RU2425013C1 - Wood concrete mixture - Google Patents
Wood concrete mixture Download PDFInfo
- Publication number
- RU2425013C1 RU2425013C1 RU2011100431/03A RU2011100431A RU2425013C1 RU 2425013 C1 RU2425013 C1 RU 2425013C1 RU 2011100431/03 A RU2011100431/03 A RU 2011100431/03A RU 2011100431 A RU2011100431 A RU 2011100431A RU 2425013 C1 RU2425013 C1 RU 2425013C1
- Authority
- RU
- Russia
- Prior art keywords
- cement
- wood
- foaming agent
- lime
- water
- Prior art date
Abstract
Description
Изобретение, относится к промышленности строительных материалов, в частности к производству изделий (плит, блоков) из древесно-цементных композиций, используемых преимущественно в малоэтажном строительстве.The invention relates to the construction materials industry, in particular to the production of products (plates, blocks) from wood-cement compositions used mainly in low-rise construction.
Известна арболитовая смесь, содержащая, кг/м3: цемент 310; древесную дробленку 140; известь 19; хлорид кальция 6; раствор пенообразователя 190 [1]. Такая смесь содержит большое количество дорогостоящих вяжущих (цемент, известь).Known arbolitic mixture containing, kg / m 3 : cement 310; wood chippings 140; lime 19; calcium chloride 6; a foaming agent solution 190 [1]. Such a mixture contains a large number of expensive binders (cement, lime).
Задача изобретения состоит в сокращении расхода вяжущих.The objective of the invention is to reduce the consumption of binders.
Технический результат достигается тем, что арболитовая смесь, содержащая цемент, древесную дробленку, известь, воду, пенообразователь, в качестве пенообразователя содержит пенообразователь ПБ-2000, древесную дробленку, измельченную до размера частиц не более 5 мм, и дополнительно включает омыленную канифоль при следующем соотношении компонентов, мас.%: цемент 40-45; известь 5-7; пенообразователь ПБ-2000 0,3-0,35; омыленная канифоль 0,003-0,005; указанная древесная дробленка остальное, причем водоцементное отношение составляет 1,1-1,3.The technical result is achieved in that the arbolite mixture containing cement, wood chips, lime, water, a foaming agent contains PB-2000 foaming agent as a foaming agent, a wood mill, crushed to a particle size of not more than 5 mm, and further includes saponified rosin in the following ratio components, wt.%: cement 40-45; lime 5-7; PB-2000 foaming agent 0.3-0.35; saponified rosin 0.003-0.005; the specified wood crusher rest, and the water-cement ratio is 1.1-1.3.
Для приготовления смеси подготавливают и дозируют сырьевые компоненты: цемент (портландцемент, шлакопортландцемент, белый цемент), древесную дробленку, известь, пенообразователь ПБ-2000 (соответствующий требованиям ТУ 2481-185-05744685-01, плотностью 1000-1200 кг/м3, pH 7-10, кратность пены рабочего раствора с объемной долей пенообразователя 4 %, устойчивость пены не менее 360 с), омыленную канифоль, воду.To prepare the mixture, the following raw materials are prepared and dosed: cement (Portland cement, slag Portland cement, white cement), wood chips, lime, PB-2000 foaming agent (meeting the requirements of TU 2481-185-05744685-01, density 1000-1200 kg / m 3 , pH 7-10, the multiplicity of the foam of the working solution with a volume fraction of a foaming agent of 4%, the stability of the foam is at least 360 s), saponified rosin, water.
Составы арболитовой смеси приведены в таблице.The compositions of the arbolite mixture are shown in the table.
Арболитовую смесь приготовляют следующим образом.Arbolite mixture is prepared as follows.
В пеногенераторе взбивают пену из смеси пенообразователя с водой, добавляют омыленную канифоль. Смешивание всех компонентов бетона происходит в шнековом смесителе, в который сначала подают сухие компоненты: цемент, молотую до удельной поверхности 4000 см2/г негашеную известь, предварительно измельченную до получения частиц размером не более 5 мм древесную дробленку, а затем приготовленную пену. Из смесителя приготовленную смесь равномерно распределяют по площади предварительно смазанных маслом металлических форм и оставляют до затвердевания. Затем готовые изделия извлекают из форм и транспортируют на склад. Прочность изделий, полученных из арболитовой смеси, в возрасте 28 сут составит не менее 1,5 МПа.In the foam generator, whip the foam from the mixture of the foaming agent with water, add saponified rosin. Mixing of all concrete components takes place in a screw mixer, into which dry components are first fed: cement, ground lime to a specific surface of 4000 cm 2 / g, preliminarily crushed to produce particles of no more than 5 mm wood crushed, and then the foam is prepared. From the mixer, the prepared mixture is evenly distributed over the area of metal forms pre-oiled and left to harden. Then the finished product is removed from the molds and transported to the warehouse. The strength of products obtained from arbolite mixture at the age of 28 days will be at least 1.5 MPa.
Источник информацииThe source of information
1. Патент РФ №2177926, 2000.1. RF patent No. 2177926, 2000.
Claims (1)
причем водоцементное отношение составляет 1,1-1,3. Arbolitic mixture containing cement, wood chips, lime, water, a foaming agent, characterized in that the foaming agent contains PB-2000 foaming agent, a wood mill, crushed to a particle size of not more than 5 mm and further includes saponified rosin in the following ratio of components, wt .%:
moreover, the water-cement ratio is 1.1-1.3.