、耐熱性及び耐候性に優れた封止膜を 形成することができる。
[0051] 本発明で使用されるガラス基板 1は、通常珪酸塩ガラスである。ガラス板厚は、 0. 1
〜 10mmが一般的であり、 0. 3〜5mmが好ましい。ガラス基板は、一般に、化学的 に、或いは熱的に強化させたものである。
[0052] 本発明で使用されるバックガード 2は、一般にプラスチックフィルム（例、ポリエチレ ンテレフタレート（PET)、ポリテトラフルォロエチレン（PTFE) )である力 耐熱性を考 慮してフッ化ポリエチレンフィルムが好まし！/、。
[0053] 以下に実施例を示し、本発明についてさらに詳述する。
実施例
[0054] [実施例 1]
[EVA榭脂組成物配合 1 (質量部) ]
EVA榭脂： 100
(酢酸ビュル含有量 28重量0 /0、メルトフローレート 15gZlO分）
架橋剤 1 :
(t ブチノレパーォキシ 2—ェチノレへキサノエ
架橋助剤（トリアリルイソシァヌレート）：
紫外線吸収剤 1 :
(2, 2 ジヒドロキシ一 4, 4 ジメトキシベンゾフエノン）
上記配合の EVA榭脂組成物を用いて、 80°Cでカレンダー成形して、 EVAフィルム を成膜した。フィルムの厚さは 600 mであった。
[0055] 得られた EVAフィルムを表面側封止用 EVAフィルム 3A及び裏面側封止用 EVA フィルム 3Bとして用い、図 1に示すように、厚さ 3mmのガラス板 1、厚さ 38 μ mのフッ 化ポリエチレンフィルムよりなるバックカバー 2との間にシリコン発電素子 4を封止して 太陽電池を製造した。なお、封止は、真空ラミネーターで温度 150°C、脱気時間 3分 、プレス時間 15分間加熱圧着し、 EVAを架橋することにより行った。
[0056] [比較例 1]
EVA榭脂組成物配合 1にさらに、ヒンダードアミン系光安定剤 [ビス（2, 2, 6, 6- テトラメチルー 4ーピペリジル)セバケート]を 0. 1質量部加えた以外、実施例 1と同様 にして太陽電池を製造した。
[0057] [実施例 2]
[EVA榭脂組成物配合 2 (質量部) ]
EVA榭脂： 100
(酢酸ビュル含有量 26重量0 /0、メルトフローレート 4gZlO分）
架橋剤 2 : 1. 3
(2, 5 ジメチルー 2, 5 ビス（t ブチルパーォキシ）へキサン）
架橋助剤（トリアリルイソシァヌレート）： 2. 0
紫外線吸収剤 1 : 0. 03
(2, 2 ジヒドロキシ一 4, 4 ジメトキシベンゾフエノン）
ヒンダードアミン系光安定剤 0. 1
[0058] [ビス（2, 2, 6, 6—テトラメチルー 4ーピペリジル）セバケート]
上記配合の EVA榭脂組成物を用いて、 80°Cでカレンダー成形して、 EVAフィルム
を成膜した。フィルムの厚さは 600 mであった。
[0059] 得られた EVAフィルムを表面側封止用 EVAフィルム 3A及び裏面側封止用 EVA フィルム 3Bとして用い、図 1に示すように、厚さ 3mmのガラス板 1、厚さ 38 μ mのフッ 化ポリエチレンフィルムよりなるバックカバー 2との間にシリコン発電素子 4を封止して 太陽電池を製造した。なお、封止は、真空ラミネーターで温度 150°C、脱気時間 3分 、プレス時間 15分間加熱圧着し、 EVAを架橋することにより行った。
[0060] [比較例 2]
EVA榭脂組成物配合 2において、紫外線吸収剤 1 (2, 2—ジヒドロキシ— 4, 4—ジ メトキシベンゾフエノン）を使用せず、その代わりに紫外線吸収剤 2 (2—ヒドロキシ一 4 ーォクチルォキシベンゾフエノン)を 0. 2質量部使用した以外、実施例 2と同様にして 太陽電池を製造した。
[0061] <上記太陽電池用封止膜の評価 >
(1)耐熱性 (耐熱 130°C耐久試験）
実施例及び比較例で得られた封止用 EVAフィルムを 2枚のフロートガラスに挟み、 真空ラミネータを用い、 90〜100°Cの温度、 2分の脱気時間及び 8分のプレス時間の 条件で予備成形を行い、次いで 150°Cに設定した耐熱オーブンで 45分間架橋させ た。
[0062] 得られた架橋 EVAフィルム（ガラスで挟まれたまま）を、 130°Cの環境下に 1000時 間保管し、保管による黄変の程度を調査するために、保管前後の YI値の差（ΔΥΙ値 )を求めた。
[0063] Δ YI値は、 JIS— K— 7105— 6 ( 1981年）に準拠して測定した。
[0064] (2)耐光性 (耐候性）（促進耐久性試験）
(1)と同様にして得た架橋 EVAフィルムを、 63°C、 50%RHの環境下で紫外線照 射 (条件 lOOmWZcm2)を 1000時間行 、、照射による黄変の程度を調査するため に、保管前後の YI値の差（ΔΥΙ値)を求めた。
[0065] ΔΥΙ値は、（1)と同様に測定した。
[0066] 得られた結果を下記に示す。
[0067] [表 1]
実施例 1 比較例 1 実施例 2 比較饲 2 配 EVA (VA:28%) 100 100 - - 合 EVA (VA:26 ) - ― 100 100 架橋剤 1 0.35 0.35 ― ―
架橘剤 2 ― - 1.3 1.3
架橘助剤 0.5 0.5 2.0 2.0
紫外線吸収剤 1 0.03 0.03 0.03 - 紫外線吸収剤 2 - - - 0.2
光安定期 - 0.1 0.1 0.1
評価結果
耐熱性 (ΔΥ I) 2.0 4.7 0.7 5.2 耐光性 （ΔΥ I) 1.1 1.3 0.2 3.8
[0068] 上記結果から明らかなように、本発明の封止膜は、本発明の特定の架橋剤と特定 紫外線吸収剤の組合せで、且つ特定の紫外線吸収剤又は光安定剤を使用しない条 件 (即ち、実施例 1では架橋剤 1を用いて、紫外線吸収剤 1を使用するが光安定剤は 使用しな ヽ；実施例 2では架橋剤 2を用いて、紫外線吸収剤 1を使用するが紫外線吸 収剤 2は使用しな 、条件)で、耐熱性及び耐光性 (耐久性)が格段に上昇して!/ヽる。 一方、比較例では、使用しない添加剤を用いた場合は満足な耐久性が得られていな い。
[0069] 従って、上記本発明の封止膜を有する太陽電池も、同様に耐熱性及び耐光性 (耐 久性）が格段に上昇している。
Claims
[化 1] o
!1
i_0 -0~C ~0 ~R2
[但し、 R1が炭素原子数 3〜5の分岐のアルキル基を表し、そして R2が炭素原子数 6 〜9の分岐のアルキル基を表す。 ]
で表されるパーォキシエステルを含み、且つ黄変防止のために、ジヒドロキシジメトキ シベンゾフエノン系紫外線吸収剤を含有し、ヒンダードアミン系光安定剤を実質的に 含有して!/、な 、ことを特徴とする太陽電池用封止膜。
[2] エチレン Z酢酸ビニル共重合体及び有機過酸化物を含む太陽電池用封止膜にお いて、
該有機過酸化物として、下記式 II：
[化 2]
R3 3
5-0-0-C-CH2-CH2~C-0-~0-R4
R3 R3
[但し、 R3が、それぞれ独立して炭素原子数 1〜3のアルキル基を表し、 R4が炭素原 子数 3〜5の分岐のアルキル基を表し、そして R5が炭素原子数 3〜5の分岐のアルキ ル基を表す。 ]
で表されるジアルキルパーオキサイドを含み、且つ黄変防止のために、ジヒドロキシ ジメトキシベンゾフエノン系紫外線吸収剤を含有し、モノヒドロキシアルコキシベンゾフ ヱノン系紫外線吸収剤を実質的に含有していないことを特徴とする太陽電池用封止
膜。
[3] R1が t—ブチルを表し、そして R2が 2—ェチルへキシル基を表す請求項 1に記載の 太陽電池用封止膜。
[4] ヒンダードアミン系光安定剤力 ビス（2, 2, 6, 6—テトラメチル一 4—ピペリジル）セ バケートである請求項 1又は 3に記載の太陽電池用封止膜。
[5] R3カ^チルを表し、そして R4及び R5カ^ーブチルを表す請求項 2に記載の太陽電池 用封止膜。
[6] モノヒドロキシアルコキシベンゾフエノン系紫外線吸収剤が 2—ヒドロキシ一 4—オタ チルォキシベンゾフヱノンである請求項 2又は 5に記載の太陽電池用封止膜。
[7] ジヒドロキシジメトキシベンゾフエノン系紫外線吸収剤力 2, 2—ジヒドロキシ一 4, 4 ージメトキシベンゾフヱノンである請求項 1〜6のいずれか 1項に記載の太陽電池用 封止膜。
[8] ジヒドロキシジメトキシベンゾフエノン系紫外線吸収剤を、エチレン/酢酸ビュル共 重合体 100質量部に対して 0. 01〜： L 0質量部含有している請求項 1〜7のいずれ 力 1項に記載の太陽電池用封止膜。
[9] 有機過酸化物を、エチレン Z酢酸ビュル共重合体 100質量部に対して 0. 1〜5. 0 質量部含有している請求項 1〜8のいずれか 1項に記載の太陽電池用封止膜。
[10] 架橋助剤を、エチレン Z酢酸ビニル共重合体 100質量部に対して 0. 1〜5. 0質量 部含有している請求項 1〜9のいずれか 1項に記載の太陽電池用封止膜。
[11] エチレン Z酢酸ビニル共重合体の酢酸ビニル単位が、エチレン酢酸ビニル共重合 体 100質量部に対して 10〜36質量％の範囲にある請求項 1〜10のいずれか 1項に 記載の太陽電池用封止膜。
[12] 表面側透明保護部材と裏面側保護部材との間に封止膜を用いて太陽電池用セル を封止してなる太陽電池において、該太陽電池用セルと裏面側保護部材との間に請 求項 1〜11のいずれか 1項に記載の太陽電池用封止膜を介在させ、架橋一体化さ れて!ヽることを特徴とする太陽電池。