RU2332385C1 - Ceramic body - Google Patents

Ceramic body Download PDF

Info

Publication number
RU2332385C1
RU2332385C1 RU2006146097/03A RU2006146097A RU2332385C1 RU 2332385 C1 RU2332385 C1 RU 2332385C1 RU 2006146097/03 A RU2006146097/03 A RU 2006146097/03A RU 2006146097 A RU2006146097 A RU 2006146097A RU 2332385 C1 RU2332385 C1 RU 2332385C1
Authority
RU
Russia
Prior art keywords
ceramic body
clay
ceramic mass
apatite ore
quartzite
Prior art date
Application number
RU2006146097/03A
Other languages
Russian (ru)
Inventor
Юли Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2006146097/03A priority Critical patent/RU2332385C1/en
Application granted granted Critical
Publication of RU2332385C1 publication Critical patent/RU2332385C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to silicate technology and refers to ceramic body, which can be used in brick manufacture. Ceramic body consists of, weight ratio %: clay 62.0-65.0; silica stone 30.0-35.0; apatite ore tailings 3.0-5.0.
EFFECT: strength enhancement of bricks made of ceramic body.
1 tbl

Description

Изобретение относится к области технологии силикатов и касается составов керамических масс, которые могут быть использованы в производстве кирпича.The invention relates to the field of technology of silicates and relates to compositions of ceramic masses that can be used in the manufacture of bricks.

Известна керамическая масса состава, мас.%: глина 20,0-30,0; кварциты 70,0-80,0 [1].Known ceramic mass of the composition, wt.%: Clay 20,0-30,0; quartzites 70.0-80.0 [1].

Задача изобретения состоит в повышении прочности кирпича, полученного из керамической массы.The objective of the invention is to increase the strength of bricks obtained from ceramic mass.

Технический результат достигается тем, что керамическая масса, содержащая глину и кварциты, дополнительно включает отходы обогащения апатитовой руды, при следующем соотношении и компонентов, мас.%: глина 62,0-65,0; кварциты 30,0-35,0; отходы обогащения апатитовой руды 3,0-5,0.The technical result is achieved by the fact that the ceramic mass containing clay and quartzite further includes waste from the processing of apatite ore, in the following ratio of components, wt.%: Clay 62.0-65.0; quartzites 30.0-35.0; apatite ore dressing wastes 3.0–5.0.

В таблице приведены составы керамической массы.The table shows the composition of the ceramic mass.

ТаблицаTable КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 ГлинаClay 65,065.0 63,563.5 62,062.0 КварцитыQuartzite 30,030,0 32,532,5 35,035.0 Отходы обогащения апатитовой рудыApatite ore dressing waste 5,05,0 4,04.0 3,03.0 Прочность на сжатие, МПаCompressive strength, MPa 65-7065-70 65-7065-70 65-7065-70 Прочность на изгиб, МПаBending Strength, MPa 20-2220-22 20-2220-22 20-2220-22

В составе керамической массы могут быть использованы глины, содержащие, мас.%: SiO2 42,0-80,0; Al2O3 13,0-35,0; TiO2 0,3-1,6; Fe2O3 1,2-11,0; CaO до 1,7; MgO 0,2-1,6; Na2O 0,1-3,6; K2O 0,1-4,4; п.п.п. 2,6-15,7.In the composition of the ceramic mass can be used clay containing, wt.%: SiO 2 42,0-80,0; Al 2 O 3 13.0-35.0; TiO 2 0.3-1.6; Fe 2 O 3 1.2-11.0; CaO up to 1.7; MgO 0.2-1.6; Na 2 O 0.1-3.6; K 2 O 0.1-4.4; p.p.p. 2.6-15.7.

Отход обогащения апатитовой руды, характеризуется следующим химическим составом, мас.%: SiO2 28,0-29,0; Al2O3 2,5-3,0; Fe2O3 2,5-3,0; CaO 54,0-55,5; MgO 1,5-2,5; Na2O 1,0-1,3; K2O 0,7-1,0.Apatite ore dressing waste is characterized by the following chemical composition, wt.%: SiO 2 28.0-29.0; Al 2 O 3 2.5-3.0; Fe 2 O 3 2.5-3.0; CaO 54.0-55.5; MgO 1.5-2.5; Na 2 O 1.0-1.3; K 2 O 0.7-1.0.

Кварцы - метаморфическая порода, на 95-98 мас.% состоящая из SiO2.Quartz is a metamorphic rock, 95-98 wt.% Consisting of SiO 2 .

Глубину измельчают до размера кусков 10-20 мм, сушат при температуре 60-70°С до влажности 3-4% и размалывают сухим способом до получения частиц размером не более 2 мм. Кварциты и отходы обогащения апатитовой руды измельчают до получения частиц размером не более 2 мм. Полученные порошки смешивают и готовят керамическую массу с влажностью 9-11%. Из керамической массы под давлением 15-18 МПа формуют кирпич, который обжигают при температуре 1000-1030°С. Возможно нанесение (напыление) до обжига на поверхность (ложок) отформованного кирпича слоя цветной глазури.The depth is crushed to a piece size of 10-20 mm, dried at a temperature of 60-70 ° C to a moisture content of 3-4% and milled dry to obtain particles no larger than 2 mm. Quartzites and apatite ore dressing waste are crushed to obtain particles no larger than 2 mm in size. The resulting powders are mixed and a ceramic mass is prepared with a moisture content of 9-11%. A brick is formed from a ceramic mass under a pressure of 15-18 MPa, which is fired at a temperature of 1000-1030 ° C. It is possible to apply (spraying) a layer of colored glaze to the surface (spoons) of the molded brick before firing.

Источники информацииInformation sources

1. SU 1542932, C04B 33/00, 1990.1. SU 1542932, C04B 33/00, 1990.

Claims (1)

Керамическая масса, содержащая глину и кварциты, отличающаяся тем, что дополнительно содержит отходы обогащения апатитовой руды при следующем соотношении компонентов, мас.%:Ceramic mass containing clay and quartzite, characterized in that it further comprises waste from the processing of apatite ore in the following ratio of components, wt.%: глинаclay 62,0-65,062.0-65.0 кварцитыquartzite 30,0-35,030.0-35.0 отходы обогащения апатитовой рудыapatite ore dressing waste 3,0-5,03.0-5.0
RU2006146097/03A 2006-12-25 2006-12-25 Ceramic body RU2332385C1 (en)