US20100279566A1 - Passive electrical article - Google Patents

Passive electrical article Download PDF

Info

Publication number
US20100279566A1
US20100279566A1 US12/771,365 US77136510A US2010279566A1 US 20100279566 A1 US20100279566 A1 US 20100279566A1 US 77136510 A US77136510 A US 77136510A US 2010279566 A1 US2010279566 A1 US 2010279566A1
Authority
US
United States
Prior art keywords
nonwoven material
article
pvdf
substrate
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/771,365
Other languages
English (en)
Inventor
Rui Yang
Guoping Mao
Dipankar Ghosh
Ji-Hwa Lee
Sungbae Min
Justine A. Mooney
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to US12/771,365 priority Critical patent/US20100279566A1/en
Assigned to 3M INNOVATIVE PROPERTIES COMPANY reassignment 3M INNOVATIVE PROPERTIES COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MOONEY, JUSTINE A., YANG, RUI, GHOSH, DIPANKAR, LEE, JI-HWA, MAO, GUOPING, MIN, SUNGBAE
Publication of US20100279566A1 publication Critical patent/US20100279566A1/en
Priority to US15/207,719 priority patent/US10399295B2/en
Abandoned legal-status Critical Current

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
    • B32B5/022—Non-woven fabric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/14—Layered products comprising a layer of metal next to a fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/20—Layered products comprising a layer of metal comprising aluminium or copper
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/12—Layered products comprising a layer of synthetic resin next to a fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/28—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42
    • B32B27/281—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42 comprising polyimides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/28—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42
    • B32B27/285—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42 comprising polyethers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
    • B32B27/308—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers comprising acrylic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/32—Layered products comprising a layer of synthetic resin comprising polyolefins
    • B32B27/322—Layered products comprising a layer of synthetic resin comprising polyolefins comprising halogenated polyolefins, e.g. PTFE
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/34—Layered products comprising a layer of synthetic resin comprising polyamides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/36—Layered products comprising a layer of synthetic resin comprising polyesters
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/42—Layered products comprising a layer of synthetic resin comprising condensation resins of aldehydes, e.g. with phenols, ureas or melamines
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B38/00—Ancillary operations in connection with laminating processes
    • B32B38/0036—Heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/14—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by a layer differing constitutionally or physically in different parts, e.g. denser near its faces
    • B32B5/147—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by a layer differing constitutionally or physically in different parts, e.g. denser near its faces by treatment of the layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B9/00—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00
    • B32B9/005—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00 comprising one layer of ceramic material, e.g. porcelain, ceramic tile
    • B32B9/007—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00 comprising one layer of ceramic material, e.g. porcelain, ceramic tile comprising carbon, e.g. graphite, composite carbon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B9/00—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00
    • B32B9/04—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00 comprising such particular substance as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B9/047—Layered products comprising a layer of a particular substance not covered by groups B32B11/00 - B32B29/00 comprising such particular substance as the main or only constituent of a layer, which is next to another layer of the same or of a different material made of fibres or filaments
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01C—RESISTORS
    • H01C7/00—Non-adjustable resistors formed as one or more layers or coatings; Non-adjustable resistors made from powdered conducting material or powdered semi-conducting material with or without insulating material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01G—CAPACITORS; CAPACITORS, RECTIFIERS, DETECTORS, SWITCHING DEVICES, LIGHT-SENSITIVE OR TEMPERATURE-SENSITIVE DEVICES OF THE ELECTROLYTIC TYPE
    • H01G4/00—Fixed capacitors; Processes of their manufacture
    • H01G4/002—Details
    • H01G4/018—Dielectrics
    • H01G4/06—Solid dielectrics
    • H01G4/14—Organic dielectrics
    • H01G4/18—Organic dielectrics of synthetic material, e.g. derivatives of cellulose
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/02—Coating on the layer surface on fibrous or filamentary layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/06—Coating on the layer surface on metal layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/10—Coating on the layer surface on synthetic resin layer or on natural or synthetic rubber layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/20—Inorganic coating
    • B32B2255/205—Metallic coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/24—Organic non-macromolecular coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2255/00—Coating on the layer surface
    • B32B2255/26—Polymeric coating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0223—Vinyl resin fibres
    • B32B2262/023—Aromatic vinyl resin, e.g. styrenic (co)polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0223—Vinyl resin fibres
    • B32B2262/0238—Vinyl halide, e.g. PVC, PVDC, PVF, PVDF
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0246—Acrylic resin fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0253—Polyolefin fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0261—Polyamide fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/02—Synthetic macromolecular fibres
    • B32B2262/0276—Polyester fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
    • B32B2264/10—Inorganic particles
    • B32B2264/105—Metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2270/00—Resin or rubber layer containing a blend of at least two different polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2305/00—Condition, form or state of the layers or laminate
    • B32B2305/10—Fibres of continuous length
    • B32B2305/20—Fibres of continuous length in the form of a non-woven mat
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2305/00—Condition, form or state of the layers or laminate
    • B32B2305/30—Fillers, e.g. particles, powders, beads, flakes, spheres, chips
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/20—Properties of the layers or laminate having particular electrical or magnetic properties, e.g. piezoelectric
    • B32B2307/202—Conductive
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/20—Properties of the layers or laminate having particular electrical or magnetic properties, e.g. piezoelectric
    • B32B2307/204—Di-electric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/30—Properties of the layers or laminate having particular thermal properties
    • B32B2307/308—Heat stability
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/546—Flexural strength; Flexion stiffness
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment
    • B32B2457/08—PCBs, i.e. printed circuit boards
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment
    • B32B2457/16—Capacitors
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y10T442/2008—Fabric composed of a fiber or strand which is of specific structural definition
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y10T442/2861—Coated or impregnated synthetic organic fiber fabric
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y10T442/2861—Coated or impregnated synthetic organic fiber fabric
    • Y10T442/2885—Coated or impregnated acrylic fiber fabric
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/20—Coated or impregnated woven, knit, or nonwoven fabric which is not [a] associated with another preformed layer or fiber layer or, [b] with respect to woven and knit, characterized, respectively, by a particular or differential weave or knit, wherein the coating or impregnation is neither a foamed material nor a free metal or alloy layer
    • Y10T442/2861—Coated or impregnated synthetic organic fiber fabric
    • Y10T442/291—Coated or impregnated polyolefin fiber fabric
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]

