WO2006114972A1 - 半導体光電極、その製造方法及び光エネルギ変換装置 - Google Patents

半導体光電極、その製造方法及び光エネルギ変換装置 Download PDF

Info

Publication number
WO2006114972A1
WO2006114972A1 PCT/JP2006/306465 JP2006306465W WO2006114972A1 WO 2006114972 A1 WO2006114972 A1 WO 2006114972A1 JP 2006306465 W JP2006306465 W JP 2006306465W WO 2006114972 A1 WO2006114972 A1 WO 2006114972A1
Authority
WO
WIPO (PCT)
Prior art keywords
semiconductor
semiconductor photoelectrode
metal substrate
photoelectrode according
metal
Prior art date
Application number
PCT/JP2006/306465
Other languages
English (en)
French (fr)
Inventor
Takashi Oi
Yasukazu Iwasaki
Kazuhiro Sayama
Original Assignee
Nissan Motor Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nissan Motor Co., Ltd. filed Critical Nissan Motor Co., Ltd.
Priority to EP06730413A priority Critical patent/EP1873277A4/en
Priority to US11/911,977 priority patent/US7961452B2/en
Publication of WO2006114972A1 publication Critical patent/WO2006114972A1/ja

Abstract

　本発明の半導体光電極は、表面に凹凸を有する金属基板と、前記金属基板の表面に作成され、光触媒作用を有する材料から成る半導体層と、を有する。これにより光の吸収効率を高め、さらに電荷の再結合を防止することができる。

Description

半導体光電極、その製造方法及び光エネルギ変換装置
技術分野
[0001] 本発明は、光エネルギによって水を分解して水素を生成する水素製造装置に適用 される半導体光電極、その製造方法及び半導体光電極を用いた光エネルギ変換装 置に関する。
背景技術
[0002] 太陽エネルギを有効利用するために、太陽エネルギを利用し易い形態に変換、貯 蔵する技術の開発が盛んに行われている。太陽電池はその代表例である力 コスト が高いことから普及が進んでおらず、より安価なシステムの開発が望まれている。
[0003] そこで、光触媒を利用して光エネルギをィ匕学エネルギに変換する技術の研究が進 められている。光触媒に太陽光を照射すると、光触媒は、光エネルギを吸収して電子 と正孔を生成し、化学反応を引き起こす。光触媒の中でも、特に、二酸化チタン (ΉΟ
2 )は価電子帯の位置が深いことから、生成した正孔による酸ィ匕カは、塩素あるいはォ ゾンよりも強いとされている。そのため TiOを半導体光電極として用いて、水を分解す
2
る方法が研究されている（A.Fujishima and K.Honda, Nature, 238(5358), 37(1972)参 照)。
[0004] これまで半導体光電極としては、 TiO単結晶あるいは TiO粉末を焼結してペレット
2 2
化した TiO焼結ペレットが使用されている。しかし TiO単結晶を使用すると、製造コス
2 2
トが高くなり、また、 TiO焼結ペレットを使用すると、光電変換効率が低くなつていた。
2
[0005] そこで、近年、導電性ガラスあるいは平滑な金属から形成される基板上に半導体層 を作成した半導体光電極が開示されている（J.Phys.Chem., 102(1998)7820及び J.Phy s.Chem.,98(1994)5552参照）。しかし、基板として導電性ガラスを使用すると、コストが 高くなり、さらに基板と半導体層との界面の密着性や安定性が低下してしまうことがあ る。したがって、基板として金属基板を用いた半導体光電極の開発が進められている
[0006] 図 11では、金属基板としてチタン板 (Ή板)を用いた半導体光電極 40を示している 。半導体光電極 40は、 Ti板を焼成して Ti板上に TiO層を作成し、これにより基板 41
2
上に半導体層 (TiO層） 42を作成している。このように Ti板を焼成してその表面に半
2
導体層 42 (TiO層）を作成すると、製造コストを削減でき、さらに半導体光電極をフレ
2
キシブルにできると 、う利点を有して 、た。
発明の開示
[0007] し力しながら、従来の金属基板を用いた半導体光電極の光電変換効率は、それほ ど高くない。そのため半導体層 (TiO層） 42を厚くすることで光の吸収効率を高め、
2
光電変換効率を向上させた半導体光電極も開発されている。
[0008] ところが、半導体層 42を厚くすると、半導体層 42中での電荷の移動距離が長くなり 、生成した電子と正孔とが再結合する割合が高くなる可能性があった。また、半導体 層 42中での電荷の移動速度は遅いため、電荷の移動距離が長くなると、光電変換 効率が低下する要因となっていた。さらに、図 11に示すように、従来の半導体光電極 40は、その表面が平坦であることから、入射光が反射すると光の吸収効率が低下す る要因となっていた。
[0009] 本発明は、上記課題を解決するためになされたものであり、その目的は、光の吸収 効率を高め、さらに電荷の再結合を防止した半導体光電極及びその製造方法、さら に光電変換効率を高めた光エネルギ変換装置を提供することにある。
[0010] 本発明の第一の態様に係る半導体光電極は、表面に凹凸を有する金属基板と、前 記金属基板の表面に作成され、光触媒作用を有する材料から成る半導体層と、を有 することを特徴とする。
[0011] 本発明の第二の態様に係る半導体光電極の製造方法は、表面に凹凸を有する金 属基板を作成する工程と、前記金属基板の表面に光触媒作用を有する材料から成 る半導体層を作成する工程と、を有することを特徴とする。
図面の簡単な説明
[0012] [図 1]図 1は、本発明の実施の形態に係る半導体光電極を示す拡大断面図である。
[図 2]図 2は、凹凸の間隔を説明するための図である。
[図 3]図 3は、半導体光電極に用いられる金属基板を示す平面図である。
[図 4]図 4は、本発明の実施の形態に係る半導体光電極を用いた水素製造装置の構 成を示す概略図である。
[図 5]図 5は、図 4に示す水素製造装置により水を分解する動作原理を説明する図で ある。
[図 6]図 6は、実施例及び比較例において使用した三電極系の実験装置の構成を示 す図である。
[図 7]図 7は、実施例 4及び実施例 5において使用した Ή板を示す図であり、（a)は、 Ti 板の上面図であり、（b)は、（a)に示す Ti板の A—A'断面図である。
[図 8]図 8は、実施例 1〜実施例 3及び比較例 1〜比較例 3につ 、ての光電流値の測 定結果を示すグラフである。
[図 9]図 9は、実施例 4、実施例 5及び比較例 3についての光電流値の測定結果を示 すグラフである。
[図 10]図 10は、実施例 6及び比較例 4についての光電流値の測定結果を示すグラフ である。
[図 11]図 11は、従来の半導体光電極を示す拡大断面図である。
発明を実施するための最良の形態
[0013] 本発明の実施の形態に係る半導体光電極、その製造方法及び半導体光電極を用
Vヽた光エネルギ変換装置にっ 、て説明する。
[0014] (半導体光電極）
図 1では、本発明の実施の形態に係る半導体光電極 1の表面状態を示す。半導体 光電極 1は、表面に凹凸を作成して高表面積とした金属基板 2と、金属基板 2表面に 作成された半導体層 3と、を備える。
