US20040033909A1 - Metal product with excellent moldability surface-treated with alkali-soluble lubricant - Google Patents

Metal product with excellent moldability surface-treated with alkali-soluble lubricant Download PDF

Info

Publication number
US20040033909A1
US20040033909A1 US10/416,976 US41697603A US2004033909A1 US 20040033909 A1 US20040033909 A1 US 20040033909A1 US 41697603 A US41697603 A US 41697603A US 2004033909 A1 US2004033909 A1 US 2004033909A1
Authority
US
United States
Prior art keywords
alkali
film
aqueous composition
polyurethane aqueous
soluble
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/416,976
Other languages
English (en)
Inventor
Ikuro Yamaoka
Hiroshi Kanai
Akihiro Miyasaka
Yoichiro Mori
Tsutomu Tawa
Mitsuhiro Nishimura
Chikako Kouda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Mitsui Chemicals Polyurethanes Inc
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Assigned to NIPPON STEEL CORPORATION, MITSUI TAKEDA CHEMICALS, INC. reassignment NIPPON STEEL CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KANAI, HIROSHI, KOUDA, CHIKAKO, MIYASAKA, AKIHIRO, MORI, YOICHIRO, NISHIMURA, MITSUHIRO, TAWA, TSUTOMU, YAMAOKA, IKURO
Publication of US20040033909A1 publication Critical patent/US20040033909A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/10—Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step
    • C08G18/12—Prepolymer processes involving reaction of isocyanates or isothiocyanates with compounds having active hydrogen in a first reaction step using two or more compounds having active hydrogen in the first polymerisation step
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/20—Deep-drawing
    • B21D22/201—Work-pieces; preparation of the work-pieces, e.g. lubricating, coating
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/0804—Manufacture of polymers containing ionic or ionogenic groups
    • C08G18/0819—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/08—Processes
    • C08G18/0804—Manufacture of polymers containing ionic or ionogenic groups
    • C08G18/0819—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups
    • C08G18/0823—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups containing carboxylate salt groups or groups forming them
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G18/00—Polymeric products of isocyanates or isothiocyanates
    • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
    • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
    • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
    • C08G18/66—Compounds of groups C08G18/42, C08G18/48, or C08G18/52
    • C08G18/6633—Compounds of group C08G18/42
    • C08G18/6659—Compounds of group C08G18/42 with compounds of group C08G18/34
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D175/00—Coating compositions based on polyureas or polyurethanes; Coating compositions based on derivatives of such polymers
    • C09D175/04—Polyurethanes
    • C09D175/12—Polyurethanes from compounds containing nitrogen and active hydrogen, the nitrogen atom not being part of an isocyanate group
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
    • C09D5/08—Anti-corrosive paints
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
    • C08L23/04—Homopolymers or copolymers of ethene
    • C08L23/06—Polyethene

