Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
  • C08J5/18—Manufacture of films or sheets
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
  • B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
  • B65D65/00—Wrappers or flexible covers; Packaging materials of special type or form
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/10—Esters; Ether-esters
  • C08K5/12—Esters; Ether-esters of cyclic polycarboxylic acids
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2327/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers
  • C08J2327/02—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment
  • C08J2327/04—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Derivatives of such polymers not modified by chemical after-treatment containing chlorine atoms
  • C08J2327/06—Homopolymers or copolymers of vinyl chloride

Definitions

• PVC Polyvinyl chloride
• FDA US Food and Drug Administration
• DOA dioctyl adipate
• Performance can be improved by reducing plasticizer volatility. That is, during the production of a PVC film, a portion of the plasticizer may be lost due to its volatility. If there is less plasticizer in the resulting film than desired, the desired physical properties cannot be obtained. Further, if additional plasticizer is used in the process to achieve the desired amount of plasticizer in the resulting film, then costs are increased. After the film is formed, avoiding migration of the plasticizer from the film into the food item can improve performance. Specifically as to reducing costs, one approach to reduce cost is to use a lower cost plasticizer blend a lower cost plasticizer with DOA.
• the inventors propose a food wrap formed from polyvinyl chloride, at least one stabilizer, and a plasticizer in an amount of 10-60 parts per hundred parts polyvinyl chloride.
• the plasticizer may be present in an amount of 30-55 parts per hundred parts polyvinyl chloride.
• the plasticizer includes dioctyl terephthalate. Dioctyl adipate or another plasticizer may be used with dioctyl terephthalate.
• the plasticizer may contain 20 to 80 wt. % dioctyl terephthalate, or more specifically 20 to 60 wt. % dioctyl terephthalate.
• the food wrap may have a thickness of 1 to 80 mils.
• the food wrap is applied to a food article.
• polyvinyl chloride is combined with the plasticizer to form a mixture.
• the mixture is heated and fused.
• a film is formed from the fused mixture.
• approval of the US Food and Drug Administration for this use must be confirmed.
• any given range is intended to include any and all lesser included ranges.
• the range of 45-90 would include the ranges of 50-90, 45-95, 46-89, etc.
• the present invention employs a film formed of polyvinyl chloride with a dioctyl terephthalate (DOTP) ester as a plasticizer.
• DOTP is the ester of terephthalic acid. DOTP can be used alone or in combination with other plasticizers, such as DOA.
• the plasticizer may be present in an amount of
• the plasticizer may be present in an amount of 30-55 PPH. If a mixture of plasticizers is used, the mixture may contain 20 to 80 wt. % dioctyl terephthalate, and more particularly 20 to 60 wt. % dioctyl terephthalate.
• the wrapping film of the present invention has a number of uses but can be employed for hand wrapping various foods and for stretch wrapping them by an automatic wrapping machine. Wrapping films according to one aspect of the present invention have a sufficiently low brittle temperature, thus allowing them be easily used to wrap refrigerated foods.
• Wrapping films according to one aspect of the present invention have a sufficiently high gas permeability, so that spoilage of wrapped perishable food can be avoided. Wrapping films according to one aspect of the present invention have a melt index lower than 20. Such a melt index improves film-forming properties and inhibits the formation of pin holes in the film. In addition, before the film can be sold as a food wrap, approval of the US Food and Drug Administration for this use must be confirmed.
• the dry ingredients such as polyvinyl chloride
• Various stabilizers can be used. These stabilizers can be provided as solid or liquid components.
• the dry components are mixed and heated, and then the liquid components are added. After further mixing and heating to below the fusion temperature, the mixture is fused using conventional fusing equipment.
• the film is made from the PVC/DOTP composition at a temperature of 150 degrees to 230 degrees C by a conventional film-forming method, for example, the T-die method, the inflation method and calendar roller method.
• the T-die method and the inflation method are described in U.S. Patent Nos. 2,736,066 and 2,878,521.
• the wrapping film has a thickness in the range of about 5 to about 100 ⁇ m, more particularly a thickness of 0.5 to 5 mils, and still more particularly a thickness of 10 to 30 microns.
• Wrapping films according to one aspect the present invention have sufficient, but not excessive stickiness.
• the wrapping film should have an adhesive strength of not less than 20 g/2 cm 2 and more particularly an adhesive strength within the range of 200 g/2 cm 2 to 700 g/2 cm 2 .
• Excessive stickiness results in the following disadvantages.
• the film is used to hand-wrap something, its workability is very poor because pieces of the film undesirably adhere to each other.
• the film is used for automatically wrapping something, its workability is very poor and the resultant package has a bad appearance, because the film sometimes undesirably winds onto the conveyor rollers due to its high stickiness.
• an undesirable necking phenomena often occurs when the film comes into contact with trays which receive the articles or food to be wrapped, due to the high adhesiveness of the film to the tray.
• the wrapping film should possess a smooth sliding property against rolls of a wrapping machine or against articles to be wrapped.
• the wrapping film should have a static friction coefficient (ASTM D1894 (1973)) of not more than 0.55.
• the wrapping film should also be relatively transparent. More specifically, a transparency such that the total light transmittance is at least 80%, is desired.
• PVC films were produced, using several different plasticizer formulations. Specifically, a first PVC film used 100 wt.% DOA as the plasticizer. A second PVC film used 100 wt.% DOTP as the plasticizer. A third PVC film used a plasticizer blend formed from 75 % wt.% DOA and 25 wt.% DOTP. Finally, a fourth PVC film used a plasticizer blend formed from 75 wt.% DOTP and 25 wt.% DOA.
• each of the PVC films was formed according to a similar process.
• the dry ingredients were combined.
• powdered PVC resin sold commercially by Oxyvinyl Corporation under the trade name Oxy 230TM was used.
• the PVC powder had an internal viscosity IV of 0.95 and a molecular weight factor K of 68.
• the powdered PVC resin was combined with a solid calcium zinc stabilizer sold commercially by Witco Corporation under the trade name Mark QTSTM to form a mixture.
• the mixture was blended in a Henschel mixer. With frictional heating, the temperature was raised to approximately 110°F. Then, the liquid ingredients were slowly added.
• the liquid ingredients include the plasticizer, DOA, DOTP or a mixture thereof, an epoxidized soybean oil (ESO) and a liquid calcium zinc stabilizer sold commercially by Akzo Chemical under the trade name CZL-720TM.
• the mixture was blended until a temperature of 191 °F was reached, at which temperature PVC is below its fusion temperature. This produced a free flowing powder of PVC particles having the other ingredients absorbed therein.
• the free flowing powder was then fused on a 2 roll mill at a temperature of 290 to 300°F. This produced a fused PVC sheet, which was compression molded into 70 mill sheets.
• the sheets were then cut to obtain samples, which sample were tested using ASTM procedures. More particularly, the modulus of elasticity and the tensile strength are measured according to ASTM D142.
• the tear resistance was measured according to ASTM D624, and the brittleness temperature was measured according to ASTM D746.
• a loop test was performed.
• a sample of the material was folded. A 70 mil sample was used, and this is relatively thick compared to the 1 to 5 mil thickness used in food wraps. The folded condition was maintained for a certain amount of time. After this, the film is unfolded and then adsorbent paper is rubbed across the crease. The paper was pbserved to determine how much plasticizer escaped due to pressure of the relatively thick material being folded.
• Loop test migration is not directly related plasticizer migration in a food wrap. That is, food wrap plasticizer migration is not caused by pressure folding a relatively thick material. Nonetheless, the loop test does provide some preliminary indication of plasticizer migration in food wrap.
• Tables 3 and 4 show additional samples formulated using the same ingredients as those for Tables 1 and 2.
• Table 3 uses the same formulations as Table 1.
• Table 4 uses a lower plasticizer level then than Tables 1 and 3.
• additional tests were performed to analyze the behavior of thin films, such as would be used for wrapping food. Specifically, 20 mil sheets were subjected to a cotton seed oil extraction test, a 1% soapy water extraction test, a hexane extraction test and a carbon extraction test. For the cotton seed oil, soapy water and hexane extraction tests, samples of the films were placed in the various liquids. After a predetermined time period was allowed to elapse, the samples were tested to determine the percentage of weight loss.
• This weight loss may be attributed to plasticizer migration out of the film.
• a disc of the film was heated to a predetermined temperature in the presence of a charcoal/carbon filter.
• the filter absorbed volatile organic compounds escaping from the heated disc. Again, the results of the test show the percentage of weight loss of the film.
• the cotton seed oil, soapy water and hexane extraction tests were performed according to ASTM D1239.
• the carbon extraction test was performed according to ASTM D1203.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Manufacturing & Machinery (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Mechanical Engineering (AREA)
• Materials Engineering (AREA)
• Wrappers (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Packging For Living Organisms, Food Or Medicinal Products That Are Sensitive To Environmental Conditiond (AREA)
• Manufacture Of Macromolecular Shaped Articles (AREA)
• Laminated Bodies (AREA)
• Treatments Of Macromolecular Shaped Articles (AREA)

Priority Applications (3)

Applications Claiming Priority (4)

Publications (1)

Family

ID=26972352

Family Applications (1)

Country Status (6)

Cited By (3)

Families Citing this family (31)

Citations (8)

Family Cites Families (4)

• 2001
  • 2001-11-26 US US09/992,483 patent/US6675560B2/en not_active Expired - Lifetime
• 2002
  • 2002-06-18 EP EP02739918A patent/EP1406954B1/en not_active Expired - Lifetime
  • 2002-06-18 JP JP2003509016A patent/JP4373205B2/ja not_active Expired - Fee Related
  • 2002-06-18 WO PCT/US2002/019265 patent/WO2003002640A1/en not_active Ceased
  • 2002-06-18 DE DE60221398T patent/DE60221398T2/de not_active Expired - Lifetime
  • 2002-06-18 AT AT02739918T patent/ATE368068T1/de not_active IP Right Cessation

Patent Citations (8)

Non-Patent Citations (6)

Also Published As

Similar Documents

Legal Events