[0015] 金属基板 2表面の凹凸は、できるだけ平均的に、かつ溝を深く作成することが好ま しい。具体的には、金属基板 2表面の算術平均粗さ（Ra)を 1 μ πι〜4 /ζ mの範囲とす ることが好ましい。この理由は、この範囲にすることで一層高い光電流値が得られるた めである。なお、金属基板 2表面の算術平均粗さ（Ra)は、粗さ計 (テンコール製アル ファステップ)を用いて、以下に示す数式から求めた値である。数式 1中の 1は基準長 さ、 x)は金属基板 2表面の形状の粗さに沿う曲線を示す。
[数 1] 1 c i ,
Ra= - J ( x
[0016] また、最大高さ（Ry)は、 1〜500 μ mの範囲とするのが好ましぐさらに 3〜200 μ m の範囲とすることが好ましい。ここで、最大高さ (Ry)とは、凹凸形状の平均線と最大 凸部の距離 (X)と、凹凸形状の平均面と最小凹部の距離 (y)との合計値 (x+y)を意 味する。なお本明細書にぉ 、て、算術平均粗さ（Ra)及び最大高さ（Ry)は、 JIS BO 601 (ISO 4287)に従!ヽ、求めること力できる。
[0017] さらに凹凸の間隔は 500 μ m以下で、できるだけ緻密であることが望ましい。ここで 凹凸の間隔とは、図 2に示すように、表面の粗さ曲線 33において、隣接する凸部の 間隔 34を示す。なお図 2中の参照符号 32は、平均線を示す。
[0018] 金属基板 2としては、元素の単体又はその元素の複合物（酸化物、窒化物、ホウィ匕 物、酸窒化物、硫化物、酸硫ィ匕物など）を用いることができる。これらの材料は、光触 媒特性又は光電極特性を示すことができる。具体的には、 Ti、 Nb、 Ta、 W、 V、 Co、 Fe 、Ni及び Inの中力 選択される少なくとも 1種以上の元素及びその複合物を金属基板 として用いることが好ましい。
[0019] 半導体層 3としては、光触媒作用を有する材料を用いることができる。具体的には、 TiO、 Nb 0、 Ta 0、 WO、 V 0、 InCuTaO、 InNiTaO、 InCoTaO、 InFeTaO、 InMn
2 2 5 2 5 3 2 5 4 4 4 4
TaO、 InTaO、 InNbTaO、 SrTiO、 TaONまたは TiO： N (窒素をドープしたチタ-ァ）
4 4 4 3 2
を挙げることができる力 例示した材料に限定されるものではない。また半導体層 3の 材料は、金属基板 2を形成する金属の化合物と異なるようにしてもかまわな ヽ。
[0020] 半導体層 3の厚さは、 0. 1 m〜l μ mの範囲とすることが好ましい。半導体層 3の 厚さが 0.： L m未満となり薄くなりすぎると、光の吸収効率が低下する。逆に、その厚 さ力 mを超えると電荷の移動距離が長くなるため、電荷の移動が遅くなつたり、電 荷が再結合してしまうからである。
[0021] このように半導体光電極 1の表面に凹凸を作成すると、入射光 4だけでなく散乱光 5 をも半導体層 3により吸収することができる。このため、半導体層 3の厚さを薄くしても 光の吸収効率が低下することはない。また、半導体層 3の厚さを薄くすると、電荷の移 動距離が短くなり、電荷はすぐに金属基板 2に到達する。金属基板 2中の抵抗は小さ いため、電荷は金属基板 2内を高速で移動することになる。また、従来の電極に比べ て、半導体層 3の実質的な表面積が広くなるため、半導体層 3中の電荷密度を低くす ることができる。この結果、半導体層 3での電荷の再結合を防止することができる。
[0022] (半導体光電極の製造方法）
次に、本発明の実施の形態に係る半導体光電極の製造方法を説明する。
[0023] まず、表面に凹凸を有する金属基板 2を作成する。凹凸の作成法としては、金属板 を機械的研磨した後、化学エッチング処理をする方法を用いることができる。この時、 最大高さ（Ry)は 1 μ m〜500 μ m、さらに 3 μ m〜200 μ mとすることが好ましぐまた 、凹凸の間隔は 500 m以下として、凹凸の間隔を狭くすることが好ましい。また凹凸 の作成法としては、金属板を研磨紙等を用いて粗研磨することにより作成しても良い
[0024] また金属基板 2としては、図 3に示すように、金属粒子 36を圧力または熱により接合 することにより成る、表面に凹凸を有する多孔質体を用いることもできる。この時に使 用する金属粒子 36の粒径 (D50)は 1 m〜400 μ m、好ましくは 3 μ m〜200 μ m の範囲とすることが好ましい。なお、接合する際の圧力や熱は、金属粒子の種類や粒 径に応じて変えることが好ま 、。このように圧力や熱により金属粒子を接合すると、 金属粒子間の界面のネッキング成長が進行して電気的な接触が良くなり、さらに機 械的強度に優れた金属基板 35とすることができる。なお図 3の金属基板 35は、金属 粒子 36が縦横とも整然と配列されているが、本発明の金属基板はこれに限らず、金 属粒子を圧力または熱により接合することにより成る、あらゆる多孔質体を用いること ができる。
[0025] なお、粒子の大きさを測定するものとして、大きさの分布 (範囲と含有率)を測定す る粒度分布がある。粒度分布は、一般には目開きの異なるいくつかのふるいを用い て、その目開きを通過する割合を測定し、（積算)重量百分率で表す。本発明で用い る金属粒子は、数/ z mレベルのため、一般の粒度分布計を用いて測定し、積算値 50 %の粒度を「粒径 (D50)」とする。 [0026] 次に、得られた金属基板 2上に半導体層 3を作成するが、半導体層 3は使用する原 材料に応じてその製造方法が異なる。
[0027] 半導体層 3が単純酸ィ匕物力も成る場合には、酸化雰囲気下 (空気中、酸素中）にお V、て、単純金属から成る金属基板を焼成あるいは電解酸化する。
[0028] 半導体層 3が単純金属の窒化物若しくは硫ィ匕物力 成る場合には、非酸化雰囲気 下 (アンモニア、窒素、硫化水素など）において、単純金属から成る金属基板を加熱 あるいはプラズマ処理をする。例えば Ta5+、 Ti4+などの d型の電子配置を有する遷移 金属イオンを含むォキシナイトライド (例えば、 TaON)、窒素をドープした半導体 (例え ば、 ΉΟ： N)、ォキシサルファイドなど力も成る半導体層 3の場合には、単純金属から
2
成る金属基板を一度部分酸化した後に窒化処理あるいは硫化処理をするか、又は 窒化処理あるいは硫化処理をした後に部分酸化することにより得られる。
[0029] 半導体層 3が複合金属半導体から成る場合には、金属基板 2上に複合金属前駆体 を塗布し、その後、酸化、窒化又は硫ィ匕のいずれかの処理を行い、半導体層 3を作 成する。
[0030] 上記半導体層 3を作成した後、後処理として、酸化、水素還元、水蒸気によって処 理をしてもよい。後処理をすると半導体層 3中の格子欠陥を減少あるいは増やすこと ができる。なお、半導体層 3中の格子欠陥を増やすと導電性が高くなる。
[0031] (水素製造装置）
本発明の半導体光電極を用いた水素製造装置 6の構成を図 4に示す。水素製造 装置 6では、水槽 7内に半導体光電極 8 (作用極）と対極 9 (例えば、 Pt電極、カーボ ン電極)とを個別に配置し、さらに半導体光電極 8と対極 9を配置した水槽 7の中間位 置にイオン交換膜 12を取り付けている。さらに半導体光電極 8と対極 9に導線を接続 することにより外部短絡線 10を作成する。また、水槽 7内には電解反応の溶液抵抗を 下げるために安定な支持電解質を含む電解液 11 (例えば、 Na SO水溶液)を貯留し
2 4
ている。本構成の水素製造装置 6では、半導体光電極 8に太陽光 13を照射して水の 電解を行う。
[0032] 対極 9の材料は、反応に合わせたものを選択することができる。水素を発生させるた めには、水素発生の過電圧の低い Pt電極及びカーボン電極が有効である力 安価 な Co-Mo電極を用いても良い。支持電解質としては、一般的な電解反応の電解質と して使用される NaOH、 Na SO、 H SO及び Na HPOを用いることができる。支持電解
2 4 2 4 2 4
質の濃度は、電解の過電圧を低下させるために高濃度にすると良ぐ 0. Olmol/L 以上とすることが好ましい。また、光触媒が容易に分解できる還元性の反応物 (例え ば、有機物、硫化水素、ヨウ素イオン)を電解液 11中に含有させても良ぐこれにより 光電変換効率が高めることができる。特に、本願発明のように金属基板に凹凸を設け ると、光触媒 (半導体層）と反応基質との反応面積が広くなるため、光散乱の影響を 受けにくくなる。このため、従来の電極に比べて飛躍的に光電変換効率が高くなる。 なお、図 4には図示しないが、外部短絡線 10にポテンシヨスタツト又はソースメータを 設置してバイアス電位を制御しても良い。また、電極の性能をチェックする場合ゃ特 殊な化学反応を起こす場合には、太陽光 13ではなく人工光源 (例えば、キセノンラン プ）を適用しても良い。
[0033] 次に、図 4に示した水素製造装置 6により水を分解する動作原理を図 5により説明 する。半導体光電極 8に太陽光 13を照射すると、図 5に示すように、半導体光電極 8 に光が吸収されて、伝導帯に電子 16が生成し、価電子帯に正孔 14が生成する。半 導体光電極 8の表面に移動した正孔 14は、式 1に示す反応により、水を酸化して酸 素 15を生成する。
[0034] H 0→2H+ + l/20 + 2e" (式 1)
2 2
一方、生成した電子 16は、半導体光電極 8中の金属基板 2に移動した後、外部短 絡線 10を通り対極 9に移動する。この電子（e_)は、対極 9上で水を還元し、式 2に示 す反応により、水素 17を生成する。
[0035] 2H + 2e"→H (式 2)
2
この結果、水が分解されて、半導体光電極 8 (作用極)では水素、対極 9では酸素が それぞれ生成する。
[0036] なお、ここでは、本発明の実施の形態に係る半導体光電極を用いて水素製造装置 6を構成した例を挙げたが、半導体光電極は水電解装置に限定されず、色素増感型 太陽電池などの光エネルギ変換装置として適用することもできる。
[0037] 以下、実施例を用いてさらに具体的に説明する。各実施例では、異なる製造方法 を用いて製造した、異なる構成の半導体光電極を用いて、図 6に示す三電極系の実 験装置に適用した実験を行った。図 6に示す三電極系の実験装置 18は、水槽 19内 に、作用極である半導体光電極 20と、対極である Pt電極 21とを配置し、半導体光電 極 20と Pt電極 21とに外部短絡線 22を接続して導通させている。また、別の水槽 23 内に、作用極の電位を設定及び制御するための基準電極となる参照極を配置してお り、この参照極として銀-塩化銀電極 (Ag-AgCl電極） 24を用いている。 2つの水槽 19 ,23はバイコールガラスフリット 25により接続されて、半導体光電極 20と Pt電極 21と の間の電気的な導通を保っている。半導体光電極 20と Pt電極 21とを接続する外部 短絡線 22には電流計 26を設置し、回路を流れる光電流値を計測している。さらに、 外部短絡線 22にポテンシヨスタツト 27を設置し、ポテンシヨスタツト 27と Ag-AgCl電極 24とを外部短絡線 28により接続している。ポテンシヨスタツト 27は、電位に応じて電 流を流し、半導体光電極 20と Ag-AgCl電極 24との間の電位差をコントロールして!/ヽ る。水槽 19内には、濃度 0. lmol/Lの Na SO水溶液を貯留している。この Na SO水
2 4 2 4 溶液は、半導体光電極 20と Pt電極 21とに電位差が生じた場合に回路中の電荷移動 を担う役割を果たしている。
[0038] 半導体光電極 20が配置された水槽 19の外部には、キセノンランプ（500W) 29を 配置し、キセノンランプ 29と半導体光電極 20との間にチヨッパ 30を設置している。チ ョッパ 30により半導体光電極 20に照射する光の ON、 OFFを一定間隔で切り替えて いる。
[0039] (実施例 1〜実施例 3)
実施例 1〜実施例 3では、金属基板 2として、平均粒径 45 mの Ti金属粒子を加熱 及び加圧することによりネッキングして作成した Ti多孔質体を使用した。 Ti多孔質体 の算術平均粗さ（Ra)は約 2 μ mであり、最大高さ（Ry)は約 5 μ mであった。
[0040] この Ti多孔質体を空気雰囲気下において 500°C〜700°Cの範囲で温度を変えて、 1時間熱処理をした。熱処理温度として、実施例 1では 500°C、実施例 2では 600°C 、実施例 3では 700°Cとした。熱処理により Ti多孔質体表面を酸化して TiO層を作成
