US20190249270A1 - Hot-band annealing equipment, hot-band annealing method and descaling method for si-containing hot rolled steel sheet - Google Patents
Hot-band annealing equipment, hot-band annealing method and descaling method for si-containing hot rolled steel sheet Download PDFInfo
- Publication number
- US20190249270A1 US20190249270A1 US16/343,217 US201716343217A US2019249270A1 US 20190249270 A1 US20190249270 A1 US 20190249270A1 US 201716343217 A US201716343217 A US 201716343217A US 2019249270 A1 US2019249270 A1 US 2019249270A1
- Authority
- US
- United States
- Prior art keywords
- steel sheet
- hot
- rolled steel
- descaling
- hot rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/34—Methods of heating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/82—Descaling by thermal stresses
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1261—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1277—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties involving a particular surface treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/0062—Heat-treating apparatus with a cooling or quenching zone
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
- C21D9/54—Furnaces for treating strips or wire
- C21D9/56—Continuous furnaces for strip or wire
- C21D9/60—Continuous furnaces for strip or wire with induction heating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
- C21D9/54—Furnaces for treating strips or wire
- C21D9/56—Continuous furnaces for strip or wire
- C21D9/62—Continuous furnaces for strip or wire with direct resistance heating
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23G—CLEANING OR DE-GREASING OF METALLIC MATERIAL BY CHEMICAL METHODS OTHER THAN ELECTROLYSIS
- C23G1/00—Cleaning or pickling metallic material with solutions or molten salts
- C23G1/02—Cleaning or pickling metallic material with solutions or molten salts with acid solutions
- C23G1/08—Iron or steel
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/34—Methods of heating
- C21D1/40—Direct resistance heating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/34—Methods of heating
- C21D1/42—Induction heating
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P10/00—Technologies related to metal processing
- Y02P10/25—Process efficiency
Definitions
- This invention relates to a hot-band annealing equipment, a hot-band annealing method and a descaling method, and more particularly to an equipment and a method for performing a hot-band annealing of a Si-containing hot rolled steel sheet containing a large amount of Si as a raw material for a grain-oriented electrical steel sheet, a non-oriented electrical steel sheet, a high-strength cold rolled steel sheet or the like, and a descaling method of the Si-containing hot rolled steel sheet after the hot-band annealing.
- Non-oriented electrical steel sheets mainly used as an iron core material of electric equipment are roughly divided into a non-oriented electrical steel sheet and a grain-oriented electrical steel sheet. Both of these steel sheets usually contain a large amount of Si or Al increasing specific resistance of steel to decrease an iron loss.
- the non-oriented electrical steel sheet is usually produced by melting a steel adjusted to a predetermined chemical composition, shaping the steel into a slab by a continuous casting method, and subjecting the slab to hot rolling or the like, hot-band annealing if necessary, pickling, cold rolling and finish annealing for primary recrystallization.
- the grain-oriented electrical steel sheet is usually produced by melting a steel adjusted to a predetermined chemical composition, shaping the steel into a slab by a continuous casting method or the like, and subjecting the slab to hot rolling, hot-band annealing if necessary, pickling, cold rolling, primary recrystallization annealing that also works as decarburization annealing, application of an annealing separator and finish annealing for secondary recrystallization.
- the hot-band annealing is conducted by subjecting the steel sheet after the hot rolling (hot rolled sheet) to an annealing to resolve insufficient recrystallization of the hot rolled sheet and to coarsen or regulate crystal grains before the cold rolling so that the texture of the steel sheet before the cold rolling can be improved into favorable one for magnetic properties thereof or ridging can be prevented.
- the pickling is a process for removing the oxidized scale from the surface of the steel sheet before the cold rolling (descaling process) and is an inevitable process in the production of not only a hot rolled steel sheet for an electrical steel sheet but also a steel sheet to be cold rolled.
- the pickling solution is usually used any one of hydrochloric acid, sulfuric acid, hydrofluoric acid and a mixed acid of these acids.
