TW501919B - Textile fabric with particle attracting finish - Google Patents
Textile fabric with particle attracting finish Download PDFInfo
- Publication number
- TW501919B TW501919B TW88118333A TW88118333A TW501919B TW 501919 B TW501919 B TW 501919B TW 88118333 A TW88118333 A TW 88118333A TW 88118333 A TW88118333 A TW 88118333A TW 501919 B TW501919 B TW 501919B
- Authority
- TW
- Taiwan
- Prior art keywords
- particles
- scope
- polymer
- item
- patent application
- Prior art date
Description
501919 Α7 Β7 五、發明說明(1 ) 本發明係有關具顆粒吸引整理劑之纖維織物。此織 物被稱為抹布。抹布發現於清潔表面之使用性,其欲使顆 粒污染達最小。 抹布被用於數種不同之请潔應用,諸如,消毒過之 房間、汽車上漆室及其它控制環境。每一種不同之應用強 調此等種類之抹布需達成之某些特定標準。例如,用於消 毒過之房間之抹布需付合嚴格之性能標準。此等標準备有 關於吸收性及污染性,包含最大允許賴粒、非特定北之可 萃取物及個別之離子污染物。顆粒污染釋放之標準係特別 嚴厲且各種方法需被發明來符合此等標準。 抹布可自針織、機織或非織造之纖維織物製成。此 等織物被切成抹布,典型上係9英吋x 9英吋之矩形。抹布 可保持未被清洗且於清潔室之洗衣房内清洗,使用特殊之 界面活性劑及高度過濾及純化之水,以降低存在於織物上 之污染。清洗後,抹布可被乾燥包裝於密閉之塑膠袋内, 或於包裝前以適當溶劑預飽和,且準備使用之。 抹布領域之習知技藝之發展包含諸WPaley等人於US 5,271,995號案所揭示之使用諸如,,淡尼龍,,(nyl〇n bright)之 特疋紗降低賴粒污染,及如Reynold之US 5,〇69,735號案 揭示之藉由使用無空氣喷氣使織物切成物件且同時密封端 緣而降低散纖維之污染。改良由親水性纖維(諸如,聚醋) 製成之抹布之吸著性之整理劑亦已被使用。具有之織物基 質及由”含有礦酸芳族殘質之交聯聚合物之續酸化產物,,製 成之多孔聚合物塗覆物之抹布已被揭示kGB2 142 225α -----I----!1,% {請先閱讀背面之注意事項再填寫本頁) 訂---- 經濟#智慧財產局員工消費合作社印製
501919 ^ - A7 • _ B7_____ 五、發明說明(2 ) 〇 • 黏性布料係已被化學處理產生黏性之相對較鬆散織 造之織物纖維。其被用於於施用塗覆物前自表面移除灰塵 • 及用以於去家理之灰塵。Hansen之US 3,208,093號案揭示 具有塑化劑/乙婦基聚合組成物之黏性布料,其係將1 Q至1 6 份之聚合物施用於約11份之基材。Bennet之Us 3,658,578 一號案揭示以具有少於1 〇,〇 〇 〇之分子量之非晶態之聚丙蘇化 φ 合物浸潰之纖維基材,以達具黏性之成品。 發明之綜诫 本發明之目的係提供:具顆粒吸引整理劑之織品抹 布;適用於消毒清潔室及其它控制環境之織品抹布,其間 抹布本身需為低污染;可應用於廣範圍(乾燥及與溶劑結 合時)之顆粒吸引之抹布;及為耐用且展現很少或無之黏 性之成品。於一實施例中,抹布係於留下界面活性劑殘質 之條件下清洗,其被發現能改良吸著性。 ^ 因此’具有顆粒吸引性聚合物整理劑之纖維織物被 提供用作抹布。抹布可乾燥或以所欲溶劑飽和而使用。於 k 一實施例中,抹布係預先以清潔溶劑飽和且被包裝於可重 I 新密封之容器内。 | 本發明抹布之顆粒吸引潛質之特徵在於以下列測試 f 測量之”顆粒吸引係數”: ^ 9”x9”之抹布預先以水濕潤且被置於含有400亳升之水 | 及毫克(〇·〇1重量%)之具有3微米大小之平均顆粒之碳黑 乍 (以 Mkrotrac UPA-150分析器測量’且自 Cabot Corporation 本紙張尺度適用中國國家標準(CMS)A4規格(210 X 297公釐) ϋ n n n n n ϋ n n n n n I Μ··· β. #διν i, ***.*** e,* ® <請先閲讀背面之注意事項再填寫本頁) 5 經濟部智慧財產局員工消費合作社印製 501919 、 A7 ____ , _. B7 五、發明說明(3) (USA)獲得被定為碳黑M-1300)之燒杯.抹布於燒杯内使 用磁式攪拌棒擾拌30秒且移除之。抹布内過量的水被擠壓 掉’使水排回燒杯内。然後,燒瓶内的水經由1〇微米之 孔洞大小之玻璃纖維過濾器過濾。留於燒杯内之碳黑顆粒 之量被計算,且被抹布吸收之碳黑顆粒之量可被決定。此 測試對相同之纖物重複之,且無施用顆粒吸引整理劑。顆 ‘'粒吸引係數(%)由下述方程式計算之: 〜 麗粒(織物+整體劑)之重量-顆粒(僅右織物)之重量X100 顆粒(僅有織物)重量 例如,具有本發明整體劑之抹布吸收33毫克之碳‘黑 ,而無整體劑之抹布僅吸收13毫克。顆粒吸引係數係154% 〇 · 顆粒吸引之聚合物係選自具有⑴展現氫鍵,諸如, 羥基、羥烷基及羧基;(ii)具有酸-鹼反應性基,諸如,-COOH 、-nh2、-so3及νο3之侧基之化合物。於本發明之一實施 例中,顆粒吸引之聚合物係水溶性且係選自: (0具有數種選自羥基、羥烷基及羧基之侧基之多醣
f />L (ii)藉由乙烯基聚合反應形成之聚合物,其具有數種 選自羥基、羥烷基、羧基、胺基及烷胺基之侧基; 其中該物#具有對於碳黑係50%或更大之顆粒吸引係 數,及大於0.5微米之顆粒含量係每平方米為7500萬顆粒 ,其•係以 Biaxial Shake test IEST-RP-CP-CC004.2測量。 本發明之謀細描述 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) r - η n n ϋ n n n n n n n n n I · n n n l n n n 一· n n n ϋ n n n I (請先閲讀背面之注意事項再填寫本頁)
501919 五、發明說明(4 ) 無限制本發明之範g[,較佳實施例及特徵於其後描 述,除非’、匕之彳日示’下述條件被應用:所有份數及百 分率係條件係周圍條件,π,I氣壓之壓力 及25°C ;,,平均,,—辭係指數平均;脂族烴(包含烧基及伸 烷基)包含1至4個碳原子。除非其它指示,顆粒吸引係數 係使用具有約3微米之平均大小之顆粒測量。 說明書内所有述及之美國專利案在此被併入以屏參 本發明之抹布可自機織、針織或非織造之織品建構 成 '非織造織品及其製備方法係業界已知。例如,非織造 織品可被濕式膠乳黏合、乾式膠乳黏合、紡黏、針刺,·且 可使用或不使用黏合劑使其穩定化。 織品可自切段纖住或連績長絲纖維製成,或自此等 纖製成之紗製成。具有寬範圍之丹尼數及長絲數之紗可被 使用之。作為例示者,具有丹尼數對長絲比例為0.1至10 (15至250之丹尼數及10至250之長絲數)之紗可被使用之 。對於某些特疋之應用,其期望增加織品之磨蝕性,織品 可加入丹尼數為10至5〇之長絲。 纖維可選自合成及天然之纖維及其摻合物。例如, 纖維可為聚酯、聚醯胺、聚烯烴,例如,聚乙烯、聚丙烯 及乙烯/丙烯之共聚物,丙烯酸、聚氨基甲酸酯、纖維素 ,例如,棉花、尼龍及乙酸酯、絲或羊毛及其摻合物。較 佳者,纖維係聚酯、聚醢胺或聚烯烴。最佳者,抹布係自 連績之長絲聚酯紗(例如,變形聚酯紗)機織或針織。 本紙張尺度適用t國國家標準(CNS)A4規格(21〇 X 297公爱) --------^---------^ (請先閱讀背面之注意事項再填寫本頁) 7 經濟部智慧財產局員工消費合作社印製 501919 : A7 _:———..... . . .. . . B7 五、發明說明(5 ) 寬範圍之纖物重量可被用於本發明^典型上,用於 消毒清潔室使甩之抹布之織物具有每平均碼為丨至^盎司 ,較佳係每平均碼為2至9盎司。 於施用顆粒吸引聚合物前,織物可被清洗或洗擦以 移除紡絲油、污塵及其它污染物。通常有利者係熱固化織 物,其可於施用聚合物之前或之後為之,以提供尺寸穩定 性。於起始之纖維紡綠後,織物較佳係於高於紗先前邊遇 之溫度熱固化。例如,聚酯紗可於180至3〇〇卞之溫度熱固 化。較隹者,織物係於熱固化時平置。 熱固化有利者可於張:布機框爐内施行,其間織物於 加熱時及開始冷卻時被平置。爐之溫度係高於紗實際遭遇 之溫度,其係爐或乾燥器溫度分布。經由爐之織物之長度 及逮率之函數。 顆粒吸引聚合物整理劑或塗覆物可以任何適當之用 於施用塗覆物之方法且以溶液、分散體、乳化物或顆粒之 开> 式施用於識物基材上。用以例示者,聚合物可藉由浸軋 、,清洗、喷灑、壓軋、刀刃或於喷射染整裝置内施用之。 較佳者,聚合物係為水性溶液形式。 塗覆重量(固體)可為以織物重量為基準係〇·〇1重量% 或更大。典型上塗覆物重量係不大於6重量%。較佳者, 塗覆物重量係以織物重量為基準係〇·〇2至3重量%,最佳 係0·05至1重量%,顆粒吸引聚合物係以對於聚合物為適 當之方法及其被施用之形式(液體或固體)固化,且任何殘 留液體被蒸發、例如,若聚合物係以溶液、分散體或乳化 本紙張尺度通用中國國家標準(CiJs)A4規袼(21〇 X 297公釐 -8 1 . ----------- ^--------!線^1^ (請先閱讀背面之注意事項再填寫本頁) 501919 A7 B7 五、發明說明(ό ) 物之形式施用,被塗覆之織物係於張布機爐内乾燥及固化 0 ----------------裝--- (請先閱讀背面之注意事項再填寫本頁) 顆粒吸引之聚合物可選自對於下述型式之顆粒物質 展現吸力之聚合物··碳黑、鋁、氧化鋁、銅、氧化銅、鐵 酸鹽、石墨、鐵、氧化鐵、錳、氧化錳、矽、二氧化矽、 鈦、一氧化鈦、鶴、二氧化鷂、鋅及氧化鋅,較佳係對於 下述型式之顆粒物質之一或多者具有吸力:礙黑、銅了氧 Φ 化鋼、碎、二氧化矽、鎢及二氧化鎢。顆粒大小係於0.5 至20微米範圍。 —線· 特定抹布之自表面或液體吸引及移除顆粒污染物之 功效在此被稱為”顆粒吸引係數,%其測試先前已描述過。 簡言之,顆粒吸引係數係相對於未被塗覆之抹布之對於特 定顆粒形式之以聚合物塗覆之抹布之增加之顆粒吸引特性 之比值。較隹者’本發明之具塗覆物之抹布具有U微米 顆粒大小之顆粒吸引係數係50%或更,最佳係l〇〇Q/。或更 • 大。 顆粒吸引之聚合物之例子包含下述: 經濟部智慧財產馬員X.消費合作社印製 (i) 纖維素醚,例如,羥基烷基纖維素,諸如,羥 基乙基纖維素及羥基丙基纖維素;羥基烷基烷基纖 維素’諸如’羥基乙基乙基纖維素,經基丁基甲基 纖維素’羥基丙基甲基纖維素及羥基乙基甲基纖維 素;烧基纖維素,諸如,甲基纖維素及乙基纖維素 :羧基烷基纖維素,諸如,羧基甲基纖維素鈉; (ii) 無機纖維素酯,諸如,纖維素硝酸鹽; 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公f ) 501919 Α7 Β7 五、發明說明(7 (iii) 聚氨基葡糖;及 (iv) 瓜耳膠及羥基,羥基烷基及羧基取代之衍生物 ,例如,羧基甲基瓜耳膠,羧基甲基(羥基丙基)瓜 耳膠,羥基乙基瓜耳膠及羥基丙基瓜耳膠。 (v) 澱粉及其羥基,羥基烷基及羧基取代之衍生物 ,例如,羥基乙基澱粉及羥基丙基澱粉; (vi) 聚(乙烯基醇)及乙烯基醇之共聚物,例如T乙 烯/乙烯基醇之共聚物及乙烯基醇/甲基丙烯酸酯或 甲基甲基丙嫦酸酯之共聚物; (vii) 聚(乙烯基。比咯啶酮); (viii) 聚(羥基烷基丙烯酸酯)及聚(羥基獍基甲基丙烯 酸酯),例如,聚(羥基丙基甲基丙烯酸酯),聚(經基 丙基丙婦S楚酯);及 (ix) 聚(烷基丙烯基醢胺)及聚(烷基丙烯基醯胺)共 聚物,例如,聚(異丙基丙烯醯胺)及異丙基丙烯醯 胺/丙烯酸之共聚物。 經濟部智慧財產局員工消費合作社印製 (請先閱讀背面之注意事項再填寫本頁) 適當顆粒吸引之聚合物種類包含具有寬範圍分子量 及於水中可溶解之化合物。作為例示者,具有平均分子量 為 1,000 至 2,000,000 (較佳係 25,000 至 1,〇〇〇,〇〇〇,最佳係 50,000至500,000)之聚舍物可被使用。較佳者,於聚合 物被施用於織物及固化前,聚合物係水溶性,其係以每1〇〇 份之水之1份之可溶解度或更大。然而,亦期望者係一旦 將聚合物施用於織物並爵化時,聚合物具有足夠的耐用性 以抵抗於諸如消毒清潔室之洗衣房内之清洗。顆粒吸引之
501919 。 * Α7 ' Β7 五、發明說明(8 ) 聚合物亦可以黏著劑施用於織物,較佳係小量,諸如結合 聚氨基葡糖之蜜胺甲醛樹脂黏著劑。 於大部份情況中相信聚合物於纖維織物之纖維上形 成膜。但是,本發明之目的可禮達成,無論聚合物形成連 續膜或非連續。 除顆粒吸引之聚合物,其它整理劑可被施用於纖維 —織物上。例如,纖維織物可以”去污”整理劑改良其可濕潤 φ 性及可清洗性,如於下述美國專利中發現者:Marco之US 4,131,550 ; Hauser之US 4,164,392 ; Marco之US 4,168,954 ;Marco之US 4,170,557 ; Marco之US 4,235,735 ; Kimbrell 之 US 4,329,389 ;及 Schuette 之 US 5,725,951。其它之可被 施用於纖維織物或與顆粒吸引之聚合物結合使用之化合物 及組成物之例子包含:塑化劑、抗靜電劑、去發泡劑、抗 微生物或抗黴菌之試劑、潤滑劑、針織油及磨蝕劑。 於被塗覆之織物固化後,織物被切成一般大小以作 φ 為消毒清潔室用之抹布,其典型上係4英吋X 4英吋至24英 吋x24英吋之矩形。但,任何幾何形狀可被使用之。織物 較佳(雖然不是必需)使用熔合紗之端緣之技術切割,藉此 ,避免解開及顆粒之產生。適當技術之例子可發現於 Reynolds之US 5,069,735,及其間所述之參考案。 抹布典型上被包裝於密封容器内以使其免於受污染 〇 對於消毐清潔室之應用,期望於包裝置於清潔室之 洗衣房内清洗織物或抹布,其可被定為用以使抹布之污染 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 11 I----111 — — — — * •丨 I I — I i I 訂· — 丨 — — — — — (請先閱讀背面之注意事項再填寫本頁) 501919 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明(9 ) 被移除及達最小之洗衣房設備。清毒清潔室之洗衣房可使 用特定之過濾、器、界面活性劑、多價螯合劑、純水等以多 除油,降低顆粒含量及萃取非所欲之離子污染物。清洗過 程不應過度’因為顆粒吸引整理劑可能被移除。依使用之 裝置而定’其可能需要調整沖洗之攪拌、體積及時間及萃 取之速率及期間。清潔室清洗房之適當裝置及描述之例子 一可發現於 Austin, Dr· Philip R·之 ”Encyci〇pedia- 〇f
Cleanrooms,Bio-Cleanrooms and Aseptic Areas”,污染控 制會讓,密西根(1995> 〇 於一實施例中,界面活性劑殘質自清洗過程留於抹 布上,且已被發現改良吸著性'界面活性劑或表面活性試 . . · . ... 劑可選自陽離子、陰離子、非離手及雙性之界面活性劑。 在此之發現使用性之界面活性劑之綜合性描述可發現於
Kirk-〇thmer Encyclopedia of Chemical technology,第 4版, 第478-541頁(1997)。較佳者,界面活性劑係選自陰離子 及陽離子之界面活性劑。 範圍為0.00001重量% (〇.1131)111)至〇·5重量% (較佳係 0.00005重量%(0.5ppm)至0.1重量%)之界面活性劑殘質被 發現重大地改良抹布之吸著性,特別是有關於極性溶劑, 諸如,醇及水'抹布上之高含量之殘質可作為污染之來源 且需被避免。 對於許多應用,諸如用於汽車上漆房之抹布,其無 需於使用前於消毒清潔室之清洗房内清洗抹布^因此,抹 布可被包裝於密封容器内,而無需於塗覆前被清洗之。 本紙張尺度適用中國國豕標準(CNS)A4規格(21〇 X 297公爱) 12 • n n n ϋ n n n n an n n a— · n n n n n· an n 一· n· n n .n It ϋ n I . (請先閱讀背面之注意事項再填寫本頁) 501919 Α7 Β7 經齊邨智慧时¾¾員工消費合泎法印製 五、發明說明(10 ) 抹布可以所欲溶劑預先飽和且於密封分散劑内出隹 ’如業界已知般。飽和及預先飽和等辭係以其寬義使用之 ,即,以溶劑濕化。適當之溶劑包含水、諸如石油精之有 機溶劑,及水可相容混之有機溶劑之水性溶液,特別是諸 WCrC8之醇之醇溶液。特別有興趣者係以異丙醇及水之 ✓谷液(诸如’含有i至99重量%之異丙醇之水溶液)預先飽 和之抹布。溶劑組成物亦可含有依其清潔性質而選用乏界 面活性劑及/或其它添加劑。用以例示者,用於預先飽和 之抹布之另外之溶劑及包裝可被發現於下述參引案:us
3,994,751; US 4,627,936; US 4,639,327; US 4,998,984; US 5,145,091; US 5,344,007及JP 6[1994]-48475。另外,抹布 可於乾燥時密封於氣密包裝内。 用於消毒清潔室之抹布之標準 用於消毒清潔室之抹布之標準包含有關於吸著性及 污染之性能標準。用以評估消毒清潔室之抹布之一標準係 環境科學及技術協會(IEST)之污染控制部門推薦之施行細 則004.2,其可被稱為IEST-RP_CC004.2,”評估用於消毒 清潔室及其它控制環境之抹拭材料”。 推薦之施行細則004·2第7節宣佈一些用於決定消毒清 潔室之抹布之吸收能力及速率。能力測試係藉由以選用之 液體飽和抹布之已知區域,然後計算抹布每單位質量及每 單位面積吸收之體積而施行之(正81^^-(^卩?4.2§7.1)。 每單位質量之吸著量被稱為”本質吸著量,,且係以克計之每 單位抹布質量吸收之以毫升計之液體體積。”非本質吸收 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公愛) — IIIIIIIII1I — · I I I I I 1 I ·ΙΙΙ!ΙΙΙ« (請先閱讀背面之注咅?事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 501919 A7 「- ____ B7 五、發明說明(11 ) 量”係以平方米計之每單位抹布面積吸收之以毫升計之液 體體積。 消毒请潔室抹布之吸收速率係以一滴水自固定高度 落至抹布表面上而測量。自液滴鏡面消失所需碑間被測量 且記錄作為吸收速率(IEST-RP_CC004.2§7.2)。 與消毒清潔室用之抹布相關之主要測試係測量顆粒 、非特定之可举取物質及個別之離子組份。濕化期間釋出 之顆粒數目及機械應力可於Biaxial Shake Test (IEST-RP-CC004.2§5.2)測試之。簡言之,抹布被置於水瓶内並搖動 之。整份物自搖動器移除且顆粒數被計算之,典型上係特 別指〇·Ί微米或更大之範圍之顆粒大小者。大於該顆粒大 小之顆粒數目被以每平方米織物之以百萬計報告之。 與消毒/月潔至用之抹布有關之可萃取污染物之量夢 由以溶劑(諸如,水、異丙基醇或丙酮)莘取抹布,蒸發溶 劑並稱重不可探發之殘質決定之(IEST_Rp_cc〇()4 2§6 ^ 〇被萃取物質之量可以抹布之每分質量之萃取出之質量或 抹布之每單位面積之萃取出之質量報告之。 當欲知道特定物種存在量時,有機及無機之非揮發 殘質可被進-步分析。典型上,非揮發性殘質被測試各種 不同之無機、陰離子或陽離子之組份,例如,A〗,Ca,ci f
Li,Mg,K,ISTa及Zn (IEST-RP-CC004.2§6.2)。 本發明可參考下列範例而進一步瞭解之。 範倒1:以羥基丙基鑪.维幸肀覆之技布 測量為9”x9”且重約4盎司/碼2之抹布自連續長絲聚酯 (請先閱讀背面之注音?事項再填寫本頁) •隹 訂-!丨ί丨
501919 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明(12) 紗(70丹尼/23長絲及70丹尼/100長絲之紗,3:1比例)針織 之。抹布於0.1%之羥基丙基纖維素水溶液(平均分子量 〜370,〇〇〇)浸潤,過量者係手擠壓掉,以達〇 2重量%聚合 物添加量。抹布於350T之加壓空氣爐乾燥6分鐘。被塗覆 之抹布使用上述之顆粒吸引測試測試對各種顆粒之吸引力 ,其係相對於未被塗覆之抹布而言。結果係如下表所禦: 顆粒 顆粒大小 (um) 未塗覆吸液量 — (mg) 被塗覆之吸液量 (mg) 碳黑 3 13 33 氧化鋁 0.3 8 19 氧化鏟 0.4 10 17 二氧化鈦 1.3 4 14 氧化鋅 2.2 2.7 8 8 25 18 石墨 3.4 1.1 23 9 32 26 鐵 3.1 6 18 氧化鐵 1.2 17 22 鋅 1·3 8 13 鐵酸鹽 1.8 12 28 二氧化矽 叛倒2 :於具有經基丙基纖維素之清洗器内塗霜之枝布 300個抹布(9”x9”)(自範例1所述織物製備)於ο 6〇/〇 之羥基丙基纖維素(平均分子量〜11〇,〇〇〇)之水溶液,過量 者以手擠壓出,以達1·2重量%聚合物之添加量。抹布於 傳統之洗衣房乾燥器内乾燥40分鐘。一些抹布被測試對碳 黑顆粒之吸力且發現24毫克之平均吸收量。其它抹布於試 測規格(351b清洗器)之消毒清潔室之洗衣房内使用標準程 序清洗’使用Biaxial Shake Test測試顆粒之釋放,且發現 I-------— ^--------— ^-------Ί <請先閱讀背面之注音?事項再填寫本頁) 15 501919 A7 B7 五、發明說明(13 ) 具有1300萬顆粒/大於〇·5微米之平方米。 範_矩··以塗霜之技布 (請先閱讀背面之注意事項再填寫本頁) 10個抹布(9,,x9,,)(自範例1所述之織物製成)被置於 0.1%羥基丙基纖維素(分子量〜400,000)之水溶液 Mathis CH-8155實驗室噴射器,且於7〇。〔内喷射2〇分鐘, 以達0·2重量%聚合物之添加量。抹布於35〇卞加壓空氣爐 ^ ‘内乾燥6分鐘,然後測試對碳黑之顆粒吸力,30亳克之吸 收量。 範例4-13:以其它聚合物手涂覆之枝布 抹布(自範例1所述之織物製成)於聚合物(如表中所 示之固體)之水溶液浸潤,過量物以手擠壓掉,以達約〇.2 重量%聚合物之添加量。抹布於3.50卞加壓空氣爐内乾燥6 分鐘,被塗覆之抹布以上述顆粒吸引測試測試對碳黑之顆 粒吸力且與未被塗覆之抹布比較。結果如下述所示。 聚合物 碳黑吸收量 (mg) 無(比較例) 10 羧基甲基纖維素鈉(0.1%) 26 聚(羧酸)(0·1°/。) 27 經基丙基纖維素(〇·1%) 21 聚(乙烯基吡咯啶酮)(〇·〇5%> 26 27 聚氨基葡糠(〇·5%)+蜜胺甲醛樹脂(0·005%) 28 聚(丙烯酸)(0.1%) 28 羥基丙基甲基纖維素(〇·1%) 29 甲基纖維素(0·1%) 36 異丙基胺/甲基丙烯酸之共聚物(0·1%) 範例14-15
經濟部智慧財產局員工消費合作社印.M 下列範例證明當界面活性劑殘質留於抹布上之吸著 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) -16 - —- " ...........j 發明說明(14 ) 性之改良。 範例1所述之織物被以2.4%之聚(乙烯基醇)水溶液浸 軋塗覆,於真空槽内抽真空且於張布機框内於2501?乾燥 以達2·1重量%聚合物之添加量。織物以雷射切割成9,,χ9,, 之抹布且於傳統消毒清潔室之清洗器内清洗並乾燥之。 抹布之吸收速率依據IEST-RP-CC004.2§7.2測量(抹 布表面上之水滴之鏡面反應消失所需之時間),且發現_為7 秒0 抹布被置回消毒清潔室之清洗器内且經簡略之清洗 循環,其間商業用清潔劑(包含壬基酚乙氧化物)於倒數第 二個沖洗循環時添加 '抹布於消毒清潔室之乾燥器内乾燥 以達除先則施用之聚合物塗覆夕卜·之約1 ΡΡ^界面活性劑之 添加量。吸收速率如上測試且發現為〇·2秒。 前述範例證實具有顆粒吸引整理劑之抹布於吸收及 保留顆粒之功效,特別是〇·5至2〇微米範圍之目標物。抹 布於濕及乾之環境吸引顆粒,特別是於水性環境,諸如, 使用以溶劑飽和之抹布時所可能遭遇者。抹布並不黏,且 於抹布被用於清潔表面(濕或乾)時,聚合物塗覆物留下殘 質0 此外,藉由依循本發明之教示,其可能製備不仓 有清潔特性且符合聯邦標準2〇9Ε所定義之第i,1〇, ,i,000’及100,000類之要求。特別是,抹布符合下歹 的之-或多者:降低大於〇·5微米難之_污染至$ 75〇〇萬/米2之量,特別是少於麵以米2之量(以跑】 以19 A7 B7 五、發明說明(15 )
Shake Test (IEST-RP-CC004.2§5.2)測試);降低大於5微米 顆粒之顆粒污染至少於100萬/米2之量,特別是少於 300,000/米2,最佳係少於150,000/米2量(以出狀化丨Sha]^ Test (IEST-RP-CC004.2§5.2)測試);以水萃取降低非揮發 性殘質至少於_005克/米2之量,且甚至係少於QQ3克米2之 量(以短期萃取(IEST-RP-CC004.2§6· 1 ·2)測試);及達成3 5 毫升/米2或更大之吸收能力,甚至係4·〇亳升/米2或更大 (IEST-RP-CC004,2§7.1)。 本發明抹布之進一步優點係顆粒吸引之聚合物被認 為係降低顆粒自抹布釋出,諸如,低分子量聚酯,其移轉 至聚酯纖維表面。不欲被特定理論所限,相信顆粒吸引之 聚合物可作為補捉顆粒污染物使其免於自抹布釋出之障壁 (請先閱讀背面之注音?事項再填寫本頁) · 經濟部智慧財產局員工消費合作社印製 消毒清潔室用之抹布發現其於其間低污染高吸著性 之抹布為所欲者之各種環·境之使用性,諸如,半導體、光 學、食品包裝及藥學之消毒清潔室,及製備用於上漆或其 它塗覆之表面。 當然’有許多本發明之另外實施例及改良,其係被 包含於下列申請專利範圍之範圍内。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐 線 18
Claims (1)
- 六 、申請專利範圍 A8 B8 C8 D8 經濟部智慧財產局員工消費合作社印製 .一種包含纖維織物及塗覆於該_上之顆粒吸引聚合 物❹件,該物件具有對於一或多種之選自碳黑、銅 、2銅、石夕、氧切、鎮及氧化鶴之顆粒之顆粒吸 係數係50%或更大,及具有以雙轴搖動測試IEST_ 二CCG04.2測試之大於〇 5微米顆粒之顆粒含量係 每平方米係7500萬個顆粒或更少。 :如申請專利範圍第1項之物件,具有相對於織物t量為 〇·〇1至6重量%之聚合物。 3·如申請專利範圍第训之物件,其中該織物係機織或針 織之聚醋纖維,且具有每平方瑪為2至9盘司之重量。 如申明專利範圍第丨項之物件,其對於碳黑具有 100% 或更大之顆粒吸引係數。 5·如申請專利範圍第丨項之物件,其中該聚合物具有 25,000至1,000,000之平均分子量且該聚合物具有數個 選自Μ基、羥烷基及羧基之侧基丨 6·如申讀專利範圍第^項之物件彳其中該物件係以溶劑飽 和且包裝於密封容器内。 7.如申請專利範圍第1項之物件,其具有以雙軸搖動測試 ΐε8Τ_ΐα^€Ρ-€(:004·2測試之大於0.5微米顆粒之顆粒含 量係每平方米係3〇〇〇萬個顆粒或更少,及以IEST-Rp_ CC004.2測量之非本質吸收量為3·5亳升/米2或更大。 8· —種包含纖維織物及塗覆於該織物上之顆粒吸引之水 溶性聚合物之物件,其中該聚合物係選自: (1)具有數種選自羥基、羥烷基及羧基之侧基之多醣; 2 (請先閲讀背面之注意事項再填 1^:頁) IJ,— · •裝· 4. 本紙浪尺度逋用中國國家標隼(CNS) M規格(21〇χ297公釐) 訂 線· 19 501919 A8 B8 C8 D8 申請專利範圍 經濟部智慧財產局員工消費合作社印製 及 (U)藉由乙烯基聚合反應形成之聚合物,其具有數種選 自經基、羥烧基、羧基、胺基及烧胺基之侧基; 其中該物件具有對於碳黑係5〇%或更大之顆粒吸引係 數’及大於0·5微米之顆粒含量係每平方米為75〇〇萬顆粒’其係以雙軸搖動測試(Biaxial Shake Test) IEST_ RP-CP-CC004.2測量。 一 9·如申請專利範圍第8項之物件,其中該聚合物具有 25,000至1,〇〇〇,〇〇〇之平均分子量。 10·如申請專利範圍第9項之物件,具有相對於織物重量為 〇·〇2至3重量%之聚合物。 11 ·如申請專利範圍第9項之物件,其中該聚合物係選自纖 維素醚、聚(乙烯基醇)及乙烯基醇之共聚物。 12·如申請專利範圍第11項之物件,其中該物件係以溶劑 飽和且被包裝於密封容器内。 13.如申請專利範圍第12項之物件,其對於碳黑具有1〇〇% 或更大之顆粒吸引係數,及其具有以雙軸搖動測試 IEST-RP-CP-CC004.2測試之大於〇·5微米顆粒之顆粒含 量係每平方米係3000萬個顆粒或更少。 14* 一種包含纖維織物及塗覆於該織物上之顆粒吸引聚合 物之抹布,其中該聚合物係選自: ⑴纖維素醚;(ii)無機纖維素酯;(iii)聚氨基葡糖 ;(iv)瓜耳膠及羥基,羥基烷基及羧基取代之衍生物 ;(v)澱粉及其羥基,羥基烷基及羧基取代之衍生物; (請先聞讀背面之注意事項再填寫本頁j m fl—ϋ ml · 裝 、訂- 線501919 A8 B8 C8 D8 六、申請專利範圍 (vi)聚(乙烯基醇)及乙烯基醇之共聚物;(vii)聚(乙烯基 咄咯啶酮);(viii)聚(羥基垸基丙烯酸酯)及聚(羥基烷 基甲基丙烯酸酯);及(ix) 聚(烧基丙烯基醮胺)及聚(烷基丙烯基醯胺)共聚物 f 其中該物件具有大於0·5微米之顆粒含量係每平方 米為7500萬顆粒,其係以雙軸搖動測試(Biaxial ghake Test)IEST-RP-CP-CC004.2測量。。 15·如申請專利範圍第14項之抹布 為〇·〇5至1重量%之聚合物。 16·如申請專利範圍第14項之抹布 或更大之顆粒吸引係數。 17·如申請專利範圍第16項之抹布,其中該織物係機織或 針織之聚酯纖維’且真有每平方碼為2至9盎司之重量 具有相對於織物重量 其對於碳黑具有100% (請先閱讀背面之注意事項再填 頁) •裝· 訂 經濟部智慧財產局員工消費合作社印製 18·如申請專利範圍第14項之抹布,其中該聚合物係選自 t纖維素醚、聚(乙烯基醇)及乙烯基醇之共聚物。 19·如申請專利範圍第18項之抹布,其具有相對於織物重 篁為0·02至3重量%之聚合物,及對於碳黑具有或 更大之顆粒吸?|係數。 20·如申請專利範圍第19項之抹布,其具有以雙軸搖動測 試IEST_RP_pP-CC004.2測試之大於〇·5微米顆粒之顆粒 含量條每平方米係3000萬個顆粒或更少,及以msT_ RP-CC004,2測量之非本質吸收量為3·5毫升/米2或更大501919 A8 B8 C8 D8 六、申請專利範圍 (vi)聚(乙烯基醇)及乙烯基醇之共聚物;(vii)聚(乙烯基 咄咯啶酮);(viii)聚(羥基垸基丙烯酸酯)及聚(羥基烷 基甲基丙烯酸酯);及(ix) 聚(烧基丙烯基醮胺)及聚(烷基丙烯基醯胺)共聚物 f 其中該物件具有大於0·5微米之顆粒含量係每平方 米為7500萬顆粒,其係以雙軸搖動測試(Biaxial ghake Test)IEST-RP-CP-CC004.2測量。。 15·如申請專利範圍第14項之抹布 為〇·〇5至1重量%之聚合物。 16·如申請專利範圍第14項之抹布 或更大之顆粒吸引係數。 17·如申請專利範圍第16項之抹布,其中該織物係機織或 針織之聚酯纖維’且真有每平方碼為2至9盎司之重量 具有相對於織物重量 其對於碳黑具有100% (請先閱讀背面之注意事項再填 頁) •裝· 訂 經濟部智慧財產局員工消費合作社印製 18·如申請專利範圍第14項之抹布,其中該聚合物係選自 t纖維素醚、聚(乙烯基醇)及乙烯基醇之共聚物。 19·如申請專利範圍第18項之抹布,其具有相對於織物重 篁為0·02至3重量%之聚合物,及對於碳黑具有或 更大之顆粒吸?|係數。 20·如申請專利範圍第19項之抹布,其具有以雙軸搖動測 試IEST_RP_pP-CC004.2測試之大於〇·5微米顆粒之顆粒 含量條每平方米係3000萬個顆粒或更少,及以msT_ RP-CC004,2測量之非本質吸收量為3·5毫升/米2或更大1 經濟部智慧財產局員工消費合作社印製 AS B8 C8 一1 D8 六、fnrnm 一 ~ ^ Q 21.如申請專利範圍第14項之抹布,其中該物件進一步包 含O.lppm至0.5重量%範圍之界面活性劑殘質。 22·如申請專利範圍第丨項之物件,其中該物件進一步包含 〇.5Ppm至0·1重量%範圍之選自陰離子及非離子性之界 面活性劑之界面活性劑殘質。 ’…23·如申請專利範圍第8項之物件,其中該物件進一歩^包含 > O.lppm至0·5重量%範圍之界面活性劑殘質。 24·—種包含纖維織物及塗覆於該織物上之顆粒吸引聚合 物之物件,該物件具有對於一或多種之選自碳黑、銅 、氧化銅、矽、氧化矽、鎢及氧化鎢之顆粒之顆粒吸 引係數係50%或更大,及具有以雙軸搖動測試mST_ RP-CP-CC004.2測試之大於〇·5微米顆粒之顆粒含量係 每平方米係100萬個顆粒或更少,且該物件被包裝於密 封容器内且於顆粒吸引之聚合物於該織物上塗覆之後 | 未被清洗。 25·如申請專利範圍第24項之物件,其對於礙黑具有」〇()〇/〇 或更大之顆粒吸引係數。 26·如申請專利範圍第24項之物件,其中該聚合物具有 25,000至1,〇〇〇,〇〇〇之平均分子量,且該聚合物具有數 個選自羥基、羥烷基及羧基之侧基。 27·如申請專利範圍第24項之物件,其中該物件具有以雙 軸搖動測試IEST-RP-CP-CC004.2測試之大於5微米顆 粒之顆粒含量係每平方米係300,000個顆粒或更少。 本紙張又度遑用中國國家標準(CNS ) A4規格(210X297公釐) ..·,-----裝 ^ ^ ^ 訂 線 (請先閱讀背面之注意事項再填寫本頁) 1 經濟部智慧財產局員工消費合作社印製 AS B8 C8 一1 D8 六、fnrnm 一 ~ ^ Q 21.如申請專利範圍第14項之抹布,其中該物件進一步包 含O.lppm至0.5重量%範圍之界面活性劑殘質。 22·如申請專利範圍第丨項之物件,其中該物件進一步包含 〇.5Ppm至0·1重量%範圍之選自陰離子及非離子性之界 面活性劑之界面活性劑殘質。 ’…23·如申請專利範圍第8項之物件,其中該物件進一歩^包含 > O.lppm至0·5重量%範圍之界面活性劑殘質。 24·—種包含纖維織物及塗覆於該織物上之顆粒吸引聚合 物之物件,該物件具有對於一或多種之選自碳黑、銅 、氧化銅、矽、氧化矽、鎢及氧化鎢之顆粒之顆粒吸 引係數係50%或更大,及具有以雙軸搖動測試mST_ RP-CP-CC004.2測試之大於〇·5微米顆粒之顆粒含量係 每平方米係100萬個顆粒或更少,且該物件被包裝於密 封容器内且於顆粒吸引之聚合物於該織物上塗覆之後 | 未被清洗。 25·如申請專利範圍第24項之物件,其對於礙黑具有」〇()〇/〇 或更大之顆粒吸引係數。 26·如申請專利範圍第24項之物件,其中該聚合物具有 25,000至1,〇〇〇,〇〇〇之平均分子量,且該聚合物具有數 個選自羥基、羥烷基及羧基之侧基。 27·如申請專利範圍第24項之物件,其中該物件具有以雙 軸搖動測試IEST-RP-CP-CC004.2測試之大於5微米顆 粒之顆粒含量係每平方米係300,000個顆粒或更少。 本紙張又度遑用中國國家標準(CNS ) A4規格(210X297公釐) ..·,-----裝 ^ ^ ^ 訂 線 (請先閱讀背面之注意事項再填寫本頁) 501919 -Α8 Β8 C8 D8 經濟部智慧財產局員工消費合作社印製 六、申請專利範圍 28·如宇明專利範圍第27項之物件,其中該顆粒吸引之聚 合物係水溶性且選自: (1)具有數種選自羥基、羥烷基及羧基之側基之多醣; 及 (ii)糟由乙烯基聚合反應形成之聚合物,其具有數種選 自羥基、羥烷基、羧基、胺基及烷胺基之側基。 29·如申請專利範圍第24項之物件,其中該物件具有-以雙 軸搖動測試IEST_RP-CP-CC004.2測試之九於5微米顆 粒之顆粒含量係每平方米係15〇,〇〇〇個顆粒或更少。 30.如申請專利範圍第29項之物件,其中該顆粒吸引之聚 合物係選自: ⑴纖維素醚;(ii)無機纖維素酯;(iii)聚氨基葡糖;(iv) 瓜耳膠及經基,羥基烧基及羧基取代之衍生物;(v) 澱粉及其羥基,羥基烷基及羧基取代之衍生物;(vi) 聚(乙烯基醇)及乙烯基醇之共聚物;(vii)聚(乙烯基 吡咯啶酮);(viii)聚(羥基烷基丙烯酸酯)及聚(羥基 烷基甲基丙烯酸酯);及(ix)聚(烷基丙烯基醯胺)及 聚(烧基丙婦基釀胺)共聚物。 31·如申請專利範圍第24項之物件,其中該物件係以溶劑 飽和且包裝於密封容器内。 (請先閲讀背面之注意事項再填t 裝! 訂- 線 本紙張尺度逋用中國國家標準(CNS ) A4規格(210X297公釐) 23