WO2006000035A1 - Materiau de construction et composition de revetement en poudre - Google Patents

Materiau de construction et composition de revetement en poudre Download PDF

Info

Publication number
WO2006000035A1
WO2006000035A1 PCT/AU2005/000919 AU2005000919W WO2006000035A1 WO 2006000035 A1 WO2006000035 A1 WO 2006000035A1 AU 2005000919 W AU2005000919 W AU 2005000919W WO 2006000035 A1 WO2006000035 A1 WO 2006000035A1
Authority
WO
WIPO (PCT)
Prior art keywords
cement
fibre
sheets
powder
powder coating
Prior art date
Application number
PCT/AU2005/000919
Other languages
English (en)
Inventor
David Murray James
Original Assignee
Orica Australia Pty. Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AU2004903490A external-priority patent/AU2004903490A0/en
Application filed by Orica Australia Pty. Ltd. filed Critical Orica Australia Pty. Ltd.
Priority to NZ552374A priority Critical patent/NZ552374A/en
Priority to AU2005256156A priority patent/AU2005256156B2/en
Publication of WO2006000035A1 publication Critical patent/WO2006000035A1/fr

Abstract

L'invention concerne une composition de revêtement en poudre qui comprend un polymère de polytétrafluoroéthylène (PTFE). L'invention porte également sur une feuille de soffite en fibro-ciment et sur un revêtement d'avant-toit munis d'un revêtement en poudre, et sur un procédé de fabrication de la feuille et du revêtement précités.
PCT/AU2005/000919 2004-06-25 2005-06-24 Materiau de construction et composition de revetement en poudre WO2006000035A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
NZ552374A NZ552374A (en) 2004-06-25 2005-06-24 Construction material and powder coating composition
AU2005256156A AU2005256156B2 (en) 2004-06-25 2005-06-24 Construction material and powder coating composition

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
AU2004903490A AU2004903490A0 (en) 2004-06-25 Construction material and powder coating composition
AU2004903490 2004-06-25

Publications (1)

Publication Number Publication Date
WO2006000035A1 true WO2006000035A1 (fr) 2006-01-05

Family

ID=35781512

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/AU2005/000919 WO2006000035A1 (fr) 2004-06-25 2005-06-24 Materiau de construction et composition de revetement en poudre

Country Status (2)

Country Link
NZ (1) NZ552374A (fr)
WO (1) WO2006000035A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006050338A1 (fr) * 2004-11-02 2006-05-11 Valspar Sourcing, Inc. Produits de fibrociment et a base de ciment
WO2012114028A1 (fr) * 2011-02-21 2012-08-30 Lafarge Gypsum International Element resistant a des transferts d'air et des transferts thermohydriques pour le domaine de la construction, notamment des murs legers ou des façades legeres
US8997924B2 (en) 2007-03-21 2015-04-07 Ashtech Industries, Llc Utility materials incorporating a microparticle matrix
US9076428B2 (en) 2007-03-21 2015-07-07 Ashtech Industries, Llc Sound attenuation building material and system
LU100188B1 (en) * 2017-05-04 2019-01-04 Tarkett Gdl Sa Floor or wall covering production method
JP2019044098A (ja) * 2017-09-04 2019-03-22 ソマール株式会社 エポキシ樹脂粉体塗料組成物
WO2022221930A1 (fr) 2021-04-23 2022-10-27 L'oreal Composition cosmétique d'un produit de protection solaire, utilisation d'une composition cosmétique d'un produit de protection solaire et procédé de fabrication d'une composition cosmétique d'un produit de protection solaire
WO2023235942A1 (fr) 2022-06-10 2023-12-14 L'oreal Composition d'écran solaire cosmétique et utilisation d'une composition d'écran solaire cosmétique
FR3142902A1 (fr) 2022-12-12 2024-06-14 L'oreal Composition écran solaire COSMÉTIQUE ET Utilisation d’une composition écran solaire COSMÉTIQUE

Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB508791A (en) * 1937-01-14 1939-07-03 Cristallex Sa Improved material for decorative plates or panels used in the facing of walls, or in the manufacture of furniture and its process of manufacture
GB1322968A (en) * 1970-12-18 1973-07-11 French B T B Low friction coatings
GB1487028A (en) * 1974-10-21 1977-09-28 Allied Chem Blend of two fluorine-containing olefin polymers
GB2056885A (en) * 1979-08-08 1981-03-25 Blundell Permoglaze Ltd Powder coating cellulose fibre substrates
GB2078136A (en) * 1980-06-24 1982-01-06 Sonneborn & Rieck Ltd Process for powder coating substrates
EP0572764A2 (fr) * 1992-06-02 1993-12-08 Elf Atochem North America, Inc. Revêtements à poudre
JPH06122841A (ja) * 1992-10-13 1994-05-06 Nippon Telegr & Teleph Corp <Ntt> はっ水性粉体塗料及びその塗装方法
JPH07331012A (ja) * 1994-06-06 1995-12-19 Du Pont Mitsui Fluorochem Co Ltd 粉末加工用フッ素樹脂粉末組成物
US5766522A (en) * 1996-07-19 1998-06-16 Morton International, Inc. Continuous processing of powder coating compositions
US5879804A (en) * 1996-04-22 1999-03-09 K.K. Seishin Kigyo Composite powder and manufacturing thereof for forming fluoro resin surface coating
JP2002194297A (ja) * 2000-12-22 2002-07-10 Nippon Paint Co Ltd プレコート材用意匠性粉体塗料組成物、意匠性塗膜の形成方法および意匠性を有する塗装プレコート材
JP2003002980A (ja) * 2001-06-20 2003-01-08 Mitsubishi Rayon Co Ltd ポリテトラフルオロエチレン含有粉体の製造方法
EP1348490A1 (fr) * 2002-03-21 2003-10-01 Bagetti Procédé pour la préparation et le dépôt d'une composition de revêtement protecteur, et objets revêtus d'une telle composition
WO2004108842A1 (fr) * 2003-06-06 2004-12-16 Akzo Nobel Coatings International B.V. Revetement en poudre anti-adhesif
US20050075411A1 (en) * 2003-10-04 2005-04-07 Degussa Ag Powder coating compositions comprising urethane (meth)acrylates and micronized waxes and their use

Patent Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB508791A (en) * 1937-01-14 1939-07-03 Cristallex Sa Improved material for decorative plates or panels used in the facing of walls, or in the manufacture of furniture and its process of manufacture
GB1322968A (en) * 1970-12-18 1973-07-11 French B T B Low friction coatings
GB1487028A (en) * 1974-10-21 1977-09-28 Allied Chem Blend of two fluorine-containing olefin polymers
GB2056885A (en) * 1979-08-08 1981-03-25 Blundell Permoglaze Ltd Powder coating cellulose fibre substrates
GB2078136A (en) * 1980-06-24 1982-01-06 Sonneborn & Rieck Ltd Process for powder coating substrates
EP0572764A2 (fr) * 1992-06-02 1993-12-08 Elf Atochem North America, Inc. Revêtements à poudre
JPH06122841A (ja) * 1992-10-13 1994-05-06 Nippon Telegr & Teleph Corp <Ntt> はっ水性粉体塗料及びその塗装方法
JPH07331012A (ja) * 1994-06-06 1995-12-19 Du Pont Mitsui Fluorochem Co Ltd 粉末加工用フッ素樹脂粉末組成物
US5879804A (en) * 1996-04-22 1999-03-09 K.K. Seishin Kigyo Composite powder and manufacturing thereof for forming fluoro resin surface coating
US5766522A (en) * 1996-07-19 1998-06-16 Morton International, Inc. Continuous processing of powder coating compositions
JP2002194297A (ja) * 2000-12-22 2002-07-10 Nippon Paint Co Ltd プレコート材用意匠性粉体塗料組成物、意匠性塗膜の形成方法および意匠性を有する塗装プレコート材
JP2003002980A (ja) * 2001-06-20 2003-01-08 Mitsubishi Rayon Co Ltd ポリテトラフルオロエチレン含有粉体の製造方法
EP1348490A1 (fr) * 2002-03-21 2003-10-01 Bagetti Procédé pour la préparation et le dépôt d'une composition de revêtement protecteur, et objets revêtus d'une telle composition
WO2004108842A1 (fr) * 2003-06-06 2004-12-16 Akzo Nobel Coatings International B.V. Revetement en poudre anti-adhesif
US20050075411A1 (en) * 2003-10-04 2005-04-07 Degussa Ag Powder coating compositions comprising urethane (meth)acrylates and micronized waxes and their use

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Week 199423, Derwent World Patents Index; Class A82, AN 1994-186504 *
DATABASE WPI Week 200265, Derwent World Patents Index; Class A82, AN 2002-603414 *
DATABASE WPI Week 200361, Derwent World Patents Index; Class A14, AN 2003-638964 *
PATENT ABSTRACTS OF JAPAN vol. 1996, no. 4 *

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006050338A1 (fr) * 2004-11-02 2006-05-11 Valspar Sourcing, Inc. Produits de fibrociment et a base de ciment
US8997924B2 (en) 2007-03-21 2015-04-07 Ashtech Industries, Llc Utility materials incorporating a microparticle matrix
US9076428B2 (en) 2007-03-21 2015-07-07 Ashtech Industries, Llc Sound attenuation building material and system
WO2012114028A1 (fr) * 2011-02-21 2012-08-30 Lafarge Gypsum International Element resistant a des transferts d'air et des transferts thermohydriques pour le domaine de la construction, notamment des murs legers ou des façades legeres
WO2012127126A1 (fr) * 2011-02-21 2012-09-27 Lafarge Gypsum International Element resistant a des transferts d'air et des transferts thermohydriques pour le domaine de la construction, notamment des murs légers ou des façades légères
CN103649432A (zh) * 2011-02-21 2014-03-19 Siniat国际有限责任公司 特别用于轻质墙体或轻质立面的建造领域中的耐空气传递且耐热和水传递的元件
LU100188B1 (en) * 2017-05-04 2019-01-04 Tarkett Gdl Sa Floor or wall covering production method
JP2019044098A (ja) * 2017-09-04 2019-03-22 ソマール株式会社 エポキシ樹脂粉体塗料組成物
JP7020825B2 (ja) 2017-09-04 2022-02-16 ソマール株式会社 エポキシ樹脂粉体塗料組成物
WO2022221930A1 (fr) 2021-04-23 2022-10-27 L'oreal Composition cosmétique d'un produit de protection solaire, utilisation d'une composition cosmétique d'un produit de protection solaire et procédé de fabrication d'une composition cosmétique d'un produit de protection solaire
FR3122087A1 (fr) 2021-04-23 2022-10-28 L'oreal Composition d’écran solaire cosmétique, utilisation d’une composition d’écran solaire cosmétique, et processus de fabrication d’une composition d’écran solaire cosmétique
WO2023235942A1 (fr) 2022-06-10 2023-12-14 L'oreal Composition d'écran solaire cosmétique et utilisation d'une composition d'écran solaire cosmétique
FR3136372A1 (fr) 2022-06-10 2023-12-15 L'oreal Composition et utilisation d’une composition écran solaire cosmétique
FR3142902A1 (fr) 2022-12-12 2024-06-14 L'oreal Composition écran solaire COSMÉTIQUE ET Utilisation d’une composition écran solaire COSMÉTIQUE

Also Published As

Publication number Publication date
NZ552374A (en) 2010-11-26

Similar Documents

Publication Publication Date Title
WO2006000035A1 (fr) Materiau de construction et composition de revetement en poudre
US7429290B2 (en) Fire-retardant coating, method for producing fire-retardant building materials
US5681639A (en) Waterproof lightweight grain-tone decorative panel
WO2005097916A1 (fr) Revetement ignifuge, procede de production de materiaux de construction ignifuges
MXPA06012718A (es) Procedimiento de realizacion de una obra, enlucido de juntas y de revestimientos de superficies para elementos de construccion y su procedimiento de preparacion.
EP1388374A1 (fr) Procede de finition avec un revetement d&#39;isolation thermique
JP2004183331A (ja) 断熱構造体
EA039443B1 (ru) Смесь строительных материалов
JP3218359B2 (ja) 発泡耐火性積層体とその形成方法
JP2000230287A (ja) 発泡耐火積層体及びその形成方法
JPH11116311A (ja) 壁塗り用モルタル組成物
AU2005256156B2 (en) Construction material and powder coating composition
US20160304725A1 (en) Liquid Drywall Composition and Methods of Use
JP4069464B2 (ja) 発泡耐火シート用組成物及び発泡耐火シート
JP2004183330A (ja) 被膜積層体の施工方法
RU2379122C1 (ru) Способ окраски диэлектрического материала методом электростатического напыления порошковой краски
US20220388907A1 (en) Cement sheets and coatings for building construction
RU92420U1 (ru) Композитный материал с диэлектрической основой и электропроводным защитно-декоративным покрытием и изделие из него
RU2388551C1 (ru) Окрашенный порошковой краской диэлектрический материал и изделие из него
DE202015009375U1 (de) Mehrschichtige Struktur, erhältlich durch ein Verfahren zum Vorbereiten einer Oberfläche zur Dekoration
JP6108424B2 (ja) 積層構造体
RU2412970C2 (ru) Композитный материал с диэлектрической основой и электропроводным защитно-декоративным покрытием и изделие из него
WO2006000036A1 (fr) Panneau de signalisation en contreplaque et composition de revetement en poudre
JP2000229368A (ja) 防火性を有する断熱積層体の形成方法
JPS58173244A (ja) 金属板成形不燃性屋根材およびその製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2005256156

Country of ref document: AU

NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Country of ref document: DE

WWE Wipo information: entry into national phase

Ref document number: 552374

Country of ref document: NZ

ENP Entry into the national phase

Ref document number: 2005256156

Country of ref document: AU

Date of ref document: 20050624

Kind code of ref document: A

WWP Wipo information: published in national office

Ref document number: 2005256156

Country of ref document: AU

122 Ep: pct application non-entry in european phase