- the oxidized scale of the hot rolled steel sheet as a raw material for the electrical steel sheet or high-strength cold rolled steel sheet containing a large amount of Si or Al is composed of outer scales such as FeO, Fe 3 O 4 , Fe 2 O 3 and the like formed by the diffusion of Fe from the inside of the steel sheet toward the outside, and subscales comprised of Si-based oxides such as SiO 2 and Fe 2 SiO 4 and Al 2 O 3 formed by the diffusion of oxygen from the outside of the steel sheet into the inside as shown in FIG. 1 . It is known that the oxidized scale is poor in the descaling property, and particularly, the subscale containing Al 2 O 3 is extremely poor in the descaling property.
- the descaling of the Si-containing hot rolled steel sheet is frequently performed by combining a light draft rolling with a mechanical descaling such as roller levelling, tension levelling, shot blasting or the like before the pickling as shown in FIG. 2( a ) .
- Patent Literature 1 discloses a method of producing a silicon steel substrate comprising a steelmaking process, a hot rolling process and a normalizing process using a normalizing furnace with a non-oxidation heating furnace part provided with three or more furnace zones, wherein an energy supply rate in the furnace zone used in the non-oxidation heating furnace part is adjusted within a range of 15-95% and an excess factor ⁇ (a rate of an actual combustion air amount to a theoretical combustion air amount) in the non-oxidation heating furnace part is adjusted within a range of 0.8 ⁇ 1.0 to prevent the formation of a high-density oxide in the normalizing process.
- the temperature distribution of the heating furnace is made non-uniform by the adjustment of the energy supply rate or the excess factor ⁇ , so that there is a problem that it is difficult to perform an adequate heating in an actual operation.
- Patent Literature 2 proposes a method for improving the descaling property by heating the steel sheet before pickling with an induction heating device so as to have cracking of the oxidized scale reach to the surface of the base iron and thereafter blowing a pickling solution into the crack.
- Patent Literature 3 discloses a method wherein a scale breaker is disposed before a pickling tank and a plurality of deflector rolls, jetting nozzles and an induction heating device are disposed in the pickling tank to cause cracking in the scale by the scale breaker and thereafter the crack is opened by bending using the deflector rolls and a pickling solution is sprayed to the opening and the temperature of the steel sheet is increased by induction heating to promote the chemical reaction.
- Patent Literature 1 JP-A-2015-511995
- Patent Literature 2 JP-A-S61-079790
- Patent Literature 3 JP-A-H09-078273
- Patent Literature 2 when the steel sheet is heated before the pickling, there is a problem that the temperature of the pickling solution is increased to generate harmful acid fume or the steel sheet is excessively pickled or the durability of the pickling tank is decreased.
- Patent Literature 3 it is necessary to dispose a heating equipment, roll, nozzle and so on in the pickling tank, and there is a problem that the service life of the facility equipment is shortened or the maintenance thereof is difficult.
- the present invention is made in view of the aforementioned problems inherent to the conventional techniques, and the object thereof is to provide a hot-band annealing equipment capable of improving a descaling property of a Si-containing hot rolled steel sheet without requiring the mechanical descaling or the heating of the steel sheet in the pickling process and to propose a hot-band annealing method and a descaling method using the above equipment.
- the inventors have focused the heating method from a viewpoint that it is important to increase the stripping property of the oxidized scale in order to improve the descaling property and made various studies to solve the above problems.
- thermal stress is caused resulting from the difference of the thermal expansion amounts between the oxidized scale and the base iron when heated to the same temperature as the base iron, and that a temperature difference is caused between the base iron and the oxidized scale due to the difference of the thermal conductivity when an induction heating or an electric heating, which causes heat generation of the steel sheet itself, is adopted instead of radiation heating, which heats the steel sheet from the outside thereof, as the method of heating the steel sheet, and that when the steel sheet is rapidly heated by using the induction heating or the electric heating, the temperature difference between the base iron and the steel sheet becomes larger to generate a remarkably large thermal stress between the oxidized scale and the base iron and hence cracking is caused in the oxidized
- a hot-band annealing equipment provided with a heating zone, a soaking zone and a cooling zone for subjecting a Si-containing hot rolled steel sheet to a hot-band annealing, characterized in that a rapid heating device is disposed at an upper stream side of the heating zone and/or near the inlet side of the heating zone.
- the hot-band annealing equipment is characterized in that the rapid heating device is an induction heating device or an electric heating device.
- a hot-band annealing method by subjecting a Si-containing hot rolled steel sheet to hot-band annealing using the aforementioned hot-band annealing equipment, characterized in that the Si-containing hot rolled sheet is heated by not lower than 50° C. at a heating rate of not less than 15° C./s by using the rapid heating device.
- the hot-band annealing method according to an embodiment of the invention is characterized in that a start temperature for heating the Si-containing hot rolled sheet by using the rapid heating device is in a range of room temperature to 700° C.
- the invention according to an embodiment is a descaling method characterized by subjecting the Si-containing hot rolled steel sheet after the hot-band annealing in the aforementioned method to pickling without conducting a mechanical descaling.
- the invention is a descaling method characterized by subjecting the Si-containing hot rolled steel sheet after the hot-band annealing in the aforementioned method to pickling after a mechanical descaling.
- the Si-containing hot rolled steel sheet to be targeted in the descaling method according to an embodiment of the invention is characterized by containing not less than 1.0 mass % of Si.
- the Si-containing hot rolled steel sheet to be targeted in the descaling method according to an embodiment of the invention is characterized by being a raw material for an electrical steel sheet.
- the rapid heating device is disposed in the equipment for subjecting a Si-containing hot rolled steel sheet to hot-band annealing to conduct a rapid heating at not less than a predetermined heating rate and by not less than a predetermined temperature rising amount, whereby cracking is introduced in the oxidized scale to improve the stripping property, so that it becomes possible to remove the oxidized scale from the steel sheet surface only by pickling without conducting a mechanical descaling.
- the heating device used in the rapid heating of the steel sheet acts as a part of the heating zone in the hot-band annealing equipment and contributes to the improvement of the thermal energy efficiency.
- FIGS. 1( a ) and 1( b ) are views illustrating a cross-sectional structure of an oxidized scale formed on a surface of a Si-containing hot rolled steel sheet.
- FIGS. 2( a ) and 2( b ) are a view showing an equipment line of an embodiment of the present invention and a view showing an equipment line of the conventional technique for comparison, respectively.
- FIG. 3 is a view showing a weight loss of a Si-containing hot rolled steel sheet subjected to a mechanical descaling or pickling after hot-band annealing for comparison.
- the inventors have focused on an influence of the difference among the heating methods of the steel sheet, i.e., the difference between a radiation heating for slowly heating the steel sheet from the outside and an induction heating or a direct electric heating for rapidly heating the steel sheet from the inside upon the descaling property, from a viewpoint that it is important to increase the stripping property of the oxidized scale in order to improve the descaling property of the Si-containing hot rolled sheet as previously mentioned.
- the oxidized scale formed on the surface of the hot rolled steel sheet is composed of plural layers having different chemical compositions as shown in FIG. 1 , but each of these layers has a thermal expansion coefficient largely different from that of the base iron, so that a thermal stress is caused resulting from the difference of the thermal expansion amounts between the scale and the base iron, even when the scale is heated to the same temperature as the base iron.
- the oxidized scale is first heated and then the steel sheet is heated, a large temperature difference is not caused therebetween.
- heat generation is caused in the steel sheet itself to produce a temperature difference between the oxidized scale and the base iron.
- the rapid heating can be conducted in the induction heating or the like, the temperature difference between the oxidized scale and the base iron is further increased as compared to the slow heating by thermal conduction such as the radiation heating.
- the inventors have conducted the following experiments to confirm the validity of the above idea.
- a test specimen is taken out from a hot rolled steel sheet for a non-oriented/grain-oriented electrical steel sheet containing 3.0 mass % of Si (hot rolled sheet) and subjected to a heat treatment simulating hot-band annealing at 1050° C. for 60 seconds for the hot rolled sheet.
- the test specimen is rapidly heating from room temperature (20° C.) up to 30° C., 50° C., 70° C., 100° C., 400° C. and 700° C. at a heating rate of 50° C./s with a solenoid-type induction heating device, heated from the each temperature after the rapid heating to 1050° C. with a direct type heating furnace (a radiation type heating furnace), held for 60 seconds, and then cooled at a rate of 25° C./s in the heat treatment.
- the atmosphere in the heat treatment is set to be a nitrogen atmosphere.
- test specimen after the heat treatment is subjected to a pickling by immersing in an aqueous solution having 8 mass % of HCl kept at a temperature of 80° C. for 60 seconds, and a stripping condition of an oxidized scale from the steel sheet surface after the pickling is visually observed to evaluate the descaling property.
- the descaling property is evaluated as superior (o) when the surface appearance after the descaling is equal to or superior to that by the conventional descaling method (mechanical descaling and pickling) for the Si-containing hot rolled steel sheet, as inferior (A) when the surface appearance is inferior to that by the conventional descaling method (mechanical descaling and pickling) but superior to that by the conventional pickling only, and as bad (x) when the surface appearance is equal to that by the conventional pickling only.
- the influence of the heating rate for the steel sheet on the descaling property is evaluated based on the results of Experiment 1 by changing the heating rate to five levels of 5° C./s, 10° C./s, 15° C./s, 20° C./s, and 50° C./s when the temperature rising amount from room temperature (20° C.) is 50° C., or the heating temperature is 70° C. (constant) and when the other conditions and the evaluation standard of the descaling property are the same as in Experiment 1.
- the present invention is based on the above new knowledge.
- the hot rolled sheet targeted by the present invention is preferable to contain not less than 1.0 mass % of Si.
- 1.0 mass % When it is less than 1.0 mass %, the decrease of the descaling property by the pickling is not remarkable, so that the mechanical descaling is not necessary before the pickling.
- an embodiment of the present invention is obviously applicable to a hot rolled steel sheet containing less than 1.0 mass % of Si.
- the upper limit of Si is not particularly defined, but it is about 5.0 mass % from a viewpoint of ensuring the threading property to a production line. Preferably, it is within a range of 1.8 to 4.0 mass %.
- the hot rolled sheet containing Si in the above range are concretely included a hot rolled steel sheet as a raw material for a non-oriented electrical steel sheet or a grain-oriented electrical steel sheet and a hot rolled steel sheet as a raw material for a high-strength cold rolled steel sheet or a high-strength surface-treated steel sheet, each of which is required to have an excellent surface property.
- the hot-band annealing equipment according to the present invention is preferable to be a continuous annealing furnace. It is because the rapid heating is impossible in a batch type (box-type) annealing furnace.
- the heating device used in the rapid heating is preferable to be an induction heating device or an electric heating device capable of generating heat from the steel sheet itself and conducting the rapid heating.
- the induction heating device is preferable to be a solenoid-type device rather than a transverse-type device because the steel sheet is uniformly heated in the widthwise direction by using the solenoid-type device.
- the heating rate is preferably not less than 30° C./s, more preferably not less than 50° C./s from a viewpoint of increasing the temperature difference between the base iron and the oxidized scale.
- the temperature rising amount in the rapid heating is preferably not lower than 80° C., more preferably not lower than 100° C. from the same viewpoint.
- the end temperature in the rapid heating exceeds 700° C.
- a large current is necessary in the heating or the heating device becomes large scale.
- the steel sheet temperature exceeds a Curie point in the heating by using a solenoid-type induction heating, the heating efficiency is violently decreased, so that the upper limit of the rapid heating (end temperature) is preferable to be about 700° C. More preferably, it is not higher than 680° C.
- the position of disposing the rapid heating device in the equipment for the hot-band annealing is preferable to be an upstream side of the heating zone (just before the heating zone) and/or in the heating zone.
- the rapid heating device is disposed just before the heating zone, there is caused no problem, but when it is disposed in the heating zone, it is preferable to be disposed in a zone having a temperature inside the furnace of not higher than 700° C. in the inlet side of the heating zone (the most upstream side), from a viewpoint of preventing thermal damage of an induction heating coil or a conducting roll.
- the temperature range for disposing the rapid heating device, or the start temperature for rapidly heating the steel sheet is preferable to be within a range of room temperature to 700° C. It is more preferably a range of room temperature to 620° C., further preferably a range of room temperature to 600° C.
- a large number of fine cracks are introduced into the oxidized scale formed on the surface of the Si-containing hot rolled steel sheet subjected to the rapid heating after the hot-band annealing to improve the stripping property of the oxidized scale, so that the descaling property equal to or more than that when the mechanical descaling is performed can be obtained even when the mechanical descaling is not performed before pickling.
- the mechanical descaling process before the pickling has been necessary in the conventional method as shown in FIG. 2( a ) , while it is possible to omit the mechanical descaling process by disposing the rapid heating device just before the heating zone in the hot-band annealing equipment, for example, as shown in FIG.
- FIG. 2( b ) shows an example that the rapid heating device is disposed just before the heating zone, but it may be disposed in a low temperature region at the upstream side of the heating zone.
- the mechanical descaling may be obviously performed in order to further improve the pickling property.
- a test specimen having a width of 100 mm and a length of 300 mm is taken out from a hot rolled steel sheet for an electrical steel sheet containing 3.5 mass % of Si and having a thickness of 2.5 mm and subjected to a heat treatment under the following conditions A and B simulating hot-band annealing.
- the atmosphere in the annealing under each of the conditions A and B is a N 2 atmosphere.
- Condition A The steel sheet is heated from room temperature (20° C.) to 1050° C. at 10° C./s, held at 1050° C. for 40 seconds and then cooled at a rate of 25° C./s in an experimental furnace simulating a direct-type side burner heating furnace (radiation heating furnace).
- Condition B The steel sheet is rapidly heated from room temperature (20° C.) to 700° C. at 60° C./s with an induction heating device, further heated from 700° C. to 1050° C. at 20° C./s with the radiation heating furnace used in the condition A, held at 1050° C. for 40 seconds and then cooled at 25° C./s.
- test specimen after the hot-band annealing is divided into two equal parts in the longitudinal direction.
- One part is subjected to a mechanical descaling (shot blasting) under the following condition, and the other part is not subjected to the mechanical descaling.
- test specimen divided into two equal parts in the longitudinal direction is further divided into two equal parts in the widthwise direction.
- One specimen is subjected to descaling by pickling under the following condition a and the other is descaled by pickling under the following condition b.
- Condition b Immersion in an aqueous solution containing 8 mass % of HCl at 80° C. for 40 seconds
- the time required for descaling (pickling time) in the pickling under the above condition is about 60 seconds.
- FIG. 3 shows a weight loss (g/m 2 ) of the test specimen in each stage after the mechanical descaling and after the pickling, after the hot-band annealing is conducted.
- the test specimen that is only subjected to the pickling without the mechanical descaling has the descaling property equal to that subjected to the mechanical descaling, by rapidly heating the specimen to 700° C. by the induction heating in the heating process of the hot-band annealing.
- the oxidized scale is removed sufficiently from the surface in the test specimen rapidly heated to 700° C. by the induction heating even when the pickling time is shortened from the usual time of 60 seconds to 40 or 20 seconds. According to the present invention, therefore, it is possible not only to omit the mechanical descaling from the descaling process but also to shorten the pickling time.
- the method according to embodiments of the present invention provides the effect of improving the descaling property regardless of the presence or absence of Si content, so that it is applicable to not only the Si-containing hot rolled steel sheet for an electrical steel sheet or high-strength steel sheet but also a general-purpose hot rolled steel sheet containing no Si.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Manufacturing & Machinery (AREA)
- Electromagnetism (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Cleaning And De-Greasing Of Metallic Materials By Chemical Methods (AREA)
- Manufacturing Of Steel Electrode Plates (AREA)
- Heat Treatment Of Strip Materials And Filament Materials (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016205194A JP6748375B2 (ja) | 2016-10-19 | 2016-10-19 | Si含有熱延鋼板の脱スケール方法 |
JP2016-205194 | 2016-10-19 | ||
PCT/JP2017/036766 WO2018074295A1 (fr) | 2016-10-19 | 2017-10-11 | Équipement de recuit de tôle laminée à chaud pour tôle d'acier laminée à chaud contenant du silicium, procédé de recuit de tôle laminée à chaud et procédé de décalaminage |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2017/036766 A-371-Of-International WO2018074295A1 (fr) | 2016-10-19 | 2017-10-11 | Équipement de recuit de tôle laminée à chaud pour tôle d'acier laminée à chaud contenant du silicium, procédé de recuit de tôle laminée à chaud et procédé de décalaminage |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US17/506,076 Division US11788165B2 (en) | 2016-10-19 | 2021-10-20 | Hot-band annealing equipment, hot-band annealing method and descaling method for Si-containing hot rolled steel sheet |
Publications (1)
Publication Number | Publication Date |
---|---|
US20190249270A1 true US20190249270A1 (en) | 2019-08-15 |
Family
ID=62018687
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/343,217 Abandoned US20190249270A1 (en) | 2016-10-19 | 2017-10-11 | Hot-band annealing equipment, hot-band annealing method and descaling method for si-containing hot rolled steel sheet |
US17/506,076 Active 2037-12-06 US11788165B2 (en) | 2016-10-19 | 2021-10-20 | Hot-band annealing equipment, hot-band annealing method and descaling method for Si-containing hot rolled steel sheet |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US17/506,076 Active 2037-12-06 US11788165B2 (en) | 2016-10-19 | 2021-10-20 | Hot-band annealing equipment, hot-band annealing method and descaling method for Si-containing hot rolled steel sheet |
Country Status (7)
Country | Link |
---|---|
US (2) | US20190249270A1 (fr) |
EP (1) | EP3530762B1 (fr) |
JP (1) | JP6748375B2 (fr) |
KR (1) | KR102292306B1 (fr) |
CN (1) | CN109844143B (fr) |
RU (1) | RU2724265C1 (fr) |
WO (1) | WO2018074295A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112143866A (zh) * | 2020-09-22 | 2020-12-29 | 武汉钢铁有限公司 | 伺服电机用无取向硅钢板及其生产方法 |
US20220119905A1 (en) * | 2019-01-16 | 2022-04-21 | Nippon Steel Corporation | Method for producing grain oriented electrical steel sheet |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP7192378B2 (ja) * | 2018-10-11 | 2022-12-20 | 日本製鉄株式会社 | 圧延設備及び鋼板の圧延方法 |
DE102019217491A1 (de) * | 2019-08-30 | 2021-03-04 | Sms Group Gmbh | Verfahren zur Herstellung eines kaltgewalzten Si-legierten Elektrobandes mit einer Kaltbanddicke dkb < 1 mm aus einem Stahlvorprodukt |
FR3102549B1 (fr) * | 2019-10-28 | 2021-11-26 | Fives Stein | Dispositif et procédé de pilotage d’un four de réchauffage |
AT524149B1 (de) * | 2020-08-20 | 2022-11-15 | Nntech Gmbh | Verfahren zur Bearbeitung eines Stahlblechs |
CN118139995A (zh) | 2021-10-27 | 2024-06-04 | 杰富意钢铁株式会社 | 热轧钢带的退火方法 |
JPWO2023190645A1 (fr) * | 2022-03-31 | 2023-10-05 | ||
JPWO2024009783A1 (fr) * | 2022-07-04 | 2024-01-11 |
Family Cites Families (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2892744A (en) | 1956-07-23 | 1959-06-30 | United States Steel Corp | Method and apparatus for the continuous heat-treatment of metal strip |
US4081296A (en) * | 1973-09-26 | 1978-03-28 | Valjim Corporation | Direct-current electrical heat-treatment of continuous metal sheets in a protective atmosphere |
JPS5214444A (en) | 1975-07-24 | 1977-02-03 | Japanese National Railways<Jnr> | Location detecting system of a moving body |
JPS5934212B2 (ja) * | 1981-01-06 | 1984-08-21 | 新日本製鐵株式会社 | 含Al一方向性珪素鋼板の製造法 |
JPS6179790A (ja) | 1984-09-26 | 1986-04-23 | Kawasaki Steel Corp | 鋼帯の酸洗方法および装置 |
US4732889A (en) | 1985-02-06 | 1988-03-22 | Chugai Seiyaku Kabushiki Kaisha | Pharmaceutical composition for the treatment of the anemia of rheumatoid arthritis |
JPH05214444A (ja) * | 1992-01-31 | 1993-08-24 | Sumitomo Metal Ind Ltd | 磁気特性面内異方性の小さい無方向性電磁鋼板の製造法 |
JPH062032A (ja) * | 1992-06-24 | 1994-01-11 | Mitsubishi Heavy Ind Ltd | 鋼板の焼鈍酸洗方法 |
AT404907B (de) * | 1993-07-13 | 1999-03-25 | Andritz Patentverwaltung | Verfahren und anlage zum herstellen von edelstahlband |
JP2970445B2 (ja) * | 1994-12-14 | 1999-11-02 | 住友金属工業株式会社 | Si添加高張力鋼材の溶融亜鉛めっき方法 |
JP2964911B2 (ja) * | 1995-04-21 | 1999-10-18 | 住友金属工業株式会社 | P添加高張力鋼材の合金化溶融亜鉛めっき方法 |
JP2955500B2 (ja) | 1995-09-13 | 1999-10-04 | 住友重機械工業株式会社 | 酸洗装置および酸洗方法 |
JP3415377B2 (ja) * | 1996-11-13 | 2003-06-09 | Jfeスチール株式会社 | 極めて鉄損の低い高磁束密度方向性電磁鋼板の製造方法 |
US5885371A (en) | 1996-10-11 | 1999-03-23 | Kawasaki Steel Corporation | Method of producing grain-oriented magnetic steel sheet |
JP2002173742A (ja) * | 2000-12-04 | 2002-06-21 | Nisshin Steel Co Ltd | 形状平坦度に優れた高強度オーステナイト系ステンレス鋼帯およびその製造方法 |
JP2002361314A (ja) * | 2001-03-30 | 2002-12-17 | Nippon Steel Corp | 方向性珪素鋼の熱延板の連続熱処理設備および連続熱処理方法 |
BRPI0811253A2 (pt) * | 2007-04-05 | 2014-11-04 | Nippon Steel Corp | Método de recozimento contínuo de tira de aço tendo um ponto curie e facilidade de recozimento contínuo da mesma. |
KR20100076744A (ko) * | 2008-12-26 | 2010-07-06 | 주식회사 포스코 | 강판의 소둔 장치, 도금 품질이 우수한 도금 강판의 제조 장치 및 이를 이용한 도금 강판의 제조방법 |
JP4840518B2 (ja) | 2010-02-24 | 2011-12-21 | Jfeスチール株式会社 | 方向性電磁鋼板の製造方法 |
JP2011219793A (ja) * | 2010-04-06 | 2011-11-04 | Nippon Steel Corp | 磁気特性の優れた一方向性電磁鋼板用熱延板及びその製造方法 |
JP2013127101A (ja) * | 2011-12-19 | 2013-06-27 | Jfe Steel Corp | メカニカルデスケーリング性に優れた引張強度600MPa以上の高張力鋼材およびその製造方法 |
CN103305745B (zh) | 2012-03-09 | 2016-04-27 | 宝山钢铁股份有限公司 | 一种高质量硅钢常化基板的生产方法 |
CN103302104B (zh) * | 2012-03-13 | 2015-07-22 | 宝山钢铁股份有限公司 | 热轧硅钢的制造方法 |
BR112015003316A2 (pt) | 2012-09-03 | 2017-07-04 | Jfe Steel Corp | aparelho de aquecimento rápido de linha de recozimento contínio |
EP2708609A1 (fr) * | 2012-09-17 | 2014-03-19 | Linde Aktiengesellschaft | Système et procédé de traitement par induction de métaux |
RU2617304C2 (ru) * | 2013-02-21 | 2017-04-24 | ДжФЕ СТИЛ КОРПОРЕЙШН | Способ изготовления полуфабриката листа из нетекстурированной электротехнической стали с превосходными магнитными свойствами |
JP6132103B2 (ja) | 2014-04-10 | 2017-05-24 | Jfeスチール株式会社 | 方向性電磁鋼板の製造方法 |
US10316382B2 (en) | 2015-02-24 | 2019-06-11 | Jfe Steel Corporation | Method for producing non-oriented electrical steel sheets |
JP6402865B2 (ja) * | 2015-11-20 | 2018-10-10 | Jfeスチール株式会社 | 無方向性電磁鋼板の製造方法 |
WO2017086036A1 (fr) * | 2015-11-20 | 2017-05-26 | Jfeスチール株式会社 | Procédé de fabrication d'une tôle d'acier électromagnétique à grains non orientés |
JP6406522B2 (ja) * | 2015-12-09 | 2018-10-17 | Jfeスチール株式会社 | 無方向性電磁鋼板の製造方法 |
JP6455468B2 (ja) | 2016-03-09 | 2019-01-23 | Jfeスチール株式会社 | 方向性電磁鋼板の製造方法 |
-
2016
- 2016-10-19 JP JP2016205194A patent/JP6748375B2/ja active Active
-
2017
- 2017-10-11 KR KR1020197009164A patent/KR102292306B1/ko active IP Right Grant
- 2017-10-11 EP EP17861698.3A patent/EP3530762B1/fr active Active
- 2017-10-11 US US16/343,217 patent/US20190249270A1/en not_active Abandoned
- 2017-10-11 RU RU2019115127A patent/RU2724265C1/ru active
- 2017-10-11 CN CN201780063342.XA patent/CN109844143B/zh active Active
- 2017-10-11 WO PCT/JP2017/036766 patent/WO2018074295A1/fr unknown
-
2021
- 2021-10-20 US US17/506,076 patent/US11788165B2/en active Active
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20220119905A1 (en) * | 2019-01-16 | 2022-04-21 | Nippon Steel Corporation | Method for producing grain oriented electrical steel sheet |
CN112143866A (zh) * | 2020-09-22 | 2020-12-29 | 武汉钢铁有限公司 | 伺服电机用无取向硅钢板及其生产方法 |
Also Published As
Publication number | Publication date |
---|---|
JP2018066040A (ja) | 2018-04-26 |
CN109844143B (zh) | 2021-09-07 |
CN109844143A (zh) | 2019-06-04 |
WO2018074295A1 (fr) | 2018-04-26 |
US11788165B2 (en) | 2023-10-17 |
EP3530762A4 (fr) | 2019-11-06 |
JP6748375B2 (ja) | 2020-09-02 |
KR20190044660A (ko) | 2019-04-30 |
EP3530762A1 (fr) | 2019-08-28 |
RU2724265C1 (ru) | 2020-06-22 |
EP3530762B1 (fr) | 2022-08-17 |
KR102292306B1 (ko) | 2021-08-24 |
US20220033928A1 (en) | 2022-02-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US11788165B2 (en) | Hot-band annealing equipment, hot-band annealing method and descaling method for Si-containing hot rolled steel sheet | |
TWI580794B (zh) | Non - directional electrical steel sheet and manufacturing method thereof | |
US20180355454A1 (en) | Method for producing non-oriented electrical steel sheet | |
US11225699B2 (en) | Method for producing non-oriented electrical steel sheet | |
US10294544B2 (en) | Method for producing grain-oriented electrical steel sheet | |
JP6119959B2 (ja) | 方向性電磁鋼板の製造方法 | |
US11286538B2 (en) | Method for manufacturing grain-oriented electrical steel sheet | |
EP3960887B1 (fr) | Procédé de fabrication de tôle en acier électrique à grains orientés | |
US20220195555A1 (en) | Method for producing grain-oriented electrical steel sheet | |
JP7197069B1 (ja) | 方向性電磁鋼板の製造方法 | |
KR20150074892A (ko) | 방향성 전기강판, 그 제조방법 및 1차 재결정 소둔 설비 | |
JP6137490B2 (ja) | 一次再結晶集合組織の予測方法および方向性電磁鋼板の製造方法 | |
JP5854236B2 (ja) | 方向性電磁鋼板の製造方法 | |
EP4335939A1 (fr) | Procédé destiné à la fabrication d'une tôle d'acier électrique à grains orientés | |
JP2014173103A (ja) | 方向性電磁鋼板の製造方法 | |
JP7338812B1 (ja) | 方向性電磁鋼板の製造方法 | |
US5572892A (en) | Method of producing silicon steel hot rolled sheets having excellent surface properties | |
JP6544344B2 (ja) | 方向性電磁鋼板の製造方法 | |
JP2003277830A (ja) | 板幅方向に均一な磁気特性を有する方向性電磁鋼板の製造方法 | |
JPH05117751A (ja) | 一方向性電磁鋼板用連続鋳造スラブの熱間圧延方法 | |
JP2016084540A (ja) | 方向性電磁鋼板の製造方法 | |
JPH04329828A (ja) | 磁気特性の優れた方向性けい素鋼板の製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: JFE STEEL CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YAMADA, GOKI;HARADA, YOSHIMITSU;TAKATSU, TAKAHIRO;AND OTHERS;SIGNING DATES FROM 20190305 TO 20190312;REEL/FRAME:049183/0154 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: APPLICATION DISPATCHED FROM PREEXAM, NOT YET DOCKETED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: ADVISORY ACTION MAILED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |