WO2004065314A1 - Verfahren zur herstellung von synthetischem quarzglas - Google Patents
Verfahren zur herstellung von synthetischem quarzglas Download PDFInfo
- Publication number
- WO2004065314A1 WO2004065314A1 PCT/EP2004/000442 EP2004000442W WO2004065314A1 WO 2004065314 A1 WO2004065314 A1 WO 2004065314A1 EP 2004000442 W EP2004000442 W EP 2004000442W WO 2004065314 A1 WO2004065314 A1 WO 2004065314A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicon compound
- mixture
- sio
- quartz glass
- oligomeric
- Prior art date
Abstract
Description
Claims