RU2020130225A - Способ селективного фосфатирования комбинированной металлической конструкции - Google Patents

Способ селективного фосфатирования комбинированной металлической конструкции Download PDF

Info

Publication number
RU2020130225A
RU2020130225A RU2020130225A RU2020130225A RU2020130225A RU 2020130225 A RU2020130225 A RU 2020130225A RU 2020130225 A RU2020130225 A RU 2020130225A RU 2020130225 A RU2020130225 A RU 2020130225A RU 2020130225 A RU2020130225 A RU 2020130225A
Authority
RU
Russia
Prior art keywords
composition
zinc
range
phosphating
zinc phosphating
Prior art date
Application number
RU2020130225A
Other languages
English (en)
Other versions
RU2783624C2 (ru
Inventor
Олаф ДАЛЕНБУРГ
Харди ВИТЦОРЕК
Йюрген ШПЕХТ
Original Assignee
Хеметалл Гмбх
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Хеметалл Гмбх filed Critical Хеметалл Гмбх
Publication of RU2020130225A publication Critical patent/RU2020130225A/ru
Application granted granted Critical
Publication of RU2783624C2 publication Critical patent/RU2783624C2/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
    • C23C22/36—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates
    • C23C22/362—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates containing also zinc cations
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
    • C23C22/36—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates
    • C23C22/364—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates containing also manganese cations
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
    • C23C22/36—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates
    • C23C22/364—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates containing also manganese cations
    • C23C22/365—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides containing also phosphates containing also manganese cations containing also zinc and nickel cations
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/40—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing molybdates, tungstates or vanadates
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/73—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals characterised by the process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/78—Pretreatment of the material to be coated
    • C23C22/80—Pretreatment of the material to be coated with solutions containing titanium or zirconium compounds
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/82—After-treatment
    • C23C22/83—Chemical after-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/40—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing molybdates, tungstates or vanadates
    • C23C22/44—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing molybdates, tungstates or vanadates containing also fluorides or complex fluorides
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2222/00—Aspects relating to chemical surface treatment of metallic material by reaction of the surface with a reactive medium
    • C23C2222/20—Use of solutions containing silanes

Landscapes

  • Chemical & Material Sciences (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Treatment Of Metals (AREA)

Claims (31)

1. Способ предварительной химической обработки и селективного фосфатирования комбинированной металлической конструкции, содержащей по меньшей мере одну часть, изготовленную из алюминия, и по меньшей мере одну часть, изготовленную из цинка, и необязательно дополнительную часть, изготовленную из железа, отличающийся тем, что способ включает
(I) на первой стадии обработку комбинированной металлической конструкции водной композицией для цинкового фосфатирования, что приводит к образованию покрывающего поверхность слоя кристаллического фосфата цинка, имеющего плотность покрытия в диапазоне от 0,5 до 5 г/м2, на частях, изготовленных из железа и цинка, но без образования слоя фосфата цинка, имеющего плотность покрытия, составляющего по меньшей мере 0,5 г/м2, на алюминиевые частях, а затем, промежуточную процедуру промывания водой,
(II) на второй стадии нанесение водной кислой пассивирующей композиции, имеющей значение рН в диапазоне от 2,0 до 5,5, на комбинированную металлическую конструкцию, при этом кислая пассивирующая композиция удаляет не более 50% кристаллического фосфата цинка на частях, изготовленных из цинка и железа, но образует пассивный слой на алюминиевых частях, который не составляет при этом покрывающего поверхность слоя кристаллического фосфата,
при этом композиция для цинкового фосфатирования на стадии (I) имеет содержание ионов натрия и/или калия и ионов алюминия,
при этом композиция для цинкового фосфатирования на стадии (I) имеет температуру в диапазоне от 20 до 65°С, и имеет содержание свободного фторида, которое составляет по меньшей мере 5 мг/л, но не более 200 мг/л,
при этом в композиции для цинкового фосфатирования присутствует по меньшей мере 0,04 г/л, но не более 3,2 г/л бора, в виде растворимых в воде неорганических соединений, в пересчете на BF4, и
при этом количество баллов свободной кислоты с добавлением KCl в композиции для цинкового фосфатирования составляет по меньшей мере 0,6 балла.
2. Способ по п. 1, отличающийся тем, что композиция для цинкового фосфатирования на стадии (I) имеет содержание свободного фторида в диапазоне от 10 до 200 мг/л, предпочтительно от 20 до 150 мг/л, более предпочтительно от 20 до 120 мг/л, особенно предпочтительно от 50 до 120 мг/л, и очень особенно предпочтительно от 70 до 120 мг/л.
3. Способ по п. 1 или 2, отличающийся тем, что композиция для цинкового фосфатирования на стадии (I) имеет концентрацию бора в виде растворимых в воде неорганических соединений в пересчете на BF4 в диапазоне от 0,08 до 2,5 г/л, более предпочтительно от 0,08 до 2 г/л, более предпочтительно от 0,25 до 2 г/л, особенно предпочтительно от 0,5 до 1,5 г/л, и очень особенно предпочтительно от 0,8 до 1,2 г/л.
4. Способ по одному из предыдущих пунктов, отличающийся тем, что содержание ионов натрия и/или калия (в пересчете на натрий) в композиции для цинкового фосфатирования на стадии (I) находится в диапазоне от 1 до 4 г/л, в частности от 2 до 3 г/л, и содержание свободного фторида находится в диапазоне от 50 до 150 мг/л, в частности от 70 до 120 мг/л.
5. Способ по одному из предыдущих пунктов, отличающийся тем, что содержание неорганических соединений, включающих кремний (в пересчете на SiF6) в композиции для цинкового фосфатирования на стадии (I) составляет менее 25 мг/л, предпочтительно менее 15 мг/л, более предпочтительно менее 5 мг/л, и наиболее предпочтительно менее 1 мг/л.
6. Способ по одному из предыдущих пунктов, отличающийся тем, что композиция для цинкового фосфатирования на стадии (I) имеет количество баллов свободной кислоты с добавлением KCl в диапазоне от 0,6 до 3,0 баллов, предпочтительно от 0,8 до 3,0 баллов, более предпочтительно от 1,0 до 3,0 баллов, и наиболее предпочтительно от 1,0 до 2,5 балла.
7. Способ по одному из предыдущих пунктов, отличающийся тем, что для композиции для цинкового фосфатирования на стадии (I) безразмерный коэффициент
(К-значение·Т) / (Fобщ.·[В]·1000)
находится в диапазоне от 0,13 до 22,5, предпочтительно от 0,2 до 15.
8. Способ по одному из предыдущих пунктов, отличающийся тем, что композиция для цинкового фосфатирования на стадии (I) дополнительно включает один или несколько из следующих катионов:
0,3-2 г/л, предпочтительно 0,5-1,5 г/л, марганца(II),
0,3-2 г/л, предпочтительно 0,8-1,2 г/л, никеля(II),
0,001-0,2 г/л, предпочтительно 0,005-0,1 г/л, железа(III).
9. Способ по одному из предыдущих пунктов, отличающийся тем, что значение рН пассивирующей композиции на стадии (II) находится в диапазоне от 2,5 до 5,5, более предпочтительно от 3,0 до 5,5 и наиболее предпочтительно от 3,5 до 5,5.
10. Способ по одному из предыдущих пунктов, отличающийся тем, что пассивирующая композиция на стадии (II) содержит Ti, Zr и/или Hf в связанной в комплекс форме, предпочтительно в концентрации, находящейся в диапазоне от 20 до 500 мг/л, более предпочтительно от 50 до 300 мг/л, и более предпочтительно от 50 до 150 мг/л (в пересчете на Ti, Zr и/или Hf), и необязательно ионы дополнительных металлов в виде растворимых в воде соединений.
11. Способ по одному из предыдущих пунктов, отличающийся тем, что пассивирующая композиция на стадии (II) дополнительно содержит по меньшей мере один органосилан и/или по меньшей мере один продукт его гидролиза и/или по меньшей мере один продукт его конденсации, предпочтительно в концентрации, находящейся в диапазоне от 5 до 200 мг/л, более предпочтительно от 10 до 100 мг/л, и особенно предпочтительно от 20 до 80 мг/л (в пересчете на Si).
12. Композиция для цинкового фосфатирования, предназначенная для селективного фосфатирования стальных, оцинкованных стальных и/или легированных оцинкованных стальных поверхностей в металлической комбинированной конструкции, содержащей часть, изготовленную из алюминия, по одному из пп. 1-8, отличающаяся тем, что она имеет количество баллов свободной кислоты с добавлением KCl, составляющее по меньшей мере 0,6 балла, и значение рН, предпочтительно находящееся в диапазоне от 2,5 до 3,5, и
(а) 5-50 г/л ионов фосфата в пересчете на Р2О5,
(б) 0,3-3 г/л ионов цинка,
(в) по меньшей мере 5 мг/л, но не более 200 мг/л, свободного фторида, и
(г) по меньшей мере 0,04 г/л, но не более 3,2 г/л, бора в виде растворимых в воде неорганических соединений, в пересчете на BF4,
при этом композиция для цинкового фосфатирования дополнительно имеет содержание ионов натрия и/или калия и ионов алюминия.
13. Концентрат, из которого можно получить композицию для цинкового фосфатирования по п. 12 посредством разбавления подходящим растворителем и/или дисперионной средой, предпочтительно водой, и необязательно регулируя при этом значение рН.
14. Комбинированная металлическая конструкция, содержащая по меньшей мере одну часть, изготовленную из алюминия, и по меньшей мере одну часть, изготовленную из цинка, и необязательно дополнительную часть, изготовленную из железа, отличающаяся тем, что ее можно получить посредством способа по одному из пп. 1-11.
15. Применение комбинированной металлической конструкции по п. 14 в промышленности поставки автомобильных комплектующих, в производстве кузовов в автомобилестроении, в сельскохозяйственном машиностроении, в судостроении, в строительном секторе или при производстве бытовой техники.
RU2020130225A 2018-02-19 2019-02-12 Способ селективного фосфатирования комбинированной металлической конструкции RU2783624C2 (ru)