Definitions

  • the present invention relates to a surface-lubricated metal product, with excellent shapability, which has an alkali-soluble lubricating film on the surface.
  • a lubricating oil or the like is usually coated so as to prevent the metal surface and the metal mold surface from being scratched due to poor lubrication.
  • a lubricating oil gives rise to a cumbersome production process and the splashing of lubricating oil worsens the working environment.
  • the lubricating oil is removed using an organic halogen-base solvent such as fluorocarbon, trichloroethane and dichloromethane, but these solvents not only adversely affect the health of workers but also the majority thereof are a substance having an extremely high load on the environment (They produce greenhouse effect gases which are ozone layer-depleting substances and have global warming effects as high as several hundred to ten thousand times the effect of CO 2 ). Many of these solvents are chemicals which will be discontinued under the Montreal Protocol in view of protecting the ozone layer. In order to avoid use of these solvents, a substitute method is required.
  • an organic halogen-base solvent such as fluorocarbon, trichloroethane and dichloromethane
  • a removing-type lubricating film which can be dissolved and removed in an alkali degreasing step, after press shaping, has been developed.
  • This alkali removing-type lubricating film is suitably used where a glossy metal surface must be made available or a good welding property is required after working.
  • Japanese Unexamined Patent Publications (Kokai) No. 8-156177, No. 8-252887, No. 10-114014 and No. 10-88364 have proposed an alkali removing-type lubricating film using an acrylic resin.
  • the alkali removing-type lubricating film using an acrylic resin sometimes fails in ensuring sufficiently high shapability and, for example, galling occurs under severe press shaping conditions such as deep drawing and ironing.
  • the press shaping is performed without a coating of a lubricating oil
  • the elastic modulus of the lubricating film coated on a metal is sufficiently high
  • the lubricating film is damaged due to pressure from the metal mold under severe shaping conditions such as deep drawing or ironing (press working with a minus clearance)
  • the metal mold and the surface of a metal to be worked adhere to induce mold galling and, as a result, the lubricating film peeled off at the galled part attaches to the metal mold or shaping failure such that impairment of the appearance of the metal surface is caused and these are a serious problem in the working.
  • An object of the present invention is to solve these problems and provide an alkali soluble lubricant surface-treated metal product having excellent shapability.
  • the present inventors have made extensive investigations to solve the above problems and to obtain an alkali soluble lubricant surface-treated metal product having excellent shapability and, as a result, have found that the above-described object can be attained when both surfaces or one surface of a metal are coated with an alkali-soluble lubricating film mainly comprising a lubricating function-imparting agent and an alkali-soluble polyurethane aqueous composition containing a carboxyl group or a sulfonic acid group within the molecule and where the elastic modulus of the film after coating is 0.5 to 20 GPa at 25° C.
  • the present invention has been accomplished based on this finding.
  • the alkali soluble lubricant surface-treated metal product with excellent shapability is characterized in that:
  • an alkali-soluble lubricating film mainly comprising (A) an alkali-soluble polyurethane aqueous composition containing a carboxyl group or a sulfonic acid group within the molecule and (B) a lubricating function-imparting agent in an amount of 1 to 30 mass % (wt %) based on the alkali-soluble polyurethane aqueous composition is coated on both surfaces or one surface of a metal product to have a film thickness of 0.5 to 10 ⁇ m and the elastic modulus of the film after coating is 0.5 to 20 GPa at 25° C., wherein by coating this alkali-soluble lubricating film, a metal product capable of exhibiting sufficiently high shapability even under severe press shaping conditions such as deep drawing or ironing can be obtained;
  • the alkali-soluble lubricating film mainly comprises (A) an alkali-soluble polyurethane aqueous composition, (B) a lubricating function-imparting agent in an amount of 1 to 30 mass % based on the alkali-soluble polyurethane aqueous composition and (C) a silica particle in an amount of 1 to 30 mass % based on the alkali soluble polyurethane aqueous composition, wherein by adding the silica particle within the above-described range, the adhesion between the alkali-soluble lubricating film and the metal product surface is enhanced and the film strength of the alkali-soluble lubricating film is increased and, as a result, the galling resistance is improved;
  • the amount of the acid radical contained in the alkali-soluble polyurethane aqueous composition (A) constituting the alkali-soluble lubricating film is from 30 to 180 in terms of the acid value wherein, by introducing a compound having an acid radical in an acid value of 30 to 180 in the polyurethane molecule, the coated film can have a flexibility capable of allowing shaping even under severe shaping conditions, despite the fact that the film after coating on a metal has a relatively high elastic modulus of 0.5 to 20 GPa at 25° C.;
  • the neutralizer for the acid radical contained in the alkali-soluble polyurethane aqueous composition (A) forming the alkali-soluble lubricating film is sodium hydroxide or potassium hydroxide, wherein by using sodium hydroxide or potassium hydroxide as the neutralizer for the acid radical, the alkali solubility required in the present invention can be achieved;
  • the main component constituting the alkali-soluble polyurethane aqueous composition (A) forming the alkali-soluble lubricating film is a polyester polyol wherein, by using a polyester polyol as the main component constituting the alkali-soluble polyurethane aqueous composition (A), the alkali solubility required in the present invention can be achieved even at a low temperature such as room temperature;
  • the lubricating function-imparting agent (B) forming the alkali-soluble lubricating film comprises one or more member selected from the group consisting of a polyolefin-base wax, a paraffin-base wax, a stearic acid-base solid lubricant and a wax comprising a fluorine-containing resin wherein, by the addition of this lubricating function-imparting agent, a low dynamic friction coefficient can be ensured over a wide temperature range and a good lubricating function can be attained;
  • the elastic modulus of the film after coating is 0.5 to 6 GPa at 25° C. and, at the same time, the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) as the main component of the film exceeds 10%, or the elastic modulus of the film after coating exceeds 6 GPa at 25° C.
  • the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) as the main component of the film is 10% or less wherein, by having such a constitution, the film can be balanced in the elasticity and elongation and a metal product capable of exhibiting a sufficiently high shapability even under severe press shaping conditions can be provided;
  • the glass transition temperature of the alkali-soluble polyurethane aqueous composition (A) in the coated lubricating film is 100° C. or more wherein, although a steel sheet surface sometimes reaches a temperature of 100° C. or more due to frictional heat during working under severe press shaping conditions of continuously performing deep drawing or ironing without using a lubricating oil, the glass transition temperature of the alkali-soluble polyurethane aqueous composition, as a continuous phase in the lubricating film, is 100° C. or more and, therefore, even when the steel sheet surface reaches a temperature of 100° C. or more, the film does not decrease in elastic modulus and exhibits an excellent galling resistance;
  • the alkali-soluble lubricating film mainly comprises (A) an alkali-soluble polyurethane aqueous composition containing a carboxyl group or a sulfonic acid group within the molecule and (B) a lubricating function-imparting agent in an amount of 1 to 30 mass % based on the alkali-soluble polyurethane aqueous composition, the main component of the alkali-soluble polyurethane aqueous composition is a polyester polyol, the neutralizer for the acid radical contained in the alkali-soluble polyurethane aqueous composition (A) is sodium hydroxide or potassium hydroxide, the amount of the acid radical contained in the alkali-soluble polyurethane aqueous composition (A) is from 30 to 180 in terms of the acid value, the lubricating function-imparting agent (B) comprises one or more member selected from the group consisting of
  • the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) as the main component of the film exceeds 10%, or the elastic modulus of the film after coating exceeds 6 GPa at 25° C. and, at the same time, the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) as the main component of the film is 10% or less, and the glass transition temperature of the alkali-soluble polyurethane aqueous composition (A) is 100° C. or more, wherein the alkali soluble lubricant surface-treated metal product maintains excellent shapability even under severe press shaping such as deep drawing or ironing and shaping failures hardly occur; and
  • the alkali soluble lubricant surface-treated metal product as described in (9) of the present invention may further comprise (C) silica particles in an amount of 1 to 30 mass % based on the alkali-soluble polyurethane aqueous composition, wherein by containing silica particles, as such, the adhesion between the alkali-soluble lubricating film and the metal product surface is enhanced and the film strength of the alkali-soluble lubricating film is increased and, as a result, the galling resistance is improved.
  • FIGS. 1 to 3 are views for explaining the process of producing and using the alkali soluble lubricant surface-treated metal product of the present invention.
  • the present inventors have made extensive investigations on an alkali soluble lubricant surface-treated metal product having a function of exhibiting sufficiently high shapability under continuous shaping conditions and bringing about dissolution or desorption of the lubricating film in the alkali degreasing step after shaping and, as a result, it has been found that this function is brought out when the film obtained after coating a coating material composition comprising an alkali-soluble polyurethane aqueous composition and a lubricating function-imparting agent on a metal surface has an elastic modulus of 0.5 to 20 GPa at 25° C. (preferably, the elastic modulus of the film after coating is from 0.5 to 6 GPa at 25° C.
  • the alkali-soluble polyurethane aqueous composition (A) as the main component of the film exceeds 10%, or the elastic modulus of the film after coating exceeds 6 GPa and at the same time, the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) as the main component of the film is 10% or less), the alkali-soluble polyurethane aqueous composition contains a carboxyl group or a sulfonic acid group within the molecule in the range from 30 to 180 in terms of the acid value, and sodium hydroxide or potassium hydroxide is used as the neutralizer for the acid.
  • the alkali-soluble polyurethane aqueous composition for use in the present invention can be obtained by reacting a compound having at least two isocyanate groups per one molecule, a compound having at least two active hydrogen groups per one molecule and a compound having at least one or more active hydrogen group within the molecule and containing an acid radical such as carboxyl group or sulfonic acid group, and dissolving or dispersing the reactant in water.
  • Examples of the compound having at least two isocyanate groups per one molecule for use in the present invention include aliphatic diisocyanates such as trimethylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, pentamethylene diisocyanate, 1,2-propylene diisocyanate, 1,2-butylene diisocyanate, 2,3-butylene diisocyanate, 1,3-butylene diisocyanate, 2,4,4- or 2,2,4-trimethylhexamethylene diisocyanate and 2,6-diisocyanatomethyl caproate; alicyclic diisocyanates such as 1,3-cyclopentane diisocyanate, 1,4-cyclohexane diisocyanate, 1,3-cyclohexane diisocyanate, 3isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4′-methylenebis(cyclohexyl)
  • isocyanate group-containing compounds may be used, but an aromatic, aroma-aliphatic or aliphatic isocyanate compound is preferably used and reacted so that the lubricating film after coating can have an elastic modulus of 0.5 to 20 GPa, mold galling can be prevented and a sufficiently high shapability can be attained.
  • Examples of the compound having at least two active hydrogen groups per one molecule include compounds having an amino group, a hydroxyl group or a mercapto group as the group having active hydrogen, Among these, in view of the reaction rate with an isocyanate group and the mechanical properties after coating, compounds having a hydroxy group are preferred. Also, from the standpoint of good mechanical properties of the film, the number of functional groups in the compound having active hydrogen groups is preferably from 2 to 6, more preferably from 2 to 4. Furthermore, in view of the concentration of a urethane bond which affects the final film performance and also in view of workability in production, the molecular weight of the compound having active hydrogen groups is preferably from 200 to 10,000, more preferably from 300 to 5,000.
  • Examples of the compound having a hydroxyl group as the active hydrogen group include a polyester polyol, a polyether polyol, a polyether ester polyol, a polyester amide polyol, an acrylpolyol, a polycarbonate polyol, a polyhydroxyalkane, a caster oil, a polyurethane polyol, and a mixture thereof.
  • a low molecular weight polyol having a molecular weight of 62 to 200 may be mixed.
  • the low molecular weight polyol include glycols for use in the production of a polyester polyol, such as ethylene glycol, propylene glycol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,9-nonanediol, 1,8-nonanediol, neopentyl glycol, 2-methylpentanediol, 3-methylpentanediol, 3,3-dimethylolheptane, 2,2,4-trimethyl-1,3-pentanediol, 2,4diethyl-1,5-pentanediol,
  • Examples of the compound having at least one or more active hydrogen group within the molecule and containing an acid group such as carboxyl group or sulfonic acid group include sulfonic acid-containing compounds, such as 2-oxyethanesulfonic acid, phenolsulfonic acid, sulfobenzoic acid, sulfosuccinic acid, 5-sulfoisophthalic acid, sulfanilic acid, 1,3-phenylenediamine-4,6-disulfonic acid and 2,4-diaminotoluene-5-sulfonic acid, derivatives thereof and polyester polyols obtained by copolymerizing these compounds or derivatives; carboxyl group-containing compounds, such as 2,2-dimethylolpropionic acid, 2,2-dimethylolbutyric acid, 2,2-dimethylolvaleric acid, dioxymaleic acid, 2,6-dioxybenzoic acid and 3,4-diaminobenzoic acid, derivatives thereof and
  • a carboxyl group or a sulfonic acid group may be introduced into the alkali-soluble polyurethane aqueous composition by copolymerizing at least one or more of the above-described acid radical-containing compounds during the production of a polyurethane prepolymer or reacting it in the chain elongation reaction.
  • the acid group is introduced into the polyurethane molecule in the acid value range of 30 to 180 whereby, despite the high elastic modulus of 0.5 to 20 GPa after coating on a metal surface, flexibility capable of allowing shaping, even under severe shaping conditions, is imparted to the film.
  • Examples of the neutralizer which can be used include primary amines such as ammonia, methylamine, ethylamine, n-propylamine and n-butylamine, secondary amines such as dimethylamine, diethylamine and diisopropylamine, tertiary amines such as trimethylamine, triethylamine, triethanolamine, triisopropanolamine and dimethylethanolamine, and alkali metal hydrides such as sodium hydroxide and potassium hydroxide. These may be used individually or in a combination of two or more thereof.
  • the neutralizer may be added directly to the polyurethane prepolymer or added to water when the prepolymer is dissolved or dispersed in the water.
  • the amount of the neutralizer added is preferably from 0.1 to 2.0 equivalent, more preferably from 0.3 to 1.3 equivalent, to the hydrophilic group.
  • sodium hydroxide or potassium hydroxide is preferably contained as the neutralizer. This is far of the following reasons.
  • sodium hydroxide or sulfonium hydroxide is used as the neutralizer for the carboxyl group (—COOH) or sulfonic acid group (—SO 3 H) in the polyurethane composition
  • the sodium ion or potassium ion becomes a neutralizing ion species of the carboxyl group or sulfonic acid group and such an ion is not dissipated by volatilization even at the film formation on a metal sheet but remains in the film as the neutralizing ion species (for example, —COO ⁇ Na + or —SO 3 ⁇ K + ) after the film is formed.
  • the film can have good alkali solubility.
  • a neutralizer such as an amine has a readily volatilized property and, due to the conditions at the film formation on a metal sheet, the neutralizer is partially or entirely volatilized to return the neutralization part which is once neutralized by the neutralizer to the carboxyl group or sulfonic acid group and, as a result, even when the surface-treated metal product is dipped in an alkali, hydration scarcely occurs.
  • the film fails to have a good alkali solubility, in some cases.
  • a surfactant or the like may be used.
  • an organic solvent may also be used.
  • specific examples of the organic solvent include acetone, methyl ethyl ketone, ethyl acetate, acetonitrile and N-methylpyrrolidone.
  • the amount of the organic solvent is preferably on the order of 3 to 50 mass % based on the reaction raw materials.
  • the polyurethane prepolymer is dissolved or dispersed in water using a homogenizer, a mixer or the like.
  • the temperature is preferably from room temperature to about 70° C. so as to prevent the evaporation of the basic substance neutralizing the hydrophilic group and ensure the workability.
  • the concentration of the polyurethane aqueous composition is preferably from 10 to 50 mass % so as to not excessively increase the viscosity and to maintain the storage stability.
  • chain elongating agent may be further reacted to give a high molecular weight.
  • chain elongating agent for example, known polyamine compounds are used.
  • known polyamine compounds include diamines such as ethylenediamine, 1,2-propanediamine, 1,6-hexamethylenediamine, piperazine, 2,5-dimethylpiperazine, isophoronediamine, 4,4′-dicyclohexylmethanediamine, 3,3′-dimethyl-4,4′-dicyclohexylmethanediamine and 1,4-cyclohexanediamine; polyamines such as diethylenetriamine, dipropylenetriamine, triethylenetetramine and tetraethylenepentamine; compounds having an amino group and a hydroxyl group, such as hydroxyethylhydrazine, hydroxyethyldiethylenetriamine, 2-[(2-aminoethyl)amino]ethanol and 3-aminopropanedio
  • a film forming aid In the alkali-soluble polyurethane aqueous composition of the present invention, a film forming aid, a leveling agent, a defoaming agent and a weather resistance stabilizer may be added, if desired.
  • the film of the alkali-soluble polyurethane aqueous composition of the present invention is most efficiently solubilized and removed by alkali degreasing but may also be removed by using warm water or a solvent.
  • the lubricating function-imparting agent for use in the present invention has a function of reducing the coefficient of friction on the film surface and thereby further imparting lubricity to prevent mold galling or the like and to improve the press workability and the drawing workability.
  • the lubricating function-imparting agent for use in the present invention is not particularly limited as long as it is a particle mainly comprising (a) a solid lubricant or wax comprising a long-chain aliphatic hydrocarbon and having no polar group, (b) a solid lubricant or wax having a long-chain aliphatic hydrocarbon group (long-chain alkyl group) and a polar group within one molecule or (c) a solid lubricant or wax comprising a fluorine-containing resin and it can be stably and uniformly dispersed in an aqueous treating solution.
  • Preferred examples of the lubricating function-imparting agent for use in the present invention include those comprising a polyolefin-base wax with the hydrocarbon group having from 125 to 700 carbons, such as polyethylene and polypropylene, or a paraffin with the hydrocarbon group having from 32 to 72 carbons (microwax) as the component (a), a stearic acid-base solid lubricant as the component (b), or a polytetrafluoroethylene, a polychlorotrifluoroethylene, a polyvinylidene fluoride, a polyvinyl fluoride or the like as the component (c), and those obtained by mixing or modifying one or more of these solid lubricants or waxes (a), (b) and (c).
  • a polyolefin-base wax with the hydrocarbon group having from 125 to 700 carbons such as polyethylene and polypropylene, or a paraffin with the hydrocarbon group having from 32 to 72 carbons (microwax) as the
  • Examples of the solid lubricant or wax (b) include a higher aliphatic alcohol with the hydrocarbon group having from 12 to 22 carbons, such as cetyl alcohol and stearyl alcohol; a higher fatty acid with the hydrocarbon group having from 13 to 17 carbons, such as stearic acid and 12-hydroxystearic acid; a metal soap comprising a divalent metal and a higher fatty acid with the hydrocarbon group having from 12 to 30 carbons, such as lead stearate, zinc stearate and calcium stearate; as the ester type, an ester of a higher fatty acid with the hydrocarbon group having from 13 to 17 carbons and another hydrocarbon, an ester of a higher aliphatic alcohol with the hydrocarbon group having from 13 to 17 carbons and an aliphatic dicarboxylic acid or a fatty acid, and an ester of a polyhydric alcohol and a higher fatty acid, such as glycerin tristearate and trimethylolpropane tristearate; as
  • the average particle size of the particle-shape lubricating function-imparting agent for use in the present invention is preferably 10 ⁇ m or less. If the average particle size exceeds 10 ⁇ m, not only does the film lose continuity and uniformity to decrease the adhesion to the substrate steel sheet or the adhesive property of the coating material and generate the peeling of the lubricating function-imparting agent but, also, the coating material composition suffers from low storage stability.
  • the average particle size of the lubricating function-imparting agent is more preferably from 0.5 to 6 ⁇ m.
  • the “average particle size” as used herein means “d50 (50% average particle size)” obtained by plotting a relational curve between the particle size and the cumulative volume ratio and reading the particle size when the cumulative volume ratio is 50%. At this timer the measurement is performed as follows. A laser ray is irradiated in the state where particles are dispersed in a solvent, and the interference fringe generated is analyzed to determine d50 or the particle size distribution. In the measurement by the present inventors, a SALD-3000S manufactured by Shimadzu Corporation was used. The “d50” can also be measured by a general-purpose measuring device of other companies, such as a CILAS manufactured by CILAS and an LA manufactured by Horiba Seisakusho.
  • the amount of the lubricating function-imparting agent added is from 1 to 30 mass %, preferably from 5 to 20 mass %, based on the solid content of the polyurethane aqueous composition. If the amount added is less than 1%, the required lubricating effect cannot be obtained, whereas if it exceeds 30 mass %, problems arise, for example, the film strength decreases or the lubrication-imparting agent is desorbed.
  • silica is added.
  • the silica particle may be any silica particle such as water-dispersible colloidal silica, ground silica and vapor phase silica.
  • the primary particle size is preferably from 2 to 30 nm and the secondary aggregated particle size is preferably 100 nm or less.
  • the amount of silica added is preferably from 1 to 30 mass % based on the solid content of the alkali-soluble polyurethane aqueous composition. If the amount added is less than 1%, a sufficiently high effect of improving the corrosion resistance is not obtained and a sufficiently strong adhesion to the lower layer is also not obtained. If the amount of silica added exceeds 30%, the film elongation decreases and this causes a reduction in workability to readily generate galling.
  • the lubricating film coated on the surface-lubricated metal product of the present invention may contain, if desired, a pigment for imparting a design property, an electrically conducting additive for imparting electrical conductivity, a thickening agent, a defoaming agent, a dispersant, a desiccating agent, a stabilizer, an anti-skinning agent, an antifungal, an antiseptic, an anti-freezing agent, and the like, according to the purpose within range which does not deteriorate the properties of film.
  • the elastic modulus of the alkali-soluble lubricating film formed on a metal surface is, as the elastic modulus after coating, from 0.5 to 20 GPa, preferably from 1.0 to 10 GPa, at 25° C. If this elastic modulus is less than 0.5 GPa, the film is readily damaged under severe press shaping conditions such as deep drawing or ironing and a sufficiently high shapability cannot be expected, whereas if it exceeds 20 GPa, the film cannot maintain the flexibility capable of allowing shaping under severe shaping conditions.
  • the “elastic modulus after coating” as used herein means a Young's modulus obtained based on the Universal hardness testing specified in DIN50359 and the like.
  • the elastic modulus of the alkali-soluble lubricating film formed on a metal surface is, as the elastic modulus after coating, from 0.5 to 6.0 GPa at 25° C. and, at the same time, the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) exceeds 10%, or the elastic modulus after coating exceeds 6.0 GPa at 25° C. and, at the same time, the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) is 10% or less, and it is more preferred that the elastic modulus after coating is from 1.0 to 6.0 GPa at 25° C.
  • the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) exceeds 10%, or the elastic modulus after coating is from more than 6.0 GPa to 10 GPa at 25° C. and, at the same time, the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition (A) is 10% or less.
  • the film lacks in the balance between elasticity and elongation, and a sufficiently high shapability cannot be exerted.
  • the glass transition temperature of the alkali-soluble polyurethane aqueous composition (A) in the alkali-soluble lubricating film formed on a metal surface is preferably 100° C. or more. Under severe press shaping conditions of continuously performing deep drawing or ironing without using a lubricating oil, a steel sheet surface sometimes reaches a temperature of 100° C.
  • the glass transition temperature of the alkali-soluble polyurethane aqueous composition (A) forming a continuous phase in the lubricating film is less than 100° C.
  • the elastic modulus of the lubricating film decreases to induce mold galling and the lubricating film peeled at the galled part adheres to the metal mold or measurement failures such as impairment of the appearance on the meal surface are caused.
  • the “glass transition temperature” as used herein means a glass transition temperature determined from peaks on a DSC curve obtained using a differential scanning calorimetry (DSC) device at a temperature increasing rate of 5.0 ° C./min in a dry nitrogen atmosphere.
  • the thickness of the lubricating film coated on the surface-lubricated metal product of the present invention is from 0.5 to 10 ⁇ m. If the thickness is less than 0.5 ⁇ m, the film pressed at the working cannot prevent damage to the plating layer and in addition, due to sliding, the required workability cannot be obtained. If the thickness exceeds 10 ⁇ m, peeled film dust increases at the shaping and this requires frequent cleaning of the metal mold, giving rise to reduction in the productivity.
  • the lubricating resin film of the present invention is coated on both front and back surfaces or one surface of a metal product according to the purpose.
  • the lubricating film coated on the surface-lubricated metal product of the present invention can be formed by coating the film using a conventionally known method such as roll coater coating method and spray method, and bake-drying it.
  • the substrate may be subjected to a phosphate treatment or a chromate treatment.
  • the chromate treatment may be any of an electrolysis-type chromate treatment, a reaction-type chromate treatment and a coating-type chromate treatment.
  • the chromate film is preferably a film formed by coating a chromate solution comprising a partially reduced chromic acid and one or more member selected from silica, phosphoric acid and hydrophilic resin, and drying the solution.
  • the amount of phosphate attached is preferably from 0.5 to 3.5 g/m 2 as phosphate.
  • the amount of chromate attached is, in terms of metal chromium, preferably from 5 to 150 mg/m 2 , more preferably from 10 to 50 mg/m 2 . If the amount attached is less than 5 mg/m 2 , an effect of giving excellent corrosion resistance cannot obtained, whereas if it exceeds 150 mg/m 2 , the chromate film undergoes cohesion failure during shaping and the workability decreases.
  • the substrate may be further subjected to an acid washing treatment, an alkali treatment, an electrolytic reduction treatment, a cobalt plating treatment, a nickel plating treatment, a silane coupling agent treatment or an inorganic silicate treatment.
  • the metal used is not particularly limited and examples of the metal which can be used include aluminum, titanium, zinc, copper, nickel, an alloy containing such a metal, and steel.
  • the components are not particularly limited and either a common steel or a chromium-containing steel, such as stainless steel, may be used.
  • the shape of the steel product is also not limited and a steel sheet such as cold-rolled steel sheet and hotrolled steel sheet, a steel tube, a steel wire or the like can be used.
  • a covering plating layer may be present on the surface of a steel and the kind thereof is not limited but examples of the plating layer which can be used include a zinc-base plating layer such as zinc plating, zinc-nickel plating, zinc-iron plating, zinc-chromium plating, zinc-aluminum plating, zinc-titanium plating, zinc-magnesium plating and zinc-manganese plating, an aluminum or aluminum alloy plating layer, a lead or lead alloy plating layer, a tin or tin alloy plating layer, and those plating layers where a small amount of one or more heteroelement such as cobalt, molybdenum, tungsten, nickel, titanium, chromium, aluminum, manganese, iron, magnesium, lead, antimony, tin, copper, cadmium and arsenic is contained or an inorganic material such as silica, alumina and titania is dispersed.
  • a zinc-base plating layer such as zinc plating, zinc-
  • the present invention can also be applied to a multilayer plating layer comprising a combination of the above-described plating and another kind of plating such as iron plating and iron-phosphorus plating.
  • the plating method is not particularly limited and electroplating, hot dipping, vapor deposition plating and the like can be used.
  • the treatment after plating includes, for example, a zero spangling treatment which is an appearance uniformalizing treatment after hot dipping, an annealing treatment which is a treatment for reforming the plating layer, and temper-rolling for adjusting the surface state or material quality, however, in the present invention, the after-treatment is not particularly limited and any of these treatments can be applied.
  • a lubricating oil or a lubricating anti-rust oil can be further coated on the film.
  • the lubricating oil or lubricating anti-rust oil coated is preferably an oil which does not swell or dissolve the lubricating film of the present invention.
  • FIGS. 1 to 3 The process of producing and using the alkali soluble lubricant surface-treated metal product of the present invention is described below by referring to FIGS. 1 to 3 .
  • An alkali-soluble lubricating film-forming composition is coated on a steel sheet 1 to form a lubricating film 2 (FIG. 1).
  • the steel sheet 1 having formed thereon the lubricating film 2 is subjected, for example, to deep drawing and thereby a molded product 3 is obtained.
  • This molded product comprises a steel sheet 4 and a lubricating film 5 and on the steel sheet 4 , and scratching or galling is not observed (FIG. 2).
  • the metal product 3 is treated with an alkali solution by a dipping method or a spray method to remove the lubricating film 5 and obtain a metal product 4 as a final product (FIG. 3).
  • Zinc electroplated steel sheet (thickness: 0.8 mm, plated amount: 20 g/m 2 )
  • Zinc-nickel alloy electroplated steel sheet (thickness: 0.8 mm, plated amount: 20 g/m 2 )
  • Zinc-iron alloy electroplated steel sheet (thickness: 0.8 mm, plated amount: 20 g/m 2 )
  • Zinc hot-dipped steel sheet (thickness: 0.8 mm, plated amount: 150 g/m 2 )
  • Zinc-iron alloy hot-dipped steel sheet (thickness: 0.8 mm, plated amount: 45 g/m 2 )
  • Zinc-aluminum alloy hot-dipped steel sheet (thickness: 0.8 mm, plated amount: 150 g/m 2 )
  • Aluminum-silicon-magnesium alloy hot-dipped steel sheet (thickness: 0.8 mm, plated amount. 50 g/m 2 )
  • the chromate treatment was not applied.
  • alkali-soluble polyurethane aqueous compositions used were prepared as follows.
  • PE wax A low-density polyethylene wax, softening temperature: 110° C., average particle size: 4.0 ⁇ m, dispersed as an aqueous emulsion, solid content: 40 mass %)
  • PE wax B low-density polyethylene wax, softening temperature: 110° C., average particle size: 1.0 ⁇ m, dispersed as an aqueous emulsion, solid content: 40 mass %)
  • PTFE wax polytetrafluoroethylene wax, average particle size: 0.8 ⁇ m, dispersed as an aqueous emulsion, solid content: 60 mass %)
  • Paraffin wax synthetic paraffin wax, melting point: 105° C., average particle size: 5.0 ⁇ m, dispersed as an aqueous emulsion, solid content: 33 mass %)
  • Calcium stearate (average particle size: 2.0 ⁇ m, dispersed as an aqueous emulsion, solid content: 40 mass %)
  • colloidal silica having a particle size of 10 to 20 nm, a pH of 8.6 and a heating residue of about 20 mass % was added to a content of 10 mass % in the film.
  • Polyurethane aqueous composition 320 parts by weight (80 mass % in of Production Example 1 terms of solid content in film)
  • a coating solution having the constitution shown above was coated on a metal sheet by a bar coater and bake-dried at a metal sheet achievable temperature of 80° C. using a heating furnace at 180° C. to form a lubricating film, having a composition shown in Tables 1 and 2, on the metal sheet.
  • a surface-lubricated metal sheet of 1 cm ⁇ 1 cm square was dipped in hydrofluoric acid and the free film after the elution of silica portion was attached on a stainless steel sheet to prepare a test sample.
  • Example Nos. 2 to 47 and Comparative Example Nos. 48 to 65 Surface-lubricated metal sheets were produced in the same manner as in Example 1 by baking a lubricating film having a composition shown in Tables 1 and 2 (Example Nos. 2 to 47 and Comparative Example Nos. 48 to 65) on each metal sheet.
  • Example Nos. 2 to 47 and Comparative Example Nos. 48 to 65 similarly to Example 1, it was confirmed by FT-IR analysis that a polyurethane composition is contained in the film.
  • an alkali-soluble acrylic aqueous composition as a comparative material of the polyurethane aqueous composition, the film formation was performed in the same manner (Comparative Example Nos. 54, 55, 61 and 62).
  • the elastic modulus of film after coating on a metal surface was determined under the following conditions using an ultrafine hardness testing machine “FISHER SCOPE H-100” manufactured by Fisher Instrument Co. This measurement can be performed not only by this device but also by other similar general-purpose devices. Indenter:
  • the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition as the main component of the lubricating film was determined under the following conditions using STROGRAPH R manufactured Toyo Seiki Seisaku-Sho, Ltd. This measurement can be performed not only by this device but also by using a general tensile tester made by another company.
  • Measurement temperature 25° C.
  • chuck-to-chuck distance 10 mm
  • pulling rate 5 mm/min.
  • the tensile elongation percentage of the alkali-soluble polyurethane aqueous composition constituting the surface-treating film of the alkali soluble lubricant surface-treated metal product may be measured as follows. An alkali-soluble surface-lubricating film is dissolved from a surface-treated metal product to remove solid matters such as lubricating function-imparting agent and silica and thereby separate the alkali-soluble polyurethane aqueous composition, then a thin film of the alkali-soluble polyurethane aqueous composition is formed in the same manner as above, and the tensile elongation percentage thereof is measured.
  • the glass transition temperature of the polyurethane aqueous composition in the lubricating film was determined from the peak on a DSC curve obtained under the following conditions using a differential scanning calorimeter (DSC-6200R) manufactured by Seiko Instruments Inc. This can also be measured by using a general-purpose device made by another company.
  • DSC-6200R differential scanning calorimeter
  • the measurement was performed from room temperature to 230° C. at a temperature-rising rate of 5.0° C./min in a dry nitrogen flow atmosphere.
  • a shaping test was performed under the following conditions using a hydraulic shaping tester with a cylindrical punch.
  • the evaluation was performed at the two levels of room temperature and a mold temperature (100° C.) elevated due to continuous pressing.
  • Punch diameter 70 mm ⁇ Blank diameter: 150 mm ⁇ Pressing load: 5 kgf/cm 2
  • Shaping rate 3.3 ⁇ 10 ⁇ 2 m/s
  • Tool condition FCD-500
  • the steel sheet was shaped to 80% of the maximum shaping height and the mold galling was evaluated according to the following indices.
  • X The steel sheet could be shaped but a large number of linear galling flaws were generated on the surface.
  • test piece was sprayed with a degreasing solution FC-4358 (produced by Nihon Parkerizing Co., Ltd., pH: adjusted to 0.5, liquid temperature: 40° C.) for 8 seconds, then washed with water and dried and thereafter, the film residual ratio was measured by infrared spectroscopic analysis and evaluated.
  • FC-4358 produced by Nihon Parkerizing Co., Ltd., pH: adjusted to 0.5, liquid temperature: 40° C.
  • ⁇ The film residual area percentage is 5% or less.
  • ⁇ The film residual area percentage is more than 5% to 10%.
  • X The film residual area percentage is more than 10%.
  • the tensile elongation percentage of the aqueous composition was 1% in the case of Production Example 1, 7% in the case of Production Example 2, 299% in the case of Production Example 3, 147% in the case of Production Example 4, 1,125% in the case of Production Example 5, and 14% in the case of acrylic resin.
  • the surface-lubricated metal product according to the present invention exhibits excellent shapability in both cases of room temperature and a mold temperature (100° C.) elevated due to continuous pressing, generates less debris after shaping and ensures good film removal by the alkali degreasing.
  • the aqueous composition, the amount of wax added, the film thickness and the elastic modulus after coating are each out of the range specified in the present invention, poor shapability results and resin debris is readily generated after shaping.
  • the metal product of the present invention is free of mold galling even under severe shaping conditions and is deprived of the lubricating film after degreasing and therefore, is suitably used for uses where the glossy metal surface or a metal texture is required or a good welding property is demanded.
  • the present invention has a very high industrial value.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Wood Science & Technology (AREA)
  • Mechanical Engineering (AREA)
  • Laminated Bodies (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Lubricants (AREA)
  • Paints Or Removers (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
US10/416,976 2000-11-16 2001-11-16 Metal product with excellent moldability surface-treated with alkali-soluble lubricant Abandoned US20040033909A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2000350175A JP2002144478A (ja) 2000-11-16 2000-11-16 成形性に優れたアルカリ可溶型潤滑表面処理金属製品
JP2000-350175 2000-11-16
PCT/JP2001/010062 WO2002040266A1 (fr) 2000-11-16 2001-11-16 Produit metallique possedant des caracteristiques excellentes de moulage de sa surface traitee par un lubrifiant soluble dans un milieu alcalin

Publications (1)

Publication Number Publication Date
US20040033909A1 true US20040033909A1 (en) 2004-02-19

Family

ID=18823455

Family Applications (1)

Application Number Title Priority Date Filing Date
US10/416,976 Abandoned US20040033909A1 (en) 2000-11-16 2001-11-16 Metal product with excellent moldability surface-treated with alkali-soluble lubricant

Country Status (8)

Country Link
US (1) US20040033909A1 (ko)
EP (1) EP1359006A4 (ko)
JP (1) JP2002144478A (ko)
KR (1) KR100521284B1 (ko)
CN (1) CN1309556C (ko)
AU (2) AU2002214316B2 (ko)
CA (1) CA2428000A1 (ko)
WO (1) WO2002040266A1 (ko)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090129762A1 (en) * 2005-07-01 2009-05-21 Ulrich Goetz Initial Wetting Auxiliary Material for a Vaporiser Body
US20120064354A1 (en) * 2009-05-11 2012-03-15 Soshi Fujita Surface-treated metal material and process for producing the same
JP2016017136A (ja) * 2014-07-08 2016-02-01 Dic株式会社 ウレタン樹脂組成物及びそれを用いた積層体
CN109054951A (zh) * 2018-09-06 2018-12-21 武汉材料保护研究所有限公司 一种铝合金板材冲压成形加工用固体润滑膜及其制备方法
US20190112765A1 (en) * 2016-03-31 2019-04-18 BTG Eclépens S.A. Masked coating blade

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4671609B2 (ja) * 2004-01-26 2011-04-20 日本パーカライジング株式会社 潤滑性水系ポリウレタン樹脂組成物、それを用いる亜鉛系メッキ鋼板の表面潤滑処理方法及びその表面処理鋼板
JP5105577B2 (ja) * 2005-08-25 2012-12-26 東洋鋼鈑株式会社 マグネシウム合金成形加工体の製造方法およびマグネシウム合金成形加工体
KR101136488B1 (ko) * 2009-11-06 2012-04-20 (주)알오호일 메탈 돔용 알루미늄층 금속박판 제조방법
JP6136105B2 (ja) * 2012-05-07 2017-05-31 東洋インキＳｃホールディングス株式会社 水性ポリウレタン樹脂およびその利用
FR3013244B1 (fr) * 2013-11-19 2015-11-20 Constellium France Procede de fabrication de capsules de bouchage metalliques brillantes
CN103878550B (zh) * 2014-03-25 2016-03-02 南方风机股份有限公司 一种有/无法兰的黄铜套的加工工艺
JP6512204B2 (ja) * 2015-12-04 2019-05-15 Ｊｆｅスチール株式会社 ステンレス鋼板用潤滑塗料および潤滑ステンレス鋼板
CN109609802B (zh) * 2018-12-01 2021-05-04 温州亮彩眼镜科技有限公司 一种无铅无镍环保眼镜铜针
CN110484040B (zh) * 2019-08-16 2021-05-18 杭州普络飞新材料科技有限公司 一种空调室外机用pcm板及其生产工艺
CN112122437B (zh) * 2020-08-05 2022-12-27 浙江安胜科技股份有限公司 一种保温容器智能化拉伸处理方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5244587A (en) * 1990-07-12 1993-09-14 Daido Machinery, Ltd. Forging lubricant and a method for forming a lubricant coat on the surface of a linear material
US5248431A (en) * 1990-02-06 1993-09-28 Dai-Ichi Kogyo Keiyaku Co., Ltd. Metal working lubricating composition
US6479152B1 (en) * 1999-11-12 2002-11-12 Nippon Steel Corporation Lubricative stainless steel sheets and pipes and method of producing lubricative stainless steel pipes
US6730407B2 (en) * 2000-08-09 2004-05-04 Nippon Steel Corporation Soluble lubricating surface-treated stainless steel sheet with excellent shapability for fuel tank and method for manufacturing fuel tank
US6797770B1 (en) * 1999-02-26 2004-09-28 Nippon Steel Corporation Coating composition capable of forming alkali-soluble lubricating film suitable for forming and use thereof

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3026385B2 (ja) * 1992-03-13 2000-03-27 関西ペイント株式会社 プレス加工性に優れた潤滑鋼板用皮膜組成物及びこれを使用した潤滑鋼板
JP2743237B2 (ja) * 1992-12-02 1998-04-22 新日本製鐵株式会社 プレス油省略可能非脱膜型潤滑めっき鋼板
JP3343842B2 (ja) * 1996-03-18 2002-11-11 日新製鋼株式会社 接着剤との接着性および耐パウダリング性に優れたアルカリ可溶型樹脂皮膜被覆亜鉛系めっき鋼板
JPH10109376A (ja) * 1996-10-08 1998-04-28 Kawasaki Steel Corp 非アルカリ脱膜型潤滑樹脂処理鋼板およびその製造方法
JP3626008B2 (ja) * 1998-03-24 2005-03-02 日新製鋼株式会社 耐カジリ性および加工性に優れたアルカリ可溶型樹脂皮膜被覆ステンレス鋼板
JP3647659B2 (ja) * 1998-11-26 2005-05-18 日新製鋼株式会社 耐カジリ性および加工性に優れたアルカリ可溶型樹脂皮膜被覆めっき鋼板

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5248431A (en) * 1990-02-06 1993-09-28 Dai-Ichi Kogyo Keiyaku Co., Ltd. Metal working lubricating composition
US5244587A (en) * 1990-07-12 1993-09-14 Daido Machinery, Ltd. Forging lubricant and a method for forming a lubricant coat on the surface of a linear material
US6797770B1 (en) * 1999-02-26 2004-09-28 Nippon Steel Corporation Coating composition capable of forming alkali-soluble lubricating film suitable for forming and use thereof
US6479152B1 (en) * 1999-11-12 2002-11-12 Nippon Steel Corporation Lubricative stainless steel sheets and pipes and method of producing lubricative stainless steel pipes
US6730407B2 (en) * 2000-08-09 2004-05-04 Nippon Steel Corporation Soluble lubricating surface-treated stainless steel sheet with excellent shapability for fuel tank and method for manufacturing fuel tank

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090129762A1 (en) * 2005-07-01 2009-05-21 Ulrich Goetz Initial Wetting Auxiliary Material for a Vaporiser Body
US20120064354A1 (en) * 2009-05-11 2012-03-15 Soshi Fujita Surface-treated metal material and process for producing the same
US8956729B2 (en) * 2009-05-11 2015-02-17 Nippon Steel & Sumitomo Metal Corporation Surface-treated metal material and process for producing the same
JP2016017136A (ja) * 2014-07-08 2016-02-01 Dic株式会社 ウレタン樹脂組成物及びそれを用いた積層体
US20190112765A1 (en) * 2016-03-31 2019-04-18 BTG Eclépens S.A. Masked coating blade
US11466407B2 (en) * 2016-03-31 2022-10-11 Btg Eclepens S.A. Masked coating blade
CN109054951A (zh) * 2018-09-06 2018-12-21 武汉材料保护研究所有限公司 一种铝合金板材冲压成形加工用固体润滑膜及其制备方法

Also Published As

Publication number Publication date
JP2002144478A (ja) 2002-05-21
EP1359006A1 (en) 2003-11-05
CN1309556C (zh) 2007-04-11
AU1431602A (en) 2002-05-27
CA2428000A1 (en) 2002-05-23
WO2002040266A1 (fr) 2002-05-23
KR100521284B1 (ko) 2005-10-14
CN1474747A (zh) 2004-02-11
KR20030046521A (ko) 2003-06-12
EP1359006A4 (en) 2005-01-26
AU2002214316B2 (en) 2005-09-08

Similar Documents

Publication Publication Date Title
US6730407B2 (en) Soluble lubricating surface-treated stainless steel sheet with excellent shapability for fuel tank and method for manufacturing fuel tank
AU2002214316B2 (en) Metal product with excellent moldability surface-treated with alkali-soluble lubricant
AU761261B2 (en) Coating composition capable of forming alkali-soluble lubricating film suitable for forming and use thereof
TWI408255B (zh) Coated steel plate
CA2442748C (en) Alkali-soluble-film surface-lubricated metal product excellent in moldability and long-term stable film-removability independent of film drying temperature
JP4318610B2 (ja) 表面処理金属板
JP4132729B2 (ja) 成形性に優れた燃料タンク用可溶型潤滑表面処理ステンレス鋼板および燃料タンクの製造方法
JP3872969B2 (ja) 成形性および耐エマルジョン型作動油性に優れたハイドロフォーム用可溶型潤滑表面処理金属製品およびその成形加工方法
JP2003027256A (ja) 成形性および皮膜乾燥温度に依存せず長期安定脱膜性に優れたアルカリ可溶型潤滑表面処理金属製品
JP4392967B2 (ja) 成形性に優れたアルカリ可溶型潤滑表面処理金属製品
JP2006218856A (ja) しごき加工性、耐エマルジョン型プレス油性に優れたアルカリ可溶型潤滑鋼板
JP2003003278A (ja) 連続成形性に優れたアルカリ可溶型潤滑表面処理金属製品
JP2000102764A (ja) 連続プレス加工性、連続しごき加工性、耐食性に優れた樹脂被覆めっき鋼板
JP2006299406A (ja) 耐久性に優れた移送用潤滑表面処理鋼板

Legal Events

Date Code Title Description
AS Assignment

Owner name: NIPPON STEEL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YAMAOKA, IKURO;KANAI, HIROSHI;MIYASAKA, AKIHIRO;AND OTHERS;REEL/FRAME:014411/0508

Effective date: 20030506

Owner name: MITSUI TAKEDA CHEMICALS, INC., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:YAMAOKA, IKURO;KANAI, HIROSHI;MIYASAKA, AKIHIRO;AND OTHERS;REEL/FRAME:014411/0508

Effective date: 20030506

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION