TW200401005A - Filled weatherable compositions having a good surface appearance - Google Patents
Filled weatherable compositions having a good surface appearance Download PDFInfo
- Publication number
- TW200401005A TW200401005A TW092106115A TW92106115A TW200401005A TW 200401005 A TW200401005 A TW 200401005A TW 092106115 A TW092106115 A TW 092106115A TW 92106115 A TW92106115 A TW 92106115A TW 200401005 A TW200401005 A TW 200401005A
- Authority
- TW
- Taiwan
- Prior art keywords
- weight
- molding composition
- scope
- composition
- thermoplastic molding
- Prior art date
Description
200401005 A7 B7 五、發明說明(i )
技術領I 本發明涉及玻璃纖維增強的熱塑性組成物;尤其是, 本發明涉及包含接枝丙烯酸酯橡膠和聚醯胺的組成物,其 適合於模塑表面品質優良的製品。 5 發明概1 經濟部智慧財產局員工消費合作社印製 本發明揭示了玻璃纖維增強的熱塑性模塑組成物,其 適合於製造表面性質優良的製品。所述組成物包含樹脂共 混物和填料組分。所述樹脂共混物包含⑴2〇到5〇重量%的 10 接枝的丙稀酸酯橡膠、(ii) 2到1〇重量%的包含衍生自苯乙 稀(甲基)丙烯腈和馬來酸酐的結構單元的第一共聚物、(出) 20到80重量%的聚醯胺和(iv) 〇到4〇重量%的包含衍生自笨 乙稀和(甲基)丙烯腈的結構單元的第二共聚物,所述百分 數為相對於(i)、(ii)、(iii)和(iv)總量的百分數。本發明組 15成物的填料組分包含5到50%的磨碎的玻璃纖維,所述百 分數為相對於所述模塑組成物重量的百分數。任選地,本 發明的組成物還包含有效量(positive amount)的石夕灰石。由 所述組成物製造的模塑製品具有優良的機械性能和 表面品質特徵。 ”、 20 生8月詳疫 本發明的熱塑性模塑組成物包含樹脂共混物和填料組 分。所述樹脂共混物包含: ⑴20到50、優選25到45重量%的接枝的丙烯酸酯橡膠
200401005 A7 B7 五、發明說明(2 ) (在此稱為ASA) ’ (ii) 2到10、優選4到8重量%的第一共聚物,其重均分 子量為60,000到 180,000、優選100,000到 140,00他/111〇1,並 且包含衍生自苯乙烯(包括取代的苯乙烯,其中取代基是 5 鹵素或者烧基基團,以及α-曱基苯乙烯)、(曱基)丙烯腈 和馬來酸酐的結構單元,和 (iii) 20到80、優選25到60重量%的聚醯胺, (iv) 0到40、優選5到25重量%的第二共聚物,其重均 分子量為70,000到200,000、優選 105,000到 155,000g/mol, 10 其結構包含僅僅衍生自苯乙稀和(甲基)丙烯腈的單元。 本發明組成物的填料組分包含5到50、優選20到40%的 磨碎的玻璃纖維,其平均長度為大約1/64"到1/16”,所述 百分數為相對於所述模塑組成物重量的百分數。 任選地,本發明的組成物可以另包含有效量的最高25 15重量%、優選最高22%(相對於所述模塑組成物的重量)的矽 灰石’其為顆粒形式,平均長度為20到300、優選40到200 微米和粒徑為2到20、優選3到10微米。 經濟部智慧財產局員工消費合作社印製 AS A榭腊— 20 組分(a) ’即ASA樹脂(丙烯酸酯-苯乙烯-丙烯腈互共聚 體)’疋已知的衝擊改性的、實質上熱塑性的樹脂,其包 含SAN基質,在該基質中分散有作為衝擊改性劑的丙烯酸 醋彈性體相。市售的有利的ASA樹脂包括交聯的(曱基)丙 稀酸_彈性體、交聯的SAN共聚物和基本上線性的SAN共 -4- 逢⑼尺度適用中國國家標準(CNS)A4規格(210 x 297公爱) 200401005 A7 B7 五、發明說明(3) 聚物。曱基化苯乙烯例如α -甲基苯乙烯或者乙烯基甲苯 可用於替代所有或者部分的苯乙烯。 10 所述ASA樹脂可以藉由各種已知方法進行製造,包括 乳液或本體聚合。優選的ASA樹脂具有芯-殼結構;這些結 5 構是本領域中眾所周知的,並且已經公開於例如美國專利 3,944,631中,在此將該專利引為參考。這些樹脂的(甲基) 丙烯酸醋彈性體芯部分可以由丙烯酸或甲基丙烯酸的烷 基、芳基或者芳烷基酯組成。這些可以藉由兩步法製造, 其中(甲基)丙烯酸酯彈性體芯部分(其可以是至少部分交聯 的’例如藉由已知的加入多官能乙烯基化合物;)被聚曱基 丙烯酸甲酯、聚苯乙烯、苯乙烯-丙烯腈共聚物或者類似 的乙稀基(共)聚合物的熱塑性殼部分涵蓋。 其他可以有利地用於本發明組成物的AS A樹脂是在以 下專利中公開的型式:美國專利3,655,824 ; ; 15 3,991,009 ; 4,433,102 ; 4,442,263 ;和4,409,363,在此將所 經濟邹智慧財產局員W消費合作钍印製 有这些文獻引為參考。這些AS A樹脂是熱塑性樹爿t,其、兩 常由丙烯酸酯、苯乙烯(或者甲基苯乙烯)和丙烯腈= 成。這些樹脂具有優良的衝擊、熱變形和耐候特徵。月衣 本發明組成物的ASA組分的存在量,相對於所述气 20共混物的重量,為20到50、優選25到45重量%。 ^樹脂 第一共聚:物 所述第一共聚物,其重均分子量為60,〇〇〇到18〇的 優選100,000到140,000g/mol’包含衍生自苯乙埽(勺括〇 張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 200401005 A7 ____ B7 五、發明說明(4) 的(《-甲基)笨乙烯’其中取代基是鹵素或者烷基基團)、 (甲基)丙烯腈和馬來酸酐的結構單元。 就結構而言,所述第一共聚物包含50到9〇、優選6〇到 80重量%的衍生自苯乙烯的單元,丨〇到50、優選2〇到4〇重 5 量%的衍生自(甲基)丙烯腈的單元和0.2到30、優選0.5到5 重量°/。的衍生自馬來酸酐的單元,所述重量百分數為相對 於所述第一共聚物的所述結構組分的重量的百分數。所述 第一共聚物的製造方法是傳統的。 所述第一共聚物在本發明組成物中的存在量,相對於 10 所述樹脂共混物的重量,為2到10、優選4到8重量%。 聚醯胺樹脂 經濟部智慧財產局員工消費合作杜印製 用於本發明共混物的聚醯胺樹脂是本領域中眾所周知 的,其包括半結晶和無定形樹脂,分子量為至少5000,並 15 且通常稱作尼龍。適合的聚醯胺包括在以下美國專利中描 述的那些:美國專利 2,071,250 ; 2,071,251 ; 2,130,523 ; 2,130,948 ; 2,241,322 ; 2,312,966 ; 2,512,606 ; 3,393,210 ; 2,071,250 ; 2,071,251 ; 2,130,523 ; 2,130,948 ; 2,241,322 ; 2,312,966 ;和2,512,606 ;在此將所有這些文獻引為參考。 2〇 所述聚醯胺樹脂可以藉由縮合等莫耳量的含有4到12 個碳原子的飽和二羧酸與含有4到14個碳原子的二胺進行 生產。可以使用過量的二胺,以在所述聚醯胺中提供超過 羧基端基的過量的胺端基聚醯胺的例子包括聚己二醯己 二胺(尼龍66)、聚壬二醯己二胺(尼龍69)、聚癸二醯己二 -6- 張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 401005 A7 B7 五、發明說明(7^ ' — ^ 胺(尼龍610)和聚十二烷醯己二胺(尼龍612)、藉由内釅胺 開裱生產的聚醯胺,即聚己内醯胺、聚月桂内醯胺、聚 11-胺基-十—烷酸、雙(對胺基環己基)甲烷十二烷醯胺\
在本發明中’還可以使用就其組分而言藉由兩種上述聚A 5物共聚或者上述聚合物三元聚合製造的聚醯胺,例如己: 酸、間苯二甲酸己二胺共聚物。優選,所述聚醯胺是線性 的’具有超過200°C的熔點。術語“尼龍,’在此指包含傳 統的本領域技術人員已知的配混成分的尼龍。聚醯胺樹月^ 的例子是尼龍4、尼龍6、尼龍7、尼龍8、尼龍9、居: 10 11 L 麗 ^、尼龍12、尼龍66、尼龍610等等。這些聚醯胺樹墙可 以單獨使用或者結合使用。 .本發明組成物的聚醯胺組分的存在量,相對於所迷樹 脂共混物的重量,為20到80、優選25到60%。 15 t二共聚物 經濟部智慧財產局員工消費合作社印製 所述第二共聚物,其重均分子量為70,000到200,000、 優選105,000到155,000g/mol,其結構包含僅僅衍生自苯乙 烯和(甲基)丙烯腈的單元,其中衍生自苯乙烯的結構單元 佔大約55到85%和衍生自丙烯腈的單元佔15到45%,所述 20 百分數為相對於所述第二共聚物的所述結構組分的總重f 的百分數。所述第二共聚物的製造方法是傳統的。 所述第二共聚物在本發明組成物中的存在量,相對# 所述樹脂共混物的重量,為0到40、優選5到25%。 終張尺度適用中國國家標準(CNS)A4規格(210x297公釐) 200401005 A7 _ B7 五、發明說明(6) 填料組分 所述填料組分在本發明組成物中的存在量,相對於所 述模塑組成物的重量,為5到50、優選20到40%。所述填 料主要疋磨碎的玻璃纖維,即平均長度為大約1/64"到 5 1/16”的玻璃纖維。在本發明另外的實施方案中,所述填料 是磨碎的玻璃纖維與矽灰石的混合物。 磨碎的玻璃纖維 磨碎的玻璃纖維已經廣範地用作填料用於聚合物體 10 系’參見例如美國專利4,381,352、4,680,214和4,861,803。 用於工業中的標準的磨碎的玻璃纖維具有大約16微米的直 徑和大約1/64"到1Π6Π的平均長度。有關磨碎玻璃纖維的 更多資料已經公開於S. H. Metzger,Jr.和K. Seel在J. Cell. 經濟部智慧財產局員工消費合作社印製
Plastics ’ 268-273(1981)中的 “ High Modulus RIM 15 Elastomers for Automotive Extedor Body Panels” 和美國專 利4,381,352,在此將兩者引為參考。玻璃纖維的長度可以 用各種方式表示,例如平均纖維長度或者堆積密度。例 如’ “1/16英寸”磨碎的玻璃纖維的平均長度為大約0.006 英寸(0.253mm),並且這樣的纖維的體積密度為大約 20 0.500g/cm3。現在已經發現,直徑為1〇到20微米的磨碎的 玻璃纖維,在用作用於本發明組成物的填料時,提供出乎 意料的優點。 本發明組成物包含5到50、優選20到40%的磨碎的玻璃 纖維’所述百分數為相對於所述模塑組成物重量的百分 ρ #許張尺度適用中國國家標準(CNS)A4規格(210 x297公釐) 2〇〇4〇1〇〇5 A7 發明說明(7) 數 10 15 經濟部智慧財產局員工消費合作社印製 20 任選组分 以顆粒的物理尺寸為特徵,在本發明範圍内的任選的 矽灰石組分的中值粒徑①一為大約2到20、優選3到10、最 優選4到10微米,其長度為大約2〇到3〇〇、優選3〇到25〇、 最優選40到200微米。所述矽灰石的中值粒徑,以當量球 徑表示,通過SedigmPh(X射線)測定。長度(體積加權平均) 用顯微鏡藉由圖像分析測定。在本發明的組成物中,任選 的矽灰石的量是最高25°/。、優選最高22%(所述百分數、 對於所述模塑組成物重量的百分數)的有效量。 相 .其他本領域中的就其技術認知的功能而言已知的添 劑也可以以起作用的量轉載入到本發明的組成物中。' 包括阻燃劑、脫模劑、潤滑劑和穩定劑,包括熱、埯二 UV穩定劑,以及染料和顏料。 和 本發明的組成物,與相應的包含短切玻璃纖維或者石夕 灰石或者短切玻璃纖維和矽灰石的混合物的組成物相比矽 提供獨特的優點。本發明組成物的表面性質較其具有入 驚奇和出人意料的改進。 7人 本發明組成物的製造方法是傳統的,並且可以通過上、 下過程和使用本領域技術人員公知的設備進行。 以 參考以下實施例可以更好地理解本發明,提出這此 施例是為了敘述的目的,而非為了限制,並且 每二實 、、·°出了考慮用於實施本發明的最佳方式。 邊參張尺度適用_關家標準(CNS)A4規格(21〇 x 297公爱)
200401005 五、發明說明(8 ) A7 B7
實施例 製造了本發明的組成物和比較例組成物,對其性能進 行了測定;測試的性能匯總於以下表格中。除以下指明的 組分外,每種組成物還另外包含相同量的添加劑,包括抗 5氧劑、吸光劑、光穩定劑和顏料,這些添加劑在本發明中 不是關鍵的。 對由所述組成物模塑的製品的表面外觀進行目測檢查 評價,確定是否存在污跡以及條紋和顏色不均勻部位。在 以下報告的評價結果中,所述組成物包含黑色顏料,因為 10 這樣使表面缺陷更明顯。 比較例 下表顯示不屬於本發明的相應組成物的結果,所有這 些組成物都基於ASA並且包含本發明的玻璃纖維。 15 按照下列過程配混所述組成物和模塑測試樣品: 配混 擠出機: ZSK30-mm雙螺桿擠出機 熔體溫度: 區-1,2,3,4,5和模頭分別設定為200 ’ 240,270,280,285,250T: 螺桿速度: 300 rpm 10- 經 濟 部 智 慧 財 產 局 員 工 消 f 合 作 社 印 製 張尺度適用中國國家標準(CNS)A4規格(210x297公釐) 200401005 A7 _ _,B7 五、發明說明(9 ) 注射模塑
模塑機: New Britain 200-Ton 熔體溫度: 區,2,3和注嘴分別設定為500,500, 500,500Τ 模具溫度: 設定為180°F 進行測試的、其性能如以下所列的組成物就其樹脂組 分和添加劑的組成而言是相同的。 5 每種組成物的樹脂組分包含: 35.0重量%的橡膠,其具有平均粒度0.4微米和0.15微 米的雙峰粒度分布,兩種型式均包括接枝到芯-殼結構橡 膠基質上的笨乙烯-丙烯腈共聚物,芯部分包含苯乙烯和 殼部分是交聯的聚丙烯酸丁酯, 10 6.0重量%的苯乙烯' 丙烯腈和馬來酸酐的共聚物(各 組分的莫耳量是66.5/32.5/1% ;該共聚物的重均分子量是 115,000g/mol); 44重量%的聚醯胺6,其相對黏度分子量為48(甲酸), 按照ASTMD 789測定; 經濟部智慧財產局員JC-消費合作.夜印製 15 15.0重量%的苯乙烯-丙烯腈共聚物,其中苯乙烯和丙 烯腈分別佔67.5重量%和32.5重量。/〇,所述共聚物的重均分 子量為 133,000k/mol。 每種組成物包含: 十八炫》基-3,5-二-第三丁基-4-經基-氮化肉桂酸醋-抗氧 20 劑-lpphr(份/100份重量樹脂);二硬脂基硫代二丙酸酯_抗 -11- 張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 200401005 A7 B7 五、發明說明(10) 氧劑-0.5pph!· ; 2-(2’-羥基-3’,5’-二-叔戊基苯基)苯並三唑-吸光劑-〇.25pphr ;雙(2,2,6,6-四甲基-4-哌啶基)癸二酸酯-光穩定劑-025pphr和N,N’-六亞甲基雙[3-(3,5-二-第三丁基-4-羥苯基)丙醯胺]-0·25pphr。在每種組成物中還包括 5 4.3pphr的色母料,該色母料包含炭黑(相對於該色母料的 重量為25%)和75重量%的SAN共聚物(31重量%的丙烯 腈)。這些加入的組分當中沒有一種被認為在本發明中具 有關鍵意義。 經濟部智慧財產局員工消費合作社印製 I 2 .、本~紙張尺度適用中國國家標準(CNS)A4規格(210x297公釐)
S:' Η j Z 200401005 Α7 Β7 五、發明說明) 經濟部智慧財產局員工消費合作社印製 實施例-6 j 15.0 15.0 1 4 288 195 114 105 m 00 1 實施例-5 _1 15.0 15.0 268 198 116 137 OO 1 實施例-4 15.0 15.0 278 199 116 148 o 實施例-3 30.0 Γ…― 290 195 114 103 實施例-2 30.0 Τ·—4 285 197 116 125 o On 1 實施例-1 30.0 269 198 114 145 5: 1 C-4 15.0 15.0 VI 303 203 125 183 102 1 C-3 30.0 in 295 196 116 131 o OS C-2 30.0 寸 276 198 115 137 〇〇 C-1 30.0 294 205 1 124 192 104 (基於模塑組成物的重量百分 數) 短切玻璃纖維,1/81'1 石夕灰石,8μπι2 矽灰石,5μηι3 磨碎玻璃纖維,1/16"4 磨碎玻璃纖維,1/32"5 磨碎玻璃纖維,1/64"5 表面質量a 黏度(1000 1/s,260°C) Pa-S P 1' 1 13 Ο * > Vicat(5kg), °C DTUL8, 66psi (0.46 Mpa), °C |DTUL, 264psi (1.8 Mpa), °C -(3 - 本紙張尺度適用中國國家標準(CNS)A4規格(210x297公釐) 200401005
A B 五、發明說明Ο2 ) 經濟部智慧財產局員工消費合作社印製
VO • r- ο r- ο 00 ο ο m CN τ—^ m 1 < 寸 〇 m (N 卜 ο 卜 Ό Ο (Ν Τ—Η r~) in i 4£) «? IK 〇〇 ο Ό Ο ο ο ο ο r—< VO «•Tv S; Γ-* Ο Ο 卜 卜 ,…·……» m 00 4.¾) οο ο 卜 Ο ο ο Ο (Ν 卜 m τ—< CN 'Ο 〇 S r- ο οο ΓΜ 卜 寸 MD cn oo cn -zrr W? ο ,…呻 ο ο ΟΝ Ο M3 Ο ο <Ν 卜 CN CS 寸· ο <Ν Os Ό ο 卜 寸 Ό ψ—* 卜! o ϊ> (M 涂 ι A ο CN \〇 Ο Ο ν〇 寸 r—H 寸 Ο r—i ( ΟΟ Ο 卜 卜 ο tn 寸 00 寸 τ—< 卜 ο m .......1 ο Ο σ\ Os m τ~·< 寸 VO ο Ό ΟΟ 卜 OS m 卜 to m 00 寸 1 U Ο r—H ο ο ,…丨___ Ι> ο ο <Ν 寸 ΟΟ Τ—4 (Ν Os cei 闼 m ο 卜 寸 〇 τ-Η cn 00 > ' "4 T—H CO 1 U 00 ο 卜 ο ΟΟ ο 卜 ο Ο Ό 寸 ........< (N 卜 m r- On 卜 〇 m 卜 t> CTN oo 1 α ο f C r- ο οο ο ο Ο ο ΠΊ 寸 Τ-Ή ..............< S 00 卜 m τ-Ή 卜 o o ι—H tn a> ψ—i 1 u CN m τ—Η (Ν CN r........* Ο 00 卜 m CN 寸 On 4: Ο m οο cn *________< 寸 寸 ON r—H φ _ ilffitl ψπ 劄. 球 _ 2 ·>*_✓ • »-Η «"Η 1 Ο 糾 ΟΟ ...........< σ\ Τ3 Ο Ν 1—* $ .............< 1 Ρ Ο m έ οο Η Sw<· Τ3 Ο Ν α •— Xi I 仁 Ο Ν >—Η C • r-4 Ιο ψ______Η I C: ΛS Ρ ο i r-Η ο Ν Η-4 • 1—« CO α, nr> ^si ♦ ·—» C/3 α, tTi I Ο 1—^ X _ 'S CX 想 Γ»<^ 〇cr ο 拿 4 • 0-4 ZA 想 -S- 4 % 療 Ul]fi 拿 00 Oh r, 1 o r—4 X ♦I -ii- 本紙張尺度適用中國國家標準(CNS)A4規格(210 x 297公釐) 200401005
發明說明 10 15 經濟部智慧財產局員工消費合作社印製 20- -六種不同的質地(在其各自的粗糙度方面不同)的視覺 3平仏並且將表面品質分級為“優良的”(1)到“差的” (5)。視覺分級的基線是未填充的-ASA的,其分級為1。 -短切玻璃纖維,其平均長度為1/8,,和平均單絲直徑 為 10微米,PPG3540。 2 _矽灰石,平均粒度為8微米,Nyco的產品。 石夕灰石,平均粒度為5微米,Nyco的產品。 4_磨碎玻璃纖維,平均長度1/16”和平均單絲直徑為 15.8微米,〇呢1^(3〇1:1^112的產品 5-磨碎玻璃纖維,平均長度1/32"和平均單絲直徑為 15·8微米,〇wens Corning的產品 磨碎玻璃纖維,平均長度1/64"和平均單纖維直徑為 15.8微米,〇wens Corning的產品 7-Vicat參照ASTM D ISM,使用指明的施加的負載。 油溫度以2°C/min的速率升高。 -DTUL參照ASTM D 648,使用指明的施加的負載。 油溫度以2°C/min的速率升高。 9- Izod參照ASTM D 256,於指明的溫度(RT指室溫)下 測定。測定的樣品6.35cmx l.27Cmx指明的厚度。在測試 樣品中央鑽出〇.25cm半徑的切口,剩餘高度為1〇2mm 10- 拉伸性能按照ASTM D ·638在室溫下用Instr〇n Univeral Machine測定,橫樑速度為5mm/分鐘,〗型拉伸樣 條。 i撓曲性能按照ASTM D -790在室溫下用Instr〇n
裝 計 線 200401005 A7 B7 五、發明說明(14)
Univeral Machine測定,橫樑速度為0.05in/分鐘。測定的樣 品為6.35cm X 1.27cm X 3.18cm 雖然上文中為了敘述的目的已經對本發明進行了詳細 5 描述,應當理解這些細節僅僅為了敘述的目的,並且本領 域技術人員可以在不背離本發明精神和範圍的情況下對其 進行改變,除非這是被本發明申請專利範圍限定的。 經濟部智慧財產局員工消費合作社印製 -16- A紙張尺度適用中國國家標準(CNS)A4規格(210x297公釐)
Claims (1)
- 200401005 A8 B8 C8 ____ D8 六、申請專利範圍 L —種熱塑性模塑組成物,其包含以下組分的樹脂共混 物: (0 20到50%的接枝的丙烯酸酯橡膠, (ii) 2到10%的第一共聚物,其重均分子量為60,000到 5 180,000g/mol,其包含衍生自苯乙烯、(曱基)丙烯 腈和馬來酸酐的結構單元,和 (iii) 20到80重量%的聚醯胺, (iv) 〇到40重量%的第二共聚物,其重均分子量為 70,000到200,000、優選 105,000到 i55,000g/mo卜其 10 結構包含僅僅衍生自苯乙烯和(甲基)丙烯腈的單 元, .所述百分數為相對於所述共混物重量的百分數,和 相對於所述模塑組成物的重量為5到50%的填料組分, 該填料組分包含平均長度為大約1/64"到1/16"的磨碎& 15 璃纖維。 經濟部智慧財產局員工消費合作社印製 2·根據申請專利範圍第1項的熱塑性模塑組成物,其中土真 料還包含相對於所述模塑組成物的重量的最高2 5 %的 有效量的顆粒形式的石夕灰石,該石夕灰石的重均顆教^ 度為20到300微米和中值粒徑為2到20微米。 2〇 3.根據申請專利範圍第1項的熱塑性模塑組成物,其中所 述接枝的丙坤酸S曰橡膠的存在量為25到45%。 4·根據申請專利範圍第1項的熱塑性模塑組成物,其中所 述第一共聚物的存在量為4到8%。 5·根據申請專利範圍第1項的熱塑性模塑組成物,其中所 -17 - 南举張尺度適用中國國家標準(CNS)A4規格(210x297公楚) ---—~~~ 92078B 200401005 10 經濟部智慧財產局員工消費合作社印製 A8 BS CS 、申請專利範圍 述第一共聚物包含5〇到90重量%的衍生自苯乙烯的結 構單元、10到50重量%的衍生自(甲基)丙烯腈的結構單 元和0.2到30重量%的衍生自馬來酸酐的結構單元。 •根據申請專利範圍第1項的熱塑性模塑組成物,其中所 迷聚酸胺的存在量為25到60重量%。 根據申睛專利範圍第3項的熱塑性模塑組成物,其中所 塊石夕灰石以最高22%的有效量存在,該石夕灰石的中值 教徑為3到1〇微米和長度為30到250微米。 .极捸申請專利範圍第1項的熱塑性模塑組成物,其中所 塊填料組分包含相對於所述模塑組成物重量為2 〇到4 〇 重夏%的磨碎玻璃纖維。 -18 ΛΙ張尺度適用令國國家標準(CNS)A4 規格(210x297公釐) 200401005 (一) 、本案指定代表圖爲:第__圖/無 (二) 、本代表圖之元件代表符號簡單說明: Μ本案若有化學式時,請揭示最能顯示發明特徵的 化學式: te-2-1-