Classifications

• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
  • C03B13/00—Rolling molten glass, i.e. where the molten glass is shaped by rolling
  • C03B13/16—Construction of the glass rollers
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F27—FURNACES; KILNS; OVENS; RETORTS
  • F27D—DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
  • F27D3/00—Charging; Discharging; Manipulation of charge
  • F27D3/02—Skids or tracks for heavy objects
  • F27D3/026—Skids or tracks for heavy objects transport or conveyor rolls for furnaces; roller rails
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
  • C03B17/00—Forming molten glass by flowing-out, pushing-out, extruding or drawing downwardly or laterally from forming slits or by overflowing over lips
  • C03B17/06—Forming glass sheets
  • C03B17/068—Means for providing the drawing force, e.g. traction or draw rollers
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
  • C03B35/00—Transporting of glass products during their manufacture, e.g. hot glass lenses, prisms
  • C03B35/14—Transporting hot glass sheets or ribbons, e.g. by heat-resistant conveyor belts or bands
  • C03B35/16—Transporting hot glass sheets or ribbons, e.g. by heat-resistant conveyor belts or bands by roller conveyors
  • C03B35/18—Construction of the conveyor rollers ; Materials, coatings or coverings thereof
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
  • C03B35/00—Transporting of glass products during their manufacture, e.g. hot glass lenses, prisms
  • C03B35/14—Transporting hot glass sheets or ribbons, e.g. by heat-resistant conveyor belts or bands
  • C03B35/16—Transporting hot glass sheets or ribbons, e.g. by heat-resistant conveyor belts or bands by roller conveyors
  • C03B35/18—Construction of the conveyor rollers ; Materials, coatings or coverings thereof
  • C03B35/185—Construction of the conveyor rollers ; Materials, coatings or coverings thereof having a discontinuous surface for contacting the sheets or ribbons other than cloth or fabric, e.g. having protrusions or depressions, spirally wound cable, projecting discs or tires
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
  • C03B35/00—Transporting of glass products during their manufacture, e.g. hot glass lenses, prisms
  • C03B35/14—Transporting hot glass sheets or ribbons, e.g. by heat-resistant conveyor belts or bands
  • C03B35/16—Transporting hot glass sheets or ribbons, e.g. by heat-resistant conveyor belts or bands by roller conveyors
  • C03B35/18—Construction of the conveyor rollers ; Materials, coatings or coverings thereof
  • C03B35/189—Disc rollers
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F27—FURNACES; KILNS; OVENS; RETORTS
  • F27B—FURNACES, KILNS, OVENS OR RETORTS IN GENERAL; OPEN SINTERING OR LIKE APPARATUS
  • F27B9/00—Furnaces through which the charge is moved mechanically, e.g. of tunnel type; Similar furnaces in which the charge moves by gravity
  • F27B9/28—Furnaces through which the charge is moved mechanically, e.g. of tunnel type; Similar furnaces in which the charge moves by gravity for treating continuous lengths of work
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F27—FURNACES; KILNS; OVENS; RETORTS
  • F27D—DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
  • F27D3/00—Charging; Discharging; Manipulation of charge
  • F27D2003/0034—Means for moving, conveying, transporting the charge in the furnace or in the charging facilities
  • F27D2003/0067—Means for moving, conveying, transporting the charge in the furnace or in the charging facilities comprising conveyors where the translation is communicated by friction from at least one rotating element, e.g. two opposed rotations combined
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T29/00—Metal working
  • Y10T29/49—Method of mechanical manufacture
  • Y10T29/49544—Roller making
  • Y10T29/49547—Assembling preformed components
  • Y10T29/49549—Work contacting surface element assembled to core
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T29/00—Metal working
  • Y10T29/49—Method of mechanical manufacture
  • Y10T29/49544—Roller making
  • Y10T29/49547—Assembling preformed components
  • Y10T29/49549—Work contacting surface element assembled to core
  • Y10T29/49554—Work contacting surface having annular axial sections
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T29/00—Metal working
  • Y10T29/49—Method of mechanical manufacture
  • Y10T29/49544—Roller making
  • Y10T29/49547—Assembling preformed components
  • Y10T29/49556—Work contacting surface element assembled to end support members

Definitions

• This invention relates to the manufacture of sheet glass. More particularly, the invention relates to improved pulling rolls for use in controlling the thickness of glass produced by, for example, the overflow downdraw fusion process.
• the invention is of particular value in the production of high quality sheet glass, which exhibits low levels of surface defects.
• Such glass can be used as substrates for flat panel displays, e.g., liquid crystal displays.
• Pulling rolls are used in the manufacture of sheet glass to apply tension to the ribbon of glass from which the sheets are formed and thus control the nominal sheet thickness.
• pulling rolls are placed downstream of the tip or root of the fusion pipe and are used to adjust the rate at which the formed ribbon of glass leaves the pipe and thus determine the nominal thickness of the finished sheet.
• Pulling rolls are preferably designed to contact the glass ribbon at its outer edges, specifically, in regions just inboard of the thickened beads which exist at the very edges of the ribbon.
• a preferred construction for such rolls employs discs of a heat resistant material, which are mounted on a driven shaft. Examples of this construction can be found in Moore, U.S. Patent No. 3,334,010, Asaumi et al., U.S. Patent No. 4,533,581, and Hart et al., U.S. Patent No. 5,989, 170.
• a successful pulling roll needs to meet a number of conflicting criteria.
• the roll needs to be able to withstand the high temperatures associated with newly formed glass for substantial periods of time. The longer a roll can last in such an environment the better, since roll replacement reduces the amount of finished glass a given machine can produce and thus increases the ultimate cost of the glass.
• the roll must be able to produce enough pulling force to control the glass' thickness.
• the roll In order not to damage the central portion of the ribbon that becomes the usable finished glass, the roll can only contact the ribbon over a limited area at its edges. Thus, the required pulling forces must be generated using only this area. However, the forces applied to the glass cannot be too large since this can create surface damage which can propagate into the usable central portion of the ribbon. Accordingly, the roll must achieve a balance between applying too little and too much force to the edge regions of the glass.
• the pulling roll must not give off excessive amounts of particles which can adhere to the glass and form surface defects (known as "onclusions").
• the invention provides a roll (13) for pulling a glass ribbon (11) comprising:
• a pair of fittings e.g., outer collars (25) or the combination of an outer collar (25) and an inner collar (31) affixed to the shaft, said fittings being spaced from one another along the shaft by a distance which causes an axial compressive force to be applied to the discs; wherein when the discs are subject to said axial compressive force, the one or more portions of the roll surface that are adapted to contact the glass ribbon have a Shore D hardness at room temperature (e.g., 23°C) of between 30 and 55.
• the invention provides a method for producing a pulling roll of the above type, said method comprising:
• step (c) monitoring the amount of force used in step (b) to compress the discs and adjusting the number of discs if said force is outside a predetermined range; wherein the predetermined range in step (c) is selected so that one or more portions (27) of the roll's surface (33) that contact the glass ribbon (11) during use of the roll have a Shore D hardness at room temperature of between 30 and 55.
• the number of discs ultimately assembled on the shaft and locked in place by the fittings will typically be in the 200-400 range depending on the size of the glass ribbon being produced, although more or less discs can be used in the practice of the invention if desired. For example, less discs will typically be used in the embodiment of Figure 6.
• the heat-resistant discs are preferably pre-fired prior to assembly to form the pulling roll so that they exhibit substantially no compositional changes when exposed to the temperatures at which the roll pulls the glass ribbon and thus will be dimensionally stable under operating conditions.
• the heat-resistant discs in addition to comprising refractory ceramic fibers, mica, and a heat resistant binder, preferably also comprise cellulose fibers, which are burned off during the pre- firing.
• any non-heat resistant materials which the discs contain can be removed in situ as the roll is put into service.
• the pressure used to assemble the roll should be adjusted (increased) to take account of the material that will burn off from the roll when exposed to the hot environment surrounding the newly-formed glass ribbon.
• the pressure should be increased so that after the in situ burnout, the one or more glass-engaging portions of the roll surface will have the required Shore D hardness at room temperature of between 30 and 55.
• the pulling rolls of the invention have been found to achieve a long service life without applying excessive force to the glass ribbon or generating high levels of particulate contamination.
• the service life of a roll can often be prematurely shortened by outside events that damage the roll (e.g., a fracture of the glass ribbon).
• the pulling rolls of the invention easily achieve long service lives, e.g., service lives in excess of 40 days, preferably in excess of 75 days, and most preferably in excess of 100 days.
• Figure 1 is a perspective view showing the use of pulling rolls constructed in accordance with the invention to pull a ribbon of newly formed glass.
• Figure 2 is an expanded view of the left hand portion of Figure 1.
• Figure 3 is an end view of the pulling rolls and glass ribbon of Figure 1.
• Figure 4 is a front cross-sectional view of a pulling roll constructed in accordance with the invention.
• Figure 5 is a perspective view, partially in section, of a pulling roll constructed in accordance with the invention and having a hexagonal shaft.
• Figure 6 is a front view of a pulling roll constructed in accordance with the invention and having semi-compliant discs only in the vicinity of the places where the pulling roll makes contact with the glass ribbon.
• the reference numbers used in the drawings correspond to the following:
• Figure 1 a perspective view of a pair of pulling rolls 13 engaging a glass ribbon 11, e.g., a newly-formed ribbon of LCD glass formed by an overflow downdraw process.
• Figures 2 and 3 show the engagement of the pulling rolls with the glass ribbon in more detail.
• each pulling roll 13 includes a shaft 17 which carries a plurality of discs 15 which are held in place by collars 25. Collars 25 are preferably locked in place on shaft 17 by split retaining rings (snap rings) 21 which seat in grooves 23 formed in the shaft. Although retaining rings are preferred, other mechanisms known in the art for attaching a collar to a shaft can be used if desired. Also, although collars are preferred, any type of fitting which can apply an axial compressive force to the heat-resistant discs when affixed to the shaft can be used in the practice of the invention. It should be noted that for each pair of fittings, only one of the fittings has to be removable to allow discs 15 to be assembled onto shaft 17. The other fitting can be permanently attached to the shaft or can be integrally formed as part of the shaft. The word "affixed" as used herein is intended to cover these various alternatives.
• the fully assembled pulling rolls can include bearing surfaces 19 at the ends of shaft 17.
• preferred materials include a cast stainless steel alloy for the shaft, e.g., a centrifugal cast HP 45 alloy, in combination with stainless steel bearing surfaces, e.g., 330 stainless steel.
• discs 15 when first mounted on shaft 17 preferably all have, or are cut to have, the same diameter (see the right hand portion of Figure 4) with an overall contour subsequently being cut in the discs to leave raised areas (flats) 27 and recessed areas 29 (see the left hand portion of Figure 4) .
• Figure 5 shows an alternate construction for pulling roll 13 where shaft 17 has a non-circular cross section, specifically, a hexagonal cross-section in this figure.
• a non-circular cross- section can be used if excessive amounts of rotation of discs 15 about shaft 17 should be observed in a particular application of the pulling roll of the invention.
• disc 15 will include a central aperture whose shape corresponds to that of the non-circular shaft, i.e., the central aperture instead of being round will have the same non- circular shape as the shaft.
• a non-circular cross section can be formed in the shaft by starting with a circular shaft and then machining the shaft to the desired configuration, e.g., by machining a shaft composed of carbon steel.
• Cast or drawn shafts can also be used in this embodiment of the invention.
• rotation of discs 15 about shaft 17 does not occur to any substantial degree and thus shafts having a circular cross-section can be used and are preferred.
• Figure 6 shows a further alternate pulling roll configuration which can be used in the practice of the invention.
• reducing the outer diameter of the discs located in central recessed area 29 is advantageous because in addition to avoiding contact with the glass, such a reduction minimizes at least to some extent the amount of material at the center of the roll which can become airborne and adhere to the glass ribbon to form defects.
• the flat location becomes more prone to lose integrity and thus reduce the life of the roll.
• the flat location is compacted and the discs at this location lose elasticity, which manifests itself through pronounced slippage of the glass ribbon.
• the integrity of the roll is so degraded that the flats deform enough to warp the glass ribbon so that the finished sheet does not conform to production specifications.
• a coating is preferably applied to the shaft to reduce the chances of oxidation of the metal making up the shaft, e.g., stainless steel.
• Suitable coatings include various ceramic coatings, such as CERAK M-720 Black Ceramic Coating distributed by Cetek Limited of Berea, Ohio.
• two inner collars 31 are affixed to shaft 17 using, for example, split retaining rings of the type discussed above in connection with outer collars 25. These inner collars enhance the packing pressure near the flats and therefore improve roll life.
• An additional benefit of this embodiment of the invention is that it allows a higher level of cooling of the glass at the location of the pulling rolls. Such additional cooling is of value since glass temperatures at this location, which can be as high as 800°C, dictate the amount of warp and stress the glass ribbon experiences and thus the finished sheet will exhibit.
• the embodiment of Figure 6 can be used with a circular or non- circular shaft and can employ bearing surfaces 19.
• discs 15 Whatever configuration is used for the pulling rolls (i.e., the configurations shown in Figures 1-6 or other configurations now known or subsequently developed), the ultimate success of a roll depends on the properties of discs 15.
• discs of a specific composition which have been pre-fired and assembled in a particular manner are used to form the pulling rolls of the invention. Such discs have been found to meet the service life, controlled force application, and low contamination criteria discussed above.
• the discs need to be substantially non-friable when subjected to the forces and operating temperatures involved in pulling a newly-formed glass ribbon.
• the discs comprising refractory ceramic fibers, mica, and a heat resistant binder have this property.
• the discs after any non-heat resistant components have been burned off, the discs preferably comprise by weight: 10-20% refractory ceramic fibers, 40- 50% mica, and 40-50% heat resistant binder.
• the discs are most preferably: (1) a composite of clay, mica, glass fibers, and cellulose fibers; and (2) pre-fired so that they exhibit substantially no compositional changes when exposed to the temperatures associated with a pulling roll during use and will thus be dimensionally stable under operating conditions.
• the pre-firing can comprise heating the discs to a temperature of 700- 800°C, preferably 760-800°C (e.g., to 760°C), holding them at that temperature for a period of at least two hours, and then cooling them back to room temperature before assembly onto the pulling roll's shaft.
• Pre-firing to such temperatures ensures that the disc material experiences all phase changes prior to use and thereby reduces variability of the material after it has entered into service.
• Other pre- firing times and temperatures can, of course, be used in the practice of the invention so long as they provide a finished pulling roll whose composition is stable at the rolls' operating temperature.
• a composite having the above composition is commercially available from Nichias Corporation of Tokyo, Japan, under the product designation SD- 115.
• This product is supplied in sheets having a thickness of about 6 millimeters and can be cut into discs having a circular outer perimeter (e.g., a diameter of 140 mm) and a center aperture (e.g., a circular aperture having a diameter of 64 mm) using, for example, a water jet cutter or an appropriately sized punch, punching being preferred.
• sheets of the composite can be prepared by, for example: (1) forming a water slurry of clay (e.g., GLOMAX LL), mica, glass fibers (e.g., 10 wt.% Al 2 0 -Si ⁇ 2 fibers), wood fiber (e.g., HIBRITE from Canada), and starch; (2) forming layers from the slurry using a rotary drum “paper making” machine; (3) stacking the layers (e.g., 20 layers) to make a millboard 6 mm thick; (4) draping the millboard over a drying rack to air dry for at least 24 hours; and (5) placing the drying rack in an oven at 110°C for 24 hours.
• clay e.g., GLOMAX LL
• mica e.g., mica
• glass fibers e.g., 10 wt.% Al 2 0 -Si ⁇ 2 fibers
• wood fiber e.g., HIBRITE from Canada
• starch e.g., a
• the assembly of the discs onto the shaft of the pulling roll is critical to the success of the invention.
• the compression force (pressing force) used in assembling the discs to form the pulling roll must be carefully controlled to achieve a long service life. For example, as discussed in more detail below, it was found that a compression force of approximately 33,000 pounds resulted in a pulling roll having only a limited life (i.e., 39 days), while a compression force of 11 ,000 to 14,000 pounds resulted in a roll having a much longer life (i.e., greater than 100 days).
• these forces correspond to axial pressures of approximately 2,250 psi for the high compressive force and approximately 750-950 psi for the low compressive force.
• the Shore hardness (specifically, the Shore D hardness) of the outer surface of the assembled roll and, in particular, the portions of the outer surface that will come into contact with the glass ribbon during use of the roll.
• Shore D hardness the Shore D hardness of these glass-engaging portions of the outer surface of the pulling roll must be in the range of 30 to 55 and preferably in the range from 40 to 55 to achieve a long service life.
• a Shore D hardness in these ranges allows the surface of the pulling roll to comply with the glass surface thereby reducing surface damage that results in checking.
• the Shore D hardness is measured using commercially available equipment. Without intending to limit it in any manner, the present invention will be more fully described by the following comparative examples.
• COMPARATIVE EXAMPLE 1 This example compares various materials used to form the discs of a pulling roll, as well as the compression force used to assemble the discs on the pulling roll shaft.
• the following materials were tested: (1) ZYALITE — a mixture of alumino silicate fibers and amorphous silica (colloid) sold by Vesuvius McDanel of Beaver Falls, PA; (2) ZYAROCK - a porous fused silica also sold by Vesuvius McDanel; (3) Nichias SD- 115 compressed at approximately 33,000 pounds (approximately 2,250 psi) (Dense Nichias); and (4) Nichias SD-115 compressed at 11,000 to 14,000 pounds (approximately 750-950 psi) (Less Dense Nichias). The results were as follows:
• Dense Nichias This material performed well compared to the above materials except roll life was short. The high density of the roll seems to encourage damage to the glass ribbon by collecting glass on the roll surface. Relatively high penetration hardness did not allow adhered glass to "sink” into the surface of the roll. (4) Less Dense Nichias — This material performed well compared to all of the above. It delivered long service life without onclusions or significant wear of the material. Although not wishing to be bound by any particular theory of operation, it is believed that this superior performance was due to the material having a low elastic modulus and low penetration hardness. The material was able to conform to the glass without generating excessive stress and glass particles on the roll surface were able to become "embedded” in the material without causing excessive damage.
• This example illustrates the importance of controlling the compression force applied to the discs in the assembly of the pulling roll.
• Five rolls made from the Nichias SD-1 15 material were tested. The rolls had the following properties and service lives where the reference in this table to compression of the discs with high pressure means a pressing force of approximately 33,000 pounds (approximately 2,250 psi) and compression with low pressure means a pressing force of 1 1,000 to 14,000 pounds (approximately 750-950 psi):
• Roll 4 is believed to have had a longer service life than rolls 1-3 because although this roll was pressed with high pressure, it was not pre-fired and as a result, it experienced in situ burnout. The in situ burnout and concomitant loss of non-heat resistant material produced a reduction in the effective pressing force. Accordingly, roll 4 behaved as if it had undergone pre-firing and had then been pressed with a low pressing force.
• Rolls 2 and 3 are believed to have had longer service lives than roll 1 because these rolls used stainless steel, rather than carbon steel, shafts.
• the stainless steel shafts had higher CTE's than the carbon steel shaft and thus produced a greater reduction in the effective pressing force on the discs as the roll was heated to operating temperature. That is, in both cases, the shaft expanded more than the discs, but in the case of the stainless steel shafts, more expansion occurred and thus the discs were under less compression during use, which enhanced their service life.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• Mechanical Engineering (AREA)
• General Engineering & Computer Science (AREA)
• Re-Forming, After-Treatment, Cutting And Transporting Of Glass Products (AREA)
• Rolls And Other Rotary Bodies (AREA)
• Rollers For Roller Conveyors For Transfer (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=28675292

Family Applications (1)

Country Status (6)

Cited By (7)

Families Citing this family (69)

Citations (3)

Family Cites Families (36)

• 2003
  • 2003-03-10 KR KR1020107027029A patent/KR101167830B1/ko not_active Expired - Lifetime
  • 2003-03-10 KR KR1020127008283A patent/KR101172245B1/ko not_active Expired - Lifetime
  • 2003-03-10 CN CNB038092433A patent/CN100506728C/zh not_active Expired - Lifetime
  • 2003-03-10 JP JP2003580230A patent/JP2005520774A/ja active Pending
  • 2003-03-10 CN CN200910141415XA patent/CN101560048B/zh not_active Expired - Lifetime
  • 2003-03-10 WO PCT/US2003/007080 patent/WO2003082755A1/en not_active Ceased
  • 2003-03-10 KR KR10-2004-7014925A patent/KR20040102050A/ko not_active Ceased
  • 2003-03-20 US US10/393,488 patent/US6896646B2/en not_active Expired - Lifetime
  • 2003-03-21 TW TW092106893A patent/TWI268912B/zh not_active IP Right Cessation
• 2005
  • 2005-05-19 US US11/132,547 patent/US7284328B2/en not_active Ceased
• 2009
  • 2009-03-25 JP JP2009073385A patent/JP4972114B2/ja not_active Expired - Lifetime
  • 2009-10-22 US US12/604,112 patent/USRE46010E1/en not_active Expired - Lifetime