TWI827536B - 層合玻璃用中間膜及層合玻璃 - Google Patents
層合玻璃用中間膜及層合玻璃 Download PDFInfo
- Publication number
- TWI827536B TWI827536B TW107104034A TW107104034A TWI827536B TW I827536 B TWI827536 B TW I827536B TW 107104034 A TW107104034 A TW 107104034A TW 107104034 A TW107104034 A TW 107104034A TW I827536 B TWI827536 B TW I827536B
- Authority
- TW
- Taiwan
- Prior art keywords
- layer
- mentioned
- laminated glass
- interlayer film
- resin
- Prior art date
Abstract
本發明提供一種可提高層合玻璃之隔音性之層合玻璃用中間膜。 本發明之層合玻璃用中間膜具有1層構造或2層以上之構造,具備於動態黏彈性測定中之玻璃轉移溫度為-30℃以上且10℃以下之第1層,於上述第1層之動態黏彈性測定中,將上述第1層之以℃為單位表示之玻璃轉移溫度記為Tg,此時Tg下之上述第1層之損耗正切tanδ滿足以下之式(1)及式(2)兩者。 (Tg下之上述第1層之損耗正切tanδ)≧1.55…(1) (Tg下之上述第1層之損耗正切tanδ)=A×(Tg-10℃下之上述第1層之第1儲存彈性模數G'/Tg+10℃下之上述第1層之第2儲存彈性模數G')+B…(2) 上述式(2)中,A為0.003以上且0.04以下,B為0.7以上且1.4以下。
Description
本發明係關於一種用以獲得層合玻璃之層合玻璃用中間膜。又,本發明係關於一種使用上述層合玻璃用中間膜之層合玻璃。
層合玻璃即便受到外部撞擊而產生破損,玻璃碎片亦少有飛散,安全性優異。因此,上述層合玻璃廣泛用於汽車、軌道車輛、飛機、船舶及建築物等。上述層合玻璃係藉由在2片玻璃板之間夾入層合玻璃用中間膜而製造。
作為上述層合玻璃用中間膜,存在具有1層構造之單層之中間膜與具有2層以上之構造之多層之中間膜。
作為上述層合玻璃用中間膜之一例,下述專利文獻1中揭示有一種隔音層,其包含:縮醛化度為60~85莫耳%之聚乙烯醇縮醛樹脂100重量份、鹼金屬鹽與鹼土金屬鹽中之至少一種金屬鹽0.001~1.0重量份、及超過30重量份之塑化劑。該隔音層能夠以單層用作中間膜。
進而,下述專利文獻1中亦記載有一種將上述隔音層與其他層積層而成之多層之中間膜。與隔音層積層之其他層包含:縮醛化度為60~85莫耳%之聚乙烯醇縮醛樹脂100重量份、鹼金屬鹽與鹼土金屬鹽中之至少一種金屬鹽0.001~1.0重量份、及30重量份以下之塑化劑。
下述專利文獻2中揭示有一種中間膜,其係具有33℃以上之玻璃轉移溫度之聚合物層。
[專利文獻1]日本專利特開2007-070200號公報
[專利文獻2]US2013/0236711A1
為了汽車駕駛之舒適性,要求減輕車內噪音。作為車內噪音,可列舉:因引擎驅動而產生之噪音、行駛時因輪胎之胎面花紋而產生之噪音、行駛時因車體振動而產生之噪音、行駛時因懸架振動而產生之噪音、及行駛時因風而產生之噪音等。針對此種噪音,期望提昇層合玻璃於2000Hz~4000Hz之中頻域之隔音性。
又,近年來,使用內燃機之燃料汽車正在向電動汽車過渡。作為電動汽車,可列舉:使用電動馬達之電動汽車、及併用內燃機與電動馬達之油電混合汽車等。於電動汽車中,因電動馬達之驅動而產生超過4000Hz之高頻域噪音。對於電動汽車而言,期望提昇層合玻璃於超過4000Hz之高頻域之隔音性。再者,對於使用內燃機之燃料汽車,亦期望層合玻璃於超過4000Hz之高頻域之隔音性優異。
再者,關於建築物等中使用之層合玻璃,亦期望自中頻域至高頻域之隔音性優異。
然而,使用如專利文獻1、2記載之先前之中間膜的層合玻璃存在隔音性不充分之情況。
又,近年來,隨著電動汽車之高性能化,續航距離不斷變長,且逐步實現更高速之行駛。業者認為今後電動汽車之高性能化將進一步發展。
認為藉由利用層合玻璃有效地減輕噪音,能夠提昇電動汽車於長時間行駛時且高速行駛時之舒適性。
本發明之目的在於提供一種可提高層合玻璃隔音性之層合玻璃用中間膜。又,本發明之目的亦在於提供一種使用上述層合玻璃用中間膜之層合玻璃。
本發明於廣義上提供一種層合玻璃用中間膜(以下有時記載為中間膜),其係具有1層構造或2層以上之構造者,上述中間膜具備於動態黏彈性測定中之玻璃轉移溫度為-30℃以上且10℃以下之第1層,於上述第1層之動態黏彈性測定中,將上述第1層之以℃為單位表示之玻璃轉移溫度記為Tg,將Tg-10℃下之上述第1層之儲存彈性模數G'記為第1儲存彈性模數G',將Tg+10℃下之上述第1層之儲存彈性模數G'記為第2儲存彈性模數G',此時Tg下之上述第1層之損耗正切tanδ滿足以下之式(1)及式(2)兩者。
(Tg下之上述第1層之損耗正切tanδ)≧1.55…(1)
(Tg下之上述第1層之損耗正切tanδ)=A×(第1儲存彈性模數G'/第2儲存彈性模數G')+B…(2)
上述式(2)中,A為0.003以上且0.04以下,B為0.7以上且1.4以下。
本發明之中間膜於某一特定情況下,上述第1層包含軟化點為70℃以上且200℃以下之化合物。
本發明之中間膜於某一特定情況下,上述第1層包含熱塑性樹脂,或者包含使光硬化性化合物或濕氣硬化性化合物硬化而成之硬化物。
本發明之中間膜於某一特定情況下,上述中間膜為具有2層以上之構
造之層合玻璃用中間膜,上述中間膜具備第2層,於上述第1層之第1表面側配置有上述第2層。
本發明之中間膜於某一特定情況下,上述中間膜為具有3層以上之構造之層合玻璃用中間膜,上述中間膜具備第3層,於上述第1層之與上述第1表面相反側之第2表面側配置有上述第3層。
本發明之中間膜於某一特定情況下,上述第1層包含熱塑性樹脂、或者包含使具有(甲基)丙烯醯基之硬化性化合物硬化而成之硬化物,上述第2層包含熱塑性樹脂,上述第3層包含熱塑性樹脂。
本發明之中間膜於某一特定情況下,上述第1層包含上述熱塑性樹脂,上述第1層中之上述熱塑性樹脂為聚乙烯醇縮醛樹脂,上述第2層中之上述熱塑性樹脂為聚乙烯醇縮醛樹脂,上述第3層中之上述熱塑性樹脂為聚乙烯醇縮醛樹脂。
本發明之中間膜於某一特定情況下,上述第1層包含塑化劑,上述第2層包含塑化劑,上述第3層包含塑化劑。
本發明於廣義上提供一種層合玻璃,其具備第1層合玻璃構件、第2層合玻璃構件、及上述層合玻璃用中間膜,於上述第1層合玻璃構件與上述第2層合玻璃構件之間配置有上述層合玻璃用中間膜。
本發明之層合玻璃用中間膜具有1層構造或2層以上之構造。本發明之層合玻璃用中間膜具備於動態黏彈性測定中之玻璃轉移溫度為-30℃以上且10℃以下之第1層。關於本發明之層合玻璃用中間膜,於上述第1層之動態黏彈性測定中,上述第1層之玻璃轉移溫度Tg下之上述第1層之損耗正切tanδ滿足式(1)及式(2)兩者。本發明之層合玻璃用中間膜由於具備
上述構成,故而可提高使用本發明之層合玻璃用中間膜之層合玻璃之隔音性。
1:第1層
1a:第1表面
1b:第2表面
2:第2層
2a:外側之表面
3:第3層
3a:外側之表面
11:中間膜
11A:中間膜
11a:第1表面
11b:第2表面
21:第1層合玻璃構件
22:第2層合玻璃構件
31:層合玻璃
31A:層合玻璃
圖1係模式性地表示本發明之第1實施形態之層合玻璃用中間膜的剖視圖。
圖2係模式性地表示本發明之第2實施形態之層合玻璃用中間膜的剖視圖。
圖3係模式性地表示使用圖1所示之層合玻璃用中間膜之層合玻璃之一例的剖視圖。
圖4係模式性地表示使用圖2所示之層合玻璃用中間膜之層合玻璃之一例的剖視圖。
以下,詳細地說明本發明。
本發明之層合玻璃用中間膜(以下有時記載為中間膜)具有1層構造或2層以上之構造。本發明之中間膜可具有1層構造,亦可具有2層以上之構造。本發明之中間膜可具有雙層構造,亦可具有3層以上之構造。本發明之中間膜可為具有僅具備第1層之1層構造的中間膜(單層之中間膜),亦可為具有具備第1層與其他層之2層以上之構造的中間膜(多層之中間膜)。
本發明之中間膜具備第1層。
進行本發明之中間膜之上述第1層之動態黏彈性測定。於該測定中,將上述第1層之以℃為單位表示之玻璃轉移溫度記為Tg,將Tg-10℃下之上述第1層之儲存彈性模數G'記為第1儲存彈性模數G'(以下有時記載為G'(Tg-10℃))、Tg+10℃下之上述第1層之儲存彈性模數G'記為第2儲存
彈性模數G'(以下有時記載為G'(Tg+10℃))。關於本發明之中間膜,上述第1層之Tg下之上述第1層之損耗正切tanδ(以下有時記載為tanδ(Tg))滿足式(1)及式(2)兩者。
(Tg下之上述第1層之損耗正切tanδ)≧1.55…(1)
(Tg下之上述第1層之損耗正切tanδ)=A×(第1儲存彈性模數G'/第2儲存彈性模數G')+B…(2)
上述式(2)中,A為0.003以上且0.04以下,B為0.7以上且1.4以下。
上述式(1)及(2)分別亦可如以下之式(1A)及式(2A)般表示。
tanδ(Tg)≧1.55…(1A)
tanδ(Tg)=A×(G'(Tg-10℃)/G'(Tg+10℃))+B…(2A)
上述式(2A)中,A為0.003以上且0.04以下,B為0.7以上且1.4以下。
本發明之中間膜由於具備上述構成,故而可提高使用本發明之中間膜之層合玻璃之隔音性。於本發明中,例如可提高20℃下之隔音性。
進而,本發明之中間膜由於具備上述構成,故而可同時提高使用本發明之中間膜之層合玻璃於2000~4000Hz之範圍內之3150Hz左右之中頻域之隔音性、與於超過4000Hz之6300Hz左右之高頻域之隔音性。
就進一步提高隔音性之觀點而言,上述式(1)中,第1層之tanδ(Tg)較佳為1.8以上,更佳為2.0以上,進而較佳為2.5以上,尤佳為3.0以上。第1層之玻璃轉移溫度Tg下之第1層之tanδ(Tg)之上限並無特別限定。
就進一步提高隔音性之觀點而言,上述式(2)及(2A)中之A較佳為0.004以上,更佳為0.005以上。
就進一步提高隔音性之觀點而言,上述式(2)及(2A)中之B較佳為0.75以上,更佳為0.8以上,又,較佳為1.35以下,更佳為1.3以下。
作為使之滿足上述式(1)(或(1A))與式(2)(或(2A))兩者之方法,例如想到使第1層中之於玻璃轉移溫度附近之分子運動加劇的方法。可使第1層中之於玻璃轉移溫度前之分子運動加劇,亦可使於玻璃轉移溫度後之分子運動加劇。例如認為藉由使高分子等分子難以彎曲,第1層中之玻璃轉移溫度附近之分子運動加劇。具體而言,例如於第1層包含熱塑性樹脂等樹脂之情形時,可於第1層中添加會於第1層之玻璃轉移溫度附近對樹脂施加較強之相互作用的化合物(例如下述化合物(A))。認為藉此上述化合物對樹脂產生作用,從而更容易引發分子運動。又,例如於第1層包含熱塑性樹脂等樹脂之情形時,認為藉由使用具有容易於第1層之玻璃轉移溫度附近產生劇烈之分子運動之骨架的樹脂,而更容易引發分子運動。
關於多層之中間膜,可使用用以獲得中間膜之積層前之第1層而測定黏彈性。於多層之中間膜中,可自第1層剝離第2層(及第3層等其他層),取出第1層,使用所取出之第1層而測定黏彈性。
可藉由如下方式自多層之中間膜取出第1層。
將多層之中間膜於室溫23±2℃、相對濕度25±5%之環境下保管1個月。繼而,於室溫23℃±2℃之環境下,自中間膜剝離第2層(及第3層等其他層),藉此將第2層(及第3層等其他層)去除而獲得第1層。將所獲得之第1層以厚度成為0.35mm之方式於150℃下進行加壓成型(不加壓狀態下為150℃、10分鐘,加壓狀態下為150℃、10分鐘)而製作樹脂膜。又,於第1層難以剝離之情形時,亦可由利用鏟刀等切削第1層所獲得之樹脂組合物而製作上述樹脂膜。
以下,參照圖式對本發明之具體實施形態加以說明。
圖1中模式性地以剖視圖之形式展示本發明之第1實施形態之層合玻
璃用中間膜。
圖1所示之中間膜11為具有2層以上之構造之多層之中間膜。中間膜11係用於獲得層合玻璃。中間膜11為層合玻璃用中間膜。中間膜11具備第1層1、第2層2、及第3層3。於第1層1之第1表面1a配置第2層2而進行積層。於第1層1之與第1表面1a相反之第2表面1b配置第3層3而進行積層。第1層1為中間層。第2層2及第3層3分別為保護層,於本實施形態中為表面層。第1層1係配置於第2層2與第3層3之間而夾入其間。因此,中間膜11具有依序積層有第2層2、第1層1及第3層3之多層構造(第2層2/第1層1/第3層3)。
再者,第2層2與第1層1之間、及第1層1與第3層3之間分別可配置其他層。第2層2與第1層1、及第1層1與第3層3分別較佳為直接積層。作為其他層,可列舉包含聚對苯二甲酸乙二酯等之層。
圖2中模式性地以剖視圖之形式展示本發明之第2實施形態之層合玻璃用中間膜。
圖2所示之中間膜11A為具有1層構造之單層之中間膜。中間膜11A為第1層。中間膜11A係用於獲得層合玻璃。中間膜11A為層合玻璃用中間膜。
以下,對構成本發明之中間膜之上述第1層、上述第2層及上述第3層之詳細內容、以及上述第1層、上述第2層及上述第3層所含之各成分之詳細內容進行說明。
上述第1層、上述第2層及上述第3層分別較佳為包含樹脂。上述樹脂可僅使用1種,亦可併用2種以上。
作為上述樹脂,可列舉熱硬化性樹脂及熱塑性樹脂。上述樹脂亦可為使光硬化性化合物或濕氣硬化性化合物硬化而成之硬化物。上述使光硬化性化合物或濕氣硬化性化合物硬化而成之硬化物有時亦為熱塑性樹脂。
再者,所謂熱塑性樹脂係指若對其進行加熱則軟化而表現出可塑性,若將其冷卻至室溫則固化之樹脂。所謂熱塑性彈性體,特指熱塑性樹脂中之於加熱下軟化而表現出可塑性,冷卻至室溫(25℃)則固化而表現出橡膠彈性之樹脂。
作為上述熱塑性樹脂,可列舉:聚乙烯醇縮醛樹脂、聚酯樹脂、脂肪族聚烯烴、聚苯乙烯、乙烯-乙酸乙烯酯共聚物樹脂、乙烯-丙烯酸共聚物樹脂、聚胺基甲酸酯樹脂、離子聚合物樹脂、聚乙烯醇樹脂及聚乙酸乙烯酯等。亦可使用該等以外之熱塑性樹脂。再者,聚乙烯醇縮醛樹脂包括聚氧亞甲基(或聚縮醛)樹脂。
上述例示之熱塑性樹脂藉由調整樹脂之分子結構或聚合度等而可成為熱塑性彈性體。
上述樹脂較佳為熱塑性樹脂,更佳為聚乙烯醇縮醛樹脂、聚酯樹脂或聚乙酸乙烯酯,進而較佳為聚乙烯醇縮醛樹脂或聚酯樹脂,上述聚乙烯醇縮醛樹脂尤佳為聚乙烯醇縮丁醛樹脂。
上述第1層較佳為包含熱塑性樹脂(以下有時記載為熱塑性樹脂(1))、或包含使光硬化性化合物或濕氣硬化性化合物硬化而成之硬化物(以下有時記載為硬化物(1))。可將熱塑性樹脂(1)及硬化物(1)統稱為樹脂(1)。上述第1層可包含熱塑性樹脂(1),亦可包含使光硬化性化合物或濕氣硬化性化合物硬化而成之硬化物。上述第1層較佳為包含聚乙烯醇縮醛樹脂(以下有時記載為聚乙烯醇縮醛樹脂(1))或聚酯樹脂(以下有時記載為聚酯樹脂
(1))作為熱塑性樹脂(1)。上述第2層較佳為包含熱塑性樹脂(以下有時記載為熱塑性樹脂(2))。上述第2層較佳為包含聚乙烯醇縮醛樹脂(以下有時記載為聚乙烯醇縮醛樹脂(2))作為熱塑性樹脂(2)。上述第3層較佳為包含熱塑性樹脂(以下有時記載為熱塑性樹脂(3))。上述第3層較佳為包含聚乙烯醇縮醛樹脂(以下有時記載為聚乙烯醇縮醛樹脂(3))作為熱塑性樹脂(3)。上述熱塑性樹脂(1)、上述熱塑性樹脂(2)及上述熱塑性樹脂(3)分別可僅使用1種,亦可併用2種以上。上述熱塑性樹脂(1)、上述熱塑性樹脂(2)及上述熱塑性樹脂(3)可相同亦可不同。
光硬化性化合物或濕氣硬化性化合物較佳為具有(甲基)丙烯醯基之硬化性化合物,更佳為(甲基)丙烯酸系聚合物。上述樹脂較佳為具有(甲基)丙烯醯基之硬化性化合物,更佳為(甲基)丙烯酸系聚合物。
上述(甲基)丙烯酸系聚合物較佳為包含具有(甲基)丙烯醯基之硬化性化合物之聚合性組合物之聚合物。上述聚合性組合物包含聚合成分。為了有效地形成包含上述硬化物之層中之上述硬化物,上述聚合性組合物可包含光反應起始劑。上述聚合性組合物可一併包含光反應起始劑與用以促進硬化反應之助劑。作為上述具有(甲基)丙烯醯基之硬化性化合物之代表例,可列舉(甲基)丙烯酸酯。上述(甲基)丙烯酸系聚合物較佳為聚(甲基)丙烯酸酯。
為了有效地獲得本發明之效果,上述聚合成分較佳為包含:具有環狀醚結構之(甲基)丙烯酸酯、具有芳香環之(甲基)丙烯酸酯、具有極性基之(甲基)丙烯酸酯、側鏈之碳數為6以下之非環式(甲基)丙烯酸酯。藉由使用該等較佳之(甲基)丙烯酸酯,可平衡性良好地同時提高隔音性與發泡抑制性能。
作為上述具有環狀醚結構之(甲基)丙烯酸酯,可列舉:(甲基)丙烯酸縮水甘油酯、(甲基)丙烯酸2-羥基乙酯縮水甘油醚、(甲基)丙烯酸3-羥基丙酯縮水甘油醚、丙烯酸4-羥基丁酯縮水甘油醚、(甲基)丙烯酸5-羥基戊酯縮水甘油基、(甲基)丙烯酸6-羥基己酯縮水甘油醚;(甲基)丙烯酸(3-甲基氧雜環丁烷-3-基)甲酯、(甲基)丙烯酸(3-丙基氧雜環丁烷-3-基)甲酯、(甲基)丙烯酸(3-乙基氧雜環丁烷-3-基)甲酯、(甲基)丙烯酸(3-丁基氧雜環丁烷-3-基)甲酯、(甲基)丙烯酸(3-乙基氧雜環丁烷-3-基)乙酯、(甲基)丙烯酸(3-乙基氧雜環丁烷-3-基)丙酯、(甲基)丙烯酸(3-乙基氧雜環丁烷-3-基)丁酯、(甲基)丙烯酸(3-乙基氧雜環丁烷-3-基)戊酯、(甲基)丙烯酸(3-乙基氧雜環丁烷-3-基)己酯;(甲基)丙烯酸四氫糠酯、γ-丁內酯(甲基)丙烯酸酯、(甲基)丙烯酸(2,2-二甲基-1,3-二氧雜環戊烷-4-基)甲酯、(甲基)丙烯酸(2-甲基-2-乙基-1,3-二氧雜環戊烷-4-基)甲酯、(甲基)丙烯酸(2-甲基-2-異丁基-1,3-二氧雜環戊烷-4-基)甲酯、(甲基)丙烯酸(2-環己基-1,3-二氧雜環戊烷-4-基)甲酯、四氫糠醇丙烯酸多聚物酯;(甲基)丙烯酸四氫-2H-吡喃-2-基酯、(甲基)丙烯酸2-{1-[(四氫-2.H-吡喃-2-基)氧基]-2-甲基丙基}酯、環狀三羥甲基丙烷縮甲醛丙烯酸酯、(甲基)丙烯醯啉等。就有效地獲得本發明之效果之觀點而言,尤佳為(甲基)丙烯酸四氫糠酯、環狀三羥甲基丙烷縮甲醛丙烯酸酯。
作為上述具有芳香環之(甲基)丙烯酸酯,可列舉:丙烯酸苄酯、苯氧基聚乙二醇丙烯酸酯等。
作為上述具有極性基之(甲基)丙烯酸酯,可列舉具有羥基、醯胺基、胺基、異氰酸基等作為極性基之(甲基)丙烯酸酯。
作為具有羥基之(甲基)丙烯酸酯,例如可列舉:(甲基)丙烯酸2-羥基
乙酯、(甲基)丙烯酸羥基丙酯等。
作為具有醯胺基或胺基之(甲基)丙烯酸酯,例如可列舉:N-二烷基胺基烷基(甲基)丙烯醯胺、N,N-二烷基胺基烷基(甲基)丙烯醯胺等。
作為具有異氰酸基之(甲基)丙烯酸酯,可列舉:異氰尿酸三烯丙酯及其衍生物等。
上述(甲基)丙烯酸酯可為具有(甲基)丙烯醯基之多元羧酸酯。作為該具有(甲基)丙烯醯基之多元羧酸酯,可列舉琥珀酸2-丙烯醯氧基乙酯等。
就有效地獲得本發明之效果之觀點而言,較佳為具有羥基之(甲基)丙烯酸酯,尤佳為(甲基)丙烯酸2-羥基乙酯、(甲基)丙烯酸羥基丙酯。
作為上述側鏈之碳數為6以下之非環式(甲基)丙烯酸酯,例如可列舉:(甲基)丙烯酸甲酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸丙酯、(甲基)丙烯酸丁酯。
為了有效地獲得本發明之效果,於上述聚合成分100重量%中,側鏈之碳數為8以上之非環式(甲基)丙烯酸酯之調配量較佳為未達20重量%。
作為上述(甲基)丙烯酸酯,除上述化合物以外,例如可列舉:二乙二醇單乙醚(甲基)丙烯酸酯、(甲基)丙烯酸異基酯、(甲基)丙烯酸3-甲氧基丁酯、鄰苯二甲酸2-丙烯醯氧基乙基-2-羥基丙酯、鄰苯二甲酸2-丙烯醯氧基乙基-2-羥基丙酯、(甲基)丙烯酸環己酯;乙二醇二(甲基)丙烯酸酯、二乙二醇二(甲基)丙烯酸酯、四乙二醇二(甲基)丙烯酸酯、1,6-己二醇二(甲基)丙烯酸酯、1,9-壬二醇二(甲基)丙烯酸酯、聚四亞甲基二醇二(甲基)
丙烯酸酯、新戊二醇二(甲基)丙烯酸酯、1,3-丁二醇二(甲基)丙烯酸酯、2,2-雙[4-(丙烯醯氧基乙氧基)苯基]丙烷二(甲基)丙烯酸酯;三羥甲基丙烷三(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、季戊四醇四(甲基)丙烯酸酯、二季戊四醇五(甲基)丙烯酸酯、二季戊四醇六(甲基)丙烯酸酯、磷酸三(2-丙烯醯氧基乙基)酯、四羥甲基甲烷三(甲基)丙烯酸酯、四羥甲基丙烷四(甲基)丙烯酸酯及其衍生物等。
上述(甲基)丙烯酸酯可僅使用1種,亦可併用2種以上。上述(甲基)丙烯酸系聚合物可為上述(甲基)丙烯酸酯之均聚物,亦可為包含上述(甲基)丙烯酸酯之聚合成分之共聚物。
作為上述光反應起始劑,具體而言,可列舉:2-甲基-1-(4-甲硫基苯基)-2-啉基丙烷-1-酮、2-苄基-2-二甲基胺基-1-(4-啉基苯基)-丁酮-1、2-(二甲基胺基)-2-[(4-甲基苯基)甲基]-1-[4-(4-啉基)苯基]-1-丁酮、2,4,6-三甲基苯甲醯基-二苯基-氧化膦、雙(2,4,6-三甲基苯甲醯基)-苯基氧化膦、雙(η5-2,4-環戊二烯-1-基)-雙(2,6-二氟-3-(1H-吡咯-1-基)-苯基)鈦、2-甲基-1-(4-甲硫基苯基)-2-啉基丙烷-1-酮、2-苄基-2-二甲基胺基-1-(4-啉基苯基)-丁酮-1、2-(二甲基胺基)-2-[(4-甲基苯基)甲基]-1-[4-(4-啉基)苯基]-1-丁酮、二乙氧基苯乙酮、2-羥基-2-甲基-1-苯基丙烷-1-酮、苄基二甲基縮酮、4-(2-羥基乙氧基)苯基-(2-羥基-2-丙基)酮、1-羥基環己基苯基酮、2-甲基-2-啉基(4-硫代甲基苯基)丙烷-1-酮、2-苄基-2-二甲基胺基-1-(4-啉基苯基)丁酮、2-羥基-2-甲基-1-[4-(1-甲基乙烯基)苯基]丙酮低聚物、安息香、安息香甲醚、安息香乙醚、安息香異丙醚、安息香異丁醚、二苯甲酮、鄰苯甲醯苯甲酸甲酯、4-苯基二苯甲酮、4-苯甲醯基-4'-甲基-二苯硫醚、3,3',4,4'-四(第三丁基過氧化羰基)二苯甲酮、
2,4,6-三甲基二苯甲酮、4-苯甲醯基-N,N-二甲基-N-[2-(1-側氧基-2-丙烯基氧基)乙基]苯甲溴化銨、氯化(4-苯甲醯基苄基)三甲基銨、2-異丙基9-氧硫、4-異丙基9-氧硫、2,4-二乙基9-氧硫、2,4-二氯9-氧硫、1-氯-4-丙氧基9-氧硫、2-(3-二甲基胺基-2-羥基)-3,4-二甲基-9H-9-氧硫-9-酮內消旋氯化物、2,4,6-三甲基苯甲醯基-二苯基氧化膦、雙(2,6-二甲氧基苯甲醯基)-2,4,4-三甲基-戊基氧化膦、雙(2,4,6-三甲基苯甲醯基)-苯基氧化膦、三苯基甲鎓四(五氟苯基)硼酸鹽等。上述光反應起始劑可僅使用1種,亦可併用2種以上。
作為上述助劑,可列舉:三乙醇胺、三異丙醇胺、4,4'-二甲基胺基二苯甲酮(米其勒酮)、4,4'-二乙基胺基二苯甲酮、2-二甲基胺基苯甲酸乙酯、4-二甲基胺基苯甲酸乙酯。又,可列舉:4-二甲基胺基苯甲酸(正丁氧基)乙酯、4-二甲基胺基苯甲酸異戊酯、4-二甲基胺基苯甲酸2-乙基己酯、2,4-二乙基噻噸酮、2,4-二異丙基噻噸酮等。上述助劑可僅使用1種,亦可併用2種以上。
上述助劑較佳為苄基二甲基縮酮、1-羥基環己基苯基酮、苯甲醯基異丙醚、4-(2-羥基乙氧基)-苯基(2-羥基-2-丙基)酮、2-羥基-2-甲基-1-苯基丙烷-1-酮、三苯基甲鎓四(五氟苯基)硼酸鹽。
於上述聚合性組合物100重量%中,上述光反應起始劑之含量較佳為0.01重量%以上,更佳為0.1重量份以上,又,較佳為10重量%以下,更佳為5重量%以下。若上述光反應起始劑之含量為上述下限以上且上述上限以下,則光硬化性及保存穩定性進一步提高。
就本發明之效果優異之方面而言,上述聚乙酸乙烯酯較佳為包含乙酸乙烯酯與上述具有官能基之單體的聚合性組合物之聚合物。
作為上述具有官能基之單體,可列舉:3-甲基-3-丁基1-醇、乙二醇單乙烯醚、及異丙基丙烯醯胺等。
就有效地提高隔音性之觀點而言,聚乙酸乙烯酯之重量平均分子量較佳為25萬以上,更佳為30萬以上,進而較佳為40萬以上,尤佳為50萬以上。就使層間接著力變得良好之觀點而言,聚乙酸乙烯酯之重量平均分子量較佳為120萬以下,更佳為90萬以下。
上述重量平均分子量表示藉由凝膠滲透層析法(GPC)所測得之以聚苯乙烯換算計之重量平均分子量。
使上述聚合性組合物聚合而合成上述聚乙酸乙烯酯之方法並無特別限定。作為該合成方法,可列舉:溶液聚合法、懸浮聚合法、及UV聚合法等。
就提高中間膜之透明性、且有效地提高透明性得到提高之中間膜之隔音性及層間接著力之觀點而言,上述聚乙酸乙烯酯之合成方法較佳為溶液聚合法。
上述聚乙烯醇縮醛樹脂例如藉由利用醛將聚乙烯醇(PVA)進行縮醛化而獲得。上述聚乙烯醇縮醛樹脂較佳為聚乙烯醇之縮醛化物。上述聚乙烯醇例如藉由將聚乙酸乙烯酯進行皂化而獲得。上述聚乙烯醇之皂化度一般為70~99.9莫耳%。
上述聚乙烯醇(PVA)之平均聚合度較佳為200以上,更佳為500以上,進而較佳為1500以上,進而較佳為1600以上,尤佳為2600以上,最佳為2700以上,又,較佳為5000以下,更佳為4000以下,進而較佳為3500以下。若上述平均聚合度為上述下限以上,則層合玻璃之耐貫通性進一步提高。若上述平均聚合度為上述上限以下,則中間膜易於成形。
上述聚乙烯醇之平均聚合度係藉由依據JIS K6726「聚乙烯醇試驗方法」之方法而求出。
上述聚乙烯醇縮醛樹脂中之縮醛基之碳數較佳為3~5,較佳為4或5。
作為上述醛,一般適宜使用碳數為1~10之醛。作為上述碳數為1~10之醛,例如可列舉:甲醛、乙醛、丙醛、正丁醛、異丁醛、正戊醛、2-乙基丁醛、正己醛、正辛醛、正壬醛、正癸醛及苯甲醛等。較佳為乙醛、丙醛、正丁醛、異丁醛、正己醛或正戊醛,更佳為乙醛、丙醛、正丁醛、異丁醛或正戊醛,進而較佳為正丁醛或正戊醛。上述醛可僅使用1種,亦可併用2種以上。
上述聚乙烯醇縮醛樹脂(1)之羥基之含有率(羥基量)較佳為17莫耳%以上,更佳為20莫耳%以上,進而較佳為22莫耳%以上。上述聚乙烯醇縮醛樹脂(1)之羥基之含有率(羥基量)較佳為30莫耳%以下,更佳為28莫耳%以下,進而較佳為27莫耳%以下,進而較佳為25莫耳%以下,尤佳為未達25莫耳%,最佳為24莫耳%以下。若上述羥基之含有率為上述下限以上,則中間膜之機械強度進一步提高。尤其若上述聚乙烯醇縮醛樹脂(1)之羥基之含有率為20莫耳%以上,則反應效率較高而生產性優異,又,若為30莫耳%以下,則層合玻璃之隔音性進一步提高,若為28莫耳%以下,則隔音性更進一步提高。又,若上述羥基之含有率為上述上限以下,則中間膜之柔軟性變高,容易對中間膜進行處理。
上述聚乙烯醇縮醛樹脂(2)及上述聚乙烯醇縮醛樹脂(3)之羥基之各含有率較佳為25莫耳%以上,更佳為28莫耳%以上,更佳為30莫耳%以上,進而較佳為超過31莫耳%。上述聚乙烯醇縮醛樹脂(2)及上述聚乙烯醇縮
醛樹脂(3)之羥基之各含有率進而較佳為31.5莫耳%以上,進而更佳為32莫耳%以上,尤佳為33莫耳%以上。上述聚乙烯醇縮醛樹脂(2)及上述聚乙烯醇縮醛樹脂(3)之羥基之各含有率較佳為37莫耳%以下,更佳為36.5莫耳%以下,進而較佳為36莫耳%以下。若上述羥基之含有率為上述下限以上,則中間膜之接著力進一步提高。又,若上述羥基之含有率為上述上限以下,則中間膜之柔軟性變高,容易對中間膜進行處理。
就進一步提高隔音性之觀點而言,上述聚乙烯醇縮醛樹脂(1)之羥基之含有率較佳為低於上述聚乙烯醇縮醛樹脂(2)之羥基之含有率。就進一步提高隔音性之觀點而言,上述聚乙烯醇縮醛樹脂(1)之羥基之含有率較佳為低於上述聚乙烯醇縮醛樹脂(3)之羥基之含有率。就進一步提高隔音性之觀點而言,上述聚乙烯醇縮醛樹脂(1)之羥基之含有率與上述聚乙烯醇縮醛樹脂(2)之羥基之含有率的差之絕對值較佳為1莫耳%以上,更佳為5莫耳%以上,進而較佳為9莫耳%以上,尤佳為10莫耳%以上,最佳為12莫耳%以上。就進一步提高隔音性之觀點而言,上述聚乙烯醇縮醛樹脂(1)之羥基之含有率與上述聚乙烯醇縮醛樹脂(3)之羥基之含有率的差之絕對值較佳為1莫耳%以上,更佳為5莫耳%以上,進而較佳為9莫耳%以上,尤佳為10莫耳%以上,最佳為12莫耳%以上。上述聚乙烯醇縮醛樹脂(1)之羥基之含有率與上述聚乙烯醇縮醛樹脂(2)之羥基之含有率的差之絕對值較佳為20莫耳%以下。上述聚乙烯醇縮醛樹脂(1)之羥基之含有率與上述聚乙烯醇縮醛樹脂(3)之羥基之含有率的差之絕對值較佳為20莫耳%以下。
