WO2006034086A1 - Reacteur a membrane ameliore - Google Patents

Reacteur a membrane ameliore Download PDF

Info

Publication number
WO2006034086A1
WO2006034086A1 PCT/US2005/033267 US2005033267W WO2006034086A1 WO 2006034086 A1 WO2006034086 A1 WO 2006034086A1 US 2005033267 W US2005033267 W US 2005033267W WO 2006034086 A1 WO2006034086 A1 WO 2006034086A1
Authority
WO
WIPO (PCT)
Prior art keywords
hydrogen
reactor
intermediate layer
membrane
particles
Prior art date
Application number
PCT/US2005/033267
Other languages
English (en)
Inventor
Scott Lee Wellington
Andreas Nicholas Matzakos
Ivan Petrovich Mardilovich
Yi Hua Ma
Erik Edwin Engwall
Original Assignee
Worcester Polytechnic Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Worcester Polytechnic Institute filed Critical Worcester Polytechnic Institute
Priority to EP05808744A priority Critical patent/EP1789172A1/fr
Priority to JP2007532531A priority patent/JP2008513337A/ja
Priority to AU2005287034A priority patent/AU2005287034B2/en
Priority to CA002580580A priority patent/CA2580580A1/fr
Publication of WO2006034086A1 publication Critical patent/WO2006034086A1/fr
Priority to NO20071532A priority patent/NO20071532L/no

Abstract

La présente invention concerne un réacteur produisant de l'hydrogène. Ce réacteur produisant de l'hydrogène possède une chambre de réaction contenant un lit de catalyseur conçu pour produire des produits de réaction contenant de l'hydrogène à partir d'une alimentation produisant de l'hydrogène. Cette chambre de réaction comprend aussi un module de séparation de gaz perméable à l'hydrogène et sélectif d'hydrogène conçu pour recevoir les produits de réaction du lit de catalyseur et pour séparer un flux de produits contenant de l'hydrogène des produits de réaction. Le module de séparation de gaz comprend un substrat poreux, une couche intermédiaire située au niveau du substrat poreux et, une membrane sélective d'hydrogène recouvrant la couche intermédiaire. Cette couche intermédiaire comprend des particules et un métal lieur, ce métal lieur étant distribué à travers la couche intermédiaire. Cette invention concerne aussi un processus de reformage de flux utilisant le réacteur de l'invention.
PCT/US2005/033267 2004-09-21 2005-09-19 Reacteur a membrane ameliore WO2006034086A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP05808744A EP1789172A1 (fr) 2004-09-21 2005-09-19 Reacteur a membrane ameliore
JP2007532531A JP2008513337A (ja) 2004-09-21 2005-09-19 膜増強反応器
AU2005287034A AU2005287034B2 (en) 2004-09-21 2005-09-19 Membrane enhanced reactor
CA002580580A CA2580580A1 (fr) 2004-09-21 2005-09-19 Reacteur a membrane ameliore
NO20071532A NO20071532L (no) 2004-09-21 2007-03-23 Membranforbedret reaktor

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US61160804P 2004-09-21 2004-09-21
US60/611,608 2004-09-21

Publications (1)

Publication Number Publication Date
WO2006034086A1 true WO2006034086A1 (fr) 2006-03-30

Family

ID=35708904

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2005/033267 WO2006034086A1 (fr) 2004-09-21 2005-09-19 Reacteur a membrane ameliore

Country Status (7)

Country Link
EP (1) EP1789172A1 (fr)
JP (1) JP2008513337A (fr)
AU (1) AU2005287034B2 (fr)
CA (1) CA2580580A1 (fr)
NO (1) NO20071532L (fr)
TW (1) TW200630158A (fr)
WO (1) WO2006034086A1 (fr)

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009143731A (ja) * 2007-12-11 2009-07-02 Dainippon Printing Co Ltd 反応膜、水素製造装置および燃料電池
WO2009105394A1 (fr) * 2008-02-18 2009-08-27 Shell Oil Company Procédé de fabrication d'un système de membrane de séparation de gaz stable en cas de fuite
WO2010104421A1 (fr) * 2009-03-10 2010-09-16 Powercell Sweden Ab Agencement et procédé de production d'hydrogène à partir de combustible hydrocarboné
WO2012067505A2 (fr) 2010-11-16 2012-05-24 Stichting Energieonderzoek Centrum Nederland Catalyseur pour la production d'hydrogène
WO2013096183A1 (fr) * 2011-12-19 2013-06-27 Shell Oil Company Procédé de fabrication d'une membrane composite de séparation de l'hydrogène
JP2013184139A (ja) * 2012-03-09 2013-09-19 Asahi Kasei Chemicals Corp 水蒸気分離膜及びその製造方法
CN113348269A (zh) * 2019-01-23 2021-09-03 保罗·谢勒学院 基于多个微米和纳米烧结多孔层的多孔传输层
US11322766B2 (en) 2020-05-28 2022-05-03 Saudi Arabian Oil Company Direct hydrocarbon metal supported solid oxide fuel cell
US11492255B2 (en) 2020-04-03 2022-11-08 Saudi Arabian Oil Company Steam methane reforming with steam regeneration
US11492254B2 (en) 2020-06-18 2022-11-08 Saudi Arabian Oil Company Hydrogen production with membrane reformer
US11578016B1 (en) 2021-08-12 2023-02-14 Saudi Arabian Oil Company Olefin production via dry reforming and olefin synthesis in a vessel
US11583824B2 (en) 2020-06-18 2023-02-21 Saudi Arabian Oil Company Hydrogen production with membrane reformer
US11617981B1 (en) 2022-01-03 2023-04-04 Saudi Arabian Oil Company Method for capturing CO2 with assisted vapor compression
US11639290B2 (en) 2020-06-04 2023-05-02 Saudi Arabian Oil Company Dry reforming of methane with carbon dioxide at elevated pressure
US11718575B2 (en) 2021-08-12 2023-08-08 Saudi Arabian Oil Company Methanol production via dry reforming and methanol synthesis in a vessel
US11787759B2 (en) 2021-08-12 2023-10-17 Saudi Arabian Oil Company Dimethyl ether production via dry reforming and dimethyl ether synthesis in a vessel

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7727596B2 (en) * 2004-07-21 2010-06-01 Worcester Polytechnic Institute Method for fabricating a composite gas separation module
JP2010523315A (ja) 2007-04-05 2010-07-15 ウスター ポリテクニック インスティチュート 多孔質アノード酸化層を有する複合構造および製造方法
JP5354516B2 (ja) * 2008-08-15 2013-11-27 日本碍子株式会社 水素分離体
CN101920332B (zh) * 2010-04-29 2012-05-02 西安西工大超晶科技发展有限责任公司 一种不锈钢/铜复合梯度材料热交换过渡区部件的制造方法
US8652239B2 (en) 2010-05-03 2014-02-18 Worcester Polytechnic Institute High permeance sulfur tolerant Pd/Cu alloy membranes
CN103182249B (zh) * 2011-12-30 2016-10-05 财团法人工业技术研究院 多孔基材的修饰方法及经修饰的多孔基材
US20130171442A1 (en) * 2011-12-30 2013-07-04 Meng-Chang Lin Method for modifying porous substrate and modified porous substrate
EP2999771A1 (fr) 2013-05-20 2016-03-30 Shell Internationale Research Maatschappij B.V. Procédé de saturation de composés aromatiques pour diesel en deux étapes faisant appel à un balayage à la vapeur intermédiaire et à un catalyseur métallique commun
CN105013297B (zh) * 2014-04-23 2017-12-26 中国科学院大连化学物理研究所 一种用分子筛修饰钯基复合膜的方法
CN111424306B (zh) * 2020-04-13 2021-02-19 厦门通富微电子有限公司 一种气泡剥离装置及电镀液电镀系统
CN111905504A (zh) * 2020-07-03 2020-11-10 王保林 一种工业废气及废气中金属颗粒物处理装置
CN113041970B (zh) * 2021-03-17 2021-11-26 南京理工大学 一种内置扰流结构催化膜式反应器
DE102022203604A1 (de) 2022-04-11 2023-10-12 Siemens Energy Global GmbH & Co. KG Pulver, keramische Wand, Reaktionskammer sowie Verfahren

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5217506A (en) * 1990-08-10 1993-06-08 Bend Research, Inc. Hydrogen-permeable composite metal membrane and uses thereof
US5393325A (en) * 1990-08-10 1995-02-28 Bend Research, Inc. Composite hydrogen separation metal membrane
US5498278A (en) * 1990-08-10 1996-03-12 Bend Research, Inc. Composite hydrogen separation element and module
WO1999030806A1 (fr) * 1997-12-15 1999-06-24 Worcester Polytechnic Institute Module d'extraction d'hydrogene
WO2002066144A2 (fr) * 2001-02-19 2002-08-29 Compagnie D'etude Des Techniques De L'hydrogene (Ceth) Structures composites de membranes selectivement permeables a l'hydrogene et processeurs de gaz combustibles en faisant usage
US20020141919A1 (en) * 2001-03-30 2002-10-03 Siemens Westinghouse Power Corporation Metal gas separation membrane
WO2003011433A1 (fr) * 2001-07-25 2003-02-13 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Membrane metallique de solubilisation-diffusion et son procede de production
WO2004022480A2 (fr) * 2002-09-05 2004-03-18 Shell Internationale Research Maatschappij B.V. Dispositif et procede de production d'hydrogene a purete elevee
US20040129135A1 (en) * 2002-03-05 2004-07-08 Roark Shane E. Dense, layered membranes for hydrogen separation
WO2004098751A1 (fr) * 2003-05-02 2004-11-18 Worcester Polytechnic Institute Modules composites de separation de gaz dotes de couches intermediaires a temperature de tamman elevee

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5139541A (en) * 1990-08-10 1992-08-18 Bend Research, Inc. Hydrogen-permeable composite metal membrane
JPH04346824A (ja) * 1991-05-21 1992-12-02 Mitsubishi Heavy Ind Ltd 水素分離膜
JPH0585702A (ja) * 1991-09-30 1993-04-06 Mitsubishi Heavy Ind Ltd 水素分離膜の製造方法
JP3117276B2 (ja) * 1992-04-09 2000-12-11 三菱重工業株式会社 水素分離膜
JP3621785B2 (ja) * 1996-07-12 2005-02-16 トヨタ自動車株式会社 水素分離構造体
JP2001286742A (ja) * 2000-04-10 2001-10-16 Mitsubishi Heavy Ind Ltd 水素分離膜
JP2002219341A (ja) * 2001-01-30 2002-08-06 Kobe Steel Ltd 水素選択透過膜支持用基材および水素選択透過部材
WO2003076050A1 (fr) * 2002-03-05 2003-09-18 Eltron Research, Inc. Membranes de transport d'hydrogene
CA2519769A1 (fr) * 2003-03-21 2004-10-07 Worcester Polytechnic Institute Modules composites de separations de gaz presentant des couches metalliques poreuses intermediaires

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5217506A (en) * 1990-08-10 1993-06-08 Bend Research, Inc. Hydrogen-permeable composite metal membrane and uses thereof
US5393325A (en) * 1990-08-10 1995-02-28 Bend Research, Inc. Composite hydrogen separation metal membrane
US5498278A (en) * 1990-08-10 1996-03-12 Bend Research, Inc. Composite hydrogen separation element and module
WO1999030806A1 (fr) * 1997-12-15 1999-06-24 Worcester Polytechnic Institute Module d'extraction d'hydrogene
WO2002066144A2 (fr) * 2001-02-19 2002-08-29 Compagnie D'etude Des Techniques De L'hydrogene (Ceth) Structures composites de membranes selectivement permeables a l'hydrogene et processeurs de gaz combustibles en faisant usage
US20020141919A1 (en) * 2001-03-30 2002-10-03 Siemens Westinghouse Power Corporation Metal gas separation membrane
WO2003011433A1 (fr) * 2001-07-25 2003-02-13 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Membrane metallique de solubilisation-diffusion et son procede de production
US20040129135A1 (en) * 2002-03-05 2004-07-08 Roark Shane E. Dense, layered membranes for hydrogen separation
WO2004022480A2 (fr) * 2002-09-05 2004-03-18 Shell Internationale Research Maatschappij B.V. Dispositif et procede de production d'hydrogene a purete elevee
WO2004098751A1 (fr) * 2003-05-02 2004-11-18 Worcester Polytechnic Institute Modules composites de separation de gaz dotes de couches intermediaires a temperature de tamman elevee
US20040244590A1 (en) * 2003-05-02 2004-12-09 Worcester Polytechnic Institute Composite gas separation modules having high Tamman temperature intermediate layers

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
EDLUND D J ET AL: "The relationship between intermetallic diffusion and flux decline in composite-metal membranes: implications for achieving long membrane lifetime", JOURNAL OF MEMBRANE SCIENCE, ELSEVIER SCIENTIFIC PUBL.COMPANY. AMSTERDAM, NL, vol. 107, no. 1, 15 November 1995 (1995-11-15), pages 147 - 153, XP004041247, ISSN: 0376-7388 *
SHU J ET AL: "Structurally stable composite Pd-Ag alloy membranes: Introduction of a diffusion barrier", THIN SOLID FILMS, ELSEVIER-SEQUOIA S.A. LAUSANNE, CH, vol. 286, no. 1, 30 September 1996 (1996-09-30), pages 72 - 79, XP004049419, ISSN: 0040-6090 *

Cited By (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8048199B2 (en) 2007-02-20 2011-11-01 Shell Oil Company Method of making a leak stable gas separation membrane system
JP2009143731A (ja) * 2007-12-11 2009-07-02 Dainippon Printing Co Ltd 反応膜、水素製造装置および燃料電池
WO2009105394A1 (fr) * 2008-02-18 2009-08-27 Shell Oil Company Procédé de fabrication d'un système de membrane de séparation de gaz stable en cas de fuite
WO2010104421A1 (fr) * 2009-03-10 2010-09-16 Powercell Sweden Ab Agencement et procédé de production d'hydrogène à partir de combustible hydrocarboné
US8936883B2 (en) 2009-03-10 2015-01-20 Powercell Sweden Ab Arrangement and method for generating hydrogen from hydrocarbon fuel
WO2012067505A2 (fr) 2010-11-16 2012-05-24 Stichting Energieonderzoek Centrum Nederland Catalyseur pour la production d'hydrogène
WO2013096183A1 (fr) * 2011-12-19 2013-06-27 Shell Oil Company Procédé de fabrication d'une membrane composite de séparation de l'hydrogène
JP2013184139A (ja) * 2012-03-09 2013-09-19 Asahi Kasei Chemicals Corp 水蒸気分離膜及びその製造方法
CN113348269A (zh) * 2019-01-23 2021-09-03 保罗·谢勒学院 基于多个微米和纳米烧结多孔层的多孔传输层
CN113348269B (zh) * 2019-01-23 2024-03-08 保罗·谢勒学院 基于多个微米和纳米烧结多孔层的多孔传输层
US11492255B2 (en) 2020-04-03 2022-11-08 Saudi Arabian Oil Company Steam methane reforming with steam regeneration
US11322766B2 (en) 2020-05-28 2022-05-03 Saudi Arabian Oil Company Direct hydrocarbon metal supported solid oxide fuel cell
US11639290B2 (en) 2020-06-04 2023-05-02 Saudi Arabian Oil Company Dry reforming of methane with carbon dioxide at elevated pressure
US11492254B2 (en) 2020-06-18 2022-11-08 Saudi Arabian Oil Company Hydrogen production with membrane reformer
US11583824B2 (en) 2020-06-18 2023-02-21 Saudi Arabian Oil Company Hydrogen production with membrane reformer
US11578016B1 (en) 2021-08-12 2023-02-14 Saudi Arabian Oil Company Olefin production via dry reforming and olefin synthesis in a vessel
US11718575B2 (en) 2021-08-12 2023-08-08 Saudi Arabian Oil Company Methanol production via dry reforming and methanol synthesis in a vessel
US11787759B2 (en) 2021-08-12 2023-10-17 Saudi Arabian Oil Company Dimethyl ether production via dry reforming and dimethyl ether synthesis in a vessel
US11617981B1 (en) 2022-01-03 2023-04-04 Saudi Arabian Oil Company Method for capturing CO2 with assisted vapor compression

Also Published As

Publication number Publication date
NO20071532L (no) 2007-06-20
TW200630158A (en) 2006-09-01
CA2580580A1 (fr) 2006-03-30
AU2005287034A1 (en) 2006-03-30
JP2008513337A (ja) 2008-05-01
EP1789172A1 (fr) 2007-05-30
AU2005287034B2 (en) 2009-06-11

Similar Documents

Publication Publication Date Title
AU2005287034B2 (en) Membrane enhanced reactor
AU2005286952B2 (en) Membrane steam reformer
AU2005286955B2 (en) Reactor and process for steam reforming
Rahimpour et al. Palladium membranes applications in reaction systems for hydrogen separation and purification: A review
JP4782423B2 (ja) 高純度水素の製造装置及び方法
KR101807112B1 (ko) 쉘-앤-튜브형 천연가스 개질용 반응기 및 이를 이용한 합성가스 또는 수소가스의 제조방법
Pal et al. A review on types, fabrication and support material of hydrogen separation membrane
Basile et al. Synthesis, characterization, and applications of palladium membranes
US8518151B2 (en) Porous hollow fiber supported dense membrane for hydrogen production, separation, or purification
US7018446B2 (en) Metal gas separation membrane
JP2004506506A (ja) 合成ガスを製造するための混合伝導膜
JP5390448B2 (ja) 膜分離型反応器及び水素の製造方法
JP5757243B2 (ja) シリカ系水素分離材料及びその製造方法、並びにそれを備えた水素分離モジュール及び水素製造装置
Li et al. Development of palladium-alloy membranes for hydrogen separation and purification
Tong et al. Thin Pd membrane prepared on macroporous stainless steel tube filter by an in-situ multi-dimensional plating mechanism
US20140251131A1 (en) Palladium-alloyed membranes and methods of making and using the same
KR102482676B1 (ko) 원통형 또는 튜브형 지지체 상에 분말 입자들이 순차적으로 적층되어 결정화된 적층막의 제조방법
JP5410937B2 (ja) 水素製造装置
TWI473760B (zh) 膜管複合體及利用該複合體之高純度氫氣產生裝置
Tanaka et al. Recent Developments on Supported Pd Membranes for Hydrogen Separation and Membrane Reactors
Hien Microfabricated Palladium-based membranes for hydrogen separation
JP2005199211A (ja) メンブレン・リアクタ
Li et al. Repair of Pd/α-Al2O3 composite membrane with defects

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV LY MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU LV MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2005287034

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: 2005808744

Country of ref document: EP

Ref document number: 2580580

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2007532531

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2005287034

Country of ref document: AU

Date of ref document: 20050919

Kind code of ref document: A

WWP Wipo information: published in national office

Ref document number: 2005287034

Country of ref document: AU

WWP Wipo information: published in national office

Ref document number: 2005808744

Country of ref document: EP