US20170183814A1 - Sheet-like article, and method for producing same - Google Patents

Sheet-like article, and method for producing same Download PDF

Info

Publication number
US20170183814A1
US20170183814A1 US15/115,518 US201515115518A US2017183814A1 US 20170183814 A1 US20170183814 A1 US 20170183814A1 US 201515115518 A US201515115518 A US 201515115518A US 2017183814 A1 US2017183814 A1 US 2017183814A1
Authority
US
United States
Prior art keywords
polyurethane resin
mass
sheet material
fibrous substrate
polyurethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/115,518
Other languages
English (en)
Inventor
Hisashi Murahara
Shunichiro Nakai
Yukihiro Matsuzaki
Makoto Nishimura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Industries Inc
Original Assignee
Toray Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Industries Inc filed Critical Toray Industries Inc
Assigned to TORAY INDUSTRIES, INC. reassignment TORAY INDUSTRIES, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MATSUZAKI, YUKIHIRO, MURAHARA, HISASHI, NAKAI, Shunichiro, NISHIMURA, MAKOTO
Publication of US20170183814A1 publication Critical patent/US20170183814A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D06N3/0002—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate
    • D06N3/0004—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate using ultra-fine two-component fibres, e.g. island/sea, or ultra-fine one component fibres (< 1 denier)
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/0804—Manufacture of polymers containing ionic or ionogenic groups
    • C08G18/0819—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups
    • C08G18/0823—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups containing carboxylate salt groups or groups forming them
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/42—Polycondensates having carboxylic or carbonic ester groups in the main chain
    • C08G18/44—Polycarbonates
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/40—High-molecular-weight compounds
    • C08G18/48—Polyethers
    • C08G18/4854—Polyethers containing oxyalkylene groups having four carbon atoms in the alkylene group
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
    • C08G18/66—Compounds of groups C08G18/42, C08G18/48, or C08G18/52
    • C08G18/6633—Compounds of group C08G18/42
    • C08G18/6659—Compounds of group C08G18/42 with compounds of group C08G18/34
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
    • C08G18/66—Compounds of groups C08G18/42, C08G18/48, or C08G18/52
    • C08G18/6666—Compounds of group C08G18/48 or C08G18/52
    • C08G18/6692—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/34
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
    • C08G18/75—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic
    • C08G18/758—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic containing two or more cycloaliphatic rings
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
    • C08G18/76—Polyisocyanates or polyisothiocyanates cyclic aromatic
    • C08G18/7614—Polyisocyanates or polyisothiocyanates cyclic aromatic containing only one aromatic ring
    • C08G18/7621—Polyisocyanates or polyisothiocyanates cyclic aromatic containing only one aromatic ring being toluene diisocyanate including isomer mixtures
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
    • C08G18/76—Polyisocyanates or polyisothiocyanates cyclic aromatic
    • C08G18/7657—Polyisocyanates or polyisothiocyanates cyclic aromatic containing two or more aromatic rings
    • C08G18/7664—Polyisocyanates or polyisothiocyanates cyclic aromatic containing two or more aromatic rings containing alkylene polyphenyl groups
    • C08G18/7671—Polyisocyanates or polyisothiocyanates cyclic aromatic containing two or more aromatic rings containing alkylene polyphenyl groups containing only one alkylene bisphenyl group
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
    • C08G18/78—Nitrogen
    • C08G18/79—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates
    • C08G18/791—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates containing isocyanurate groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
    • C08G18/78—Nitrogen
    • C08G18/79—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates
    • C08G18/797—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates containing carbodiimide and/or uretone-imine groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
    • C08G18/72—Polyisocyanates or polyisothiocyanates
    • C08G18/80—Masked polyisocyanates
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D06N3/0002—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate
    • D06N3/0015—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate using fibres of specified chemical or physical nature, e.g. natural silk
    • D06N3/0036—Polyester fibres
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D06N3/12—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof with macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. gelatine proteins
    • D06N3/14—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof with macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. gelatine proteins with polyurethanes
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D06N3/12—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof with macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. gelatine proteins
    • D06N3/14—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof with macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. gelatine proteins with polyurethanes
    • D06N3/147—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof with macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds, e.g. gelatine proteins with polyurethanes characterised by the isocyanates used

Definitions

  • the present invention relates to eco-conscious sheet materials produced by a process using no organic solvent and methods for producing such sheet materials, and more particularly to a sheet material having a good surface appearance and touch and a method for producing such a sheet material.
  • sheet materials including polyester fibrous substrates have high light fastness and thus have been increasingly used year by year in applications such as clothing, chair upholstery, and automotive interior materials.
  • Such sheet materials are produced, typically, by a combined process of impregnating a fibrous substrate with a solution of a polyurethane resin in an organic solvent, and then dipping the fibrous substrate impregnated with polyurethane resin into water or an aqueous organic solvent solution that does not dissolve the polyurethane resin to wet-coagulate the polyurethane resin.
  • a water-miscible organic solvent such as N,N-dimethylformamide
  • Organic solvents are generally very harmful to health and environment, and thus there is a strong need for methods for producing a sheet material using no organic solvent.
  • aqueous dispersed type polyurethane resins which are in the form of a water dispersion of a polyurethane resin containing hydrophilic groups in its molecule, in place of traditional organic-solvent-based polyurethane resins.
  • aqueous dispersed type polyurethane resins are coagulated by “moist-hot coagulation” in which the state of hydration of a polyurethane emulsion in water is destroyed mainly by heating, whereby polyurethane molecules in the emulsion are aggregated.
  • This method forms a nonporous polyurethane membrane with a highly dense structure.
  • the fibrous substrate and the polyurethane resin adhere closely to each other to firmly hold entangled portions of fibers, which results in a hard touch.
  • a fibrous substrate in the form of, for example, a sheet made of a fabric such as a nonwoven fabric is provided with an aqueous dispersed type polyurethane solution containing a blowing agent, and the blowing agent is blown by heating to make the polyurethane in the fibrous substrate porous (see Patent Document 1).
  • a technique has been proposed for providing a soft touch by impregnating a fibrous substrate with a polyurethane resin prepared from a polyol having low crystallinity.
  • the polyol used here is not a polyhexamethylene carbonate diol, which is a crystalline polyol solid at normal temperature, but a polycarbonate polyol made to be an amorphous polyol liquid at normal temperature by copolymerizing a carbonate polyol having a linear structure with a different carbon number (see Patent Document 2).
  • Patent Document 1 JP 2011-214210 A
  • Patent Document 2 JP 05-43647 A
  • making a polyurethane resin porous reduces the area of adhesion of fibers to the polyurethane resin to reduce the holding of entanglement points of the fibers, as a result of which a sheet material having a soft texture and a good touch can be produced, but its softness tends to be lower than in the case where an organic-solvent-based polyurethane is used.
  • the present inventors focused on molecular structures of polyurethane resins, which have not been focused in the related art, i.e., microphase-separated structures including hard segment domains (HS domains), which are composed mainly of urethane bonds and urea bonds, and soft segment domains (SS domains), which are composed mainly of polymeric polyols, and discovered such important properties that a polyurethane resin, when applied to a fibrous substrate, provides a good touch.
  • HS domains hard segment domains
  • SS domains soft segment domains
  • an embodiment of a sheet material of the present invention has the following structure (1) or (2):
  • a sheet material including a fibrous substrate made of microfibers and a hydrophilic-group-containing resin applied to the fibrous substrate, the hydrophilic-group-containing resin having a microphase-separated structure that satisfies Condition I:
  • a standard deviation of a mode of brightness distribution of areas of 0.2 ⁇ m 2 in the area of 1 ⁇ m 2 is from 0 to 10; or
  • a sheet material including a fibrous substrate made of microfibers and a hydrophilic-group-containing resin applied to the fibrous substrate, the hydrophilic-group-containing resin containing an aromatic polyisocyanate, the hydrophilic-group-containing resin being a polyurethane resin crosslinked with a crosslinking agent.
  • a method for producing a sheet material including impregnating a dispersion into a fibrous substrate made of microfibers, the dispersion containing a crosslinking agent and an aqueous dispersed type polyurethane resin containing an aromatic polyisocyanate, and coagulating the dispersion.
  • the crosslinking agent is preferably at least one of a polyisocyanate crosslinking agent and a carbodiimide crosslinking agent.
  • the hydrophilic-group-containing resin applied to the fibrous substrate is preferably an aqueous dispersed type polyurethane resin.
  • the fibrous substrate made of microfibers is preferably provided with an aqueous dispersed type polyurethane resin satisfying Conditions A to C.
  • the aqueous dispersed type polyurethane resin when in the form of a dry film, has a storage elastic modulus (E′) of 1 to 100 MPa.
  • the aqueous dispersed type polyurethane resin when in the form of a dry film, has a loss elastic modulus (E′′) of 0.1 to 20 MPa.
  • the aqueous dispersed type polyurethane resin when in the form of a dry film, has a tan ⁇ of 0.01 to 0.30.
  • the crosslinking agent is preferably at least one of a polyisocyanate crosslinking agent and a carbodiimide crosslinking agent.
  • the method for producing the sheet material of the present invention preferably further includes heating the impregnated and coagulated dispersion at 80° C. to 200° C. after the dispersion is impregnated and coagulated.
  • the method for producing the sheet material of the present invention preferably further includes applying a highly saponified polyvinyl alcohol having a degree of saponification of 95% to 100% to the fibrous substrate made of microfibers before the dispersion is impregnated and coagulated.
  • the present invention provides a sheet material that is produced through an eco-conscious production process using an aqueous dispersed type resin such as aqueous dispersed type polyurethane and yet has such a uniform nap length that is comparable to those of man-made leathers produced using organic-solvent-based polyurethanes, an elegant surface appearance with very fine fibers, and such a good touch that is soft and excellent in wrinkle recovery.
  • the sheet material of the present invention achieves a touch without a paper-like feel but with a highly rubberlike feel that is comparable to those of man-made leathers produced using organic-solvent-based polyurethanes, which could not be achieved by the conventional use of an aqueous dispersed type polyurethane.
  • FIG. 1 is an AFM micrograph of the microphase-separated structure of the polyurethane extracted from the man-made leather obtained in Example 8 of the present invention
  • FIG. 2 is an AFM micrograph of the microphase-separated structure of the polyurethane extracted from the man-made leather obtained in Example 15 of the present invention.
  • FIG. 3 is an AFM micrograph of the microphase-separated structure of the polyurethane extracted from the man-made leather obtained in Comparative Example 2.
  • the sheet material of an embodiment of the present invention includes a fibrous substrate (e.g., a nonwoven fabric) made of microfibers, and a hydrophilic-group-containing resin (e.g., an aqueous dispersed type polyurethane resin) acting as a binder applied to the fibrous substrate.
  • a fibrous substrate e.g., a nonwoven fabric
  • a hydrophilic-group-containing resin e.g., an aqueous dispersed type polyurethane resin
  • the fibers constituting the fibrous substrate include fibers made of polyesters such as polyethylene terephthalate, polybutylene terephthalate, polytrimethylene terephthalate, and polylactide; polyamides such as 6-nylon and 66-nylon; and melt-spinnable thermoplastic resins such as acryl, polyethylene, polypropylene, and thermoplastic cellulose.
  • polyester fibers are suitable for use in terms of strength, dimensional stability, and light fastness.
  • the fibrous substrate may be made of mixed fibers of different materials.
  • the cross-sectional shape of the microfibers may be circular.
  • microfibers having oval, polygonal (e.g., flat, triangular), or modified (e.g., fan-shaped, cross-shaped) cross-sections may be used.
  • the average filament diameter of the microfibers constituting the fibrous substrate is preferably 0.1 to 7 ⁇ m.
  • the average filament diameter is preferably 7 ⁇ m or less, more preferably 6 ⁇ m or less, and still more preferably 5 ⁇ m or less.
  • An average filament diameter in this range provides a sheet material with excellent softness and raising quality.
  • the average filament diameter is preferably 0.3 ⁇ m or more, more preferably 0.7 ⁇ m or more, and still more preferably 1 ⁇ m or more.
  • An average filament diameter in this range provides excellent post-dyeing color-developing properties and excellent dispersibility of bundled fibers in raising, such as buffing with sandpaper or other abrasive material.
  • the fibrous substrate made of microfibers may be in the form of a fabric such as a woven, knitted, or nonwoven fabric.
  • a nonwoven fabric is suitable for use because it provides a sheet material that has a good surface appearance when napped.
  • the nonwoven fabric may be a short-fiber nonwoven fabric or a long-fiber nonwoven fabric but is preferably a short-fiber nonwoven fabric in terms of a touch and appearance.
  • the fiber length of short fibers in the short-fiber nonwoven fabric is preferably 25 mm to 90 mm, more preferably 35 mm to 75 mm.
  • a fiber length of 25 mm or more allows for entanglement to provide a sheet material with high abrasion resistance.
  • a fiber length of 90 mm or less provides a sheet material with a more excellent touch and appearance.
  • the nonwoven fabric When the fibrous substrate made of microfibers is a nonwoven fabric, the nonwoven fabric preferably has a structure in which bundles of microfibers (fiber bundles) are entangled with each other. The entanglement of bundled microfibers provides a sheet material with increased strength.
  • the nonwoven fabric having such a structure can be produced by entangling microfiber-developing fibers with each other in advance and then developing microfibers.
  • a woven fabric or knitted fabric can be inserted into the nonwoven fabric in order, for example, to increase its strength.
  • the average filament diameter of fibers constituting such a woven fabric or knitted fabric is preferably about 0.1 to 10 ⁇ m.
  • hydrophilic-group-containing resin used as a binder in the sheet material of the present invention examples include aqueous dispersed type silicone resins, aqueous dispersed type acrylic resins, aqueous dispersed type urethane resins, and copolymers thereof. Of these, aqueous dispersed type polyurethane resins are suitable for use in terms of a touch.
  • Preferred polyurethane resins are resins produced by the reaction of a polymeric polyol preferably having a number average molecular weight of 500 to 5,000, an organic polyisocyanate, and a chain extender.
  • a compound containing an active hydrogen component having a hydrophilic group is used in combination.
  • polyether polyols include polyols produced by addition polymerization of, for example, ethylene oxide, propylene oxide, butylene oxide, styrene oxide, tetrahydrofuran, epichlorohydrin, and cyclohexylene monomers using a polyhydric alcohol or a polyamine as an initiator; and polyols produced by ring opening polymerization of these monomers in the presence of a catalyst such as a proton acid, a Lewis acid, or a cation catalyst.
  • a catalyst such as a proton acid, a Lewis acid, or a cation catalyst.
  • Specific examples include polyethylene glycol, polypropylene glycol, polytetramethylene glycol, and copolyols thereof.
  • polyester polyols examples include polyester polyols produced by condensing one or more low-molecular-weight polyols and polybasic acids and polyester polyols produced by opening polymerization of lactones.