Definitions

  • This invention relates to passive electrical articles.
  • it relates to the dielectric layer in passive electrical articles such as capacitors and resistors.
  • Electrical articles such as the capacitors and resistors described in U.S. Pat. No. 6,274,224 and U.S. Pat. No. 6,577,492 typically include a polymeric insulating or electrically conducting layer between first and second self supporting substrates.
  • the dielectric material of the insulating layer is typically a metal oxide, such as tantalum oxide, or a high dielectric constant ceramic, such as barium titanate.
  • the dielectric material is typically dispersed in a matrix of some thermally and mechanically stable polymer, such as an epoxy.
  • the electrical articles can be used as a layer in printed wiring boards and multichip modules.
  • One embodiment of the present invention features a passive electrical article having a dielectric layer comprising a resin and a nonwoven material.
  • Another embodiment of the present invention features a method of making an electrical article comprising providing two conductive substrates, coating a resin on a surface of each conductive substrate, providing a nonwoven material between the resin-coated surfaces of the conductive substrates, and laminating the resin-coated conductive substrates and the nonwoven material together.
  • Another embodiment of the present invention features a method of making an electrical article comprising coating a resin layer on a surface of a first conductive substrate, forming a nonwoven material on a surface of a second conductive substrate, and laminating the conductive substrate together with the resin layer and nonwoven material facing each other.
  • Another embodiment of the present invention features a method of making an electrical article comprising forming a nonwoven material on a first surface of one or both of a first and second conductive substrate; coating a resin layer on the first surfaces of both conductive substrates, and laminating the conductive substrates together with the resin-coated first surfaces facing each other.
  • An advantage of at least one embodiment of the present invention is that it provides a strong, flexible dielectric layer suitable for use in a copper-clad laminate capacitor structure that is subjected to a double-sided copper patterning etch process. Being able to etch both copper layers at the same time, rather than one at a time enables a process cost reduction.
  • self-supporting refers to a film, web, material, layer, or substrate having sufficient structural integrity such that the it is capable of being handled an/or subjected to at least some processed without a separate supporting layer.
  • the invention is a dielectric layer that may be used in a passive electrical article, such as a capacitor, resistor, or inductor.
  • the passive electrical articles are preferably suitable for embedding in a printed circuit board.
  • the electrical articles generally include a first self-supporting conductive substrate having two opposing major surfaces and a second self-supporting conductive substrate having two opposing major surfaces. A dielectric layer between the first and second substrate provides an electrical insulating function and adheres the two substrates together.
  • the substrates of the electrical article of the invention may include a single layer, or a plurality of layers arranged in a laminate structure.
  • the first and second substrates may be made of graphite; composites such as silver particles in a polymer matrix; metal such as Copper, Aluminum, Nickel, Chromium, Zinc, Tin, Gold, Silver, Palladium; and alloys or laminates thereof.
  • a substrate may be made by coating a layer of metal, such as copper or aluminum, onto a removable carrier layer. For example, a copper layer may be coated onto a removable polyester carrier.
  • the first and second substrates may be the same or different.
  • the electrical article of the invention may include multiple insulating and conductive layers.
  • a substrate in accordance with the electrical articles of the invention is preferably self-supporting. It is preferable that a substrate is flexible; however, rigid substrates may also be used.
  • the major surface of the first substrate in contact with the dielectric layer and the major surface of the second substrate in contact with the dielectric layer are electrically conductive.
  • Surface treatment which adds material to these major surfaces by, for example, oxidation or reaction with a coupling agent, may be used to promote adhesion.
  • a separate coating step may be performed to apply an adhesion promoting primer, such as 5-aminobenzotriazole.
  • Treatment of the substrate surface with 5-aminobenzotriazole may be particularly relevant for copper foils not having a chromate anti-tarnish surface treatment.
  • the resulting material on the major surface of the substrate itself may not necessarily be conductive, but a suitable electrical article can be formed provided the substrates themselves are conductive.
  • a substrate has a thickness ranging from 0.5 to 3 mils (approximately 10 to 80 ⁇ m), more typically 0.5 to 1.5 mils (approximately 10 to 38 ⁇ m).
  • the metal When the substrate is a metal, the metal typically has an anneal temperature which is at or below the temperature for curing the dielectric layer, or the metal is annealed before the dielectric layer is coated.
  • a preferred substrate is copper.
  • the copper may be any suitable type such as, but not limited to, rolled annealed, electrodeposited, and reverse electrodeposited. Exemplary copper includes copper foil available from Carl Schlenk, A G, Nurnberg, Germany and Oak Mitsui, Camden, S.C.
  • the dielectric layer of the electrical article which may be made of one or more layers, includes a polymer. Any polymer may be used that can withstand the temperatures encountered in a typical solder reflow operation, for example, about 180 to about 290° C. Suitable polymeric materials for the dielectric layer include Acrylates, Allyated Polyphenylene Ether (APPE), Benzocyclobutene (BCB), Bismaleimide Triazine (BT), Cyanate Ester, Epoxy, Polyamide, Polyester, Polyimide, Polyphenylene Oxide (PPO), Polytetrafluoroethylene (PTFE), and combinations thereof.
  • APPE Allyated Polyphenylene Ether
  • BCB Benzocyclobutene
  • BT Bismaleimide Triazine
  • Cyanate Ester Epoxy, Polyamide, Polyester, Polyimide, Polyphenylene Oxide (PPO), Polytetrafluoroethylene (PTFE), and combinations thereof.
  • Suitable epoxy resin compositions may be made from thermally curable epoxy resins.
  • the term epoxy resin composition will typically be used to refer to an uncured composition.
  • An exemplary epoxy resin composition includes one or more aromatic polyepoxides and one or more 9,9-bis(aminophenyl)fluorene curing agents.
  • Suitable aromatic polyepoxides include poly(glycidyl ether)s of polyhydric phenols and epoxy resins available from Shell Chemical Company, Houston, Tex., under the trade designations EPON 1001F and EPON 1050.
  • Suitable resins include blends of a diglycidylether of bisphenol A and a novolac epoxy, for example, 75 to 90% by weight EPON 1001F and 25 to 10% by weight EPON 1050F based on the total weight of the resin.
  • Suitable curing agents for the epoxy resin compositions include, but are not limited to, di(4-aminophenyl)sulfone and 9,9-bis(aminophenyl)fluorene as described in U.S. Pat. No. 4,684,678.
  • the polymer of the dielectric layer of the present invention is typically loaded with particles having high dielectric constants to increase the dielectric constant of the dielectric layer.
  • Suitable particles include Barium Titanate, Barium Strontium Titanate, Titanium Oxide, Barium Strontium Titanate (BST), Calcium Copper Titanate, Lead Zirconium Titanate, Lead Lanthanium Zirconate Titanate, Lead Magnesium Titanate, Lead Magnesium Niobate-Lead Titanate (Pb (Mg 1/3 Nb 2/3 )O 3 .-PbTiO 3 ), Iron Titanium Tantalate (FeTiTaO 6 ), Bismuth Ferrite (BiAlO 3 ), Bismuth Ferrite (BiFeO 3 ), NiO co-doped with Li and Ti, La 1.5 Sr 0.5 NiO 4 , Nd 1.5 Sr 0.5 NiO 4 , and mixtures thereof.
  • the particles may be any shape and may be regularly or irregularly shaped. Exemplary shapes include spheres, platelets, cubes, needles, oblate, spheroids, pyramids, prisms, flakes, rods, plates, fibers, chips, whiskers, and mixtures thereof.
  • a suitable particle size, e.g., diameter may have a lower range of about 100 nm to about 5 nm and an upper range of about 2 micrometer ( ⁇ m) to about 11 ⁇ m.
  • the particles have a size allowing at least two to three particles to be stacked vertically within the electrically insulating layer thickness.
  • dielectric layers with spherical dielectric particles having a small diameter e.g., about 100 nm
  • dielectric layers with spherical dielectric particles having a small diameter e.g., about 100 nm
  • a suitable coatable resin composition used to form the dielectric layer is typically made from a mixture of epoxy resin, a dispersant, a curing agent, the dielectric particles, and other optional ingredients. Typically, the resulting substantially uniform mixture is subsequently coated on a suitable substrate, then heated for a time and at temperature sufficient to remove volatile components.
