USRE48079E1 - Process for preparing granules of pigments by means of double extrusion - Google Patents
Process for preparing granules of pigments by means of double extrusion Download PDFInfo
- Publication number
- USRE48079E1 USRE48079E1 US15/234,512 US200615234512A USRE48079E US RE48079 E1 USRE48079 E1 US RE48079E1 US 200615234512 A US200615234512 A US 200615234512A US RE48079 E USRE48079 E US RE48079E
- Authority
- US
- United States
- Prior art keywords
- process according
- extruder
- extrusion
- screws
- diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active, expires
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09B—ORGANIC DYES OR CLOSELY-RELATED COMPOUNDS FOR PRODUCING DYES, e.g. PIGMENTS; MORDANTS; LAKES
- C09B67/00—Influencing the physical, e.g. the dyeing or printing properties of dyestuffs without chemical reactions, e.g. by treating with solvents grinding or grinding assistants, coating of pigments or dyes; Process features in the making of dyestuff preparations; Dyestuff preparations of a special physical nature, e.g. tablets, films
- C09B67/0001—Post-treatment of organic pigments or dyes
- C09B67/0002—Grinding; Milling with solid grinding or milling assistants
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
- B29C48/05—Filamentary, e.g. strands
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/395—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders
- B29C48/40—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders using two or more parallel screws or at least two parallel non-intermeshing screws, e.g. twin screw extruders
- B29C48/405—Intermeshing co-rotating screws
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/50—Details of extruders
- B29C48/505—Screws
- B29C48/625—Screws characterised by the ratio of the threaded length of the screw to its outside diameter [L/D ratio]
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/50—Details of extruders
- B29C48/76—Venting, drying means; Degassing means
- B29C48/761—Venting, drying means; Degassing means the vented material being in liquid form
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/78—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling
- B29C48/80—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling at the plasticising zone, e.g. by heating cylinders
- B29C48/83—Heating or cooling the cylinders
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/78—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling
- B29C48/80—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling at the plasticising zone, e.g. by heating cylinders
- B29C48/83—Heating or cooling the cylinders
- B29C48/832—Heating
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/78—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling
- B29C48/80—Thermal treatment of the extrusion moulding material or of preformed parts or layers, e.g. by heating or cooling at the plasticising zone, e.g. by heating cylinders
- B29C48/83—Heating or cooling the cylinders
- B29C48/834—Cooling
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09B—ORGANIC DYES OR CLOSELY-RELATED COMPOUNDS FOR PRODUCING DYES, e.g. PIGMENTS; MORDANTS; LAKES
- C09B67/00—Influencing the physical, e.g. the dyeing or printing properties of dyestuffs without chemical reactions, e.g. by treating with solvents grinding or grinding assistants, coating of pigments or dyes; Process features in the making of dyestuff preparations; Dyestuff preparations of a special physical nature, e.g. tablets, films
- C09B67/0001—Post-treatment of organic pigments or dyes
- C09B67/0004—Coated particulate pigments or dyes
- C09B67/0008—Coated particulate pigments or dyes with organic coatings
- C09B67/0013—Coated particulate pigments or dyes with organic coatings with polymeric coatings
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09B—ORGANIC DYES OR CLOSELY-RELATED COMPOUNDS FOR PRODUCING DYES, e.g. PIGMENTS; MORDANTS; LAKES
- C09B67/00—Influencing the physical, e.g. the dyeing or printing properties of dyestuffs without chemical reactions, e.g. by treating with solvents grinding or grinding assistants, coating of pigments or dyes; Process features in the making of dyestuff preparations; Dyestuff preparations of a special physical nature, e.g. tablets, films
- C09B67/0071—Process features in the making of dyestuff preparations; Dehydrating agents; Dispersing agents; Dustfree compositions
- C09B67/0092—Dyes in solid form
- C09B67/0095—Process features in the making of granulates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/395—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders
- B29C48/40—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using screws surrounded by a cooperating barrel, e.g. single screw extruders using two or more parallel screws or at least two parallel non-intermeshing screws, e.g. twin screw extruders
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/50—Details of extruders
- B29C48/76—Venting, drying means; Degassing means
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2061/00—Use of condensation polymers of aldehydes or ketones or derivatives thereof, as moulding material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/0005—Condition, form or state of moulded material or of the material to be shaped containing compounding ingredients
- B29K2105/0032—Pigments, colouring agents or opacifiyng agents
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/06—Condition, form or state of moulded material or of the material to be shaped containing reinforcements, fillers or inserts
- B29K2105/16—Fillers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
- B29K2105/25—Solid
- B29K2105/251—Particles, powder or granules
Definitions
- the present invention relates to a double-extrusion production process for coating organic and inorganic pigments preferably with acrylic, aldehyde and/or ketone resins in order to provide a particle composition preferably in the form of granules.
- pigments are solids both of an organic and an inorganic nature which are defined as such when they are used within a fixing system, such as resins, absorbing a part of the light and reflecting their complementary part which forms the colour of the coated surface.
- the formation of the colour, resulting from the mixture of various pigments is not uniform among the various preparations, due not only to the change in environmental conditions, which vary in each case, but also the differences in properties of the surface of the pigment and the surface tension properties of the polymers during melting which, even though not different from batch to batch, may vary slightly.
- insertion of the pigments is performed by means of simple physical mixing of the said pigments with granules of varying form (chips or flakes) of the resins, which form the vehicle with the addition of chemical additives able to improve the contact between pigment and resin so as to integrate the pigment in the resin, during extrusion where melting of the resin contained in the mix and dispersion or milling of the pigment(s) in a liquid/viscous phase occurs.
- This process normally uses single-screw extruders (single-screw Bandera type) which have a pigment milling capacity which is not sufficiently powerful and therefore not exactly suitable for extruding organic pigments with a high calorimetric yield and for this reason are mainly used for inorganic or organic pigments, but in products where formation of the colour and the calorimetric yield are not to be regarded as decisive.
- single-screw extruders single-screw Bandera type
- Twin-screw extruders with composite screws are normally used and known; these, compared to single-screw extruders, provide a better performance in terms of pigment refining and milling capacity and are therefore used whenever pigments which are difficult to mill are used and where a high calorimetric yield is required.
- Both the single-screw and twin-screw extruders use heat supplied to the extrusion chamber in order to favour melting of the polymer and milling of the pigments in the liquid/viscous-phase.
- twin-screw extruders has also proved to have limitations in terms of dispersion capacity in the case where particularly sophisticated and costly organic pigments are used, such as those developed for use in paints with a good resistance to external agents, transparency for use in metallic paints, high colour tone and high saturation, and where it is required to maximize the degree of dispersion and consequently the calorimetric yield; or also inorganic pigments which are particularly difficult to disperse or in both cases simply in order to be able to increase the concentration of the pigment in the extruded preparations, while maintaining good results in terms of dispersion.
- organic pigments such as those developed for use in paints with a good resistance to external agents, transparency for use in metallic paints, high colour tone and high saturation, and where it is required to maximize the degree of dispersion and consequently the calorimetric yield
- inorganic pigments which are particularly difficult to disperse or in both cases simply in order to be able to increase the concentration of the pigment in the extruded preparations, while maintaining good results in terms of
- the fineness and the degree of homogeneity of milling which can be achieved with many organic pigments (such as, for example, magenta dimethylquinacridone Red 122 pigment, violet-red betaquinacridone Violet 19 pigment, orange diketo′pyrrolo-pyrrole Orange 73 pigment), are not acceptable for application sectors such as, for example, that of high-performance paints.
- organic pigments such as, for example, magenta dimethylquinacridone Red 122 pigment, violet-red betaquinacridone Violet 19 pigment, orange diketo′pyrrolo-pyrrole Orange 73 pigment
- the pigment particles remain, in fact, too large (i.e. 5-30 microns for magenta dimethylquinacridone Red 122 pigment, 10-30 microns for violet-red betaquinacridone Violet 19 pigment, and 10-25 microns for orange diketo-pyrrolo-pyrrole Orange 73 pigment) as well as not being dispersed in a sufficiently homogeneous manner, negatively affecting properties such as the colorimetric yield, the brilliance and the tone.
- the first extrusion is performed in a co-rotating twin-screw extruder which allows a first step to be performed without induced heating, using only the heat developed naturally by the cutting and friction forces inside the extruder.
- the twin-screw extruder preferred for the invention uses screws with a diameter of 27-110 mm, preferably 30-87 mm, and length 25-48 times the diameter, preferably 32-40 times.
- the temperature inside the abovementioned extruder may vary from about 0 to about 50° C., preferably from 5 to 35° C.; dividing ideally the inside of the extruder into 9 zones of identical length, the temperature is normally set in the first three zones to 5/15° C., preferably 10° C., in the second zones (3 to 6) to 15/25° C., preferably 20° C., and in the third zones (6 to 9) to 25/35° C., preferably 30° C.
- the temperature inside the extruder is controlled both by the cooling set in the first zones of the extruder and by evaporation of the water present as a component of the mix; this is performed preferably by means of a breather valve situated towards the end part in the extruder conveying zone. Control of the temperature is important for keeping the mix in a not entirely melted state so that the cutting forces may exert their action more effectively.
- the flowrate of the first extrusion is about 5-20 kg/h, preferably 10-15 kg/h.
- the semifinished product in a shapeless but homogeneous solid state of pigment and resin leaving the extruder after the first step, may contain water in large quantities, something which may make use thereof during subsequent extrusion difficult.
- the mixture surfactants or dispersants (which are preferably non-ionic, such as epoxidized sorbitan and soy bean oil esters, preferably epoxidized sorbitan ester), in order to favour wetting of the solid phase and provide a homogeneous mix with good extrudibility characteristics.
- the extrudate from the first extrusion is then transferred for secondary extrusion; this procedure may be performed both in batches and continuously.
- the second twin-screw extruder has screws with a diameter of 27-110 mm, preferably 30-87 mm, and length 30/60 times the diameter, preferably 48-60 times the diameter.
- the temperature inside the abovementioned extruder may vary from about 50 to about 130° C., preferably from 80 to 110° C.; dividing ideally the inside of the extruder into 9 zones of identical length, the temperature is normally set, by means of the supply of induced heat, in the first three extrusion zones to 70/90° C., preferably 80° C., in the second zones (3 to 6) to 80/100° C., preferably 90° C., and in the third zones (6 to 9) to 90/110° C., preferably 100° C.
- the flowrate of the first extrusion is 15-35 kg/h, preferably 20-30 kg/h.
- the extrusion process is completed using a die and pelletizer.
- the remaining water present in the mix is extracted also by means of application of a vacuum, if necessary, through the breather valve of the degassing system.
- the fineness of milling and homogenization of the dispersed particles is completed obtaining a very narrow distribution of the particle size curve with particle size values which are small and less than values of 1-2 microns when measured using an optical microscope with ⁇ 200 magnification.
- the melted state of the mass output from the second operation will also allow the production of microgranules by means of a die and water-cutting microgranulator mounted on the extruder head.
- a dual cold/hot pass not only reduces the size of the particles to less than 1-2 microns, but also results in perfect uniformity thereof (narrow distribution of the particle size curve) and consequently a higher calorimetric yield.
- an aqueous solution of the dispersant is prepared (the water is preferably used in quantities ranging between 10 and 20% relative to the total weight of the formulation); the resin is introduced into the mixer (preferably an open receptacle of the high-speed blade type) and it is wetted with a quantity equal to about 50% of said solution; the pigment is introduced while mixing and the remaining amount of aqueous solution is added; the inert filler is added and, after mixing, the product is discharged and transferred to the extruder.
- the mixer preferably an open receptacle of the high-speed blade type
- the granular formulation which can be obtained according to the process of the present invention may be used for the production of granular systems based on resin and pigment and known in the art, and in particular those described in the international patent applications PCT/IT2005/000443, PCT/IT2005/000536, PCT/EP2006/000019 and PCT/IT2006/000588, in the name of the same Applicants and incorporated herein by way of reference.
- a high-speed turbomixer with propeller impeller and number of revolutions ranging from 1000 to 3000 per minute, preferably 2000/2500 rpm, which allows homogenization of the components consisting of pigment(s), resin, additives and water.
- the “cold pass” does not supply heat and therefore avoids complete melting of the resin, but ensures, using only the “friction” heat produced by the high cutting forces which are generated, a perfect dispersion of the pigment, nevertheless obtaining a non-granular shapeless physical form.
- a heated co-rotating twin-screw extruder (Leistriz type) in which the mixture melting process takes place, with complete outflow of the aqueous phase.
- a microgranulator (Gala underwater pelletizing type) which is mounted on the extruder head is used for microgranulation of the extrudate in the aqueous phase.
- the granules are produced by means of a water jet cutting granulator of the type produced by Gala Industries Inc. and described in international patent application WO/21371, incorporated herein by way of reference.
- microgranules obtained from the extrusion process which depending on the specific weight of the extruded mixture may have a number variable from 80 to 200 granules per gramme are supplemented with any silica fluidizing additive where required to avoid problems of compaction of the microgranules during storage or transportation in temperature conditions which are not properly controlled and conveyed away for packaging.
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Pigments, Carbon Blacks, Or Wood Stains (AREA)
- Paints Or Removers (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US15/234,512 USRE48079E1 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US15/234,512 USRE48079E1 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
PCT/IT2006/000613 WO2008018097A1 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
US12/376,207 US8802752B2 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
Publications (1)
Publication Number | Publication Date |
---|---|
USRE48079E1 true USRE48079E1 (en) | 2020-07-07 |
Family
ID=38124859
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/376,207 Ceased US8802752B2 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
US15/234,512 Active 2028-10-24 USRE48079E1 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
Family Applications Before (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/376,207 Ceased US8802752B2 (en) | 2006-08-09 | 2006-08-09 | Process for preparing granules of pigments by means of double extrusion |
Country Status (20)
Country | Link |
---|---|
US (2) | US8802752B2 (ja) |
EP (1) | EP2049317B1 (ja) |
JP (1) | JP5248500B2 (ja) |
KR (1) | KR101352825B1 (ja) |
CN (1) | CN101505944B (ja) |
AR (1) | AR062302A1 (ja) |
AT (1) | ATE506166T1 (ja) |
AU (1) | AU2006347136B2 (ja) |
BR (1) | BRPI0621936A2 (ja) |
CA (1) | CA2659546C (ja) |
DE (1) | DE602006021492D1 (ja) |
DK (1) | DK2049317T3 (ja) |
ES (1) | ES2365413T3 (ja) |
IL (1) | IL196735A (ja) |
MX (1) | MX2009001391A (ja) |
PL (1) | PL2049317T3 (ja) |
PT (1) | PT2049317E (ja) |
SI (1) | SI2049317T1 (ja) |
TW (1) | TW200815536A (ja) |
WO (1) | WO2008018097A1 (ja) |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
MX2011006338A (es) | 2008-12-16 | 2011-07-13 | Dow Global Technologies Llc | Una composicion de recubrimiento que comprende pigmentos opacificantes de oxido metalico encapsulados en un polimero y proceso para producirla. |
EP2361956A1 (en) * | 2010-02-22 | 2011-08-31 | Inxel Trademark & Patents SAGL | Composition of pigments soluble in water and/or in organic solvents |
BRPI1105379B1 (pt) | 2011-12-26 | 2021-08-10 | Embraco Indústria De Compressores E Soluções Em Refrigeração Ltda | Sistema de válvula semi-comandada aplicado em compressor e método de modulação de capacidade de compressor dotado de sistema de válvula semi-comandada |
CN107722709A (zh) * | 2017-11-09 | 2018-02-23 | 中国科学院包头稀土研发中心 | 一种含有有机和无机颜料的复合颜料及其制备方法 |
DE102017131437A1 (de) | 2017-12-29 | 2019-07-04 | Heubach Gmbh | Verwendung einer Pigmentpräparation zur Herstellung von Lackfarben sowie die danach hergestellte Lackfarbe |
CN108192423A (zh) * | 2018-02-06 | 2018-06-22 | 加圣(上海)新材料有限公司 | 一种色浆及其制备方法 |
CN114437569A (zh) * | 2022-01-21 | 2022-05-06 | 中国科学院兰州化学物理研究所 | 一种黏土矿物杂化钴蓝颜料的制备方法 |
Citations (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4176143A (en) * | 1975-12-13 | 1979-11-27 | Hoechst Aktiengesellschaft | Highly reactive powder resin compositions containing polycarboxylic acid anhydrides |
JPS5715910A (en) | 1980-07-03 | 1982-01-27 | Toshiba Mach Co Ltd | Molding method for pellet and screw and die plate used for said method |
US4347003A (en) * | 1979-06-15 | 1982-08-31 | Hermann Berstorff Maschinenbau Gmbh | Two-stage extruder |
US5158725A (en) | 1991-04-29 | 1992-10-27 | The Goodyear Tire & Rubber Company | Continuous mixing of elastomeric compounds |
JPH09239726A (ja) | 1996-03-12 | 1997-09-16 | Mitsubishi Chem Corp | タンデム型混練装置及びそれを用いた熱可塑性樹脂及び/又はゴムの混練方法 |
US5711904A (en) * | 1995-09-05 | 1998-01-27 | The Goodyear Tire & Rubber Company | Continuous mixing of silica loaded elastomeric compounds |
JPH1190926A (ja) | 1997-09-18 | 1999-04-06 | Mitsui Chem Inc | ベール状ゴム組成物の製造方法 |
JP2000080172A (ja) | 1998-09-02 | 2000-03-21 | Sumika Color Kk | マスターバッチ樹脂ペレットおよびその製造方法 |
US6160037A (en) * | 1997-07-10 | 2000-12-12 | Ciba Specialty Chemicals Corporation | Reactive extrusion of latent pigments |
EP1277808A2 (en) | 2001-07-09 | 2003-01-22 | Ciba SC Holding AG | Easily distributable pigment compositions |
EP1277809A1 (en) * | 2001-07-16 | 2003-01-22 | Ver-Plast S.r.l. | A coating which reproduces the aesthetic effect of a fine weave fabric |
JP2003105224A (ja) | 2001-07-09 | 2003-04-09 | Ciba Specialty Chem Holding Inc | 易分散性顔料組成物及びその製造方法 |
US6551087B1 (en) * | 1999-09-21 | 2003-04-22 | Gala Industries, Inc. | Flow guide for underwater pelletizer |
JP2004018827A (ja) | 2002-06-20 | 2004-01-22 | Nippon Paint Co Ltd | 粉体塗料の製造方法 |
WO2004078852A1 (de) | 2003-03-05 | 2004-09-16 | Heubach Gmbh | Pigmentzubereitung und verfahren zu deren herstellung |
JP2004268505A (ja) | 2003-03-11 | 2004-09-30 | Japan Polypropylene Corp | 樹脂ペレットの製造方法 |
US20060020062A1 (en) * | 2004-07-08 | 2006-01-26 | Bloom Paul D | Epoxidized esters of vegetable oil fatty acids as reactive diluents |
WO2006082603A1 (en) | 2005-02-07 | 2006-08-10 | Inxel Trademark & Patents Sagl | Coating of organic and inorganic pigments with aldehyde or ketone resins |
US20090182081A1 (en) * | 2006-07-28 | 2009-07-16 | Inxel Trademark & Patents Sagl | Coating of inorganic pigments with aldehyde or ketone resins |
US20100298472A1 (en) * | 2006-01-16 | 2010-11-25 | Inxel Trademark & Patents Sagl | Coating of organic and inorganic pigments with acrylic resins |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5678927A (en) * | 1979-11-30 | 1981-06-29 | Matsushita Electric Works Ltd | Kneading and extrusion granulating apparatus of thermosetting resing molding material |
JPS62167012A (ja) * | 1986-01-21 | 1987-07-23 | Teijin Eng Kk | 造粒装置 |
JPH0550487A (ja) * | 1991-08-21 | 1993-03-02 | Furukawa Electric Co Ltd:The | 熱可塑性樹脂の多段押出し方法 |
JP2963380B2 (ja) * | 1995-11-15 | 1999-10-18 | 株式会社日本製鋼所 | 熱可塑性樹脂の造粒方法および造粒装置 |
CN1243051C (zh) * | 2002-09-30 | 2006-02-22 | 新泰市春晖色母料有限责任公司 | 聚乙烯轮胎包装膜着色母粒及其制备方法 |
-
2006
- 2006-08-09 AT AT06796263T patent/ATE506166T1/de active
- 2006-08-09 ES ES06796263T patent/ES2365413T3/es active Active
- 2006-08-09 PT PT06796263T patent/PT2049317E/pt unknown
- 2006-08-09 CA CA2659546A patent/CA2659546C/en active Active
- 2006-08-09 US US12/376,207 patent/US8802752B2/en not_active Ceased
- 2006-08-09 PL PL06796263T patent/PL2049317T3/pl unknown
- 2006-08-09 EP EP06796263A patent/EP2049317B1/en active Active
- 2006-08-09 KR KR1020097004396A patent/KR101352825B1/ko active IP Right Grant
- 2006-08-09 US US15/234,512 patent/USRE48079E1/en active Active
- 2006-08-09 AU AU2006347136A patent/AU2006347136B2/en active Active
- 2006-08-09 CN CN2006800555583A patent/CN101505944B/zh active Active
- 2006-08-09 BR BRPI0621936-5A patent/BRPI0621936A2/pt not_active IP Right Cessation
- 2006-08-09 SI SI200631055T patent/SI2049317T1/sl unknown
- 2006-08-09 MX MX2009001391A patent/MX2009001391A/es active IP Right Grant
- 2006-08-09 DE DE602006021492T patent/DE602006021492D1/de active Active
- 2006-08-09 DK DK06796263.9T patent/DK2049317T3/da active
- 2006-08-09 WO PCT/IT2006/000613 patent/WO2008018097A1/en active Application Filing
- 2006-08-09 JP JP2009523447A patent/JP5248500B2/ja active Active
-
2007
- 2007-08-07 TW TW096128993A patent/TW200815536A/zh unknown
- 2007-08-09 AR ARP070103523A patent/AR062302A1/es unknown
-
2009
- 2009-01-26 IL IL196735A patent/IL196735A/en active IP Right Grant
Patent Citations (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4176143A (en) * | 1975-12-13 | 1979-11-27 | Hoechst Aktiengesellschaft | Highly reactive powder resin compositions containing polycarboxylic acid anhydrides |
US4347003A (en) * | 1979-06-15 | 1982-08-31 | Hermann Berstorff Maschinenbau Gmbh | Two-stage extruder |
JPS5715910A (en) | 1980-07-03 | 1982-01-27 | Toshiba Mach Co Ltd | Molding method for pellet and screw and die plate used for said method |
US5158725A (en) | 1991-04-29 | 1992-10-27 | The Goodyear Tire & Rubber Company | Continuous mixing of elastomeric compounds |
US5711904A (en) * | 1995-09-05 | 1998-01-27 | The Goodyear Tire & Rubber Company | Continuous mixing of silica loaded elastomeric compounds |
JPH09239726A (ja) | 1996-03-12 | 1997-09-16 | Mitsubishi Chem Corp | タンデム型混練装置及びそれを用いた熱可塑性樹脂及び/又はゴムの混練方法 |
US6160037A (en) * | 1997-07-10 | 2000-12-12 | Ciba Specialty Chemicals Corporation | Reactive extrusion of latent pigments |
JPH1190926A (ja) | 1997-09-18 | 1999-04-06 | Mitsui Chem Inc | ベール状ゴム組成物の製造方法 |
JP2000080172A (ja) | 1998-09-02 | 2000-03-21 | Sumika Color Kk | マスターバッチ樹脂ペレットおよびその製造方法 |
US6551087B1 (en) * | 1999-09-21 | 2003-04-22 | Gala Industries, Inc. | Flow guide for underwater pelletizer |
EP1277808A2 (en) | 2001-07-09 | 2003-01-22 | Ciba SC Holding AG | Easily distributable pigment compositions |
US6734231B2 (en) | 2001-07-09 | 2004-05-11 | Ciba Specialty Chemicals Corporation | Easily distributable pigment compositions |
JP2003105224A (ja) | 2001-07-09 | 2003-04-09 | Ciba Specialty Chem Holding Inc | 易分散性顔料組成物及びその製造方法 |
EP1277809A1 (en) * | 2001-07-16 | 2003-01-22 | Ver-Plast S.r.l. | A coating which reproduces the aesthetic effect of a fine weave fabric |
JP2004018827A (ja) | 2002-06-20 | 2004-01-22 | Nippon Paint Co Ltd | 粉体塗料の製造方法 |
WO2004078852A1 (de) | 2003-03-05 | 2004-09-16 | Heubach Gmbh | Pigmentzubereitung und verfahren zu deren herstellung |
JP2004268505A (ja) | 2003-03-11 | 2004-09-30 | Japan Polypropylene Corp | 樹脂ペレットの製造方法 |
US20060020062A1 (en) * | 2004-07-08 | 2006-01-26 | Bloom Paul D | Epoxidized esters of vegetable oil fatty acids as reactive diluents |
WO2006082603A1 (en) | 2005-02-07 | 2006-08-10 | Inxel Trademark & Patents Sagl | Coating of organic and inorganic pigments with aldehyde or ketone resins |
US20080206568A1 (en) * | 2005-02-07 | 2008-08-28 | Angelo Achille Bardelli | Coating of Organic and Inorganic Pigments with Aldehyde or Ketone Resins |
US20100298472A1 (en) * | 2006-01-16 | 2010-11-25 | Inxel Trademark & Patents Sagl | Coating of organic and inorganic pigments with acrylic resins |
US20090182081A1 (en) * | 2006-07-28 | 2009-07-16 | Inxel Trademark & Patents Sagl | Coating of inorganic pigments with aldehyde or ketone resins |
Non-Patent Citations (4)
Also Published As
Publication number | Publication date |
---|---|
EP2049317A1 (en) | 2009-04-22 |
TW200815536A (en) | 2008-04-01 |
DK2049317T3 (da) | 2011-08-01 |
EP2049317B1 (en) | 2011-04-20 |
US20100004387A1 (en) | 2010-01-07 |
AU2006347136B2 (en) | 2012-05-24 |
AR062302A1 (es) | 2008-10-29 |
ES2365413T3 (es) | 2011-10-04 |
JP5248500B2 (ja) | 2013-07-31 |
KR101352825B1 (ko) | 2014-02-17 |
DE602006021492D1 (de) | 2011-06-01 |
WO2008018097A1 (en) | 2008-02-14 |
ATE506166T1 (de) | 2011-05-15 |
CA2659546A1 (en) | 2008-02-14 |
IL196735A (en) | 2013-10-31 |
JP2010500442A (ja) | 2010-01-07 |
US8802752B2 (en) | 2014-08-12 |
CA2659546C (en) | 2013-07-02 |
BRPI0621936A2 (pt) | 2011-12-20 |
SI2049317T1 (sl) | 2011-08-31 |
CN101505944B (zh) | 2013-04-17 |
PT2049317E (pt) | 2011-07-26 |
PL2049317T3 (pl) | 2011-09-30 |
CN101505944A (zh) | 2009-08-12 |
KR20090035731A (ko) | 2009-04-10 |
MX2009001391A (es) | 2009-04-30 |
IL196735A0 (en) | 2009-11-18 |
AU2006347136A1 (en) | 2008-02-14 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
USRE48079E1 (en) | Process for preparing granules of pigments by means of double extrusion | |
AU2006335650B2 (en) | Coating of organic and inorganic pigments with acrylic resins | |
KR101178502B1 (ko) | 알데히드 또는 케톤 수지를 이용한 유기 및 무기 안료의코팅 | |
Gale | Compounding with single‐screw extruders | |
KR101290221B1 (ko) | 알데히드 또는 케톤 수지로 무기 안료를 코팅 | |
US7241822B2 (en) | Dye composition for dyeing powder coatings | |
KR100556017B1 (ko) | 미립자형상 착색수지의 제조방법, 미립자형상 착색수지 및물품의 착색방법 | |
US6734231B2 (en) | Easily distributable pigment compositions | |
KR100502594B1 (ko) | 안료 | |
KR20060061341A (ko) | 유기용매 중 고형 안료 조제물 및 이의 분산액, 이의제조방법 및 이의 용도 | |
US5462709A (en) | Process for coloring thermoplastics | |
EP1277808B1 (en) | Easily distributable pigment compositions | |
Elemans et al. | The effect of feeding mode on dispersive mixing efficiency in single‐screw extrusion | |
CN111704760A (zh) | 一种单色有机母粒及其制备方法与应用、一种色母 | |
BRPI0621936B1 (pt) | Process for the production of a composition in particles of pigeons by means of double extinguishment | |
AlSadi | Color Mismatch in Compounding of Polycarbonate Composition: Processing Parameters and Pigment Dispersion Effects | |
Cameron | Dry color concentrate manufacture |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: INXEL TRADEMARKS & PATENTS SAGL, SWITZERLAND Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BROGGI, GIOVANNI;REEL/FRAME:052299/0065 Effective date: 20090209 |
|
AS | Assignment |
Owner name: PPG INDUSTRIES OHIO, INC., OHIO Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:INXEL TRADEMARKS & PATENTS SAGL;REEL/FRAME:052316/0715 Effective date: 20150515 |
|
MAFP | Maintenance fee payment |
Free format text: PAYMENT OF MAINTENANCE FEE, 8TH YEAR, LARGE ENTITY (ORIGINAL EVENT CODE: M1552); ENTITY STATUS OF PATENT OWNER: LARGE ENTITY Year of fee payment: 8 |