US20240170206A1 - Method for producing r-t-b based sintered magnet - Google Patents

Method for producing r-t-b based sintered magnet Download PDF

Info

Publication number
US20240170206A1
US20240170206A1 US18/284,308 US202218284308A US2024170206A1 US 20240170206 A1 US20240170206 A1 US 20240170206A1 US 202218284308 A US202218284308 A US 202218284308A US 2024170206 A1 US2024170206 A1 US 2024170206A1
Authority
US
United States
Prior art keywords
sintering
temperature
sintered
mass
stage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US18/284,308
Other languages
English (en)
Inventor
Kouta SAITOU
Futoshi Kuniyoshi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Proterial Ltd
Original Assignee
Proterial Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Proterial Ltd filed Critical Proterial Ltd
Assigned to PROTERIAL, LTD. reassignment PROTERIAL, LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KUNIYOSHI, FUTOSHI, SAITOU, Kouta
Publication of US20240170206A1 publication Critical patent/US20240170206A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F41/00—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties
    • H01F41/02—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets
    • H01F41/0253—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets for manufacturing permanent magnets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/10—Sintering only
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/12—Both compacting and sintering
    • B22F3/16—Both compacting and sintering in successive or repeated steps
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F9/00—Making metallic powder or suspensions thereof
    • B22F9/02—Making metallic powder or suspensions thereof using physical processes
    • B22F9/023—Hydrogen absorption
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F9/00—Making metallic powder or suspensions thereof
    • B22F9/02—Making metallic powder or suspensions thereof using physical processes
    • B22F9/04—Making metallic powder or suspensions thereof using physical processes starting from solid material, e.g. by crushing, grinding or milling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C33/00—Making ferrous alloys
    • C22C33/02—Making ferrous alloys by powder metallurgy
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/10—Ferrous alloys, e.g. steel alloys containing cobalt
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
    • H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
    • H01F1/047—Alloys characterised by their composition
    • H01F1/053—Alloys characterised by their composition containing rare earth metals
    • H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
    • H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F41/00—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties
    • H01F41/02—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F41/00—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties
    • H01F41/02—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets
    • H01F41/0253—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets for manufacturing permanent magnets
    • H01F41/0293—Apparatus or processes specially adapted for manufacturing or assembling magnets, inductances or transformers; Apparatus or processes specially adapted for manufacturing materials characterised by their magnetic properties for manufacturing cores, coils, or magnets for manufacturing permanent magnets diffusion of rare earth elements, e.g. Tb, Dy or Ho, into permanent magnets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F9/00—Making metallic powder or suspensions thereof
    • B22F9/02—Making metallic powder or suspensions thereof using physical processes
    • B22F9/04—Making metallic powder or suspensions thereof using physical processes starting from solid material, e.g. by crushing, grinding or milling
    • B22F2009/044—Making metallic powder or suspensions thereof using physical processes starting from solid material, e.g. by crushing, grinding or milling by jet milling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2202/00—Treatment under specific physical conditions
    • B22F2202/05—Use of magnetic field
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2301/00—Metallic composition of the powder or its coating
    • B22F2301/35—Iron
    • B22F2301/355—Rare Earth - Fe intermetallic alloys
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2304/00—Physical aspects of the powder
    • B22F2304/10—Micron size particles, i.e. above 1 micrometer up to 500 micrometer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2998/00—Supplementary information concerning processes or compositions relating to powder metallurgy
    • B22F2998/10—Processes characterised by the sequence of their steps
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B22—CASTING; POWDER METALLURGY
    • B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F2999/00—Aspects linked to processes or compositions used in powder metallurgy
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C2202/00—Physical properties
    • C22C2202/02—Magnetic
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
    • H01F1/04—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials metals or alloys
    • H01F1/047—Alloys characterised by their composition
    • H01F1/053—Alloys characterised by their composition containing rare earth metals
    • H01F1/055—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5
    • H01F1/057—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B
    • H01F1/0571—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes
    • H01F1/0575—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes pressed, sintered or bonded together
    • H01F1/0577—Alloys characterised by their composition containing rare earth metals and magnetic transition metals, e.g. SmCo5 and IIIa elements, e.g. Nd2Fe14B in the form of particles, e.g. rapid quenched powders or ribbon flakes pressed, sintered or bonded together sintered

