RU97118359A - Обжиг золь-гель частиц оксида алюминия - Google Patents
Обжиг золь-гель частиц оксида алюминияInfo
- Publication number
- RU97118359A RU97118359A RU97118359/03A RU97118359A RU97118359A RU 97118359 A RU97118359 A RU 97118359A RU 97118359/03 A RU97118359/03 A RU 97118359/03A RU 97118359 A RU97118359 A RU 97118359A RU 97118359 A RU97118359 A RU 97118359A
- Authority
- RU
- Russia
- Prior art keywords
- furnace
- aluminum oxide
- sintering
- temperature
- composition
- Prior art date
Links
- PNEYBMLMFCGWSK-UHFFFAOYSA-N al2o3 Chemical compound [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 title claims 18
- 239000002245 particle Substances 0.000 title claims 15
- 238000005245 sintering Methods 0.000 claims 12
- 239000000463 material Substances 0.000 claims 10
- 239000000203 mixture Substances 0.000 claims 10
- 239000000843 powder Substances 0.000 claims 10
- 238000005296 abrasive Methods 0.000 claims 7
- 239000002360 explosive Substances 0.000 claims 7
- 239000007787 solid Substances 0.000 claims 5
- TVFDJXOCXUVLDH-UHFFFAOYSA-N Cesium Chemical compound [Cs] TVFDJXOCXUVLDH-UHFFFAOYSA-N 0.000 claims 4
- 229910052792 caesium Inorganic materials 0.000 claims 4
- 229910052761 rare earth metal Inorganic materials 0.000 claims 4
- 150000002910 rare earth metals Chemical class 0.000 claims 4
- IGLNJRXAVVLDKE-UHFFFAOYSA-N rubidium Chemical compound [Rb] IGLNJRXAVVLDKE-UHFFFAOYSA-N 0.000 claims 4
- 229910052701 rubidium Inorganic materials 0.000 claims 4
- 229910052723 transition metal Inorganic materials 0.000 claims 4
- 150000003624 transition metals Chemical class 0.000 claims 4
- VWQVUPCCIRVNHF-UHFFFAOYSA-N yttrium Chemical compound [Y] VWQVUPCCIRVNHF-UHFFFAOYSA-N 0.000 claims 4
- 229910052727 yttrium Inorganic materials 0.000 claims 4
- 230000015572 biosynthetic process Effects 0.000 claims 3
- 238000005755 formation reaction Methods 0.000 claims 3
- 238000000227 grinding Methods 0.000 claims 3
- 238000010438 heat treatment Methods 0.000 claims 3
- 229910052751 metal Inorganic materials 0.000 claims 3
- 239000002184 metal Substances 0.000 claims 3
- 150000003839 salts Chemical class 0.000 claims 3
- 239000011780 sodium chloride Substances 0.000 claims 3
- 239000003082 abrasive agent Substances 0.000 claims 2
- 238000001704 evaporation Methods 0.000 claims 1
- FYYHWMGAXLPEAU-UHFFFAOYSA-N magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 claims 1
- 229910052749 magnesium Inorganic materials 0.000 claims 1
- 239000011777 magnesium Substances 0.000 claims 1
- 239000000126 substance Substances 0.000 claims 1
- 239000000758 substrate Substances 0.000 claims 1
- QCWXUUIWCKQGHC-UHFFFAOYSA-N zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 claims 1
- 229910052726 zirconium Inorganic materials 0.000 claims 1
Claims (28)
1. Способ взрывного превращения в порошок состава, включающего в себя высушенный, но не обожженный золь-гель оксида алюминия, причем указанный состав имеет содержание способных к испарению веществ по меньшей мере 5% по весу, отличающийся тем, что способ предусматривает непосредственную подачу частиц состава в печь, в которой поддерживается температура в диапазоне ориентировочно от 400 до 1600oС и управление временем пребывания в печи для получения превращенных в порошок взрывным образом частиц оксида алюминия.
2. Способ по п. 1, отличающийся тем, что печь представляет собой трубчатую вращающуюся печь.
3. Способ по п. 1, отличающийся тем, что время пребывания в зоне максимальной температуры в печи составляет ориентировочно от 1 с до 30 мин.
4. Способ по п. 2, отличающийся тем, что трубка наклонена на угол от 1 до ориентировочно 60o к горизонтали.
5. Способ по п. 4, отличающийся тем, что трубка вращается со скоростью ориентировочно от 0,5 до 40 об/мин.
6. Способ по п. 1, отличающийся тем, что подаваемый в печь состав, содержащий высушенный золь-гель оксид алюминия, имеет содержание от 5 до 60% по весу способного к испарению материала ориентировочно.
7. Способ по п. 1, отличающийся тем, что состав, содержащий высушенный золь-гель оксида алюминия, подают в печь прямо в непосредственной близости от зоны нагрева.
8. Способ по п. 1, отличающийся тем, что температура и время пребывания в печи достаточны для образования альфа фазы и для спекания до плотности по меньшей мере 95% от теоретической.
9. Способ по п. 1, отличающийся тем, что температура в печи поддерживается ниже температуры, необходимой для спекания оксида алюминия, причем превращенный взрывным образом в порошок материал в последующем спекается до главным образом теоретической плотности.
10. Способ по п. 9, отличающийся тем, что превращенный взрывным образом в порошок материал подвергается дроблению для дополнительного уменьшения размера частиц перед его спеканием.
11. Способ по п. 9, отличающийся тем, что превращенный взрывным образом в порошок материал подвергается до проведения операции спекания обработке раствором растворимой соли металла, выбранного из группы, образованной редкоземельными металлами, переходными металлами, рубидием, цезием и иттрием.
12. Способ взрывного превращения в порошок состава, включающего в себя высушенный, но не обожженный золь-гель оксида алюминия, причем указанный состав имеет содержание способных к испарению веществ ориентировочно от 20 до 40% по весу, отличающийся тем, что способ предусматривает подачу состава в трубчатую роторную печь, имеющую зону нагрева, в которой поддерживается температура в диапазоне ориентировочно от 600 до 1500oС и в которой трубка наклонена к горизонтали на угол ориентировочно от 2 до 20o и вращается со скоростью ориентировочно от 2 до 20 об/мин.
13. Способ по п. 12, отличающийся тем, что температура и время пребывания в печи достаточны для образования альфа фазы и для спекания до плотности по меньшей мере 95% от теоретической.
14. Способ по п. 12, отличающийся тем, что температура в печи поддерживается ниже температуры, необходимой для спекания оксида алюминия, причем превращенный взрывным образом в порошок материал в последующем спекается до главным образом теоретической плотности.
15. Способ по п. 14, отличающийся тем, что превращенный взрывным образом в порошок материал подвергается дроблению для дополнительного уменьшения размера частиц перед его спеканием.
16. Способ по п. 14, отличающийся тем, что превращенный взрывным образом в порошок материал подвергается обработке раствором растворимой соли металла, выбранного из группы, образованной редкоземельными металлами, переходными металлами, рубидием, цезием и иттрием, до проведения операции спекания.
17. Способ взрывного превращения в порошок состава, включающего в себя высушенный, но не обожженный золь-гель оксида алюминия, причем указанный состав имеет содержание способных к испарению веществ ориентировочно от 20 до 40% по весу, отличающийся тем, что способ предусматривает подачу высушенного золь-гель оксида алюминия в трубчатую роторную печь, имеющую зону нагрева, в которой поддерживается температура в диапазоне ориентировочно от 600 до 1650oC и в которой трубка наклонена к горизонтали на угол ориентировочно от 3 до 20° и вращается со скоростью ориентировочно от 1 до 20 об/ мин.
18. Способ по п. 17, отличающийся тем, что температура и время пребывания в печи достаточны для образования альфа фазы и для спекания до плотности по меньшей мере 95% от теоретической.
19. Способ по п. 17, отличающийся тем, что температура в печи поддерживается ниже температуры, необходимой для спекания оксида алюминия, причем превращенный взрывным образом в порошок материал в последующем спекается до главным образом теоретической плотности.
20. Способ по п. 19, отличающийся тем, что превращенный взрывным образом в порошок материал подвергается дроблению для дополнительного уменьшения размера частиц перед его спеканием.
21. Способ по п. 19, отличающийся тем, что превращенный взрывным образом в порошок материал до проведения операции спекания подвергается обработке раствором растворимой соли металла, выбранного из группы, образованной редкоземельными металлами, переходными металлами, рубидием, цезием и иттрием.
22. Мелкие твердые абразивные частицы из оксида алюминия, которые не симметричны относительно их продольного размера, отличающиеся тем, что в любой полученной фракции порошка содержится более 25% указанных частиц с коэффициентом формы по меньшей мере 2 : 1, имеющих плотность по меньшей мере 95% от теоретической.
23. Мелкие твердые абразивные частицы из оксида алюминия по п. 22, отличающиеся тем, что процентное содержание указанных частиц с коэффициентом формы более чем 2 : 1 превышает 30%.
24. Мелкие твердые абразивные частицы из оксида алюминия по п. 22, отличающиеся тем, что они содержат спеченные кристаллы оксида алюминия с размерами от 0, 01 до 10 мкм.
25. Мелкие твердые абразивные частицы из оксида алюминия по п. 24, отличающиеся тем, что кристаллиты оксида алюминия являются субмикронными по размерам.
26. Мелкие твердые абразивные частицы из оксида алюминия по п. 22, отличающиеся тем, что они содержат спеченный оксид алюминия, модифицированный введением до 10% одного или нескольких оксидов, выбранных из группы, состоящей из оксидов магния, циркония, редкоземельных металлов, переходных металлов, рубидия, цезия и иттрия.
27. Связанный абразивный материал, отличающийся тем, что он включает в себя абразивные частицы по любому из пп. 22-26.
28. Нанесенный на подложку абразивный материал, отличающийся тем, что он включает в себя абразивные частицы по любому из пп. 22-26.