US20080089801A1 - Iron-Based Powder Combination - Google Patents
Iron-Based Powder Combination Download PDFInfo
- Publication number
- US20080089801A1 US20080089801A1 US11/794,500 US79450006A US2008089801A1 US 20080089801 A1 US20080089801 A1 US 20080089801A1 US 79450006 A US79450006 A US 79450006A US 2008089801 A1 US2008089801 A1 US 2008089801A1
- Authority
- US
- United States
- Prior art keywords
- powder
- weight
- iron
- alloyed
- molybdenum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C33/00—Making ferrous alloys
- C22C33/02—Making ferrous alloys by powder metallurgy
- C22C33/0207—Using a mixture of prealloyed powders or a master alloy
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C33/00—Making ferrous alloys
- C22C33/02—Making ferrous alloys by powder metallurgy
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F1/00—Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
Definitions
- the present invention refers to iron-based powder metallurgical combinations and to methods for preparing sintered powder metallurgical components therefrom. More specifically the invention refers to the production of sintered components including copper, nickel and molybdenum by using these combinations.
- Sintered iron-based components can be produced by mixing alloying elements with the pure iron powders. However, this may cause problems with dust and segregation which may lead to variations in size and mechanical properties of the sintered component.
- the alloying elements may be pre-alloyed or diffusion alloyed with the iron powder. In one method molybdenum is pre-alloyed with iron powder and this pre-alloyed iron powder is subsequently diffusion alloyed with copper and nickel for production of sintered components from iron-based powder compositions containing molybdenum, nickel and copper.
- the present invention provides a method of eliminating the need of producing a specific powder for each desired chemical composition of the sintered iron-based component having alloying elements from molybdenum, copper and nickel.
- the invention also offers the advantage of providing a method for controlling the dimensional change and the tensile strength to predetermined values.
- the dimensional change is independent of the carbon content and the density.
- the invention concerns a powder metallurgical combination of three different iron-based powders.
- the first of these iron-based powders consisting of core particles of iron, pre-alloyed with molybdenum, which is additionally diffusion alloyed with copper and the second iron-based powder consisting of core particles of iron, pre-alloyed with molybdenum, which is diffusion alloyed with nickel.
- the third iron-based powder essentially consists of particles of iron pre-alloyed with molybdenum.
- the invention also concerns the two diffusion alloyed iron-based powders.
- a method according to the invention comprises the steps of combining these three iron-based powders in predetermined amounts, mixing the combination with graphite, compacting the obtained mixture and sintering the obtained green body.
- Another aspect of the invention concerns a method of providing a sintered component having a predetermined strength and a predetermined dimensional change during sintering.
- FIG. 1-4 illustrate diagrams for determining the copper and nickel content in the powder metallurgical combination for a predetermined strength and dimensional change.
- iron-based powder metallurgical combination according to the invention comprises:
- the amount of pre-alloyed molybdenum in the particles in the iron-based powders A, B and C, respectively, may vary between 0.3-2% by weight, preferably 0.5 and 1.5% by weight. In one embodiment the particles in all three powders are pre-alloyed with the same amount of molybdenum. Amounts above 2% of Mo does not give an increase of the strength justifying the increase of the costs. Amounts of Mo below 0.3% does not give a significant effect of the strength.
- the amount of copper and nickel which is diffusion alloyed to the core particles is limited in the upper range to 15% copper and 12% nickel.
- the lower limit of copper and nickel which is diffusion alloyed to the core particles should be substantially higher than the amount required in the sintered component to achieve the advantages of the invention.
- an iron-based powder essentially consisting of core particles pre-alloyed with molybdenum and comprising at least 6% copper diffusion alloyed to the core particles and an iron-based powder having core particles pre-alloyed with molybdenum and comprising at least 4.5% nickel diffusion alloyed to the core particles are of special interest.
- the powders A, B and C essentially consist of particles of iron pre-alloyed with molybdenum, but other elements, except unavoidable impurities, may be pre-alloyed to the particles.
- Such elements may be nickel, copper, chromium and manganese.
- the respective amounts of powder A, B and C are determined and mixed with graphite in the amount required for the predetermined strength.
- the obtained mixture may be mixed with other additives before compaction and sintering.
- the amount of graphite which is mixed in the powder combination is up to 1%, preferably 0.3-0.7%.
- additives are selected from the group consisting of lubricants, binders, other alloying elements, hard phase materials, machinability enhancing agents.
- powder C is essentially free from Cu and Ni.
- the relation between powder A, B and C is preferably chosen so that the copper content will be 0.2-2% by weight, the nickel content will be 0.1-4% by weight and the molybdenum content will be 0.3-2% by weight, preferably 0.5-1.5% by weight of the sintered component.
- the copper content is 0.2-2%, preferably 0.4-0.8% and the nickel content is 0.1-4%. It has unexpectedly been found that in this particular embodiment the dimensional change during sintering is independent of the carbon content and sintered density.
- the amounts of copper, nickel and carbon, respectively, in the sintered component is determined by means of diagrams, e.g. from FIG. 1-4 .
- the required amounts of powder A, B and C, respectively, may then be determined by a person skilled in the art.
- the powders are mixed with graphite to obtain the final desired carbon content.
- the powder combination is compacted at a compaction pressure between 400-1000 MPa and the obtained green body is sintered at 1100-1300° C. for 10-60 minutes in a protective atmosphere.
- the sintered body may be subjected to further post treatments, such as heat treatment, surface densification, machining etc.
- the exemplifying diagrams in FIG. 1-4 are valid at a compaction pressure of 600 MPa, sintered at 1120° C. for 30 minutes in an atmosphere of 90% nitrogen and 10% of hydrogen.
- sintered components containing various amounts of molybdenum, copper and nickel may be produced. This is achieved by using a combination of three different powders, which are mixed in different proportions to achieve a powder having the required chemical composition for the actual sintered component.
- a particular advantage of the invention is that the dimensional change during sintering as well as the strength of the sintered component can be controlled.
- the advantage of being able to control the dimensional change will facilitate the use of existing pressing tools.
- a certain scatter in carbon content and density may be unavoidable.
- the scatter in dimensions after sintering will be reduced hence subsequent machining and machining costs can be decreased.
- This example demonstrates how to choose an alloying composition having a desired strength of about 600 MPa and three levels of dimensional change ( ⁇ 0.1%, 0.0% and +0.1%). This was done for two carbon levels, 0.5% C and 0.3% C, respectively, in the powder combinations according to table 1, where the lower carbon content yields better ductility as can be seen in table 2.
- the powder combinations according to the present invention were prepared from a powder A with 10% of copper diffusion alloyed to the surface of an iron-based powder pre-alloyed with 0.85% of molybdenum, a powder B with 5% of nickel diffusion alloyed to the surface of an iron-based powder pre-alloyed with 0.85% of molybdenum and a powder C of an iron-based powder pre-alloyed with 0.85% of molybdenum.
- the powder combinations were mixed with 0.8% amide wax as a lubricant and graphite, to yield a sintered carbon content of 0.3% and 0.5%, respectively.
- the obtained mixtures were compacted to tensile test specimen according to ISO 2740.
- the compaction pressure was 600 MPa and the sintering conditions were: 1120° C., 30 min, 90% N 2 /10% H 2 .
- table 2 other mechanical properties from the powder combinations according to the invention are presented. It can be clearly seen that the powder combinations according to the invention have the predetermined dimensional change according to FIG. 3 .
- Powder combination (1) 0.6 1.3 0.83 0.5 7.08 ⁇ 0.104 Powder combination (2) 1.15 0.8 0.83 0.5 7.06 0.004 Powder combination (3) 1.55 0.4 0.83 0.5 7.04 0.096 Powder combination (4) 0.9 2.3 0.83 0.3 7.11 ⁇ 0.096 Powder combination (5) 1.3 2 0.83 0.3 7.09 0.007 Powder combination (6) 1.6 1.7 0.83 0.3 7.07 0.095
- This example illustrates powder combinations according to the invention, comprising 0.6% Cu and 2% Ni and a specific embodiment having dimensional change independent of carbon content and sintered density as shown in table 3.
- the results obtained with these combinations are compared with the results obtained with Distaloy AB (available from Höganäs AB, Sweden) as well as with a powder having the same chemical composition as the powder combination according to the invention but wherein iron-based powder pre-alloyed with molybdenum has both copper and nickel diffusion alloyed to the surface, in table 3 designated as “fixed composition”.
- the powder combinations according to the present invention were prepared from a powder A with 10% of copper diffusion alloyed to the surface of an iron-based powder pre-alloyed with 0.85% of molybdenum, a powder B with 5% of nickel diffusion alloyed to the surface of an iron-based powder pre-alloyed with 0.85% of molybdenum and a powder C consisting of an iron-based powder pre-alloyed with 0.85% of molybdenum.
- Table 3 shows a specific example where a mixture of powder A, powder B and powder C having a total content of 0.6% copper, 2% of nickel and 0.83% of molybdenum is compared with a known powder, Distaloy AB, and an iron-based powder having 0.83% of pre-alloyed molybdenum, 0.6% of copper and 2% of nickel diffusion alloyed to the surface of the iron-based powder.
- the dimensional change of sintered samples, produced from the powder combination according to the invention is essentially independent of the carbon content and density compared with the known powder Distaloy AB or the iron-based powder diffusion alloyed with both copper and nickel.
- the powder combinations were mixed with 0.8% amide wax as a lubricant and graphite, to yield a sintered carbon content according to table 3.
- the obtained mixture were compacted to tensile test specimen according to ISO 2740 at different compaction pressures according to table 3.
- the tensile test specimen were sintered at 1120° C. for 30 minutes in an atmosphere of 90% nitrogen and 10% of hydrogen.
- table 4 further mechanical properties are presented.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Powder Metallurgy (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE0500261-3 | 2005-02-04 | ||
SE0500261 | 2005-02-04 | ||
PCT/SE2006/000080 WO2006083206A1 (en) | 2005-02-04 | 2006-01-20 | Iron-based powder combination |
Publications (1)
Publication Number | Publication Date |
---|---|
US20080089801A1 true US20080089801A1 (en) | 2008-04-17 |
Family
ID=36777515
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/794,500 Abandoned US20080089801A1 (en) | 2005-02-04 | 2006-01-20 | Iron-Based Powder Combination |
Country Status (12)
Country | Link |
---|---|
US (1) | US20080089801A1 (ko) |
EP (1) | EP1844172B1 (ko) |
JP (1) | JP5108531B2 (ko) |
KR (1) | KR100970796B1 (ko) |
CN (1) | CN100532606C (ko) |
BR (1) | BRPI0607356A2 (ko) |
CA (1) | CA2595905A1 (ko) |
MX (1) | MX2007009531A (ko) |
RU (1) | RU2366537C2 (ko) |
TW (1) | TWI325896B (ko) |
WO (1) | WO2006083206A1 (ko) |
ZA (1) | ZA200705662B (ko) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100233014A1 (en) * | 2007-07-17 | 2010-09-16 | Hoganas Ab (Publ) | Iron-based powder combination |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR100992713B1 (ko) | 2007-10-04 | 2010-11-05 | 기아자동차주식회사 | 전동식 조향컬럼 잠금장치의 데드 록 장치 |
RU2524510C2 (ru) * | 2008-12-23 | 2014-07-27 | Хеганес Аб (Пабл) | Способ получения диффузионно-легированного порошка железа или порошка на основе железа, диффузионно-легированный порошок, композиция, включающая диффузионно-легированный порошок, и прессованная и спеченная деталь, изготовленная из упомянутой композиции |
BR112013025725B1 (pt) * | 2011-04-06 | 2019-09-03 | Hoeganaes Corp | composição de pó metalúrgico, peça compactada e aditivo para preparar a composição de pó metalúrgico |
CN105344992A (zh) * | 2015-11-19 | 2016-02-24 | 苏州紫光伟业激光科技有限公司 | 一种冶金粉末组合物 |
DE102018209682A1 (de) * | 2018-06-15 | 2019-12-19 | Mahle International Gmbh | Verfahren zum Herstellen eines pulvermetallurgischen Erzeugnisses |
US11939646B2 (en) | 2018-10-26 | 2024-03-26 | Oerlikon Metco (Us) Inc. | Corrosion and wear resistant nickel based alloys |
RU2701232C1 (ru) * | 2018-12-12 | 2019-09-25 | Публичное акционерное общество "Северсталь" | Способ получения легированной порошковой смеси для изготовления порошковых конструкционных деталей ответственного назначения |
KR20210029582A (ko) | 2019-09-06 | 2021-03-16 | 현대자동차주식회사 | 철계 예합금 분말, 철계 확산접합 분말 및 이를 이용하는 분말야금용 철계 합금 분말 |
KR20210104418A (ko) * | 2020-02-17 | 2021-08-25 | 현대자동차주식회사 | 가변 오일 펌프용 아우터링 및 이의 제조방법 |
CN116024483B (zh) * | 2022-12-30 | 2023-09-15 | 江苏群达机械科技有限公司 | 一种低合金高强度的Cr-Mo钢材料及其制备方法 |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4069044A (en) * | 1976-08-06 | 1978-01-17 | Stanislaw Mocarski | Method of producing a forged article from prealloyed-premixed water atomized ferrous alloy powder |
US5567890A (en) * | 1991-06-12 | 1996-10-22 | Hoganas Ab | Iron-based powder composition having good dimensional stability after sintering |
US6613122B1 (en) * | 1998-10-16 | 2003-09-02 | Eurotungstene Poudres | Micronic pre-alloyed metal powder based on three-dimensional transition metal |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1305608A (ko) | 1970-03-18 | 1973-02-07 | ||
JPS54104406A (en) * | 1978-02-06 | 1979-08-16 | Toyo Kohan Co Ltd | Production of high temperature abrasion resistant sintered alloy steel |
JPS5594401A (en) * | 1979-01-09 | 1980-07-17 | Daido Steel Co Ltd | Stainless steel powder |
JPS59215401A (ja) * | 1983-05-19 | 1984-12-05 | Kawasaki Steel Corp | 粉末冶金用合金鋼粉およびその製造方法 |
JPS61130401A (ja) * | 1984-11-28 | 1986-06-18 | Kawasaki Steel Corp | 粉末冶金用合金鋼粉およびその製造方法 |
JPS61183444A (ja) * | 1985-02-08 | 1986-08-16 | Toyota Motor Corp | 高強度焼結合金及びその製造方法 |
JPS61253342A (ja) * | 1985-04-30 | 1986-11-11 | Fuji Electric Co Ltd | 焼結ステンレス鋼の製造方法 |
JPH0745683B2 (ja) * | 1987-09-30 | 1995-05-17 | 川崎製鉄株式会社 | 圧縮性および均質性に優れる複合鋼粉 |
JPH01165702A (ja) * | 1987-12-23 | 1989-06-29 | Kawasaki Steel Corp | 高密度および高強度の合金鋼焼結体の製造方法 |
JPH01312056A (ja) * | 1988-06-09 | 1989-12-15 | Kawasaki Steel Corp | 高密度高強度合金鋼焼結体の製造方法 |
DE3942091C1 (ko) * | 1989-12-20 | 1991-08-14 | Etablissement Supervis, Vaduz, Li | |
JPH04297502A (ja) * | 1991-03-25 | 1992-10-21 | Kawasaki Steel Corp | Ni含有鉄系焼結材料の製造方法 |
JPH0681001A (ja) * | 1992-09-02 | 1994-03-22 | Kawasaki Steel Corp | 合金鋼粉 |
JP3351844B2 (ja) * | 1993-03-01 | 2002-12-03 | 川崎製鉄株式会社 | 鉄系焼結材料用の合金鋼粉及びその製造方法 |
JPH07233402A (ja) * | 1993-12-28 | 1995-09-05 | Kawasaki Steel Corp | 切削性、耐摩耗性に優れたアトマイズ鋼粉およびその焼結鋼 |
JP3446322B2 (ja) * | 1994-08-03 | 2003-09-16 | Jfeスチール株式会社 | 粉末冶金用合金鋼粉 |
JP3475545B2 (ja) * | 1995-02-08 | 2003-12-08 | Jfeスチール株式会社 | 粉末冶金用混合鋼粉及びそれを含む焼結用材料 |
SE0201824D0 (sv) * | 2002-06-14 | 2002-06-14 | Hoeganaes Ab | Pre-alloyed iron based powder |
SE0203135D0 (sv) * | 2002-10-23 | 2002-10-23 | Hoeganaes Ab | Dimensional control |
JP2004292861A (ja) * | 2003-03-26 | 2004-10-21 | Jfe Steel Kk | 粉末冶金用鉄基混合粉およびその製造方法 |
-
2006
- 2006-01-09 TW TW095100709A patent/TWI325896B/zh not_active IP Right Cessation
- 2006-01-20 KR KR1020077020100A patent/KR100970796B1/ko active IP Right Grant
- 2006-01-20 CN CNB2006800033070A patent/CN100532606C/zh active Active
- 2006-01-20 EP EP06701553.7A patent/EP1844172B1/en active Active
- 2006-01-20 WO PCT/SE2006/000080 patent/WO2006083206A1/en active Application Filing
- 2006-01-20 BR BRPI0607356-5A patent/BRPI0607356A2/pt not_active IP Right Cessation
- 2006-01-20 JP JP2007554043A patent/JP5108531B2/ja active Active
- 2006-01-20 US US11/794,500 patent/US20080089801A1/en not_active Abandoned
- 2006-01-20 MX MX2007009531A patent/MX2007009531A/es active IP Right Grant
- 2006-01-20 CA CA002595905A patent/CA2595905A1/en not_active Abandoned
- 2006-01-20 ZA ZA200705662A patent/ZA200705662B/xx unknown
- 2006-01-20 RU RU2007133101/02A patent/RU2366537C2/ru not_active IP Right Cessation
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4069044A (en) * | 1976-08-06 | 1978-01-17 | Stanislaw Mocarski | Method of producing a forged article from prealloyed-premixed water atomized ferrous alloy powder |
US5567890A (en) * | 1991-06-12 | 1996-10-22 | Hoganas Ab | Iron-based powder composition having good dimensional stability after sintering |
US6613122B1 (en) * | 1998-10-16 | 2003-09-02 | Eurotungstene Poudres | Micronic pre-alloyed metal powder based on three-dimensional transition metal |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100233014A1 (en) * | 2007-07-17 | 2010-09-16 | Hoganas Ab (Publ) | Iron-based powder combination |
US8858675B2 (en) | 2007-07-17 | 2014-10-14 | Hoganas Ab (Publ) | Iron-based powder combination |
Also Published As
Publication number | Publication date |
---|---|
BRPI0607356A2 (pt) | 2009-09-01 |
WO2006083206A1 (en) | 2006-08-10 |
RU2366537C2 (ru) | 2009-09-10 |
JP5108531B2 (ja) | 2012-12-26 |
EP1844172A1 (en) | 2007-10-17 |
JP2008528811A (ja) | 2008-07-31 |
RU2007133101A (ru) | 2009-03-10 |
CA2595905A1 (en) | 2006-08-10 |
KR100970796B1 (ko) | 2010-07-16 |
EP1844172B1 (en) | 2019-07-03 |
TW200632111A (en) | 2006-09-16 |
TWI325896B (en) | 2010-06-11 |
CN100532606C (zh) | 2009-08-26 |
CN101111617A (zh) | 2008-01-23 |
KR20070099690A (ko) | 2007-10-09 |
MX2007009531A (es) | 2008-02-12 |
EP1844172A4 (en) | 2010-07-21 |
ZA200705662B (en) | 2009-01-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20080089801A1 (en) | Iron-Based Powder Combination | |
EP2176019B1 (en) | Iron-based powder combination and process for producing it | |
EP0331679B1 (en) | High density sintered ferrous alloys | |
KR20110099336A (ko) | 확산 합금된 철 또는 철계 파우더, 확산 합금 파우더, 확산 합금된 파우더를 포함한 조성물을 생산하기 위한 방법, 및 상기 조성물로부터 생산된 압축되고 소결된 부품 | |
US8287615B2 (en) | High-strength composition iron powder and sintered part made therefrom | |
KR20160045825A (ko) | 분말 야금용 합금 강분 및 철기 소결체의 제조 방법 | |
JP7395635B2 (ja) | 鉄基粉末 | |
KR20170094321A (ko) | 분말야금용 철계 합금 분말 및 소결단조부재 | |
US6261514B1 (en) | Method of preparing sintered products having high tensile strength and high impact strength | |
US7329380B2 (en) | Method of controlling the dimensional change when sintering an iron-based powder mixture | |
JP4121383B2 (ja) | 寸法精度、強度および摺動特性に優れた鉄基燒結合金およびその製造方法 | |
CA2495697A1 (en) | Method of preparing iron-based components by compaction with elevated pressures | |
JP4839271B2 (ja) | 粉末冶金用混合粉末および鉄粉焼結体 | |
US6551373B2 (en) | Copper infiltrated ferro-phosphorous powder metal | |
US6652618B1 (en) | Iron based mixed power high strength sintered parts | |
WO2021044869A1 (ja) | 粉末冶金用鉄基予合金粉末、粉末冶金用拡散接合粉末、粉末冶金用鉄基合金粉末、および焼結鍛造部材 | |
EP0157750A2 (en) | Material for the powder metallurgical manufacture of soft magnetic components | |
JPS5819722B2 (ja) | コウミツドシヨウケツコウ ノ セイゾウホウホウ | |
JP5119006B2 (ja) | 粉末冶金用混合粉末および鉄粉焼結体 | |
KR20240095297A (ko) | 분말 야금용 철기 혼합분 및 철기 소결체 | |
JPH09118965A (ja) | 疲労強度に優れた鉄基焼結合金 | |
JPH1072647A (ja) | 耐摩耗性に優れた高強度鉄基焼結合金およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: HOGANAS AB, SWEDEN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:LARSSON, MATS;REEL/FRAME:019959/0184 Effective date: 20070928 |
|
STCB | Information on status: application discontinuation |