  • the dielectric constant of the dielectric material of at least some embodiments of the present invention is greater than about 4, preferably greater than about 11, and more preferably greater than about 15.
  • the loading levels of the dielectric particles may be very high, which can make the dielectric material very brittle. If it is brittle, it cannot endure being processed as a free-standing layer. For example, if both substrates are to be pattern etched, the brittleness of the dielectric layer requires that one substrate is etched, a supporting layer is applied to the etched substrate, then the other substrate is etched. In this manner, the dielectric layer is always supported on at least one side.
  • the present invention provides a more flexible and robust dielectric layer, which allows both substrates to be etched at the same time. This enables a faster and more efficient manufacturing process.
  • the present invention provides these benefits while also providing a dielectric constant and capacitance on par with existing dielectric materials such as those used to form capacitors.
  • the improved properties of the dielectric material of the present invention are achieved by using a nonwoven material in the dielectric layer. Although the nonwoven material itself may have a low dielectric constant, because it has openings that allow the polymer material of the dielectric layer to form a continuous path from one substrate to the other, it does not have the disadvantages of a solid film, which would prevent the polymer material from forming a continuous path from one substrate to the other.
  • Suitable nonwoven materials can be made of any material that can be formed into a nonwoven material.
  • Such materials include, but are not limited to liquid crystal polymer (LCP), nylon, polyester, polystyrene, polyacrylonitrile, polypropylene, polyvinylidene fluoride (PVDF), and hybrid materials such as poly(ether sulfone)-polyvinylidene fluoride (PES-PVDF), polyetherimide-polyvinylidene fluoride (PEI-PVDF), polyacrylonitrile-polyvinylidene fluoride (PAN-PVDF), ethylene chlorotrifluoroethylene (ECTFE), and combinations thereof.
  • LCP liquid crystal polymer
  • nylon nylon
  • polyester polystyrene
  • PVDF polyacrylonitrile
  • Ppropylene polyvinylidene fluoride
  • PVDF polyvinylidene fluoride
  • hybrid materials such as poly(ether sulfone)-polyvinyliden
  • the nonwoven materials may be of any suitable form such as, but not limited to, meltblown nonwovens, spunbond nonwovens, and electrospun nonwovens.
  • Various additives may be added to the precursor material for the nonwoven materials to influence certain properties of the nonwoven material such as dielectric properties, mechanical properties, chemical properties, and thermal properties.
  • the precursor material used to make the nonwoven materials may contain a crosslinking agent so that the fibers in the nonwoven materials can be crosslinked after the nonwoven material is formed.
  • Suitable crosslinking agents can be thermal, e-beam, and UV crosslinking agents and include, but are not limited to, triallycyanurate and triallyisocyanurate.
  • the crosslinking agent may be added in any suitable amount, typically about 2 to about 3 wt %. Crosslinking the nonwoven material can improve properties such as thermal stability, solvent resistance, and durability.
  • the fibers in the nonwoven material may be loaded with dielectric particles, i.e., dielectric particles are embedded in the fibers of the nonwoven material, to increase the dielectric constant of the dielectric layer.
  • dielectric particles include those previously described, e.g., Barium Titanate, Barium Strontium Titanate, Titanium Oxide, Barium Strontium Titanate (BST), Calcium Copper Titanate, Lead Zirconium Titanate, Lead Lanthanium Zirconate Titanate, Lead Magnesium Titanate, and mixtures thereof.
  • the dielectric particles will be loaded with an amount of dielectric particles suitable to provide the desired properties for the dielectric layer. In at least one embodiment, the particles are loaded in an amount of about 10 to about 15 wt % of the precursor material used to form the nonwoven material.
  • silicon dioxide may be added to change the mechanical properties of the nonwoven material.
  • the fibers in the nonwoven material may be arranged randomly or uniformly. If the passive electrical articles being made will be divided into small pieces for their ultimate use, e.g., in a small microphone or other miniaturized devices, a more uniform fiber pattern will provide more consistent properties, such as capacitance, from piece to piece.
  • the nonwoven material may be etched.
  • an LCP nonwoven material may be etched in a similar manner as an LCP film by using a highly alkaline etching solution such as that described in U.S. Pat. No. 7,348,045.
  • the highly alkaline etching solution comprises an alkali metal salt and optionally a solubilizer.
  • a solution of an alkali metal salt alone may be used as an etching solution for polyimide but has a low etching rate when etching materials such as LCP.
  • a solubilizer is combined with the alkali metal salt etchant, it can be used to effectively etch polyimide copolymers having carboxylic ester units in the polymeric backbone and LCPs.
  • Water soluble salts suitable for use in the etching solution include, for example, potassium hydroxide (KOH), sodium hydroxide (NaOH), substituted ammonium hydroxides, such as tetramethylammonium hydroxide and ammonium hydroxide or mixtures thereof.
  • Useful alkaline etching solutions include aqueous solutions of alkali metal salts including alkali metal hydroxides, particularly potassium hydroxide, and their mixtures with amines, as described in U.S. Pat. Nos. 6,611,046 B1 and 6,403,211 B1. Useful concentrations of the etching solutions vary depending upon the thickness of the film to be etched.
  • Typical useful concentrations of a suitable salt range for etching LCP have a lower range of about 30 wt. % to 40 wt. % and an upper range of about 50 wt. % to about 55 wt. %.
  • Typical useful concentrations of a suitable solubilizer have a lower range of about 10 wt. % to about 15 wt. % and an upper range of about 30 wt. % to about 35 wt. %.
  • the use of KOH with a solubilizer is preferred for producing a highly alkaline solution because KOH-containing etching solutions have higher etching rates.
  • the etching solution is generally at a temperature of from about 50° C. (122° F.) to about 120° C. (248° F.) preferably from about 70° C. (160° F.) to about 95° C. (200° F.) during etching.
  • the solubilizer in the etching solution is an amine compound, preferably an alkanolamine.
  • Solubilizers for etching solutions according to the present invention may be selected from the group consisting of amines, including ethylene diamine, propylene diamine, ethylamine, methylethylamine, and alkanolamines such as ethanolamine, diethanolamine, propanolamine, and the like.
  • the etching solution, including the amine solubilizer works most effectively within the above-referenced percentage ranges.
  • the amine acts as a solubilizer for the liquid crystal polymers most effectively within a limited range of concentrations of alkali metal salt in aqueous solution.
  • the nonwoven material can be formed on a supporting backing layer, such as a polyester layer.
  • a supporting backing layer such as a polyester layer.
  • the nonwoven fibers are formed into a web or layer directly on the supporting backing layer, they can be made thinner than are required for a self-supporting nonwoven material.
  • nonwoven materials are made thin by using nanofibers to form the nonwoven material, i.e., the fibers in the nonwoven material have diameters in the nanometer range, i.e., less that one micrometer, and typically from about 20 to about 500 nanometers.
  • the nanofiber nonwoven materials can be made using the same materials that are used to form other nonwoven materials.
  • Nanofibers and nanofiber nonwoven materials may be made by any suitable method, typically electrospinning Nanofibers, nanofiber webs, i.e., materials, and electrospinning are described in more detail in “Polymeric Nanofibers and Nanofiber Webs: A New Class of Nonwovens,” Timothy Grafe, et al., presented at INTC 2002: International Nonwovens Technical Conference ( Joint INDA - TAPPI Conference ), Atlanta, Ga., Sep. 24-26, 2002.
  • a method for manufacturing an electrical article of the invention includes providing first and second substrates, each having two opposing major surfaces.
  • a polymer composition such as an epoxy resin composition, may then be coated onto a first major surface of each of the substrates.
  • the two substrates may then be laminated together with their polymer-coated sides facing each other and a nonwoven layer between the two first major surfaces.
  • the polymer fills the voids in the nonwoven material so that the polymer and nonwoven material essentially form a single layer.
  • the amount of polymer coated on the first major surfaces and the thickness of the nonwoven material may be controlled such that the nonwoven material contacts, or does not contact, the first major surface of one or both of the substrates.
  • the resulting laminate may then heated for a time and a temperature sufficient to cure the polymer composition such as an epoxy resin.
  • the major surfaces of the substrates are preferably substantially free of debris or chemisorbed or adsorbed materials to maximize adhesion with the electrically insulating layer. Suitable substrate cleaning methods known in the art may be used.
  • the cleaned substrate may be coated with the polymer composition using any suitable method, for example, a gravure coater.
  • the polymer composition is then dried to remove residual solvent.
  • the dry thickness of the coated polymer composition depends on the percent solids in the composition, the relative speeds of the gravure roll and the coating substrate, and on the cell volume of the gravure used. Typically, to achieve a dry thickness in the range of about 3 to about 10 ⁇ m, the percent solids in the polymer resin composition are about 20 to 75% by weight.
  • the coating is typically dried to a substantially tack-free state in the oven of the coater, typically at a temperature of less than about 100° C. More typically, the coating is dried in stages starting with a temperature of about 30° C. and ending with a temperature of about 100° C., and then wound onto a roll. Higher final drying temperatures, e.g., up to about 200° C. can be used, but are not required.
  • Lamination is preferably carried out using two of the coated substrates described above.
  • One or both of the coated substrates may go through an oven or over a heated roller before reaching the laminator, for example, at a temperature ranging from about 125 to about 175° C. for less than 30 seconds, and more typically at a temperature about 125 to about 160°.
  • adhesion of the substrate may be improved by heat treating the coating before lamination.
  • the time for heat treatment is typically short, for example, less than about 10 minutes, particularly at higher temperatures.
  • the polymer composition is applied directly to the nonwoven material and the nonwoven material is subsequently laminated between two substrates.
  • a batch process or roll-to-roll process may be used.
  • the coated substrates may be laminated, polymer layer to polymer layer with the nonwoven material fed between the two coated substrates, using a laminator with two nip rollers heated to a temperature ranging from about 120 to about 200° C., typically about 135° C.
  • Suitable air pressure is supplied to the laminator rolls, typically at a pressure ranging from about 5 to about 40 psi (34 to 280 kPa), typically about 15 psi (100 kPa).
  • the roller speed can be set at any suitable value and typically ranges from about 12 to about 36 inches/minute (0.5 to 1.5 cm/second), more typically about 15 inches/minute (0.64 cm/second). If the nonwoven layer is self-supporting, it can be fed between the coated substrates from a roll. If it is not self-supporting it can be fed between the coated substrates as a supporting backing layer is peeled away from the nonwoven material.
  • the time, temperature, and pressure used during the lamination process can be adjusted to ensure that the polymer material fills the voids in the nonwoven material during of the process. In some embodiments, it may be suitable to use a vacuum-pressure impregnation (VPI) method such as that described in U.S. Pat. No. 7,524,388 to impregnate the nonwoven material with the polymer dielectric material.
  • the resulting laminated material can be cut into sheets of the desired length or wound onto a suitable core.
  • the nonwoven material may be formed on, or supported by, a sheet or film then coated with a polymer material, such as epoxy.
  • a polymer material such as epoxy
  • the polymer-coated nonwoven material may then be fed between the substrate layers, generally as described above.
  • the substrate layers may, or may not be, separately coated with polymer.
  • the nonwoven material may be formed directly on a sheet or film that will become one of the substrates in the electrical article.
  • a nonwoven material can be formed on a copper sheet that will become one of the substrates of a capacitive or resistive article.
  • the substrate serves as a support layer, which allows the nonwoven material to be made very thin, and because the copper sheet is never removed from the nonwoven material, problems associated with handling a fragile nonwoven material are reduced.
  • the substrate carrying the nonwoven material may be laminated directly to another substrate having a polymer layer coated thereon.
  • the polymer will fill the voids in the nonwoven material, thereby forming an electrical article having a polymer/nonwoven material dielectric layer.
  • the nonwoven material will be in physical contact with one substrate, and may or may not be in physical contact with the other substrate, depending on the thickness of the polymer layer.
  • a nonwoven material may be formed directly on one or both of the sheets or films that will become the substrates in the electrical article then coated with a polymer composition.
  • a nonwoven material can be formed on one or both of the sheets that will become the substrates of a capacitive or resistive article.
  • a substrate carrying the nonwoven material may be solvent-coated with a polymer solution, such as an epoxy resin solution. It is believed that the solvent solution will easily penetrate the nonwoven material and allow the polymer to fill most or all of the voids in the nonwoven material.
  • the substrate may be laminated directly to another identical substrate (i.e., having a nonwoven material and solvent-coated polymer) or a substrate having only a polymer layer coated thereon.
  • the polymer will be further pressed into any open voids in the nonwoven material, thereby forming an electrical article having a polymer/nonwoven material dielectric layer. If both substrates have a nonwoven material on their surface, in the finished electrical article, a nonwoven material will be in physical contact with each substrate, and may or may not be in physical contact with the nonwoven material on the other substrate, depending on the thicknesses of the polymer layers.
  • the nonwoven material will only make physical contact with the substrate on which it was formed because, depending on the thickness of the polymer layer, most or all of its voids will likely be filled with polymer prior to lamination with the second polymer -coated substrate.
  • the laminated material is typically then heated for a sufficient time and temperature to cure the polymer composition, typically an epoxy.
  • exemplary curing temperatures include temperatures ranging from about 150 to about 225° C., typically about 160 to about 200° C.
  • exemplary curing times include a period ranging from about 90 to about 180 minutes, typically about 90 to about 120 minutes.
  • Adhesion of the dielectric layer to a metal substrate may be enhanced if the metal is sufficiently soft at the time of coating or becomes soft during lamination and/or cure; i.e., the foil is annealed before coating or becomes annealed during subsequent processing.
  • Annealing may be accomplished by heating the substrate before the coating step or as a result of the curing or drying step if the metal anneal temperature is at or lower than the cure temperature of the polymer resin composition. It is preferred to use a metal substrate with an anneal temperature below the temperature at which curing occurs. Annealing condition will vary depending on the metal substrate used.
  • the metal substrate obtains a Vickers hardness, using a 10 g load, of less than about 75 kg/mm2.
  • a typical temperature range of copper to achieve this hardness ranges from about 100 to about 180° C., more typically about 120 to about 160° C.
  • an electrical article of the present invention can be functional as it is fabricated, the electrical article may be patterned, for example, to form discrete islands or removed regions of material in order to limit lateral conductivity. Any suitable patterning technique known in the art may be employed. The patterned electrical article may be used as a circuit article itself or as a component in a circuit article.
  • a surface of the first or second substrate of the electrical article that is accessible may be contacted, for example, by an electrical trace, to make electrical contact so that the first or second substrate acts as an electrode.
  • it may be desirable to make electrical contact with the major surface of the first or second substrate in contact with the dielectric layer or to provide a through hole contact. Through hole contacts are useful when no interaction with the electrical device is desired.
  • An electrical article of the present invention may further comprise one or more additional layers, for example, to prepare it for use in a printed circuit board (PCB) or flexible circuit.
  • the additional layer may be rigid or flexible.
  • Exemplary rigid layers include fiberglass/epoxy composite commercially available from Polyclad, Franklin, N. H., under the trade designation PCL-FR-226, ceramic, metal, or combinations thereof.
  • Exemplary flexible layers comprise a polymer film such as polyimide or polyester, metal foils, or combinations thereof.
  • Polyimide is commercially available from DuPont under the trade designation KAPTON and polyester is commercially available from 3M Company, St. Paul, Minn., under the trade designation SCOTCHPAR.
  • These additional layers may also contain electrically conductive traces on top of the layer or embedded within the layer.
  • the term “electrically conductive traces” refers to strips or patterns of a conductive material designed to carry current. Suitable materials for an electrically conductive trace comprise copper, aluminum, tin, solder, silver paste, gold, and
  • a circuit article may be made by providing an electrical article of the present invention, patterning at least one side of the electrical article, attaching an additional layer to the patterned side of the electrical article, and providing at least one electrical contact to at least one substrate of the electrical article.
  • the second side of the electrical article is also patterned and a second additional layer is provided and attached to this second side of the electrical article.
  • a circuit article is made by providing an electrical article of the present invention, simultaneously patterning both sides of the electrical article, and subsequently attaching an additional layer to one or both sides of the electrical article.
  • the electrical article may be embedded or integrated in a PCB or flexible circuit.
  • Methods for manufacturing a flexible circuit or PCB using the electrical article of the present invention are described in WO 00/45624 and are cited herein by reference.
  • the present invention also encompasses an electrical device comprising an electrical article of the present invention functioning in an electrical circuit of a PCB or a flexible circuit.
  • the electrical device may include any electrical device which typically employs a PCB or flexible circuit having a capacitive component. Exemplary electrical devices include cell phones, telephones, fax machines, computers, printers, pagers, and other devices as recognized by one skilled in the art.
  • the electrical article of the present invention is particularly useful in electrical devices in which space is at a premium or that operate at frequencies greater than 1 GHz.
  • Dispersants SOLSPERSE 76500, a solution of 50% active polymeric dispersant in n-butyl acetate, Lubrizol, Ltd., United Kingdom
  • Methylethylketone MEK
  • Methylisobutylketone MIBK
  • Epoxy EPON 1001F; EPON 1050, Shell Chemical Company, Houston, Tex.
  • LCP (liquid crystal polymer) nonwoven material HM060 Type B, (Basis weight: 6.2 g/m 2 (gsm)), Thickness: 15 um, Tensile strength: 8.2 N/1.5 cm, Air permeability: 302 cc/cm 2 /sec), Crane & Co., Dalton, Mass.
  • Copper foil 18 um thick (1 ⁇ 2 oz) copper foil, Oak Mitsui, Camden, S.C.
  • Plasma etching Plasmatherm PE 2480 system from Plasmatherm, Inc. (St. Moscow, Fla.)
  • Step 1 Mill 1250 grams (g) BaTiO 3 with 15 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BaTiO 3 solution (made in Step 1), and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 7 um thickness of the final solution onto two pieces of copper foil
  • Step 6 Laminate the two coated copper pieces together with the LCP nonwoven material (6.2 g/m 2 (gsm)) between them using a standard nip roller laminator at a temperature of 163° C. and speed of 0.9 meter/minutes.
  • Step 7 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter and the thickness of the dielectric layer was measured after removal of Cu.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 (BT) with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • BT BaTiO 3
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution (made in Step 1), and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Laminate the two coated copper pieces together with the LCP nonwoven material (6.2 gsm) between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 7 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter and the thickness of the dielectric layer was measured.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1500 grams (g) BaTiO 3 with 18 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 5 um thickness of the final solution onto one piece of copper foil and a 7 um thickness of the final solution on another piece of copper.
  • Step 6 Laminate the two coated copper pieces together with the LCP nonwoven material (6.2 gsm) between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 7 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter and the thickness of the dielectric layer was measured.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1250 grams (g) BaTiO 3 with 15 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 7 um thickness of the final solution onto two pieces of copper foil.
  • Step 6 Thin the LCP non-woven material (49.2 wt. % reduction) using a chemical etching process including a 45 wt. % KOH solution as etchant at an elevated temperature of 79° C. for 4 minutes, followed by washing with deionized water and drying at 120° C. for about 15 minutes.
  • a chemical etching process including a 45 wt. % KOH solution as etchant at an elevated temperature of 79° C. for 4 minutes, followed by washing with deionized water and drying at 120° C. for about 15 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (48.1 wt. % reduction) using a chemical etching process including a 45% KOH solution as etchant at an elevated temperature of 67° C. for 9 minutes, followed by washing with deionized water and drying at 120° C. for about 15 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (49.2 wt. % reduction) using a chemical etching process including a 45% KOH solution as etchant at an elevated temperature of 79° C. for 4 minutes, followed by washing with deionized water and drying at 120° C. for about 15 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 with 1.2 wt % SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (51.1 wt. % reduction) using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 4 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 4 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer (or LMZ-2) at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (38.4 wt. % reduction) using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 3.2 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 3.2 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (29.9 wt. % reduction) using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 2.4 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 2.4 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1375 grams (g) BaTiO 3 with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 10 um thickness of the final solution onto one piece of copper foil and a 2.5 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (20 wt. % reduction) using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 1.6 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 1.6 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1500 grams (g) BaTiO 3 with 16.5 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer (or LMZ-2) at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 5 um thickness of the final solution onto one piece of copper foil and a 7 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (30 wt. % reduction) using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 2.4 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 2.4 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1500 grams (g) BaTiO 3 with 18 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 5 um thickness of the final solution onto one piece of copper foil and a 7 um thickness of the final solution on another piece of copper foil.
  • Step 6 Thin the LCP non-woven material (20 wt. % reduction) using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 1.6 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 1.6 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.
  • Step 1 Mill 1500 grams (g) BaTiO 3 with 18 g SOLSPERSE 76500 dispersant, 110 g MEK, and 164 g MIBK in the MiniCer at 4320 rpm for about 10 minutes to produce a milled dispersion.
  • Step 2 Add 32 g EPON 1001 F and 8 g EPON 1050 to 40 g MEK solvent, spin in the Dispermat dissolver until completely dissolved.
  • Step 3 Add 10 g CAF to the epoxy solution from Step 2.
  • Step 4 Add 240 g of the BT solution, and 120 g MEK, to the epoxy solution from step 3, spin in the Dispermat dissolver until uniform dispersion is obtained.
  • Step 5 Coat a 7 um thickness of the final solution onto two pieces of copper foil.
  • Step 6 Thin the non-woven material 30 wt. % using a plasma etching process including oxygen and C 3 F 8 plasma with oxygen gas flow rate of 500 standard cc 3 /min (SCCM) and C 3 F 8 gas flow rate of 100 SCCM, a pressure of 300 mTorr and RF power of 2000 Watts for 2.4 minutes.
  • SCCM standard cc 3 /min
  • RF power 2000 Watts for 2.4 minutes.
  • Step 7 Laminate the two coated copper pieces together with the nonwoven material between them using a standard nip roller laminator at a temperature of 166° C. and speed of 0.3 meter/minute.
  • Step 8 Conduct a final high temperature cure in air at 190° C. for 4 hours to form a capacitor laminate.
  • the capacitance of the capacitor laminates were measured using a standard ohmmeter.
  • the capacitive density was calculated by dividing the measured capacitance (C) by the area (A) of the sample.

Landscapes

  • Engineering & Computer Science (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Ceramic Engineering (AREA)
  • Power Engineering (AREA)
  • Textile Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Manufacturing & Machinery (AREA)
  • Chemical & Material Sciences (AREA)
  • Electromagnetism (AREA)
  • Thermal Sciences (AREA)
  • Laminated Bodies (AREA)
  • Fixed Capacitors And Capacitor Manufacturing Machines (AREA)
  • Reinforced Plastic Materials (AREA)
  • Nonwoven Fabrics (AREA)
US12/771,365 2009-05-01 2010-04-30 Passive electrical article Abandoned US20100279566A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US12/771,365 US20100279566A1 (en) 2009-05-01 2010-04-30 Passive electrical article
US15/207,719 US10399295B2 (en) 2009-05-01 2016-07-12 Passive electrical article

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US17466709P 2009-05-01 2009-05-01
US29541110P 2010-01-15 2010-01-15
US12/771,365 US20100279566A1 (en) 2009-05-01 2010-04-30 Passive electrical article

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/207,719 Division US10399295B2 (en) 2009-05-01 2016-07-12 Passive electrical article

Publications (1)

Publication Number Publication Date
US20100279566A1 true US20100279566A1 (en) 2010-11-04

Family

ID=43030734

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/771,365 Abandoned US20100279566A1 (en) 2009-05-01 2010-04-30 Passive electrical article
US15/207,719 Expired - Fee Related US10399295B2 (en) 2009-05-01 2016-07-12 Passive electrical article

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/207,719 Expired - Fee Related US10399295B2 (en) 2009-05-01 2016-07-12 Passive electrical article

Country Status (7)

Country Link
US (2) US20100279566A1 (enExample)
EP (1) EP2425691A4 (enExample)
JP (1) JP5732045B2 (enExample)
KR (1) KR101679896B1 (enExample)
CN (1) CN102461347B (enExample)
SG (1) SG175763A1 (enExample)
WO (1) WO2010127245A2 (enExample)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120199262A1 (en) * 2011-02-09 2012-08-09 Waukesha Electric Systems, Inc. Method of manufacturing a dry type electrical insulation
JP2015528756A (ja) * 2012-06-28 2015-10-01 スリーエム イノベイティブ プロパティズ カンパニー 熱伝導性基板物品
WO2021007274A1 (en) * 2019-07-08 2021-01-14 Vdi Llc Dielectric thin film coatings for unidirectional and bidirectional wavelength selective reflective color generation
US11452959B2 (en) * 2018-11-30 2022-09-27 Hollingsworth & Vose Company Filter media having a fine pore size distribution
US11566112B2 (en) * 2020-02-17 2023-01-31 Southwest University Of Science And Technology High-performance triple-crosslinked polymer and preparation method thereof
US11819789B2 (en) 2015-04-17 2023-11-21 Hollingsworth & Vose Company Stable filter media including nanofibers
US20250176097A1 (en) * 2023-11-27 2025-05-29 Nano And Advanced Materials Institute Limited Milliwave rf device based on flexible and deformable materials with low dielectric constant and dielectric loss

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013091197A1 (en) 2011-12-21 2013-06-27 3M Innovative Properties Company Resin composition and dielectric layer and capacitor produced therefrom
JP6414697B2 (ja) * 2015-09-25 2018-10-31 サムソン エレクトロ−メカニックス カンパニーリミテッド． プリプレグ及びその製造方法、及びこれを用いた印刷回路基板及びその製造方法
JP2021502493A (ja) * 2017-11-09 2021-01-28 オクトパス テクノロジーズ インコーポレイテッドＯｃｔｏｐｕｓ Ｔｅｃｈｎｏｌｏｇｉｅｓ Ｉｎｃ． 電解二酸化マンガン及びその調製方法
CN110978576B (zh) 2019-12-20 2021-09-10 江门市德众泰工程塑胶科技有限公司 一种液晶聚合物薄膜的制备方法
WO2024257396A1 (ja) * 2023-06-13 2024-12-19 株式会社村田製作所 積層フィルムおよび積層フィルムの製造方法

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5085928A (en) * 1989-04-06 1992-02-04 E. I. Dupont De Nemours And Company Fiber reinforced composites comprising uni-directional fiber layers and aramid spunlaced fabric layers
US5705534A (en) * 1995-09-22 1998-01-06 National Power Plc Method for the preparation of cation exchange membranes doped with insoluble metal salts
US6274224B1 (en) * 1999-02-01 2001-08-14 3M Innovative Properties Company Passive electrical article, circuit articles thereof, and circuit articles comprising a passive electrical article
US6323436B1 (en) * 1997-04-08 2001-11-27 International Business Machines Corporation High density printed wiring board possessing controlled coefficient of thermal expansion with thin film redistribution layer
US6399924B1 (en) * 2000-07-10 2002-06-04 Edward Zhihua Cai Cooktop hygiene device and method
US6473950B1 (en) * 1997-05-07 2002-11-05 Teijin Limited Method of manufacturing electronic component
US6608760B2 (en) * 1998-05-04 2003-08-19 Tpl, Inc. Dielectric material including particulate filler
US6657849B1 (en) * 2000-08-24 2003-12-02 Oak-Mitsui, Inc. Formation of an embedded capacitor plane using a thin dielectric
US20040106343A1 (en) * 2000-02-24 2004-06-03 Kris Senecal Conductive (electrical, ionic, and photoelectric) polymer membrane articles, and method for producing same
WO2007132708A1 (ja) * 2006-05-15 2007-11-22 Panasonic Corporation アルミ電解コンデンサ
US20080070463A1 (en) * 2006-09-20 2008-03-20 Pankaj Arora Nanowebs

Family Cites Families (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3878316A (en) * 1970-07-08 1975-04-15 Gaylord L Groff Laminate comprising non-woven fibrous backing
EP0062491B2 (en) * 1981-04-04 1991-12-11 National Research Development Corporation Polymers in matrix reinforcement
US4637851A (en) * 1985-01-25 1987-01-20 Shin-Etsu Chemical Co., Ltd. Method for the preparation of a laminate
JPH01205411A (ja) * 1988-02-10 1989-08-17 Matsushita Electric Works Ltd コンデンサ
AU2392592A (en) 1992-07-16 1994-02-14 Zycon Corporation Printed circuit board with internal capacitor
JPH06196357A (ja) * 1992-12-25 1994-07-15 Murata Mfg Co Ltd フィルムコンデンサ
US6229096B1 (en) 1997-10-07 2001-05-08 Mitsubishi Gas Chemical Company, Inc. Nonwoven reinforcement for printed wiring base board and process for producing the same
JP4224190B2 (ja) * 2000-06-20 2009-02-12 パナソニック電工株式会社 プリント配線板の製造方法及びプリント配線板
US7348045B2 (en) * 2002-09-05 2008-03-25 3M Innovative Properties Company Controlled depth etched dielectric film
US6730439B2 (en) 2000-08-01 2004-05-04 Tonen Tapyrus Co., Ltd. Heat-resistant separator
JP2002160317A (ja) * 2000-11-28 2002-06-04 Matsushita Electric Works Ltd 金属箔張り積層板の製造方法及び金属箔張り積層板
US6577492B2 (en) 2001-07-10 2003-06-10 3M Innovative Properties Company Capacitor having epoxy dielectric layer cured with aminophenylfluorenes
US6847527B2 (en) 2001-08-24 2005-01-25 3M Innovative Properties Company Interconnect module with reduced power distribution impedance
JP2003166191A (ja) 2001-11-22 2003-06-13 Mitsubishi Paper Mills Ltd 耐熱絶縁性不織布
JP2003188483A (ja) * 2001-12-20 2003-07-04 Kyocera Corp 配線基板用絶縁樹脂層およびそれを用いた配線基板
WO2003092342A1 (en) 2002-04-26 2003-11-06 E.I. Du Pont De Nemours And Company Low loss dielectric material for printed circuit boards and integrated circuit chip packaging
DE10313399A1 (de) 2002-05-27 2003-12-11 Hans-Juergen Schaefer Micorvia Conductor Prepreg-Layer zur Herstellung von HDI-Multilayern durch gemeinsame Verpressung von Einzellagen, von optoelektronischen und Chip in Polymer Schaltungselementen sowie Verfahren und Vorrichtung zu deren Herstellung
JP2004174730A (ja) * 2002-11-25 2004-06-24 Sumitomo Bakelite Co Ltd 積層板の連続製造方法
JP2004241647A (ja) * 2003-02-06 2004-08-26 Shin Kobe Electric Mach Co Ltd プリント配線板用長尺積層体及びその製造法
KR100463874B1 (ko) 2003-03-03 2004-12-30 김학용 문양을 갖는 나노섬유 부직포의 제조방법
JP2005187800A (ja) 2003-12-01 2005-07-14 Hitachi Chem Co Ltd 樹脂組成物、該樹脂組成物を用いたプリプレグ、金属張積層板及びプリント配線板
JP2005175265A (ja) * 2003-12-12 2005-06-30 Hitachi Chem Co Ltd 多層配線板用接着シート及び多層配線板の製造方法
JP4501475B2 (ja) 2004-03-17 2010-07-14 住友ベークライト株式会社 絶縁層付き金属箔及び多層プリント配線板
JP2004345355A (ja) 2004-06-25 2004-12-09 Sumitomo Chemical Co Ltd 積層体の製造方法
KR100619367B1 (ko) 2004-08-26 2006-09-08 삼성전기주식회사 고유전율을 갖는 커패시터를 내장한 인쇄회로기판 및 그제조 방법
JP2006107770A (ja) * 2004-09-30 2006-04-20 Sumitomo Bakelite Co Ltd 誘電体ペースト、キャパシタおよび基板
JP4771702B2 (ja) * 2005-01-07 2011-09-14 旭化成イーマテリアルズ株式会社 補強材を有する高分子固体電解質膜
KR100722626B1 (ko) 2005-05-10 2007-05-28 삼성전기주식회사 인쇄회로기판용 수지적층판 및 그 제조방법
US7524388B2 (en) 2005-05-10 2009-04-28 World Properties, Inc. Composites, method of manufacture thereof, and articles formed therefrom
JP2006316171A (ja) 2005-05-12 2006-11-24 Shin Kobe Electric Mach Co Ltd プリプレグ、積層板及び多層積層板
US20060286696A1 (en) 2005-06-21 2006-12-21 Peiffer Joel S Passive electrical article
JP4852292B2 (ja) * 2005-10-17 2012-01-11 京セラケミカル株式会社 銅張り積層板
JP4260789B2 (ja) * 2005-10-31 2009-04-30 日本ピラー工業株式会社 プリント基板をミリメートル波帯域通信に使用する方法
JP4974609B2 (ja) * 2006-08-22 2012-07-11 旭化成イーマテリアルズ株式会社 フィルム状電子機器用部材
JP5130011B2 (ja) * 2007-09-21 2013-01-30 株式会社クラレ セパレータの製造方法

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5085928A (en) * 1989-04-06 1992-02-04 E. I. Dupont De Nemours And Company Fiber reinforced composites comprising uni-directional fiber layers and aramid spunlaced fabric layers
US5705534A (en) * 1995-09-22 1998-01-06 National Power Plc Method for the preparation of cation exchange membranes doped with insoluble metal salts
US6323436B1 (en) * 1997-04-08 2001-11-27 International Business Machines Corporation High density printed wiring board possessing controlled coefficient of thermal expansion with thin film redistribution layer
US6473950B1 (en) * 1997-05-07 2002-11-05 Teijin Limited Method of manufacturing electronic component
US6608760B2 (en) * 1998-05-04 2003-08-19 Tpl, Inc. Dielectric material including particulate filler
US6274224B1 (en) * 1999-02-01 2001-08-14 3M Innovative Properties Company Passive electrical article, circuit articles thereof, and circuit articles comprising a passive electrical article
US20040106343A1 (en) * 2000-02-24 2004-06-03 Kris Senecal Conductive (electrical, ionic, and photoelectric) polymer membrane articles, and method for producing same
US6399924B1 (en) * 2000-07-10 2002-06-04 Edward Zhihua Cai Cooktop hygiene device and method
US6657849B1 (en) * 2000-08-24 2003-12-02 Oak-Mitsui, Inc. Formation of an embedded capacitor plane using a thin dielectric
WO2007132708A1 (ja) * 2006-05-15 2007-11-22 Panasonic Corporation アルミ電解コンデンサ
US7990681B2 (en) * 2006-05-15 2011-08-02 Panasonic Corporation Aluminum electrolytic capacitor
US20080070463A1 (en) * 2006-09-20 2008-03-20 Pankaj Arora Nanowebs

Non-Patent Citations (6)

* Cited by examiner, † Cited by third party
Title
Definition "Aramid" (Aromatic Polyamide), Wikipedia, https://en.wikipedia.org/wiki/Aramid, 3/11/2016. *
Definition of "cross-link" Merriam-Webster Dictionary, www.merriam-webster.com/dictionary/cross-link, no date. *
Definition of "Liquid crystal polymer" Wikipedia, https://en.wikipedia.org/wiki/Liquid_crystal_polymer, 9/21/2015. *
Definition of "Thermosetting polymer" Wikipedia, https://en.wikipedia.org/wiki/Thermosetting_polymer, 3/21/2016. *
Modern Armour From Chemistry, www.scienceshorts.com/Ssw/050604.htm, no date. *
Polyclad Technical Data Sheet, downloaded 11/13/2013. *

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120199262A1 (en) * 2011-02-09 2012-08-09 Waukesha Electric Systems, Inc. Method of manufacturing a dry type electrical insulation
US9362020B2 (en) * 2011-02-09 2016-06-07 Waukesha Electric Systems, Inc. Method of manufacturing a dry type electrical insulation
JP2015528756A (ja) * 2012-06-28 2015-10-01 スリーエム イノベイティブ プロパティズ カンパニー 熱伝導性基板物品
US10568233B2 (en) 2012-06-28 2020-02-18 3M Innovative Properties Company Thermally conductive substrate article
US11819789B2 (en) 2015-04-17 2023-11-21 Hollingsworth & Vose Company Stable filter media including nanofibers
US11452959B2 (en) * 2018-11-30 2022-09-27 Hollingsworth & Vose Company Filter media having a fine pore size distribution
US11890561B2 (en) * 2018-11-30 2024-02-06 Hollingsworth & Vose Company Filter media having a fine pore size distribution
WO2021007274A1 (en) * 2019-07-08 2021-01-14 Vdi Llc Dielectric thin film coatings for unidirectional and bidirectional wavelength selective reflective color generation
US11364708B2 (en) 2019-07-08 2022-06-21 Vdi Llc Dielectric thin film coatings for unidirectional and bidirectional wavelength selective reflective color generation
US11566112B2 (en) * 2020-02-17 2023-01-31 Southwest University Of Science And Technology High-performance triple-crosslinked polymer and preparation method thereof
US20250176097A1 (en) * 2023-11-27 2025-05-29 Nano And Advanced Materials Institute Limited Milliwave rf device based on flexible and deformable materials with low dielectric constant and dielectric loss

Also Published As

Publication number Publication date
KR101679896B1 (ko) 2016-11-25
CN102461347A (zh) 2012-05-16
US20160318279A1 (en) 2016-11-03
CN102461347B (zh) 2016-03-16
EP2425691A2 (en) 2012-03-07
JP5732045B2 (ja) 2015-06-10
WO2010127245A2 (en) 2010-11-04
US10399295B2 (en) 2019-09-03
WO2010127245A3 (en) 2011-02-03
SG175763A1 (en) 2011-12-29
KR20120005042A (ko) 2012-01-13
JP2012525719A (ja) 2012-10-22
EP2425691A4 (en) 2013-09-04

Similar Documents

Publication Publication Date Title
US10399295B2 (en) Passive electrical article
US6274224B1 (en) Passive electrical article, circuit articles thereof, and circuit articles comprising a passive electrical article
US20100105806A1 (en) Passive electrical article
US20060286696A1 (en) Passive electrical article
TW202007526A (zh) 高頻銅箔基板及其製法
TWI321975B (en) Resin composition and adhesive film for multi-layered printed wiring board
TW201543983A (zh) 具有保護層之貼銅積層板及多層印刷配線板
CN106031316A (zh) 内置电容器层形成用覆铜层压板、多层印刷线路板以及多层印刷线路板的制造方法
EP1407463A2 (en) Capacitor having epoxy dielectric layer cured with aminophenylfluorenes
US10568233B2 (en) Thermally conductive substrate article
JP2008227153A (ja) キャパシタ内蔵多層プリント配線板用誘電体材料，キャパシタ部材とキャパシタ内蔵多層プリント配線板およびキャパシタ内蔵多層プリント配線板の製造方法
TWI521003B (zh) 樹脂組合物及其應用
US20120141777A1 (en) Laminate composed of ceramic insulating layer and metal layer, and method for producing the same
JP2003200526A (ja) プリント配線板製造用材料及びプリント配線板及びその製造方法
JPS6381998A (ja) Ｉｃチツプ搭載用多層板の製造法
JP2005044940A (ja) プリント基板用基材

Legal Events

Date Code Title Description
AS Assignment

Owner name: 3M INNOVATIVE PROPERTIES COMPANY, MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YANG, RUI;MAO, GUOPING;GHOSH, DIPANKAR;AND OTHERS;SIGNING DATES FROM 20100603 TO 20100615;REEL/FRAME:024536/0160

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION