Classifications

• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F27—FURNACES; KILNS; OVENS; RETORTS
  • F27D—DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
  • F27D3/00—Charging; Discharging; Manipulation of charge
  • F27D3/14—Charging or discharging liquid or molten material
  • F27D3/145—Runners therefor
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B22—CASTING; POWDER METALLURGY
  • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
  • B22D35/00—Equipment for conveying molten metal into beds or moulds
  • B22D35/06—Heating or cooling equipment
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21B—MANUFACTURE OF IRON OR STEEL
  • C21B7/00—Blast furnaces
  • C21B7/14—Discharging devices, e.g. for slag
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F27—FURNACES; KILNS; OVENS; RETORTS
  • F27D—DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
  • F27D3/00—Charging; Discharging; Manipulation of charge
  • F27D3/14—Charging or discharging liquid or molten material

Definitions

• the invention relates to a launder used in manufacturing and casting molten metal, such as copper.
• the manufacture of copper includes a stage, where copper anodes are cast from coarse copper in casting equipment for the electrolytic cleaning of copper.
• the copper is directed and dosed from a melting furnace to a casting machine through launders and troughs.
• the launders which are provided with steel jackets, are lined with refractory material and they are open launders or launders provided with covers.
• the launders are installed at a suitable inclination so as to effect the flow of melt by means of gravity.
• troughs such as a stabilizing trough, are needed, the melt being poured into the stabilizing trough from the melting furnace and the movement of the molten metal being stabilized therein before directing it to the launders.
• the melt launders When increasing the capacity of the casting equipment, the melt launders must be rendered ever longer, causing a bigger problem with cooling and solidification of copper in the launders than before.
• the molten flow of the melt is prevented and the molten metal flows over the launder.
• the molten copper is heated to a sufficiently high temperature in a melting reactor so that the temperature of the molten metal keeps the metal running and the launder hot up to the casting machine.
• the launders are lined with refractory material, its wear being directly proportional to the temperature of the metal that is conveyed: the higher the temperature of the melt, the quicker the lining of the launders wear. Naturally, this brings about extra maintenance costs.
• the solidification of the melt in the launders is especially probable at the initial stage of casting, when the launders are still cold.
• the launders and troughs cool quickly, whereby the molten metal in them solidifies.
• the flow of molten metal in the troughs and launders may be interrupted or reduced to the extent that the metal solidifies and the entire launder system should be serviced before continuing the casting or beginning a new casting.
• the purpose of the present invention is to eliminate the problems of prior art and to provide an improved launder construction for the transfer of molten metal.
• Another purpose of the invention is to provide a launder and trough construction, which is used to transfer molten metal from the melting furnace to the casting machine reliably and tolerant to interruptions in casting.
• the objective is a reliable transfer of copper from the anode furnace to the casting machine of the anodes.
• the solution according to the invention to the problems of the prior art is based on the fact that a cover that is provided with electrical resistors is arranged in the melt launder construction, its launders and troughs, heating the launder and the troughs, where the copper flows, and on the fact that the chimney effect that is created in the launder provided with the cover is limited by the stagnation pressure generated at the upper end of the covered launder portion.
• the heating covers according to the invention can be fitted to be used, for example, in the molten metal launders, the intermediate troughs, from which the melt is dosed into casting troughs, and the casting troughs, from which the melt is dosed into the casting moulds.
• the invention provides considerable advantages.
• the invention enables the heating of the launder construction with less power compared with traditional burner solutions.
• the heat production is easy to adjust and local thermal stress is avoided, whereby the cracking of the launder embeddings is also avoided.
• the tendency to downtime of the casting equipment is reduced, as the casting can be interrupted without a risk of the metal solidifying in the launders and troughs.
• the invention extends the working life of the embeddings of the troughs and the launders and especially of the anode furnace.
• molten metal such as molten copper
• molten metal is arranged to flow under gravity in an inclined launder that is lined with refractory material and has a metal jacket, and at least part of the launder and the troughs is covered with an insulating cover.
• At least one electrical resistor element is arranged in the cover of the launder to heat the launder and to keep the metal melted, and a burner of a hot gas blower is arranged at the upper end of the covered launder portion to provide a stagnation pressure in the launder channel to decelerate the flowing gas or to prevent it from flowing or even make it flow downwards.
• the covers that are arranged on top of the troughs are used during casting and during the periods between castings and during any breaks in casting.
• the covers of the troughs are easy to fit in place and remove because of their light structures.
• the heating elements can be placed in the cover of the troughs so that the heating elements extend to the area in the pit of the trough, where the melt flows during the process.
• the lower part of the launder in the launder construction according to the invention comprises the launder itself, wherein the molten metal flows.
• the cross section of the launder's space for the melt is, for example, a U-shape that opens and widens upwards.
• the inner surface of the launder, which is in contact with the molten metal is defined by refractory material, such as a ceramic wearing composition.
• a suitable material is a refractory, castable mortar.
• the refractory material forms a flow channel for the molten metal, which is preferably an upward- widening groove that has a rounded bottom.
• the outer shell of the launder is preferably made of metal, such as steel.
• the steel shell serves as a mould and facilitates the transportation to the installation site.
• the launder construction according to the invention comprises a metal shell, such as a steel jacket, which forms the outer surface of the launder bottom, a refractory lining, which defines a flow channel for the molten metal, and an insulating layer that is arranged between the refractory lining and the metal shell, the insulating layer being considerably better in heat insulation than the refractory lining.
• a metal shell such as a steel jacket
• a refractory lining which defines a flow channel for the molten metal
• an insulating layer that is arranged between the refractory lining and the metal shell, the insulating layer being considerably better in heat insulation than the refractory lining.
• the temperature of the copper that flows in the launder is within a range of 1080 to 1300 0 C.
• the refractory lining of the flow channel of the launder construction is preferably made so thick that the temperature of the outer surface of its bottom is within a range of 700 to 900 0 C in an operating state, where there is copper flowing in the launder.
• the copper to be cast, which flows in the launder solidifies at ca. 1070 0 C.
• the molten copper penetrates the porous refractory lining and solidifies therein, forming a fixed layer of copper in the lining in a place, where the temperature is in the area of the solidification point of copper.
• the refractory lining so thick and to arrange the heat insulation of the launder so that, in the operating state, the temperature range that corresponds to the solidification point of copper is inside the refractory lining.
• molten aluminium, zinc or metal alloy flows in the launder, whereby the insulations of the launder are constructed to correspond to the melting temperatures of these metals.
• the refractory lining of the launder is a separate element, which can be detached as an integral part and replaced so that the thermal insulation and/or the steel shell keeps installed in place.
• ceramic wool separates the compound from the steel jacket and makes it easy to replace the compound.
• the compound is anchored to the steel shell by means of fastening members, such as screws. The anchoring screws are screwed to the nuts, which have been cast in the compound, through the steel shell and the wool insulation.
• the preferred temperature gradient described above is provided for the refractory lining, for example, by suitably selecting the thickness and the thermal insulation capacity of the insulation layer that is arranged between the refractory lining of the launder construction and the outer shell.
• a particularly preferred insulation material for the said insulating layer is ceramic wool insulation. The significance of the insulating layer is essential, as without it, the losses of heat are too great and the power required by the heating resistor will melt the resistor itself. On the other hand, if the insulation is too good, the molten metal, such as copper, is allowed to infiltrate through the ceramic refractory compound and the launder will leak.
• the cover of the launder construction according to the invention is arranged on top of the launder so that no significant amounts of gases are able to discharge to the outside from between the cover and the launder, and no losses of heat will occur through radiation or gas flows.
• the surfaces of the cover and the launder, which are placed against each other, are preferably essentially even, whereby the launder supports the cover continuously at its long edges essentially throughout its length.
• the cover of the launder construction comprises a metal cover, such as a steel jacket; at least one electrical resistor, which is arranged so as to heat the lower part of the launder; and a insulating layer to prevent the loss of heat by radiation through the metal shell.
• the heating resistor(s) is (are) located above the flow channel of the launder so that the heat from the resistors radiates essentially without obstruction on the metal, which flows on the bottom of the launder, and on the refractory lining.
• the electrical resistors are heated to 1100 - 1300 0 C.
• the heat insulation is preferably made of ceramic wool insulation, whereby the insulation may comprise one or more layers of lining.
• the wool insulation in the cover and the launder preferably comprises aluminium silicate wool, magnesium silicate wool, or aluminium oxide wool, which endures high temperatures.
• the heating resistors are thick enough, whereby any creeping and bending caused by the heat are minor.
• the heating resistor preferably consists of a metal rod or pipe with a round diameter.
• One or more heating resistors can be arranged in the cover to travel side by side in the longitudinal direction of the launder.
• the resistors are preferably selected so as to have their operating voltage in the so- called safety voltage area.
• the resistors are preferably fitted in the cover part on so-called supporting cross-arms, which are arranged in the longitudinal direction of the launder transversely under the resistors.
• the supporting cross-arms can be metal rods or pipes that are coated with ceramic refractory material.
• the cover portion covers part of the launder construction.
• the superimposed cover and launder constitute a launder channel.
• a gas burner or a hot gas blower is arranged in this place, providing a stagnation pressure to limit or prevent the gas flow that discharges from the launder.
• the hot gas of the burner or the blower is directed towards the opening between the cover and the lower part, whereby the effect of the stagnation pressure becomes the strongest.
• the fuel of the burner can be, for example, natural gas or liquid gas.
• the hot gas burner may be even electrically heated.
• thermoelement installed at the lower end of the launder channel.
• the thermoelement indicates the temperature of the gas space at the lower end of the launder channel and the cooling effect of the cool air flowing into the launder channel.
• a power control for the heating resistors can be arranged to prevent the resistors from overheating.
• the thermal insulation material of the launder is used to limit its heat losses to such a level that the heating resistor's own temperature will not exceed its normal operating range.
• the invention provides considerable advantages.
• the invention decreases the need of embedding materials and the maintenance intervals of the launders that are used in connection with copper casting, any downtime caused by the embedding, and the energy used for preheating and heating the melting furnace during casting.
• the cover is lightweight, as there are no cables or gas ducts, which are diffiult to detach, connected thereto. Accordingly, the cover can be provided with fixed or detachable liftnig members and connected to a lifting mechanism. In this way, the cover is easy to move aside during the maintenance and the replacemant of the lower part of the launder.
• Fig. 1 shows the cross-section of the launder construction according to one embodiment of the invention.
• Fig. 2 shows the section of the launder according to Fig. 1 from the lateral direction B-B.
• Fig. 3 shows the implementation of the control of a launder construction according to the invention.
• Figs. 4 to 6 show a casting trough provided with an electrically heated cover.
• Fig. 5 is the cross-sectional side view of the casting trough according to Fig. 4.
• Fig. 6 is the cross section of the casting trough according to Fig. 6 in the direction B-B.
• Fig. 1 shows the cover part 5 and the launder construction 10, both comprising a steel jacket 1 , 2.
• a heating resistor loop 3 is arranged on supporting cross-arms 32 in the groove defined by the ceramic wool insulation 11 of the cover 5.
• the supporting cross-arms 32 are arranged at equal intervals below the resistor loop.
• a ceramic insulation 33 is arranged in the heatable area of the cross-arms 32.
• the connecting terminals 31 of the current feed of the heating resistors 32 are taken through the insulating lining 11 of the cover and the metal jacket 1.
• Molten metal 4 flows in the flow channel formed by a refractory lining 22.
• the refractory lining 22 is formed of an embedding composition.
• a layer of ceramic wool insulation 21 is arranged between the refractory lining 22 and the steel jacket 2.
• the cover 5 rests on the lower part, being supported by the same so that the gas flow and the heat radiation on the long sides of the launder construction are essentially prevented.
• the cover part 5 only covers part of the total length of the launder, as illustrated in Fig. 2.
• the launder is installed in a slanted position to enable the flow of molten metal in the launder.
• the cover part and the launder form a launder channel, a gas burner or a hot gas blower 23 being arranged at its upper end, the flow of hot gas being directed at the opening of the launder channel to provide a stagnation pressure, whereby the gas flow in the launder channel is decelerated or prevented.
• the heating resistors 3 extend essentially throughout the length of the covered launder portion.
• a thermoelement 24 measures the temperature of the heating resistor and is arranged in a control circuit, which prevents the temperature resistor from overheating. Such a control that prevents overheating is preferably arranged in connection with each heating resistor.
• a thermoelement 25 measures the temperature of the cool air flowing into the launder channel and is arranged in a control circuit, which controls the power of the burner or a hot gas blower 23. The cooler the air that flows into the channel, the stronger the chimney effect and the more power is required of the burner 23.
• T1 is a temperature measured by the temperature sensor 24 in the cover of the launder
• T2 is a temperature measured by the temperature sensor 25 at the lower end of the launder, indicating the cooling effect of the gas that flows into the launder channel.
• the control of the gas burner adjusts the power of the burner or a hot gas blower according to the fluctuation of the cooling effect of the air that flows into the launder. In that case, the stagnation pressure caused by the burner at the upper end of the launder remains suitable throughout the process.
• the power of the launder cover is adjusted by a separate control of the electric power.
• the thermoelement T1 measures the temperature in the vicinity of the electrical resistor.
• the casting trough 40 of Figs. 4 to 6 is provided with an insulated cover 41 , which is provided with electrical resistances.
• the resistance material and the associated cabling are arranged in the volume 45, which is formed by the steel jacket of the cover 41.
• Supports 43, 44 for the cover are arranged on the walls 42 of the casting trough.
• the cover 41 that is arranged in the troughs is, for example, a rigid steel framework that supports the electrical heating elements at a suitable distance from the trough 40.
• the cover preferably has three support points 43, 44, at which it is supported by the trough so that it fits accurately enough in the trough.
• a layer of heat insulation is provided between the cover 41 and the heating elements.
• the insulating wool of the cover is suitably soft, whereby the wool settles tightly against the edge of the trough, when the cover is in place, allowing small variations and any solidified metal splatters on the edge of the trough.

Landscapes

• Engineering & Computer Science (AREA)
• Chemical & Material Sciences (AREA)
• Mechanical Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Materials Engineering (AREA)
• Metallurgy (AREA)
• Organic Chemistry (AREA)
• General Engineering & Computer Science (AREA)
• Vertical, Hearth, Or Arc Furnaces (AREA)
• Furnace Charging Or Discharging (AREA)
• Manufacture And Refinement Of Metals (AREA)
• Furnace Details (AREA)
• Continuous Casting (AREA)
• Control Of Combustion (AREA)
• Processing Of Solid Wastes (AREA)
• Refinement Of Pig-Iron, Manufacture Of Cast Iron, And Steel Manufacture Other Than In Revolving Furnaces (AREA)
• Glanulating (AREA)
• Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
• Moulding By Coating Moulds (AREA)

Priority Applications (12)

Applications Claiming Priority (2)

Publications (1)

Family

ID=33548044

Family Applications (1)

Country Status (19)

Cited By (3)

Families Citing this family (23)

Citations (7)

Family Cites Families (7)

• 2004
  • 2004-12-30 FI FI20041686A patent/FI119418B/fi not_active IP Right Cessation
• 2005
  • 2005-12-16 PE PE2005001483A patent/PE20060799A1/es active IP Right Grant
  • 2005-12-29 DE DE602005024862T patent/DE602005024862D1/de active Active
  • 2005-12-29 EA EA200701189A patent/EA010006B1/ru not_active IP Right Cessation
  • 2005-12-29 KR KR1020077015100A patent/KR101240029B1/ko not_active Expired - Fee Related
  • 2005-12-29 US US11/722,868 patent/US7700036B2/en not_active Expired - Fee Related
  • 2005-12-29 PT PT05823355T patent/PT1836015E/pt unknown
  • 2005-12-29 WO PCT/FI2005/000555 patent/WO2006070057A1/en not_active Ceased
  • 2005-12-29 AT AT05823355T patent/ATE488316T1/de active
  • 2005-12-29 MX MX2007007891A patent/MX2007007891A/es active IP Right Grant
  • 2005-12-29 EP EP05823355A patent/EP1836015B1/en active Active
  • 2005-12-29 CN CNB2005800454840A patent/CN100553825C/zh not_active Expired - Fee Related
  • 2005-12-29 AU AU2005321205A patent/AU2005321205B2/en not_active Ceased
  • 2005-12-29 BR BRPI0519791-0A patent/BRPI0519791A2/pt not_active Application Discontinuation
  • 2005-12-29 PL PL05823355T patent/PL1836015T3/pl unknown
  • 2005-12-29 CA CA2591952A patent/CA2591952C/en not_active Expired - Fee Related
  • 2005-12-29 JP JP2007548848A patent/JP4809847B2/ja not_active Expired - Fee Related
  • 2005-12-29 ES ES05823355T patent/ES2356721T3/es active Active
• 2007
  • 2007-06-28 ZA ZA200704678A patent/ZA200704678B/xx unknown