TWI833789B - 基板處理方法及基板處理裝置 - Google Patents

基板處理方法及基板處理裝置 Download PDF

Info

Publication number
TWI833789B
TWI833789B TW108129948A TW108129948A TWI833789B TW I833789 B TWI833789 B TW I833789B TW 108129948 A TW108129948 A TW 108129948A TW 108129948 A TW108129948 A TW 108129948A TW I833789 B TWI833789 B TW I833789B
Authority
TW
Taiwan
Prior art keywords
gas
substrate
gap
raw material
wafer
Prior art date
Application number
TW108129948A
Other languages
English (en)
Other versions
TW202025236A (zh
Inventor
松永浩一
Original Assignee
日商東京威力科創股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日商東京威力科創股份有限公司 filed Critical 日商東京威力科創股份有限公司
Publication of TW202025236A publication Critical patent/TW202025236A/zh
Application granted granted Critical
Publication of TWI833789B publication Critical patent/TWI833789B/zh

Abstract

[課題]在藉由氣體來處理半導體裝置被形成於表面側之基板的方法中，可在基板之背面形成膜厚的面內均勻性良好之薄膜。 [解決手段]包含有：在使表面朝上的狀態下，藉由支撐部支撐基板之背面，並在基板的背面與對向於背面的導引面之間形成間隙的工程；從比被支撐於支撐部之基板更外側進行排氣的工程；及從導引面側經由氣體吐出口對間隙供給原料氣體，並且加熱原料氣體，藉由蒸鍍，在基板之背面形成薄膜的工程，且具備有如下述中至少一方的條件：(a)進行成膜之工程，係包含在成膜途中，將前述間隙的高度從第1值及小於該第1值之第2值的一者變更成另一者的工程；及(b)進行成膜之工程，係包含在成膜途中，使基板之徑方向的位置彼此不同之第1氣體吐出口及第2氣體吐出口的各吐出流量之流量比變更的工程。

Description

基板處理方法及基板處理裝置
本揭示，係關於基板處理方法及基板處理裝置。
在專利文獻1中，係記載有發現了如下述內容：在使基板的表面疏水化之際，當在基板未曝露於HMDS氣體之前，為了熱處理而對基板進行加熱時，即便提高熱處理溫度，基板之疏水化亦不會如期待般變高。因此，如下述般地對晶圓進行疏水化處理。首先，晶圓，係藉由已上升之狀態的支撐銷所支撐，藉此，在處理空間內，被水平地配置為表面朝向上方，並在該狀態下，從被設置於上側殼體之中心部的氣體吐出口實施處理氣體的供給。亦即，在將晶圓配置於自熱板隔離之上方位置的狀態下，對基板之表面側實施處理氣體的供給。此時之處理氣體的溫度，係例如15~30℃。其次，使支撐銷下降，將晶圓配置於熱板上，並將晶圓的表面溫度加熱至60~80℃。
根據像這樣的方法，可十分穩定地對基板施加因應基板之熱處理溫度所期待的疏水化度。
[先前技術文獻] [專利文獻]
[專利文獻1]日本特開2016-46515號公報
本揭示，係基於像這樣的情事而進行研究者，提供一種如下述技術：在藉由氣體來處理半導體裝置被形成於表面側之基板的方法中，可在基板之背面形成膜厚的面內均勻性良好之薄膜。
本揭示，係一種基板處理方法，在處理容器內，藉由氣體來處理半導體裝置被形成於表面側之基板的方法中，包含有：在使表面朝上的狀態下，藉由支撐部支撐基板之背面，並在該基板的背面整體與對向於該背面整體的導引面之間形成間隙的工程；以從比被支撐於前述支撐部之基板更外側進行排氣的方式，從沿著前述處理容器之圓周方向所形成的排氣口，對處理容器內進行排氣的工程；及經由與前述基板之背面對向的氣體吐出口對前述間隙供給原料氣體，並且加熱該原料氣體，藉由蒸鍍，在前述基板之背面整體形成薄膜的工程， 且具備有如下述中至少一方的條件：(條件a)前述進行成膜之工程，係包含將前述間隙的高度設定成第1值並對前述間隙供給原料氣體的工程及將前述間隙的高度設定成小於第1值之第2值並對前述間隙供給原料氣體的工程；及(條件b)前述進行成膜之工程，係包含在成膜途中，使基板之徑方向的位置彼此不同之第1氣體吐出口及第2氣體吐出口的各吐出流量之流量比變更的工程。
根據本揭示，在藉由氣體來處理半導體裝置被形成於表面側之基板的方法中，可在基板之背面形成膜厚的面內均勻性良好之薄膜。
本揭示之一實施形態的基板處理裝置，係如圖1所示般，具備有下構件1與上構件2，處理容器10藉由下構件1與上構件2所構成。下構件1，係具備有：圓板狀的熱板3，具有比基板即半導體晶圓(以下稱為「晶圓」)W之半徑大的半徑；及扁平之圓筒狀的外裝部30，包圍熱板3的上面以外。 熱板3，係具備有：板狀部31；及加熱器32，由形成被設置於該板狀部31內之加熱部的電阻發熱體所構成。加熱器32，係被構成為例如分割成複數個以熱板3之中心為中心的同心圓狀，並可具有高均熱性來對熱板3的表面進行加熱。 在圖1中，電阻發熱加熱器32，係為了方便起見而記載為被分割成2個者。
如圖1及圖2所示般，在熱板3之表面，係以熱板3之中心為中心而沿著比晶圓的半徑短之半徑的圓設置有複數個例如8根間隙銷33。各間隙銷33，係例如被設定成0.3mm的高度。 在熱板3中之比間隙銷33更靠近中央處，係於圓周方向上，沿著以熱板3之中心為中心的圓而貫通該熱板3地設置有3根升降銷34。3根升降銷34，係經由升降構件35被連接於例如藉由氣缸所構成的升降機構36。在圖1中，係為了方便起見，圖示有2根間隙銷33及2根升降銷34。
在熱板3之中心部，係貫通地形成有氣體流路41，該氣體流路41，係流動有後述之蒸鍍用的原料氣體。氣體流路41之前端側，係形成朝熱板3之中心部呈開口的氣體吐出口40。亦即，氣體流路41之出口形成氣體吐出口40。又，氣體流路41之基端側，係貫通外裝部30的中心部，並被連接於原料氣體供給管42。原料氣體供給管42之基端側，係經由閥V1被連接於氣化器43。氣化器43，係用以藉由載體氣體來對液體原料進行氣化者，且連接有液體原料供給管51及載體氣體供給管52。在該例中，係使用氮氣作為載體氣體。 在液體原料供給管51，係從下游側起依序連接有閥V2、流量調整部511、液體原料供給源512。在載體氣體供給管52，係從下游側起依序連接有閥V3、流量調整部521、載體氣體供給源522。 液體原料，係使用氟樹脂即聚四氟乙烯(PTFE)例如鐵氟龍(註冊商標)。
上構件2，係以覆蓋下構件1之上方空間的方式，具備有扁平之圓筒狀的蓋部21，蓋部21中之周壁部22的下面，係被形成為與外裝部30的上面重疊。蓋部21，係被構成為可藉由升降機構20，在「重疊於下構件1」的位置與「在外部的基板搬送機構與升降銷34之間進行晶圓W之收授」的位置之間進行升降。 在蓋部21，係設置有氣體分散板23，以將由該蓋部21之周壁部22所包圍的空間區劃成上下，氣體分散板23之上方側及下方側，係分別形成氣體的擴散空間及處理空間。氣體分散板23，係在該例中，由平面觀看處理空間時，涵蓋整體地設置有氣體噴出孔24。 在蓋部21之上面板的中心部，係貫通地形成有氣體流路25，氣體流路25之下端，係朝已述的擴散空間呈開口。氣體流路25之上端，係被連接於沖洗氣體供給管26，在沖洗氣體供給管26，係從下游側起依序連接有閥V4、流量調整部27、沖洗氣體供給源28。在該例中，係使用氮氣作為沖洗氣體。又，氣體分散板23及氣體流路25，係構成沖洗氣體供給部。
在蓋部21之周壁部22的內部，係如圖1及圖3所示般，沿著該蓋部21之圓周方向，分別配置有上下貫通的複數個排氣路徑6。在周壁部22之下面側，係涵蓋全周地切去包含排氣路徑6之蓋部21的中央附近部位，從處理空間側觀看該周壁部22的下部時，形成有段部61。因此，排氣路徑6之下端，係朝段部61呈開口，形成排氣口60。在蓋部21之上面的周緣部，係設置有沿著圓周方向而形成為環狀的排氣室62，在排氣室62之底部，係排氣路徑6的上端呈開口，在排氣室62，係沿著圓周方向連接有複數個排氣管63，排氣管63之下游端，係例如被連接於排氣導管，該排氣導管，係共同地連接工廠內之各部分的排氣路徑。
本揭示之實施形態的基板處理裝置，係具備有藉由電腦所構成的控制部100，控制部100，係將用於進行後述之動作的程式儲存於記憶部。程式，係經由光碟、記憶卡、磁光碟等的記憶媒體被安裝於記憶部。在圖1中，係記載有從控制部100發送控制信號之控制線的一部分，升降銷34之升降機構36、閥V1~V4、流量調整部27、511、521，係藉由控制部100來控制。
其次，說明關於上述之基板處理裝置的作用。首先，設成為使蓋部21上升而開放了處理容器10的狀態，並藉由未圖示之基板搬送機構，將在表面側形成有半導體裝置的晶圓W搬送至熱板3之上方區域，並從基板搬送機構收授至升降銷34。在基板搬送機構退避至處理容器10外後，設成為使蓋部21下降而關閉了處理容器10的狀態(圖1所示的狀態)。晶圓W，係在晶圓W之背面與熱板3之表面的距離亦即圖1中記載了符號之間隙G的高度被設成為第1值例如2mm的狀態下，被支撐於升降銷34。此時，以使晶圓W之中心在預定的容許範圍內與熱板3之中心，亦即氣體吐出口40之中心一致的方式，予以載置。 在一例中，熱板3，係在晶圓W被收授至升降銷34之前，藉由加熱器32，被加熱至比原料氣體結露之溫度高的溫度且比液體原料即鐵氟龍分解之溫度低的溫度，例如50~180℃。
而且，開啟閥V4，將氮氣即沖洗氣體從沖洗氣體供給源28供給至處理容器10內。沖洗氣體，係從蓋部21之中心部的氣體流路25經由氣體分散板23被供給至晶圓W的表面及晶圓W的外側區域。又，藉由排氣路徑6，對處理室10內進行排氣。 在該狀態中，如圖4所示般，作為「鐵氟龍氣體(蒸氣)與載體氣體即氮氣之混合氣體」的原料氣體，從熱板3之中心部的氣體吐出口40以例如2.0升/分之流量被供給至晶圓W的背面與熱板3之間的間隙G。
記載關於原料氣體之供給，液體原料即鐵氟龍與載體氣體即氮氣分別從液體原料供給管51及載體氣體供給管52被送至氣化器43，鐵氟龍被氣化而與氮氣一起在原料氣體供給管42內流動並從氣體吐出口40吐出。 從氣體吐出口40吐出之原料氣體，係涵蓋全周地擴散晶圓W的背面與熱板3之間的間隙G且流出至晶圓W之外方側，並與從氣體分散板23流動而來的沖洗氣體一起經由蓋部22之下部的段部61流入至排氣路徑6內，從處理氛圍中排出。 沿著蓋部22的周壁部22所形成複數個之排氣路徑6的下端，係朝段部61呈開口，段部61，係涵蓋周壁部22之全周來形成。因此，相互鄰接的排氣路徑6之間的段部61，係具有排氣流路之所謂緩衝區域的功能，原料氣體及沖洗氣體，係沿圓周方向而高均勻性地被排出。
藉由原料氣體流動於前述間隙G的方式，蒸鍍原料即鐵氟龍被蒸鍍於晶圓W的背面。靠近晶圓W的背面之周緣的區域亦即周緣部，係迴繞著從氣體分散板23下降而來的沖洗氣體，因此，存在有原料氣體之氣流紊亂，原料氣體未擴散至晶圓W的背面而在該周緣部出現鐵氟龍膜未被蒸鍍之區域的情形，且膜厚之面內均勻性不穩定。當不供給沖洗氣體的情況下，雖係在晶圓W之背面的周緣部形成鐵氟龍膜，但在圖1所示的裝置構造中，有原料氣體迴繞於晶圓W之表面而導致在半導體裝置的形成區域形成鐵氟龍之虞。
因此，本實施形態中，係在將晶圓W之背面與熱板3的距離亦即間隙G的高度(尺寸)設定成第1值即例如2mm的狀態下，如已述般地對該背面進行蒸鍍，之後，在將晶圓W之背面與熱板3的距離較小地設定至第2值即例如0.3mm的狀態下，進行蒸鍍。在該例中，間隙銷33之高度為0.3mm，藉由使升降銷34下降且使被支撐於升降銷34之晶圓W如圖5所示般地收授至間隙銷33的方式，將前述間隙G之高度從2mm變更成0.3mm。升降銷34，雖係位於比熱板3之表面更下方側，但在圖5中，並未圖示升降銷34。
而且，在將晶圓W支撐於間隙銷33的狀態下，原料氣體從氣體吐出口40以1升/分之流量被供給至晶圓W的背面與熱板3之間的間隙G。當像這樣地縮小間隙G時，則由於沖洗氣體變得難以迴繞至晶圓W的背面，故在晶圓W之背面的周緣部，可抑制沖洗氣體對原料氣體之氣流的影響，因此，進行蒸鍍而形成鐵氟龍膜。原料氣體，雖係亦擴散至比晶圓W的背面之周緣部更靠中央的區域，但由於在形成單分子膜後，鐵氟龍並未被進一步層積，因此，並非涵蓋晶圓W之背面整體而層積，而是被層積於晶圓W之背面的周緣部。
在此，將間隙G之高度較大的狀態(在該例中，係將該尺寸設定成2mm的狀態)稱為寬間隙，並將尺寸較小的狀態(在該例中，係將該尺寸設定成0.3mm的狀態)稱為窄間隙。在本實施形態中，係首先，以寬間隙進行蒸鍍，其次，以窄間隙進行蒸鍍，進行2階段的步驟。因此，可在第2段步驟，對第1段步驟中所未蒸鍍的晶圓W之背面的周緣部補足蒸鍍。 若欲僅在第2段步驟，將鐵氟龍膜形成於晶圓W的背面時，則由於間隙G狹窄，因此，當增大原料氣體之流量時，會導致晶圓W浮起，故不得不使原料氣體以所謂的小流量來流動，因此，鐵氟龍之蒸鍍速度變慢。
對此，當在以寬間隙進行第1段步驟後，以窄間隙進行第2段步驟時，則第2段步驟中之蒸鍍速度會變快。亦即，在進行第2段步驟時，係由於鐵氟龍膜已被形成於比晶圓W之背面的周緣部更靠近中央的區域，故可抑制該區域中之原料氣體的消耗，且被供給至晶圓W之背面周緣部之原料氣體的流量會變多，因此，該周緣部中之蒸鍍速度變快。該結果，可在晶圓W之背面整體快速地形成作為薄膜的樹脂膜即鐵氟龍膜。 針對蒸鍍處理的時間列舉出一例，第1段步驟，係180秒，第2段步驟，係120秒。
當第2段步驟結束時，則停止原料氣體之供給，且蓋部21上升而開放與外裝部33之間，並藉由升降銷34將被支撐於間隙銷33的晶圓W上堆而上升。接著，未圖示之基板搬送機構從外部進入至晶圓W的下方，晶圓W以與搬入晶圓W時相反的動作被收授至基板搬送機構且從基板處理裝置搬出。 寬間隙中之間隙G的高度亦即第1值，係並非限於2mm，例如可被設定成比0.5mm大且從7mm以下之範圍所選擇的值。又，窄間隙中之間隙G的高度亦即第2值，係並非限於0.3mm，例如可被設定成從0.1mm以上0.5mm以下之範圍所選擇的值。
針對本實施形態中所使用之升降銷34、間隙銷33及熱板3的功能進行說明。 升降銷34及間隙銷33，係相當於用以在熱板3之上方支撐晶圓W的支撐部。在變更晶圓W的高度位置之際，間隙銷33雖不進行升降，但由於升降銷34會進行升降，因此，控制部100，係能以在成膜途中使晶圓W相對於熱板3的晶圓W之高度位置的方式，控制支撐部。 又，熱板3，係除了加熱原料氣體的功能以外，另具有「在與晶圓W的背面之間形成使原料氣體流通的間隙G，並沿著晶圓W的背面，將原料氣體導引至晶圓W之外緣」的功能。亦即，熱板3之表面，係具有作為原料氣體之導引面的功能。因此，在本實施形態中，熱板3，係導引面形成構件的一態樣。
根據上述之實施形態，具有以下效果。如已述般，當欲僅在第1段步驟進行蒸鍍處理時，則膜厚之面內均勻性不穩定。又，當欲僅在第2段步驟進行蒸鍍處理時，則導致需耗費較長時間來在晶圓W的背面整體形成鐵氟龍膜。因此，在以寬間隙進行第1段步驟後，以窄間隙進行第2段步驟，藉此，在僅進行第1段步驟的情況下，補足在僅進行第2段步驟之情況下的課題，作為結果，可在晶圓W之背面整體快速地形成膜厚之面內均勻性良好的鐵氟龍膜。 在本發明中，係與上述的例子相反地，亦可以窄間隙進行第1段步驟，其次，以寬間隙進行第2段步驟。在該情況下，以不在途中變更間隙G而維持固定的狀態(維持寬間隙或維持窄間隙)，與進行晶圓W的鐵氟龍膜之成膜的情況相比，用以實現膜厚的面內均勻性及處理時間整體的縮短之原料氣體流量等的參數之設定的自由度大。因此，變得容易運用裝置，結果，可實現膜厚的面內均勻性及處理時間的縮短。
在已述的專利文獻1中，係記載有如下述：在將晶圓配置於自熱板隔離之上方位置的狀態下，對基板實施處理氣體的供給。但是，由於處理氣體從設置於上側殼體之中心部的氣體吐出口被供給至基板之表面側，且處理氣體為疏水化處理用的HMDS氣體，因此，方法本身不同於本揭示的手法，又，亦可為進行成膜處理的手法。因此，本揭示，係與專利文獻1所示的手法完全不同。
當在晶圓W之背面形成鐵氟龍膜時，則具有如以下般的優點。在半導體製造工程之一具有曝光處理，該曝光處理，係在將表面形成有光阻膜的晶圓吸附於曝光裝置之平台的狀態下來進行。曝光裝置之平台，係多數個插銷被配列於表面，晶圓，係被載置於該些插銷群上，並被真空夾頭吸引至平台側且平坦化而進行曝光。 圖6，係示意地表示表面側彎曲成凸狀的晶圓W被吸附於平台S之態樣的圖，在被吸附於平台S之晶圓W的外緣附近會產生較大的應力，有時成為圖案之疊加惡化的要因之一。 如本揭示般，在晶圓W之背面形成鐵氟龍膜，藉此，由於平台S與晶圓W之間的摩擦變小，故在晶圓W被吸附於平台S時圓滑地擴展，因此，可抑制晶圓W之應力並可抑制疊加的惡化。 另外，在本揭示中，係亦可「以窄間隙進行第1段步驟，其次，以寬間隙進行第2段步驟」來代替「在以寬間隙進行第1段步驟後，以窄間隙進行第2段步驟」。在該情況下，原料氣體之流量的大小亦成為相反，第1段步驟中之原料氣體的流量，係例如被設定成1.0升/分，第2段步驟中之原料氣體的流量，係例如被設定成2.0升/分。
圖7，係表示本揭示之另一實施形態的基板處理裝置。該基板處理裝置，係除了在熱板3之中心部貫通地形成有氣體流路41的構成以外，另在從熱板3之中心部朝周緣側遠離的位置貫通地形成有氣體流路71。氣體流路71，係以熱板3之中心為中心，沿著比晶圓W的半徑小之半徑(在該例中，係晶圓W的半徑之一半左右的半徑)的圓，等間隔地例如形成有3個，各氣體流路71之前端側，係形成朝熱板3之表面呈開口的氣體吐出口70。圖8，雖係表示該例子的熱板3，但在同圖中，省略間隙銷33、升降銷34。
各氣體流路71之基端側，係貫通外裝部30，並被連接於原料氣體供給管72。原料氣體供給管72之基端側，係與被連接熱板33之中心部的氣體流路41之已述的原料氣體供給管42匯流，並被連接於氣化器43。在各原料氣體供給管72，係設置有藉由控制部100之控制信號來進行開關控制的閥V5。在圖7中，為了方便起見，氣體流路71，係表示2條。除了設置氣體流路71且具備有與該氣體流路71相關的構造以外，其餘與圖1所示的基板處理裝置相同。
其次，說明關於本揭示之另一實施形態之基板處理裝置的作用。將熱板3之中心部的氣體吐出口即40稱為第1氣體吐出口40，並將從該中心部朝外側遠離的3個氣體吐出口70稱為第2氣體吐出口70。在該實施形態中，係晶圓W從外部的基板搬送機構經由升降銷34被收授至間隙銷33。而且，與已述的一實施形態相同地，對處理容器10內供給沖洗氣體，又從排氣口60進行排氣。在該狀態中，如圖9所示般，原料氣體即鐵氟龍氣體與載體氣體之混合氣體從第1氣體吐出口40例如以1.0升/分的流量被供給至晶圓W的背面與熱板3之間的間隙G一預定時間。此時，閥V5被關閉，未從第2氣體吐出口70供給原料氣體。
其次，關閉閥V1，並且開啟閥V5，停止來自第1氣體吐出口40之原料氣體的供給，如圖10所示般，將原料氣體從第2氣體吐出口70供給至間隙G。來自3個氣體吐出口70之原料氣體的總流量，係例如被設定成1.0升/分。針對蒸鍍處理的時間列舉出一例，第1段步驟，係180秒，第2段步驟，係120秒。 而且，在進行蒸鍍處理一預定時間後，停止原料氣體的供給，並如已述般地，將晶圓W搬出至基板處理裝置外。
在該實施形態中，係由於在第1段步驟中以窄間隙從第1氣體吐出口40吐出原料氣體，因此，晶圓W的背面之周緣部的蒸鍍速度雖慢，但在背面之中央區域，係快速地形成有鐵氟龍膜。而且，由於在第2段步驟中以窄間隙從第2氣體吐出口70吐出原料氣體，因此，在背面之周緣部快速地形成有鐵氟龍膜。因此，可在晶圓W之背面整體快速地形成膜厚之面內均勻性良好的鐵氟龍膜。 在前述其他實施形態中，雖係在第1段步驟以窄間隙從第1氣體吐出口40吐出原料氣體，但如圖11所示般，亦可以寬間隙進行第1段步驟。在該情況下，在第1段步驟中，係使升降銷34上升，且將間隙銷33上的晶圓W頂出，間隙G之高度被設定成例如2mm，原料氣體的流量，係被設定成例如2.0升/分。
又，如圖12所示般，亦可以寬間隙進行來代替在第2段步驟中以窄間隙從第2氣體吐出口70吐出原料氣體。在該情況下，在第2段步驟中，係晶圓W藉由升降銷34所支撐，間隙G之高度被設定成例如2mm，來自3個氣體吐出口70之原料氣體的總流量，係被設定成例如2.0升/分。 因此，在使用圖7所示之基板處理裝置來進行蒸鍍處理的情況下，總結已述的說明，第1段步驟、第2段步驟，係亦可設成為如下述般組合。 第1段步驟    第2段步驟 圖9狀態       圖10狀態 圖11狀態      圖10狀態 圖9狀態       圖12狀態 圖11狀態      圖12狀態
又，在本揭示中，係在使用圖7所示之基板處理裝置來進行蒸鍍處理的情況下，亦可使已述之對應於第1段步驟的蒸鍍處理與對應於第2段步驟的蒸鍍處理之實施順序成為相反。亦即，在該情況下，上述的第2段步驟成為第1段步驟，上述的第1段步驟則成為第2段步驟。在以下中，記載像這樣的步驟之組合。 第1段步驟    第2段步驟 圖10狀態      圖9狀態 圖10狀態      圖11狀態 圖12狀態      圖9狀態 圖12狀態      圖11狀態
本揭示之基板處理裝置，係可採用沿熱板3的徑方向設置複數個原料氣體之氣體吐出口的構成，並列舉出圖7之基板處理裝置作為該一例。而且，列舉出如下述例子：從第1氣體吐出口40及第2氣體吐出口70之一者供給原料氣體，並停止來自另一者之原料氣體的供給。但是，亦可從第1氣體吐出口40及第2氣體吐出口70兩者供給原料氣體，並在第1段步驟與第2段步驟之間，變更第1氣體吐出口40之氣體流量及第2氣體吐出口70之氣體流量的比率亦即氣體流量比。例如，可採用如下述等的手法：一面從兩者的氣體吐出口40、70供給原料氣體，一面在第1段步驟中，將第1氣體吐出口40之氣體流量設定成「適合晶圓W的中央區域之蒸鍍」的值，並在第2段步驟中，將第2氣體吐出口70之氣體流量設定成「適合晶圓的周緣區域之蒸鍍」的值。 另外，在第1段步驟與第2段步驟中，當不變更第1氣體吐出口40及第2氣體吐出口70的流量之比率的情況下，係具有下述的缺點。亦即，極難以同時滿足下述者：使鐵氟龍確實地蒸鍍於晶圓W之周緣區域且防止原料氣體迴繞至晶圓W的表面，並進一步防止晶圓W的浮起。 又，用以進行晶圓W的中央區域之蒸鍍的原料氣體之吐出口即第1氣體吐出口40，係不限定於設置在熱板3的中心部，例如亦可為在該中心部附近沿圓周方向設置複數個的構成。第2氣體吐出口70，係不限於3個，亦可設置2個或4個以上。
使用了圖1之基板處理裝置的成膜手法，係如下述方法之一例：在成膜途中，變更晶圓W相對於熱板3之表面的高度位置亦即間隙G的高度。 又，使用了圖7之基板處理裝置的成膜手法，係如下述方法之一態樣：使用晶圓W之徑方向的位置彼此不同之第1氣體吐出口40及第2氣體吐出口70作為原料氣體的氣體吐出口，並在成膜途中，變更第1氣體吐出口40及第2氣體吐出口70之各吐出流量的流量比。而且，使用了圖7之基板處理裝置的成膜手法，係亦含有組合了「變更第1氣體吐出口40及第2氣體吐出口70之各吐出流量的流量比」與「變更間隙G的高度」之例子。 因此，本揭示，係一種基板處理方法，具備有如下述中至少一方的條件： (條件a)包含在成膜途中，變更基板相對於前述導引面之高度位置的工程；及 (條件b)包含在成膜途中，使基板之徑方向的位置彼此不同之第1氣體吐出口及第2氣體吐出口的各吐出流量之流量比變更的工程。
在使用晶圓W之徑方向的位置彼此不同之第1氣體吐出口40及第2氣體吐出口70的情況下，係如已述的例子般，不限於設置前述徑方向的位置彼此不同之2群組亦即第1氣體吐出口40及第2氣體吐出口70。例如，亦可使用前述徑方向的位置彼此不同的3群組或4以上之群組的氣體吐出口，在成膜途中，改變彼此不同之群組之原料氣體的流量。作為該一例，可列舉出設置位於比第2氣體吐出口70更往晶圓W的外周側之第3氣體吐出口的情形。
本揭示中進行成膜之薄膜，雖係在上述的例子中，將鐵氟龍膜記載為「在形成單分子膜後，膜之成分未被層積於該單分子膜上」的膜，但作為像這樣的單分子膜，係不限於鐵氟龍膜。又，在形成作為薄膜的氟樹脂之膜的情況下，係不限於聚四氟乙烯膜，亦可為其他氟樹脂即例如全氟烷氧基烷烴(PFA)。 本揭示中進行成膜之薄膜，係不限於氟樹脂，亦可為其他樹脂膜或亦可為樹脂膜以外的膜。又，在上述的例子中，薄膜，雖係被使用作為「具有在晶圓之曝光時，減少平台與晶圓的摩擦之功能」的膜，但亦可為在製造半導體裝置時具有其他輔助功能的輔助膜例如保護晶圓之背面的保護膜。
針對關於本揭示之技術，進一步如以下般地進行追加記載。 關於從晶圓W之上方所供給的沖洗氣體，雖係亦可將第1段步驟中之流量與第2段步驟中之流量設成為相同，但亦可依照各步驟設定成適當的流量。例如，在以寬間隙進行成膜時之原料氣體的流量比以窄間隙進行成膜時之原料氣體的流量多之情況下，為了防止原料氣體迴繞至晶圓W的表面及防止晶圓W的浮起，亦可採用「相較於窄間隙時，增大寬間隙時之沖洗氣體流量」這樣的手法。 在本揭示之基板處理方法中，係不限定於從晶圓W的上方側供給沖洗氣體。例如亦可調製排氣口之配置、排氣流量、晶圓W之外方側的構造等，以實現原料氣體之氣流的最佳化而不用供給沖洗氣體。
而且，又亦可在成膜途中，變更晶圓W之朝向。像這樣的手法之優點，係如下述般。存在有：氣流在處理容器10內之全區域不完全一致的情形，又相對於被支撐在支撐部(間隙銷33或升降銷34)的晶圓W而從水平稍微傾斜的情形。因此，須擔心膜難以附著於晶圓W之周緣部的一部分之區域的狀態明顯化。因此，藉由在成膜途中，變更晶圓W之朝向的方式，膜容易附著的部位與膜難以附著的部位相對地置換，其結果，在晶圓W之周緣部，膜會均勻地附著於圓周方向上。
作為變更晶圓W之朝向的手法之一，可列舉出將旋轉機構組合至熱板3且使晶圓W與熱板3一起旋轉的手法。在該情況下，可列舉出如下述手法：在成膜途中，暫時停止原料氣體的供給，在將晶圓W載置於間隙銷33的狀態下，使熱板3旋轉且改變晶圓W之朝向後，重新開始原料氣體的供給。 作為變更晶圓W之朝向的手法，可列舉出如下述例子：在成膜途中，暫時停止原料氣體的供給，將晶圓W搬出至處理容器3外且改變晶圓W之朝向，並使晶圓W返回到處理容器3內，重新開始原料氣體的供給。在該情況下，亦可在處理容器3之外部設置晶圓W的旋轉台，藉由該旋轉台改變晶圓W之朝向。抑或，亦可設置不具備旋轉功能的保持平台，在使晶圓W載置於該保持平台後，改變搬送機構之朝向且從保持平台接收晶圓W，藉此，改變晶圓W之朝向。
在上述的實施形態中，雖係將晶圓W載置於間隙銷33上而設成為窄間隙，但亦可不使用間隙銷33，在支撐於升降銷34的狀態下形成窄間隙。 又，間隙G之高度的變更，係亦可固定晶圓W的高度位置，並使熱板3升降。 並且，亦可不使用熱板3而使用具有與晶圓W的背面相對向之原料氣體的導引面之板狀體例如石英製之板狀體，並在該板狀體的下方設置形成加熱部之加熱燈，藉由從加熱燈透過了板狀體的紅外線來加熱原料氣體。
其次，記載關於本揭示之基板處理裝置的適用例。作為用以形成光阻圖案之系統，已知將塗佈、顯像裝置連接於曝光裝置的系統，該塗佈、顯像裝置，係將光阻塗佈於晶圓W，並對曝光後之晶圓進行顯像。圖13，係表示塗佈、顯像裝置之一例之外觀的概略圖，塗佈、顯像裝置，係依照載體區塊A1、中間區塊A2、處理區塊A3、介面區塊A4該順序，沿水平方向直線狀地連接而構成。在介面區塊A4，係連接有曝光機A5。儲存有基板即晶圓W的載體C，係藉由未圖示之載體搬送機構被搬送且載置於載體區塊A1。在處理區塊A3，係設置有塗佈模組、顯像模組等，該塗佈模組，係將光阻供給至基板即晶圓W的表面而形成光阻膜，該顯像模組，係將顯像液供給至經曝光的光阻膜而形成光阻圖案。在中間區塊A2，係設置有對經顯像的晶圓W之表面整體進行拍攝的攝像模組等。 收納於載體C之晶圓W，係被晶圓搬送機構取出，在進行光阻膜的形成曝光、顯像處理後，返回到載體C。
本揭示之基板處理裝置，係被設置於塗佈、顯像裝置內的例如介面區塊A4，在形成有光阻膜之晶圓W的背面形成鐵氟龍膜。作為形成光阻膜之一連串處理，具有加熱光阻液塗佈後之晶圓的處理，進行該加熱處理的加熱模組群雖被設置於處理區塊A3內，但本揭示之基板處理裝置，係亦可配置於設置有加熱模組群的區域。又，本揭示之基板處理裝置，係亦可作為個別之單獨的裝置而配置於塗佈、顯像裝置之外部。 [實施例]
記載關於如下述實驗結果：使用裝置構造與圖1所示之構成同等的基板處理裝置，在「將間隙G之高度設成固定且藉由蒸鍍形成鐵氟龍」的情形與「在成膜途中，變更間隙G之高度且藉由蒸鍍形成鐵氟龍」的情形下，分別調查300mm晶圓背面之膜厚成為哪個狀態。
＜比較例1＞ 在圖14中，表示將間隙G之高度設定成0.3mm並將原料氣體以1.0升/分的流量供給至晶圓之背面300秒的結果。圖14，係將晶圓上的位置作為橫軸且將晶圓之背面的水之接觸角作為縱軸的曲線圖。在橫軸中，0，係相當於晶圓之中心的位置。 ＜比較例2＞ 藉由圖15的實線(1)，表示「將間隙G之高度設定成2.0mm並將原料氣體以2.0升/分的流量供給至晶圓之背面300秒」的結果。 ＜比較例3＞ 藉由圖15的虛線(2)，表示「將間隙G之高度設定成5.0mm並將原料氣體以2.0升/分的流量供給至晶圓之背面300秒」的結果。 ＜實施例1＞ 在圖16中，表示「將間隙G之高度設定成2.0mm並將原料氣體以2.0升/分的流量供給至晶圓之背面180秒，接著，將間隙G之高度變更成0.3mm並將原料氣體以1.0升/分的流量供給至晶圓之背面120秒」的結果。
＜討論＞ 圖14~16，係針對晶圓之背面的複數點計測水之接觸角，並對其計測值的排列進行示意化且表示接觸角之面內分布的傾向者。鐵氟龍膜之膜厚越大，則接觸角亦變得越大，因此，圖14~16，係表示晶圓的背面中之鐵氟龍膜的膜厚分布者。 由該結果可知，當縮小間隙G時，則晶圓之背面的周緣部中之蒸鍍速度緩慢。即便在晶圓W之中央附近的區域中形成有單分子膜，亦在周緣部中尚未建立鐵氟龍之分子單位的蒸鍍，且持續著付著有未成為單分子之碳及氟的化合物之狀態。 又，當加大間隙G時，則產生鐵氟龍未附著於晶圓的背面之周緣部的區域。在該實驗中，在加大了間隙G的情況下，在晶圓之圓周方向會出現附著有薄膜的部位與未附著的部位。該理由，係考慮到如下述等的要因：處理容器內之氣流的流動因排氣壓力的稍微變動等而在圓周方向並不完全固定、晶圓之翹曲的狀態在圓周方向並不一致。 對此可知，當變更間隙G時，則涵蓋晶圓之背面的整體形成有鐵氟龍膜。
W:晶圓 1:下構件 10:處理容器 2:上構件 21:蓋部 22:周壁部 23:氣體分散板 25:氣體流路 26:沖洗氣體供給管 3:熱板 32:加熱器 33:間隙銷 34:升降銷 35:升降構件 36:升降機構 40:氣體吐出口 41:氣體流路 51:液體原料供給管 52:載體氣體供給管 6:排氣路徑 60:排氣口 70:氣體吐出口 71:氣體流路 100:控制部
[圖1]表示本揭示之一實施形態之基板處理裝置的縱剖面圖。
[圖2]表示被使用於圖1所示之基板處理裝置之熱板的平面圖。
[圖3]沿著圖1所示之基板處理裝置之A-A'線的橫剖平面圖。
[圖4]表示圖1所示之基板處理裝置之動作的說明圖。
[圖5]表示圖1所示之基板處理裝置之動作的說明圖。
[圖6]示意地表示曝光裝置之平台與被載置於該平台之基板的說明圖。
[圖7]表示本揭示之另一實施形態之基板處理裝置的縱剖面圖。
[圖8]表示被使用於圖7所示之基板處理裝置之熱板的平面圖。
[圖9]表示圖7所示之基板處理裝置之動作的說明圖。
[圖10]表示圖7所示之基板處理裝置之動作的說明圖。
[圖11]表示圖7所示之基板處理裝置之動作的說明圖。
[圖12]表示圖7所示之基板處理裝置之動作的說明圖。
[圖13]表示本揭示之基板處理裝置之配置的一例之對象即塗佈、顯像裝置之例子的外觀圖。
[圖14]示意地表示用以評估基板之背面的膜厚分布之實驗資料之結果的曲線圖。
[圖15]示意地表示用以評估基板之背面的膜厚分布之實驗資料之結果的曲線圖。
[圖16]示意地表示用以評估基板之背面的膜厚分布之實驗資料之結果的曲線圖。
1:下構件
2:上構件
3:熱板
6:排氣路徑
10:處理容器
20:升降機構
21:蓋部
22:周壁部
23:氣體分散板
24:氣體噴出孔
25:氣體流路
26:沖洗氣體供給管
27:流量調整部
28:沖洗氣體供給源
30:外裝部
31:板狀部
32:加熱器
33:間隙銷
34:升降銷
35:升降構件
36:升降機構
40:氣體吐出口
41:氣體流路
42:原料氣體供給管
43:氣化器
51:液體原料供給管
52:載體氣體供給管
60:排氣口
61:段部
62:排氣室
63:排氣管
100:控制部
511:流量調整部
512:液體原料供給源
521:流量調整部
522:載體氣體供給源
G:間隙
V1:閥
V2:閥
V3:閥
V4:閥
W:晶圓

Claims (13)

  1. 一種基板處理方法，係在處理容器內，藉由氣體來處理半導體裝置被形成於表面側之基板的方法中，包含有：在使表面朝上的狀態下，藉由支撐部支撐基板之背面，並在該基板的背面整體與對向於該背面整體的導引面之間形成間隙的工程；以從比被支撐於前述支撐部之基板更外側進行排氣的方式，從沿著前述處理容器之圓周方向所形成的排氣口，對處理容器內進行排氣的工程；及經由與前述基板之背面對向的氣體吐出口對前述間隙供給原料氣體，並且加熱該原料氣體，藉由蒸鍍，在前述基板之背面整體形成薄膜的工程，且具備有如下述中至少一方的條件：(條件a)前述進行成膜之工程，係包含將前述間隙的高度設定成第1值並對前述間隙供給原料氣體的工程及將前述間隙的高度設定成小於第1值之第2值並對前述間隙供給原料氣體的工程；及(條件b)前述進行成膜之工程，係包含在成膜途中，使基板之徑方向的位置彼此不同之第1氣體吐出口及第2氣體吐出口的各吐出流量之流量比變更的工程。
  2. 如申請專利範圍第1項之基板處理方法，其中，具備有前述條件a， 前述間隙的高度被設定成第1值時所供給至該間隙之原料氣體的流量，係比前述間隙的高度被設定成第2值時所供給至該間隙之原料氣體的流量多。
  3. 如申請專利範圍第1項之基板處理方法，其中，在執行前述進行成膜之工程的期間，將沖洗氣體從上方供給至基板的表面側。
  4. 如申請專利範圍第1~3項中任一項之基板處理方法，其中，具備有前述條件a，前述第1值大於0.5mm且為7mm以下，前述第2值為0.1mm以上、0.5mm以下。
  5. 如申請專利範圍第1~3項中任一項之基板處理方法，其中，前述氣體吐出口，係被設置於導引面形成構件之氣體流路的出口，該導引面形成構件，係上面被形成為前述導引面。
  6. 如申請專利範圍第1~3項中任一項之基板處理方法，其中，前述導引面，係熱板所具有的面，該熱板，係具備有加熱部。
  7. 如申請專利範圍第1~3項中任一項之基板處理方法，其中，前述薄膜，係指在形成單分子膜後未被蒸鍍於該單分子膜上的膜。
  8. 如申請專利範圍第1~3項中任一項之基板處理方法，其中，前述薄膜，係由氟樹脂所構成的薄膜。
  9. 一種基板處理裝置，係在處理容器內，藉由氣體來處理半導體裝置被形成於表面側之基板的裝置中，具備有：導引面形成構件，具備有「用以在與表面朝向上側之基板的背面之間形成使原料氣體流通的間隙」之原料氣體的導引面；加熱部，用以加熱流動於前述間隙的原料氣體；支撐部，用以在前述導引面的上方支撐前述基板；氣體吐出口，用以將前述原料氣體從前述導引面側供給至前述間隙，該前述原料氣體，係用以藉由蒸鍍，在前述基板的背面形成薄膜；排氣口，以從比被支撐於前述支撐部之基板更外側進行排氣的方式，沿著前述處理容器之圓周方向而形成；及控制部，且具備有如下述中至少一方的條件： a)前述控制部，係以在成膜途中，將前述間隙的高度從第1值及小於該第1值之第2值的一者變更成另一者的方式，進行控制；及b)具備有基板之徑方向的位置彼此不同之第1氣體吐出口及第2氣體吐出口來作為前述氣體吐出口，前述控制部，係以在成膜途中，使基板之徑方向的位置彼此不同之第1氣體吐出口及第2氣體吐出口的各吐出流量之流量比變更的方式，進行控制。
  10. 如申請專利範圍第9項之基板處理裝置，其中，具備有前述條件a，前述控制部，係以「使前述間隙的高度被設定成第1值時所供給至該間隙之原料氣體的流量比前述間隙的高度被設定成第2值時所供給至該間隙之原料氣體的流量多」的方式，輸出控制信號。
  11. 如申請專利範圍第9或10項之基板處理裝置，其中，具備有：沖洗氣體供給部，被設置於該基板之上方側，以將沖洗氣體供給至前述基板的表面側，前述控制部，係以至少在藉由蒸鍍而成膜於基板的背面時進行前述沖洗氣體之供給的方式，輸出控制信號。
  12. 如申請專利範圍第9或10項之基板處理裝置，其中， 前述氣體吐出口，係被設置於前述導引面形成構件之氣體流路的出口。
  13. 如申請專利範圍第9或10項之基板處理裝置，其中，前述薄膜，係氟樹脂膜。
TW108129948A 2018-09-05 2019-08-22 基板處理方法及基板處理裝置 TWI833789B (zh)