RU2461531C1 - Artificial rock - Google Patents
Artificial rock Download PDFInfo
- Publication number
- RU2461531C1 RU2461531C1 RU2011121734/03A RU2011121734A RU2461531C1 RU 2461531 C1 RU2461531 C1 RU 2461531C1 RU 2011121734/03 A RU2011121734/03 A RU 2011121734/03A RU 2011121734 A RU2011121734 A RU 2011121734A RU 2461531 C1 RU2461531 C1 RU 2461531C1
- Authority
- RU
- Russia
- Prior art keywords
- artificial rock
- calcium carbonate
- water
- cement
- carboxymethyl cellulose
- Prior art date
Abstract
Description
Изобретение относится к промышленности строительных материалов.The invention relates to the construction materials industry.
Известна искусственная порода следующего состава, мас.%: цемент 25,0-30,0; мука и песок на основе карбоната кальция ≤55,0; оксиды металлов (железо, хром, свинец, ртуть) 2,0-12,0; кальциевые силикаты 2,0-3,0; силициды углерода 0,1-0,6; фторсиликаты ≤6,0; сульфаты железа и меди 0,4-0,8; щавелевая кислота 0,3-0,5; вода 10,0-23,0 [1].Known artificial rock of the following composition, wt.%: Cement 25.0-30.0; flour and sand based on calcium carbonate ≤55.0; metal oxides (iron, chromium, lead, mercury) 2.0-12.0; calcium silicates 2.0-3.0; carbon silicides 0.1-0.6; fluorosilicates ≤6.0; sulfates of iron and copper 0.4-0.8; oxalic acid 0.3-0.5; water 10.0-23.0 [1].
Задача изобретения состоит в получении легкой и прочной искусственной породы.The objective of the invention is to obtain a light and durable artificial breed.
Технический результат достигается тем, что искусственная порода из смеси, содержащей цемент, песок на основе карбоната кальция, окрашивающую добавку, воду, дополнительно включает пенообразователь ПБ-2000, карбоксиметилцеллюлозу. и суперпластификатор С-3 при следующем соотношении компонентов, мас.%: цемент 25,0-30,0; песок на основе карбоната кальция 40,0-43,5; окрашивающая добавка 3,0-10,0; вода 20,0-25,0; пенообразователь ПБ-2000 0,37-0,48; карбосиметилцеллюлоза 0,02-0,03; суперпластификатор С-3 1,1-1,5.The technical result is achieved by the fact that artificial rock from a mixture containing cement, sand based on calcium carbonate, a coloring additive, water, further includes a blowing agent PB-2000, carboxymethyl cellulose. and C-3 superplasticizer in the following ratio of components, wt.%: cement 25.0-30.0; sand based on calcium carbonate 40.0-43.5; coloring additive 3.0-10.0; water 20.0-25.0; PB-2000 foaming agent 0.37-0.48; carbosimethyl cellulose 0.02-0.03; superplasticizer C-3 1.1-1.5.
В таблице приведены составы искусственной породы.The table shows the compositions of artificial rock.
Для получения искусственной породы подготавливают и дозируют сырьевые компоненты: портландцемент, песок на основе карбоната кальция, просеянный через сетку с отверстиями размером 0,14 мм, окрашивающую добавку, пенообразователь ПБ-2000 (соответствующий требованиям ТУ 2481-185-05744685-01, плотностью 1000-1200 кг/м3, pH 7-10, кратность пены рабочего раствора с объемной долей пенообразователя 4%, устойчивость пены не менее 360 с), карбоксиметилцеллюлозу, суперпластификатор С-3, воду.To obtain artificial rock, the following raw materials are prepared and dosed: Portland cement, calcium carbonate sand sifted through a mesh with 0.14 mm holes, a dyeing additive, PB-2000 foaming agent (corresponding to the requirements of TU 2481-185-05744685-01, density 1000 -1200 kg / m 3 , pH 7-10, the multiplicity of the foam of the working solution with a volume fraction of foaming agent of 4%, the stability of the foam is not less than 360 s), carboxymethyl cellulose, superplasticizer C-3, water.
В пеногенераторе взбивают пену из смеси пенообразователя ПБ-2000 с водой. Смешивание всех компонентов проводят в шнековом смесителе, в который сначала подают сухие компоненты: портландцемент, песок на основе карбоната кальция, окрашивающую добавку, а затем приготовленную пену, карбоксиметилцеллюлозу и суперпластификатор С-3. Из смесителя приготовленную смесь равномерно распределяют по площади предварительно смазанных маслом металлических форм и подают на тепловлажностную обработку, которую проводят по режиму 3+9+3 ч при температуре изотермической выдержки 90°C. Затем готовые изделия извлекают из форм и транспортируют на склад. Полученные изделия шлифуют и полируют. Прочность искусственной породы при сжатии составит не менее 3 МПа. Материал может быть эффективно использован для внутренней и наружной отделки архитектурных сооружений.In the foam generator, foam is whipped from a mixture of the PB-2000 blowing agent with water. All components are mixed in a screw mixer, into which dry components are first fed: Portland cement, calcium carbonate sand, a coloring agent, and then the prepared foam, carboxymethyl cellulose and C-3 superplasticizer. From the mixer, the prepared mixture is evenly distributed over the area of metal forms pre-oiled with oil and fed to the heat-moisture treatment, which is carried out according to the regime of 3 + 9 + 3 hours at an isothermal holding temperature of 90 ° C. Then the finished product is removed from the molds and transported to the warehouse. The resulting products are ground and polished. The compressive strength of artificial rock will be at least 3 MPa. The material can be effectively used for interior and exterior decoration of architectural structures.
Источник информацииThe source of information
1. PL 268011, C04B 28/00, 1990.1. PL 268011, C04B 28/00, 1990.
Claims (1)