Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/30—Low-molecular-weight compounds
  • C08G18/32—Polyhydroxy compounds; Polyamines; Hydroxyamines
  • C08G18/3203—Polyhydroxy compounds
  • C08G18/3215—Polyhydroxy compounds containing aromatic groups or benzoquinone groups
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C271/00—Derivatives of carbamic acids, i.e. compounds containing any of the groups, the nitrogen atom not being part of nitro or nitroso groups
  • C07C271/06—Esters of carbamic acids
  • C07C271/08—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms
  • C07C271/10—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms with the nitrogen atoms of the carbamate groups bound to hydrogen atoms or to acyclic carbon atoms
  • C07C271/20—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms with the nitrogen atoms of the carbamate groups bound to hydrogen atoms or to acyclic carbon atoms to carbon atoms of hydrocarbon radicals substituted by nitrogen atoms not being part of nitro or nitroso groups
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C271/00—Derivatives of carbamic acids, i.e. compounds containing any of the groups, the nitrogen atom not being part of nitro or nitroso groups
  • C07C271/06—Esters of carbamic acids
  • C07C271/08—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms
  • C07C271/24—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms with the nitrogen atom of at least one of the carbamate groups bound to a carbon atom of a ring other than a six-membered aromatic ring
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C271/00—Derivatives of carbamic acids, i.e. compounds containing any of the groups, the nitrogen atom not being part of nitro or nitroso groups
  • C07C271/06—Esters of carbamic acids
  • C07C271/08—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms
  • C07C271/26—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms with the nitrogen atom of at least one of the carbamate groups bound to a carbon atom of a six-membered aromatic ring
  • C07C271/28—Esters of carbamic acids having oxygen atoms of carbamate groups bound to acyclic carbon atoms with the nitrogen atom of at least one of the carbamate groups bound to a carbon atom of a six-membered aromatic ring to a carbon atom of a non-condensed six-membered aromatic ring
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F2/00—Processes of polymerisation
  • C08F2/46—Polymerisation initiated by wave energy or particle radiation
  • C08F2/48—Polymerisation initiated by wave energy or particle radiation by ultraviolet or visible light
  • C08F2/50—Polymerisation initiated by wave energy or particle radiation by ultraviolet or visible light with sensitising agents
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F283/00—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G
  • C08F283/12—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G on to polysiloxanes
  • C08F283/124—Macromolecular compounds obtained by polymerising monomers on to polymers provided for in subclass C08G on to polysiloxanes on to polysiloxanes having carbon-to-carbon double bonds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F290/00—Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups
  • C08F290/02—Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups on to polymers modified by introduction of unsaturated end groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F290/00—Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups
  • C08F290/02—Macromolecular compounds obtained by polymerising monomers on to polymers modified by introduction of aliphatic unsaturated end or side groups on to polymers modified by introduction of unsaturated end groups
  • C08F290/04—Polymers provided for in subclasses C08C or C08F
  • C08F290/042—Polymers of hydrocarbons as defined in group C08F10/00
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/2805—Compounds having only one group containing active hydrogen
  • C08G18/285—Nitrogen containing compounds
  • C08G18/2875—Monohydroxy compounds containing tertiary amino groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/48—Polyethers
  • C08G18/50—Polyethers having heteroatoms other than oxygen
  • C08G18/5003—Polyethers having heteroatoms other than oxygen having halogens
  • C08G18/5015—Polyethers having heteroatoms other than oxygen having halogens having fluorine atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/48—Polyethers
  • C08G18/50—Polyethers having heteroatoms other than oxygen
  • C08G18/5021—Polyethers having heteroatoms other than oxygen having nitrogen
  • C08G18/5024—Polyethers having heteroatoms other than oxygen having nitrogen containing primary and/or secondary amino groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/61—Polysiloxanes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/64—Macromolecular compounds not provided for by groups C08G18/42 - C08G18/63
  • C08G18/6415—Macromolecular compounds not provided for by groups C08G18/42 - C08G18/63 having nitrogen
  • C08G18/6446—Proteins and derivatives thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/67—Unsaturated compounds having active hydrogen
  • C08G18/675—Low-molecular-weight compounds
  • C08G18/677—Low-molecular-weight compounds containing heteroatoms other than oxygen and the nitrogen of primary or secondary amino groups
  • C08G18/678—Low-molecular-weight compounds containing heteroatoms other than oxygen and the nitrogen of primary or secondary amino groups containing nitrogen
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/728—Polymerisation products of compounds having carbon-to-carbon unsaturated bonds and having isocyanate or isothiocyanate groups or groups forming isocyanate or isothiocyanate groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/80—Masked polyisocyanates
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/80—Masked polyisocyanates
  • C08G18/8061—Masked polyisocyanates masked with compounds having only one group containing active hydrogen
  • C08G18/807—Masked polyisocyanates masked with compounds having only one group containing active hydrogen with nitrogen containing compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/81—Unsaturated isocyanates or isothiocyanates
  • C08G18/8141—Unsaturated isocyanates or isothiocyanates masked
  • C08G18/815—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen
  • C08G18/8158—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen with unsaturated compounds having only one group containing active hydrogen
  • C08G18/8166—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen with unsaturated compounds having only one group containing active hydrogen with unsaturated monofunctional alcohols or amines
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/81—Unsaturated isocyanates or isothiocyanates
  • C08G18/8141—Unsaturated isocyanates or isothiocyanates masked
  • C08G18/815—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen
  • C08G18/8158—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen with unsaturated compounds having only one group containing active hydrogen
  • C08G18/8175—Polyisocyanates or polyisothiocyanates masked with unsaturated compounds having active hydrogen with unsaturated compounds having only one group containing active hydrogen with esters of acrylic or alkylacrylic acid having only one group containing active hydrogen
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
  • C08G77/42—Block-or graft-polymers containing polysiloxane sequences
  • C08G77/442—Block-or graft-polymers containing polysiloxane sequences containing vinyl polymer sequences
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
  • G02B1/04—Optical elements characterised by the material of which they are made; Optical coatings for optical elements made of organic materials, e.g. plastics
  • G02B1/041—Lenses
  • G02B1/043—Contact lenses
• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
  • G03F7/004—Photosensitive materials
  • G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
  • G03F7/004—Photosensitive materials
  • G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
  • G03F7/028—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds with photosensitivity-increasing substances, e.g. photoinitiators
  • G03F7/031—Organic compounds not covered by group G03F7/029
• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
  • G03F7/004—Photosensitive materials
  • G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
  • G03F7/032—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds with binders
  • G03F7/033—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds with binders the binders being polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds, e.g. vinyl polymers
• • G—PHYSICS
  • G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
  • G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
  • G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
  • G03F7/004—Photosensitive materials
  • G03F7/075—Silicon-containing compounds
  • G03F7/0757—Macromolecular compounds containing Si-O, Si-C or Si-N bonds
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
  • C07C2601/00—Systems containing only non-condensed rings
  • C07C2601/12—Systems containing only non-condensed rings with a six-membered ring
  • C07C2601/14—The ring being saturated
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10S522/00—Synthetic resins or natural rubbers -- part of the class 520 series
  • Y10S522/904—Monomer or polymer contains initiating group

Definitions

• the present invention describes a crosslinked polymer which is composed of a polymerization product of a highly unsaturated polymer (a) and a polysiloxane (b) with terminal or pendent hydrosilane groups, with numerous unsaturated carbon-carbon bonds still being retained, to which at least one vinylic monomer may be grafted is;
• Processes for producing cross-linked polymers Shaped bodies, in particular contact lenses, biomedical articles or artificial corneas consisting entirely or essentially of such crosslinked polymers; furthermore the use of cross-linked polymers for the coating of surfaces of molded bodies.
• Polysiloxane (meth) acrylate copolymers which are crosslinked, for example, by photopolymerization, often show phase separation.
• ester groups due to their relatively high content of ester groups, such materials are often not sufficiently stable to be autoclaved in buffered physiological saline.
• such materials for example in implants do not show sufficient long-term stability under physiological conditions and can in particular be easily broken down enzymatically.
• the problem was solved by crosslinking an unsaturated polymer (a) with a polysiloxane (b) and, in a second optional step, graft-copolymerizing with a vinyl monomer as required.
• One object of the present invention therefore relates to a crosslinking product obtainable by reacting an unsaturated polymer (a) with a polysiloxane (b) containing hydrosilane groups.
• the invention further relates to a graft copolymer obtainable by reacting a crosslinking product with a hydrophilic or hydrophobic vinyl monomer, the crosslinking product being obtainable by reacting an unsaturated polymer (a) with a polysiloxane (b) containing hydrosilane groups.
• an unsaturated polymer (a) preferably stands for a compound comprising repeating units which are selected from units of the formulas (I) and (II),
• R 1 is hydrogen, alkyl or trialkylsilyl
• R 2 represents alkyl which is unsubstituted or by alkoxy, alkoxycarbonyl, hydroxyl,
• Hydroxycarbonyl, halogen or aryl is substituted; for alkenyl which is unsubstituted or substituted by alkoxy, alkoxycarbonyl, hydroxycarbonyl, halogen or aryl; or for
• Alkynyl which is unsubstituted or substituted by alkoxy, alkoxycarbonyl, hydroxycarbonyl, halogen or aryl;
• R 3 and R 4 are independently hydrogen or alkyl
• R 2 and R 3 together represent - (CH 2 ) q -, where q is an integer from 3 to 5, or R 2 and R 3 together represent a divalent radical of the formula (III),
• R 3 and R4 together represent - (CH 2 ) P -, where p is an integer from 3 to 5; n and m independently represent an integer from 10 to 100,000; and the sum of n and m also represents an integer from 10 to 100,000.
• An unsaturated polymer (a) which contains repeating units of the formula (I) and / or (II) is typically terminated by a radical R 1, R 2 , 3 or R 4 .
• radicals R 1t R 2 , R 3 and R 4 in the units of the formula (I) and / or (II) are preferably selected with the proviso that at least 20% of all segments each have at least one unsaturated carbon-carbon bond.
• R 1 is preferably hydrogen or lower alkyl having up to 8 carbon atoms, more preferably hydrogen or lower alkyl having up to 4 carbon atoms, more preferably hydrogen or lower alkyl having up to 2 carbon atoms and in particular hydrogen or methyl.
• Another preferred meaning of Ri is tri-lower alkylsilyl and especially trimethylsilyl, especially when Ri is linked to a unit of the formula (II).
• R 2 preferably represents lower alkenyl having up to 8 carbon atoms, which is unsubstituted or substituted by lower alkoxy, lower alkoxycarbonyl, hydroxycarbonyl, halogen or phenyl; more preferably lower alkenyl having up to 4 carbon atoms, which is unsubstituted or substituted by lower alkoxy, lower alkoxycarbonyl, hydroxycarbonyl, halogen or phenyl; and in particular for lower alkenyl having up to 4 carbon atoms, which is unsubstituted or substituted by halogen or phenyl.
• R 2 preferably represents lower alkyl having up to 8 carbon atoms, which is unsubstituted or substituted by lower alkoxy, hydroxy, halogen or phenyl; more preferably lower alkyl having up to 4 carbon atoms, which is unsubstituted or substituted by lower alkoxy, halogen or phenyl; and in particular for lower alkyl with up to 4 carbon atoms, which is unsubstituted or substituted by halogen or phenyl.
• R 3 preferably represents hydrogen or lower alkyl having up to 8 carbon atoms, more preferably hydrogen or lower alkyl having up to 4 carbon atoms, particularly preferably hydrogen or lower alkyl having up to 2 carbon atoms and in particular hydrogen or methyl.
• R has the same meaning and preference regardless of R 3 .
• R 2 and R 3 together have a preferred meaning for - (CH 2 ) q -, where q is an integer from 3 to 4, R 2 and R 3 are particularly preferably trimethylene.
• R 2 and R 3 likewise preferably together represent a divalent radical of the formula (III),
• r is an integer from 1 to 3 and s is 2.
• R 3 and R together represent - (CH 2 ) P - where p is an integer from 3 to 4.
• R 3 and R are in particular trimethylene.
• n and m is, independently of one another, an integer from 10 to 100,000, more preferably 20 to 1,000 and in particular 25 to 1,000.
• the sum of the indices m and n likewise preferably represents an integer from 10 to 100,000, more preferably for 20 to 10,000 and especially for 25 to 1,000.
• a preferred unsaturated polymer (a) is a compound comprising repeating units which are selected from units of the formula (I) and (II), in which R 1 ( R 3 and R are hydrogen and R 2 is lower alkenyl or by halogen substituted lower alkenyl.
• a preferred unsaturated polymer (a) is a compound containing repeating units which are selected from units of the formulas (I) and (II), in which R 1t R 3 and R 4 are hydrogen and R 2 is lower alkenyl with bis stands for 4 carbon atoms.
• a preferred unsaturated polymer (a) is a compound containing repeating units of the formula (I), in which R 1f R 3 and R 4 are hydrogen and R 2 is lower alkenyl having up to 4 carbon atoms.
• a preferred unsaturated polymer (a) is a compound containing repeating units of the formula (II) in which R 1 is tri-lower alkylsilyl and R 2 is lower alkyl.
• a preferred unsaturated polymer (a) is a compound comprising alternatingly repeating units of the formulas (I) and (II), in which R 1 p R 3 and R 4 are hydrogen and R 2 is lower alkyl or lower alkenyl with up to 4 C - Atoms stands.
• An unsaturated polymer (a) is, for example, a polymer of a conjugated aliphatic or alicyclic conjugated diene which is substituted, for example, by halogen or lower alkyl; a polymer of an alkyne or dialkin that is unsubstituted or substituted by lower alkyl or trimethylsilyl; a copolymer of a conjugated diene with a hydrophilic or hydrophobic vinyl monomer; also partially hydrogenated derivatives of the compounds mentioned.
• Examples of preferred polymeric conjugated dienes are ice, trans, iso- or syndiotactic poly-1,2-butadiene, poly-1,4-butadiene or polyisoprene; Poly-pentenamer; Polychloroprene; Polypiperylene;
• Examples of copolymers are butadiene or isoprene copolymers with hydrophilic or hydrophobic vinyl monomers such as e.g. Acrylonitrile, styrene, acrylic acid or hydroxyethyl methacrylate; an example of a polyalkyne is poly-1-trimethylsilyl-propyne.
• a highly preferred unsaturated polymer (a) is selected from syndiotactic poly-1,2-butadiene, poly-1, 4-butadiene and polyisoprene.
• a highly preferred unsaturated polymer (a) is poly-1-trimethylsilyl propyne.
• a polysiloxane (b) containing hydrosilane groups is preferably understood to mean a polysiloxane of the formula (IV)
• index x stands for 1 to 1000, in particular for 1 to 500, especially for 1 to 200 or for 1 to 100 and particularly preferably for 2 to 85.
• radicals R 5 , R 6 and R 7 independently of one another represent hydrogen, alkyl, alkoxy, phenyl or fluorine-containing lower alkyl, with the proviso that in a compound of the formula (IV) at least two of the radicals R 5 , R ⁇ and R 7 are hydrogen .
• radicals R 5 , R ⁇ and R 7 In connection with the radicals R 5 , R ⁇ and R 7 , the condition must be fulfilled that at least two of them, but preferably not more than about 20% of all radicals R 5 , R 6 and R 7 are hydrogen. It is particularly preferred that no more than about 15% of all radicals R 5 , R 6 and R are hydrogen. It is particularly preferred that exactly two of the radicals Rs, Re and R 7 are hydrogen. These are preferably the two R 7 radicals.
• the radicals R 5 and R ⁇ are preferably alkyl, fluorine-containing lower alkyl or phenyl, in particular lower alkyl, such as methyl or ethyl, or phenyl.
• the meaning lower alkyl having up to 8 carbon atoms, such as methyl is particularly preferred.
• the R 7 radicals denote hydrogen.
• Compounds of the formula (IV) in which the radicals R 5 , R ⁇ and R 7 have these meanings are ⁇ , ⁇ -dihydrogen polysiloxanes.
• radicals Rs, R ⁇ and R 7 denote hydrogen, fluorine-containing lower alkyl, alkyl or phenyl, in particular hydrogen, lower alkyl, such as methyl or ethyl, or phenyl, with the proviso that at least two of the radicals R s , R ⁇ and R 7 and preferably a maximum of 20% of the radicals R 5 , R ⁇ and R 7 are hydrogen.
• An unsaturated polymer (a) and an abovementioned polysiloxane (b) containing hydrosilane groups is reacted in the presence or absence of a solvent and advantageously in the presence of a catalyst, which is referred to below as crosslinking.
• a solvent is advantageously used which is largely inert, i.e. does not participate in the reaction.
• Suitable examples are ethers such as tetrahydrofuran (THF), dimethoxyethane, diethylene glycol dimethyl ether or dioxane, halogenated hydrocarbons such as chloroform or chlorobenzene, hydrocarbons such as toluene, hexane, methylcyclohexane or mixtures of several of these solvents.
• the amount of solvent used is preferably in a range such that solutions with a concentration of 1 to 60%, more preferably 20 to 60% and in particular 5 to 50% weight / volume result, the weight information being based on the amount of ⁇ set reactants.
• Suitable catalysts for the crosslinking reaction (or polyaddition reaction) between an unsaturated polymer (a) and a polysiloxane (b) containing hydrosilane groups are, in particular, platinum and rhodium complexes or salts of such metals such as H 2 PtCl ⁇ , PtCL or platinum-divinyltetramethyldisiloxane; also peroxides such as dibenzoyl peroxide or high-energy radiation such as UV light of a suitable wavelength.
• the amount of catalyst added is, in particular in the case of liquid, in a range from 0.0001 to 1% by volume and advantageously in a range from 0.001 to 0.1% by volume. The number ranges mentioned are% by weight for solid catalysts.
• the reactants, an unsaturated polymer (a) and a polysiloxane (b), are typically used in such a mass ratio that a crosslinking product therefrom has a polysiloxane content of preferably 30-80% by weight and in particular 40-70% by weight .
• the reaction temperature of the crosslinking can be, for example, from -30 to 150 ° C. The range of 10 to 100 ° C is a preferred temperature range. Another preferred temperature range is room temperature (RT).
• the reaction times are in the range from about 5 minutes to 48 hours, preferably in the range from 0.5 to 12 hours. If necessary, work is carried out under argon or nitrogen as a protective gas.
• the end point of the reaction is expediently determined by an infrared (IR) absorption measurement of the Si-H vibration. As soon as the Si-H band disappears in the IR spectrum, the crosslinking (polyaddition reaction) approaches the end.
• IR infrared
• a vinyl monomer grafted onto a crosslinking product obtainable by reacting an unsaturated polymer (a) with a polysiloxane (b) containing hydrosilane groups can be hydrophilic or hydrophobic. This reaction is called graft copolymerization.
• a graft copolymerization is typically heated with the addition of a radical generator (or radical initiator).
• a radical generator is e.g. Azadiisobutyronitrile (AIBN), potassium peroxodisulfate, dibenzoyl peroxide, hydrogen peroxide or sodium percarbonate. If, for example, the components mentioned are heated, radicals form under homolysis, which then typically initiate a graft copolymerization.
• the amount of radical generator added is typically in the range from about 0.001 to 5% by weight, based on the total amount of polymer, preferably in the range from about 0.01 to 2% by weight and in particular in the range from about 0.05 to 1% by weight.
• a graft copolymerization can also be initiated with high-energy radiation, such as UV light of a suitable wavelength, in particular with the addition of suitable photoinitiators such as Darocure ⁇ 2959. Darocure * 1171 or Irgacure ⁇ 184.
• suitable photoinitiators such as Darocure ⁇ 2959. Darocure * 1171 or Irgacure ⁇ 184.
• the amount of photoinitiator added is typically in the range of about 0.001 to 10% by weight with respect to the total amount of polymer, preferably in the range from approximately 0.01 to 5% by weight and in particular in the range from approximately 0.05 to 2% by weight.
• a graft copolymerization can be carried out in the presence or absence of a solvent.
• solvents which dissolve the monomers used are suitable as solvents, for example dipolar aprotic solvents such as dimethyl sulfoxide, acetonitrile, N-methylpyrrolidone (NMP) or dimethylacetamide, ketones such as methylethyl ketone or cyclohexanone, ethers such as THF, dimethoxyethane or dioxane, Hydrocarbons such as toluene or cyclohexane, as well as mixtures of suitable solvents, such as mixtures of THF and methyl ethyl ketone or NMP and cyclohexanone.
• dipolar aprotic solvents such as dimethyl sulfoxide, acetonitrile, N-methylpyrrolidone (NMP) or dimethylacetamide
• ketones such as methylethyl ketone or cyclohexanone
• ethers such as THF, dimethoxyethane or dioxane
• Solutions containing a vinylic monomer for grafting are usually adjusted to a range from 10 to 70% and preferably to a range from 20 to 60% weight / volume, the weight information relating to the amount of monomer used. If no solvent is present, for example, a vinylic monomer can function as a solvent per se, which is ideally also used for the graft copolymerization.
• a crosslinking product to which a vinyl monomer is to be grafted is removed from the solution, for example in a solution containing a vinyl monomer, for example swollen for 2 to 15 minutes, and then graft-copolymerized thermally or with high-energy radiation according to the methods below.
• the graft polymerization, in the thermal variant, is preferably carried out in a temperature range from 0 to 150 ° C. and more preferably in a range from 20 to 100 ° C.
• the reaction times are typically in the range from about 5 minutes to about 12 hours, preferably in the range from 0.5 to 4 hours. If necessary, the process is carried out under argon or nitrogen as a protective gas.
• the graft polymerization is carried out under the influence of high-energy radiation, it is typically irradiated with UV light of a suitable wavelength, usually at room temperature and typically for about 2 to 10 minutes (e.g. with a 2000 watt UV high-pressure lamp). If necessary, work is carried out under argon or nitrogen as a protective gas.
• the extent to which a vinyl monomer is grafted is typically dependent on the nature of a crosslinking product on the one hand and on the vinyl monomer on the other.
• Another factor is, for example, the steric hindrance both in the basic body and in the case of a vinyl monomer, which, for example, decides how much of a monomer can be grafted on.
• a vinyl monomer grafted onto a crosslinking product is a secondary polymer which either partially or completely penetrates the crosslinking product or forms a grafted layer.
• the layer thickness of a graft polymer which can typically be controlled by the duration of a graft copolymerization, is generally in the range from 1 to 200 ⁇ m, preferably in the range from 1 to 150 ⁇ m and in particular in the range from 1 to 100 ⁇ m.
• the quantitative ratio of primary polymer to secondary polymer can vary within wide limits; it is preferably in a range from 10:90 to 90:10% by weight.
• hydrophilic vinyl monomer preferably depends on the water content of the end product, the graft copolymer, which e.g. preferably up to 50% by weight and in particular from 15 to 35% by weight.
• a hydrophobic vinyl monomer is understood to mean a monomer which, as a homopolymer, typically gives a polymer which is water-insoluble and can absorb less than 10% by weight of water.
• hydrophilic vinyl monomer is understood to mean a monomer which, as a homopolymer, typically results in a polymer which is water-soluble or can absorb at least 10% by weight of water.
• Suitable hydrophobic vinylic monomers include, without the list being off to close, C.-C ⁇ alkyl and C 3 -C 18 -Cycloalkylacrylate and methacrylates, C 3 -C 1fl. Alkyl acrylamides and methacrylamides, acrylonitrile, methacrylonitrile, vinyl-C ⁇ C ⁇ -alkanoates, C 2 - C 1 ⁇ - alkenes, C 2 -C 1 ⁇ - haloalkenes, styrene, lower alkyl styrene, lower alkyl vinyl ether, C 2 -C 10 - perfluoroalkyl acrylates and methacrylates or correspondingly partially fluorinated acrylates and Methacrylates, C 3 -C 12 perfluoroalkyl-ethyl-thiocarbonylaminoethyl-acrylates and methacrylates, acryloxy and methacryloxy-alkylsiloxanes
• hydrophobic vinylic monomers examples include methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl acrylate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl, vinyl chloride, vinyl chlorophenyl chloride, vinyl chloride en vinyl chloride Acrylonitrile, 1-butene, butadiene, methacrylonitrile, vinyl toluene, vinyl ethyl ether, perfluorohexylethylthiocarbonylaminoethyl methacrylate, isobornyl methacrylate, trifluoroethyl methacrylate, hexafluoroisopropyl methacrylate, hexafluorobutyl methacrylate
• hydrophobic vinylic monomers are tris-trimethylsilyloxysilyl-propyl methacrylate, methyl methacrylate, trifluoroethyl methacrylate and hexafluoroisopropyl methacrylate.
• Suitable hydrophilic vinyl monomers include hydroxy-substituted lower alkyl acrylates and methacrylates, acrylamide, methacrylamide, lower alkyl acrylates and methacrylamides, ethoxylated acrylates and methacrylates, hydroxy-substituted lower alkyl acrylates and methacrylamides, hydroxy-substituted vinyl sulfonyl vinyl ether , Sodium styrene sulfonate, 2-acrylamido-2-methylpropanesulfonic acid, N-vinylpyrrole, N-vinyl-2-pyrrolidone, 2- and 4-vinylpyridine, vinyl-unsaturated carboxylic acids with a total of 3 to 5 carbon atoms, amino-lower alkyl- (the term "amino" also quaternary ammonium), mono-lower alkylamino-lower alkyl and di-lower alkylamino-low
• N-vinyl-2-pyrrolidone acrylamide, methacrylamide, lower alkyl (meth) acrylates substituted by hydroxy, lower alkyl acrylamides and methacrylamides substituted by hydroxyl and vinylically unsaturated carboxylic acids with a total of 3 to 5 carbon atoms.
• hydrophilic vinyl monomers examples include hydroxyethyl methacrylate, hydroxyethyl acrylate, hydroxypropyl acrylate, ammonium ethyl methacrylate hydrochloride, acrylamide, methacrylamide, NN-dimethylacrylamide, N- (meth) acryloylmo ⁇ holin, allyl alcohol, vinylpyridine, glycerol methacrylate, N- (1,1-dimethyl) acrylamide, N-vinyl-2-pyrrolidone, (meth) acrylic acid, methacrylic acid and the like.
• Preferred hydrophilic vinyl monomers are N.N-dimethylacrylamide, N-vinyl-2-pyrrolidone, glycerol methacrylate, (meth) acrylic acid and N- (meth) acryloylmo ⁇ holin.
• Alkyl has up to 20 carbon atoms and can be straight-chain or branched.
• Alkyl is preferably lower alkyl which has up to 8 carbon atoms and more preferably up to 4 and in particular up to 2 carbon atoms. Suitable examples include dodecyl, octyl, hexyl, pentyl, butyl, propyl, ethyl, methyl, 2-propyl. 2-butyl or 3-pentyl.
• Aryl stands for a carbocyclic aromatic compound with up to 20 C atoms, which is unsubstituted or substituted by preferably lower alkyl or lower alkoxy. Examples are phenyl, toluyl, xylyl, methoxyphenyl, t-butoxyphenyl, naphthyl or phenantryl.
• lower means, in connection with radicals and compounds, unless defined otherwise, in particular radicals or compounds with up to 8 carbon atoms, preferably with up to 6 and in particular with up to 4 carbon atoms.
• Fluorine-containing lower alkyl stands for a linear or branched lower alkyl with up to 8 carbon atoms, which is partially or completely substituted by fluorine. Examples of these are trifluoromethyl, difluoromethyl, hexafluoropropyl or 1,1,1-trifluoropropyl.
• Alkenyl has up to 2 to 20 carbon atoms and can be linear or branched. Alkenyl is in particular lower alkenyl with 2 to 8 C atoms, preferably 2 to 6 C atoms and in particular 2 to 4 C atoms.
• alkenyl examples are vinyl, allyl, 1-propen-2-yl, 1-buten-2- or -3- or -4-yl, 2-buten-3-yl, the isomers of pentenyl, hexenyl or octenyl.
• Alkynyl has up to 2 to 20 carbon atoms and can be linear or branched. Alkynyl is in particular lower alkynyl with 2 to 8 carbon atoms, preferably 2 to 6 carbon atoms and in particular 2 to 4 carbon atoms. Examples of alkynyl are ethynyl, propargyl, 1-butyn-1-, 3- or -4-yl, the isomers of pentynyl, hexynyl or octynyl.
• Halogen is especially fluorine, chlorine, bromine or iodine, preferably fluorine, chlorine and bromine and especially fluorine and chlorine.
• Alkoxy has up to 20 carbon atoms and is preferably lower alkoxy.
• Lower alkoxy has up to 8 carbon atoms, preferably up to 6 carbon atoms, and is e.g. Methoxy, ethoxy, propoxy, butoxy, tert-butoxy or hexyloxy.
• Trialkylsilyl stands for silyl which carries three alkyl ligands independently of one another.
• Trialkylsilyl preferably represents tri-lower alkylsilyl. Examples of tri-lower alkylsilyl are t-butyldimethylsilyl, thexyldimethylsilyl or trimethylsilyl.
• the invention further relates to processes for producing the crosslinked polymers according to the invention.
• An unsaturated polymer (a) for example polybutadiene, is mixed, for example, with a polysiloxane dihydride, for example in a ratio of 1: 1 or 2: 1, a suitable solvent usually being used; the resulting mixture is then preferably degassed, usually mixed with a suitable catalyst and preferably filled under protective gas, for example into a mold, for example a contact lens mold; the molds are closed and typically heated at 20-100 ° C. for 0.5-12 hours until all H-Si groups have been converted, which can be determined suitably by means of an IR spectroscopic measurement; finally the cross-linked shaped bodies are removed.
• These molded articles containing a (primary, as described above) crosslinking product can typically be graft-copolymerized in a second step, for example as follows:
• the shaped bodies are e.g. immersed in a solution containing vinylic monomer and optionally a graft copolymerization catalyst and swollen for 10 minutes, for example; the swollen moldings are generally removed from the solution, and finally typically heated under protective gas and, alternatively or additionally, with e.g. UV light of a suitable wavelength is irradiated.
• the two process steps can also be carried out in reverse order, namely e.g. as follows:
• a vinylic monomer can first be grafted onto an unsaturated polymer (a), typically under the graft copolymerization conditions mentioned above, and can then be crosslinked in a second step with a polysiloxane (b) containing hydrosilane groups, usually under the crosslinking conditions described above a hydrosilyiation reaction.
• the polymers according to the invention can be processed to shaped bodies in a manner known per se, in particular to contact lenses, for example by crosslinking the polymers in a suitable contact lens form.
• Another object of the invention is therefore directed to molded bodies and in particular to contact lenses which essentially or completely consist of a crosslinking product according to the invention and in particular a graft copolymer.
• shaped bodies according to the invention in addition to contact lenses, are biomedical articles or specifically ophthalmic shaped bodies, for example artificial cornea, intraocular lenses, eye bandages, shaped bodies which can be used in surgery, such as heart valves, artificial arteries or the like, as well as further coatings, films or Membranes, for example membranes for diffusion control, photostructural foils for information storage, or photoresist materials, for example membranes or molded bodies for etching resist or screen printing resist, furthermore particles, in particular microparticles, capsules, in particular microcapsules, films and plasters for drug delivery systems.
• Contact lenses, especially soft ones, which contain a crosslinked polymer according to the invention have a range of unusual and extremely advantageous properties.
• These properties include, for example, their excellent compatibility with the human comea (possibly after a suitable surface treatment (e.g. plasma hydrophilization)) and with the tear fluid, which are based on a balanced ratio of water content, oxygen permeability and mechanical and adsorbent properties.
• a suitable surface treatment e.g. plasma hydrophilization
• contact lenses according to the invention impair the natural metabolic processes in the comea only insignificantly or not at all.
• lenses which contain a crosslinked polymer according to the invention as an essential component show high dimensional stability and excellent storage stability.
• Another object of the present invention is directed to moldings, in particular contact lenses, which consist essentially or completely of a crosslinking product according to the invention or a graft copolymer according to the invention.
• Another object is directed to contact lenses which consist essentially or completely of a graft copolymer according to the invention, the water content being in particular in a range from 15 to 30% by weight.
• Contact lenses according to the invention with a preferred water content in a range of 15-30% by weight also show a high water permeability and furthermore an advantageous mobility on the eye.
• Another object of the present invention is directed to contact lenses which essentially consist of a crosslinked polymer according to the invention, which are weakly water-containing, flexible gas-permeable (RGP) contact lenses.
• RGP flexible gas-permeable
• Another object of the present invention is directed to the use of a crosslinked polymer according to the invention for the coating of a base material, such as glass, ceramic or metal, and preferably polymer substrates, such as, for example, ophthalmic products such as contact lenses, intraocular lenses or eye bandages, and of medically usable products, for example in surgical or pharmaceutical systems, with hydrophilic coatings (coatings) being preferred in the latter cases (ophthalmic uses).
• a base material such as glass, ceramic or metal
• polymer substrates such as, for example, ophthalmic products such as contact lenses, intraocular lenses or eye bandages, and of medically usable products, for example in surgical or pharmaceutical systems, with hydrophilic coatings (coatings) being preferred in the latter cases (ophthalmic uses).
• a crosslinked polymer according to the invention is also suitable for being used as a home skin implant or an artificial cornea (corneal impiant, artificial comea); furthermore as cell growth substrates, as material for the attachment and cultivation of animal cells in vitro and in vivo, as medical implants such as e.g. implantable semipermeable membrane materials, as tissue implants for cosmetic surgery, as an implant containing hormone-secreting cells, e.g. Pancreatic islet cells, as a breast implant or as an artificial joint and the like.
• a corneal implant which is produced from a crosslinked polymer described above.
• a named skin implant can be produced using the same method as described above for the production of contact lenses.
• Corneal implants can be implanted using conventional surgical procedures, e.g. under, in or through the epithelial tissue of the cornea or into the stroma of the cornea or into other tissue layers of the cornea. Such implants can change the optical properties of the cornea, e.g. in the sense of correcting a visual deficit and / or by changing the appearance of the eye, e.g. pupil staining.
• a corneal implant may include the area above the optical axis that, when implanted, covers the pupil and provides vision, as well as the area that surrounds the periphery of the optical axis. The implant can have the same visual properties over the entire area.
• tissue fluid for example proteins or glycoproteins, such as growth factors, peptides, hormones or proteins, which are responsible for the transport of essential Metal ions through a skin implant, especially between epithelial cells and stromal cells and even behind the endothelial layer, are important both for tissue survival and for the viability of tissue outside and inside a skin implant.
• a corneal implant is therefore preferably produced with a porosity that is sufficient to allow liquid components of tissue with a molecular weight of> 100,000 Daltons to pass through, a flow of components of tissue fluid being ensured in addition to a flow of low molecular weight nutrient components such as glucose, Fats or amino acids or breathing gases between cells on both sides of an implant.
• the porosity of a corneal implant is either given by the polymer material itself from which it is made.
• pores can additionally be incorporated into a crosslinked polymer according to the invention, namely by one of the numerous known processes which are described, for example, in WO 90/07575, WO91 / 07687, US5'244799, US5'238 * 613, US 4799'931 or US 5 * 213721.
• an implant preferably has a porosity sufficient for passing proteins and other biological macromolecules having a molecular weight up to or greater than 10 * 000 Dalton, such as a molecular weight of from 10 * 000 - 1'OOOOOO Dalton, but not so big that whole cells can pass through and penetrate into the area above the optical axis of the implant.
• the porosity of the implant is made possible by pores, the area above the optical axis contains a large number of pores, the number of which should not be restricted, but which should be sufficient to allow free flow of tissue components between the outer and the inner area of an implant .
• the pores that lie over the area of the optical axis preferably do not cause scattering of visible light to an extent that would be problematic in terms of vision correction.
• the term “pore” is understood above and below to mean a pore which has no geometric restrictions and has both a regular and an irregular shape. The specification of a pore size does not mean that all pores have the same diameter. Rather, it is an average diameter.
• the homophane implant can have the same porosity as in the area above the optical axis.
• This peripheral area of an implant which surrounds the area of the optical axis, is also referred to as a skirt, but, in contrast to the area of the optical axis, can allow corneal cells to grow in, as a result of which the implant is anchored to the eye.
• the porosity in the apron can also be an independent feature of the material from which the apron is made. If the apron is made of the same material as the material above the optical axis, pores with different diameters can be installed on the apron on the one hand and above the optical axis on the other. On the other hand, the apron can be made of a different material than the material above the optical axis, and as stated above, the porosity in the apron should be greater than that above the optical axis.
• An apron is preferably made of an optically clear polymer such as one over the optical axis; The apron can also consist of an optically non-clear material, or it is made of porous material that is not optically clear.
• a crosslinked polymer according to the invention can support the colonization with tissue cells such as, for example, vascular endothelial cells, fibroplasts or cells formed in bone, it not being necessary for a specific surface texture to be present in order to stimulate cell adhesion and cell growth. This is advantageous because the process costs can be kept low.
• tissue cells such as, for example, vascular endothelial cells, fibroplasts or cells formed in bone, it not being necessary for a specific surface texture to be present in order to stimulate cell adhesion and cell growth.
• tissue cells such as, for example, vascular endothelial cells, fibroplasts or cells formed in bone
• a specific surface texture such as, for example, vascular endothelial cells, fibroplasts or cells formed in bone
• a specific surface texture such as, for example, vascular endothelial cells, fibroplasts or cells formed in bone
• a specific surface texture such as, for example, vascular endothelial cells, fibroplasts or cells formed in bone
• a crosslinked polymer according to the invention can be coated with one or more components on its surface, for example to promote the growth of tissue.
• Such materials are, for example, fibronectin, chondroitan sulfate, collagen, laminin, cell attachment proteins, globulin, chondronectin, epidermal growth factors, muscle fiber proteins and / or derivatives thereof, active fragments and mixtures thereof. Fibronectin, epidermal growth factors and / or their derivatives, active fragments and mixtures thereof are especially useful. If necessary, such a surface coating can also be carried out after a surface modification described above.
• a crosslinked polymer according to the invention can advantageously combine several of the properties mentioned, such as, for example, attachment to cells with good biostability and resistance to deposits.
• the mechanical properties of a crosslinked polymer according to the invention are suitable for being used as a home skin implant, the material preferably having a modulus of elasticity of 0.5-10 MPa.
• a named modulus of elasticity gives a corneal implant suitable flexibility to enable insertion into the eye, such as over the area of Bowman's membrane.
• a cross-linked polymer according to the invention can also be used as a cell growth sublayer, e.g. as a cell culture device, e.g. Dishes, bottles, dishes and the like, furthermore in biological reactors, for example in the production of valuable proteins and other cell culture components.
• a cell growth sublayer e.g. as a cell culture device, e.g. Dishes, bottles, dishes and the like, furthermore in biological reactors, for example in the production of valuable proteins and other cell culture components.
• Example 2 Analogously to Example 1, 2.2 g of poly (1,2-syndiotactic) butadiene and 4.4 g of H-siloxane (test product K-3272, Goldschmidt AG) were converted into DME.
• the film in this example is pretty brittle.
• a polymer film is produced with the following components: 3.3 g of poly (1,2-syndiotactic) butadiene and 2.0 g of H-siloxane (test product K-3272, from Goldschmidt AG).
• a polymer film is produced with the following components: 3.0 g of poly (1,2-syndiotactic) butadiene and 2.0 g of H-siloxane (test product 1085 from Goldschmidt AG).
• Part of this solution is used to fill polypropylene contact lens molds (Molds) with a diameter of 21 mm and a center height of 0.5 mm and then closed with a loose-fitting polypropylene cover. These molds are heated under nitrogen (60 ° C.) for 12 hours.
• Lenses are produced analogously to Example 7, starting from 6 g of hydroxyl-terminated polybutadiene (Polysciences Inc., catalog No. 06508) and 4.0 g of H-siloxane (test product 1085 from Goldschmidt AG).
• a polymer film is produced and a 2 x 1 cm piece of it is immersed for 10 minutes in a solution containing 2.6 g of N-vinylpyrrolidone (NVP), 6.4 g of methyl ethyl ketone and 0.2 g of iracure'184 (photoinitiator Ciba-Geigy ) contains.
• NDP N-vinylpyrrolidone
• iracure'184 photoinitiator Ciba-Geigy
• Example 9 the polymer film from Example 4 was treated with a solution which contained 2.6 g of dimethylacrylamide (DMA), 4 g of methyl ethyl ketone and 0.2 g of Irgacure * 184 (photo initiator Ciba-Geigy). As in Example 9, it is immersed for ten minutes, rinsed and irradiated with UV.
• DMA dimethylacrylamide
• Irgacure * 184 photo initiator Ciba-Geigy

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Physics & Mathematics (AREA)
• General Physics & Mathematics (AREA)
• Spectroscopy & Molecular Physics (AREA)
• Optics & Photonics (AREA)
• Macromonomer-Based Addition Polymer (AREA)
• Graft Or Block Polymers (AREA)
• Materials For Medical Uses (AREA)
• Silicon Polymers (AREA)
• Eyeglasses (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Polymerisation Methods In General (AREA)
• Other Resins Obtained By Reactions Not Involving Carbon-To-Carbon Unsaturated Bonds (AREA)
• Curing Cements, Concrete, And Artificial Stone (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Surface Treatment Of Optical Elements (AREA)
• Polyurethanes Or Polyureas (AREA)
• Application Of Or Painting With Fluid Materials (AREA)
• Heterocyclic Carbon Compounds Containing A Hetero Ring Having Nitrogen And Oxygen As The Only Ring Hetero Atoms (AREA)
• Preparation Of Clay, And Manufacture Of Mixtures Containing Clay Or Cement (AREA)
• Solid-Sorbent Or Filter-Aiding Compositions (AREA)
• Compounds Of Unknown Constitution (AREA)
• Fats And Perfumes (AREA)
• Photoreceptors In Electrophotography (AREA)
• Liquid Crystal Substances (AREA)

Priority Applications (10)

Applications Claiming Priority (4)

Publications (1)

Family

ID=25694297

Family Applications (3)

Family Applications After (2)

Country Status (20)

Cited By (5)

Families Citing this family (47)

Citations (8)

Family Cites Families (6)

• 1995
  • 1995-12-27 AT AT95940936T patent/ATE173742T1/de not_active IP Right Cessation
  • 1995-12-27 FI FI972611A patent/FI972611A7/fi not_active Application Discontinuation
  • 1995-12-27 CA CA002208967A patent/CA2208967A1/en not_active Abandoned
  • 1995-12-27 DK DK95940937T patent/DK0793541T3/da active
  • 1995-12-27 DK DK95940936T patent/DK0800657T3/da active
  • 1995-12-27 CA CA002208977A patent/CA2208977A1/en not_active Abandoned
  • 1995-12-27 ES ES95940935T patent/ES2128110T3/es not_active Expired - Lifetime
  • 1995-12-27 DE DE59504366T patent/DE59504366D1/de not_active Expired - Fee Related
  • 1995-12-27 CA CA002208996A patent/CA2208996A1/en not_active Abandoned
  • 1995-12-27 DE DE59506915T patent/DE59506915D1/de not_active Expired - Lifetime
  • 1995-12-27 WO PCT/CH1995/000308 patent/WO1996020964A1/de not_active Ceased
  • 1995-12-27 FI FI972738A patent/FI972738L/fi unknown
  • 1995-12-27 DE DE59505153T patent/DE59505153D1/de not_active Expired - Fee Related
  • 1995-12-27 FI FI972737A patent/FI972737A7/fi unknown
  • 1995-12-27 JP JP8520659A patent/JPH10512308A/ja active Pending
  • 1995-12-27 US US08/860,132 patent/US6087412A/en not_active Expired - Lifetime
  • 1995-12-27 WO PCT/CH1995/000309 patent/WO1996021167A1/de not_active Ceased
  • 1995-12-27 ES ES95940937T patent/ES2138246T3/es not_active Expired - Lifetime
  • 1995-12-27 CZ CZ972061A patent/CZ206197A3/cs unknown
  • 1995-12-27 KR KR1019970704468A patent/KR987001001A/ko not_active Withdrawn
  • 1995-12-27 EP EP95940937A patent/EP0793541B1/de not_active Expired - Lifetime
  • 1995-12-27 ES ES95940936T patent/ES2125676T3/es not_active Expired - Lifetime
  • 1995-12-27 AT AT95940935T patent/ATE176915T1/de not_active IP Right Cessation
  • 1995-12-27 BR BR9510122A patent/BR9510122A/pt not_active Application Discontinuation
  • 1995-12-27 AU AU42516/96A patent/AU701751B2/en not_active Ceased
  • 1995-12-27 AU AU42514/96A patent/AU4251496A/en not_active Abandoned
  • 1995-12-27 HU HU9800218A patent/HUT77423A/hu unknown
  • 1995-12-27 CN CN95197442A patent/CN1173227A/zh active Pending
  • 1995-12-27 EP EP95940936A patent/EP0800657B1/de not_active Expired - Lifetime
  • 1995-12-27 EP EP95940935A patent/EP0800541B1/de not_active Expired - Lifetime
  • 1995-12-27 WO PCT/CH1995/000310 patent/WO1996020795A1/de not_active Ceased
  • 1995-12-27 CN CN95197183A patent/CN1171798A/zh active Pending
  • 1995-12-27 PL PL95321142A patent/PL321142A1/xx unknown
  • 1995-12-27 JP JP52066096A patent/JP3560980B2/ja not_active Expired - Fee Related
  • 1995-12-27 CN CN95197443A patent/CN1173148A/zh active Pending
  • 1995-12-27 AT AT95940937T patent/ATE184812T1/de not_active IP Right Cessation
  • 1995-12-27 BR BR9510434-8A patent/BR9510434A/pt not_active Application Discontinuation
  • 1995-12-27 NZ NZ297369A patent/NZ297369A/xx unknown
  • 1995-12-27 AU AU42515/96A patent/AU692979B2/en not_active Ceased
  • 1995-12-27 JP JP52066196A patent/JP4375811B2/ja not_active Expired - Lifetime
• 1997
  • 1997-06-27 NO NO973020A patent/NO973020L/no unknown
  • 1997-06-27 NO NO973018A patent/NO973018L/no unknown
  • 1997-06-27 NO NO973019A patent/NO973019L/no unknown
• 1999
  • 1999-02-12 GR GR990400461T patent/GR3029377T3/el unknown
  • 1999-12-22 GR GR990403297T patent/GR3032210T3/el unknown

Patent Citations (8)

Non-Patent Citations (5)

Also Published As

Similar Documents

Legal Events