2 した。
[0041] X線回折 (XRD)により構造を同定したところ、 TiOはルチル型であることが判明し た。また、断面 SEM分析の結果から、熱処理温度が高くなるに従い、 TiO層の厚さ
2 が増大していた。 TiO層の厚さは、測定場所に応じてばらつきがあるものの、実施例
2
1は 100nm、実施例 2は 200nm、実施例 3は 600 mであった。
[0042] (比較例 1〜比較例 3)
比較例 1〜比較例 3では、実施例 1〜実施例 3により使用した Ti多孔質体に替えて Ti平板を用いた。 Ti平板の算術平均粗さ（Ra)は 0. 2 μ m〜0. 3 μ mであった。また Ti平板表面には大きな凹凸が作成されず、最大高さ（Ry)は 1 μ m未満であった。な お、 Ti平板を使用した以外は、実施例 1〜実施例 3に示した製造方法と同様の方法 を用いて、半導体光電極を製造した。 TiO層の厚さは、測定場所に応じてばらつき
2
があるが、比較例 1は 100nm、比較例 2は 200nm、比較例 3は 600 mであった。
[0043] (実施例 4、実施例 5)
実施例 4、実施例 5では、金属基板 2として、 Ti平板をフォトレジストマスクにてパタ ーンユングしたものをエッチング処理して、表面に凹凸を作成した Ti板 31を使用した 。 Ti板の表面は、図 7 (a)に示す形状とした。また、図 7 (a)に示す Ti板表面の A— A' 断面図を図 7(b)に示した。実施例 4では、図 7(b)に示す X, Yをそれぞれに 5 m, 7 0 mとし、実施例 5では、 X, Yをそれぞれ 40 m, 70 mとした。実施例 4及び実 施例 5の Ή板の算術平均粗さ（Ra)を測定したところ、実施例 4は 3. O ^ m,実施例 5 は 3. 3 ！11で&)った。
[0044] 得られた Ti板を、空気雰囲気下にて 700°Cの温度で 1時間熱処理し、 Ti板表面を 酸化して TiO層を作成した。 TiO層の厚さは、測定場所に応じてばらつきがあるが、
2 2
実施 f列 4ίま 600 μ m、実施 f列 5ίま 600 μ mであった。
[0045] (実施例 6)
実施例 6では、まず WOの水和コロイドを調製した。 WOの水和コロイドは、イオン
3 3
交換榭脂を用いて Na WO水溶液中の Na+イオンをプロトン交換することにより調製し
2 4
た。この水和コロイド水溶液を等量エタノールと混合した後、減圧蒸留（60°C)して、 その体積を 1/4に減少させた。その後、 1/2量のポリエチレングリコール 300 (和光 純薬製)を加えてスターラを用いて混合し、 WOをコロイド状としたスラリーを得た。
3
[0046] 得られたスラリーを実施例 1で使用した Ti多孔質体上に塗布した後、 500°Cで 1時 間熱処理することにより、 Ti多孔質体上に WO層を作成した。なお WO層は粒子の
3 3
集合体で凹凸はあるが一様の厚さでないため層厚は測定できな力つた。
[0047] (比較例 4)
比較例 4では、実施例 6により製造したスラリーを用いて、このスラリーを比較例 1で 使用した Ti平板上に塗布した後、 500°Cで 1時間熱処理をして、 Ti平板上に WO層を
3 作成した。なお WO層は粒子の集合体で凹凸はあるが一様の厚さでないため層厚は
3
測定できな力つた。
[0048] 実施例 1〜実施例 6及び比較例 1〜比較例 4の各半導体光電極について、光電流 測定試験により光電流値を測定した。測定結果を表 1に示す。
[表 1] 金属基板 半導体層
光電流値 算術平均粗さ ( Ra) 最大高さ （Ry) 厚さ ( μ A ) ( μ m ) m ) V μ m )
実施例 1 2 . 0 5 . 0 0 . 1 1 2 0 実施例 2 2 . 0 5 . 0 . 2 3 2 0 実施例 3 2 . 0 5 . 0 . 6 4 0 0 実施例 4 3 . 0 1 0 . 0 0 . 6 3 0 0 実施例 5 3 . 3 8 . 8 0 . 6 3 2 0 比較例 1 0 . 2 ^ 0 . 3 1未満 0 . 1 8 0 比較例 2 0 . 2 - 0 . 3 1未満 0 . 2 9 5 比較例 3 0 . 2 ^ 0 . 3 1未満 0 . 6 1 4 0 実施例 6 2 . 0 5 . ― 5 5 0 比較例 4 0 . 2 ' ^ 0 . 3 1未満 ― 3 1 0
[0049] なお、光電流測定試験は、参照極に対する半導体光電極の電位を 0.05 V/sの操 作速度で変化させるポテンシャルスイープ法を用いた。この結果、半導体光電極に 光を照射した場合のみ、 Ag/AgCl基準で 0 V付近カゝら水の分解に伴う光電流が確認 された。なお、以下、電位は Ag/AgClを基準として標記する。
[0050] 光電流値を測定したところ、電圧が貴になるに伴い光電流値の値は徐々に増加し ていた。実施例 1〜実施例 3及び比較例 1〜比較例 3について、 0.8 Vとして光電流 値を測定した結果を図 8に示す。図 8に示すように、実施例及び比較例の両者ともに 、熱処理温度が高くなるに伴い ΉΟ層が厚くなるため、光吸収特性が高まり、光電流
2
値が増大することが判明した。また、同一温度で熱処理した場合には、比較例に比 ベて実施例の光電流値は、いずれも約 1. 5倍〜 3. 0倍の高い光電流値を示してい た。これは、 Ti平板を使用した比較例 1〜比較例 3に比べて、 Ti多孔質体を使用した 実施例 1〜実施例 3では、半導体光電極表面に凹凸が作成されているため、散乱光 をも吸収することができるからである。また、半導体層の実質的な表面積を広げ、半 導体層中の電荷密度を低くすることにより、電荷の再結合を防ぐこともできるからであ る。さら〖こ、電子は半導体層よりも金属基板中を移動すると、抵抗が小さく有利である ため、金属基板を大面積化すると、半導体層から金属基板までの電荷の移動距離を 短くできる力 である。
[0051] 次に、実施例 4、実施例 5及び比較例 3につ 、て、光電流値を測定した結果を図 9 に示す。図 9に示すように、表面に凹凸を作成した Ή板を使用した実施例 4及び実施 例 5は、 Ti平板を使用した比較例 3に比べて、光電流値は約 2倍増加していることが 判明しており、前述した実施例 1〜実施例 3と同様に、金属基板に凹凸を設けること が有効な手段であることが示された。
[0052] さらに、実施例 6及び比較例 4について、光電流値を測定した結果を図 10に示す。
なお、実施例 6及び比較例 4では、 WOの光吸収特性のみを切り分けて考えるため
3
に、 TiOの光吸収波長ではなぐ WOの光吸収波長である 420nm以上の光のみを
2 3
照射して、光電流値を測定した結果を示す。図 10に示すように、多孔質体を用いた 実施例 6の方が平板を用いた比較例 4に対して光電流値が約 1. 8倍であり、多孔質 体と平板とで有意な差が現れた。表面に凹凸を作成した半導体光電極は、表面を平 坦とした半導体光電極に比べて光吸収特性が良いという事実は、金属基板を酸ィ匕し て得た金属酸ィ匕物を光触媒とする光電極のみではなぐ凹凸を作成した金属基板上 にその金属の酸ィ匕物とは異なる光触媒を作成した場合でも成り立つことが判明した。
[0053] 以上、本発明の詳細について述べてきたが、本発明の思想に合致するものであれ ば、これらの構成及び文言に限定されるものではない。例えば、実施例 1では、 Ti多 孔質体を焼結したものを基板として使用したが、平板上に Ti多孔質体を作成して最 表面に凹凸を形成した半導体光電極を用いても良い。また、本発明の実施の形態で は、金属基板上に光触媒を担持する方法として、ペースト状とした光触媒を金属基板 上に塗布した後、熱処理をする方法を示したが、この方法に限定されず、物理蒸着 法または化学蒸着法を用いて、金属基板上に光触媒を担持しても良い。
[0054] さらに、図 4に示した水素製造装置 6では、半導体光電極 8と対極 9との間に電位を 印加するデバイスを設置していない。しかし外部短絡線 10上に電圧印加用のデバィ スを設置した構成としても良ぐまた、 2つの水槽 7間で pHの差をつけて濃度のバイ ァスをかける構成としても良!、。
[0055] また、本発明ではホールにより酸ィ匕される物質として水を例に挙げた力 酸化される 物質は水に限定されず、例えば、工場廃水など有機物を含む電解質を用いてその 有機物を犠牲試薬として酸化することも考えられる。さらに実施例 4及び実施例 5で は、表面に凹凸を作成する方法として化学エッチング法を挙げたが、これに限定され ず、イオンエッチング、 LIGAプロセス若しくは陽極酸ィ匕により、表面に凹凸を作成し ても良い。
産業上の利用の可能性
[0056] 本発明の半導体光電極によれば、光の吸収効率を高め、さらに電荷の再結合を防 止することができる。本発明の半導体光電極の製造方法によれば、表面に凹凸が作 成されて表面積を高めた半導体光電極を容易に製造することができる。また本発明 の光エネルギ変換装置によれば、光の吸収効率が高ぐさらに電荷の再結合を防止 できる半導体光電極を用いたため、光電変換効率を高めることができる。

Claims

請求の範囲
[I] 表面に凹凸を有する金属基板と、
前記金属基板の表面に作成され、光触媒作用を有する材料から成る半導体層と、 を有することを特徴とする半導体光電極。
[2] 前記金属基板の表面における算術平均粗さは、 1 μ m〜4 μ mの範囲であることを 特徴とする請求項 1に記載の半導体光電極。
[3] 前記光触媒作用を有する材料は、 Ti、 Nb、 Ta、 W、 V、 Co、 Fe、 Ni及び Inの中力 選 択される少なくとも 1種以上の元素を含むことを特徴とする請求項 1に記載の半導体 光電極。
[4] 前記半導体層の厚さは、 0. 1 m〜l μ mの範囲であることを特徴とする請求項 1に 記載の半導体光電極。
[5] 前記光触媒作用を有する材料は、前記金属基板を形成する金属の化合物と異なる ことを特徴とする請求項 1に記載の半導体光電極。
[6] 前記金属基板は、金属粒子を接合することにより成る多孔質体であることを特徴と する請求項 1に記載の半導体光電極。
[7] 前記金属粒子の粒径は、 1 μ m〜400 μ mの範囲であることを特徴とする請求項 6 に記載の半導体光電極。
[8] 前記金属粒子の粒径は、 3 μ m〜200 μ mの範囲であることを特徴とする請求項 7 に記載の半導体光電極。
[9] 表面に凹凸を有する金属基板を作成する工程と、
前記金属基板の表面に光触媒作用を有する材料から成る半導体層を作成するェ 程と、
を有することを特徴とする半導体光電極の製造方法。
[10] 前記金属基板の表面における算術平均粗さは、 1 μ m〜4 μ mの範囲であることを 特徴とする請求項 9に記載の半導体光電極の製造方法。
[II] 前記金属基板は、複数の金属粒子を圧力または熱により接合することにより作成さ れることを特徴とする請求項 9に記載の半導体光電極の製造方法。
[12] 前記金属粒子の粒径は、 1 μ m〜400 μ mの範囲であることを特徴とする請求項 1 1に記載の半導体光電極の製造方法。
[13] 前記金属粒子の粒径は、 3 μ m〜200 μ mの範囲であることを特徴とする請求項 1
2に記載の半導体光電極の製造方法。
[14] 前記金属基板の表面における凹凸は、粗研磨若しくは化学エッジング法により作 成されることを特徴とする請求項 9に記載の半導体光電極の製造方法。
[15] 前記半導体層は、前記金属基板と気体とを化学反応させることにより作成されること を特徴とする請求項 9に記載の半導体光電極の製造方法。
[16] 前記化学反応は、酸化、窒化及び硫ィ匕の 、ずれかであることを特徴とする請求項 1
5に記載の半導体光電極の製造方法。
[17] 前記半導体層は、前記金属基板の表面に光触媒作用を有する材料を含むスラリー を塗布した後、熱処理することにより作成されることを特徴とする請求項 9に記載の半 導体光電極の製造方法。
[18] 請求項 1に記載の半導体光電極を用いた光エネルギ変換装置。
[19] 請求項 1に記載の半導体光電極を用いた水素製造装置。
PCT/JP2006/306465 2005-04-21 2006-03-29 半導体光電極、その製造方法及び光エネルギ変換装置 WO2006114972A1 (ja)