WO2005056893A1 - ポリベンザゾール繊維およびそれからなる物品 - Google Patents
ポリベンザゾール繊維およびそれからなる物品 Download PDFInfo
- Publication number
- WO2005056893A1 WO2005056893A1 PCT/JP2004/018392 JP2004018392W WO2005056893A1 WO 2005056893 A1 WO2005056893 A1 WO 2005056893A1 JP 2004018392 W JP2004018392 W JP 2004018392W WO 2005056893 A1 WO2005056893 A1 WO 2005056893A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fiber
- yarn
- polybenzazole
- durability
- high temperature
- Prior art date
Abstract
Description
Claims