  • low-molecular-weight polyols include linear alkylene glycols such as ethylene glycol, 1,3-propylene glycol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, 1,9-nonanediol, and 1,10-decanediol; branched alkylene glycols such as neopentyl glycol, 3-methyl-1,5-pentanediol, 2,4-diethyl-1,5-pentanediol, and 2-methyl-1,8-octanediol; alicyclic diols such as 1,4-cyclohexanediol; and aromatic dihydric alcohols such as 1,4-bis( ⁇ -hydroxyethoxy)benzene. These may be used alone or in combination. Adducts produced
  • polybasic acids examples include succinic acid, maleic acid, adipic acid, glutaric acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, dodecanedicarboxylic acid, phthalic acid, isophthalic acid, terephthalic acid, and hexahydroisophthalic acid. These may be used alone or in combination.
  • polylactone polyols examples include polyols produced by ring opening polymerization of lactones such as ⁇ -butyrolactone, ⁇ -valerolactone, and ⁇ -caprolactone alone or in combination using a polyhydric alcohol as an initiator.
  • polycarbonate polyols examples include compounds produced by the reaction between polyols and carbonate compounds such as dialkyl carbonates and diaryl carbonates.
  • polyols for use as starting materials of polycarbonate polyols include polyols listed as starting materials of polyester polyols.
  • dialkyl carbonates include dimethyl carbonate and diethyl carbonate, and examples of diaryl carbonates include diphenyl carbonate.
  • a non-limiting example of the component for incorporating a hydrophilic group into the resin is a hydrophilic-group-containing active hydrogen component.
  • the hydrophilic-group-containing active hydrogen component include compounds containing active hydrogen and at least one of a nonionic group, an anionic group, and a cationic group.
  • the compound having a nonionic group and active hydrogen include compounds containing two or more active hydrogen components or two or more isocyanate groups and having, for example, a pendant polyoxyethylene glycol group with a molecular weight of 250 to 9,000, and triols such as trimethylolpropane and trimethylolbutane.
  • Examples of the compound having an anionic group and active hydrogen include carboxyl-group-containing compounds such as 2,2-dimethylolpropionic acid, 2,2-dimethylol butane acid, and 2,2-dimethylolvaleric acid, and derivatives thereof; sulfo-group-containing compounds such as 1,3-phenylenediamine-4,6-disulfonic acid and 3-(2,3-dihydroxypropoxy)-1-propanesulfonic acid, and derivatives thereof; and salts of these compounds obtained by neutralization with a neutralizer.
  • carboxyl-group-containing compounds such as 2,2-dimethylolpropionic acid, 2,2-dimethylol butane acid, and 2,2-dimethylolvaleric acid, and derivatives thereof
  • sulfo-group-containing compounds such as 1,3-phenylenediamine-4,6-disulfonic acid and 3-(2,3-dihydroxypropoxy)-1-propanesulfonic acid, and derivatives thereof
  • Examples of the compound containing a cationic group and active hydrogen include tertiary-amino-group-containing compounds such as 3-dimethylaminopropanol, N-methyldiethanolamine, and N-propyldiethanolamine, and derivatives thereof.
  • hydrophilic-group-containing active hydrogen components listed above can be used in the form of salts obtained by neutralization with a neutralizer.
  • the hydrophilic-group-containing active hydrogen component in polyurethane molecules is preferably 2,2-dimethylolpropionic acid, 2,2-dimethylolbutanoic acid, or a neutralized salt thereof.
  • hydrophilic-group-containing active hydrogen components in particular, hydroxyl groups, sulfo groups, and carboxyl groups
  • a crosslinking agent described below in combination may form a three-dimensional crosslinked structure in the polyurethane molecules to improve physical properties.
  • chain extenders include compounds conventionally used to produce polyurethane resins. Particularly preferred are low-molecular-weight compounds with molecular weights of 600 or less having two or more active hydrogen atoms reactive with isocyanate groups in their molecules. Specific examples include diols such as ethylene glycol, propylene glycol, 1,4-butanediol, 1,6-hexanediol, 3-methyl-1,5-pentanediol, neopentyl glycol, 1,4-cyclohexanediol, and xylylene diglycol; triols such as trimethylolpropane and trimethylolbutane; diamines such as hydrazine, ethylenediamine, isophoronediamine, piperazine, 4,4′-methylenedianiline, tolylenediamine, xylylenediamine, hexamethylenediamine, and 4,4′-dicyclohexylmethanediamine; tri
  • organic polyisocyanates examples include aliphatic diisocyanates such as hexamethylene diisocyanate; alicyclic diisocyanates such as isophorone diisocyanate (hereinafter also referred to as IPDI for short), hydrogenated xylylene diisocyanate, and dicyclohexylmethane diisocyanate (hereinafter also referred to as hydrogenated MDI for short); aromatic/aliphatic diisocyanates such as xylylene diisocyanate (hereinafter also referred to as XDI for short) and tetramethyl-m-xylylene diisocyanate; and aromatic diisocyanates such as tolylene diisocyanate (hereinafter also referred to as TDI for short), 4,4′-diphenylmethane diisocyanate (hereinafter also referred to as MDI for short), tolidine diisocyanate, and naphthalene diisocyanate (hereinafter
  • polystyrene resin In producing a polyurethane resin, the polyisocyanates listed above can be used alone in combination.
  • aromatic polyisocyanates such as TDI, MDI, NDI, and XDI, are more suitable for use because the resonance of ⁇ electrons in molecules facilitates the aggregation of HS domains to form a well-defined microphase-separated structure.
  • Introducing sulfonic groups, carboxyl groups, hydroxyl groups, or primary or secondary amino groups into the polyurethane resin for use in the present invention and incorporating crosslinking agents reactive with these functional groups into a dispersion of the polyurethane can increase the molecular weight and crosslink density of the resin after reaction to enhance durability, weather resistance, heat resistance, and wet strength retention.
  • Crosslinking agents having in their molecules two or more reactive groups reactive with a reactive group introduced into the polyurethane resin can be used.
  • Specific examples include polyisocyanate crosslinking agents such as water-soluble isocyanate compounds and blocked isocyanate compounds, melamine crosslinking agents, oxazoline crosslinking agents, carbodiimide crosslinking agents, aziridine crosslinking agents, epoxy crosslinking agents, and hydrazine crosslinking agents. These crosslinking agents may be used alone or in combination.
  • Water-soluble isocyanate compounds have two or more isocyanate groups in their molecules, and examples include compounds containing the organic polyisocyanates listed above. Examples of commercially available products thereof include “Bayhydur” (registered trademark) series and “Desmodur” (registered trademark) series available from Bayer-Material Science.
  • Block isocyanate compounds have two or more blocked isocyanate groups in their molecules.
  • the term “blocked isocyanate group” refers to a group obtained by blocking any one of the organic polyisocyanate compounds listed above with a blocking agent, such as an alcohol, amine, phenol, imine, mercaptan, pyrazole, oxime, or active methylene. Examples of commercially available products thereof include “Erastron” (registered trademark) series available from Dai-ichi Kogyo Seiyaku, “Duranate” (registered trademark) series available from ASAHI KASEI CHEMICALS, and “TAKENATE” (registered trademark) series available from Mitsui Chemicals, Inc.
  • Examples of melamine crosslinking agents include compounds having two or more methylol groups or methoxymethylol groups in their molecules.
  • Examples of commercially available products thereof include “U-VAN” (registered trademark) series available from Mitsui Chemicals, Inc., “Cymel” (registered trademark) series available from Nihon Cytec, Inc., and “Sumimal” (registered trademark) series available from Sumitomo Chemical Co., Ltd.
  • Examples of oxazoline crosslinking agents include compounds having two or more oxazoline groups (an oxazoline backbone) in their molecules.
  • Examples of commercially available products thereof include “EPOCROS” (registered trademark) series available from Nippon Shokubai Co., Ltd.
  • Examples of carbodiimide crosslinking agents include compounds having two or more carbodiimide groups in their molecules.
  • Examples of commercially available products thereof include “Carbodilite” (registered trademark) series available from Nisshinbo Industries, Inc.
  • Examples of aziridine crosslinking agents include compounds having two or more aziridinyl groups in their molecules.
  • Examples of hydrazine crosslinking agents include hydrazine and compounds having two or more hydrazine groups (a hydrazine backbone) in their molecules.
  • Preferred functional groups that the polyurethane resin should have are hydroxyl groups and/or carboxyl groups and/or sulfonic groups, and preferred crosslinking agents are polyisocyanate crosslinking agents and carbodiimide compounds.
  • preferred crosslinking agents are polyisocyanate crosslinking agents and carbodiimide compounds.
  • the combined use of a carbodiimide compound and a polyisocyanate crosslinking agent can further strengthen the crosslinked structure of the polyurethane resin and improve moist-heat resistance while maintaining softness.
  • Aqueous dispersed type polyurethane resins typically contain hydrophilic groups in their molecular structures and thus have higher affinity for water molecules than traditional organic-solvent-based polyurethane resins. Thus, in a wet environment, the aqueous dispersed type polyurethane resins tend to swell and loosen their molecular structures to lose their high physical properties that could have been maintained in a dry environment. However, adding the crosslinking agents listed above can improve moist-heat resistance to increase the wet tensile strength of a sheet.
  • Carbodiimide crosslinking agents have high crosslinking reactivity even at low temperatures of 100° C. or lower and thus are suitable for use in terms of productivity.
  • Isocyanate compounds and/or blocked isocyanate compounds react mainly with hydroxyl groups and, at a high temperature, in particular, 120° C. to 200° C., preferably 140° C. to 200° C., become more reactive with urethane bonds and/or urea bonds constituting HS domains of a polyurethane resin to form allophanate bonds and/or biuret bonds. These bonds provide a stronger crosslinked structure to provide the polyurethane resin with a well-defined microphase-separated structure.
  • the polyurethane resin of the present invention in the form of a film preferably has a storage elastic modulus E′ at 20° C. of 1 to 100 MPa, more preferably 2 to 50 MPa, in terms of softness and impact resilience.
  • the polyurethane resin film preferably has a loss elastic modulus of 0.1 MPa to 20 MPa, more preferably 0.5 MPa to 12 MPa, and preferably has a tans of 0.01 to 0.4, more preferably 0.02 to 0.35.
  • the values of storage elastic modulus E′ and tan ⁇ in the present invention were determined using a polyurethane resin film having a thickness of 200 ⁇ m with a DMA7100 storage elastic modulus measurement apparatus (Hitachi High-Tech Science Corporation) at a frequency of 12 Hz. Tan ⁇ is represented by E′′/E′ (E′′ is a loss elastic modulus).
  • E′ represents elastic properties of a polyurethane resin. An excessively small E′ results in a sheet having poor wrinkle recovery, and an excessively large E′ results in a sheet having a hard touch.
  • E′′ is a loss elastic modulus, which represents viscous properties. Similarly to E′, an excessively small E′′ results in a sheet having poor wrinkle recovery, and an excessively large E′′ results in a sheet having a hard touch.
  • Tan ⁇ is a ratio of the viscous properties to the elastic properties of a polyurethane resin.
  • the sheet material of the present invention preferably has a density of 0.2 to 0.7 g/cm 3 .
  • the density is more preferably 0.2 g/cm 3 or more, still more preferably 0.25 g/cm 3 or more. A density in this range leads to a fine surface appearance and develops a luxurious appearance.
  • the density of the sheet material is preferably 0.7 g/cm 3 or less, more preferably 0.6 g/cm 3 or less. A density in this range prevents the sheet material from having a hard touch.
  • the proportion of a polyurethane resin in the sheet material of the present invention is preferably 10 to 80% by mass. Not less than 10% by mass, more preferably not less than 15% by mass, of a polyurethane resin provides sheet strength and also prevents fibers from falling off. Not more than 80% by mass, more preferably not more than 70% by mass, of a polyurethane resin prevents a hard touch and provides good raising quality.
  • the sheet material provided according to aspects of the present invention is a sheet material provided with a uniform appearance, elegant surface appearance, and good touch and durability by impregnating a fibrous substrate with a hydrophilic-group-containing resin (a polyurethane resin) having specific properties.
  • a hydrophilic-group-containing resin a polyurethane resin
  • the present invention aims to achieve the object described above, and the sheet material of an embodiment of the present invention is a sheet material including a fibrous substrate made of microfibers and a hydrophilic-group-containing resin applied to the fibrous substrate, the hydrophilic-group-containing resin having a microphase-separated structure that satisfies Condition I.
  • a standard deviation of a mode of brightness distribution of areas of 0.2 ⁇ m 2 in the area of 1 ⁇ m 2 is from 0 to 10.
  • the standard deviation is preferably 6 or less.
  • Polyurethane resins satisfying the above condition have a structure in which HS domains and SS domains are distinctly separated, specifically, a microphase-separated structure in which spherical HS domains having a size of 100 nm or smaller are dispersed in uniform SS domains, and have high rubber elasticity.
  • the hydrophilic-group-containing resin is a polyurethane resin.
  • the fibrous substrate for use in the present invention is preferably a fabric such as a woven, knitted, or nonwoven fabric.
  • a nonwoven fabric is suitable for use because it provides a sheet material that has a good surface appearance when napped.
  • the fibrous substrate of the present invention may optionally be a laminate of these fabrics such as a woven, knitted, and nonwoven fabric.
  • the nonwoven fabric for use in the present invention may be a short-fiber nonwoven fabric or a long-fiber nonwoven fabric but is preferably a short-fiber nonwoven fabric to provide a surface appearance having a uniform nap length.
  • the fiber length of short fibers in the short-fiber nonwoven fabric is preferably 25 mm to 90 mm, more preferably 35 mm to 75 mm.
  • a fiber length of 25 mm or more allows for entanglement to provide a sheet material with high abrasion resistance.
  • a fiber length of 90 mm or less provides a sheet material with more excellent appearance.
  • the fibers constituting the fibrous substrate include fibers made of polyesters such as polyethylene terephthalate, polybutylene terephthalate, polytrimethylene terephthalate, and polylactide; polyamides such as 6-nylon and 66-nylon; and melt-spinnable thermoplastic resins such as acryl, polyethylene, polypropylene, and thermoplastic cellulose.
  • polyester fibers are suitable for use in terms of strength, dimensional stability, and light fastness.
  • the fibrous substrate may be made of mixed fibers of different materials.
  • the cross-sectional shape of the fiber for use in the present invention may be circular.
  • microfibers having oval, polygonal (e.g., flat, triangular), or modified (e.g., fan-shaped, cross-shaped) cross-sections may be used.
  • the average fiber diameter of the fibers constituting the fibrous substrate is preferably 0.1 to 7 ⁇ m, more preferably 0.3 to 5 ⁇ m. An average fiber diameter of 7 ⁇ m or less softens the texture of the fibrous substrate. An average fiber diameter of 0.1 ⁇ m or more provides more excellent post-dyeing color-developing properties.
  • a woven fabric or knitted fabric when the fibrous substrate is a nonwoven fabric, a woven fabric or knitted fabric can be combined with the nonwoven fabric for an increase in strength and other purposes.
  • the woven fabric or knitted fabric may be laminated on the nonwoven fabric or inserted into the nonwoven fabric.
  • using a woven fabric is preferred because it can improve shape stability and strength.
  • single yarns (warp and weft) of the woven fabric or knitted fabric include single yarns made of synthetic fibers, such as polyester fibers and polyamide fibers. In terms of color fastness, preferred is the same material as microfibers constituting the fabric such as a nonwoven fabric in the end.
  • Examples of the form of such single yarns include filament yarns and spun yarns, and hard twist yarns of such yarns are suitable for use. Filament yarns are more suitable for use because spun yarns may give rise to falling off of surface fuzz.
  • the number of twists is preferably 1,000 T/m to 4,000 T/m, more preferably 1,500 T/m to 3,500 T/m. Twists in this preferred range causes little breakage of filaments of the hard twist yarn during needle punching, no reduction in physical properties of products, and no increase in exposure of filaments on a product surface. In addition, twists in this preferred range causes no excessive hardening of the hard twist yarn of the woven fabric or knitted fabric, and thus no hardened touch.
  • microfiber-developing fibers for the fibrous substrate.
  • microfiber-developing fibers for the fibrous substrate Through the use of microfiber-developing fibers for the fibrous substrate, the entanglement of microfiber bundles described above can be stably created.
  • the nonwoven fabric When the fibrous substrate is a nonwoven fabric, the nonwoven fabric preferably has a structure in which bundles of microfibers (fiber bundles) are entangled with each other. The entanglement of bundled microfibers provides a sheet material with increased strength.
  • the nonwoven fabric having such a structure can be produced by entangling microfiber-developing fibers with each other in advance and then developing microfibers.
  • microfiber-developing fibers examples include sea-island type conjugated fibers, which are composed of a sea component and an island component made of thermoplastic resins having different solvent solubilities, which sea component is to be dissolved away using, for example, a solvent to leave the island component in the form of microfibers; and peel type conjugated fibers, which are composed of two thermoplastic resins disposed alternately in a radial or layered manner in a fiber cross-section, which two components are to be peeled apart to form microfibers.
  • sea-island type conjugated fibers which are composed of a sea component and an island component made of thermoplastic resins having different solvent solubilities, which sea component is to be dissolved away using, for example, a solvent to leave the island component in the form of microfibers
  • peel type conjugated fibers which are composed of two thermoplastic resins disposed alternately in a radial or layered manner in a fiber cross-section, which two components are to be peeled apart to form microfibers.
  • sea-island type conjugated fibers are preferred because appropriate space can be provided between the island component portions, i.e., microfibers by removing the sea component.
  • sea-island type conjugated fibers examples include sea-island type conjugated fibers produced by spinning alternately arranged two components, a sea component and an island component, using a sea-island type conjugating spinneret; and mix-spun fibers produced by spinning a mixture of two components, a sea component and an island component.
  • Sea-island type conjugated fibers are preferred because they develop into microfibers having a uniform fineness and microfibers having so sufficient length that contributes to the strength of sheet materials.
  • sea component of the sea-island type conjugated fibers examples include polyethylenes, polypropylenes, polystyrenes, copolyesters of, for example, sodium sulfoisophthalate and polyethylene glycol, polylactic acids, and polyvinyl alcohols.
  • the mass ratio of island fibers to the sea-island type conjugated fiber is preferably 0.2 to 0.9, more preferably 0.3 to 0.8.
  • a mass ratio of the island component to the sea component of 0.2 or greater leads to a reduced removal of the sea component, leading to higher productivity.
  • a mass ratio of 0.9 or less leads to improved dispersibility of island fibers and prevents the island component portions from uniting with each other.
  • the number of islands can be appropriately controlled by spinneret design.
  • the major axis of filaments is preferably 5 to 80 ⁇ m, more preferably 10 to 50 ⁇ m.
  • a filament fineness in this preferred range prevents excessively weak fibers, causing little filament breakage during treatments such as needle punching described below, and, at the same time, enables efficient entanglement in treatments such as needle punching.
  • the nonwoven fabric for use as a fibrous substrate in the present invention can be produced, for example, by entanglement of fiber webs by needle punching or water-jet punching, spunbonding, meltblowing, and papermaking.
  • methods involving a treatment such as needle punching or water-jet punching are suitable for use to create the microfiber bundle configuration described above.
  • needle punching and water jet punching are suitable for use in terms of the entanglement properties of fibers.
  • needle punching which is not restricted by sheet thickness and enables orientation of fibers in the vertical direction of the fibrous substrate, is suitable for use.
  • needles used for needle punching each have one to nine barbs. Having at least one barb enables efficient entanglement of fibers. Having up to nine barbs prevents or minimizes fiber damage and leaves no needle holes, which might result in a product having a poor appearance, on the fibrous substrate.
  • the nonwoven fabric is preferably preliminarily entangled in order to minimize the wrinkling during the integration of the nonwoven fabric and the woven fabric or knitted fabric by needle punching.
  • Such preliminary entanglement by needle punching is effective when carried out at a punch density of 20 punches/cm 2 or more.
  • the preliminary entanglement is preferably carried out at a punch density of 100 punches/cm 2 or more, more preferably 300 punches/cm 2 to 1,300 punches/cm 2 .
  • a punch density in the preliminary entanglement in the above preferred range is less likely to cause wrinkles in the woven fabric or knitted fabric even if there are some variations in width, resulting in a flat fibrous substrate.
  • the punch density in this range also prevents excessive entanglement of the nonwoven fabric itself to secure room for movement sufficient for entanglement with fibers constituting the woven fabric or knitted fabric, as a result of which an integral structure in which the nonwoven fabric and the woven fabric or knitted fabric are firmly entangled can be advantageously achieved.
  • the punch density is preferably in the range of 300 punches/cm 2 to 6,000 punches/cm 2 , more preferably 1,000 punches/cm 2 to 3,000 punches/cm 2 , regardless of the presence of the woven fabric or knitted fabric.
  • the nonwoven fabric and the woven fabric or knitted fabric may be entangled to form a fibrous substrate in such a manner that fibers are entangled with each other by needle punching with the woven fabric or knitted fabric laminated on one or both surfaces of the nonwoven fabric or with the woven fabric or knitted fabric sandwiched between a plurality of nonwoven fabrics.
  • Water jet punching is preferably carried out using water in the form of a columnar stream. Specifically, it is preferable to squirt water from a nozzle with a diameter of 0.05 to 1.0 mm under a pressure of 1 to 60 MPa.
  • the nonwoven fabric made of microfiber-developing fibers that has been subjected to needle punching or water jet punching preferably has an apparent density of 0.130 to 0.450 g/cm 3 , more preferably 0.150 to 0.300 g/cm 3 .
  • An apparent density of 0.130 g/cm 3 or more provides a man-made leather with sufficient shape stability and dimensional stability.
  • An apparent density of 0.450 g/cm 3 or less secures a space sufficient for providing an elastic polymer.
  • the fibrous substrate preferably has a thickness of 0.3 mm to 6.0 mm, more preferably 1.0 mm to 3.0 mm.
  • a thickness of the fibrous substrate in this preferred range provides a sheet with high shape stability and, in addition, is less likely to cause needles to break during needle punching.
  • the nonwoven fabric thus obtained made of microfiber-developing fibers is preferably shrunk by dry heat or wet heat, or both, for further densification.
  • dissolution for removing a sea component of the fibers may be carried out before or/and after a dispersion containing an aqueous dispersed type polyurethane resin is applied to a fibrous substrate. Dissolution before application of a dispersion tends to form a structure in which the polyurethane resin is in direct contact with microfibers. This structure enables the microfibers to be firmly held, thus providing a sheet material with good abrasion resistance.
  • an inhibitor for inhibiting the adhesion of the fibrous substrate to polyurethane such as a cellulose derivative or a polyvinyl alcohol (hereinafter also referred to as PVA for short), may be applied.
  • PVA polyvinyl alcohol
  • the inhibitor may be applied before or after the dissolution of the fibers having a sea-island structure.
  • Application before the dissolution increases the shape retention of the fibrous substrate, which enables stable processing into a thin sheet even if the sheet has a low tensile strength due to a reduced fiber unit weight.
  • the application before the dissolution also increases the thickness retention of the fibrous substrate during the dissolution process and, therefore, inhibits densification of the fibrous substrate.
  • the timing of the application is preferably selected as appropriate depending on the intended use.
  • suitable inhibitors include PVAs, which effectively reinforce the fibrous substrate and are less soluble in water.
  • PVAs highly saponified PVAs, which are even less soluble in water, are more preferred because these inhibitors are less soluble during the application of a PU resin composition and further inhibit the adhesion of microfibers to polyurethane.
  • the degree of saponification of a highly saponified PVA is preferably 95% to 100%, more preferably 98% to 100%.
  • a degree of saponification of 95% or more inhibits dissolution during the application of a polyurethane resin composition.
  • the degree of polymerization is preferably 500 to 3,500, more preferably 500 to 2,000.
  • a degree of polymerization of not less than 500 inhibits dissolution of the highly saponified PVA during the application of a polyurethane resin composition.
  • a degree of polymerization of not more than 3,500 prevents an excessive increase in viscosity of a solution of the highly saponified PVA, which allows for stable application of the highly saponified PVA to the fibrous substrate.
  • the amount of PVA applied is preferably 0.1% by mass to 80% by mass, more preferably 5% by mass to 60% by mass, based on the fibrous substrate that will remain in a product.
  • Applying a highly saponified PVA in an amount of 0.1% by mass or more increases the shape stability during the dissolution process and prevents inadhesion of microfibers to polyurethane.
  • Applying a highly saponified PVA in an amount of 80% by mass or less prevents an excessive decrease in adhesion of microfibers to polyurethane and provides uniform napped fibers, leading to a product having a uniform surface appearance.
  • the inhibitor is preferably applied in such a manner that the fibrous substrate is impregnated with an aqueous solution of the inhibitor and dried by heating.
  • the drying is preferably carried out at 80° C. to 180° C., more preferably 110° C. to 160° C. Drying at a temperature in this preferred range does not require an excessively long time and, in addition, prevents the inhibitor from being insolubilized to be incapable of being dissolved away later.
  • the drying is preferably carried out for 1 to 30 minutes in terms of processability.
  • the inhibitor is preferably dissolved away by dipping the fibrous substrate provided with the inhibitor into steam at 100° C. or higher and hot water at 60° C. to 100° C. and, optionally, nipping the fibrous substrate, for example, with a mangle.
  • the dissolution can be carried out by dipping the fibrous substrate containing sea-island type conjugated fibers into a solution and nipping the fibrous substrate.
  • the solvent for dissolving the sea component include organic solvents such as toluene and trichloroethylene (in the case where the sea component is polyethylene, polypropylene, or polystyrene), alkaline solutions such as an aqueous solution of sodium hydroxide (in the case where the sea component is a copolyester or polylactic acid), and hot water (in the case where the sea component is polyvinyl alcohol).
  • a polyurethane resin When a polyurethane resin is dispersed into an aqueous medium in the form of particles, in terms of dispersion stability, it is preferable to use, as a component of the polyurethane resin, the above-described hydrophilic-group-containing active hydrogen component, more preferably, a neutralized salt thereof.
  • neutralizers used for the neutralized salt of the compound having hydrophilic groups and active hydrogen include amine compounds such as trimethylamine, triethylamine, and triethanolamine, and hydroxides such as sodium hydroxide and potassium hydroxide.
  • the neutralizer used for the hydrophilic-group-containing active hydrogen component may be added at any timing, for example, before or after polyurethane polymerization or before or after dispersion into an aqueous medium.
  • the component is preferably added before or during dispersion into an aqueous medium.
  • the amount of hydrophilic-group-containing active hydrogen component and/or salt thereof based on the mass of the polyurethane resin is preferably 0.005 to 30% by mass, more preferably 0.01 to 15% by mass, in terms of dispersion stability and water resistance of the polyurethane resin.
  • one or more surfactants that serve as external emulsifiers for the polyurethane resin may be used to disperse the polyurethane resin into an aqueous medium.
  • surfactants examples include nonionic surfactants, anionic surfactants, cationic surfactants, and amphoteric surfactants. These surfactants may be used alone or in combination.
  • nonionic surfactants examples include alkylene oxide adduct type nonionic surfactants, such as polyoxyethylene nonylphenyl ether, polyoxyethylene dinonylphenyl ether, polyoxyethylene lauryl ether, and polyoxyethylene stearyl ether; and polyhydric alcohol type nonionic surfactants, such as glycerol monostearate.
  • anionic surfactants include carboxylic acid salts, sulfuric acid ester salts, sulfonic acid salts, and phosphoric acid ester salts, such as sodium laurate, sodium lauryl sulfate, ammonium lauryl sulfate, dodecyl sodium benzenesulfonate, and higher alcohol sodium diphosphate.
  • cationic surfactants include quarternary ammonium salts, such as distearyl dimethyl ammonium chloride.
  • amphoteric surfactants include lauryl amino methyl propionate, lauryl dimethyl betaine, and coconut oil fatty acid amide propyl dimethyl amino betaine acetate.
  • the dispersion containing a polyurethane resin for use in the present invention can be produced by any conventional method for producing a polyurethane dispersion.
  • Examples include a method including reacting the above-described polyisocyanate, polyol, chain extender, and/or hydrophilic-group-containing polyol, and emulsifying the resulting liquid polymer in water in the presence of an emulsifier; a method including reacting the above-described polyisocyanate, polyol, and/or chain extender, and/or hydrophilic-group-containing polyol to produce a prepolymer having isocyanate end groups, and emulsifying the prepolymer in water in the presence of an emulsifier, while (or followed by) adding a chain extender to complete extension reaction; and a method including reacting the above-described polyisocyanate, polyol, and/or chain extender, and/or hydrophilic-group-containing polyol, and then emulsifying
  • the polymerization of the prepolymer and the polymerization without forming a prepolymer may be carried out in the absence of a solvent or in the presence of an organic solvent, such as methyl ethyl ketone, toluene, or acetone.
  • the above-described synthesized dispersion of an aqueous dispersed type polyurethane resin is, for example, impregnated into a fibrous substrate to apply the polyurethane resin to the fibrous substrate.
  • the fibrous substrate is then coagulated and solidified by heat drying.
  • the dispersion applied to the fibrous substrate preferably contains a heat-sensitive coagulant. This is because the coagulant prevents or reduces migration of the polyurethane resin during polyurethane coagulation, which allows the fibrous substrate to be uniformly impregnated with the polyurethane resin.
  • heat-sensitive coagulants examples include inorganic salts such as sodium sulfate, magnesium sulfate, calcium sulfate, calcium chloride, magnesium chloride, and calcium chloride; sodium persulfate; potassium persulfate; and ammonium salts such as ammonium persulfate and ammonium sulfate.
  • the heat coagulation temperature of the dispersion is preferably 40 to 90° C., more preferably 50 to 80° C., in terms of storage stability and a touch of processed fiber products.
  • additives include pigments such as carbon black; antioxidants (e.g., hindered phenol, sulfur, and phosphorus antioxidants); UV absorbers (e.g., benzotriazole, triazine, benzophenone, and benzoate UV absorbers); weathering stabilizers such as hindered amine light stabilizers; softening water-repellents (e.g., silicone compounds such as polysiloxane and modified silicone oil, and fluorine compounds such as fluoroalkyl acrylate polymers); wetting agents (e.g., ethylene glycol, diethylene glycol, propylene glycol, and glycerol); antifoaming agents (e.g., octyl alcohol, sorbitan monooleate, polydimethylsiloxane, polyether-modified silicone, and fluorine-modified silicone); fill
  • inorganic blowing agents including sodium hydrogen carbonate (e.g., “Cellmic 266” [registered trademark] available from Sankyo Kasei Co., Ltd.); 2,2′-azobis [2-methyl-N-(2-hydroxyethyl)propionamide] (e.g., “VA-086” available from Wako Pure Chemical Industries, Ltd.); viscosity modifiers; plasticizers (e.g., phthalic acid esters and adipic acid esters); and release agents (e.g., wax, metallic soap, and mixed release agents).
  • sodium hydrogen carbonate e.g., “Cellmic 266” [registered trademark] available from Sankyo Kasei Co., Ltd.
  • 2,2′-azobis [2-methyl-N-(2-hydroxyethyl)propionamide] e.g., “VA-086” available from Wako Pure Chemical Industries, Ltd.
  • viscosity modifiers e.g., plasticizers (e.g., phthal
  • the dispersion when impregnated, can be coagulated, for example, by means of dry heating, wet heating, hot water, acids, salts, and infrared coagulation.
  • the coagulation is preferably heated (cured) in order to promote the fusion of the aqueous dispersed type polyurethane emulsion to normalize the molecular structure of the polyurethane resin, thereby improving moist-heat resistance.
  • the curing can be carried out successively to the coagulation after the aqueous dispersed type polyurethane dispersion is impregnated, or can be carried out separately after the aqueous dispersed type polyurethane dispersion is impregnated and coagulated.
  • the heating is preferably carried out at 80° C. to 200° C., more preferably at 120° C. to 190° C., and still more preferably at 150° C. to 180° C.
  • the heating is preferably carried out for 1 to 60 minutes, more preferably 1 to 30 minutes, in terms of processability.
  • heating at a high temperature for a short time is preferred because such heating increases the flowability of polyurethane molecules, facilitates the aggregation of HS domains in a molecular structure composed of HS domains and SS domains, forms a well-defined microphase-separated structure, and also prevents pyrolysis of the polyurethane molecules.
  • the sheet material provided with polyurethane resin is preferably cut in the sheet thickness direction into half or several pieces to increase production efficiency.
  • the sheet material provided with polyurethane resin can be provided with a lubricant such as a silicone emulsion. It is also preferable to provide an antistatic agent before the napping because the antistatic agent prevents dust generated by buffing of the sheet material from settling on sandpaper.
  • the sheet material can be napped to form raising on the surface of the sheet material.
  • the napping can be carried out by buffing using sandpaper, a roll sander, or the like.
  • the thickness of the sheet material is preferably about 0.1 to 5.0 mm to prevent a reduction in physical properties, such as tensile strength and tear strength, of the sheet material and keep the touch of the sheet material soft.
  • the sheet material can be dyed.
  • the dyeing is preferably carried out using a jet dyeing machine because the sheet material can be softened by crumpling while being dyed.
  • the dyeing temperature is preferably 80° C. to 150° C., more preferably 110° C. to 130° C., to prevent deterioration of polyurethane and dye the fibers sufficiently.
  • the dye may be selected depending on the type of fibers constituting the fibrous substrate.
  • disperse dyes can be used for polyester fibers, and acidic dyes, metal complex dyes, and combinations thereof can be used for polyamide fibers.
  • reduction cleaning can be carried out after the dyeing.
  • Dyeing auxiliaries can improve the uniformity and reproducibility of dyeing.
  • the sheet material can be subjected to a finishing treatment using softening agents (e.g., silicone), antistatic agents, water-repellents, flame retardants, light stabilizers, antibacterial agents, and other agents.
  • a piece of polyurethane was cut out from a man-made leather, and the piece was cut cross-sectionally using a microtome under freezing conditions to obtain a test sample.
  • Measurements were made using a NanoScopeV Dimension Icon scanning probe microscope (SPM), an AFM available from BrukerAXS, by phase imaging in a tapping mode.
  • SPM NanoScopeV Dimension Icon scanning probe microscope
  • AFM available from BrukerAXS
  • a silicon cantilever was used as a measurement probe.
  • the measurements were made at a scan rate of 0.3 to 0.5 Hz in the ambient atmosphere at room temperature (20° C.).
  • the measured section was 1 ⁇ m 2 (1 ⁇ m ⁇ 1 ⁇ m, 512 by 512 pixels).
  • the phase of vibration of the cantilever during the measurement lags on a soft surface that is highly adhesive and viscous, whereas the phase leads on a hard surface. Since the measurements are made such that areas where the phase leads are brightly displayed, HS domains, which are hard, are brightly displayed, whereas SS domains, which are relatively soft, are darkly displayed.
  • the cross-sectional structure of the polyurethane resin was photographed at 25 points with an AFM to obtain microphase-separated structure images.
  • the images each showing a 1 ⁇ m 2 area in the cross-section of the polyurethane resin were processed into JPEG images of 512 by 512 pixels using image processing software (drag and drop image transformation, version: 3.01).
  • the image data were then analyzed using ImageJ image analysis software (version: 1.44p) developed by National Institutes of Health.
  • the image analysis was carried out as follows: the image obtained was converted into an 8-bit gray-scale image using ImageJ; its brightness was expressed by numerical values from 0 (minimum) to 256 (maximum); and then parameter A was calculated as described in Section D below.
  • the storage elastic modulus E′ and tan ⁇ were measured using a polyurethane resin film having a thickness of 200 ⁇ m with a DMA7100 storage elastic modulus measurement apparatus (Hitachi High-Tech Science Corporation) at a frequency of 12 Hz.
  • the appearance of a sheet material was evaluated by twenty evaluators, ten healthy men and ten healthy women, through visual observation and sensory evaluation and rated on the following 5-point scale. The most rate was used as the appearance of the sheet material. Grade 4 and grade 5 were evaluated as good.
  • Grade 5 Fibers are raised uniformly and dispersed well, and appearance is good.
  • Grade 4 Between grade 5 and grade 3.
  • Grade 3 Fibers are dispersed not well at some parts, but fibers are raised and appearance is acceptably good.
  • Grade 2 Between grade 3 and grade 1.
  • Grade 1 Fibers are dispersed very badly overall, and appearance is bad.
  • the paper-like feel of a sheet material was evaluated by twenty evaluators, ten healthy men and ten healthy women, through sensory evaluation by touch and rated on the following 5-point scale. The most rate was used as the paper-like feel of the sheet material. Grade 4 and grade 5 were evaluated as good (excellent in rubber elasticity).
  • Grade 5 Wrinkle recovers, and touch is soft.
  • Grade 4 Between grade 5 and grade 3.
  • Grade 3 Between grade 4 and grade 3.
  • Grade 2 Between grade 3 and grade 1.
  • Grade 1 Sheet is hard and has a texture with a paper-like feel.
  • Table 1 shows the properties of the polyurethane resin compositions A to I.
  • Table 2 shows the properties of the polyurethane resin compositions J to M.
  • Polyethylene terephthalate copolymerized with 8 mol % 5-sodium sulfoisophthalate was used as a sea component, and polyethylene terephthalate was used as an island component.
  • the sea component and the island component were conjugated in a ratio of 20% by mass to 80% by mass to give sea-island type conjugated fibers having 16 islands per filament and an average fiber diameter of 20 ⁇ m.
  • the sea-island type conjugated fibers obtained were cut into staple fibers 51 mm in length and passed through a card and a crosslapper to form a fiber web. The fiber web was processed into a nonwoven fabric by needle punching.
  • the nonwoven fabric thus obtained was shrunk by dipping in hot water at 97° C. for 5 minutes, and dried at 100° C. for 10 minutes.
  • the resulting nonwoven fabric was then provided with an aqueous solution of a PVA (NM-14 available from Nippon Synthetic Chemical Industry), having a degree of saponification of 99% and a degree of polymerization of 1,400, the aqueous solution being adjusted to have a solid content of 10% by mass.
  • the nonwoven fabric was dried at 100° C. for 10 minutes and then additionally heated at 150° C. for 20 minutes.
  • the sheet thus obtained was then dipped into an aqueous solution of sodium hydroxide at a concentration of 50 g/L heated to 50° C.
  • the dissolved sheet was then impregnated with a dispersion of the polyurethane resin composition A adjusted to have a solids concentration of 20%, an active ingredient of a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount of 6% based on solid polyurethane, and magnesium sulfate in an amount of 0.4 part by mass based on solid polyurethane.
  • a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount of 6% based on solid polyurethane
  • magnesium sulfate in an amount of 0.4 part by mass based on solid polyurethane.
  • the impregnated sheet was treated in a moist-hot atmosphere at a temperature of 97° C. and a humidity of 100% for 5 minutes and then dried at 110° C. for 15 minutes to give a sheet provided with aqueous dispersed type polyurethane resin such that the mass of polyurethane based on the mass of the island component of the nonwoven fabric was 35% by mass.
  • the sheet provided with polyurethane resin was dipped in hot water at 98° C. for 10 minutes to remove the PVA and then dried at 100° C. for 10 minutes. Thereafter, the resulting sheet was further additionally heated at 160° C. for 20 minutes.
  • the dissolved sheet was then cut in half perpendicularly to the thickness direction using a slicer equipped with an endless band knife.
  • the surface opposite to the cut side was napped by buffing with 120-mesh and 240-mesh sandpaper, dyed with a disperse dye using a circular dyeing machine, and then subjected to reduction cleaning, thereby obtaining a man-made leather with a unit weight of 250 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel. From the man-made leather, the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 5.8, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a dispersion of the polyurethane resin composition B adjusted to have a solids concentration of 20%, an active ingredient of a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount of 6% based on solid polyurethane, and magnesium sulfate in an amount of 0.3 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 222 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 4.2, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a dispersion of the polyurethane resin composition C adjusted to have a solids concentration of 20%, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 6% by mass based on solid polyurethane, and magnesium sulfate in an amount of 0.4 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 252 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane was collected and observed under an AFM.
  • the parameter A was 2.2, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Polyethylene terephthalate copolymerized with 8 mol % 5-sodium sulfoisophthalate was used as a sea component, and polyethylene terephthalate was used as an island component.
  • the sea component and the island component were conjugated in a ratio of 20% by mass to 80% by mass to give sea-island type conjugated fibers having 16 islands per filament and an average fiber diameter of 20 ⁇ m.
  • the sea-island type conjugated fibers obtained were cut into staple fibers 51 mm in length and passed through a card and a crosslapper to form a fiber web. The fiber web was processed into a nonwoven fabric by needle punching.
  • the nonwoven fabric thus obtained was shrunk by dipping in hot water at 97° C. for 5 minutes, and dried at 100° C. for 10 minutes.
  • the sheet thus obtained was then dipped into an aqueous solution of sodium hydroxide at a concentration of 10 g/L heated to 95° C. and treated for 25 minutes to give a dissolved sheet from which the sea component of the sea-island type conjugated fibers was removed.
  • the average fiber diameter of the surface of the dissolved sheet was 4.2 ⁇ m.
  • the resulting nonwoven fabric was then provided with an aqueous solution of a PVA (NM-14 available from Nippon Synthetic Chemical Industry), having a degree of saponification of 99% and a degree of polymerization of 1,400, the aqueous solution being adjusted to have a solid content of 10% by mass.
  • the nonwoven fabric was dried at 100° C. for 10 minutes and then additionally heated at 160° C. for 10 minutes.
  • the nonwoven fabric was then impregnated with a dispersion of the polyurethane resin composition C adjusted to have a solids concentration of 20%, an active ingredient of an aqueous isocyanate (“Desmodur” [registered trademark] N3900 available from Bayer-Material Science) in an amount of 6% based on solid polyurethane, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 7% based on solid polyurethane, and magnesium sulfate in an amount of 0.3 part by mass based on solid polyurethane.
  • an active ingredient of an aqueous isocyanate (“Desmodur” [registered trademark] N3900 available from Bayer-Material Science) in an amount of 6% based on solid polyurethane
  • an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark]
  • the impregnated nonwoven fabric was treated in a moist-hot atmosphere at a temperature of 97° C. and a humidity of 100% for 5 minutes and then dried at 110° C. for 15 minutes to give a sheet provided with aqueous dispersed type polyurethane resin such that the mass of polyurethane based on the mass of the island component of the nonwoven fabric was 35% by mass.
  • Example 1 the same procedure as in Example 1 was repeated to obtain a man-made leather with a unit weight of 219 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel. From the man-made leather, the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.5, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a dispersion of the polyurethane resin composition C adjusted to have a solids concentration of 20%, an active ingredient of an aqueous isocyanate (“Desmodur” [registered trademark] N3900 available from Bayer-Material Science) in an amount of 6% based on solid polyurethane, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 7% based on solid polyurethane, and magnesium sulfate in an amount of 0.1 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 251 g/m 2 .
  • an active ingredient of an aqueous isocyanate (“Desmodur” [registered trademark] N3900 available from Bayer-Material Science) in an amount of 6%
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.2, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 5 The same procedure as in Example 5 was repeated except that the sea-island conjugated fibers of Example 1 were passed through a card and a crosslapper to form fiber webs, and after the fiber webs were laminated, a woven fabric with 96 ends and 76 picks per inch made of a warp yarn and a weft yarn both having a fineness of 84 dtex and 72 filaments was superposed on both surfaces of the fiber web laminate, after which the laminate was processed into a nonwoven fabric laminate by needle punching; and the aqueous dispersed type polyurethane resin was provided such that the mass of polyurethane based on the mass of the island component of the nonwoven fabric was 28% by mass, thereby obtaining a man-made leather with a unit weight of 398 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.4, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • the nonwoven fabric obtained in Example 1 was shrunk by dipping in hot water at 97° C. and dried at 100° C. for 5 minutes to give a sheet.
  • the sheet was then dipped into an aqueous solution of sodium hydroxide at a concentration of 5 g/L heated to 95° C. and treated for 25 minutes to give a dissolved sheet from which the sea component of the sea-island type conjugated fiber was removed.
  • the average fiber diameter of the surface of the dissolved sheet was 4.2 ⁇ m.
  • the dissolved sheet was then impregnated with a dispersion of the polyurethane resin composition C adjusted to have a solids concentration of 20%, an active ingredient of an aqueous isocyanate (“Desmodur” [registered trademark] N3900 available from Bayer-Material Science) in an amount of 6% based on solid polyurethane, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 7% based on solid polyurethane, magnesium sulfate in an amount of 0.1 part by mass based on solid polyurethane, and sodium hydrogen carbonate (“Cellmic” [registered trademark] 266 available from Sankyo Kasei Co., Ltd.) in an amount of 3 parts by mass based on solid polyurethane resin.
  • an active ingredient of an aqueous isocyanate (“Desmodur” [registered trademark] N3900 available from Bayer
  • the impregnated sheet was treated in a moist-hot atmosphere at a temperature of 97° C. and a humidity of 100% for 5 minutes and then hot-air dried at a drying temperature of 110° C. for 15 minutes to give a sheet provided with aqueous dispersed type polyurethane resin such that the mass of polyurethane resin based on the mass of the island component of the dissolved sheet was 35% by mass.
  • the sheet obtained was additionally heated at 160° C. for 15 minutes and then cut in half perpendicularly to the thickness direction using a slicer equipped with an endless band knife.
  • the surface opposite to the cut side was napped by buffing with 120-mesh and 240-mesh sandpaper, dyed with a disperse dye using a circular dyeing machine, and then subjected to reduction cleaning, thereby obtaining a man-made leather with a unit weight of 236 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.0, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a solution of the polyurethane resin composition C adjusted to have a solids concentration of 20% and magnesium sulfate in an amount of 0.1 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 221 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 1.9, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • FIG. 1 is an AFM micrograph of the microphase-separated structure of the polyurethane resin extracted from the man-made leather obtained in Example 8 of the present invention.
  • FIG. 1 a microphase-separated structure in which spherical HS domains mainly having a size of 100 nm or smaller are dispersed in uniform SS domains is observed, which structure is not observed in FIG. 3 .
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a dispersion of the polyurethane resin composition D adjusted to have a solids concentration of 20%, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 6% based on solid polyurethane, and magnesium sulfate in an amount of 0.5 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 215 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 3.5, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a dispersion of the polyurethane resin composition E adjusted to have a solids concentration of 20%, an active ingredient of a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount of 6% based on solid polyurethane, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 7% based on solid polyurethane, and magnesium sulfate in an amount of 0.5 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 215 g/m 2 .
  • a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.8, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the sheet substrate was impregnated with a dispersion of the polyurethane resin composition F adjusted to have a solids concentration of 20%, an active ingredient of a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount of 6% based on solid polyurethane, an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 5% based on solid polyurethane, and magnesium sulfate in an amount of 0.6 part by mass based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 227 g/m 2 .
  • a blocked isocyanate (“Erastron” [registered trademark] BN-77 available from Dai-ichi Kogyo Seiyaku) in an amount
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 3.2, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • spherical HS domains mainly having a size of 100 nm or smaller were dispersed in uniform SS domains.
  • Example 5 The same procedure as in Example 5 was repeated except that the polyurethane resin composition G was used as a polyurethane resin, thereby obtaining a man-made leather with a unit weight of 248 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.3, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were uniformly dispersed in uniform SS domains.
  • Example 6 The same procedure as in Example 6 was repeated except that the polyurethane resin composition G was used as a polyurethane resin, thereby obtaining a man-made leather with a unit weight of 390 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.2, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were uniformly dispersed in uniform SS domains.
  • Example 7 The same procedure as in Example 7 was repeated except that the polyurethane resin composition G was used as a polyurethane resin, thereby obtaining a man-made leather with a unit weight of 257 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.1, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were uniformly dispersed in uniform SS domains.
  • Example 2 The same procedure as in Example 1 was repeated except that the polyurethane resin composition G was used as a polyurethane resin, and the sheet substrate was impregnated with a solution of the polyurethane resin composition G, magnesium sulfate in an amount of 0.1 part by mass based on solid polyurethane, and an active ingredient of a carbodiimide crosslinking agent (“Carbodilite” [registered trademark] V02-L2 available from Nisshinbo Chemical) in an amount of 4% based on solid polyurethane, thereby obtaining a man-made leather with a unit weight of 229 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 2.0, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed.
  • FIG. 2 is an AFM micrograph of the microphase-separated structure of the polyurethane resin extracted from the man-made leather obtained in Example 15 of the present invention.
  • a microphase-separated structure in which spherical HS domains mainly having a size of 100 nm or smaller are uniformly dispersed is observed, which structure is not observed in FIG. 3 .
  • spherical HS domains mainly having a size of 100 nm or smaller are uniformly dispersed in uniform SS domains.
  • Example 9 The same procedure as in Example 9 was repeated except that the polyurethane resin composition H was used as a polyurethane resin, thereby obtaining a man-made leather with a unit weight of 238 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 3.8, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were uniformly dispersed in uniform SS domains.
  • Example 11 The same procedure as in Example 11 was repeated except that the polyurethane resin composition J was used as a polyurethane resin, thereby obtaining a man-made leather with a unit weight of 240 g/m 2 .
  • the man-made leather obtained had a good appearance and a touch without a paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 3.1, and the polyurethane resin had a microphase-separated structure with HS domains and SS domains finely dispersed. In the microphase-separated structure observed, spherical HS domains mainly having a size of 100 nm or smaller were uniformly dispersed in uniform SS domains.
  • Example 4 The same procedure as in Example 4 was repeated except that the polyurethane resin composition J was used as a polyurethane resin; the sheet substrate was impregnated with a dispersion of the polyurethane resin composition J and magnesium sulfate in an amount of 0.8 part by mass based on solid polyurethane; and additional heating after polyurethane was provided was not performed, thereby obtaining a man-made leather with a unit weight of 237 g/m 2 .
  • the man-made leather obtained had a relatively uniform appearance but had a touch with a strong paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 12.3, and the polyurethane resin had a microphase-separated structure in which HS domains and SS domains were ill-defined.
  • Example 7 The same procedure as in Example 7 was repeated except that the polyurethane resin composition J was used as a polyurethane resin; the sheet substrate was impregnated with a dispersion of the polyurethane resin composition J and magnesium sulfate in an amount of 0.8 part by mass based on solid polyurethane; and additional heating after polyurethane was provided was not performed, thereby obtaining a man-made leather with a unit weight of 202 g/m 2 .
  • the man-made leather obtained had a relatively uniform appearance but had a touch with a strong paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 12.1, and the polyurethane resin had a microphase-separated structure in which HS domains and SS domains were ill-defined.
  • FIG. 3 is an AFM micrograph of the microphase-separated structure of the polyurethane extracted from the man-made leather obtained in Comparative Example 2.
  • FIG. 3 unlike FIG. 1 , spherical HS domains having a size of some tens of nanometers are not observed, and HS domains are ununiformly dispersed.
  • Example 2 The same procedure as in Example 2 was repeated except that the polyurethane resin composition M was used as a polyurethane resin; the sheet substrate was impregnated with a dispersion of the polyurethane resin composition M and magnesium sulfate in an amount of 1.2 parts by mass based on solid polyurethane; and additional heating at 160° C. for 20 minutes was not performed after the removal of PVA and the subsequent drying at 100° C. for 10 minutes, thereby obtaining a man-made leather with a unit weight of 233 g/m 2 .
  • the man-made leather obtained had a relatively uniform appearance but had a touch with a somewhat paper-like feel.
  • the polyurethane resin was collected and observed under an AFM.
  • the parameter A was 15.8, and the polyurethane resin had a microphase-separated structure in which HS domains and SS domains were ill-defined.
  • the sheet material according to the present invention is used mainly as a man-made leather and suitable for use as, for example, interior materials having very elegant appearances, such as facing materials of furnishings, chairs, wallings, and seats, ceilings, and interiors in compartments of vehicles such as automobiles, trains, and aircraft; clothing materials used for shirts, jackets, uppers and trims of shoes such as casual shoes, sports shoes, men's shoes, and women's shoes, bags, belts, wallets, and parts thereof; and industrial materials such as wiping cloths, polishing cloths, and compact-disk curtains.
  • interior materials having very elegant appearances such as facing materials of furnishings, chairs, wallings, and seats, ceilings, and interiors in compartments of vehicles such as automobiles, trains, and aircraft
  • clothing materials used for shirts, jackets, uppers and trims of shoes such as casual shoes, sports shoes, men's shoes, and women's shoes, bags, belts, wallets, and parts thereof
  • industrial materials such as wiping cloths, polishing cloths, and

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Health & Medical Sciences (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Dispersion Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Synthetic Leather, Interior Materials Or Flexible Sheet Materials (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
US15/115,518 2014-01-30 2015-01-22 Sheet-like article, and method for producing same Abandoned US20170183814A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2014015350 2014-01-30
JP2014-015350 2014-01-30
PCT/JP2015/051620 WO2015115290A1 (fr) 2014-01-30 2015-01-22 Article de type feuille et son procédé de fabrication

Publications (1)

Publication Number Publication Date
US20170183814A1 true US20170183814A1 (en) 2017-06-29

Family

ID=53756866

Family Applications (1)

Application Number Title Priority Date Filing Date
US15/115,518 Abandoned US20170183814A1 (en) 2014-01-30 2015-01-22 Sheet-like article, and method for producing same

Country Status (7)

Country Link
US (1) US20170183814A1 (fr)
EP (1) EP3101172B1 (fr)
JP (1) JPWO2015115290A1 (fr)
KR (1) KR20160114069A (fr)
CN (1) CN105940154B (fr)
TW (1) TWI658096B (fr)
WO (1) WO2015115290A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170298569A1 (en) * 2014-09-30 2017-10-19 Toray Industries, Inc. Method for manufacturing sheet-like product
WO2021063757A1 (fr) * 2019-09-30 2021-04-08 Covestro Intellectual Property Gmbh & Co. Kg Composition résistante aux acides et résistante aux alcalis
CN113907582A (zh) * 2021-09-17 2022-01-11 江苏鼎顺医疗用品有限公司 一种医用枕套及其制造方法
US11566378B2 (en) 2019-11-27 2023-01-31 Seiko Epson Corporation Fiber assembly-forming method and fiber assembly-forming apparatus

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106029976B (zh) * 2014-02-27 2018-08-31 东丽株式会社 片状物及其制造方法
JP6631218B2 (ja) * 2015-12-09 2020-01-15 Dic株式会社 凝固物の製造方法
TWI622679B (zh) * 2016-04-29 2018-05-01 財團法人紡織產業綜合研究所 高摩擦性纖維及其製造方法
JP6834222B2 (ja) * 2016-07-29 2021-02-24 東レ株式会社 シート状物およびその製造方法
US11795267B2 (en) 2016-12-12 2023-10-24 Dic Corporation Aqueous urethane resin composition and synthetic leather
JP6903912B2 (ja) * 2016-12-26 2021-07-14 大日本印刷株式会社 物品及びその製造方法、並びに物品の触感評価方法
EP3530322A1 (fr) * 2018-02-27 2019-08-28 Covestro Deutschland AG Composition cosmétique permettant d'améliorer la permanence d'une coiffure
KR102027323B1 (ko) * 2018-09-18 2019-10-01 조맹상 수성 방오처리된 폴리우레탄 인조피혁의 제조방법
KR20210141506A (ko) * 2019-03-29 2021-11-23 도레이 카부시키가이샤 시트상물 및 그 제조 방법
KR102399862B1 (ko) * 2021-02-04 2022-05-18 장영환 원형 보존이 가능한 모자 및 그 제조 방법

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS591823B2 (ja) * 1979-11-21 1984-01-14 株式会社 鈴寅整染工場 ウレタン樹脂加工布帛の製造法
JPH0543647A (ja) 1990-09-21 1993-02-23 Asahi Chem Ind Co Ltd 人工皮革用ポリウレタン組成物
JP3285583B2 (ja) * 1992-10-28 2002-05-27 株式会社クラレ ポリウレタン及び該ポリウレタンを使用した皮革様シート
US6322851B1 (en) * 1998-06-30 2001-11-27 Kuraray Co., Ltd. Manufacturing process for leather-like sheet
KR100625223B1 (ko) * 2000-02-28 2006-09-19 마쓰모토유시세이야쿠 가부시키가이샤 다공체의 제조 방법
JP2002061081A (ja) * 2000-08-18 2002-02-28 Toray Ind Inc スエード調皮革様シート状物
JP2005213411A (ja) * 2004-01-30 2005-08-11 Nicca Chemical Co Ltd 多孔性構造体の製造方法、多孔性構造体及び皮革状構造物
JP2006307000A (ja) * 2005-04-28 2006-11-09 Toray Ind Inc ポリウレタン組成物およびそれを用いてなるシート状物ならびに内装材
JP2008208510A (ja) * 2007-01-29 2008-09-11 Toray Ind Inc 皮革様シート状物、その製造方法、並びに該皮革様シート状物を用いた内装材、衣料用資材および工業用資材および研磨布
CN101725052B (zh) * 2009-11-04 2012-06-13 烟台万华超纤股份有限公司 水性聚氨酯树脂超细纤维革及制造方法
WO2011114956A1 (fr) * 2010-03-16 2011-09-22 東レ株式会社 Matériau de type feuille et son procédé de fabrication
JP5779424B2 (ja) * 2011-06-30 2015-09-16 株式会社クラレ 銀付調皮革様シート
CN102382278B (zh) * 2011-08-29 2013-08-28 旭川化学（苏州）有限公司 一种水性聚氨酯树脂及其制备方法和应用
CN102391461B (zh) * 2011-08-29 2013-04-03 旭川化学（苏州）有限公司 一种超软质聚氨酯树脂及其制备方法和应用
JP2013083031A (ja) * 2011-09-29 2013-05-09 Kuraray Co Ltd 多孔性構造体の製造方法
JP5958060B2 (ja) * 2012-05-10 2016-07-27 東レ株式会社 シート状物およびその製造方法

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Koide US 2013/0005848 A1 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170298569A1 (en) * 2014-09-30 2017-10-19 Toray Industries, Inc. Method for manufacturing sheet-like product
WO2021063757A1 (fr) * 2019-09-30 2021-04-08 Covestro Intellectual Property Gmbh & Co. Kg Composition résistante aux acides et résistante aux alcalis
US11566378B2 (en) 2019-11-27 2023-01-31 Seiko Epson Corporation Fiber assembly-forming method and fiber assembly-forming apparatus
CN113907582A (zh) * 2021-09-17 2022-01-11 江苏鼎顺医疗用品有限公司 一种医用枕套及其制造方法

Also Published As

Publication number Publication date
CN105940154A (zh) 2016-09-14
KR20160114069A (ko) 2016-10-04
TW201538627A (zh) 2015-10-16
TWI658096B (zh) 2019-05-01
EP3101172A4 (fr) 2017-10-11
WO2015115290A1 (fr) 2015-08-06
EP3101172A1 (fr) 2016-12-07
CN105940154B (zh) 2018-06-26
EP3101172B1 (fr) 2024-01-17
JPWO2015115290A1 (ja) 2017-03-23

Similar Documents

Publication Publication Date Title
US20200149216A1 (en) Sheet-like article and a production method therefor
EP3101172B1 (fr) Cuir artificiel en feuille et son procédé de fabrication
CN107002351B (zh) 片状物
JP6520709B2 (ja) シート状物
EP3202975B1 (fr) Procédé de fabrication d&#39;un produit de type feuille
JP6007900B2 (ja) シート状物およびその製造方法
JP2017172074A (ja) シート状物およびその製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: TORAY INDUSTRIES, INC., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MURAHARA, HISASHI;NAKAI, SHUNICHIRO;MATSUZAKI, YUKIHIRO;AND OTHERS;REEL/FRAME:039943/0489

Effective date: 20160602

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE AFTER FINAL ACTION FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: ADVISORY ACTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION