WO2001030722A1 - Briquette frittee en ceramique composite a structure de base en wc - Google Patents

Briquette frittee en ceramique composite a structure de base en wc Download PDF

Info

Publication number
WO2001030722A1
WO2001030722A1 PCT/JP2000/007477 JP0007477W WO0130722A1 WO 2001030722 A1 WO2001030722 A1 WO 2001030722A1 JP 0007477 W JP0007477 W JP 0007477W WO 0130722 A1 WO0130722 A1 WO 0130722A1
Authority
WO
WIPO (PCT)
Prior art keywords
sintered body
wcxoy
ceramic sintered
vol
composite ceramic
Prior art date
Application number
PCT/JP2000/007477
Other languages
English (en)
French (fr)
Inventor
Mitsuyoshi Nagano
Shigeya Sakaguchi
Norimitsu Mukae
Kouki Minamoto
Toyoshige Sasaki
Original Assignee
Nippon Tungsten Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Tungsten Co., Ltd. filed Critical Nippon Tungsten Co., Ltd.
Priority to US09/869,241 priority Critical patent/US6551954B1/en
Priority to EP00970077A priority patent/EP1146025B1/en
Publication of WO2001030722A1 publication Critical patent/WO2001030722A1/ja

Description

明 細 書
wc基複合セラミックス焼結体 技術分野
本発明は、 耐摩耗性を必要とする機械の摺動部品、 ポリエチレンなどの高分 子やアルミニウム合金などの金属を切断する刃物、 金属や高分子材料の曲げ、 切断などを行うプレス用金型に使用する WC基複合セラミックス焼結体に関す る。 背景技術
従来、 機械の摺動部品、 切断刃、 金型などの耐摩耗部材はダイス鋼などに代 表される鉄系金属材料が主に用いられてきた。 しかしながら、 このような金属 材料では耐摩耗性が不足しており、 これに代えて、 Z r O z系、 S i 3N 4系の セラミックスが利用されるようになった。
特に、 精密な製品サイズを要求されるプレスでは、 被プレス材との溶着が発 生し易い上に摩耗が早いために、 耐摩耗性に優れた長寿命の金型材料が求めら れている。
このような要求に対し、 金属材料よりも硬さが高く、 耐溶着性に優れたセラ ミックス金型材料として、 特公平 1一 2 4 7 4 7号公報 （特開昭 5 8 - 1 2 0 5 7 1号公報）、 特開平 3— 5 1 6 6 7号公報、 特開平 9一 2 2 1 3 5 2号公 報には、 Z r 02ラミックスに遷移金属の炭化物、 窒化物粒子によって分散強 化した金型材料が開示されている。
セラミックスを上記の摺動部品、 刃物、 金型材料に適用する場合、 特に、 金 型材料に要求される特性は、 ヤング率、 硬さ、 熱伝導率、 それに、 電気的加工 性の 4点である。
まず、 ヤング率についていうと、 従来のダイス鋼を中心とした鉄系金属材料 や強度 ·靭性が高いジルコニァを主成分としたセラミックス系の材料は、 ヤン グ率が 2 . 5 G P a以下と低く、 摺動時の相手材との高速運動時に剛性がない ために、弾性変形を生じ、相互に過大な摩擦を引き起こして異常摩耗を生じる。 鉄系材料の場合は異常摩耗であり、 Z r O 2系の場合には過大な摩擦熱による 結晶変態による粒子の脱落摩耗である。 この摩耗は部品の寿命を左右し、特に、 精密な動きを要求される分野においては、 致命的であった。
次に、硬さにおいては、従来の金属系材料に対するセラミックスの優位性は、 硬さが高いことに起因する耐摩耗性の向上にあるが、 ジルコニァを主成分とし たセラミックス系の金型材料は、 硬さが十分ではなく、 耐摩耗性、 すなわち、 寿命が短いという欠点がある。
WCはフリー力一ボンを含有しており、 不活性雰囲気での焼結において、 焼 結体中にフリーカーボンが残存し、 破壊の起源となって、 強度低下を引き起こ していた。 また、 Z r 02— WC複合体の場合、 それぞれの熱膨張係数が異な り、 それそれが炭化物と酸化物であって、 相互に固溶しないことから、 高温で ある焼結状態から低温である室温に降温した段階で、 熱膨張差によるクラック が残り易く、機械的性質、特に、 曲げ強度で低強度で破壊しやすい傾向がある。 また、 さらに、 熱伝導率についていうと、 高速運動時には、 摩擦は熱を発生 するが、 熱伝導率が低い場合には熱がこもりやすく、 ジルコニァ主成分の熱に よる相転移を起こし、 変態破壊に至る場合がある。
さらに、電気的加工性についていうと、近年の部品は、機械加工のみならず、 ワイヤ一カットや放電加工などで加工するといつた、 電気的加工が進歩し、 電 気加工の面状態で使用するケースが増加する傾向にある。電気加工面は、超硬、 導電性を付加したジルコニァ系セラミックス材料においても、 金型材料の内部 組織の微細さと均一性が不足しており、 その結果、 面粗度が低下して電気加工 の面状態で使用することができなかった。
本願発明において解決すべき課題は、 摺動部品、 刃物、 金型材料として要求 されるヤング率、 硬さ、 熱伝導率、 それに、 電気的加工性の特性を十分に充足 するセラミックス焼結体を得ることにある。 発明の開示 本発明は、 WCxO O. 005<yZx + y<0. 05) の化学式で表さ れる酸素を固溶した WCを 40体積％以上 9 0体積％以下と、 残部が Y2〇3, C e02, Mg〇の 1種又は 2種以上を安定化剤として含む部分安定化 Z r 02 及び不可避不純物からなる WC基複合セラミックス焼結体である。
この WC— Z r〇2系セラミックス焼結体は、 焼結する前の原料調整紛を酸 素が存在する雰囲気下、 200" 以上 600で以下の温度域で 0. 1時間から 3時間保持することによって、 WCを WCXOY(0. 005<y/x + y<0. 0 5) の化学式で表される酸素を固溶した WC粒子とし、 その粒界を埋める相 として、 Y2〇3， Ce02, MgOの 1種又は 2種以上を安定化剤として含む 部分安定化 Z r〇2セラミックス材料とし、 さらに、 不活性ガス中で 2023 K~2 1 2 3 Kの温度域で普通焼結あるいは、 ホットプレス焼結することによ つて得ることができる。 同時に、 上記酸化熱処理によって、 WC粒子中のフリ —カーボンを除去することが可能となり、 その結果、 複合材の結晶粒子の耐脱 落性が改善でき、 硬さ、 靭性、 強度が向上し、 電気抵抗を下げて電気加工性と 熱伝導率が改善される。 発明を実施するための最良の形態
以下、 本願発明の実施の形態を実施例によって説明する。
表 1に示す原料配合物を、 主成分として、 平均粒子径が 0. 5 mの WC粉 末に、 平均粒子径が 0. 5 mで、 3モル％の丫203で部分安定化した Z r〇 2を所定量添加し、 メタノール溶媒中で焼結体の純度が 9 9. 5 %以上の Z r 02ボールを入れたナイロンポット中にて 20時間分散混合を行った。 得られ たスラリー取り出した後、 アルコール系のバインダーを添加して、 クローズド スブレードライヤ一によって窒素雰囲気中で造粒乾燥を行い調製した。
得られた調製造粒粉を 4 X 5 45 mmの曲げ試験片、 Φ 2 0 X 3 t mmの 熱伝導率測定用試料を金型プレスで作製し、 真空雰囲気中 50 0での温度で 1 時間保持して脱脂を行った。 脱脂後に、 得られたプレス体を大気雰囲気中、 4 0 ox:cで 1時間熱処理し、 WC粒子に酸素を導入した。 その後、 アルゴンガ ス中、 2 0 2 3 K〜2 1 2 3 Κの温度域で普通焼結を行った。 得られた試料の 一部を、 1 9 2 3 Κ〜2 0 2 3 Κの温度域で窒素ガスを用いた H I Ρ処理を行 つた。 また、 酸化熱処理は、 原料紛、 もしくは、 造粒乾燥後の調整紛の状態で 行っても同様な効果が得られる。
また、 脱脂を行った 5 0 X 5 0 X 5 mmのプレス体をそのサイズをカーボン ダイスに入れ、 ホットプレス焼結を行った。 2通りの焼結法で作製した試料を それぞれ加工して機械的性質熱伝導率測定を行った。
得られた試料を研削加工し、 硬さや曲げ強度などの物性調査と熱伝導率など の熱的特性の測定を行なった。
WC中の酸素暈は得られた焼結体の X線回折において、 低角度側の WCと W 〇3の回折強度を測定し、 その Cと Oの比率を決定した。
以上の測定結果を表 1に示す。 また、 それぞれの測定結果からそれぞれの成 分の効果として以下のことがいえる。
Figure imgf000007_0001
温度 £300°C 上 水中落下法 0 S度差 250~300¾
X S度 ¾250 以下 ワイヤ-カット © 面粗度 Ra 1.5wm以下 面の面粗度 o 面粗度 Ra 1.5~2. Ομιτι
X 面粗度 Ra 2. Oitm以上 攆動庫耗 ◎ 犀耗量 50jum以下
0 耗量50~100//01以下 ：
X 縻耗置 100/im以上
1 . Z r 02添加量と焼結性との関係
WC粒子は、 硬さやヤング率が高く、 導電性に優れ、 融点が高いという優れ た性質を有している。 しかし、 焼結性に乏しいため、 単体での焼結が困難であ るため、 超硬合金のように C oや N iのような金属を添加してバインダー相と し、 焼結体の構造としている。 しかしながら、 硬さに左右される耐摩耗性や高 温特性などの評価では、 バインダー相である金属の性質が顕著に現れる。 本発 明では、 C oや N iのような金属バインダー相の代わりに、 セラミックスの中 でも強度、 靭性が高い Z r 02を用いることで、 ほぼ、 理諭密度に近い密度に 焼結することが可能となった。
WCの成分量は、 Z r 02の添加量による焼結性に依存しており、 少なくと も、 2 0体積％の添加量で緻密で、 Z r 02による高い強度を示す焼結体が得 られることが認められた。
Z Γ θ 2成分は、 2〜4モル％添加した Υ 2〇3で安定化した Z r〇2が好まし いが、同じく M g Oや C e〇2で安定化した Z r 02でも同様な効果が得られる。 ただし、 Z r 02量が 2 0体積％以下の場台には、 焼結性が確保できず、 気孔 の多い焼結体となり、 強度や硬さが低下する。 また、 6 0体積％以上では、 Z r〇2の性質が顕著に現れて、 硬さの低下による耐摩耗性の低下や Z r 02特有 の摩擦熱による相変態を伴う粒子の脱落が発生し、 摺動摩耗特性に劣ることか 認められた。
2. フリ一カーボンの除去効果
WCは、 フリーカーボンを含有しているために、 アルゴンなどの不活性ガス 雰囲気内では、 カーボンの塊として残存しやすく、 破壊の起源になり、 低強度 の原因となっていた。 本発明のように、 圧粉体の段階で酸化熱処理し、 フリー カーボンを炭化水素化合物として昇華させることで、 除去が可能となり、 高い 強度を確保することか可能となった。 表 1の実施例である N o . 1〜9が、 最 低強度の強度低下率か 1 5 %以下であるのに対し、範囲外の同組成である N o . 1 6〜1 9は、 ほとんどの諸特性に差が少ない傾向にあるが、 フリー力一ボン が残存しているために、 最低強度が低く、 2 5 %以上の低下を引き起こしてい る。
3. WCへの酸素固溶量
WCの酸化は 600 までで徐々に進行し、 600で以上では急激に酸化が 進行する。 酸化が進むと酸素固溶量が増大し、 WCx〇Yにおける yZx + yの 値が 0. 05以上になると、 WC表面が酸化皮膜を形成し、 強度低下の原因と なり、 また、 絶縁体である酸化皮膜によって、 電気伝導性が阻害される。 よつ て、 WCの酸素固溶量は、 WCXOY (0. 005<y/x + y<0. 05) の 範囲にあることが好ましい。 酸素固溶量の増加によって、 表 1の実施例である No. 1〜9と範囲外の同組成である No. 20〜 23との比較で、 強度低下 率、 熱伝導率、 電気抵抗に差があり、 動的特性として、 ワイヤ一カットの面粗 度ゃ摺動摩耗特性が劣る。
4. WCXOYに Z r O2を配合した場合の効果
WCと Z r 02の複合材か優れた特性を有することには以下のような理由が ある。
(1) WCと Z r O2粒子界面における在留応力の発生
熱膨張係数は、 WCが 4X 10— 6、 Z r 02が 10 X 10— 6と大きな差があ り、 焼結温度から降温で室温に戻ったときに、 WCには圧縮応力、 Z r02に は引っ張り応力が働き、 焼結体としての強度、 靭性が大きくなるという効果が ある。 よって、 マトリックスと分散粒子の組み合わせから、 この熱膨脹の差は 本発明の組み合わせの場合がもっとも大きくなるが、 クラックが発生しやすく なるため、 WCXOY (0. 005<y x + y<0. 05) のような酸素固溶 型の WCとして、 結晶粒界の応力緩和を図って、 クラックの発生を抑えること が効果的である。
(2) Z r〇 2の焼結時における超塑性現象
セラミックスは Coや N iを含む超硬合金とは異なり、 焼結時には液相焼結 ではなく、 固相焼結で緻密化が進行する。 例えば、 A 12〇3と WCのような固 相焼結では、 焼結は A 12〇3が律速しており、 結晶組織が緻密化する過程で塑 性流動しないために気孔が残る傾向にある。 しかしながら、 本発明に係る WC XOYと Z r〇2の組み合わせでは、 Z r〇2が焼結温度域で超塑性現象が発現し、 結晶間空隙に Z r〇2が入り込む構造となって、 緻密化が推進され、 また、 W Cのみよりも酸素を微量固溶させた WCXOYの方が緻密化が推進される。 この ため、 単に WCと Z r O 2とを組み合わせて用いた場合よりも少ない Z r 02量 で焼結が可能である。
5. WC量と熱的性質や電気的性質の関係
前述のように、 本願発明の WCXOYと Z r 02粒子との組み合わせでは、 相 互に反応することなく双方が独立した形態で分散しており、 マトリックスであ る WCXOYに対し、 Z r〇2は粒界結合相の働きと同じ粒成長抑制の働きをし ており、 WCと Z r 02との均一分散が可能となる。 また、 残留応力の発生に よって、 強度ゃ靭性、 硬さがこれまでのセラミックスにはない値を示す。 同時 に、 熱的性質や電気的性質には、 今までにない優れた特性を付与することが可 能となった。 表 1に示すように、 WCXOYに Z r 02よりも熱膨脹係率の低い A I 203を配合した場合には、 諸特性の向上の程度は小さい。 これによつて、 WCXOYと Z r02との複合材がもっとも効果的であることがわかる。
特に、 ヤング率は、 300MP a以上となり、 Z r 02系セラミックスや金 属材料に比較して 1. 5倍以上で、 S i 3N4とほぼ同等の剛性が確保でき、 例 えば、 軸受けとスリーブや高速プレスのような高速運動用に適用した時には歪 みや変形が少なく、 摩擦熱の発生が抑えられ、 摺動摩耗が少ないことが認めら れる。
熱的性質では、 Z r〇2量が多いセラミックスは熱伝導率が低いが、 本発明 では熱伝導率の高い WCが主成分となることで、 Z r02単体の 1 0倍以上の 熱伝導率が得られ、 その結果、 急熱急冷に対する熱衝撃抵抗を向上させること が可能となった。
6. WCXOY量と電気的性質の関係
WCXOY自体は導電性が高く、 WCXOY量が多くなるほど、 電気抵抗は低く なる。 導電性は、 WCXOYか 3 0体積％以上でワイヤ一カットなどの電気的加 ェが可能となるか、 電気的加工面の面粗度はその導電性と導電 ^子の分散度合 いによって影響を受けることかわかった。 表 1に示すように、 WCXOY量が 5 0体積％以上であると、 電気的加工面の面粗度が向上することがわかった。
7. WCXOYと Z r 02の分散状態の影響
本発明の材料では、 複合材の各成分の分散状態が機械的、 熱的、 電気的性質 に大きく影響する。 W.Cx〇Y、 Z r〇2の凝集がある場合には、 機械的性質で は破壊の起源となる欠陥として残る。 また、 電気的性質では、 Z r〇2の凝集 は電気的加工ができないために未加工部分として残る。 さらに、 摺動摩耗にお いては、 WCXOY, Z r 02の凝集が異常摩耗になる。 よって、 凝集は WCxO γ, Z r O2それぞれ、 同面積の径に換算して、 10 m以下である必要があり、 その数は、 1 cm2あたりに 3個以下である必要がある。
8. WC量と摺動摩耗特性の関係
摩耗試験は、 径が 50 mm ·内径 4 Omm ·長さ 50mmの超硬合金の円筒 の内側に、 径が 40 mm ·内径 30 mm ·長さ 50 mmの本発明材料及び比較 材料の試料を挿入し、 円筒 500 r pmで回転し、 3分間摺動したものの摩耗 を測定した。内側のスリーブの外径摩耗量を測定した。その結果を表 1に示す。 W C X O γの添加量が多くなるにしたがつて摩耗量は少なくなる傾向にあるが、 その理由として以下のようなことが考えられる。 ヤング率が高いと、 高速運動 時の歪みや変形が少なく、 変形によって片当たりなどで発生する異常摩耗や発 熱が少なくなり、 摩耗が抑制される。 ヤング率は 300MP a以上は必要とな る。 範囲外の WCx〇Y40体積％以下のものや比較例の Z r〇2単体では、 ャ ング率が 300MP a以下となり、耐摩耗性に劣ることが認められる。さらに、 WCXOYは炭化物であるために固体潤滑性に富むため、 その量か多くなるにつ れ、 摺動摩耗は小さくなる傾向にある。 表 1に示すように、 その特性は WCが WCXOYが 50体積％以上で顕著に示されることとなる。 本発明の WC基複合 セラミックス焼結体は、 機械的性質、 熱的性質、 電気的加工性、 摺動特性に優 れ、 長寿命の摺動部品、 刃物、 金型材料が得られる。. 産業上の利用可能性 本発明は、 耐摩耗性を必要とする機械の摺動部品、 ポリエチレンなどの高分 子やアルミニウム合金などの金属を切断する刃物、 金属や高分子材料の曲げ、 切断などを行うプレス用金型に使用する。

Claims

請 求 の 範 囲
1. WCXOY(0. 005<y/x + y<0. 05 ) の化学式で表される酸素 を固溶した WCを 40体積％以上 90体積％以下と、
残部が Υ2〇3， Ce〇， MgOの 1種又は 2種以上を安定化剤として含む部分 安定化 Z r〇2及び不^避不純物からなる WC基複合セラミックス焼結体。
2. 焼結体中の WCXOY (0. 005<y/x + y<0. 05) 及び Z r〇2 粒子のいずれかの凝集粒子が、 同体積の球と換算した場合の径で 3以上 10 m以下であり、 かつ、 その凝集粒子が、 1mm 3あたりに 3個以下である請求 項 1に記載の WC基複合セラミックス焼結体。
3. ヤング率が 300 GP a以上である請求項 1に記載の WC基複合セラミツ クス焼結体。
4. 熱伝導率が 2 OW/m · K以上である請求項 1に記載の WC基複合セラミ ックス焼結体。
5. WCを 40体積％以上 90体積％以下と、 残部が Υ2〇3, CeO， MgO の 1種又は 2種以上を安定化剤として含む部分安定化 Ζ Γ θ2からなる調合粉 末を、 酸素が存在する雰囲気下で、 200で以上 600で以下の温度域で 0. 1時間から 3時間保持して、 WCxOY(0. 005<y/x + y<0. 05) の化学式で表される酸素を固溶した WCとする WC基複合セラミックス焼結体 の製造方法。
PCT/JP2000/007477 1999-10-27 2000-10-26 Briquette frittee en ceramique composite a structure de base en wc WO2001030722A1 (fr)