上述聚乙烯醇縮醛樹脂之羥基之含有率係將羥基所鍵結之伸乙基量除以主鏈之伸乙基總量所求出之莫耳分率以百分率表示之值。上述羥基所
鍵結之伸乙基量例如可依據JIS K6728「聚乙烯醇縮丁醛試驗方法」而測定。
上述聚乙烯醇縮醛樹脂(1)之乙醯化度(乙醯基量)較佳為0.01莫耳%以上,更佳為0.1莫耳%以上,進而較佳為7莫耳%以上,進而較佳為9莫耳%以上,又,較佳為30莫耳%以下,更佳為25莫耳%以下,進而較佳為24莫耳%以下,尤佳為20莫耳%以下。若上述乙醯化度為上述下限以上,則聚乙烯醇縮醛樹脂與塑化劑之相溶性變高。若上述乙醯化度為上述上限以下,則中間膜及層合玻璃之耐濕性變高。尤其若上述聚乙烯醇縮醛樹脂(1)之乙醯化度為0.1莫耳%以上且25莫耳%以下,則耐貫通性更優異。
上述聚乙烯醇縮醛樹脂(2)及上述聚乙烯醇縮醛樹脂(3)之各乙醯化度較佳為0.01莫耳%以上,更佳為0.5莫耳%以上,又,較佳為10莫耳%以下,更佳為2莫耳%以下。若上述乙醯化度為上述下限以上,則聚乙烯醇縮醛樹脂與塑化劑之相溶性變高。若上述乙醯化度為上述上限以下,則中間膜及層合玻璃之耐濕性變高。
上述乙醯化度係將乙醯基所鍵結之伸乙基量除以主鏈之伸乙基總量所求出之莫耳分率以百分率表示之值。上述乙醯基所鍵結之伸乙基量例如可依據JIS K6728「聚乙烯醇縮丁醛試驗方法」而測定。
上述聚乙烯醇縮醛樹脂(1)之縮醛化度(於聚乙烯醇縮丁醛樹脂之情形時為縮丁醛化度)較佳為47莫耳%以上,更佳為60莫耳%以上,又,較佳為85莫耳%以下,更佳為80莫耳%以下,進而較佳為75莫耳%以下。若上述縮醛化度為上述下限以上,則聚乙烯醇縮醛樹脂與塑化劑之相溶性變高。若上述縮醛化度為上述上限以下,則用以製造聚乙烯醇縮醛樹脂所需之反應時間變短。
上述聚乙烯醇縮醛樹脂(2)及上述聚乙烯醇縮醛樹脂(3)之各縮醛化度(於聚乙烯醇縮丁醛樹脂之情形時為縮丁醛化度)較佳為55莫耳%以上,更佳為60莫耳%以上,又,較佳為75莫耳%以下,更佳為71莫耳%以下。若上述縮醛化度為上述下限以上,則聚乙烯醇縮醛樹脂與塑化劑之相溶性變高。若上述縮醛化度為上述上限以下,則用以製造聚乙烯醇縮醛樹脂所需之反應時間變短。
上述縮醛化度係藉由如下方式求出。首先,求出自主鏈之伸乙基總量減去羥基所鍵結之伸乙基量與乙醯基所鍵結之伸乙基量所得之值。用所獲得之值除以主鏈之伸乙基總量而求出莫耳分率。將該莫耳分率以百分率表示之值即為縮醛化度。
再者,上述羥基之含有率(羥基量)、縮醛化度(縮丁醛化度)及乙醯化度較佳為由利用依據JIS K6728「聚乙烯醇縮丁醛試驗方法」之方法所測得之結果而算出。但亦可採用依據ASTM D1396-92之測定。於聚乙烯醇縮醛樹脂為聚乙烯醇縮丁醛樹脂之情形時,上述羥基之含有率(羥基量)、上述縮醛化度(縮丁醛化度)及上述乙醯化度可由利用依據JIS K6728「聚乙烯醇縮丁醛試驗方法」之方法所測得之結果而算出。
上述聚酯樹脂可藉由通常所知之聚酯之製造方法而製造。上述聚酯樹脂例如可藉由如下方法製造:藉由多元酸與多元醇之縮合反應而獲得聚酯,藉由使多元酸之烷基酯與多元醇進行酯交換反應而獲得聚酯,使藉由上述方法所獲得之聚酯於聚合觸媒之存在下進一步聚合而獲得聚酯。
作為上述多元酸,例如可列舉:對苯二甲酸、間苯二甲酸、鄰苯二甲酸、萘二甲酸等芳香族二羧酸;琥珀酸、戊二酸、己二酸、壬二酸、癸二酸、十二烷二酸、二聚酸等脂肪族二羧酸;順丁烯二酸(酐)、反丁烯二
酸、十二碳烯基琥珀酸酐、萜烯-順丁烯二酸加成體等不飽和二羧酸;1,4-環己烷二羧酸、四氫鄰苯二甲酸、六氫間苯二甲酸、1,2-環己烯二羧酸等脂環族二羧酸;偏苯三甲酸(酐)、均苯四甲酸(酐)、甲基環己烯三羧酸等三元以上之羧酸;4,4-雙(4'-羥基苯基)戊酸、4-單(4'-羥基苯基)戊酸、對羥基苯甲酸等單羧酸等。
作為上述多元醇,可列舉:乙二醇、丙二醇(1,2-丙二醇、1,3-丙二醇)、1,4-丁二醇、1,2-丁二醇、1,3-丁二醇、2-甲基-1,3-丙二醇、新戊二醇、1,5-戊二醇、1,6-己二醇、3-甲基-1,5-戊二醇、2-乙基-2-丁基-1,3-丙二醇、2,4-二乙基-1,5-戊二醇、1-甲基-1,8-辛二醇、3-甲基-1,6-己二醇、4-甲基-1,7-庚二醇、4-甲基-1,8-辛二醇、4-丙基-1,8-辛二醇、1,9-壬二醇等脂肪族二醇;二乙二醇、三乙二醇、聚乙二醇、聚丙二醇、聚四亞甲基二醇等醚二醇;1,4-環己烷二甲醇、1,3-環己烷二甲醇、1,2-環己烷二甲醇、三環癸二醇、氫化雙酚等脂環族多元醇;三羥甲基丙烷、三羥甲基乙烷、季戊四醇等三元以上之多元醇等。
作為上述聚酯樹脂之市售品,例如可列舉:Unitika公司製造之「elitel UE-3220」及Unitika公司製造之「elitel UE-3223」。
上述第1層較佳為包含塑化劑(以下有時記載為塑化劑(1))。上述第2層較佳為包含塑化劑(以下有時記載為塑化劑(2))。上述第3層較佳為包含塑化劑(以下有時記載為塑化劑(3))。藉由使用塑化劑,進而藉由將聚乙烯醇縮醛樹脂與塑化劑併用,包含聚乙烯醇縮醛樹脂與塑化劑之層對層合玻璃構件或其他層之接著力適度變高。上述塑化劑並無特別限定。上述塑化劑(1)與上述塑化劑(2)與上述塑化劑(3)可相同亦可不同。上述塑化劑
(1)、上述塑化劑(2)及上述塑化劑(3)分別可僅使用1種,亦可併用2種以上。
作為上述塑化劑,可列舉:一元性有機酸酯及多元性有機酸酯等有機酯塑化劑、以及有機磷酸塑化劑及有機亞磷酸塑化劑等有機磷酸塑化劑等。較佳為有機酯塑化劑。上述塑化劑較佳為液狀塑化劑。
作為上述一元性有機酸酯,可列舉藉由二醇與一元性有機酸之反應而獲得之二醇酯等。作為上述二醇,可列舉:三乙二醇、四乙二醇及三丙二醇等。作為上述一元性有機酸,可列舉:丁酸、異丁酸、己酸、2-乙基丁酸、庚酸、正辛酸、2-乙基己基酸、正壬酸及癸酸及苯甲酸等。
作為上述多元性有機酸酯,可列舉多元性有機酸與碳數4~8之具有直鏈或支鏈結構之醇之酯化合物等。作為上述多元性有機酸,可列舉:鄰苯二甲酸、己二酸、癸二酸及壬二酸等。
作為上述有機酯塑化劑,可列舉:三乙二醇二-2-乙基丙酸酯、三乙二醇二-2-乙基丁酸酯、三乙二醇二-2-乙基己酸酯、三乙二醇二辛酸酯、三乙二醇二正辛酸酯、三乙二醇二正庚酸酯、四乙二醇二正庚酸酯、癸二酸二丁酯、壬二酸二辛酯、二丁基卡必醇己二酸酯、乙二醇二-2-乙基丁酸酯、1,3-丙二醇二-2-乙基丁酸酯、1,4-丁二醇二-2-乙基丁酸酯、二乙二醇二-2-乙基丁酸酯、二乙二醇二-2-乙基己酸酯、二丙二醇二-2-乙基丁酸酯、三乙二醇二-2-乙基戊酸酯、四乙二醇二-2-乙基丁酸酯、二乙二醇二辛酸酯、二乙二醇二苯甲酸酯、二丙二醇二苯甲酸酯、順丁烯二酸二丁酯、己二酸雙(2-丁氧基乙基)酯、己二酸二丁酯、己二酸二異丁酯、己二酸2,2-丁氧基乙氧基乙酯、苯甲酸二醇酯、己二酸1,3-丁二醇聚酯、己二酸二己酯、己二酸二辛酯、己二酸己基環己酯、己二酸庚酯與己二酸壬酯
之混合物、己二酸二異壬酯、己二酸二異癸酯、己二酸庚基壬酯、檸檬酸三丁酯、乙醯基檸檬酸三丁酯、碳酸二乙酯、癸二酸二丁酯、油改性癸二酸醇酸、及磷酸酯與己二酸酯之混合物等。亦可使用該等以外之有機酯塑化劑。亦可使用上述己二酸酯以外之其他己二酸酯。
作為上述有機磷酸塑化劑,可列舉:磷酸三丁氧基乙酯、磷酸異癸基苯酯、磷酸三甲苯酯及磷酸三異丙酯等。
上述塑化劑較佳為下述式(11)所表示之二酯塑化劑。
上述式(11)中,R1及R2分別表示碳數2~10之有機基,R3表示伸乙基、伸異丙基或伸正丙基,p表示3~10之整數。上述式(11)中之R1及R2分別較佳為碳數5~10之有機基,更佳為碳數6~10之有機基。
上述塑化劑較佳為包含三乙二醇二-2-乙基己酸酯(3GO)、三乙二醇二-2-乙基丁酸酯(3GH)或三乙二醇二-2-乙基丙酸酯。上述塑化劑更佳為包含三乙二醇二-2-乙基己酸酯或三乙二醇二-2-乙基丁酸酯,進而較佳為包含三乙二醇二-2-乙基己酸酯。
將上述第1層中之相對於上述樹脂(1)100重量份之上述塑化劑(1)之含量設為含量(1)。於上述樹脂(1)為熱塑性樹脂(1)之情形時,樹脂(1)100重量份即為熱塑性樹脂(1)100重量份。於樹脂(1)為聚乙烯醇縮醛樹脂(1)之情形時,樹脂(1)100重量份即為聚乙烯醇縮醛樹脂(1)100重量份。於樹脂(1)為聚酯樹脂(1)之情形時,樹脂(1)100重量份即為聚酯樹脂(1)100重量份。其他樹脂之基準亦相同。上述含量(1)較佳為50重量份以上,更佳為
55重量份以上,進而較佳為60重量份以上,又,較佳為130重量份以下,更佳為100重量份以下,進而較佳為90重量份以下,尤其更佳為85重量份以下,最佳為80重量份以下。若上述含量(1)為上述下限以上,則中間膜之柔軟性變高,容易對中間膜進行處理。若上述含量(1)為上述上限以下,則層合玻璃之耐貫通性進一步提高。
將上述第2層中之相對於上述熱塑性樹脂(2)100重量份之上述塑化劑(2)之含量設為含量(2)。於上述第3層中之熱塑性樹脂(2)為聚乙烯醇縮醛樹脂(2)之情形時,熱塑性樹脂(2)100重量份即為聚乙烯醇縮醛樹脂(2)100重量份。於熱塑性樹脂(2)為聚酯樹脂(2)之情形時,熱塑性樹脂(2)100重量份即為聚酯樹脂(2)100重量份。其他樹脂之基準亦相同。將上述第3層中之相對於上述熱塑性樹脂(3)100重量份之上述塑化劑(3)之含量設為含量(3)。於熱塑性樹脂(3)為聚乙烯醇縮醛樹脂(3)之情形時,熱塑性樹脂(3)100重量份即為聚乙烯醇縮醛樹脂(3)100重量份。於熱塑性樹脂(3)為聚酯樹脂(3)之情形時,熱塑性樹脂(3)100重量份即為聚酯樹脂(3)100重量份。其他樹脂之基準亦相同。上述含量(2)及上述含量(3)分別較佳為10重量份以上,更佳為15重量份以上,又,較佳為40重量份以下,更佳為39重量份以下,進而較佳為35重量份以下,進而更佳為32重量份以下,尤佳為30重量份以下。若上述含量(2)及上述含量(3)為上述下限以上,則中間膜之柔軟性變高,容易對中間膜進行處理。若上述含量(2)及上述含量(3)為上述上限以下,則耐貫通性進一步提高。
為了進一步提高層合玻璃之隔音性,上述含量(1)較佳為大於上述含量(2),上述含量(1)較佳為大於上述含量(3)。
就進一步提高層合玻璃之隔音性之觀點而言,上述含量(2)與上述含
量(1)之差之絕對值、以及上述含量(3)與上述含量(1)之差之絕對值分別較佳為10重量份以上,更佳為15重量份以上,進而較佳為20重量份以上。上述含量(2)與上述含量(1)之差之絕對值、以及上述含量(3)與上述含量(1)之差之絕對值分別較佳為80重量份以下,更佳為75重量份以下,進而較佳為70重量份以下。
就有效地提高隔音性之觀點而言,上述第1層較佳為包含軟化點為70℃以上且200℃以下之化合物(以下有時記載為化合物(A))。認為藉由使用上述化合物(A),第1層中之於玻璃轉移溫度附近之分子運動加劇,結果使隔音性變高。上述化合物(A)可僅使用1種,亦可併用2種以上。
就有效地提高隔音性之觀點而言,上述化合物(A)之軟化點較佳為80℃以上,又,較佳為190℃以下。
再者,於上述化合物(A)為不具有軟化點之化合物之情形時,就有效地提高隔音性之觀點而言,上述第1層較佳為包含熔點為70℃以上且200℃以下之化合物。
上述化合物(A)較佳為與熱塑性樹脂不同之化合物。上述化合物(A)較佳為與聚乙烯醇縮醛樹脂不同之化合物。
作為上述化合物(A),具體而言,可列舉:具有複數個芳香族之酯化合物;具有複數個芳香族之醚化合物;松香樹脂、萜烯樹脂及石油樹脂等黏著賦予劑;氯化石蠟等。
作為上述化合物(A)之市售品,可列舉:KE-311(荒川化學工業公司製造,軟化點95℃)及Enpara 70(Ajinomoto Fine-Techno公司製造,軟化點100℃)等。
於上述第1層100重量%中,上述化合物(A)之含量較佳為20重量%以上,更佳為30重量%以上,又,較佳為50重量%以下,更佳為40重量%以下。又,相對於上述熱塑性樹脂(1)100重量份(於熱塑性樹脂(1)為聚乙烯醇縮醛樹脂(1)之情形時為聚乙烯醇縮醛樹脂(1)100重量份)之上述化合物(A)之含量較佳為50重量份以上,更佳為60重量份以上。相對於上述熱塑性樹脂(1)100重量份(於熱塑性樹脂(1)為聚乙烯醇縮醛樹脂(1)之情形時為聚乙烯醇縮醛樹脂(1)100重量份)之上述化合物(A)之含量較佳為200重量份以下,更佳為150重量份以下。若上述化合物(A)之含量為上述下限以上,則隔音性有效地變高。若上述化合物(A)之含量為上述上限以下,則成形性變得更良好。
上述中間膜亦可包含隔熱性物質(隔熱性化合物)。上述第1層可包含隔熱性物質。上述第2層可包含隔熱性物質。上述第3層可包含隔熱性物質。上述隔熱性物質可僅使用1種,亦可併用2種以上。
成分X:
上述中間膜亦可包含酞菁化合物、萘酚菁化合物及蒽酞菁化合物中之至少1種成分X。上述第1層可包含上述成分X。上述第2層可包含上述成分X。上述第3層可包含上述成分X。上述成分X為隔熱性物質。上述成分X可僅使用1種,亦可併用2種以上。
上述成分X並無特別限定。作為成分X,可使用先前公知之酞菁化合物、萘酚菁化合物及蒽酞菁化合物。
就進一步提高中間膜及層合玻璃之隔熱性之觀點而言,上述成分X較佳為選自由酞菁、酞菁之衍生物、萘酚菁及萘酚菁之衍生物所組成之群中
之至少1種,更佳為酞菁及酞菁之衍生物中之至少1種。
就有效地提高隔熱性、且長時間持續以更高水準維持可見光光線透過率之觀點而言,上述成分X較佳為含有釩原子或銅原子。上述成分X較佳為含有釩原子,亦較佳為含有銅原子。上述成分X更佳為含有釩原子或銅原子之酞菁及含有釩原子或銅原子之酞菁之衍生物中之至少1種。就進一步提高中間膜及層合玻璃之隔熱性之觀點而言,上述成分X較佳為具有於釩原子上鍵結有氧原子之結構單元。
於包含上述成分X之層(第1層、第2層或第3層)100重量%中,上述成分X之含量較佳為0.001重量%以上,更佳為0.005重量%以上,進而較佳為0.01重量%以上,尤佳為0.02重量%以上。於包含上述成分X之層(第1層、第2層或第3層)100重量%中,上述成分X之含量較佳為0.2重量%以下,更佳為0.1重量%以下,進而較佳為0.05重量%以下,尤佳為0.04重量%以下。若上述成分X之含量為上述下限以上且上述上限以下,則隔熱性充分變高,且可見光光線透過率充分變高。例如可使可見光光線透過率達到70%以上。
隔熱粒子:
上述中間膜亦可包含隔熱粒子。上述第1層可包含上述隔熱粒子。上述第2層可包含上述隔熱粒子。上述第3層可包含上述隔熱粒子。上述隔熱粒子為隔熱性物質。藉由使用隔熱粒子,可有效地遮斷紅外線(熱射線)。上述隔熱粒子可僅使用1種,亦可併用2種以上。
就進一步提高層合玻璃之隔熱性之觀點而言,上述隔熱粒子更佳為金屬氧化物粒子。上述隔熱粒子較佳為由金屬之氧化物所形成之粒子(金屬氧化物粒子)。
與紫外線相比,波長大於可見光之780nm以上之紅外線之能量較小。然而,紅外線之熱作用較大,被物質吸收之紅外線可作為熱而釋出。因此,紅外線一般被稱為熱射線。藉由使用隔上述熱粒子,可有效地遮斷紅外線(熱射線)。再者,所謂隔熱粒子,意指能夠吸收紅外線之粒子。
作為上述隔熱粒子之具體例,可列舉:摻鋁氧化錫粒子、摻銦氧化錫粒子、摻銻氧化錫粒子(ATO粒子)、摻鎵氧化鋅粒子(GZO粒子)、摻銦氧化鋅粒子(IZO粒子)、摻鋁氧化鋅粒子(AZO粒子)、摻鈮氧化鈦粒子、摻鈉氧化鎢粒子、摻銫氧化鎢粒子、摻鉈氧化鎢粒子、摻銣氧化鎢粒子、摻錫氧化銦粒子(ITO粒子)、摻錫氧化鋅粒子、摻矽氧化鋅粒子等金屬氧化物粒子、或六硼化鑭(LaB6)粒子等。亦可使用該等以外之隔熱粒子。由於熱射線之遮斷功能較高,故較佳為金屬氧化物粒子,更佳為ATO粒子、GZO粒子、IZO粒子、ITO粒子或氧化鎢粒子,尤佳為ITO粒子或氧化鎢粒子。尤其是由於熱射線之遮斷功能較高、且容易獲得,故較佳為摻錫氧化銦粒子(ITO粒子),亦較佳為氧化鎢粒子。
就進一步提高中間膜及層合玻璃之隔熱性之觀點而言,氧化鎢粒子較佳為摻金屬之氧化鎢粒子。上述「氧化鎢粒子」包括摻金屬之氧化鎢粒子。作為上述摻金屬之氧化鎢粒子,具體而言,可列舉:摻鈉氧化鎢粒子、摻銫氧化鎢粒子、摻鉈氧化鎢粒子及摻銣氧化鎢粒子等。
就進一步提高中間膜及層合玻璃之隔熱性之觀點而言,尤佳為摻銫氧化鎢粒子。就進一步提高中間膜及層合玻璃之隔熱性之觀點而言,該摻銫氧化鎢粒子較佳為式:Cs0.33WO3所表示之氧化鎢粒子。
上述隔熱粒子之平均粒徑較佳為0.01μm以上,更佳為0.02μm以上,又,較佳為0.1μm以下,更佳為0.05μm以下。若平均粒徑為上述下
限以上,則熱射線之遮斷性充分變高。若平均粒徑為上述上限以下,則隔熱粒子之分散性變高。
上述「平均粒徑」表示體積平均粒徑。平均粒徑可使用粒度分佈測定裝置(日機裝公司製造之「UPA-EX150」)等進行測定。
於包含上述隔熱粒子之層(第1層、第2層或第3層)100重量%中,上述隔熱粒子之含量較佳為0.01重量%以上,更佳為0.1重量%以上,進而較佳為1重量%以上,尤佳為1.5重量%以上。於包含上述隔熱粒子之層(第1層、第2層或第3層)100重量%中,上述隔熱粒子之含量較佳為6重量%以下,更佳為5.5重量%以下,進而較佳為4重量%以下,尤佳為3.5重量%以下,最佳為3重量%以下。若上述隔熱粒子之含量為上述下限以上且上述上限以下,則隔熱性充分變高,且可見光光線透過率充分變高。
上述中間膜亦可包含鹼金屬鹽、鹼土金屬鹽及Mg鹽中之至少1種金屬鹽(以下有時記載為金屬鹽M)。上述第1層可包含上述金屬鹽M。上述第2層較佳為包含上述金屬鹽M。上述第3層可包含上述金屬鹽M。上述表面層可包含上述金屬鹽M。藉由使用上述金屬鹽M,易於控制中間膜與層合玻璃構件之接著性或中間膜中之各層間之接著性。上述金屬鹽M可僅使用1種,亦可併用2種以上。
上述金屬鹽M較佳為包含選自由Li、Na、K、Rb、Cs、Mg、Ca、Sr及Ba所組成之群中之至少1種金屬。中間膜中所含之金屬鹽較佳為包含K及Mg中之至少1種金屬。
又,上述金屬鹽M更佳為碳數2~16之有機酸之鹼金屬鹽、碳數2~16之有機酸之鹼土金屬鹽或碳數2~16之有機酸之Mg鹽,進而較佳為碳數
2~16之羧酸鎂鹽或碳數2~16之羧酸鉀鹽。
作為上述碳數2~16之羧酸鎂鹽及上述碳數2~16之羧酸鉀鹽,可列舉:乙酸鎂、乙酸鉀、丙酸鎂、丙酸鉀、2-乙基丁酸鎂、2-乙基丁酸鉀、2-乙基己酸鎂及2-乙基己酸鉀等。
包含上述金屬鹽M之層(第1層、第2層或第3層)中之Mg與K之合計含量較佳為5ppm以上,更佳為10ppm以上,進而較佳為20ppm以上,又,較佳為300ppm以下,更佳為250ppm以下,進而較佳為200ppm以下。若Mg與K之合計含量為上述下限以上且上述上限以下,則可更良好地控制中間膜與層合玻璃構件之接著性或中間膜中之各層間之接著性。
上述中間膜亦可包含紫外線遮斷劑。上述第1層可包含紫外線遮斷劑。上述第2層可包含紫外線遮斷劑。上述第3層可包含紫外線遮斷劑。藉由使用紫外線遮斷劑,中間膜及層合玻璃即便經過長期使用,可見光光線透過率亦更加不容易降低。上述紫外線遮斷劑可僅使用1種,亦可併用2種以上。
上述紫外線遮斷劑包括紫外線吸收劑。上述紫外線遮斷劑較佳為紫外線吸收劑。
作為上述紫外線遮斷劑,例如可列舉:包含金屬原子之紫外線遮斷劑、包含金屬氧化物之紫外線遮斷劑、具有苯并三唑結構之紫外線遮斷劑、具有二苯甲酮結構之紫外線遮斷劑、具有三結構之紫外線遮斷劑、具有丙二酸酯結構之紫外線遮斷劑、具有草醯替苯胺結構之紫外線遮斷劑及具有苯甲酸酯結構之紫外線遮斷劑等。
作為上述包含金屬原子之紫外線遮斷劑,例如可列舉:鉑粒子、利
用二氧化矽被覆鉑粒子表面而成之粒子、鈀粒子及利用二氧化矽被覆鈀粒子表面而成之粒子等。紫外線遮斷劑較佳為並非隔熱粒子。
上述紫外線遮斷劑較佳為具有苯并三唑結構之紫外線遮斷劑、具有二苯甲酮結構之紫外線遮斷劑、具有三結構之紫外線遮斷劑或具有苯甲酸酯結構之紫外線遮斷劑。上述紫外線遮斷劑更佳為具有苯并三唑結構之紫外線遮斷劑或具有二苯甲酮結構之紫外線遮斷劑,進而較佳為具有苯并三唑結構之紫外線遮斷劑。
作為上述包含金屬氧化物之紫外線遮斷劑,例如可列舉:氧化鋅、氧化鈦及氧化鈰等。進而,關於上述包含金屬氧化物之紫外線遮斷劑,表面亦可經被覆。作為上述包含金屬氧化物之紫外線遮斷劑之表面之被覆材料,可列舉:絕緣性金屬氧化物、水解性有機矽化合物及聚矽氧化合物等。
作為上述具有苯并三唑結構之紫外線遮斷劑,例如可列舉:2-(2'-羥基-5'-甲基苯基)苯并三唑(BASF公司製造之「Tinuvin P」)、2-(2'-羥基-3',5'-二第三丁基苯基)苯并三唑(BASF公司製造之「Tinuvin 320」)、2-(2'-羥基-3'-第三丁基-5-甲基苯基)-5-氯苯并三唑(BASF公司製造之「Tinuvin 326」)、及2-(2'-羥基-3',5'-二戊基苯基)苯并三唑(BASF公司製造之「Tinuvin 328」)等。由於吸收紫外線之性能優異,上述紫外線遮斷劑較佳為包含鹵素原子之具有苯并三唑結構之紫外線遮斷劑,更佳為包含氯原子之具有苯并三唑結構之紫外線遮斷劑。
作為上述具有二苯甲酮結構之紫外線遮斷劑,例如可列舉辛苯酮(BASF公司製造之「Chimassorb 81」)等。
作為上述具有三結構之紫外線遮斷劑,例如可列舉ADEKA公司製
造之「LA-F70」及2-(4,6-二苯基-1,3,5-三-2-基)-5-[(己基)氧基]-苯酚(BASF公司製造之「Tinuvin 1577FF」)等。
作為上述具有丙二酸酯結構之紫外線遮斷劑,可列舉:2-(對甲氧基亞苄基)丙二酸二甲酯、2,2-(1,4-伸苯基二亞甲基)雙丙二酸四乙酯、2-(對甲氧基亞苄基)-雙(1,2,2,6,6-五甲基4-哌啶基)丙二酸酯等。
作為上述具有丙二酸酯結構之紫外線遮斷劑之市售品,可列舉:Hostavin B-CAP、Hostavin PR-25、Hostavin PR-31(均由Clariant公司製造)。
作為上述具有草醯替苯胺結構之紫外線遮斷劑,可列舉:N-(2-乙基苯基)-N'-(2-乙氧基-5-第三丁基苯基)草酸二醯胺、N-(2-乙基苯基)-N'-(2-乙氧基苯基)草酸二醯胺、2-乙基-2'-乙氧基-草醯替苯胺(Clariant公司製造之「Sanduvor VSU」)等氮原子上具有經取代之芳基等的草酸二醯胺類。
作為上述具有苯甲酸酯結構之紫外線遮斷劑,例如可列舉3,5-二第三丁基-4-羥基苯甲酸2,4-二第三丁基苯酯(BASF公司製造之「Tinuvin 120」)等。
於包含上述紫外線遮斷劑之層(第1層、第2層或第3層)100重量%中,上述紫外線遮斷劑之含量較佳為0.1重量%以上,更佳為0.2重量%以上,進而較佳為0.3重量%以上,尤佳為0.5重量%以上。於包含上述紫外線遮斷劑之層(第1層、第2層或第3層)100重量%中,上述紫外線遮斷劑之含量較佳為2.5重量%以下,更佳為2重量%以下,進而較佳為1重量%以下,尤佳為0.8重量%以下。若上述紫外線遮斷劑之含量為上述下限以上且上述上限以下,則可進一步抑制經過一段時間後之可見光光線透過率之降低。尤其藉由使包含上述紫外線遮斷劑之層100重量%中之上述紫外線遮斷劑
之含量為0.2重量%以上,可顯著抑制中間膜及層合玻璃於經過一段時間後之可見光光線透過率之降低。
上述中間膜亦可包含抗氧化劑。上述第1層可包含抗氧化劑。上述第2層可包含抗氧化劑。上述第3層可包含抗氧化劑。上述抗氧化劑可僅使用1種,亦可併用2種以上。
作為上述抗氧化劑,可列舉:酚系抗氧化劑、硫系抗氧化劑及磷系抗氧化劑等。上述酚系抗氧化劑為具有酚骨架之抗氧化劑。上述硫系抗氧化劑為含有硫原子之抗氧化劑。上述磷系抗氧化劑為含有磷原子之抗氧化劑。
上述抗氧化劑較佳為酚系抗氧化劑或磷系抗氧化劑。
作為上述酚系抗氧化劑,可列舉:2,6-二第三丁基對甲酚(BHT)、丁基羥基苯甲醚(BHA)、2,6-二第三丁基-4-乙基苯酚、β-(3,5-二第三丁基-4-羥基苯基)丙酸硬脂酯、2,2'-亞甲基雙(4-甲基-6-丁基苯酚)、2,2'-亞甲基雙(4-乙基-6-第三丁基苯酚)、4,4'-亞丁基雙(3-甲基-6-第三丁基苯酚)、1,1,3-三(2-甲基羥基-5-第三丁基苯基)丁烷、四[亞甲基-3-(3',5'-丁基-4-羥基苯基)丙酸酯]甲烷、1,3,3-三(2-甲基-4-羥基-5-第三丁基苯酚)丁烷、1,3,5-三甲基-2,4,6-三(3,5-二第三丁基-4-羥基苄基)苯、雙(3,3'-第三丁基苯酚)丁酸二醇酯及伸乙基雙(氧基伸乙基)雙(3-第三丁基-4-羥基-5-甲基苯丙酸酯)等。可適當使用該等抗氧化劑中之1種或2種以上。
作為上述磷系抗氧化劑,可列舉:亞磷酸十三烷基酯、亞磷酸三(十三烷基)酯、亞磷酸三苯酯、亞磷酸三壬基苯酯、雙(十三烷基)季戊四醇二亞磷酸酯、雙(癸基)季戊四醇二亞磷酸酯、亞磷酸三(2,4-二第三丁基苯
基)酯、亞磷酸雙(2,4-二第三丁基-6-甲基苯基)酯乙酯、及2,2'-亞甲基雙(4,6-二第三丁基-1-苯基氧基)(2-乙基己基氧基)磷等。可適當使用該等抗氧化劑中之1種或2種以上。
作為上述抗氧化劑之市售品,例如可列舉:BASF公司製造之「IRGANOX 245」、BASF公司製造之「IRGAFOS 168」、BASF公司製造之「IRGAFOS 38」、住友化學工業公司製造之「Sunilizer BHT」、以及BASF公司製造之「IRGANOX 1010」等。
為了使中間膜及層合玻璃長期維持較高之可見光光線透過率,於上述中間膜100重量%中或包含抗氧化劑之層(第1層、第2層或第3層)100重量%中,上述抗氧化劑之含量較佳為0.1重量%以上。又,由於抗氧化劑之添加效果會達到飽和,故而於上述中間膜100重量%中或包含上述抗氧化劑之層100重量%中,上述抗氧化劑之含量較佳為2重量%以下。
上述第1層、上述第2層及上述第3層分別視需要亦可含有:包含矽、鋁或鈦之偶合劑、分散劑、界面活性劑、阻燃劑、防靜電劑、顏料、染料、耐濕劑、交聯劑、螢光增白劑及紅外線吸收劑等添加劑。該等添加劑可僅使用1種,亦可併用2種以上。
上述中間膜之一端與另一端之距離較佳為0.5m以上,更佳為0.8m以上,尤佳為1m以上,又,較佳為3m以下,更佳為2m以下,尤佳為1.5m以下。於中間膜具有長度方向與寬度方向之情形時,一端與另一端之距離即為中間膜之長度方向之距離。於中間膜具有正方形之平面形狀之情形時,一端與另一端之距離即為相對向之一端與另一端之距離。
上述中間膜之厚度並無特別限定。就實用面之觀點、以及充分提高層合玻璃之耐貫通性及抗撓剛度之觀點而言,中間膜之厚度較佳為0.1mm以上,更佳為0.25mm以上,又,較佳為3mm以下,更佳為2mm以下,進而較佳為1.5mm以下。若中間膜之厚度為上述下限以上,則層合玻璃之耐貫通性及抗撓剛度變高。若中間膜之厚度為上述上限以下,則中間膜之透明性變得更良好。
將中間膜之厚度記為T。上述第1層之厚度較佳為0.0625T以上,更佳為0.1T以上,又,較佳為0.4T以下,更佳為0.375T以下,進而較佳為0.25T以下,進而較佳為0.15T以下。若上述第1層之厚度為0.4T以下,則抗撓剛度變得更良好。
上述第2層及上述第3層之各厚度較佳為0.3T以上,更佳為0.3125T以上,進而較佳為0.375T以上,又,較佳為0.9375T以下,更佳為0.9T以下。上述第2層及上述第3層之各厚度亦可為0.46875T以下,亦可為0.45T以下。又,若上述第2層及上述第3層之各厚度為上述下限以上且上述上限以下,則層合玻璃之剛性與隔音性進一步提高。
上述第2層與上述第3層之合計厚度較佳為0.625T以上,更佳為0.75T以上,進而較佳為0.85T以上,又,較佳為0.9375T以下,更佳為0.9T以下。又,若上述第2層與上述第3層之合計厚度為上述下限以上且上述上限以下,則層合玻璃之剛性與隔音性進一步提高。
上述中間膜可為厚度均勻之中間膜,亦可為厚度變化之中間膜。上述中間膜之剖面形狀可為矩形,亦可為楔形。
本發明之中間膜之製造方法並無特別限定。作為本發明之中間膜之製造方法,例如可列舉如下等方法:使用用以形成各層之各樹脂組合物而
分別形成各層後,積層所獲得之各層;以及使用擠出機將用以形成各層之各樹脂組合物共擠出,藉此積層各層。由於適於進行連續生產,較佳為擠出成形之製造方法。
就中間膜之製造效率優異之方面而言,較佳為上述第2層與上述第3層包含同一種聚乙烯醇縮醛樹脂。就中間膜之製造效率優異之方面而言,更佳為上述第2層與上述第3層包含同一種聚乙烯醇縮醛樹脂及同一種塑化劑。就中間膜之製造效率優異之方面而言,進而較佳為上述第2層與上述第3層係由同一種樹脂組合物所形成。
上述中間膜較佳為於兩側之表面中之至少一表面具有凹凸形狀。上述中間膜更佳為於兩側之表面具有凹凸形狀。作為形成上述凹凸形狀之方法,並無特別限定,例如可列舉:模唇壓印(rip emboss)法、壓紋輥法、砑光輥法、及異形擠出法等。由於可定量地形成具有固定凹凸花樣之複數個凹凸形狀之壓紋,較佳為壓紋輥法。
圖3係模式性地表示使用圖1所示之層合玻璃用中間膜之層合玻璃之一例的剖視圖。
圖3所示之層合玻璃31具備第1層合玻璃構件21、第2層合玻璃構件22、及中間膜11。中間膜11係配置於第1層合玻璃構件21與第2層合玻璃構件22之間而夾入其間。
於中間膜11之第1表面11a積層有第1層合玻璃構件21。於中間膜11之與第1表面11a相反之第2表面11b積層有第2層合玻璃構件22。於第1層1之外側之表面1a積層有第1層合玻璃構件21。於第3層3之外側之表面3a積層有第2層合玻璃構件22。
圖4係模式性地表示使用圖2所示之層合玻璃用中間膜之層合玻璃之一例的剖視圖。
圖4所示之層合玻璃31A具備第1層合玻璃構件21、第2層合玻璃構件22、及中間膜11A。中間膜11A係配置於第1層合玻璃構件21與第2層合玻璃構件22之間而夾入其間。
於中間膜11A之第1表面11a積層有第1層合玻璃構件21。於中間膜11A之與第1表面11a相反之第2表面11b積層有第2層合玻璃構件22。
如此,上述層合玻璃具備第1層合玻璃構件、第2層合玻璃構件、及中間膜,該中間膜為本發明之層合玻璃用中間膜。於上述層合玻璃中,於上述第1層合玻璃構件與上述第2層合玻璃構件之間配置有上述中間膜。
作為上述層合玻璃構件,可列舉:玻璃板及PET(聚對苯二甲酸乙二酯)膜等。層合玻璃包括於兩片玻璃板之間夾入有中間膜之層合玻璃、以及於玻璃板與PET膜等之間夾入有中間膜之層合玻璃。上述層合玻璃為具備玻璃板之積層體,較佳為使用至少一片玻璃板。較佳為上述第1層合玻璃構件及上述第2層合玻璃構件分別為玻璃板或PET膜,且上述層合玻璃具備玻璃板作為上述第1層合玻璃構件及上述第2層合玻璃構件中之至少一者。較佳為上述第1層合玻璃構件及上述第2層合玻璃構件兩者均為玻璃板(第1玻璃板及第2玻璃板)。上述中間膜適宜被配置於第1玻璃板與第2玻璃板之間以獲得層合玻璃。
作為上述玻璃板,可列舉:無機玻璃及有機玻璃。作為上述無機玻璃,可列舉:浮法平板玻璃、熱射線吸收板玻璃、熱射線反射板玻璃、磨光平板玻璃、壓花玻璃、及線板玻璃等。上述有機玻璃為代替無機玻璃之合成樹脂玻璃。作為上述有機玻璃,可列舉:聚碳酸酯板及聚(甲基)丙烯
酸系樹脂板等。作為上述聚(甲基)丙烯酸系樹脂板,可列舉聚(甲基)丙烯酸甲酯板等。
上述層合玻璃構件之厚度較佳為1mm以上,又,較佳為5mm以下,更佳為3mm以下。又,於上述層合玻璃構件為玻璃板之情形時,該玻璃板之厚度較佳為0.5mm以上,更佳為0.7mm以上,又,較佳為5mm以下,更佳為3mm以下。於上述層合玻璃構件為PET膜之情形時,該PET膜之厚度較佳為0.03mm以上,又,較佳為0.5mm以下。
上述層合玻璃之製造方法並無特別限定。首先,於上述第1層合玻璃構件與上述第2層合玻璃構件之間夾入中間膜而獲得積層體。其次,例如藉由使所獲得之積層體通過擠壓輥或藉由裝入橡膠袋內進行減壓抽氣,而去除上述第1層合玻璃構件與上述第2層合玻璃構件與中間膜之間殘留之空氣。其後,於約70~110℃下進行預接著而獲得實現預壓接之積層體。繼而,將已實現預壓接之積層體放入高壓釜中或對其加壓,而於約120~150℃及1~1.5MPa之壓力下進行壓接。如此可獲得層合玻璃。於製造上述層合玻璃時,可將第1層與第2層與第3層進行積層。
上述中間膜及上述層合玻璃可用於汽車、軌道車輛、飛機、船舶及建築物等。上述中間膜及上述層合玻璃亦可用於該等以外之用途。上述中間膜及上述層合玻璃較佳為車輛用或建築用之中間膜及層合玻璃,更佳為車輛用之中間膜及層合玻璃。上述中間膜及上述層合玻璃可用於汽車之擋風玻璃、側窗玻璃、後窗玻璃或天窗玻璃等。上述中間膜及上述層合玻璃適用於汽車。上述中間膜可用於獲得汽車之層合玻璃。
以下,揭示實施例而更詳細地說明本發明。本發明並不僅限定於該等實施例。
準備以下之材料。
聚乙烯醇縮醛樹脂:
使用下述表1所示之聚乙烯醇縮醛樹脂。所使用之全部聚乙烯醇縮醛樹脂於縮醛化時均使用碳數4之正丁醛。關於聚乙烯醇縮醛樹脂,縮醛化度(縮丁醛化度)、乙醯化度及羥基之含有率係藉由依據JIS K6728「聚乙烯醇縮丁醛試驗方法」之方法進行測定。再者,即便於藉由ASTM D1396-92進行測定之情形時,亦顯示出與依據JIS K6728「聚乙烯醇縮丁醛試驗方法」之方法相同之數值。
聚酯樹脂:
PEs1(UE3220,Unitika公司製造)
PEs2(UE3223,Unitika公司製造)
(甲基)丙烯酸系聚合物:
藉由以下之合成方法所獲得之(甲基)丙烯酸系聚合物Ac1、Ac2、Ac3、Ac4及Ac5
於兩片經單面脫模處理之PET片材(Nippa公司製造,厚度50μm)之間夾持具有下述表3所示之調配組成之聚合性組合物,而形成厚度100μm之聚合性組合物層。再者,於兩片PET片材之周圍配置間隔件。使用高壓水銀UV燈,以照射量3000mJ/cm2對聚合性組合物層照射紫外線,藉此使聚合性組合物進行反應而硬化,而獲得(甲基)丙烯酸系聚合物Ac1、Ac2、Ac3、Ac4及Ac5。
聚乙酸乙烯酯:
藉由以下之合成方法所獲得之聚乙酸乙烯酯PVAc1
準備具有回流冷卻器、滴液漏斗、溫度計及氮氣導入口之玻璃製聚合容器。向該聚合容器內添加乙酸乙烯酯單體100重量份、3-甲基-3-丁基-1-醇1.0重量份、及甲醇3.8重量份,進行加熱及攪拌並對聚合容器內進行氮氣置換。繼而,使上述聚合容器內之溫度成為60℃,歷時4小時滴加作為聚合起始劑之過氧化新癸酸第三丁酯0.02重量份、乙酸乙烯酯單體150重量份、及3-甲基-3-丁基-1-醇1.5重量份,滴加結束後進行2小時之聚合,而獲得包含聚乙酸乙烯酯之溶液。將該溶液於110℃之烘箱內乾燥3小時,藉此獲得聚乙酸乙烯酯PVAc1。
藉由以下之合成方法所獲得之聚乙酸乙烯酯PVAc2
準備具有回流冷卻器、滴液漏斗、溫度計及氮氣導入口之玻璃製聚合容器。向該聚合容器內添加乙酸乙烯酯單體250重量份與甲醇3.8重量份,進行加熱及攪拌並對聚合容器內進行氮氣置換。繼而,使上述聚合容器內之溫度成為60℃,歷時2.5小時滴加作為聚合起始劑之過氧化新癸酸第三丁酯0.06重量份,滴加結束後進行2小時之聚合,而獲得包含聚乙酸乙烯酯之溶液。將該溶液於110℃之烘箱內乾燥3小時,藉此獲得聚乙酸乙烯酯PVAc2。
三乙二醇二-2-乙基己酸酯(3GO)
苯甲酸系塑化劑(PB-3A,DIC公司製造)(P1)
己二酸二(2-丁氧基乙基)酯(DBEA)
己二酸雙(2-丁氧基乙基)酯(D931)
己二酸二丁酯(DBA)
(化合物(A))
化合物(A1)(KE-311,荒川化學工業公司製造,軟化點95℃)
化合物(A2)(Enpara 70,Ajinomoto Fine-Techno公司製造,軟化點100℃)
Tinuvin 326(2-(2'-羥基-3'-第三丁基-5-甲基苯基)-5-氯苯并三唑,BASF公司製造之「Tinuvin 326」)
BHT(2,6-二第三丁基對甲酚)
Mg混合物(2-乙基丁酸鎂與乙酸鎂之50:50(重量比)混合物)
用以形成第1層之組合物之製作:
將下述表1所示之種類之聚乙烯醇縮醛樹脂100重量份、塑化劑(3GO)75重量份、化合物(A1)(KE-311)100重量份、紫外線遮斷劑(Tinuvin 326)0.2重量份、及抗氧化劑(BHT)0.2重量份加以混合,而獲得用以形成第1層之組合物。
用以形成第2層及第3層之組合物之製作:
將下述表1所示之種類之聚乙烯醇縮醛樹脂100重量份、塑化劑(3GO)35重量份、紫外線遮斷劑(Tinuvin 326)0.2重量份、抗氧化劑(BHT)0.2重量份、及使所獲得之中間膜中之金屬元素濃度(Mg濃度)成為70ppm之量之Mg混合物加以混合,而獲得用以形成第2層及第3層之組合物。
中間膜之製作:
使用共擠出機,將用以形成第1層之組合物與用以形成第2層及第3層之組合物共擠出,藉此製作具有第2層(厚度340μm)/第1層(厚度100μm)/第3層(厚度340μm)之積層構造之中間膜(厚度780μm)。
層合玻璃A之製作(隔音性測定用):
將所獲得之中間膜之中央部切成縱6.5cm×橫6.5cm之大小。繼而,於依據JIS R3208之兩片綠玻璃(縱6.5cm×橫6.5cm×厚度2mm)之間夾入中間膜,而獲得積層體。將該積層體裝入橡膠袋內,於2.6kPa之真空度下脫氣20分鐘後,保持脫氣狀態移入烘箱內,進而於90℃下保持30分鐘,進行真空加壓,而使積層體實現預壓接。於高壓釜中,於135℃及壓力1.2MPa之條件下,對已實現預壓接之積層體進行20分鐘之壓接,而獲得層合玻璃A。
如下述表1、2所示般設定用以形成第1層之組合物與用以形成第2層及第3層之組合物中使用之熱塑性樹脂、塑化劑及化合物(A)之種類與調配量,除此以外,藉由與實施例1相同之方式獲得中間膜及層合玻璃。又,實施例2~13及比較例1~2中,以與實施例1相同之調配量(相對於聚乙烯醇縮醛樹脂100重量份為0.2重量份)調配與實施例1相同種類之紫外線遮斷劑及抗氧化劑,以與實施例1相同之調配量(使中間膜中之金屬元素濃度(Mg濃度)成為70ppm之量)調配與實施例1相同種類之Mg混合物。
再者,實施例7中,相對於熱塑性樹脂100重量份,分別使用化合物(A1)與化合物(A2)各60重量份。
第1層之製作:
準備上述獲得之(甲基)丙烯酸系聚合物Ac1(包含硬化物之層,厚度100μm)。
第2層及第3層之製作:
用以形成第2/第3層之組合物之製作:
將以下之調配成分進行混合,利用混合輥充分混練,而獲得用以形成第2/第3層之組合物。
聚乙烯醇縮醛樹脂(PVB)100重量份
塑化劑(3GO)40重量份
使所獲得之第2/第3層中之Mg成為70ppm之量之金屬鹽M(Mg混合物)
於所獲得之第2/第3層中成為0.2重量%之量之紫外線遮斷劑(Tinuvin 326)
於所獲得之第2/第3層中成為0.2重量%之量之抗氧化劑(BHT)
使用擠出機將所獲得之用以形成第2/第3層之組合物擠出,而獲得第2/第3層(厚度各為380μm)。
中間膜之製作:
於第1層之外側積層第2層及第3層。使用滾筒貼合機(ACCO Brands Japan公司製造之「GDRB316 A3」),將速度設定為3,於100℃下進行層壓,藉此獲得具有第2層/第1層/第3層之構造之中間膜。
層合玻璃之製作:
使用所獲得之中間膜,除此以外,藉由與實施例1相同之方式獲得層合玻璃。
如下述表4所示般設定調配成分之種類及調配量,除此以外,藉由與實施例14相同之方式獲得中間膜及層合玻璃。又,實施例15~17及比較例3中,以與實施例14相同之調配量(第2/第3層中之調配量)調配與實施例1相同種類之紫外線遮斷劑及抗氧化劑,以與實施例14相同之調配量(第2/第3層中之調配量)調配與實施例14相同種類之Mg混合物。
用以形成第1層之組合物之製作:
將以下之調配成分進行混合,利用混合輥充分混練,而獲得用以形成第1層之組合物。
聚乙酸乙烯酯PVAc1 100重量份
塑化劑(D931)70重量份
於所獲得之第1層中成為0.2重量%之量之紫外線遮斷劑(Tinuvin 326)
於所獲得之第1層中成為0.2重量%之量之抗氧化劑(BHT)
用以形成第2/第3層之組合物之製作:
將以下之調配成分進行混合,利用混合輥充分混練,而獲得用以形成第2/第3層之組合物。
聚乙烯醇縮醛樹脂(PVB)100重量份
塑化劑(D931)30重量份
使所獲得之第2/第3層中之Mg成為70ppm之量之金屬鹽M(Mg混合物)
於所獲得之第2/第3層中成為0.2重量%之量之紫外線遮斷劑(Tinuvin 326)
於所獲得之第2/第3層中成為0.2重量%之量之抗氧化劑(BHT)
中間膜之製作:
使用共擠出機將所獲得之用以形成第1層之組合物與所獲得之用以形成第2/第3層之組合物擠出,而獲得具有第2層(厚度370μm)/第1層(厚度100μm)/第3層(厚度370μm)之構造之中間膜。
如下述表4所示般設定調配成分之種類及調配量,除此以外,藉由與實施例18相同之方式獲得中間膜及層合玻璃。又,比較例4中,以與實施例18相同之調配量(第2/第3層中之調配量)調配與實施例18相同種類之紫外線遮斷劑及抗氧化劑,以與實施例18相同之調配量(第2/第3層中之調配量)調配與實施例18相同種類之Mg混合物。
藉由如下方式進行第1層之黏彈性測定。
準備用以形成第1層之組合物之混練物。利用加壓成型機,於150℃下對所獲得之混練物進行加壓成型,而獲得厚度0.35mm之樹脂膜。將所獲得之樹脂膜於25℃及相對濕度30%之條件下放置2小時。放置2小時後,使用TA Instruments公司製造之「ARES-G2」測定黏彈性。使用直徑8mm之平行板作為輔具。於以3℃/min之降溫速度使溫度自30℃降至-50℃之條件、及頻率1Hz及應變1%之條件下進行測定。將所獲得之測定結果中之損耗正切之峰值溫度設為玻璃轉移溫度Tg(℃)。
再者,亦可藉由如下方式製作樹脂膜。將所獲得之中間膜於室溫23±2℃、相對濕度25±5%之環境下保管1個月。繼而,於室溫23℃±2℃之環境下,自中間膜剝離第2層及第3層,藉此去除第2層及第3層而獲得第1
層。以厚度成為0.35mm之方式於150℃下對所獲得之第1層進行加壓成型(不加壓狀態下為150℃、10分鐘,加壓狀態下為150℃、10分鐘)而製作樹脂膜。
評價第1層(樹脂膜)之玻璃轉移溫度Tg(℃)、Tg-10℃下之第1層之第1儲存彈性模數G'(G'(Tg-10℃))、及Tg+10℃下之第1層之第2儲存彈性模數G'(G'(Tg+10℃)),求出上述第1層之Tg下之上述第1層之損耗正切tanδ(tanδ(Tg))。又,評價是否分別滿足式(1)及式(2),於滿足之情形時判定為「○」,於不滿足之情形時判定為「×」。
將厚度100μm之複數層之第1層重疊,而獲得厚度500μm之樹脂膜。將上述(1)之黏彈性測定中之樹脂膜變更為所獲得之樹脂膜,除此以外,進行與上述(1)之黏彈性測定相同之黏彈性測定。
使用設置於安靜房間內之音箱,對所獲得之層合玻璃之隔音性進行評價。音箱為使用厚度10mm之木製板材組合而成之縱10cm、橫10cm、高度10cm之木箱,於一面設有縱7cm、7cm之開口部。又,於音箱之內部安裝有具備揚聲器之音樂播放器。繼而,將所製作之用以測定隔音性之層合玻璃A配置於開口部,使用黏土填補層合玻璃A之周圍與開口部之間的間隙而將層合玻璃固定於開口部。預先以揚聲器每隔一段時間會發出頻率500Hz至8000Hz之蜂鳴聲(蜂鳴信號音)之方式於音樂播放器內錄入蜂鳴聲。
評價者位於設置在音箱開口部之層合玻璃A之正面,聽自音樂播放器發出之聲響,進行如下官能評價:通過層合玻璃A自音箱漏出之蜂鳴信號
音是否處於特定頻率而未變大,是否能夠自低頻側至高頻側均等地進行隔音。
評價者無論於何頻率下均可聽到均等之蜂鳴信號音之情形時判定為「○」,評價者於特定頻率下聽到大於其他頻率之蜂鳴信號音之情形時判定為「×」。
將詳細內容及結果示於下述表1~4。再者,下述表1~4中,省略記載熱塑性樹脂等樹脂、塑化劑及化合物(A)以外之調配成分。
合成(甲基)丙烯酸系聚合物Ac1、Ac2、Ac3、Ac4及Ac5時使用之表3所示之成分之詳細說明如下所示。
EA:丙烯酸乙酯(日本觸媒公司製造)
HEA:丙烯酸2-羥基乙酯(大阪有機化學工業公司製造)
BzA:丙烯酸苄酯(大阪有機化學工業公司製造,Viscoat#160)
BA:丙烯酸丁酯(日本觸媒公司製造)
AMP-20GY:苯氧基聚乙二醇丙烯酸酯(新中村化學工業公司製造)
3GO:三乙二醇二-2-乙基己酸酯
IRGACURE 184:2,2-二甲氧基-1,2-二苯基乙烷-1-酮(BASF公司製造)
Claims (8)
- 一種層合玻璃用中間膜,其係具有2層以上之構造者,並且上述中間膜具備於動態黏彈性測定中之玻璃轉移溫度為-30℃以上且10℃以下之第1層,上述中間膜具備第2層,於上述第1層之第1表面側配置有上述第2層,上述第1層包含聚乙烯醇縮醛樹脂以外之樹脂以及塑化劑,上述第1層包含軟化點為70℃以上且200℃以下之化合物,上述第2層包含樹脂以及塑化劑,相對於上述第1層中之上述樹脂100重量份之上述第1層中之上述塑化劑之含量,大於相對於上述第2層中之上述樹脂100重量份之上述第2層中之上述塑化劑之含量,於上述第1層之動態黏彈性測定中,將上述第1層之以℃為單位表示之玻璃轉移溫度記為Tg,將Tg-10℃下之上述第1層之儲存彈性模數G'記為第1儲存彈性模數G',將Tg+10℃下之上述第1層之儲存彈性模數G'記為第2儲存彈性模數G',此時Tg下之上述第1層之損耗正切tanδ滿足以下之式(1)及式(2)兩者,(Tg下之上述第1層之損耗正切tanδ)≧1.55…(1)(Tg下之上述第1層之損耗正切tanδ)=A×(第1儲存彈性模數G'/第2儲存彈性模數G')+B…(2)上述式(2)中,A為0.003以上且0.04以下,B為0.7以上且1.4以下。
- 如請求項1之層合玻璃用中間膜,其中上述第1層包含聚乙烯醇縮醛樹脂以外之熱塑性樹脂,或者包含使光硬化性化合物或濕氣硬化性化合物硬化而成之硬化物。
- 如請求項1或2之層合玻璃用中間膜,其係具有3層以上之構造者,上述中間膜具備第3層,於上述第1層之與上述第1表面相反側之第2表面側配置有上述第3層。
- 如請求項3之層合玻璃用中間膜,其中上述第1層包含聚乙烯醇縮醛樹脂以外之熱塑性樹脂,或者包含使具有(甲基)丙烯醯基之硬化性化合物硬化而成之硬化物,上述第2層包含熱塑性樹脂,上述第3層包含熱塑性樹脂。
- 如請求項4之層合玻璃用中間膜,其中上述第1層包含上述聚乙烯醇縮醛樹脂以外之熱塑性樹脂,上述第2層中之上述熱塑性樹脂為聚乙烯醇縮醛樹脂,上述第3層中之上述熱塑性樹脂為聚乙烯醇縮醛樹脂。
- 如請求項3之層合玻璃用中間膜,其中上述第3層包含塑化劑。
- 如請求項1或2之層合玻璃用中間膜,其中上述第1層包含樹脂,上述樹脂為聚酯樹脂、脂肪族聚烯烴、聚苯乙烯、乙烯-乙酸乙烯酯共聚物樹脂、乙烯-丙烯酸共聚物樹脂、聚胺基甲酸酯樹脂、離子聚合物樹脂、聚乙烯醇樹脂、聚乙酸乙烯酯或(甲基)丙烯酸系聚合物。
- 一種層合玻璃,其具備:第1層合玻璃構件、第2層合玻璃構件、及如請求項1至7中任一項之層合玻璃用中間膜,於上述第1層合玻璃構件與上述第2層合玻璃構件之間配置有上述層合玻璃用中間膜。