US20070079908A1 - Titanium boride - Google Patents
Titanium boride Download PDFInfo
- Publication number
- US20070079908A1 US20070079908A1 US11/544,820 US54482006A US2007079908A1 US 20070079908 A1 US20070079908 A1 US 20070079908A1 US 54482006 A US54482006 A US 54482006A US 2007079908 A1 US2007079908 A1 US 2007079908A1
- Authority
- US
- United States
- Prior art keywords
- titanium
- powder
- alloy
- boride
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F9/00—Making metallic powder or suspensions thereof
- B22F9/16—Making metallic powder or suspensions thereof using chemical processes
- B22F9/18—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds
- B22F9/28—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds starting from gaseous metal compounds
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
- B22F3/02—Compacting only
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F3/00—Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
- B22F3/10—Sintering only
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22F—WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- B22F9/00—Making metallic powder or suspensions thereof
- B22F9/16—Making metallic powder or suspensions thereof using chemical processes
- B22F9/18—Making metallic powder or suspensions thereof using chemical processes with reduction of metal compounds
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
- C22B34/00—Obtaining refractory metals
- C22B34/10—Obtaining titanium, zirconium or hafnium
- C22B34/12—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08
- C22B34/1263—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08 obtaining metallic titanium from titanium compounds, e.g. by reduction
- C22B34/1268—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08 obtaining metallic titanium from titanium compounds, e.g. by reduction using alkali or alkaline-earth metals or amalgams
- C22B34/1272—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08 obtaining metallic titanium from titanium compounds, e.g. by reduction using alkali or alkaline-earth metals or amalgams reduction of titanium halides, e.g. Kroll process
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22B—PRODUCTION AND REFINING OF METALS; PRETREATMENT OF RAW MATERIALS
- C22B34/00—Obtaining refractory metals
- C22B34/10—Obtaining titanium, zirconium or hafnium
- C22B34/12—Obtaining titanium or titanium compounds from ores or scrap by metallurgical processing; preparation of titanium compounds from other titanium compounds see C01G23/00 - C01G23/08
- C22B34/1295—Refining, melting, remelting, working up of titanium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C14/00—Alloys based on titanium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C32/00—Non-ferrous alloys containing at least 5% by weight but less than 50% by weight of oxides, carbides, borides, nitrides, silicides or other metal compounds, e.g. oxynitrides, sulfides, whether added as such or formed in situ
- C22C32/0047—Non-ferrous alloys containing at least 5% by weight but less than 50% by weight of oxides, carbides, borides, nitrides, silicides or other metal compounds, e.g. oxynitrides, sulfides, whether added as such or formed in situ with carbides, nitrides, borides or silicides as the main non-metallic constituents
- C22C32/0073—Non-ferrous alloys containing at least 5% by weight but less than 50% by weight of oxides, carbides, borides, nitrides, silicides or other metal compounds, e.g. oxynitrides, sulfides, whether added as such or formed in situ with carbides, nitrides, borides or silicides as the main non-metallic constituents only borides
Definitions
- Relatively small boron additions to conventional titanium alloys provide important improvements in strength, stiffness and microstructural stability. Because boron is essentially insoluble in titanium at all temperatures of interest, the titanium boride is formed for even very small boron additions. The density of titanium boride is nearly equal to those of conventional Ti alloys, but its stiffness is over four times higher than conventional titanium alloys. Thus, titanium boride offers significant improvements in stiffness, tensile strength, creep, and fatigue properties. Since titanium boride is in thermodynamic equilibrium with titanium alloys, there are no interfacial reactions to degrade properties at elevated temperature.
- Negatives of the blended elemental approach are the added effort to blend the powders to obtain a uniform distribution (which is never perfect) and the added time and temperature it takes the solid state reaction to transform TiB 2 to TiB (1300 C for 6 hours). Also, this approach has the potential to form larger Titanium boride particles or have residual titanium boride particles that adversely affect properties.
- the titanium boride whiskers that are formed can lead to anisotropic properties of the part depending on the type of process used to make the part.
- a negative of the pre-alloyed approach is that it has a tendency to leave large primary borides in the pre-alloyed materials that cause low fracture toughness.
- the Armstrong Process as disclosed in U.S. Pat. Nos. 5,779,761, 5,958,106 and 6,409,797, the entire disclosures of which are herein incorporated by reference appears very unexpectedly to give uniform distribution of very fine submicron titanium boride within the Ti or Ti alloy powder. This eliminates the need for blending and solid state reaction to form titanium boride; it also eliminates concerns regarding larger particles that can adversely affect fracture toughness and other mechanical properties. Because of the fineness of the titanium boride particles and the uniform distribution in most if not substantially all of the particles forming the powder, more isotropic mechanical properties may be achievable. None of the current approaches to boron addition to Ti powder can achieve this type of distribution of titanium boride, particularly in the submicron size ranges.
- Another object of the invention is to provide a Ti powder or a Ti base alloy powder having submicron titanium boride substantially uniformly dispersed therein, wherein the Ti powder or Ti base alloy powder and titanium boride are made by the subsurface reduction of TiCl 4 and a boron halide and other chlorides and/or halides of the Ti base alloy constituents, if present, with liquid alkali or alkaline earth metal or mixtures thereof in a reaction zone.
- a further object of the invention is to provide a Ti powder or a Ti base alloy powder having submicron titanium boride which is other than whisker-shaped or spherical substantially uniformly dispersed therein.
- a final object of the invention is to provide a product having an SEM substantially as shown in one or more of FIGS. 1-8 .
- FIG. 1 is an SEM of a titanium powder having submicron titanium boride substantially uniformly dispersed therethrough at a magnification of 50;
- FIG. 2 is another SEM of a titanium powder having submicron titanium boride substantially uniformly dispersed therethrough at a magnification of 50;
- FIG. 3 is a similar SEM of a titanium powder having submicron titanium boride substantially uniformly dispersed therethrough at a magnification of 3000;
- FIG. 4 is another SEM of a titanium powder having submicron titanium boride substantially uniformly dispersed therethrough at a magnification of 3000;
- FIG. 5 is a titanium base alloy having about 10% total of aluminum and vanadium with titanium boride with submicron titanium borides substantially uniformly dispersed throughout the particles forming the powder at a 40 magnification;
- FIG. 6 is a titanium base alloy having about 10% total of aluminum and vanadium with titanium boride with submicron titanium borides substantially uniformly dispersed throughout the particles forming the powder at a 50 magnification;
- FIG. 8 is a titanium base alloy having about 10% total of aluminum and vanadium with titanium boride with submicron titanium borides substantially uniformly dispersed throughout the particles forming the powder at a 3000 magnification (a different portion of the same sample as FIG. 7 ).
- the equipment used to produce the 6/4 alloy with submicron titanium boride substantially uniformly dispersed therein is similar to that disclosed in the aforementioned patents disclosing the Armstrong Process with the exception that instead of only having a titanium tetrachloride boiler 22 as illustrated in those patents, there is also a boiler for each constituent of the alloy connected to the reaction chamber by suitable valves. Boron addition is from a boiler for BCl 3 .
- the piping acts as a manifold so that the gases are completely mixed as they enter the reaction chamber and are introduced subsurface to the flowing liquid sodium, preferably at least at sonic velocity, as disclosed in the incorporated patents.
- the halides Upon subsurface contact with the liquid metal the halides immediately and completely react exothermically to form a reaction zone in which the reaction products are produced.
- the flowing liquid metal preferably sodium, sweeps the reaction products away from the reaction zone maintaining the reaction products at a temperature below the sintering temperatures of the reaction products. It was determined during production of the 6/4 alloy that aluminum trichloride is corrosive and required special materials not required for handling either titanium tetrachloride or vanadium tetrachloride. Therefore, Hastelloy C-276 was used for the aluminum trichloride boiler and the piping to the reaction chamber. The BCl 3 is not as corrosive as AlCl 3 .
- the reactor was generally operated for approximately 250 seconds injecting approximately 11 kg of TiCl 4 .
- the salt and titanium alloy solids were captured on a wedge wire filter and free sodium metal was drained away.
- the product cake containing titanium alloy, sodium chloride and sodium was distilled at approximately 100 milli-torr at 550 to 575° C. vessel wall temperatures for 20 hours. Once all the sodium metal was removed via distillation, the trap was re-pressurized with argon gas and heated to 750° C. and held at temperature for 48 hours.
- the vessel containing the salt and titanium alloy cake was cooled and the cake was passivated with a 0.7 wt % oxygen/argon mixture. After passivation, the cake was washed with deionized water and subsequently dried in a vacuum oven at less than 100° C.
- Table 2 below sets forth a chemical analysis of various runs for both Ti as well as 6/4 alloy with submicron titanium boride substantially uniformly dispersed therein from an experimental loop running the Armstrong Process.
- titanium boride means principally TiB but does not exclude minor amounts of TiB 2 or other borides.
- the process described herein produces a novel powder in which most, if not substantially all, of the particles forming the powder have submicron titanium boride dispersed therein. While the boride dispersion may not always be perfect in every particle, the titanium boride is very small, submicron, and generally uniformly dispersed within the particles forming the powder, whether the powder is titanium or a titanium alloy.
- the sodium levels for 6/4 with submicron titanium boride are very low while the sodium level for Ti with submicron titanium boride are somewhat higher, but still less than commercially pure titanium, without submicron titanium boride dispersed therein, made by the Armstrong Process, as described in the incorporated application.
- the surface area of the 6/4 alloy compared to the CP titanium, as determined using BET Specific Surface Area analysis with krypton as the adsorbate is much larger than the CP titanium.
- the surface area of the 6/4 alloy with titanium boride is even greater, that is the alloy powder with titanium boride was smaller in average diameter and more difficult to grow into larger particles than Ti alloy without titanium boride.
- FIGS. 1-8 show that the 6/4 powder and/or Ti powder with submicron titanium boride distributed therein is “frillier” than the previously made 6/4 powder in the referenced application.
- Each of the figures references a run disclosed in Table 1 and represents samples taken from that run at different magnifications.
- by-product fines from the Kroll or Hunter Processes contain large amounts of undesirable chlorine which is not present in the CP titanium powder or alloy made by the Armstrong Process.
- the morphology of the Hunter and Kroll fines is different from the CP powder or the 6/4 alloy powder or either with submicron titanium boride therein made by the Armstrong Process. Neither the Kroll nor the Hunter process has been adapted to produce 6/4 alloy or any alloy. Alloy powders have been produced by melting prealloyed stock and thereafter using either gas atomization or a hydride-dehydride process (MHR).
- MHR hydride-dehydride process
- the Moxson et al. article discloses 6/4 powder made in Tula, Russia and as seen from FIG. 2 in that article, particularly FIGS. 2 c and 2 d the powders made by Tula Hydride Reduction process are significantly different than those made by the Armstrong Process. Moreover, referring to the Moxson et al.
- solid objects can be made by forming 6/4 or CP titanium powders into a near net shapes and thereafter sintering, see the Moxson et al. article and can also be formed by hot isostatic pressing, laser deposition, metal injecting molding, direct powder rolling or various other well known techniques. Therefore, the titanium alloy powder or titanium powder with submicron titanium boride dispersed substantially uniformly therein made by the Armstrong method may be formed into a consolidated or a consolidated and sintered product or may be formed into a solid object by well known methods in the art and the subject invention is intended to cover all such products made from the powder of the subject invention.
- alloys have at least 50% by weight titanium with titanium boride, preferably TiB, present in any required amount.
- halide Any halide may be used in the process, as previously described, but chlorides are preferred because they are readily available and less expensive than other halides.
- Various alkali or alkaline earth metals may be used, i.e. Na, K, Mg, Ca, but Na is preferred.
- Solid products are routinely made by a variety of processes from the powders described herein. Products made from powder produced by the Armstrong method including BCl 3 introduced into flowing liquid reducing metal produce superior hardness and other desirable physical properties are within the scope of this invention.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Organic Chemistry (AREA)
- Metallurgy (AREA)
- Materials Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Environmental & Geological Engineering (AREA)
- Geology (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Powder Metallurgy (AREA)
- Ceramic Products (AREA)
- Manufacture Of Metal Powder And Suspensions Thereof (AREA)
- Manufacture Of Alloys Or Alloy Compounds (AREA)
- Inorganic Compounds Of Heavy Metals (AREA)
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/544,820 US20070079908A1 (en) | 2005-10-06 | 2006-10-06 | Titanium boride |
US13/706,946 US8821611B2 (en) | 2005-10-06 | 2012-12-06 | Titanium boride |
US14/444,672 US20140334963A1 (en) | 2005-10-06 | 2014-07-28 | Titanium boride |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US72416605P | 2005-10-06 | 2005-10-06 | |
US11/544,820 US20070079908A1 (en) | 2005-10-06 | 2006-10-06 | Titanium boride |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/706,946 Continuation US8821611B2 (en) | 2005-10-06 | 2012-12-06 | Titanium boride |
Publications (1)
Publication Number | Publication Date |
---|---|
US20070079908A1 true US20070079908A1 (en) | 2007-04-12 |
Family
ID=37808330
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/544,820 Abandoned US20070079908A1 (en) | 2005-10-06 | 2006-10-06 | Titanium boride |
US13/706,946 Expired - Fee Related US8821611B2 (en) | 2005-10-06 | 2012-12-06 | Titanium boride |
US14/444,672 Abandoned US20140334963A1 (en) | 2005-10-06 | 2014-07-28 | Titanium boride |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US13/706,946 Expired - Fee Related US8821611B2 (en) | 2005-10-06 | 2012-12-06 | Titanium boride |
US14/444,672 Abandoned US20140334963A1 (en) | 2005-10-06 | 2014-07-28 | Titanium boride |
Country Status (8)
Country | Link |
---|---|
US (3) | US20070079908A1 (fr) |
EP (1) | EP1945394A2 (fr) |
JP (1) | JP2009511739A (fr) |
CN (1) | CN101277775A (fr) |
BR (1) | BRPI0616916A2 (fr) |
CA (1) | CA2623544A1 (fr) |
EA (1) | EA200801029A1 (fr) |
WO (1) | WO2007044635A2 (fr) |
Cited By (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20050284824A1 (en) * | 2002-09-07 | 2005-12-29 | International Titanium Powder, Llc | Filter cake treatment apparatus and method |
US20060107790A1 (en) * | 2002-10-07 | 2006-05-25 | International Titanium Powder, Llc | System and method of producing metals and alloys |
US20060123950A1 (en) * | 2002-09-07 | 2006-06-15 | Anderson Richard P | Process for separating ti from a ti slurry |
US20060150769A1 (en) * | 2002-09-07 | 2006-07-13 | International Titanium Powder, Llc | Preparation of alloys by the armstrong method |
US20060230878A1 (en) * | 2001-10-09 | 2006-10-19 | Richard Anderson | System and method of producing metals and alloys |
US20070180951A1 (en) * | 2003-09-03 | 2007-08-09 | Armstrong Donn R | Separation system, method and apparatus |
US20080031766A1 (en) * | 2006-06-16 | 2008-02-07 | International Titanium Powder, Llc | Attrited titanium powder |
US20080152533A1 (en) * | 2006-12-22 | 2008-06-26 | International Titanium Powder, Llc | Direct passivation of metal powder |
US20080199348A1 (en) * | 1994-08-01 | 2008-08-21 | International Titanium Powder, Llc | Elemental material and alloy |
US20080264208A1 (en) * | 2007-04-25 | 2008-10-30 | International Titanium Powder, Llc | Liquid injection of VCI4 into superheated TiCI4 for the production of Ti-V alloy powder |
US20100329919A1 (en) * | 2005-07-21 | 2010-12-30 | Jacobsen Lance E | Titanium Alloy |
US8821611B2 (en) | 2005-10-06 | 2014-09-02 | Cristal Metals Inc. | Titanium boride |
CN111961902A (zh) * | 2020-08-14 | 2020-11-20 | 东南大学 | 一种异构结构的钛基复合材料及其制备方法和应用 |
Families Citing this family (29)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9682425B2 (en) | 2009-12-08 | 2017-06-20 | Baker Hughes Incorporated | Coated metallic powder and method of making the same |
BRPI0708013A2 (pt) * | 2006-02-02 | 2011-05-17 | Int Titanium Powder Llc | composição de matéria, artigo sólido, e, método de fabricar uma composição |
US8889065B2 (en) * | 2006-09-14 | 2014-11-18 | Iap Research, Inc. | Micron size powders having nano size reinforcement |
US7758784B2 (en) | 2006-09-14 | 2010-07-20 | Iap Research, Inc. | Method of producing uniform blends of nano and micron powders |
US10240419B2 (en) | 2009-12-08 | 2019-03-26 | Baker Hughes, A Ge Company, Llc | Downhole flow inhibition tool and method of unplugging a seat |
US9080098B2 (en) | 2011-04-28 | 2015-07-14 | Baker Hughes Incorporated | Functionally gradient composite article |
US8631876B2 (en) | 2011-04-28 | 2014-01-21 | Baker Hughes Incorporated | Method of making and using a functionally gradient composite tool |
US9139928B2 (en) | 2011-06-17 | 2015-09-22 | Baker Hughes Incorporated | Corrodible downhole article and method of removing the article from downhole environment |
US9707739B2 (en) | 2011-07-22 | 2017-07-18 | Baker Hughes Incorporated | Intermetallic metallic composite, method of manufacture thereof and articles comprising the same |
US9643250B2 (en) | 2011-07-29 | 2017-05-09 | Baker Hughes Incorporated | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US9833838B2 (en) | 2011-07-29 | 2017-12-05 | Baker Hughes, A Ge Company, Llc | Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle |
US9033055B2 (en) | 2011-08-17 | 2015-05-19 | Baker Hughes Incorporated | Selectively degradable passage restriction and method |
US9090956B2 (en) | 2011-08-30 | 2015-07-28 | Baker Hughes Incorporated | Aluminum alloy powder metal compact |
US9856547B2 (en) | 2011-08-30 | 2018-01-02 | Bakers Hughes, A Ge Company, Llc | Nanostructured powder metal compact |
US9109269B2 (en) | 2011-08-30 | 2015-08-18 | Baker Hughes Incorporated | Magnesium alloy powder metal compact |
US9643144B2 (en) | 2011-09-02 | 2017-05-09 | Baker Hughes Incorporated | Method to generate and disperse nanostructures in a composite material |
US9010416B2 (en) | 2012-01-25 | 2015-04-21 | Baker Hughes Incorporated | Tubular anchoring system and a seat for use in the same |
US9605508B2 (en) | 2012-05-08 | 2017-03-28 | Baker Hughes Incorporated | Disintegrable and conformable metallic seal, and method of making the same |
US9816339B2 (en) | 2013-09-03 | 2017-11-14 | Baker Hughes, A Ge Company, Llc | Plug reception assembly and method of reducing restriction in a borehole |
CA2936851A1 (fr) | 2014-02-21 | 2015-08-27 | Terves, Inc. | Systeme metallique de desintegration a activation par fluide |
US11167343B2 (en) | 2014-02-21 | 2021-11-09 | Terves, Llc | Galvanically-active in situ formed particles for controlled rate dissolving tools |
US10865465B2 (en) | 2017-07-27 | 2020-12-15 | Terves, Llc | Degradable metal matrix composite |
US9910026B2 (en) | 2015-01-21 | 2018-03-06 | Baker Hughes, A Ge Company, Llc | High temperature tracers for downhole detection of produced water |
US10378303B2 (en) | 2015-03-05 | 2019-08-13 | Baker Hughes, A Ge Company, Llc | Downhole tool and method of forming the same |
US10221637B2 (en) | 2015-08-11 | 2019-03-05 | Baker Hughes, A Ge Company, Llc | Methods of manufacturing dissolvable tools via liquid-solid state molding |
CN105108162B (zh) * | 2015-08-21 | 2017-11-24 | 中国科学院理化技术研究所 | 一种将液态金属分散成微纳米颗粒的方法 |
US10016810B2 (en) | 2015-12-14 | 2018-07-10 | Baker Hughes, A Ge Company, Llc | Methods of manufacturing degradable tools using a galvanic carrier and tools manufactured thereof |
CN109019625B (zh) * | 2018-09-30 | 2021-07-20 | 成都先进金属材料产业技术研究院有限公司 | 硼化钛粉末的制备方法 |
CN114892057B (zh) * | 2020-06-16 | 2023-09-15 | 中山火炬职业技术学院 | 一种结合度强的高球形度Cr基合金-TiB2微纳米粉体及其制备方法 |
Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3379522A (en) * | 1966-06-20 | 1968-04-23 | Titanium Metals Corp | Dispersoid titanium and titaniumbase alloys |
US4915905A (en) * | 1984-10-19 | 1990-04-10 | Martin Marietta Corporation | Process for rapid solidification of intermetallic-second phase composites |
US5779761A (en) * | 1994-08-01 | 1998-07-14 | Kroftt-Brakston International, Inc. | Method of making metals and other elements |
US5897830A (en) * | 1996-12-06 | 1999-04-27 | Dynamet Technology | P/M titanium composite casting |
US5958106A (en) * | 1994-08-01 | 1999-09-28 | International Titanium Powder, L.L.C. | Method of making metals and other elements from the halide vapor of the metal |
US6099664A (en) * | 1993-01-26 | 2000-08-08 | London & Scandinavian Metallurgical Co., Ltd. | Metal matrix alloys |
US6409797B2 (en) * | 1994-08-01 | 2002-06-25 | International Titanium Powder Llc | Method of making metals and other elements from the halide vapor of the metal |
US6488073B1 (en) * | 1999-07-02 | 2002-12-03 | Rolls-Royce Plc | Method of adding boron to a heavy metal containing titanium aluminide alloy and a heavy metal containing titanium aluminide alloy |
US20060057017A1 (en) * | 2002-06-14 | 2006-03-16 | General Electric Company | Method for producing a titanium metallic composition having titanium boride particles dispersed therein |
US20060102255A1 (en) * | 2004-11-12 | 2006-05-18 | General Electric Company | Article having a dispersion of ultrafine titanium boride particles in a titanium-base matrix |
Family Cites Families (163)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR664108A (fr) | 1927-05-02 | 1929-09-05 | ||
US2205854A (en) | 1937-07-10 | 1940-06-25 | Kroll Wilhelm | Method for manufacturing titanium and alloys thereof |
US2607675A (en) | 1948-09-06 | 1952-08-19 | Int Alloys Ltd | Distillation of metals |
US2647826A (en) | 1950-02-08 | 1953-08-04 | Jordan James Fernando | Titanium smelting process |
GB722184A (en) | 1951-09-04 | 1955-01-19 | Joseph Peppo Levy | Improvements in or relating to the production of pure titanium and zirconium |
NL77870C (fr) | 1951-11-01 | |||
US2882143A (en) | 1953-04-16 | 1959-04-14 | Nat Lead Co | Continuous process for the production of titanium metal |
US2846304A (en) | 1953-08-11 | 1958-08-05 | Nat Res Corp | Method of producing titanium |
US2846303A (en) | 1953-08-11 | 1958-08-05 | Nat Res Corp | Method of producing titanium |
US2823991A (en) | 1954-06-23 | 1958-02-18 | Nat Distillers Chem Corp | Process for the manufacture of titanium metal |
GB778021A (en) | 1954-08-23 | 1957-07-03 | Bayer Ag | Process for the production of titanium |
US2890112A (en) | 1954-10-15 | 1959-06-09 | Du Pont | Method of producing titanium metal |
US2835567A (en) | 1954-11-22 | 1958-05-20 | Du Pont | Method of producing granular refractory metal |
US2882144A (en) | 1955-08-22 | 1959-04-14 | Allied Chem | Method of producing titanium |
DE1069884B (de) | 1956-01-17 | 1960-04-21 | Imperial Chemical Industries Limited, London | Verfahren zur Herstellung von Titan |
DE1071350B (fr) | 1956-03-20 | |||
US2816828A (en) | 1956-06-20 | 1957-12-17 | Nat Res Corp | Method of producing refractory metals |
US3067025A (en) | 1957-04-05 | 1962-12-04 | Dow Chemical Co | Continuous production of titanium sponge |
US2941867A (en) | 1957-10-14 | 1960-06-21 | Du Pont | Reduction of metal halides |
US2915382A (en) | 1957-10-16 | 1959-12-01 | Nat Res Corp | Production of metals |
US3085871A (en) | 1958-02-24 | 1963-04-16 | Griffiths Kenneth Frank | Method for producing the refractory metals hafnium, titanium, vanadium, silicon, zirconium, thorium, columbium, and chromium |
US3085872A (en) | 1958-07-01 | 1963-04-16 | Griffiths Kenneth Frank | Method for producing the refractory metals hafnium, titanium, vanadium, silicon, zirconium, thorium, columbium, and chromium |
US3058820A (en) | 1958-07-25 | 1962-10-16 | Bert W Whitehurst | Method of producing titanium metal |
US3113017A (en) | 1960-07-06 | 1963-12-03 | Vernon E Homme | Method for reacting titanic chloride with an alkali metal |
US3519258A (en) | 1966-07-23 | 1970-07-07 | Hiroshi Ishizuka | Device for reducing chlorides |
US3331666A (en) | 1966-10-28 | 1967-07-18 | William C Robinson | One-step method of converting uranium hexafluoride to uranium compounds |
US3535109A (en) | 1967-06-22 | 1970-10-20 | Dal Y Ingersoll | Method for producing titanium and other reactive metals |
US3847596A (en) | 1968-02-28 | 1974-11-12 | Halomet Ag | Process of obtaining metals from metal halides |
SE350469B (fr) | 1968-08-08 | 1972-10-30 | Mizusawa Industrial Chem | |
US3867515A (en) | 1971-04-01 | 1975-02-18 | Ppg Industries Inc | Treatment of titanium tetrachloride dryer residue |
GB1355433A (en) | 1971-07-28 | 1974-06-05 | Electricity Council | Production of titanium |
US3836302A (en) | 1972-03-31 | 1974-09-17 | Corning Glass Works | Face plate ring assembly for an extrusion die |
US3919087A (en) | 1972-07-25 | 1975-11-11 | Secondary Processing Systems | Continuous pressure filtering and/or screening apparatus for the separation of liquids and solids |
US4062679A (en) | 1973-03-29 | 1977-12-13 | Fansteel Inc. | Embrittlement-resistant tantalum wire |
US3927993A (en) | 1973-11-21 | 1975-12-23 | Ronald W Griffin | Fire starter and method |
JPS5812545B2 (ja) | 1974-05-08 | 1983-03-09 | ドウリヨクロ カクネンリヨウカイハツジギヨウダン | アルゴンガスチユウ ノ スイソノウドレンゾクソクテイホウ |
US3966460A (en) | 1974-09-06 | 1976-06-29 | Amax Specialty Metal Corporation | Reduction of metal halides |
US4007055A (en) | 1975-05-09 | 1977-02-08 | Exxon Research And Engineering Company | Preparation of stoichiometric titanium disulfide |
US4009007A (en) | 1975-07-14 | 1977-02-22 | Fansteel Inc. | Tantalum powder and method of making the same |
USRE32260E (en) | 1975-07-14 | 1986-10-07 | Fansteel Inc. | Tantalum powder and method of making the same |
US4017302A (en) | 1976-02-04 | 1977-04-12 | Fansteel Inc. | Tantalum metal powder |
US4070252A (en) | 1977-04-18 | 1978-01-24 | Scm Corporation | Purification of crude titanium tetrachloride |
US4141719A (en) | 1977-05-31 | 1979-02-27 | Fansteel Inc. | Tantalum metal powder |
US4149876A (en) | 1978-06-06 | 1979-04-17 | Fansteel Inc. | Process for producing tantalum and columbium powder |
US4190442A (en) | 1978-06-15 | 1980-02-26 | Eutectic Corporation | Flame spray powder mix |
JPS5811497B2 (ja) | 1978-10-04 | 1983-03-03 | 日本電気株式会社 | Ti↓−Al多孔質合金及びその製造方法 |
LU81469A1 (fr) | 1979-07-05 | 1981-02-03 | Luniversite Libre Bruxelles | Procede et installation pour la production de metaux reactifs par reduction de leurs halogenures |
GB2085031B (en) | 1980-08-18 | 1983-11-16 | Diamond Shamrock Techn | Modified lead electrode for electrowinning metals |
US4445931A (en) | 1980-10-24 | 1984-05-01 | The United States Of America As Represented By The Secretary Of The Interior | Production of metal powder |
US4401467A (en) | 1980-12-15 | 1983-08-30 | Jordan Robert K | Continuous titanium process |
FR2502181B1 (fr) | 1981-03-23 | 1985-09-27 | Servimetal | Procede et appareillage pour l'injection precise et continue d'un derive halogene a l'etat gazeux dans un metal liquide |
US4379718A (en) | 1981-05-18 | 1983-04-12 | Rockwell International Corporation | Process for separating solid particulates from a melt |
US4519837A (en) | 1981-10-08 | 1985-05-28 | Westinghouse Electric Corp. | Metal powders and processes for production from oxides |
US4432813A (en) | 1982-01-11 | 1984-02-21 | Williams Griffith E | Process for producing extremely low gas and residual contents in metal powders |
US4454169A (en) | 1982-04-05 | 1984-06-12 | Diamond Shamrock Corporation | Catalytic particles and process for their manufacture |
US4414188A (en) | 1982-04-23 | 1983-11-08 | Aluminum Company Of America | Production of zirconium diboride powder in a molten salt bath |
US4556420A (en) | 1982-04-30 | 1985-12-03 | Westinghouse Electric Corp. | Process for combination metal reduction and distillation |
US4423004A (en) | 1983-03-24 | 1983-12-27 | Sprague Electric Company | Treatment of tantalum powder |
US4487677A (en) | 1983-04-11 | 1984-12-11 | Metals Production Research, Inc. | Electrolytic recovery system for obtaining titanium metal from its ore |
GB8317243D0 (en) | 1983-06-24 | 1983-07-27 | Alcan Int Ltd | Producing aluminium boride |
US4521281A (en) | 1983-10-03 | 1985-06-04 | Olin Corporation | Process and apparatus for continuously producing multivalent metals |
US4687632A (en) | 1984-05-11 | 1987-08-18 | Hurd Frank W | Metal or alloy forming reduction process and apparatus |
AU587782B2 (en) | 1984-05-25 | 1989-08-31 | William Reginald Bulmer Martin | Reducing of metals with liquid metal reducing agents |
US4555268A (en) | 1984-12-18 | 1985-11-26 | Cabot Corporation | Method for improving handling properties of a flaked tantalum powder composition |
CH666639A5 (fr) | 1985-04-16 | 1988-08-15 | Battelle Memorial Institute | Procede de fabrication de poudres metalliques. |
US4689129A (en) | 1985-07-16 | 1987-08-25 | The Dow Chemical Company | Process for the preparation of submicron-sized titanium diboride |
US4606902A (en) | 1985-10-03 | 1986-08-19 | The United States Of America As Represented By The Secretary Of Commerce | Process for preparing refractory borides and carbides |
FR2595101A1 (fr) | 1986-02-28 | 1987-09-04 | Rhone Poulenc Chimie | Procede de preparation par lithiothermie de poudres metalliques |
US4985069A (en) | 1986-09-15 | 1991-01-15 | The United States Of America As Represented By The Secretary Of The Interior | Induction slag reduction process for making titanium |
JPS63207612A (ja) | 1987-02-24 | 1988-08-29 | 日本碍子株式会社 | セラミツク押出法及びそれに用いる装置 |
US4828008A (en) | 1987-05-13 | 1989-05-09 | Lanxide Technology Company, Lp | Metal matrix composites |
JPS6415334A (en) | 1987-07-09 | 1989-01-19 | Toho Titanium Co Ltd | Production of metal from metal halide |
CA1328561C (fr) | 1987-07-17 | 1994-04-19 | Toho Titanium Co., Ltd. | Methode pour la preparation de titane metallique et appareillage a cette fin |
JPS6452031A (en) | 1987-08-24 | 1989-02-28 | Toho Titanium Co Ltd | Production of titanium alloy |
JPH0643248B2 (ja) | 1987-09-18 | 1994-06-08 | 科学技術庁金属材料技術研究所長 | 遷移金属ほう化物繊維の製造法 |
US5211741A (en) | 1987-11-30 | 1993-05-18 | Cabot Corporation | Flaked tantalum powder |
US4940490A (en) | 1987-11-30 | 1990-07-10 | Cabot Corporation | Tantalum powder |
US4897116A (en) | 1988-05-25 | 1990-01-30 | Teledyne Industries, Inc. | High purity Zr and Hf metals and their manufacture |
US4923577A (en) | 1988-09-12 | 1990-05-08 | Westinghouse Electric Corp. | Electrochemical-metallothermic reduction of zirconium in molten salt solutions |
US5167271A (en) | 1988-10-20 | 1992-12-01 | Lange Frederick F | Method to produce ceramic reinforced or ceramic-metal matrix composite articles |
US4941646A (en) | 1988-11-23 | 1990-07-17 | Bethlehem Steel Corporation | Air cooled gas injection lance |
US5338379A (en) | 1989-04-10 | 1994-08-16 | General Electric Company | Tantalum-containing superalloys |
IT1230774B (it) | 1989-05-05 | 1991-10-29 | Sir Ind Spa | Preforme ceramiche ad elevata resistenza meccanica, procedimento per la loro preparazione e compositi a matrice metallica con esse ottenuti. |
JPH0747787B2 (ja) | 1989-05-24 | 1995-05-24 | 株式会社エヌ・ケイ・アール | チタン粉末またはチタン複合粉末の製造方法 |
US5242481A (en) | 1989-06-26 | 1993-09-07 | Cabot Corporation | Method of making powders and products of tantalum and niobium |
US5028491A (en) | 1989-07-03 | 1991-07-02 | General Electric Company | Gamma titanium aluminum alloys modified by chromium and tantalum and method of preparation |
JPH0357595A (ja) | 1989-07-24 | 1991-03-12 | Kuri Kagaku Sochi Kk | 連続濾過装置 |
US5082491A (en) | 1989-09-28 | 1992-01-21 | V Tech Corporation | Tantalum powder with improved capacitor anode processing characteristics |
FI87896C (fi) | 1990-06-05 | 1993-03-10 | Outokumpu Oy | Foerfarande foer framstaellning av metallpulver |
US5176741A (en) | 1990-10-11 | 1993-01-05 | Idaho Research Foundation, Inc. | Producing titanium particulates from in situ titanium-zinc intermetallic |
US5064463A (en) | 1991-01-14 | 1991-11-12 | Ciomek Michael A | Feedstock and process for metal injection molding |
US5147451A (en) | 1991-05-14 | 1992-09-15 | Teledyne Industries, Inc. | Method for refining reactive and refractory metals |
JPH0578762A (ja) * | 1991-05-23 | 1993-03-30 | Sumitomo Light Metal Ind Ltd | 強度に優れたTiAl基複合材料およびその製造方法 |
US5149497A (en) | 1991-06-12 | 1992-09-22 | General Electric Company | Oxidation resistant coatings of gamma titanium aluminum alloys modified by chromium and tantalum |
DE4214720C2 (de) | 1992-05-04 | 1994-10-13 | Starck H C Gmbh Co Kg | Vorrichtung zur Herstellung feinteiliger Metall- und Keramikpulver |
US5259862A (en) | 1992-10-05 | 1993-11-09 | The United States Of America As Represented By The Secretary Of The Interior | Continuous production of granular or powder Ti, Zr and Hf or their alloy products |
US5448447A (en) | 1993-04-26 | 1995-09-05 | Cabot Corporation | Process for making an improved tantalum powder and high capacitance low leakage electrode made therefrom |
US5439750A (en) | 1993-06-15 | 1995-08-08 | General Electric Company | Titanium metal matrix composite inserts for stiffening turbine engine components |
US5951822A (en) | 1993-09-09 | 1999-09-14 | Marcal Paper Mills, Inc. | Apparatus for making granular material |
US5460642A (en) | 1994-03-21 | 1995-10-24 | Teledyne Industries, Inc. | Aerosol reduction process for metal halides |
US5498446A (en) | 1994-05-25 | 1996-03-12 | Washington University | Method and apparatus for producing high purity and unagglomerated submicron particles |
US5437854A (en) | 1994-06-27 | 1995-08-01 | Westinghouse Electric Corporation | Process for purifying zirconium tetrachloride |
US20030061907A1 (en) | 1994-08-01 | 2003-04-03 | Kroftt-Brakston International, Inc. | Gel of elemental material or alloy and liquid metal and salt |
US6861038B2 (en) | 1994-08-01 | 2005-03-01 | International Titanium Powder, Llc. | Ceramics and method of producing ceramics |
US20030145682A1 (en) | 1994-08-01 | 2003-08-07 | Kroftt-Brakston International, Inc. | Gel of elemental material or alloy and liquid metal and salt |
US7435282B2 (en) | 1994-08-01 | 2008-10-14 | International Titanium Powder, Llc | Elemental material and alloy |
US7445658B2 (en) | 1994-08-01 | 2008-11-04 | Uchicago Argonne, Llc | Titanium and titanium alloys |
US5427602A (en) | 1994-08-08 | 1995-06-27 | Aluminum Company Of America | Removal of suspended particles from molten metal |
US6027585A (en) | 1995-03-14 | 2000-02-22 | The Regents Of The University Of California Office Of Technology Transfer | Titanium-tantalum alloys |
USH1642H (en) | 1995-03-20 | 1997-04-01 | The United States Of America As Represented By The Secretary Of The Navy | Wear and impact tolerant plow blade |
US5637816A (en) | 1995-08-22 | 1997-06-10 | Lockheed Martin Energy Systems, Inc. | Metal matrix composite of an iron aluminide and ceramic particles and method thereof |
US6103651A (en) | 1996-02-07 | 2000-08-15 | North American Refractories Company | High density ceramic metal composite exhibiting improved mechanical properties |
US5954856A (en) | 1996-04-25 | 1999-09-21 | Cabot Corporation | Method of making tantalum metal powder with controlled size distribution and products made therefrom |
US5948495A (en) | 1996-07-01 | 1999-09-07 | Alyn Corporation | Ceramic-metal matrix composites for magnetic disk substrates for hard disk drives |
US20080187455A1 (en) | 1996-08-02 | 2008-08-07 | International Titanium Powder, Llc | Titanium and titanium alloys |
JP3794713B2 (ja) | 1997-02-19 | 2006-07-12 | エイチ・シー・スタルク・ゲゼルシヤフト・ミツト・ベシユレンクテル・ハフツング | タンタル粉末、その製造法およびそれから得られる焼結アノード |
KR100511027B1 (ko) | 1997-02-19 | 2005-08-31 | 하.체. 스타르크 게엠베하 | 탄탈 분말, 그의 제조 방법 및 그로부터 얻어진 소결 양극 |
US5914440A (en) | 1997-03-18 | 1999-06-22 | Noranda Inc. | Method and apparatus removal of solid particles from magnesium chloride electrolyte and molten magnesium by filtration |
US6309595B1 (en) | 1997-04-30 | 2001-10-30 | The Altalgroup, Inc | Titanium crystal and titanium |
US6180258B1 (en) | 1997-06-04 | 2001-01-30 | Chesapeake Composites Corporation | Metal-matrix composites and method for making such composites |
JP2894326B2 (ja) | 1997-06-30 | 1999-05-24 | 日本電気株式会社 | タンタル粉末及びそれを用いた固体電解コンデンサ |
US5993512A (en) | 1997-12-09 | 1999-11-30 | Allmettechnologies, Inc. | Method and system for recycling byproduct streams from metal processing operations |
US6309570B1 (en) | 1998-01-14 | 2001-10-30 | American Equipment Systems | Vacuum extrusion system for production of cement-based articles |
US6210461B1 (en) | 1998-08-10 | 2001-04-03 | Guy R. B. Elliott | Continuous production of titanium, uranium, and other metals and growth of metallic needles |
JP4116161B2 (ja) | 1998-09-03 | 2008-07-09 | 三菱電機株式会社 | 過電圧保護機能付半導体装置及びその製造方法 |
DE19847012A1 (de) | 1998-10-13 | 2000-04-20 | Starck H C Gmbh Co Kg | Niobpulver und Verfahren zu dessen Herstellung |
JP3871824B2 (ja) | 1999-02-03 | 2007-01-24 | キャボットスーパーメタル株式会社 | 高容量コンデンサー用タンタル粉末 |
US6010661A (en) | 1999-03-11 | 2000-01-04 | Japan As Represented By Director General Of Agency Of Industrial Science And Technology | Method for producing hydrogen-containing sponge titanium, a hydrogen containing titanium-aluminum-based alloy powder and its method of production, and a titanium-aluminum-based alloy sinter and its method of production |
AT407393B (de) | 1999-09-22 | 2001-02-26 | Electrovac | Verfahren zur herstellung eines metall-matrix-composite (mmc-) bauteiles |
AT408345B (de) | 1999-11-17 | 2001-10-25 | Electrovac | Verfahren zur festlegung eines aus metall-matrix- composite-(mmc-) materiales gebildeten körpers auf einem keramischen körper |
IT1307298B1 (it) | 1999-12-20 | 2001-10-30 | Ct Sviluppo Materiali Spa | Procedimento per la preparazione di componenti a bassa densita', consubstrato eventualmente composito a matrice metallica o polimerica, |
US6432161B1 (en) | 2000-02-08 | 2002-08-13 | Cabot Supermetals K.K. | Nitrogen-containing metal powder, production process thereof, and porous sintered body and solid electrolytic capacitor using the metal powder |
JP3671133B2 (ja) | 2000-03-30 | 2005-07-13 | 東邦チタニウム株式会社 | チタンの製造方法 |
DE10030252A1 (de) | 2000-06-20 | 2002-01-03 | Degussa | Abtrennung von Metallchloriden aus deren Suspensionen in Chlorsilanen |
US6884522B2 (en) | 2002-04-17 | 2005-04-26 | Ceramics Process Systems Corp. | Metal matrix composite structure and method |
US6921510B2 (en) | 2003-01-22 | 2005-07-26 | General Electric Company | Method for preparing an article having a dispersoid distributed in a metallic matrix |
US7416697B2 (en) | 2002-06-14 | 2008-08-26 | General Electric Company | Method for preparing a metallic article having an other additive constituent, without any melting |
US7329381B2 (en) | 2002-06-14 | 2008-02-12 | General Electric Company | Method for fabricating a metallic article without any melting |
US6737017B2 (en) | 2002-06-14 | 2004-05-18 | General Electric Company | Method for preparing metallic alloy articles without melting |
AU2003268428A1 (en) | 2002-09-07 | 2004-03-29 | International Titanium Powder, Llc. | Safety mechanism |
WO2004028655A2 (fr) | 2002-09-07 | 2004-04-08 | International Titanium Powder, Llc. | Appareil et procede de traitement d'un gateau au moyen d'un filtre |
WO2004022269A2 (fr) | 2002-09-07 | 2004-03-18 | International Titanium Powder, Llc. | Procede et appareil de regulation de la taille de la poudre produite par le procede armstrong |
CA2497999A1 (fr) | 2002-09-07 | 2004-03-18 | International Titanium Powder, Llc. | Procede et dispositif pour la separation de titane dans une suspension de titane |
UA79310C2 (en) | 2002-09-07 | 2007-06-11 | Int Titanium Powder Llc | Methods for production of alloys or ceramics with the use of armstrong method and device for their realization |
US20050225014A1 (en) | 2002-09-07 | 2005-10-13 | International Titanium Powder, Llc | Filter extraction mechanism |
WO2004026511A2 (fr) | 2002-09-07 | 2004-04-01 | International Titanium Powder, Llc. | Procede et appareil permettant de reguler la taille d'une poudre produite par le procede armstrong |
WO2004022798A1 (fr) | 2002-09-07 | 2004-03-18 | International Titanium Powder, Llc. | Dispositif a vis utilise pour transferer de la boue reactionnelle contenant du ti dans une enceinte sous vide |
US6902601B2 (en) | 2002-09-12 | 2005-06-07 | Millennium Inorganic Chemicals, Inc. | Method of making elemental materials and alloys |
AU2003263082A1 (en) | 2002-10-07 | 2004-05-04 | International Titanium Powder, Llc. | System and method of producing metals and alloys |
AU2003270305A1 (en) | 2002-10-07 | 2004-05-04 | International Titanium Powder, Llc. | System and method of producing metals and alloys |
UA78623C2 (en) | 2002-11-20 | 2007-04-10 | Int Titanium Powder Llc | Method of separating, meant for separation of metal powder from a slurry (variants) and separating system for realization the same |
US6824585B2 (en) | 2002-12-03 | 2004-11-30 | Adrian Joseph | Low cost high speed titanium and its alloy production |
US6955703B2 (en) | 2002-12-26 | 2005-10-18 | Millennium Inorganic Chemicals, Inc. | Process for the production of elemental material and alloys |
WO2005019485A1 (fr) | 2003-08-22 | 2005-03-03 | International Titanium Powder, Llc. | Indexation d'un systeme de separation |
US20070180951A1 (en) | 2003-09-03 | 2007-08-09 | Armstrong Donn R | Separation system, method and apparatus |
US7803235B2 (en) | 2004-01-08 | 2010-09-28 | Cabot Corporation | Passivation of tantalum and other metal powders using oxygen |
EP1761352B1 (fr) | 2004-06-24 | 2008-08-13 | H.C. Starck Inc. | Production de poudres de metaux valves presentant de meilleures proprietes physiques et electriques |
US20070017319A1 (en) | 2005-07-21 | 2007-01-25 | International Titanium Powder, Llc. | Titanium alloy |
WO2007044635A2 (fr) * | 2005-10-06 | 2007-04-19 | International Titanium Powder, Llc | Borure de titane |
BRPI0708013A2 (pt) | 2006-02-02 | 2011-05-17 | Int Titanium Powder Llc | composição de matéria, artigo sólido, e, método de fabricar uma composição |
US20080031766A1 (en) | 2006-06-16 | 2008-02-07 | International Titanium Powder, Llc | Attrited titanium powder |
EP2104583A1 (fr) | 2006-12-22 | 2009-09-30 | International Titanium Powder, LLC. | Passivation directe de poudre métallique |
US7753989B2 (en) | 2006-12-22 | 2010-07-13 | Cristal Us, Inc. | Direct passivation of metal powder |
-
2006
- 2006-10-06 WO PCT/US2006/039331 patent/WO2007044635A2/fr active Application Filing
- 2006-10-06 EA EA200801029A patent/EA200801029A1/ru unknown
- 2006-10-06 US US11/544,820 patent/US20070079908A1/en not_active Abandoned
- 2006-10-06 CA CA002623544A patent/CA2623544A1/fr not_active Abandoned
- 2006-10-06 BR BRPI0616916A patent/BRPI0616916A2/pt not_active IP Right Cessation
- 2006-10-06 EP EP06816508A patent/EP1945394A2/fr not_active Withdrawn
- 2006-10-06 JP JP2008534752A patent/JP2009511739A/ja active Pending
- 2006-10-06 CN CNA2006800368869A patent/CN101277775A/zh active Pending
-
2012
- 2012-12-06 US US13/706,946 patent/US8821611B2/en not_active Expired - Fee Related
-
2014
- 2014-07-28 US US14/444,672 patent/US20140334963A1/en not_active Abandoned
Patent Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3379522A (en) * | 1966-06-20 | 1968-04-23 | Titanium Metals Corp | Dispersoid titanium and titaniumbase alloys |
US4915905A (en) * | 1984-10-19 | 1990-04-10 | Martin Marietta Corporation | Process for rapid solidification of intermetallic-second phase composites |
US6099664A (en) * | 1993-01-26 | 2000-08-08 | London & Scandinavian Metallurgical Co., Ltd. | Metal matrix alloys |
US5779761A (en) * | 1994-08-01 | 1998-07-14 | Kroftt-Brakston International, Inc. | Method of making metals and other elements |
US5958106A (en) * | 1994-08-01 | 1999-09-28 | International Titanium Powder, L.L.C. | Method of making metals and other elements from the halide vapor of the metal |
US6409797B2 (en) * | 1994-08-01 | 2002-06-25 | International Titanium Powder Llc | Method of making metals and other elements from the halide vapor of the metal |
US5897830A (en) * | 1996-12-06 | 1999-04-27 | Dynamet Technology | P/M titanium composite casting |
US6488073B1 (en) * | 1999-07-02 | 2002-12-03 | Rolls-Royce Plc | Method of adding boron to a heavy metal containing titanium aluminide alloy and a heavy metal containing titanium aluminide alloy |
US20060057017A1 (en) * | 2002-06-14 | 2006-03-16 | General Electric Company | Method for producing a titanium metallic composition having titanium boride particles dispersed therein |
US20060102255A1 (en) * | 2004-11-12 | 2006-05-18 | General Electric Company | Article having a dispersion of ultrafine titanium boride particles in a titanium-base matrix |
Cited By (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080199348A1 (en) * | 1994-08-01 | 2008-08-21 | International Titanium Powder, Llc | Elemental material and alloy |
US20060230878A1 (en) * | 2001-10-09 | 2006-10-19 | Richard Anderson | System and method of producing metals and alloys |
US20050284824A1 (en) * | 2002-09-07 | 2005-12-29 | International Titanium Powder, Llc | Filter cake treatment apparatus and method |
US20090202385A1 (en) * | 2002-09-07 | 2009-08-13 | Donn Reynolds Armstrong | Preparation of alloys by the armstrong method |
US20060123950A1 (en) * | 2002-09-07 | 2006-06-15 | Anderson Richard P | Process for separating ti from a ti slurry |
US20060150769A1 (en) * | 2002-09-07 | 2006-07-13 | International Titanium Powder, Llc | Preparation of alloys by the armstrong method |
US20060107790A1 (en) * | 2002-10-07 | 2006-05-25 | International Titanium Powder, Llc | System and method of producing metals and alloys |
US20070180951A1 (en) * | 2003-09-03 | 2007-08-09 | Armstrong Donn R | Separation system, method and apparatus |
US9630251B2 (en) | 2005-07-21 | 2017-04-25 | Cristal Metals Inc. | Titanium alloy |
US8894738B2 (en) | 2005-07-21 | 2014-11-25 | Cristal Metals Inc. | Titanium alloy |
US20100329919A1 (en) * | 2005-07-21 | 2010-12-30 | Jacobsen Lance E | Titanium Alloy |
US8821611B2 (en) | 2005-10-06 | 2014-09-02 | Cristal Metals Inc. | Titanium boride |
US20110103997A1 (en) * | 2006-06-16 | 2011-05-05 | Dariusz Kogut | Attrited titanium powder |
US20080031766A1 (en) * | 2006-06-16 | 2008-02-07 | International Titanium Powder, Llc | Attrited titanium powder |
US20080152533A1 (en) * | 2006-12-22 | 2008-06-26 | International Titanium Powder, Llc | Direct passivation of metal powder |
US7753989B2 (en) | 2006-12-22 | 2010-07-13 | Cristal Us, Inc. | Direct passivation of metal powder |
US9127333B2 (en) | 2007-04-25 | 2015-09-08 | Lance Jacobsen | Liquid injection of VCL4 into superheated TiCL4 for the production of Ti-V alloy powder |
US20080264208A1 (en) * | 2007-04-25 | 2008-10-30 | International Titanium Powder, Llc | Liquid injection of VCI4 into superheated TiCI4 for the production of Ti-V alloy powder |
CN111961902A (zh) * | 2020-08-14 | 2020-11-20 | 东南大学 | 一种异构结构的钛基复合材料及其制备方法和应用 |
Also Published As
Publication number | Publication date |
---|---|
US20130343945A1 (en) | 2013-12-26 |
WO2007044635A2 (fr) | 2007-04-19 |
BRPI0616916A2 (pt) | 2017-05-23 |
EP1945394A2 (fr) | 2008-07-23 |
WO2007044635A3 (fr) | 2007-05-31 |
AU2006302273A1 (en) | 2007-04-19 |
JP2009511739A (ja) | 2009-03-19 |
EA200801029A1 (ru) | 2008-10-30 |
CA2623544A1 (fr) | 2007-04-19 |
US8821611B2 (en) | 2014-09-02 |
US20140334963A1 (en) | 2014-11-13 |
AU2006302273B2 (en) | 2010-08-19 |
CN101277775A (zh) | 2008-10-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8821611B2 (en) | Titanium boride | |
US20080199348A1 (en) | Elemental material and alloy | |
US10604452B2 (en) | Article having a dispersion of ultrafine titanium boride particles in a titanium-base matrix | |
JP5025084B2 (ja) | 融解せずに金属合金物品を製造する方法 | |
Bolton et al. | Microstructural development and sintering kinetics in ceramic reinforced high speed steel metal matrix composites | |
Chrysanthou et al. | Production of copper-matrix composites by in situ processing | |
US6551377B1 (en) | Spherical rhenium powder | |
US3143789A (en) | Dispersion strengthened metal composition | |
US20060120943A1 (en) | Method for manufacturing nanophase TiC-based composite powders by metallothermic reduction | |
US20080187455A1 (en) | Titanium and titanium alloys | |
US9138806B2 (en) | In-situ combustion synthesis of titanium carbide (TiC) reinforced aluminum matrix composite | |
US11008639B2 (en) | Powder metallurgy titanium alloys | |
US20030061907A1 (en) | Gel of elemental material or alloy and liquid metal and salt | |
US4595413A (en) | Group IVb transition metal based metal and processes for the production thereof | |
WO2016100226A1 (fr) | Incorporation de particules de taille nanométrique dans de l'aluminium ou d'autres métaux légers par décoration de particules de taille micrométrique | |
AU2006302273C1 (en) | Titanium or titanium alloy with titanium boride dispersion | |
JP2009525407A (ja) | セラミック粒子が分散した金属マトリクス | |
US7435282B2 (en) | Elemental material and alloy | |
US7445658B2 (en) | Titanium and titanium alloys | |
Dolata et al. | Influence of the Sr and Mg alloying additions on the bonding between matrix and reinforcing particles in the AlSi7Mg/SiC-Cg hybrid composite | |
JPH10298684A (ja) | 強度、耐摩耗性及び耐熱性に優れたアルミニウム基合金−硬質粒子複合材料 | |
LIANG et al. | Microstructure and Mechanical Properties of Al-4.9 Ni-4.9 Ti Alloy Prepared by Mechanical Alloying | |
EP0187741A4 (fr) | Metal a base de metaux de transition de groupe ivb et ses procedes de production. | |
Kainer | Properties of consolidated magnesium alloy powder | |
McCracken et al. | Powder characterisation: key titanium powder characteristics manufactured using the hydride-dehydride (HDH) process |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: TWACG, LLC, ILLINOIS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:INTERNATIONAL TITANIUM POWDER, L.L.C.;REEL/FRAME:020497/0632 Effective date: 20070801 |
|
AS | Assignment |
Owner name: INTERNATIONAL TITANIUM POWDER, L.L.C., ILLINOIS Free format text: CHANGE OF NAME;ASSIGNOR:TWACG, LLC;REEL/FRAME:020617/0212 Effective date: 20070802 |
|
AS | Assignment |
Owner name: THE NATIONAL TITANIUM DIOXIDE CO. LTD., MARYLAND Free format text: SECURITY AGREEMENT;ASSIGNOR:INTERNATIONAL TITANIUM POWDER, L.L.C.;REEL/FRAME:021127/0493 Effective date: 20080602 |
|
AS | Assignment |
Owner name: INTERNATIONAL TITANIUM POWDER, LLC, ILLINOIS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:JACOBSEN, LANCE;BENISH (DECEASED), ADAM JOHN;BENISH (EXECUTOR), AMY;REEL/FRAME:021107/0709;SIGNING DATES FROM 20080519 TO 20080527 |
|
AS | Assignment |
Owner name: INTERNATIONAL TITANIUM POWDER, LLC, ILLINOIS Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:THE NATIONAL TITANIUM DIOXIDE CO. LTD.;REEL/FRAME:021824/0319 Effective date: 20081111 |
|
AS | Assignment |
Owner name: CRISTAL US, INC., MARYLAND Free format text: MERGER;ASSIGNOR:INTERNATIONAL TITANIUM POWDER, L.L.C.;REEL/FRAME:021846/0175 Effective date: 20081016 |
|
STCB | Information on status: application discontinuation |
Free format text: EXPRESSLY ABANDONED -- DURING EXAMINATION |