RU98101098A - Аморфная, прозрачная, уф-стабилизированная пластина из кристаллизуемого термопласта - Google Patents
Аморфная, прозрачная, уф-стабилизированная пластина из кристаллизуемого термопластаInfo
- Publication number
- RU98101098A RU98101098A RU98101098/04A RU98101098A RU98101098A RU 98101098 A RU98101098 A RU 98101098A RU 98101098/04 A RU98101098/04 A RU 98101098/04A RU 98101098 A RU98101098 A RU 98101098A RU 98101098 A RU98101098 A RU 98101098A
- Authority
- RU
- Russia
- Prior art keywords
- paragraphs
- plate according
- polyethylene terephthalate
- measured
- range
- Prior art date
Links
- -1 4,6-diphenyl-1.3,5-triazin-2-yl Chemical group 0.000 claims 11
- 229920000139 polyethylene terephthalate Polymers 0.000 claims 10
- 239000005020 polyethylene terephthalate Substances 0.000 claims 10
- 229920001169 thermoplastic Polymers 0.000 claims 8
- 239000004416 thermosoftening plastic Substances 0.000 claims 8
- 239000003381 stabilizer Substances 0.000 claims 6
- 238000002425 crystallisation Methods 0.000 claims 2
- 230000005712 crystallization Effects 0.000 claims 2
- 238000000113 differential scanning calorimetry Methods 0.000 claims 2
- 238000010438 heat treatment Methods 0.000 claims 2
- IYAZLDLPUNDVAG-UHFFFAOYSA-N 2-(benzotriazol-2-yl)-4-(2,4,4-trimethylpentan-2-yl)phenol Chemical compound CC(C)(C)CC(C)(C)C1=CC=C(O)C(N2N=C3C=CC=CC3=N2)=C1 IYAZLDLPUNDVAG-UHFFFAOYSA-N 0.000 claims 1
- PHBCDAHASFSLMJ-UHFFFAOYSA-N 2-hydroxybenzotriazole Chemical group C1=CC=CC2=NN(O)N=C21 PHBCDAHASFSLMJ-UHFFFAOYSA-N 0.000 claims 1
- YCIMNLLNPGFGHC-UHFFFAOYSA-N Catechol Chemical compound OC1=CC=CC=C1O YCIMNLLNPGFGHC-UHFFFAOYSA-N 0.000 claims 1
- JXTHNDFMNIQAHM-UHFFFAOYSA-N Dichloroacetic acid Chemical compound OC(=O)C(Cl)Cl JXTHNDFMNIQAHM-UHFFFAOYSA-N 0.000 claims 1
- 239000004594 Masterbatch (MB) Substances 0.000 claims 1
- 230000005540 biological transmission Effects 0.000 claims 1
- 150000001875 compounds Chemical class 0.000 claims 1
- 229920001577 copolymer Polymers 0.000 claims 1
- 238000001125 extrusion Methods 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 238000005259 measurement Methods 0.000 claims 1
- 239000000155 melt Substances 0.000 claims 1
- 238000002844 melting Methods 0.000 claims 1
- 229920001707 polybutylene terephthalate Polymers 0.000 claims 1
- 229920000642 polymer Polymers 0.000 claims 1
- 150000003918 triazines Chemical class 0.000 claims 1
- 238000005429 turbidity Methods 0.000 claims 1
Claims (1)
1. Прозрачная, аморфная пластина толщиной в пределах 1 -20 мм, содержащая в качестве основного компонента кристаллизуемый термопласт, отличающаяся тем, что она содержит в качестве противосветостарителя, по меньшей мере, один УФ - стабилизатор
2. Пластина по п. 1, отличающаяся тем, что концентрация Уф-стабилизатора лежит в диапазоне 0,01 - 5 вес.% в зависимости от веса кристаллизуемых термопластов.
2. Пластина по п. 1, отличающаяся тем, что концентрация Уф-стабилизатора лежит в диапазоне 0,01 - 5 вес.% в зависимости от веса кристаллизуемых термопластов.
3. Пластина по п. 1 или 2, отличающаяся тем, что Уф-стабилизатор выбран из 2-гидроксибензотриазолов или триазинов.
4. Пластина по п. 3, отличающаяся тем, что в качестве Уф-стабилизатора выбрано, по меньшей мере, одно соединение из 2 -(4,6-дифенил-1.3,5-триазин-2-ил)-5-(гекси)окси-фенол и 2,2-метилен-бис(6-(2Н-бензотриазол-2-ил)-4-(1,1,3,3-тетраметил-бутил)-фенол.
5. Пластина по любому из пп. 1-4, отличающаяся тем, что поверхностный блеск, измеренный согласно DIN 67530 (угол измерения 20°) больше, чем 120.
6. Пластина по любому из пп. 1-5. отличающаяся тем, что светопередача, измеренная согласно ASTM D 1003, более 84%.
7. Пластина по любому из пп. 1-6. отличающаяся тем, что мутность, измеренная согласно ASTM D 1003, составляет менее 15%.
8. Пластина по любому из пп. 1-7. отличающаяся тем, что кристаллизуемый термопласт имеет кристалличность в пределах 5 -65 вес.%.
9. Пластина по любому из пп. 1-8, отличающаяся тем, что кристаллизуемый термопласт выбирают из полиэтилентерефталата, полибутилентерефталата, полимера циклоофелина и сополимера циклоофелина.
10. Пластина по п. 9, отличающаяся тем, что в качестве кристаллизуемого термопласта применяют полиэтилентерефталат.
11. Пластина по п. 10, отличающаяся тем, что полиэтилентерефталат содержит рециклат полиэтилентерефталата.
12. Пластина по п. 10 или 11, отличающаяся тем, что при измерении ударной вязкости an по Шарли в соответствии с ISO 179/1D не происходит разлома.
13. Пластина по любому из пп. 10-12, отличающаяся тем, что ударная вязкость ak с надрезом по Изоду, измеренная в соответствии с ISO 180/1А, лежит в пределах 2-8 кДж/м2.
14. Пластина по любому из пп. 10-13, отличающаяся тем, что контрастность изображения, измеренная в соответствии с ASTM D 1003 под углом меньше 2,5°, составляет более 96%.
15. Пластина по любому из пп. 10-14, отличающаяся тем, что полиэтилентерефталат имеет точку кристаллизации, измеренную с помощью дифференциальной сканирующей калориметрии (DSC) при скорости нагрева 10°С/мин, лежащую в интервале 220-280°С.
16. Пластина по любому из пп. 10-15, отличающаяся тем, что полиэтилентерефталат имеет температуру кристаллизации, измеренную с помощью дифференциальной сканирующей калориметрии (DSC) при скорости нагрева 10°С/мин, лежащую в интервале 75-280°С.
17. Пластина по любому из пп. 10-16, отличающаяся тем, что применяемый полиэтилентерефталат имеет стандартную вязкость SV (DCE), измеренную в дихлоруксусной кислоте в соответствии с DIN 53728, лежащую в пределах 800 - 1800.
18. Способ изготовления прозрачных, аморфных пластин по любому из пп. 1 -17, отличающийся тем, что кристаллизуемый термопласт вместе с УФ-стабилизатором расплавляют в экструдере, расплав формуют с помощью сопла, калибруют в каландре с помощью, по меньшей мере, двух валков, выглаживают и охлаждают, прежде чем пластины будут иметь определенный размер, причем первый каландровый валок имеет температуру 50 - 80°С.
19. Способ по п. 18, отличающийся тем, что кристаллизуемый термопласт перед расплавлением высушивают в экструдере.
20. Способ по п. 18 или 19, отличающийся тем, что кристаллизуемый термопласт является полиэтилентерефталатом.
21. Способ по п. 20, отличающийся тем, что полиэтилентерефталат перед экструзией высушивают в течение 4 - 6 ч при температуре 160 - 180°С.
22. Способ по п.20 или 21, отличающийся тем, что температура ПЭТ расплава 250 - 320°С.
23. Способ по пп. 20-22, отличающийся тем, что добавление УФ-стабилизатора проводят по технологии маточной смеси.