RU2007124548A - Свободные от галогенов огнестойкие вспенивающиеся стирольные полимеризаты - Google Patents
Свободные от галогенов огнестойкие вспенивающиеся стирольные полимеризаты Download PDFInfo
- Publication number
- RU2007124548A RU2007124548A RU2007124548/04A RU2007124548A RU2007124548A RU 2007124548 A RU2007124548 A RU 2007124548A RU 2007124548/04 A RU2007124548/04 A RU 2007124548/04A RU 2007124548 A RU2007124548 A RU 2007124548A RU 2007124548 A RU2007124548 A RU 2007124548A
- Authority
- RU
- Russia
- Prior art keywords
- styrene
- range
- aluminum
- graphite
- weight
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/0066—Use of inorganic compounding ingredients
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/16—Making expandable particles
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L25/00—Compositions of, homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Compositions of derivatives of such polymers
- C08L25/02—Homopolymers or copolymers of hydrocarbons
- C08L25/04—Homopolymers or copolymers of styrene
- C08L25/06—Polystyrene
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K21/00—Fireproofing materials
- C09K21/14—Macromolecular materials
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2203/00—Foams characterized by the expanding agent
- C08J2203/12—Organic compounds only containing carbon, hydrogen and oxygen atoms, e.g. ketone or alcohol
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2203/00—Foams characterized by the expanding agent
- C08J2203/14—Saturated hydrocarbons, e.g. butane; Unspecified hydrocarbons
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2325/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Derivatives of such polymers
- C08J2325/02—Homopolymers or copolymers of hydrocarbons
- C08J2325/04—Homopolymers or copolymers of styrene
- C08J2325/06—Polystyrene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K2201/00—Specific properties of additives
- C08K2201/002—Physical properties
- C08K2201/005—Additives being defined by their particle size in general
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2201/00—Properties
- C08L2201/02—Flame or fire retardant/resistant
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Medicinal Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Health & Medical Sciences (AREA)
- Polymers & Plastics (AREA)
- Inorganic Chemistry (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
- Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
Claims (6)
1. Вспенивающиеся гранулированные стирольные полимеры, содержащие
а) от 5 до 50 мас.% наполнителя, выбираемого из таких порошкообразных неорганических веществ, как тальк, мел, каолин, гидроксид алюминия, нитрит алюминия, силикат алюминия, сульфат бария, карбонат кальция, диоксид титана, сульфат кальция, кремниевая кислота, кварцевая мука, аэросил, глинозем или волластонит, и
б) от 2 до 40 мас.% расширенного графита со средним размером частиц в пределах от 10 до 1000 мкм,
в) от 0 до 20 мас.% красного фосфора или же органического или неорганического фосфата, фосфита или фосфоната,
г) от 0 до 10 мас.% сажи или графита.
2. Вспенивающиеся гранулированные стирольные полимеры по п.1, отличающиеся тем, что они содержат от 1 до 10 мас.% красного фосфора, трифенилфосфата или 9,10-дигидро-9-окса-10-фосфафенантрен-10-оксида.
3. Вспенивающиеся гранулированные стирольные полимеры по п.2, отличающиеся тем, что они содержат от 0,1 до 5 мас.% графита со средним размером частиц в пределах от 0,1 до 100 мкм.
4. Вспенивающиеся гранулированные стирольные полимеры по одному из пп.1-3, отличающиеся тем, что они содержат от 3 до 7 мас.% органического порообразующего средства.
5. Способ получения вспенивающихся стирольных полимеризатов, включающий стадии:
а) введение в состав расплавленного стирольного полимеризата с помощью статического или динамического смесителя при температуре не менее 150°С
(i) органического порообразующего средства,
(ii) от 5 до 50 мас.% из расчета на стирольный полимеризат наполнителя, выбираемого из таких порошкообразных неорганических веществ, как тальк, мел, каолин, гидроксид алюминия, нитрит алюминия, силикат алюминия, сульфат бария, карбонат кальция, диоксид титана, сульфат кальция, кремниевая кислота, кварцевая мука, аэросил, глинозем или волластонит, и
(iii) от 2 до 40 мас.% из расчета на стирольный полимеризат расширенного графита со средним размером частиц в пределах от 10 до 1000 мкм,
б) охлаждение содержащего порообразующее средство и наполнитель расплава полимера до температуры не менее 120°С,
в) пропускание через пластину с фильерами, представляющими собой сверления с диаметром на выходе из фильеры не более 1,5 мм, и
г) гранулирование содержащего порообразующее средство расплава непосредственно после выхода из пластины с фильерами под слоем воды при давлении в пределах от 1 до 20 бар.
6. Способ получения формованных деталей из частиц пенопласта, отличающийся тем, что гранулированные вспенивающиеся стирольные полимеризаты по п.1 на первой стадии предварительно вспенивают с помощью горячего воздуха или водяного пара с образованием частиц пенопласта с плотностью в пределах от 8 до 200 г/м3 и на второй стадии проводят их сплавление в закрытой форме.