Definitions

  • the present application relates to a method for producing a sintered R-T-B based magnet.
  • Sintered R-T-B based magnets each include a main phase formed of a compound having an R 2 Fe 14 B-type crystal structure, a grain boundary phase at grain boundaries of the main phase, and a compound phase generated by an influence of trace amount of elements incorporated thereto or impurities.
  • the sintered R-T-B based magnets exhibit high remanence B r (hereinafter, may be referred to simply as “B r ”) and high coercivity H cJ (hereinafter, may be referred to simply as “H cJ ”), and thus are known as magnets of highest performance among permanent magnets. Therefore, the sintered R-T-B based magnets are used for various uses including various types of motors such as voice coil motors (VCM) of hard disc drives, motors for electric vehicles (EV, HV, PHV) and motors for industrial equipment, home appliance products, and the like.
  • VCM voice coil motors
  • EV, HV, PHV motors for electric vehicles
  • the sintered R-T-B based magnets decrease the size and the weight of various types of motors and the like, and thus contribute to energy savings and environmental load reduction.
  • Such a sintered R-T-B based magnet is produced by a method including a step of preparing an alloy powder, a step of pressing the alloy powder to form a compact, a step of sintering the compact, and the like.
  • Patent Document 1 discloses one example of such sintered R-T-B based magnets.
  • Embodiments of the present disclosure provide a method for producing a sintered R-T-B based magnet capable of solving such a problem.
  • a method for producing a sintered R-T-B based magnet includes a sintering step of sintering a compact of an R-T-B based alloy powder.
  • the sintering step includes a first-stage step of heating the compact to a first sintering temperature T1 to form a first-stage sintered body, a cooling step of decreasing the temperature of the first-stage sintered body to a cooling temperature T0, and a second-stage step of heating the first-stage sintered body to a second sintering temperature T2 to form a second-stage sintered body.
  • the first sintering temperature T1 and the second sintering temperature T2 are higher than 900° C.
  • the cooling temperature T0 is not higher than 900° C.
  • a first sintering time t1, for which the first sintering temperature T1 is maintained in the first-stage step, is shorter than a second sintering time t2, for which the second sintering temperature T2 is maintained in the second-stage step.
  • the first sintering temperature T1 and the second sintering temperature T2 are not lower than 1000° C. and not higher than 1100° C.
  • the first sintering temperature T1 is not lower than 1040° C. and lower than 1080° C.
  • the second sintering temperature T2 is not lower than 1020° C. and lower than 1060° C.
  • the first sintering time t1 is not shorter than 30 minutes and not longer than 2 hours
  • the second sintering time t2 is not shorter than 1 hour and not longer than 15 hours.
  • the first sintering time t1 is not longer than a half of the second sintering time t2.
  • the cooling temperature T0 is not lower than 700° C. and is not higher than 900° C.
  • the alloy powder has a composition containing R at a content not lower than 28% by mass and not higher than 35% by mass, B at a content not lower than 0.8% by mass and not higher than 1.20% by mass, T at a content not lower than 61.5% by mass, and satisfying 14[B]/10.8 ⁇ [T]/55.85 where [B] is a content of B represented with % by mass and [T] is a content of T represented with % by mass.
  • a method for producing a sintered R-T-B based magnet capable of realizing high H cJ and high H k /H cJ is provided.
  • FIG. 1 is a flowchart showing a sintering step according to the present disclosure.
  • FIG. 2 schematically shows an example of temperature profile of heat treatment targets (compact and sintered body) in the sintering step in an embodiment.
  • FIG. 3 is schematically shows another example of temperature profile of the heat treatment targets (compact and sintered body) in the sintering step in the embodiment.
  • FIG. 4 is schematically shows still another example of temperature profile of the heat treatment targets (compact and sintered body) in the sintering step in the embodiment.
  • FIG. 5 is schematically shows yet another example of temperature profile of the heat treatment targets (compact and sintered body) in the sintering step in the embodiment.
  • R is a rare-earth element and contains at least one selected from the group consisting of Nd, Pr and Ce with no exception.
  • T is at least one transition metal and contains Fe with no exception.
  • the method for producing a sintered R-T-B based magnet in this embodiment includes:
  • the first sintering temperature T1 and the second sintering temperature T2 are higher than 900° C., and the cooling temperature T0 is not higher than 900° C.
  • a first sintering time t1, for which the first sintering temperature T1 is maintained in the first-stage step, is shorter than a second sintering time t2, for which the second sintering temperature T2 is maintained in the second-stage step.
  • a sintered R-T-B based magnet includes crystal grains of an Nd 2 Fe 14 B phase (ferromagnetic) as a main phase and an intermetallic compound, such as a B-rich phase rich in boron (B), an Nd-rich phase or the like, located at boundaries of the crystal grains of the main phase.
  • a sintering reaction is caused to proceed by generation of a liquid phase that is contained in powder particles forming the compact and involves such a phase. On a stage where the amount of the liquid phase is insufficient, a reaction of generating a dense texture does not occur. As the amount of the liquid phase increases along with the increase in the temperature, the reaction of generating a dense texture proceeds rapidly.
  • the liquid phase which is generated by a part of the intermetallic compound in the powder particles being melted during the sintering, modifies surfaces of the crystal grains of the main phase or reduces an oxide, while the grains are bound and become dense progressively.
  • H cJ and H,/H cJ may occasionally be decreased unexpectedly due to variations or dispersion in the composition of an alloy powder and in the production conditions. It has also been found out that this phenomenon is conspicuous in the case where the composition ratio of B contained in the sintered R-T-B based magnet is low. It is difficult to avoid the dispersion in the composition of the alloy powder and in the production conditions. Therefore, it is required to realize high H cJ and high H k /H cJ even when there is dispersion in the composition of the alloy powder and in the production conditions.
  • the sintering time is set to be long (for example, 25 hours). However, this extends the sintering time and deteriorates the mass-productivity. In the case where the sintering step is performed at a lower sintering temperature in an attempt to prevent the deterioration in the mass-productivity, the crystal grains exhibit abnormal growth, which may possibly deteriorate the magnetic characteristics rapidly.
  • the sintering needs to be performed so as to avoid the abnormal growth of the crystal grains.
  • the present inventors have found out that the optimal sintering conditions to obtain a dense and uniform crystal texture vary.
  • the present inventors made further investigations based on such knowledge, and as a result, have found out the following.
  • first-stage step to promote formation of a dense texture
  • second-stage step to further sintered
  • a dense and uniform crystal texture is realized even when there is dispersion in the composition of the alloy powder and in the production conditions.
  • a sintered magnet having high H cJ and high H k /H cJ is provided without the sintering being performed for a long time.
  • H k which is one of the parameters defining H k /H cJ , is generally determined as follows.
  • the intensity of magnetization is J
  • the intensity of the magnetic field is H
  • the reading on the H axis of the position at which J has a value of 0.9 ⁇ J r is used.
  • FIG. 2 through FIG. 5 examples of the steps S 10 , S 20 and S 30 mentioned above will be described in more detail.
  • These figures show graphs in which the horizontal axis represents the time and the vertical axis represents the temperature.
  • the graphs schematically show examples of temperature profile of the heat treatment targets (compact and sintered body) in the sintering step.
  • the temperature of such a heat treatment target is measured by a thermometer installed in a sintering device (sintering furnace), such as a thermocouple or the like.
  • the actual temperature of the compact or the sintered body and the reading (measured temperature value) indicated by the thermometer in the sintering furnace do not need to be precisely equal to each other, and a tolerance of ⁇ 5° or less is permitted.
  • the thick solid line represents the relationship between the temperature and the time.
  • the time is an elapsed time from the start of the sintering step.
  • the unit of the elapsed time is, for example, hour, but alternatively, may be minute or second.
  • the temperature is a temperature value measured by the thermometer as described above, but is substantially equal to a set temperature designated by a temperature control program.
  • the thick solid line is formed of straight line segments, but the actual temperature or the set temperature may change in a curve.
  • the temperature of the treatment target increases monotonously from room temperature to the first sintering temperature T1, and the temperature rise rate is constant.
  • the temperature rise rate does not need to be constant, and there may be a period in the middle where the temperature rise rate is zero.
  • the temperature may be kept, for example, at about 200° C. for a time that is not shorter than 1 hour and not longer than 10 hours.
  • each of the first sintering temperature T1 and the second sintering temperature T2 is not lower than 1000° C. and not higher than 1100° C.
  • the first sintering temperature T1 is higher than the second sintering temperature T2.
  • the first sintering temperature T1 and the second sintering temperature T2 may be equal to each other.
  • the first sintering temperature T1 is, for example, not lower than 1040° C. and lower than 1080° C.
  • the second sintering temperature T2 is, for example, not lower than 1020° C. and lower than 1060° C.
  • the first sintering time t1 is not shorter than 30 minutes and not longer than 2 hours, and the second sintering time t2 is not shorter than 1 hour and not longer than 15 hours.
  • a sintered magnet having high H cJ and high H k /H cJ is provided without the sintering being performed for a long time. Therefore, preferably, the first sintering time t1 is not shorter than 30 minutes and not longer than 1 hour, and the second sintering time t2 is not shorter than 1 hour and not longer than 8 hours.
  • the first sintering time t1 is not shorter than 30 minutes and not longer than 1 hour
  • the second sintering time t2 is not shorter than 1 hour and not longer than 8 hours.
  • the first sintering temperature T1 is higher than the second sintering temperature T2, it is preferred that the first sintering time t1 is shorter than the second sintering time t2. In this case, it is preferred that, for example, the first sintering time t1 is not longer than a half of the second sintering time t2.
  • the cooling step (S 20 ) of decreasing the temperature of the first-stage sintered body to the cooling temperature T0 is performed between the first-stage step (S 10 ) and the second-stage step (S 30 ).
  • a time t0, in the cooling step, in which the temperature of the treatment target (first-stage sintered body) is not higher than 900° C. is defined as a “cooling time”. Therefore, the cooling time t0 includes a temperature drop time and a transition time.
  • the temperature drop time is a time period required for the temperature, while decreasing from the first sintering temperature T1, to decrease from 900° C. to the cooling temperature T0.
  • the transition time is a time period required for the temperature, while increasing from the cooling temperature T0, to increase from the cooling temperature T0 to 900° C. It is preferred that the first sintering temperature T1 and the cooling temperature t0 are different from each other by 50° C. or more. That is, it is preferred that the cooling temperature t0 is lower by 50° C. or more than the first sintering temperature T1. T0 is made lower by 50° C. or more than T1, so that a sintered magnet having high H cJ and high H k /H cJ may be provided certainty.
  • the temperature drop rate during the cooling may be less than that in the example shown in FIG. 2 .
  • the magnetic characteristics do not depend much on the temperature drop rate during the cooling. Therefore, from the point of view of shortening the time necessary for the sintering step and thus improving the mass-productivity, the temperature drop rate is preferably not less than 3° C./min., and more preferably not less than 20° C./min.
  • the cooling temperature T0 which is not higher than 900° C., may be in the range that is not lower than 700° C. and not higher than 900° C., or at the level of room temperature as shown in FIG. 5 . From the point of view of shortening the time necessary for the cooling step and thus improving the mass-productivity, the cooling temperature T0 may be set in the range that is, for example, not lower than 800° C. and not higher than 900° C.
  • R is a rare-earth element and contains at least one selected from the group consisting of Nd, Pr and Ce with no exception.
  • a combination of rare-earth elements represented by Nd—Dy, Nd—Tb, Nd—Dy—Tb, Nd—Pr—Dy, Nd—Pr—Tb, or Nd—Pr—Dy—Tb is used.
  • Dy and Tb are especially effective to improve the H cJ .
  • La or any other rare-earth element is usable.
  • misch metal or didymium may be used.
  • R does not need to be a pure element, and may contain impurities unavoidably mixed during the production, in an amount of an industrially available range.
  • R is contained at a content of, for example, not lower than 27% by mass and not higher than 35% by mass.
  • the R content in the sintered R-T-B based magnet is preferably not higher than 31% by mass (not lower than 27% by mass and not higher than 31% by mass, and preferably not lower than 29% by mass and not higher than 31% by mass).
  • the R content in the sintered R-T-B based magnet is set to a level that is not higher than 31% by mass and a content of oxygen therein is set to a level that is not lower than 400 ppm and not higher than 4000 ppm (preferably, not lower than 400 ppm and not higher than 2500 ppm, and more preferably, not lower than 400 ppm and not higher than 2000 ppm), so that the generation of oxidized R is alleviated. Therefore, higher magnetic characteristics are obtained.
  • T contains iron (a case where T is substantially formed of iron is encompassed), and at most 50% by mass of the iron may be replaced with cobalt (Co) (a case where T is substantially formed of iron and cobalt is encompassed). Co is effective to improve the temperature characteristics and the corrosion resistance.
  • the alloy powder may contain cobalt at a content of not higher than 10% by mass.
  • a content of T may be a part other than R and B, or a part other than R, B and M described below.
  • a content of B may be a known content, and is preferably, for example, 0.8% by mass to 1.2% by mass. If the B content is lower than 0.8% by mass, high H cJ may not be obtained. If the B content is higher than 1.2% by mass, the B r may be decreased. A part of B may be replaced with C (carbon).
  • an M element may be incorporated in order to improve the H cJ .
  • the M element is at least one selected from the group consisting of Al, Si, Ti, V, Cr, Mn, Ni, Cu, Zn, Ga, Zr, Nb, Mo, In, Sn, Hf, Ta and W.
  • a content of the M element is preferably not higher than 5.0% by mass. A reason for this is that if the M content is higher than 5.0% by mass, the B r may be decreased. Unavoidable impurities may be contained.
  • a content of N (nitrogen) in the sintered R-T-B based magnet is preferably not lower than 50 ppm and not higher than 600 ppm. Pulverization is performed such that the N (nitrogen) content is not lower than 50 ppm and not higher than 600 ppm, so that the deterioration in the magnetic characteristics caused by the nitriding is suppressed while the ease of pulverization is improved.
  • the nitrogen content is more preferably not lower than 50 ppm and not higher than 400 ppm, and most preferably not lower than 100 ppm and not higher than 300 ppm.
  • a reason for this is that with such a range of nitrogen content, the deterioration in the magnetic characteristics caused by the nitriding is suppressed while the ease of pulverization is further improved.
  • a content of C (carbon) in the sintered R-T-B based magnet is preferably not lower than 50 ppm and not higher than 1300 ppm.
  • composition of the sintered R-T-B based magnet in this embodiment will be shown below.
  • the sintered R-T-B based magnet contains R, B and T at the following contents:
  • Expression 1 i.e., 14[B]/10.8 ⁇ [T]/55.85 is satisfied, so that the content of B is lower than that in a general sintered R-T-B based magnet.
  • [T]/55.85 atomic weight of Fe
  • 14[B]/10.8 atomic weight of B
  • the step of preparing a coarse-pulverized powder of an alloy for the sintered R-T-B based magnet in this embodiment includes a step of preparing an alloy for the sintered R-T-B based magnet and a step of coarse-pulverizing the alloy by, for example, a hydrogen pulverization method or the like.
  • a metal material or an alloy adjusted in advance so as to have the above-described composition is subjected to an ingot casting method, namely, is melted and put into a casting mold. As a result, an alloy ingot is obtained.
  • a molten metal material or alloy may be subjected to a quenching method, for example, a strip casting method or a centrifugal casting method. As a result, an alloy flake is produced.
  • the molten metal material or alloy is put into contact with a monoaxial roll, a biaxial roll, a rotatable disc, a rotatable cylindrical casting mold or the like and quenched, and as a result, a coagulated alloy thinner than an alloy produced by an ingot method is produced.
  • the alloy produced by either the ingot method or the quenching method is usable. It is preferred that the alloy is produced by the quenching method such as the strip casting method or the like.
  • a quenched alloy produced by such a quenching method usually has a thickness in the range of 0.03 mm to 1 mm, and is flake-shaped. The molten alloy starts coagulating from a surface that is in contact with the cooling roll (roll contact surface), and crystal grows like columns in a thickness direction from the roll contact surface.
  • the quenched alloy is formed by cooling performed in a shorter time than an alloy (ingot alloy) produced by the conventional ingot casting method (mold casting method), and therefore, includes a finer texture, has a shorter crystal grain size, and a larger area size of grain boundaries.
  • An R-rich phase expands broadly in the grain boundaries. Therefore, the R-rich phase in the alloy produced by the quenching method is highly dispersed. For this reason, the alloy is easily broken at the grain boundaries by the hydrogen pulverization method.
  • the quenched alloy is pulverized by the hydrogen pulverization method, so that the size (average particle size) of the hydrogen-pulverized powder (coarse-pulverized powder) may be, for example, not longer than 1.0 mm, preferably, not shorter than 10 ⁇ m and not longer than 500 ⁇ m.
  • the coarse-pulverized powder is provided to a jet mill machine including a pulverization chamber filled with inert gas, and is pulverized, to obtain a fine-pulverized powder.
  • a fine-pulverized powder R-T-B based alloy powder having an average particle size that is, for example, not shorter than 2.0 ⁇ m and not longer than 4.5 ⁇ m is obtained.
  • the step of obtaining such a fine-pulverized powder may be performed by use of, for example, a jet mill pulverization system.
  • the content of oxygen in the sintered R-T-B based magnet is increased by, preferably, a level not lower than 50 ppm and not higher than 300 ppm, and more preferably, a level not lower than 50 ppm and not higher than 200 ppm.
  • it is preferred that magnetic field wet press or magnetic field press in an inert gas atmosphere is performed as described below, and the obtained compact is sintered.
  • the fine-pulverized powder obtained in the step of obtaining the fine-pulverized powder preferably has an average particle size of not shorter than 2.0 ⁇ m and not longer than 4.5 ⁇ m. The average particle size is made shorter, so that the magnetic characteristics may be improved.
  • the magnetic field press performed in the step of forming a compact it is preferred to perform the press in an inert gas atmosphere or the wet press to form a compact, from the point of view of suppressing oxidation.
  • a dispersant such as an oily material or the like, and thus are suppressed from contacting oxygen or water vapor in the air. Therefore, the particles are prevented or suppressed from being oxidized by the air before, during and after the pressing step.
  • a slurry containing a dispersant mixed in the fine-pulverized powder is prepared and is supplied to a cavity of a die of a wet pressing apparatus.
  • the slurry is pressed in the magnetic field.
  • a dispersant is a liquid that forms a slurry by having an alloy powder dispersed therein.
  • a dispersant preferably usable for the present disclosure may be mineral oil or synthetic oil.
  • the type of the mineral oil or the synthetic oil there is no specific limitation on the type of the mineral oil or the synthetic oil. If the mineral oil or the synthetic oil has a kinetic viscosity larger than 10 cSt at room temperature, such an increased viscosity strengthens the binding force between the alloy powder particles and may have an adverse influence on the ease of alignment of the alloy powder during the magnetic field wet press. Therefore, the kinetic viscosity of the mineral oil or the synthetic oil at room temperature is preferably not higher than 10 cSt. If the mineral oil or the synthetic oil has a fractional distillation point higher than 400° C., it is difficult to deoil the obtained compact.
  • the fractional distillation point of the mineral oil or the synthetic oil is preferably not higher than 400° C.
  • Vegetable oil may be used as the dispersant.
  • the “vegetable oil” refers to oil extracted from a plant, and there is no specific limitation on the type of the plant.
  • the slurry is obtained by mixing the obtained alloy powder and the dispersant.
  • the mixing ratio of the alloy powder and the dispersant there is no specific limitation on the mixing ratio of the alloy powder and the dispersant. It is preferred that the slurry contains the alloy powder at a concentration that is not lower than 70% on the mass basis (i.e., not lower than 70% by mass), for the following reasons. With such a concentration range, the alloy powder is supplied into the cavity efficiently at a flow rate of 20 to 600 cm 3 /sec., and superb magnetic characteristics are obtained. Preferably, the concentration of the alloy powder in the slurry is not higher than 90% by mass.
  • the alloy powder and the dispersant may be separately prepared and mixed with respective predetermined weights to form a slurry.
  • the slurry may be formed as follows: in the process of dry-pulverizing the coarse-pulverized powder by a jet mill or the like to obtain the alloy powder, a container accommodating a dispersant is located at an alloy powder outlet of a pulverization machine such as the jet mill or the like, and the alloy powder obtained as a result of the pulverization is directly recovered into the dispersant in the container.
  • a slurry is formed.
  • the container is provided with an atmosphere formed of nitrogen gas and/or argon gas, so that the obtained alloy powder is directly recovered into the dispersant without contacting the air to form the slurry.
  • the coarse-pulverized powder may be wet-pulverized by a vibration mill, a ball mill, an attritor or the like while being held in the dispersant.
  • a slurry is formed of the alloy powder and the dispersant.
  • the slurry obtained in such a manner is pressed by a known wet pressing apparatus to obtain a compact having a predetermined size and a predetermined shape.
  • the obtained compact is sintered to obtain a sintered body.
  • the compact is sintered to obtain a sintered body.
  • the sintering step in this embodiment includes:
  • the compact may be sintered by use of vacuum or inert gas such as helium, argon or the like.
  • the obtained sintered body is heat-treated.
  • the heat treatment improves the magnetic characteristics.
  • the conditions for the heat treatment such as the heat treatment temperature, the heat treatment time and the like, may be known conditions.
  • the sintered body is heat-treated at a temperature that is not higher than the first sintering temperature T1 or the second sintering temperature T2 (e.g., 400° C. to 800° C.) for a time not shorter than 1 hour.
  • the sintered R-T-B based magnet obtained in this manner is subjected to a grinding and/or polishing step, a surface treatment step, and a magnetization step as necessary.
  • a sintered R-T-B based magnet is obtained as a final product.
  • the method for producing a sintered R-T-B based magnet according to the present disclosure includes a diffusion step of diffusing a heavy rare-earth element RH (RH is at least one of Tb, Dy and Ho) from the surface to the interior of the sintered body. Diffusion of the heavy rare-earth element RH from the surface to the interior of the sintered body efficiently improves the coercivity.
  • RH is at least one of Tb, Dy and Ho
  • the elements were weighed such that sintered R-T-B based magnets would generally have the composition of No. 1 shown in Table 1 and cast by a strip casting method to obtain a flake-like alloy.
  • the obtained flake-like alloy was hydrogen-embrittled in a hydrogen-pressurized atmosphere, and then dehydrogenated, namely, was heated and cooled in vacuum, to obtain a coarse-pulverized powder.
  • the obtained coarse-pulverized powder was pulverized by use of a jet mill machine to obtain an alloy powder having a D 50 of 3.6 ⁇ m.
  • a lubricant was incorporated into the alloy powder at a ratio of 0.4% by mass with respect to 100% by mass of the alloy powder, and mixed therewith. The mixture was pressed in a magnetic field to obtain a compact.
  • a so-called orthogonal magnetic field pressing apparatus transverse magnetic field pressing apparatus
  • the direction of magnetic field application was orthogonal to the pressurizing direction.
  • the obtained compact was sintered under the conditions shown in Table 2.
  • Table 2 No. 1-4 was obtained as follows.
  • the compact formed so as to have the composition of No. 1 in Table 1 was heated at 1050° C. as the first sintering temperature T1 for 0.5 hours (30 minutes) as the first sintering time t1 to form a first sintered body (first-stage step), the first sintered body was quenched to room temperature (about 30° C.) as the cooling temperature T0 (at a rate of 10° C./min. or more), and the post-cooling first sintered body was heated at 1040° C. as the second sintering temperature for 4 hours as the second sintering time t2 to form a second sintered body (second-stage step).
  • the conditions for forming the other samples are represented in the same manner.
  • the sintering step was performed only once.
  • the post-sintering sintered R-T-B based magnets were each heat-treated; specifically, kept at 900° C. for 2 hours, then cooled to room temperature, kept at 500° C. for 2 hours, and then cooled to room temperature.
  • sintered R-T-B based magnets No. 1-1 through No. 1-9 were obtained.
  • the components of the obtained sintered R-T-B based magnets are shown in Table 1.
  • a sum of the amounts of the components in Table 1, oxygen and carbon is not 100% by mass.
  • a reason for this is that the sintered R-T-B based magnets contain elements as impurities that are not shown in the table. This is also applicable to the other tables.
  • “ ⁇ ” indicates that expression 1 is satisfied
  • “x” indicates that expression 1 is not satisfied.
  • the sintered R-T-B based magnets were each mechanically processed to produce a sample having a length of 7 mm, a width of 7 mm and a thickness of 7 mm. The samples were measured by a B-H tracer to find the magnetic characteristics.
  • the ratio of the H k with respect to the H cJ of the demagnetization curve, i.e., H k /H cJ was found by H k (kA/m)/H cJ (kA/m) ⁇ 100(%).
  • Table 3 The results are shown in Table 3.
  • the sintered R-T-B based magnets in the examples of the present invention each have H cJ 1646 kA/m and H k /H cJ ⁇ 90.1%.
  • the sintered R-T-B based magnets have higher H cJ and higher H k /H cJ than those of the comparative examples.
  • the comparative examples No. 1-1 through No. 1-3
  • the H cJ is significantly decreased (No. 1-1) or the coarse grains are generated (No. 1-3). Therefore, the magnetic characteristics may possibly be decreased unexpectedly due to dispersion in the production conditions.
  • the sintered R-T-B based magnets in the present invention examples all have high H cJ and high H k /H cJ even when the sintering temperatures (T1 and T2) change.
  • the sintering time of the present invention examples and the sintering time of the comparative examples are different from each other by about 0.5 hours, that is, are not much different.
  • the sintered R-T-B based magnets having high H cJ and high H k /H cJ are obtained without the sintering being performed for a long time.
  • the components of the obtained sintered R-T-B based magnets are shown in Tables 4. As shown in Tables 4 and 5, No. 2-1 and No. 2-2 each have the composition of No. 2 in Table 4, No. 2-3 and No. 2-4 each have the composition of No. 3 in Table 4, and No. 2-5 and No. 2-6 each have the composition of No. 4 in Table 4.
  • the magnetic characteristics and the H k /H cJ of the obtained sintered R-T-B based magnets were found in the same manner as in experiment 1. The results are shown in Table 6.
  • the sintered R-T-B based magnets in the present invention examples all have higher H cJ and higher H k /H cJ than those of the comparative examples (No. 2-1, No. 2-2 and No. 2-3 are compared respectively against No. 2-4, No. 2-5 and No. 2-6).
  • each of the sintered R-T-B based magnets was coated with a pressure-sensitive adhesive containing sugar alcohol by a dipping method.
  • the atomized powder was attached to each of the sintered R-T-B based magnets coated with the pressure-sensitive adhesive at a ratio of 2% by mass with respect to the mass of the sintered R-T-B based magnet.
  • the sintered R-T-B based magnets with the atomized powder were heated at 920° C. for 10 hours in a heat treatment furnace to perform the diffusion step, and then cooled.
  • the obtained sintered R-T-B based magnets were heat-treated at 480° C. for 3 hours in a heat treatment furnace.
  • the magnetic characteristics and H k /H cJ of the obtained post-diffusion sintered R-T-B based magnets were found in the same manner as in experiment 1. The results are shown in Table 9.
  • the sintered R-T-B based magnets in the present invention examples have higher H. J and higher H k /H cJ than those of the comparative examples.
  • a method for producing a sintered R-T-B based magnet according to the present disclosure is applicable for a permanent magnet usable for various uses including various types of motors such as voice coil motors (VCM) of hard disc drives, motors for electric vehicles (EV, HV, PHV) and motors for industrial equipment, home appliance products, and the like.
  • VCM voice coil motors
  • EV electric vehicles
  • HV PHV
  • motors for industrial equipment home appliance products, and the like.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Power Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Inorganic Chemistry (AREA)
  • Hard Magnetic Materials (AREA)
  • Powder Metallurgy (AREA)
US18/284,308 2021-03-29 2022-02-24 Method for producing r-t-b based sintered magnet Pending US20240170206A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2021054568 2021-03-29
JP2021-054568 2021-03-29
PCT/JP2022/007631 WO2022209466A1 (ja) 2021-03-29 2022-02-24 Ｒ－ｔ－ｂ系焼結磁石の製造方法

Publications (1)

Publication Number Publication Date
US20240170206A1 true US20240170206A1 (en) 2024-05-23

Family

ID=83458375

Family Applications (1)

Application Number Title Priority Date Filing Date
US18/284,308 Pending US20240170206A1 (en) 2021-03-29 2022-02-24 Method for producing r-t-b based sintered magnet

Country Status (4)

Country Link
US (1) US20240170206A1 (zh)
JP (1) JPWO2022209466A1 (zh)
CN (1) CN117099180A (zh)
WO (1) WO2022209466A1 (zh)

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10303008A (ja) * 1997-04-23 1998-11-13 Hitachi Metals Ltd Ｒ−Ｆｅ−Ｂ系希土類焼結磁石およびその製造方法ならびにそれを用いた超電導磁気軸受装置
JP2004103659A (ja) * 2002-09-05 2004-04-02 Hitachi Metals Ltd 機械強度に優れた希土類焼結磁石およびその製造方法
JP4329318B2 (ja) * 2002-09-13 2009-09-09 日立金属株式会社 希土類焼結磁石およびその製造方法
EP2226137A4 (en) * 2007-12-13 2012-01-25 Showa Denko Kk R-T-B ALLOYING, R-T-B ALLOY MANUFACTURING METHOD, FINE-POWDER FOR R-T-B-R-SELTENER-PERMANENT MAGNETS, AND R-T-B-RARENTER PERMANENT MAGNETS
CN103680918B (zh) * 2013-12-11 2016-08-17 烟台正海磁性材料股份有限公司 一种制备高矫顽力磁体的方法
JP7021577B2 (ja) * 2018-03-22 2022-02-17 日立金属株式会社 Ｒ－ｔ－ｂ系焼結磁石の製造方法

Also Published As

Publication number Publication date
CN117099180A (zh) 2023-11-21
WO2022209466A1 (ja) 2022-10-06
JPWO2022209466A1 (zh) 2022-10-06

Similar Documents

Publication Publication Date Title
CN107871582B (zh) R-Fe-B烧结磁体
CN107871581B (zh) 制备R-Fe-B烧结磁体的方法
JP6361813B2 (ja) Ｒ−ｔ−ｂ系焼結磁石の製造方法
JP6729446B2 (ja) Ｒ−ｔ−ｂ系永久磁石
CN107527699B (zh) R-Fe-B烧结磁体及制备方法
EP1780736B1 (en) R-T-B type alloy, production method of R-T-B type alloy flake, fine powder for R-T-B type rare earth permanent magnet, and R-T-B type rare earth permanent magnet
CN104900361A (zh) R-t-b系稀土族烧结磁铁用合金、合金材料、该磁铁和它们的制造方法及电动机
JP6451900B2 (ja) Ｒ−Ｆｅ−Ｂ系焼結磁石及びその製造方法
JP6221233B2 (ja) Ｒ−ｔ−ｂ系焼結磁石およびその製造方法
JP6582940B2 (ja) Ｒ−ｔ−ｂ系希土類焼結磁石及びその製造方法
JP6471669B2 (ja) Ｒ−ｔ−ｂ系磁石の製造方法
JP2013115156A (ja) Ｒ−ｔ−ｂ系永久磁石の製造方法
JP2012195392A (ja) Ｒ−ｔ−ｂ系永久磁石の製造方法
JP5743458B2 (ja) Ｒ−ｔ−ｂ系希土類永久磁石用合金材料、ｒ−ｔ−ｂ系希土類永久磁石の製造方法およびモーター
JP7179799B2 (ja) Ｒ－Ｆｅ－Ｂ系焼結磁石
US20240170206A1 (en) Method for producing r-t-b based sintered magnet
US10991492B2 (en) R-T-B based permanent magnet
JP7021577B2 (ja) Ｒ－ｔ－ｂ系焼結磁石の製造方法
JP2016169438A (ja) Ｒ−ｔ−ｂ系希土類焼結磁石及びｒ−ｔ−ｂ系希土類焼結磁石用合金
JP4618437B2 (ja) 希土類永久磁石の製造方法およびその原料合金
JP6773150B2 (ja) Ｒ−ｔ−ｂ系希土類焼結磁石用合金、ｒ−ｔ−ｂ系希土類焼結磁石
JP2023037123A (ja) Ｒ－ｔ－ｂ系焼結磁石の製造方法
JP2021097067A (ja) 希土類焼結磁石
JP2021089931A (ja) 希土類焼結磁石

Legal Events

Date Code Title Description
AS Assignment

Owner name: PROTERIAL, LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SAITOU, KOUTA;KUNIYOSHI, FUTOSHI;REEL/FRAME:065049/0347

Effective date: 20230920

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION