US20030159622A1 - Barium sulphate method for producing the same and the use thereof - Google Patents
Barium sulphate method for producing the same and the use thereof Download PDFInfo
- Publication number
- US20030159622A1 US20030159622A1 US10/182,592 US18259203A US2003159622A1 US 20030159622 A1 US20030159622 A1 US 20030159622A1 US 18259203 A US18259203 A US 18259203A US 2003159622 A1 US2003159622 A1 US 2003159622A1
- Authority
- US
- United States
- Prior art keywords
- organic
- barium sulfate
- barium
- substances
- neopentyl glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- TZCXTZWJZNENPQ-UHFFFAOYSA-L barium sulfate Chemical compound [Ba+2].[O-]S([O-])(=O)=O TZCXTZWJZNENPQ-UHFFFAOYSA-L 0.000 title claims abstract description 146
- 238000004519 manufacturing process Methods 0.000 title claims description 6
- 239000002245 particle Substances 0.000 claims abstract description 35
- 239000006259 organic additive Substances 0.000 claims abstract description 20
- 238000000034 method Methods 0.000 claims description 12
- 239000000126 substance Substances 0.000 claims description 12
- 239000000725 suspension Substances 0.000 claims description 12
- WXZMFSXDPGVJKK-UHFFFAOYSA-N pentaerythritol Chemical compound OCC(CO)(CO)CO WXZMFSXDPGVJKK-UHFFFAOYSA-N 0.000 claims description 10
- 239000000344 soap Substances 0.000 claims description 10
- 150000005846 sugar alcohols Polymers 0.000 claims description 10
- 239000004033 plastic Substances 0.000 claims description 8
- 229920003023 plastic Polymers 0.000 claims description 8
- 238000002360 preparation method Methods 0.000 claims description 8
- 239000002202 Polyethylene glycol Substances 0.000 claims description 7
- QAOWNCQODCNURD-UHFFFAOYSA-L Sulfate Chemical compound [O-]S([O-])(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-L 0.000 claims description 7
- 238000002156 mixing Methods 0.000 claims description 7
- SLCVBVWXLSEKPL-UHFFFAOYSA-N neopentyl glycol Chemical compound OCC(C)(C)CO SLCVBVWXLSEKPL-UHFFFAOYSA-N 0.000 claims description 7
- 229920001223 polyethylene glycol Polymers 0.000 claims description 7
- -1 siloxanes Chemical class 0.000 claims description 7
- 229920001169 thermoplastic Polymers 0.000 claims description 7
- 239000004416 thermosoftening plastic Substances 0.000 claims description 7
- ZJCCRDAZUWHFQH-UHFFFAOYSA-N Trimethylolpropane Chemical compound CCC(CO)(CO)CO ZJCCRDAZUWHFQH-UHFFFAOYSA-N 0.000 claims description 6
- DYJIIMFHSZKBDY-UHFFFAOYSA-N (3-benzoyloxy-2,2-dimethylpropyl) benzoate Chemical compound C=1C=CC=CC=1C(=O)OCC(C)(C)COC(=O)C1=CC=CC=C1 DYJIIMFHSZKBDY-UHFFFAOYSA-N 0.000 claims description 5
- 150000001298 alcohols Chemical class 0.000 claims description 5
- 150000003857 carboxamides Chemical class 0.000 claims description 5
- 150000001735 carboxylic acids Chemical class 0.000 claims description 5
- 150000002576 ketones Chemical class 0.000 claims description 5
- 150000002895 organic esters Chemical class 0.000 claims description 5
- 229920001451 polypropylene glycol Polymers 0.000 claims description 5
- 150000004756 silanes Chemical class 0.000 claims description 5
- 229920002545 silicone oil Polymers 0.000 claims description 5
- 150000003457 sulfones Chemical class 0.000 claims description 5
- 150000003462 sulfoxides Chemical class 0.000 claims description 5
- 239000006185 dispersion Substances 0.000 claims description 4
- 239000010408 film Substances 0.000 claims description 4
- 239000012065 filter cake Substances 0.000 claims description 4
- 239000000203 mixture Substances 0.000 claims description 4
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 claims description 3
- WDIHJSXYQDMJHN-UHFFFAOYSA-L barium chloride Chemical compound [Cl-].[Cl-].[Ba+2] WDIHJSXYQDMJHN-UHFFFAOYSA-L 0.000 claims description 3
- 229910001626 barium chloride Inorganic materials 0.000 claims description 3
- 239000011248 coating agent Substances 0.000 claims description 3
- 238000000576 coating method Methods 0.000 claims description 3
- 239000000463 material Substances 0.000 claims description 3
- 150000002825 nitriles Chemical class 0.000 claims description 3
- 239000007832 Na2SO4 Substances 0.000 claims description 2
- PMZURENOXWZQFD-UHFFFAOYSA-L Sodium Sulfate Chemical compound [Na+].[Na+].[O-]S([O-])(=O)=O PMZURENOXWZQFD-UHFFFAOYSA-L 0.000 claims description 2
- 239000000853 adhesive Substances 0.000 claims description 2
- 230000001070 adhesive effect Effects 0.000 claims description 2
- 229920001971 elastomer Polymers 0.000 claims description 2
- 239000000806 elastomer Substances 0.000 claims description 2
- 229910052938 sodium sulfate Inorganic materials 0.000 claims description 2
- 239000007921 spray Substances 0.000 claims description 2
- 229920001187 thermosetting polymer Polymers 0.000 claims description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 2
- 150000002826 nitrites Chemical class 0.000 claims 2
- RQPZNWPYLFFXCP-UHFFFAOYSA-L barium dihydroxide Chemical compound [OH-].[OH-].[Ba+2] RQPZNWPYLFFXCP-UHFFFAOYSA-L 0.000 claims 1
- 238000001035 drying Methods 0.000 claims 1
- 238000010298 pulverizing process Methods 0.000 claims 1
- 238000001556 precipitation Methods 0.000 abstract description 5
- 229920000139 polyethylene terephthalate Polymers 0.000 description 7
- 239000005020 polyethylene terephthalate Substances 0.000 description 7
- 229920000642 polymer Polymers 0.000 description 6
- 239000000243 solution Substances 0.000 description 6
- 229920000728 polyester Polymers 0.000 description 5
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 4
- 229910052799 carbon Inorganic materials 0.000 description 4
- 239000000945 filler Substances 0.000 description 4
- 239000007787 solid Substances 0.000 description 4
- PNEYBMLMFCGWSK-UHFFFAOYSA-N Alumina Chemical compound [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 3
- 239000004594 Masterbatch (MB) Substances 0.000 description 3
- 239000007864 aqueous solution Substances 0.000 description 3
- 230000000052 comparative effect Effects 0.000 description 3
- 239000000123 paper Substances 0.000 description 3
- 239000000049 pigment Substances 0.000 description 3
- LYCAIKOWRPUZTN-UHFFFAOYSA-N Ethylene glycol Chemical compound OCCO LYCAIKOWRPUZTN-UHFFFAOYSA-N 0.000 description 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 239000007788 liquid Substances 0.000 description 2
- 239000003973 paint Substances 0.000 description 2
- 239000000843 powder Substances 0.000 description 2
- 239000012463 white pigment Substances 0.000 description 2
- 239000003513 alkali Substances 0.000 description 1
- 238000000149 argon plasma sintering Methods 0.000 description 1
- 229910001422 barium ion Inorganic materials 0.000 description 1
- 238000006243 chemical reaction Methods 0.000 description 1
- 238000004040 coloring Methods 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 239000012141 concentrate Substances 0.000 description 1
- 238000010924 continuous production Methods 0.000 description 1
- 239000008367 deionised water Substances 0.000 description 1
- 238000011161 development Methods 0.000 description 1
- 230000018109 developmental process Effects 0.000 description 1
- 238000003745 diagnosis Methods 0.000 description 1
- YWEUIGNSBFLMFL-UHFFFAOYSA-N diphosphonate Chemical compound O=P(=O)OP(=O)=O YWEUIGNSBFLMFL-UHFFFAOYSA-N 0.000 description 1
- 238000001914 filtration Methods 0.000 description 1
- 238000005189 flocculation Methods 0.000 description 1
- 230000016615 flocculation Effects 0.000 description 1
- 238000000227 grinding Methods 0.000 description 1
- 239000007970 homogeneous dispersion Substances 0.000 description 1
- WGCNASOHLSPBMP-UHFFFAOYSA-N hydroxyacetaldehyde Natural products OCC=O WGCNASOHLSPBMP-UHFFFAOYSA-N 0.000 description 1
- 239000012535 impurity Substances 0.000 description 1
- 239000001023 inorganic pigment Substances 0.000 description 1
- 239000000155 melt Substances 0.000 description 1
- 239000012452 mother liquor Substances 0.000 description 1
- 239000012860 organic pigment Substances 0.000 description 1
- 239000000825 pharmaceutical preparation Substances 0.000 description 1
- 229940127557 pharmaceutical product Drugs 0.000 description 1
- DLYUQMMRRRQYAE-UHFFFAOYSA-N phosphorus pentoxide Inorganic materials O1P(O2)(=O)OP3(=O)OP1(=O)OP2(=O)O3 DLYUQMMRRRQYAE-UHFFFAOYSA-N 0.000 description 1
- 238000006068 polycondensation reaction Methods 0.000 description 1
- 230000001376 precipitating effect Effects 0.000 description 1
- 239000000047 product Substances 0.000 description 1
- 238000005204 segregation Methods 0.000 description 1
- 235000012239 silicon dioxide Nutrition 0.000 description 1
- 239000000377 silicon dioxide Substances 0.000 description 1
- 238000005406 washing Methods 0.000 description 1
- 238000001238 wet grinding Methods 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F11/00—Compounds of calcium, strontium, or barium
- C01F11/46—Sulfates
- C01F11/462—Sulfates of Sr or Ba
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/02—Compounds of alkaline earth metals or magnesium
- C09C1/027—Barium sulfates
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/80—Particles consisting of a mixture of two or more inorganic phases
- C01P2004/82—Particles consisting of a mixture of two or more inorganic phases two phases having the same anion, e.g. both oxidic phases
- C01P2004/84—Particles consisting of a mixture of two or more inorganic phases two phases having the same anion, e.g. both oxidic phases one phase coated with the other
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
- Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]
- Y10T428/2991—Coated
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
- Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]
- Y10T428/2991—Coated
- Y10T428/2998—Coated including synthetic resin or polymer
Definitions
- This invention relates to barium sulfate hating an average particle diameter d 50 of from 0.1 to 10 ⁇ m and precipitated by mixing of barium- or of sulfate-containing solution, a process for its preparation and its use.
- Barium sulfate is used in particular in the production of photographic paper, paints and plastics as well as in medical diagnosis and in medical plastics.
- Barium sulfate is a high-quality, pure white, inert, acid- and alkali-resistant filler which is completely weather-resistant.
- Very finely-divided barium sulfate imparts colour stability and gloss to photographic paper.
- the very finely-divided barium sulfate produces resistance to flocculation in organic and inorganic pigments, so that segregation phenomena are largely prevented, depth of colour and purity of colour are increased and brightness and fogging are improved.
- the mechanical properties of the plastics are improved as a result of the nucleating action of the barium sulfate powder.
- thermoplastics in particular polymers containing incorporated very finely-divided barium sulfate
- the latter acts as a white pigment, scattering light at the boundaries of the barium sulfate particles to the air, so that the films have an opaque colouring and a high gloss.
- a suitable thermoplastic is, in particular polyester, in which glycol suspension containing barium sulfate has been incorporated, generally during the polycondensation.
- DE-A 26 47 713 describes an opaque, simple thermoplastic film support made of a molecularly oriented film of a synthetic, linear polyester, in which 5 to 50 wt. %, based on the weight of the polyester, of barium sulfate particles having an average particle size of from 0.5 to 10 ⁇ m is dispersed, with the proviso that the actual particle size of 99.9% of the particles does not exceed 50 ⁇ m and that at least one light-sensitive image layer is disposed on at least one surface of the film support.
- DE-C 44 31 735 discloses the coating of barium sulfate particles with phosphorus pentoxide, aluminium oxide and silicon dioxide in order to achieve an excellent adhesion between the barium sulfate particles serving as filler and the polymer, so that the light scattering does not occur.
- DE-A 22 46 818 provides a continuous process for the preparation of crystalline barium sulfate powder having an average particle size d 50 >2 ⁇ m to 20 ⁇ m by precipitating barium sulfate from barium chloride solution using sulfuric acid, wherein the barium sulfate particles having the intended particle size are deposited in the outlet of the precipitation vessel and the smaller barium sulfate particles remain in the upper region of the precipitation vessel.
- DE-A 36 35 050 provides a process for the continuous preparation of barium sulfate having a defined particle-size range, wherein barium sulfate is precipitated in a first step by the reaction of barium ions with sulfate ions.
- the suspension containing barium sulfate is withdrawn and transferred to a single-stage or multistage wet-grinding step, in which the grinding to the required particle-size range is carried out.
- the barium sulfate and mother liquor are subsequently separated.
- the barium sulfate powder chemically precipitated by the known methods has an undesirable tendency to form agglomerates which prevent a homogeneous dispersion of the barium sulfate particles as white pigment and/or filler in the thermoplastics.
- the object of the present invention is to provide barium sulfate precipitated by mixing of barium- and of sulfate-containing solution and, having an average particle diameter d 50 of from 0.1 to 10 ⁇ m; this barium sulphate is to show no tendency to form agglomerates and consequently is to have excellent properties as regards dispersibility and freedom from specks and is to produce an optimal film surface.
- This object is achieved by covering the barium sulfate with at least one organic additive, the organic additive being selected from one or more of the substances or groups of substances: carboxylic acids, soaps, metallic soaps, alcohols; polyhydric alcohols, such as pentaerythritol, neopentyl glycol and trimethylolpropane; polyalcohols, such as polypropylene glycol and polyethylene glycol; organic esters, such as neopentyl glycol dibenzoate; silanes, siloxanes, silicone oils, organic sulfones corresponding to the formula RSO 2 R, organic ketones (R—(C ⁇ O)—R), organic nitriles (RCN), organic sulfoxides (R 2 —SO 2 ), organic amides (R—(C ⁇ O)—NR′R or R—(S ⁇ O)—ONR′R).
- the organic additive being selected from one or more of the substances or groups of substances: carboxylic acids, soaps,
- the organic additives can be used in liquid or in solid form.
- barium sulfate particles can be covered with organic additive by a process described in claims 4 to 6. Further developments of this process are given in claims 7 to 9.
- the solution containing organic additive is sprayed onto the barium sulfate particles with an even-speed mixer, or the solution is added to a suspension of BaSO 4 and the mixture is homogenised by means of a dispersing apparatus.
- a particular advantage is that the barium sulfate particles aftertreated according to the invention render possible the preparation of masterbatches (pigment and filler concentrates) and compounds (mixtures) of thermoplastics in which the barium sulfate particles are so excellently dispersed that high-quality products can be made from them without special additional expense.
- the superior dispersibility in plastics of the barium sulfate particles aftertreated according to the invention is clearly shown by the fact that no specks arise in these plastics containing barium sulfate and the filter does not clog during a pressure filter test.
- the barium sulfate particles according to the invention are suitable in particular for dispersion in plastics compositions, such as thermoplastics, thermosetting plastics and elastomers.
- plastics compositions such as thermoplastics, thermosetting plastics and elastomers.
- the plastics thus treated are used in the production of fibres, coating materials, adhesives, films, film supports and the like.
- a BaSO 4 suspension was prepared.
- an aqueous solution of Na 2 SO 4 and an aqueous solution of BaCl 2 in a molar ratio of 1:0.98 were simultaneously introduced into a precipitation apparatus.
- the precipitated BaSO 4 was then filtered and washed several times with deionised water.
- the filter cake obtained was dispersed in water.
- the suspension of barium sulfate had a solids content of approximately 250 g/l and was further processed in the following manner.
- Samples A and 1 to 4 were extruded in a twin-screw extruder, with PETP (polyethylene terephthalate) in a mass ratio of 30:70 (BaSO 4 :PETP) at a temperature of approximately 270° C. A 30% masterbatch was prepared in each case.
- PETP polyethylene terephthalate
- BaSO 4 :PETP polyethylene terephthalate
- the 30% masterbatch control A and the 30% masterbatch sample 1 (containing neopentyl glycol) according to the invention were diluted to a solids content of 18 and directly extruded to form films.
- the PETP film produced using untreated BaSO 4 contained clearly visible non-dispersible particles, which were present as agglomerates (so-called specks).
- the PETP film produced using treated BaSO 4 contained scarcely any such specks, which is to be attributed to the considerably better dispersibility of the BaSO 4 treated according to the invention.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Geology (AREA)
- Inorganic Chemistry (AREA)
- Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
- Pigments, Carbon Blacks, Or Wood Stains (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Compounds Of Unknown Constitution (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/787,567 US20040167251A1 (en) | 2000-02-09 | 2004-02-26 | Barium sulfate, process for its preparation, and its use |
US11/867,361 US7776149B2 (en) | 2000-02-02 | 2007-10-04 | Barium sulfate, process for its preparation, and its use |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE10005685.7 | 2000-02-09 | ||
DE10005685A DE10005685A1 (de) | 2000-02-09 | 2000-02-09 | Bariumsulfat, Verfahren zu dessen Herstellung und dessen Verwendung |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2001/000453 A-371-Of-International WO2001058809A2 (de) | 2000-02-02 | 2001-01-17 | Bariumsulfat, verfahren zu dessen herstellung und dessen verwendung |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/787,567 Continuation US20040167251A1 (en) | 2000-02-02 | 2004-02-26 | Barium sulfate, process for its preparation, and its use |
Publications (1)
Publication Number | Publication Date |
---|---|
US20030159622A1 true US20030159622A1 (en) | 2003-08-28 |
Family
ID=7630323
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/182,592 Abandoned US20030159622A1 (en) | 2000-02-02 | 2001-01-17 | Barium sulphate method for producing the same and the use thereof |
US10/787,567 Abandoned US20040167251A1 (en) | 2000-02-02 | 2004-02-26 | Barium sulfate, process for its preparation, and its use |
US11/867,361 Expired - Lifetime US7776149B2 (en) | 2000-02-02 | 2007-10-04 | Barium sulfate, process for its preparation, and its use |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/787,567 Abandoned US20040167251A1 (en) | 2000-02-02 | 2004-02-26 | Barium sulfate, process for its preparation, and its use |
US11/867,361 Expired - Lifetime US7776149B2 (en) | 2000-02-02 | 2007-10-04 | Barium sulfate, process for its preparation, and its use |
Country Status (11)
Country | Link |
---|---|
US (3) | US20030159622A1 (de) |
EP (1) | EP1257604B1 (de) |
JP (1) | JP4824242B2 (de) |
AT (1) | ATE427983T1 (de) |
AU (1) | AU2001240513A1 (de) |
DE (2) | DE10005685A1 (de) |
DK (1) | DK1257604T3 (de) |
ES (1) | ES2325476T3 (de) |
PT (1) | PT1257604E (de) |
TW (1) | TWI264417B (de) |
WO (1) | WO2001058809A2 (de) |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2006131500A1 (en) * | 2005-06-04 | 2006-12-14 | Solvay Infra Bad Hoenningen Gmbh | Method of generating a dispersion of deagglomerated barium sulphate in plastics or plastics precursors |
WO2006131493A1 (en) * | 2005-06-04 | 2006-12-14 | Solvay Infra Bad Hoenningen Gmbh | Nanoparticle-containing macrocyclic oligoesters |
US20070217992A1 (en) * | 2004-05-04 | 2007-09-20 | Michael Berkei | Process For Preparing Dispersible Sulfate, Preferably Barium Sulfate Nanoparticles |
US20070249773A1 (en) * | 2004-06-29 | 2007-10-25 | Bernhard Becker | Polymeric Materials, Which Contain Inorganic Solids, and Methods for the Production Thereof |
US7288239B2 (en) | 2002-11-21 | 2007-10-30 | Nanosolutions Gmbh | Method for producing alkaline earth sulphate nanoparticles |
US20080108528A1 (en) * | 2006-11-03 | 2008-05-08 | M-I Llc | Methods to enhance the pneumatic handling characteristics of weighting agents |
US20080107513A1 (en) * | 2006-11-03 | 2008-05-08 | M-I Llc | Transfer of finely ground weight material |
US20080226522A1 (en) * | 2005-12-14 | 2008-09-18 | Mckee Michael W | Barium Sulfate Product |
US20080314291A1 (en) * | 2006-02-21 | 2008-12-25 | Sonja Grothe | Barium Sulfate |
US20090060960A1 (en) * | 2005-07-18 | 2009-03-05 | Petra Biehl | Preparation containing barium sulfate |
US20090318594A1 (en) * | 2006-08-25 | 2009-12-24 | Sachtleben Chemie Gmbh | Barium sulfate-containing composite |
US20100255308A1 (en) * | 2007-07-18 | 2010-10-07 | Christian Vogler | Cyclic process for the preparation of barium sulphate and lithium metal phosphate compounds |
CN107200344A (zh) * | 2017-07-07 | 2017-09-26 | 河北科技大学 | 一种微米级大颗粒硫酸钡的制备方法 |
US11434378B2 (en) | 2016-10-28 | 2022-09-06 | Sakai Chemical Industry Co., Ltd. | Barium sulfate powder and resin composition comprising same |
Families Citing this family (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE10209698A1 (de) | 2002-03-06 | 2003-09-18 | Sachtleben Chemie Gmbh | Verfahren zur Herstellung von gecoateten, feinteiligen, anorganischer Festkörpern und deren Verwendung |
DE10261806A1 (de) * | 2002-12-19 | 2004-07-01 | Universität Potsdam | Polymer-modifizierte Nanopartikel |
DE10338929A1 (de) * | 2003-08-21 | 2005-03-24 | Sachtleben Chemie Gmbh | Verfahren zur Herstellung von gecoateten, feinpartikulären anorganischen Festkörpern und deren Verwendung |
DE10357116A1 (de) * | 2003-12-06 | 2005-07-07 | Solvay Barium Strontium Gmbh | Desagglomeriertes Bariumsulfat |
DE102004010201A1 (de) * | 2003-12-06 | 2005-07-07 | Basf Coatings Ag | Desagglomeriertes Bariumsulfat enthaltende, härtbare Massen, Verfahren zu ihrer Herstellung und ihre Verwendung |
WO2005100467A1 (ja) * | 2004-04-12 | 2005-10-27 | Nisshinbo Industries, Inc. | 樹脂組成物 |
DE102005025717A1 (de) * | 2004-08-14 | 2006-02-23 | Solvay Barium Strontium Gmbh | Strontiumcarbonat-Dispersion und daraus erhältliches redispergierbares Pulver |
WO2007033953A2 (de) * | 2005-09-19 | 2007-03-29 | Sachtleben Chemie Gmbh | Beschichtungszusammensetzung für die papierherstellung |
DE102007050728A1 (de) * | 2007-10-22 | 2009-04-23 | Sachtleben Chemie Gmbh | Additiv für Polymere und Verfahren zu dessen Herstellung |
EP2157133A1 (de) * | 2008-08-19 | 2010-02-24 | Bayer MaterialScience AG | Folien mit verbesserten Eigenschaften |
DE102009006014A1 (de) * | 2009-01-23 | 2010-08-05 | Sachtleben Chemie Gmbh | Polymerzusammensetzungen mit anorganischen Füllstoffen und Verfahren zu deren Herstellung |
WO2014007325A1 (ja) * | 2012-07-06 | 2014-01-09 | 堺化学工業株式会社 | 硫酸バリウム複合粒子、それを配合した樹脂組成物及びその製造方法 |
CN103059606B (zh) * | 2012-12-24 | 2014-10-08 | 暨南大学 | 一种含有天然生物钙化物的硬质复合颗粒材料及其制备方法与应用 |
EP3425009A1 (de) | 2017-07-05 | 2019-01-09 | Venator Germany GmbH | Oberflächenbehandelte bariumsulfatpartikel und deren verwendung |
CN109279640B (zh) * | 2018-11-27 | 2020-06-23 | 清华大学 | 一种硫酸钡材料及其制备方法 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4894093A (en) * | 1987-05-30 | 1990-01-16 | Metallgesellschaft Aktiengesellschaft | Process for producing barium sulfate with reactive surface |
Family Cites Families (34)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US1915748A (en) * | 1930-04-28 | 1933-06-27 | Sachtleben Ag Fur Bergbau Und | Process for manufacturing barium sulphate of definite granule size |
GB397553A (en) * | 1932-02-26 | 1933-08-28 | Ici Ltd | Acid pickling baths |
US2006219A (en) * | 1934-02-17 | 1935-06-25 | Grasselli Chemical Co | Blanc fixe |
US2125342A (en) * | 1935-11-04 | 1938-08-02 | Du Pont | Process of making pigment barium sulphate from barium chloride |
US2358050A (en) * | 1941-12-06 | 1944-09-12 | Eastman Kodak Co | Method and apparatus for manufacturing and controlling the grain size of barium sulphate |
US2685499A (en) * | 1950-12-21 | 1954-08-03 | Eastman Kodak Co | Method of proeparing blanc fixe |
GB1158146A (en) * | 1965-08-20 | 1969-07-16 | Laporte Titanium Ltd | Improvements in and relating to the Treatment of Pigments |
CH533670A (de) * | 1968-12-05 | 1973-02-15 | Ciba Geigy Ag | Optische Aufhellmittel enthaltende anorganische Weisspigmente |
US3844810A (en) * | 1971-03-31 | 1974-10-29 | Plastic Molders Supply Co | Pigment dispersion |
JPS5142617B2 (de) * | 1971-11-12 | 1976-11-17 | ||
DE2455679C3 (de) * | 1974-11-25 | 1978-11-02 | Bayer Ag, 5090 Leverkusen | Verfahren und Bindemittel zum Herstellen einer elastischen Schicht aus Granulaten und einem Bindemittel |
EP0008083A1 (de) * | 1978-08-15 | 1980-02-20 | Ciba-Geigy Ag | Verfahren zur Herstellung von Granulaten schwerschmelzbarer Zusatzstoffe für Kunststoffe, insbesondere von Pigmenten, durch thermische Rollgranulierung und die so erhaltenen Granulate |
DE3018966A1 (de) * | 1980-05-17 | 1981-12-10 | Bayer Ag, 5090 Leverkusen | Mit organischem material beschichtetes baso (pfeil abwaerts)4(pfeil abwaerts) -pulver |
JPS5751119A (en) * | 1980-09-11 | 1982-03-25 | Onahama Sakai Kagaku Kk | Ultrafine barium sulfate |
JPS5849615A (ja) * | 1981-09-16 | 1983-03-23 | Onahama Sakai Kagaku Kk | 造粒硫酸バリウムの製造方法 |
GB2134094B (en) * | 1982-12-28 | 1987-07-22 | Onahama Sakai Kagaku Kk | A method of producing surface-treated barium sulfate and a resin composition including the same |
JPS59124958A (ja) * | 1982-12-29 | 1984-07-19 | Harima Kasei Kogyo Kk | 顔料コ−テイング剤 |
AU551948B2 (en) * | 1983-12-16 | 1986-05-15 | Mitsui Toatsu Chemicals Inc. | Producing porous film |
JPS60129240A (ja) * | 1983-12-16 | 1985-07-10 | Mitsui Toatsu Chem Inc | 多孔性フイルム及びその製造法 |
JPS60199037A (ja) * | 1984-03-22 | 1985-10-08 | Mitsui Toatsu Chem Inc | 多孔性フイルム及びその製造法 |
JPS60199036A (ja) * | 1984-03-22 | 1985-10-08 | Mitsui Toatsu Chem Inc | 多孔性フイルム及びその製造法 |
JPS60185803A (ja) * | 1984-03-05 | 1985-09-21 | 三井東圧化学株式会社 | 使い捨ておむつ |
DE3635050C2 (de) * | 1986-10-15 | 1994-09-22 | Kali Chemie Ag | Verfahren zur Herstellung von Bariumsulfat |
DE3810423A1 (de) * | 1988-03-26 | 1989-10-12 | Metallgesellschaft Ag | Thermoplastische formmassen |
DE3825774A1 (de) * | 1988-07-29 | 1990-02-01 | Metallgesellschaft Ag | Verfahren zur herstellung von ultrafeinem bariumsulfat |
EP0371530A1 (de) * | 1988-11-27 | 1990-06-06 | METALLGESELLSCHAFT Aktiengesellschaft | Verfahren zur Herstellung von chemoreaktivem Bariumsulfat unterschiedlicher Morphologie |
JPH0660301B2 (ja) * | 1989-05-08 | 1994-08-10 | 横浜ゴム株式会社 | 接着用組成物 |
JP2551649B2 (ja) * | 1989-03-07 | 1996-11-06 | 横浜ゴム株式会社 | ホースと継手金具の結合方法 |
US5149732A (en) * | 1989-03-07 | 1992-09-22 | The Yokohama Rubber Co., Ltd. | Rubber composition for polymer-metal bonding and method of hose-metal fitting attachment |
GB8909730D0 (en) * | 1989-04-27 | 1989-06-14 | Ici Plc | Inorganic particles |
DE4404953C2 (de) * | 1994-02-17 | 1997-09-18 | Metallgesellschaft Ag | Verwendung einer Oberflächenbeschichtung füe Bariumsulfat-Füllstoffe |
JP3799558B2 (ja) * | 1995-12-12 | 2006-07-19 | 日本化学工業株式会社 | 硫酸バリウムとその製造方法ならびに樹脂組成物 |
US5908498A (en) * | 1996-02-16 | 1999-06-01 | Kerr-Mcgee Chemical Llc | Process for preparing an improved low-dusting, free-flowing pigment |
DE10026791A1 (de) * | 2000-05-31 | 2001-12-06 | Solvay Barium Strontium Gmbh | Mikronisiertes Bariumsulfat |
-
2000
- 2000-02-09 DE DE10005685A patent/DE10005685A1/de not_active Ceased
-
2001
- 2001-01-17 ES ES01911489T patent/ES2325476T3/es not_active Expired - Lifetime
- 2001-01-17 AU AU2001240513A patent/AU2001240513A1/en not_active Abandoned
- 2001-01-17 US US10/182,592 patent/US20030159622A1/en not_active Abandoned
- 2001-01-17 DE DE50114820T patent/DE50114820D1/de not_active Expired - Lifetime
- 2001-01-17 EP EP01911489A patent/EP1257604B1/de not_active Revoked
- 2001-01-17 WO PCT/EP2001/000453 patent/WO2001058809A2/de active Application Filing
- 2001-01-17 AT AT01911489T patent/ATE427983T1/de active
- 2001-01-17 DK DK01911489T patent/DK1257604T3/da active
- 2001-01-17 JP JP2001558366A patent/JP4824242B2/ja not_active Expired - Lifetime
- 2001-01-17 PT PT01911489T patent/PT1257604E/pt unknown
- 2001-02-01 TW TW090101999A patent/TWI264417B/zh not_active IP Right Cessation
-
2004
- 2004-02-26 US US10/787,567 patent/US20040167251A1/en not_active Abandoned
-
2007
- 2007-10-04 US US11/867,361 patent/US7776149B2/en not_active Expired - Lifetime
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4894093A (en) * | 1987-05-30 | 1990-01-16 | Metallgesellschaft Aktiengesellschaft | Process for producing barium sulfate with reactive surface |
Cited By (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7288239B2 (en) | 2002-11-21 | 2007-10-30 | Nanosolutions Gmbh | Method for producing alkaline earth sulphate nanoparticles |
US7575734B2 (en) * | 2004-05-04 | 2009-08-18 | Centrum Fur Angewandte Nanotechnologie (Can) Gmbh | Process for preparing dispersible sulfate, preferably barium sulfate nanoparticles |
AU2004319070B2 (en) * | 2004-05-04 | 2010-03-04 | Centrum Fur Angewandte Nanotechnologie (Can) Gmbh | Process for preparing dispersible sulfate, preferably barium sulfate nanoparticles |
US20070217992A1 (en) * | 2004-05-04 | 2007-09-20 | Michael Berkei | Process For Preparing Dispersible Sulfate, Preferably Barium Sulfate Nanoparticles |
US20070249773A1 (en) * | 2004-06-29 | 2007-10-25 | Bernhard Becker | Polymeric Materials, Which Contain Inorganic Solids, and Methods for the Production Thereof |
US20100197838A1 (en) * | 2005-06-04 | 2010-08-05 | Solvay Infra Bad Hoenningen | Nanoparticle-containing macrocyclic oligoesters |
US8119716B2 (en) | 2005-06-04 | 2012-02-21 | Solvay Infra Bad Hoenningen Gmbh | Method of generating a dispersion of deagglomerated barium sulphate in plastics or plastics precursors |
WO2006131500A1 (en) * | 2005-06-04 | 2006-12-14 | Solvay Infra Bad Hoenningen Gmbh | Method of generating a dispersion of deagglomerated barium sulphate in plastics or plastics precursors |
WO2006131493A1 (en) * | 2005-06-04 | 2006-12-14 | Solvay Infra Bad Hoenningen Gmbh | Nanoparticle-containing macrocyclic oligoesters |
CN101355921B (zh) * | 2005-07-18 | 2013-03-27 | 萨克特本化学有限责任公司 | 含硫酸钡的制剂 |
US20090060960A1 (en) * | 2005-07-18 | 2009-03-05 | Petra Biehl | Preparation containing barium sulfate |
US20080226522A1 (en) * | 2005-12-14 | 2008-09-18 | Mckee Michael W | Barium Sulfate Product |
US20080314291A1 (en) * | 2006-02-21 | 2008-12-25 | Sonja Grothe | Barium Sulfate |
US7645334B2 (en) | 2006-02-21 | 2010-01-12 | Sachtleben Chemie Gmbh | Barium sulfate |
US20090326114A1 (en) * | 2006-08-25 | 2009-12-31 | Sonja Grothe | Barium sulfate-containing composite |
US20090318594A1 (en) * | 2006-08-25 | 2009-12-24 | Sachtleben Chemie Gmbh | Barium sulfate-containing composite |
WO2008058015A3 (en) * | 2006-11-03 | 2011-07-21 | M-I Llc | Methods to enhance the pneumatic handling characteristics of weighting agents |
US20080107513A1 (en) * | 2006-11-03 | 2008-05-08 | M-I Llc | Transfer of finely ground weight material |
US20080108528A1 (en) * | 2006-11-03 | 2008-05-08 | M-I Llc | Methods to enhance the pneumatic handling characteristics of weighting agents |
US20100255308A1 (en) * | 2007-07-18 | 2010-10-07 | Christian Vogler | Cyclic process for the preparation of barium sulphate and lithium metal phosphate compounds |
US8420215B2 (en) | 2007-07-18 | 2013-04-16 | Sued-Chemie Ip Gmbh & Co. Kg | Cyclic process for the preparation of barium sulphate and lithium metal phosphate compounds |
US11434378B2 (en) | 2016-10-28 | 2022-09-06 | Sakai Chemical Industry Co., Ltd. | Barium sulfate powder and resin composition comprising same |
CN107200344A (zh) * | 2017-07-07 | 2017-09-26 | 河北科技大学 | 一种微米级大颗粒硫酸钡的制备方法 |
Also Published As
Publication number | Publication date |
---|---|
EP1257604A2 (de) | 2002-11-20 |
JP4824242B2 (ja) | 2011-11-30 |
US20040167251A1 (en) | 2004-08-26 |
DE10005685A1 (de) | 2001-08-23 |
WO2001058809A2 (de) | 2001-08-16 |
ES2325476T3 (es) | 2009-09-07 |
US7776149B2 (en) | 2010-08-17 |
PT1257604E (pt) | 2009-06-29 |
ATE427983T1 (de) | 2009-04-15 |
US20080268149A1 (en) | 2008-10-30 |
TWI264417B (en) | 2006-10-21 |
EP1257604B1 (de) | 2009-04-08 |
AU2001240513A1 (en) | 2001-08-20 |
DK1257604T3 (da) | 2009-07-27 |
WO2001058809A3 (de) | 2002-04-11 |
JP2003523914A (ja) | 2003-08-12 |
DE50114820D1 (de) | 2009-05-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7776149B2 (en) | Barium sulfate, process for its preparation, and its use | |
JP3121246B2 (ja) | 処理された無機固体 | |
AU593675B2 (en) | Pigments and fillers for incorporation in synthetic resins | |
US5332433A (en) | Titanium dioxide dispersibility | |
US6126915A (en) | Titanium dioxide reduced in volatile water content, process for producing the same, and masterbatch containing the same | |
US7264672B1 (en) | Titanium dioxide pigment composite and method of making same | |
US3669896A (en) | Inorganic white pigments containing optical brighteners and process for their manufacture | |
EP0721966A1 (de) | Glänzende Emulsionsfarbe | |
US20170174864A1 (en) | Calcium carbonate filler for resin and resin composition including said filler | |
US5895795A (en) | Composition containing fine solid particles | |
JPH0641535B2 (ja) | 樹脂用顔料 | |
EP2726555B1 (de) | Behandelte anorganische pigmente mit reduzierter fotoaktivität und verbesserten antimikrobiellen eigenschaften sowie ihre verwendung für polymerzusammensetzungen | |
DE69916552T2 (de) | Feine rote Eisenoxidpigmente und diese enthaltende Farb- oder Harzzusammensetzungen | |
MXPA01002213A (es) | Agentes de tratamiento. | |
EA003372B1 (ru) | Концентрат пигмента | |
AU643070B2 (en) | Addition of additives to polymeric materials | |
US6616746B2 (en) | Titanium dioxide pigment and method for production thereof | |
US2945840A (en) | Process for manufacture of a polyethylene terephthalate in finely divided form | |
FI62327C (fi) | Porlack innehaollande vitpigment eller vitt fyllnadsmedel | |
GB2477876A (en) | Improved titanium dioxide composite particle and its method of manufacture | |
US8163828B2 (en) | Additive for polymers and process for preparation thereof | |
JPH1046097A (ja) | 着色剤組成物およびその着色剤組成物を用いて成る成形物 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: SACHTLEBEN CHEMIE GMBH, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:AMIRZADEH-ASL, DJAMSCHID;SCHWARZ, KARL-HEINZ;REEL/FRAME:013273/0330;SIGNING DATES FROM 20020816 TO 20020819 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |