WO2005037919A1 - 光ディスク保護膜用組成物 - Google Patents

光ディスク保護膜用組成物 Download PDF

Info

Publication number
WO2005037919A1
WO2005037919A1 PCT/JP2004/015356 JP2004015356W WO2005037919A1 WO 2005037919 A1 WO2005037919 A1 WO 2005037919A1 JP 2004015356 W JP2004015356 W JP 2004015356W WO 2005037919 A1 WO2005037919 A1 WO 2005037919A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
optical disk
protective film
component
monomer
Prior art date
Application number
PCT/JP2004/015356
Other languages
English (en)
French (fr)
Inventor
Kiichiro Oguni
Satoshi Yanagida
Kozaburo Hayashi
Original Assignee
Sony Chemicals Corp.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sony Chemicals Corp. filed Critical Sony Chemicals Corp.
Priority to DE602004023414T priority Critical patent/DE602004023414D1/de
Priority to KR1020067007517A priority patent/KR101150144B1/ko
Priority to EP04792525A priority patent/EP1686154B1/en
Publication of WO2005037919A1 publication Critical patent/WO2005037919A1/ja
Priority to US11/405,438 priority patent/US7744979B2/en

Abstract

　本発明は、耐擦傷性を損なわずに低粘度かつ基材侵食性の低い光ディスク保護膜用組成物を提供するものである。 　本発明の光ディスク保護膜用組成物は、アクリルラジカル系のバインダー樹脂中に無機系微粒子を分散させたものである。上記バインダー樹脂原料としては、ベース成分と、耐擦傷性成分と、希釈成分とを含有するバインダーモノマーが用いられ、この希釈成分は、主鎖構造に環構造又は分岐炭素鎖構造の官能基を有するモノマーである。希釈成分としては、単官能又は２官能の官能基を有するモノマーを用いることができる。

Description

明 細 書
光ディスク保護膜用組成物
技術分野
[0001] 本発明は、保護膜用榭脂組成物に関し、特に、コンパクトディスク (CD)、ディジタ ルバーサタイルディスク (DVD)等の光ディスクの保護膜に用いられる保護膜用榭脂 組成物に関する。
背景技術
[0002] 一般に、この種の光ディスクにおいては、外装部材表面の擦傷を防止するため、外 装部材の表面にコーティング処理が施されて 、る。
[0003] このようなコーティング用の材料としては、高い耐擦傷性を有する無機系の材料が 有効であるが、無機系の材料は塗工液の粘度が高ぐ膜厚を薄くすることが困難であ るという問題がある。
[0004] この問題を解決するため、従来、溶剤の希釈によって塗工液の粘度を抑えることが 行われている力 希釈溶液が基材を侵食することによって、種々の問題が生ずる。
[0005] 例えば、基材成分の溶出によりコーティング層の平坦性が低下し、透明性が損なわ れる（マット調になる)。
[0006] また、溶出した基材成分とコーティング材料が溶け合うことにより、耐擦傷性が低下 する。
[0007] その一方、上記問題への対処方法として溶剤の代わりに低粘度のアクリルモノマー を反応性希釈材として用い、低粘度コーティング用塗工液を調製することも考えられ るが、その場合には、選択するモノマーによっては耐擦傷性が大きく低下する場合が ある。
発明の開示
発明が解決しょうとする課題
[0008] 本発明は、このような従来の技術の課題を解決するためになされたもので、耐擦傷 性を損なわずに低粘度かつ基材侵食性の低い光ディスク保護膜用組成物を提供す ることを目的とする。 課題を解決するための手段
[0009] 本発明者らは上記目的を達成するため鋭意努力を重ねた結果、バインダー榭脂の 希釈成分として主鎖構造に環構造又は分岐炭素鎖を有するモノマーを用いることで 耐擦傷性を損なわずに光ディスク保護膜用組成物の粘度を低く抑えることを見い出 し、本発明を完成するに至った。
[0010] 力かる知見に基づいてなされた本発明は、アクリルラジカル系のバインダー榭脂中 に無機系微粒子を分散させた保護膜用組成物であって、上記バインダー榭脂の原 料として、ベース成分と、耐擦傷性成分と、希釈成分とを含有するバインダーモノマ 一が用いられ、上記希釈成分が、主鎖構造に環構造又は分岐炭素鎖構造の官能基 を有するモノマーであるものである。
本発明は、上記希釈成分が、単官能又は 2官能の官能基を有する光ディスク保護 膜用組成物であるものである。
本発明はまた、上記希釈成分の粘度が lOmPa · s以上である光ディスク保護膜用 組成物であるものである。
本発明は、上記希釈成分の粘度が 50mPa · s未満である光ディスク保護膜用榭脂 組成物であるものである。
さらに本発明は、上記希釈成分の粘度が 20mPa ' s未満である光ディスク保護膜用 組成物である。
本発明は、上記希釈成分の粘度が当該光ディスク保護膜用組成物の粘度より小さ いものである。
本発明は、上記光ディスク保護膜用組成物の粘度が 20mPa' s以上 lOOmPa' s未 満であるものである。
本発明は、上記光ディスク保護膜用組成物の硬化により得られた光ディスク用保護 膜である。
本発明は、基板上に記録パターンを有する光ディスクであって、アクリルラジカル系 のバインダー榭脂中に無機系微粒子を分散させてなり、上記ノインダー榭脂の原料 として、ベース成分と、耐擦傷性成分と、希釈成分とを含有するバインダーモノマー が用いられ、上記希釈成分が、主鎖構造に環構造又は分岐炭素鎖構造の官能基を 有するモノマーである光ディスク保護膜用組成物の硬化により得られた光ディスク用 保護膜が、上記基板の読取側の面上に設けられている光ディスクである。
[0011] 本発明の場合、バインダーモノマーの希釈成分として、主鎖構造に環構造又は分 岐炭素鎖構造の官能基を有するモノマーを用いることによって、硬化樹脂の骨格構 造が剛直になるため、耐擦傷性を損なわずに保護膜用組成物の粘度を低く抑えるこ とが可能になる。
発明の効果
[0012] 本発明によれば、耐擦傷性を損なわずに光ディスク保護膜用組成物の粘度を低く 抑えることが可能になる。
図面の簡単な説明
[0013] [図 1]本発明の光ディスク保護膜用組成物の適用した光ディスクの例を示す概略構 成図である。
符号の説明
[0014] 1…光ディスク
2· "基板
5· ··光ディスク用保護膜
20· ··読取側の面
発明を実施するための最良の形態
[0015] 以下、本発明に係る保護膜用組成物の最良の形態を詳細に説明する。
本発明の (光ディスク)保護膜用組成物は、アクリルラジカル系のノインダー榭脂中 に無機系微粒子を分散させたものである。
[0016] 本発明にお 、ては、ノ インダー榭脂の原料として、ベース成分と、耐擦傷性成分と
、希釈成分を含有するバインダーモノマーが用いられる。
[0017] ここで、ベース成分としては、種々のモノマーが用いられるが、無機系微粒子の分 散加工性 (分散作業性)の観点力もは、できるだけ低粘度（lOOmPa' s未満)のもの を用いることが好ましい。
[0018] このようなモノマーとしては、例えば、トリメチロールプロパントリアタリレート（TMPT A)、 1, 6 キサンジオールジアタリレート、力プロラタトン変性ジペンタエリスリトー ルへキサアタリレート（2)、ネオペンチルダリコールジアタリレート等があげられる。
[0019] また、耐擦傷性成分としては、種々のモノマーが用いられるが、耐擦傷性を向上さ せる観点からは、アクリル基数が 3官能以上のものを用いることが好ま U、。
[0020] このようなモノマーとしては、トリス（アタリ口キシェチル)イソシァヌレート、ジペンタエ リストールペンタおよびへキサアタリレート、ジトリメチロールプロパンテトラアタリレート
(DTMPTA)、ペンタエリスリトールテトラアタリレート等があげられる。
[0021] 一方、本発明に用いる希釈成分は、主鎖構造に環構造の官能基を有するモノマー と、主鎖構造に分岐炭素鎖構造の官能基を有するモノマーである。
[0022] ここで、主鎖構造の環構造は、例えばベンゼン環のような芳香環のほ力、シクロア ルカン等の脂環状の環構造も含まれる。
[0023] 一方、主鎖構造の分岐炭素鎖構造としては、例えば炭素 -炭素単結合を有する鎖 状炭化水素構造などがあげられる。
[0024] また、本発明の場合、希釈成分の官能基の数は、単官能又は 2官能の ヽずれも適 用可能である。
[0025] 本発明の希釈成分として使用可能なもののうち、環構造の官能基を有するモノマー としては、例えば、ジシクロペンテ-ルアタリレート（単官能）、アタリロイルモルフォリン (単官能)等があげられる。
[0026] また、分岐炭素構造の官能基を有するモノマーとしては、例えば、ジプロピレンダリ コールジアタリレート（DPGDA: 2官能）等があげられる。
[0027] 本発明の場合、希釈成分の粘度 (本明細書では平均粘度をいう。 )は特に限定され ることはないが、組成物の粘度を抑制することにより光ディスク基板表面への塗工性 の向上を図る観点からは、当該組成物の粘度より小さいことが好ましぐ具体的には、 lOm'Pa以上 50m'Pa未満とすることが好ましぐより好ましくは、 lOm'Pa以上 20m •Pa未満である。
[0028] 他方、希釈成分が、単官能の官能基を有するモノマーであり、かつ、当該希釈成分 の粘度が lOm'Pa以上のものである場合には、被侵食性の高い基材に対して有効 な保護膜用組成物を得ることができる。 [0029] 本発明の場合、バインダーモノマーの、ベース成分、耐擦傷性成分及び希釈成分 の配合比は特に限定されることはな 、が、光ディスク用の耐擦傷性コーティングとして 必要十分な耐擦傷性を付与する観点からは、 70： 5： 25— 60： 20： 20とすることが好 ましい。
[0030] そして、このような本発明の光ディスク保護膜用組成物の粘度は、光ディスク基板表 面への塗工性の向上を図る観点から、 20mPa' s以上 lOOmPa' s未満とすることが 好ましい。
[0031] 本発明の場合、無機系微粒子としては、例えば、コロイダルシリカ（SiO )ゃコロイダ
2 ルアルミナ (Al O )等の種々の無機系微粒子を用いることができる。
2 3
[0032] この無機系微粒子の粒径は、特に限定されることはないが、分散性及び光透過性 の観点からは、 10— 30nmのものを用いることが好まし!/、。
[0033] また、無機系微粒子の配合量は、特に限定されることはな ヽが、耐擦傷性付与の観 点力 は、 15— 30重量％とすることが好ましい。
[0034] なお、本発明の光ディスク保護膜用組成物には、光重合開始剤のほか、他の成分 として、紫外線吸収剤、表面張力調整剤等を含ませることも可能である。
[0035] 図 1は、本発明の光ディスク保護膜用組成物の適用した光ディスクの例を示す概略 構成図である。
[0036] 図 1に示すように、本発明の光ディスク 1は、通常の構成を有するもので、ポリカーボ ネートからなる円盤状の基板 2上に、記録パターン 2a、反射膜 3及び保護膜 4が形成 されている。
[0037] さらに、本発明の場合は、基板 2の読取側の面 20上に、上述した光ディスク保護膜 用組成物を硬化させた光ディスク用保護膜 5が設けられている。
[0038] 本発明の場合、この光ディスク用保護膜 5の厚さは特に限定されることはないが、耐 擦傷性及び光透過性確保の観点からは、 1一 5 mとすることが好ましい。
[0039] なお、本発明は光ディスク用のみならず、種々の保護膜用組成物に適用することが できる。ただし、光ディスク保護膜用組成物に適用した場合に最も有効となるもので ある。
実施例 [0040] 以下、本発明の実施例を比較例とともに詳細に説明する。
<実施例 1 >
ベース成分として、トリメチロールプロパントリアタリレート（TMPTA— N ダイセル U CB社製） 25重量部、 1, 6—へキサンジオールジアタリレート（HDODA ダイセル U CB社製） 15重量部、ネオペンチルグリコールジアタリレート（カャラッド NPGDA 日本化薬社製） 15重量部、力プロラタトン変性ジペンタエリスリトールへキサアタリレ ート（2) (カャラッド DPCA— 30 日本ィ匕薬社製） 5重量部の混合液に、コロイダルシ リカ（ナノテック シーアィ化成社製） 15重量部を分散させた。
[0041] そして、この分散液に、耐擦傷性成分として、トリス (アタリ口キシェチル)イソシァヌ レート（SR— 368 化薬サートマ一社製）、ジペンタエリストールペンタおよびへキサァ タリレート（ァロニックス M— 400 東亞合成社製）、ジトリメチロールプロパンテトラァク リレート（SR— 355 化薬サートマ一社製）、ペンタエリスリトールテトラアタリレート（SR -295 化薬サートマ一社製)のいずれかを 5重量部と、希釈成分として、ジシクロべ ンテュルアタリレート（Laromer DPGDA BASF社製 粘度： lOmPa' s) 20重量 部を添加した。
[0042] また、光開始剤として、ィルガキュア 184とダロキュア 1173 (いずれもチバ 'スぺシャ リティケミカルズ社製)をそれぞれ 5重量部添加した。
[0043] このようにして調製された塗工液の平均粘度を、コーンプレート式粘度計によって 測定した。その結果を表 1に示す。
[0044] また、この塗工液を、射出成形によって形成された低分子量ポリカーボネート基板と
、キャスト法によって形成された高分子量のポリカーボネート基板上に、乾燥後の厚 さが 15 mとなるように塗布した。
[0045] そして、この塗布膜に対し、メタルノヽライドランプ（120WZcm)を用い、積算光量が
300miZcmとなるように紫外線を照射した。
[0046] このようにして硬化させた塗布膜の耐擦傷性の評価を行った。その結果を表 2に示 す。
[0047] ここでは、テーバー摩耗試験機 (CS— 10F摩耗輪、荷重 250g、 100回転)を用い、 試験後のサンプルの Δ haze値が 10%未満のものを〇、試験後のサンプルの A haz e値が 10%以上のものを Xとする。
[0048] <実施例 2>
希釈成分として、アタリロイルモルフォリン (ACMO 興人社製 粘度： 12mPa' s) 2 0重量部を添加した以外は実施例 1と同様の方法によって塗布膜を形成し、耐擦傷 性の評価を行った。その結果を表 1及び表 2に示す。
[0049] <比較例 1 >
希釈成分として、トリプロピレングリコールジアタリレート（TRPGDA ダイセル UCB 社製 粘度： 8mPa' s) 20重量部を添加した以外は実施例 1と同様の方法によって塗 布膜を形成し、耐擦傷性の評価を行った。その結果を表 1及び表 2に示す。
[0050] <比較例 2>
希釈成分として、 1, 4ブタンジオールジアタリレート（Laromer BDDA BASF社 製 粘度： 5mPa' s) 20重量部を添加した以外は実施例 1と同様の方法によって塗布 膜を形成し、耐擦傷性の評価を行った。その結果を表 1及び表 2に示す。
[0051] <比較例 3 >
希釈成分として、イソボ-ルアタリレート（IBOA ダイセル UCB社製 粘度： 4mPa' s) 20重量部を添加した以外は実施例 1と同様の方法によって塗布膜を形成し、耐擦 傷性の評価を行った。その結果を表 1及び表 2に示す。
[0052] [表 1] 配合組成物（塗工液）の粘度（mP-s) 耐擦傷性成分
希釈成分
SR368 M400 SR355 SR295
実施例 1 DPGDA 37 37 34 34
比較例 1 TRPGDA 42 40 38 38
比較例 2 BDDA 21 22 20 19
実施例 2 ACMO 44 43 45 39
比較例 3 旧 OA 36 35 33 32 [0053] [表 2] 表 2 実施例及び比較例の評価結果
Figure imgf000009_0001
0·· Δ Ρι a z e値 1 0 %未満 X— A h a z e値 1 0 %以上
[0054] 〔評価結果〕
表 1に示すように、実施例 1、実施例 2は、塗工液の粘度が 50mPa' s未満であった
。また、硬化後の塗布膜については、低分子ポリカーボネート、高分子ポリカーボネ ートともに耐擦傷性が良好で、またモノマーによる侵食も生じな力つた。
[0055] 一方、バインダーモノマーの希釈成分が、主鎖構造に環構造及び分岐炭素鎖構造 の官能基をいずれも有しない比較例 1及び比較例 2の塗布膜は、低分子ポリカーボ ネート基材においてモノマーによる侵食が生じた。
[0056] また、バインダーモノマーの希釈成分が、主鎖構造に環構造及び分岐炭素鎖構造 の官能基をいずれも有する比較例 3の塗布膜は、低分子ポリカーボネート基材にお ける耐擦傷性が劣って 、た。
産業上の利用可能性
[0057] 以上述べたように本発明は、例えば、コンパクトディスク (CD)、ディジタルバーサタ ィルディスク (DVD)等の光ディスクの保護膜として有用な保護膜用榭脂組成物であ る。

Claims

請求の範囲
[1] アクリルラジカル系のバインダー榭脂中に無機系微粒子を分散させた保護膜用組 成物であって、
上記バインダー榭脂の原料として、ベース成分と、耐擦傷性成分と、希釈成分とを 含有するバインダーモノマーが用いられ、
上記希釈成分が、主鎖構造に環構造又は分岐炭素鎖構造の官能基を有するモノ マーである保護膜用組成物。
[2] アクリルラジカル系のバインダー榭脂中に無機系微粒子を分散させた光ディスク保 護膜用組成物であって、
上記バインダー榭脂の原料として、ベース成分と、耐擦傷性成分と、希釈成分とを 含有するバインダーモノマーが用いられ、
上記希釈成分が、主鎖構造に環構造又は分岐炭素鎖構造の官能基を有するモノ マーである光ディスク保護膜用組成物。
[3] 請求項 2において、上記希釈成分が、単官能又は 2官能の官能基を有する光ディ スク保護膜用組成物。
[4] 請求項 2において、上記希釈成分の粘度が lOmPa' s以上である光ディスク保護膜 用組成物。
[5] 請求項 2において、上記希釈成分の粘度が 50mPa' s未満である光ディスク保護膜 用組成物。
[6] 請求項 2において、上記希釈成分の粘度が 20mPa' s未満である光ディスク保護膜 用組成物。
[7] 請求項 2において、上記希釈成分の粘度が当該光ディスク保護膜用組成物の粘度 より小さ 、光ディスク保護膜用組成物。
[8] 請求項 2において、上記光ディスク保護膜用組成物の粘度が 20mPa' s以上 100m
Pa · s未満である光ディスク保護膜用組成物。
[9] アクリルラジカル系のバインダー榭脂中に無機系微粒子を分散させてなり、上記バ インダー榭脂の原料として、ベース成分と、耐擦傷性成分と、希釈成分とを含有する ノ^ンダ一モノマーが用いられ、上記希釈成分が、主鎖構造に環構造又は分岐炭素 鎖構造の官能基を有するモノマーである光ディスク保護膜用組成物の硬化により得 られた光ディスク用保護膜。
基板上に記録パターンを有する光ディスクであって、
アクリルラジカル系のバインダー榭脂中に無機系微粒子を分散させてなり、上記バ インダー榭脂の原料として、ベース成分と、耐擦傷性成分と、希釈成分とを含有する バインダーモノマーが用いられ、上記希釈成分が、主鎖構造に環構造又は分岐炭素 鎖構造の官能基を有するモノマーである光ディスク保護膜用組成物の硬化により得 られた光ディスク用保護膜が、上記基板の読取側の面上に設けられて ヽる光ディスク
PCT/JP2004/015356 2003-10-20 2004-10-18 光ディスク保護膜用組成物 WO2005037919A1 (ja)