RU2005129329A - Состав цветного стекла для автомобильных обзорных панелей со сниженным сдвигом пропускаемого цвета и способа его получения - Google Patents
Состав цветного стекла для автомобильных обзорных панелей со сниженным сдвигом пропускаемого цвета и способа его получения Download PDFInfo
- Publication number
- RU2005129329A RU2005129329A RU2005129329/03A RU2005129329A RU2005129329A RU 2005129329 A RU2005129329 A RU 2005129329A RU 2005129329/03 A RU2005129329/03 A RU 2005129329/03A RU 2005129329 A RU2005129329 A RU 2005129329A RU 2005129329 A RU2005129329 A RU 2005129329A
- Authority
- RU
- Russia
- Prior art keywords
- glass
- less
- million
- composition according
- shift
- Prior art date
Links
- 239000000203 mixture Substances 0.000 title claims 39
- 238000000034 method Methods 0.000 title claims 9
- 239000011521 glass Substances 0.000 claims 47
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 33
- 239000011669 selenium Substances 0.000 claims 19
- 229910052742 iron Inorganic materials 0.000 claims 13
- 230000033116 oxidation-reduction process Effects 0.000 claims 13
- 239000000463 material Substances 0.000 claims 11
- 230000035699 permeability Effects 0.000 claims 10
- BUGBHKTXTAQXES-UHFFFAOYSA-N Selenium Chemical compound [Se] BUGBHKTXTAQXES-UHFFFAOYSA-N 0.000 claims 8
- 229910052711 selenium Inorganic materials 0.000 claims 8
- 229910004298 SiO 2 Inorganic materials 0.000 claims 7
- 239000000758 substrate Substances 0.000 claims 7
- 239000000975 dye Substances 0.000 claims 5
- 230000007935 neutral effect Effects 0.000 claims 5
- XLOMVQKBTHCTTD-UHFFFAOYSA-N Zinc monoxide Chemical compound [Zn]=O XLOMVQKBTHCTTD-UHFFFAOYSA-N 0.000 claims 4
- 238000002844 melting Methods 0.000 claims 3
- 230000008018 melting Effects 0.000 claims 3
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims 2
- 239000000981 basic dye Substances 0.000 claims 2
- 230000015572 biosynthetic process Effects 0.000 claims 2
- 230000005284 excitation Effects 0.000 claims 2
- AMWRITDGCCNYAT-UHFFFAOYSA-L hydroxy(oxo)manganese;manganese Chemical compound [Mn].O[Mn]=O.O[Mn]=O AMWRITDGCCNYAT-UHFFFAOYSA-L 0.000 claims 2
- MRELNEQAGSRDBK-UHFFFAOYSA-N lanthanum(3+);oxygen(2-) Chemical compound [O-2].[O-2].[O-2].[La+3].[La+3] MRELNEQAGSRDBK-UHFFFAOYSA-N 0.000 claims 2
- 229920001021 polysulfide Polymers 0.000 claims 2
- 239000005077 polysulfide Substances 0.000 claims 2
- 150000008117 polysulfides Polymers 0.000 claims 2
- 230000005855 radiation Effects 0.000 claims 2
- 238000002310 reflectometry Methods 0.000 claims 2
- 239000011787 zinc oxide Substances 0.000 claims 2
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 1
- 229910052684 Cerium Inorganic materials 0.000 claims 1
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 claims 1
- KKCBUQHMOMHUOY-UHFFFAOYSA-N Na2O Inorganic materials [O-2].[Na+].[Na+] KKCBUQHMOMHUOY-UHFFFAOYSA-N 0.000 claims 1
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 claims 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims 1
- WGLPBDUCMAPZCE-UHFFFAOYSA-N Trioxochromium Chemical compound O=[Cr](=O)=O WGLPBDUCMAPZCE-UHFFFAOYSA-N 0.000 claims 1
- 239000011358 absorbing material Substances 0.000 claims 1
- GWXLDORMOJMVQZ-UHFFFAOYSA-N cerium Chemical compound [Ce] GWXLDORMOJMVQZ-UHFFFAOYSA-N 0.000 claims 1
- 229910000420 cerium oxide Inorganic materials 0.000 claims 1
- 229910000423 chromium oxide Inorganic materials 0.000 claims 1
- 238000000576 coating method Methods 0.000 claims 1
- 238000000151 deposition Methods 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 239000011733 molybdenum Substances 0.000 claims 1
- 229910052750 molybdenum Inorganic materials 0.000 claims 1
- 229910000476 molybdenum oxide Inorganic materials 0.000 claims 1
- 229910052759 nickel Inorganic materials 0.000 claims 1
- BMMGVYCKOGBVEV-UHFFFAOYSA-N oxo(oxoceriooxy)cerium Chemical compound [Ce]=O.O=[Ce]=O BMMGVYCKOGBVEV-UHFFFAOYSA-N 0.000 claims 1
- PQQKPALAQIIWST-UHFFFAOYSA-N oxomolybdenum Chemical compound [Mo]=O PQQKPALAQIIWST-UHFFFAOYSA-N 0.000 claims 1
- XOLBLPGZBRYERU-UHFFFAOYSA-N tin dioxide Chemical compound O=[Sn]=O XOLBLPGZBRYERU-UHFFFAOYSA-N 0.000 claims 1
- 229910001887 tin oxide Inorganic materials 0.000 claims 1
- 239000010936 titanium Substances 0.000 claims 1
- 229910052719 titanium Inorganic materials 0.000 claims 1
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 claims 1
- 229910052720 vanadium Inorganic materials 0.000 claims 1
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C4/00—Compositions for glass with special properties
- C03C4/08—Compositions for glass with special properties for glass selectively absorbing radiation of specified wave lengths
- C03C4/085—Compositions for glass with special properties for glass selectively absorbing radiation of specified wave lengths for ultraviolet absorbing glass
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
- C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
- C03C3/087—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal containing calcium oxide, e.g. common sheet or container glass
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C4/00—Compositions for glass with special properties
- C03C4/02—Compositions for glass with special properties for coloured glass
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C4/00—Compositions for glass with special properties
- C03C4/08—Compositions for glass with special properties for glass selectively absorbing radiation of specified wave lengths
- C03C4/082—Compositions for glass with special properties for glass selectively absorbing radiation of specified wave lengths for infrared absorbing glass
Landscapes
- Chemical & Material Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Glass Compositions (AREA)
Claims (41)
1. Состав нейтрального серого стекла для автомобильных обзорных панелей с пониженными характеристиками сдвига пропускаемого цвета, базовая часть которого включает следующие компоненты, вес.%:
а основные красители содержат
и при котором стекло имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, коэффициент окисления-восстановления от 0,26 до 0,675, TSET менее или равное 65% и стандартный сдвиг пропускаемого цвета менее 6.
2. Состав стекла по п.1, в который по существу не входит никель.
3. Состав стекла по п.1, который включает один или более дополнительных компонентов, выбранных из группы, состоящей из оксида хрома, оксида марганца, оксида титана, оксида цинка, оксида молибдена или полисульфида железа.
4. Состав стекла по п.1, при котором коэффициент окисления-восстановления составляет менее 0,4.
5. Состав стекла по п.4, в котором суммарное железо составляет от более 0,5 до 7,0 вес.%.
6. Состав стекла по п.4, при котором коэффициент окисления-восстановления составляет от 0,265 до менее 0,4.
7. Состав стекла по п.4, в котором CoO составляет менее 12 млн-1.
8. Состав стекла по п.4, в котором Se составляет менее 8 млн-1.
9. Состав стекла по п.4, при котором стандартный сдвиг пропускаемого цвета составляет менее или равное 4.
10. Состав стекла по п.4, при котором TSET составляет менее или равное 60%.
11. Состав стекла по п.4, при котором чистота возбуждения составляет менее 8%.
12. Состав стекла по п.4, при котором чистота возбуждения составляет менее 3%.
13. Состав стекла по п.4, при котором стекло характеризуется доминантной длиной волны в диапазоне от 480 до 580 нм.
14. Состав стекла по п.4, в который дополнительно включены материалы, поглощающие ультрафиолетовое излучение.
15. Состав стекла по п.14, в котором дополнительные поглощающие ультрафиолетовое излучение материалы представляют собой окись материалов, выбранных из группы: церий, окись цинка, окись олова, ванадий, титан, молибден или их смеси.
16. Состав стекла по п.14, в котором содержание дополнительного поглощающего ультрафиолетовое излучение материала составляет не более 3 вес.% состава стекла.
17. Состав стекла по п.4, в котором суммарное железо составляет от более 0,5 до 0,72 вес.%, коэффициент окисления-восстановления составляет 0,265-0,35, СоО составляет менее 9 млн-1 и Se составляет от 1 до 6 млн-1.
18. Состав стекла по п.1, при котором коэффициент окисления-восстановления составляет не менее 0,4.
19. Состав стекла по п.18, при котором суммарное железо составляет 0,3-0,5 вес.%.
20. Состав стекла по п.18, при котором коэффициент окисления-восстановления составляет 0,4-0,675.
21. Состав стекла по п.18, в котором Se составляет 3-6 млн-1.
22. Состав стекла по п.18, при котором суммарное железо составляет 0,3-0,5 вес.%, коэффициент окисления-восстановления составляет 0,4-0,675, СоО равен 0 млн-1 и Se составляет 4-5 млн-1.
23. Состав стекла по п.18, в который включено до 10 млн-1 полисульфида железа.
24. Состав нейтрального серого стекла со сниженными характеристиками сдвига пропускаемого цвета как у автомобильных обзорных панелей, базовая часть у которого включает следующие компоненты, вес.%:
а основные красители содержат
при котором стекло по существу не содержит, по меньшей мере, либо оксид лантана, либо оксид церия и имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, при этом коэффициент окисления-восстановления составляет 0,2-0,675, TSET составляет менее или равное 65%, а стандартный сдвиг пропускаемого цвета составляет менее 6.
25. Состав нейтрального серого стекла со сниженными характеристиками сдвига пропускаемого цвета как у автомобильных обзорных панелей, базовая часть у которого включает следующие компоненты, вес.%:
а основные красители содержат
при котором стекло имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, коэффициент окисления-восстановления составляет 0,2-0,675, TSET составляет менее или равное 65%, а стандартный сдвиг пропускаемого цвета составляет менее 6.
26. Автомобиль, имеющий внутреннюю и, по меньшей мере, одну обзорную панель со сниженными характеристиками сдвига пропускаемого цвета, выполненную из стекла, состав которого включает базовую часть, содержащую следующие компоненты, вес.%:
и основные красители, содержащие
при котором стекло имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, при этом коэффициент окисления-восстановления составляет 0,2-0,675, TSET составляет менее или равное 65%, а стандартный сдвиг цвета составляет менее 6.
27. Способ снижения сдвига воспринимаемого цвета интерьера автомобиля, видимого через автомобильную обзорную панель, содержащий стадии изготовления обзорной панели из стекла, состав которого включает базовую часть, содержащую следующие компоненты, вес.%:
а основные красители содержат
при котором стекло имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, при этом коэффициент окисления-восстановления составляет 0,2-0,675, TSET составляет менее или равное 65%, а стандартный сдвиг пропускаемого цвета составляет менее 6.
28. Способ определения стандартного сдвига пропускаемого цвета относительно выбранного материала, содержащий следующие стадии:
(a) измерение отражательной способности выбранного материала при множестве длин волны с помощью опорного источника света и измерительного устройства;
(b) измерение проницаемости опорной подложки при разных длинах волн с помощью опорного источника света и измерительного устройства;
(c) расчет величины сдвига пропускаемого цвета выбранного материала, видимого через опорную подложку;
(d) измерение проницаемости испытуемой подложки при разных длинах волн с использованием опорного источника света и измерительного устройства;
(e) расчет величины сдвига пропускаемого цвета для выбранного материала, видимого через испытуемую подложку; и
(f) сравнение величин сдвига пропускаемого цвета на этапе (с) с величиной сдвига пропускаемого цвета на этапе (е) для определения стандартного сдвига пропускаемого цвета.
29. Способ по п.27, в котором сдвиг пропускаемого цвета рассчитывается по формуле
Тλ=STλ·TGλ·ROλ·TGλ·SOλ,
где Тλ - количество света от опорного источника, пропускаемого через подложку, отраженного от выбранного материала, прошедшего назад через подложку к измерительному устройству при длине волны λ, SIλ - относительная мощность опорного источника света при длине волны λ, TGλ - проницаемость подложки при длине волны λ, ROλ - отражательная способность выбранного материала при длине волны λ, и SOλ - величина по трехцветной системе стандартного наблюдателя при длине волны λ.
30. Пропускающие свет элементы, выполненные из стекла с составом, приведенном в п.1 формулы.
31. Пропускающие свет элементы по п.30, толщина которых составляет от 1 до 20 мм.
32 Пропускающие свет элементы по п.31, имеющие регулирующую солнечную энергию покрытия, получаемые осаждением, по меньшей мере, на часть прозрачной панели.
33. Пропускающие свет элементы по п.31, которыми являются автомобильные обзорные панели.
34. Способ получения содержащего селен стекла со стабилизированным остаточным селеном, заключающийся в плавлении селеносодержащего материала стекольной шихты для обеспечения коэффициента окисления-восстановления не менее 0,35.
35. Способ по п.34, в котором осуществляют плавление селеносодержащего материала стекольной шихты для обеспечения коэффициента окисления-восстановления от 0,35 до 0,60.
36. Способ получения содержащего селен стекла со стабилизированным остаточным селеном, заключающийся в образовании селеносодержащей стекольной шихты для обеспечения после расплавления коэффициента окисления-восстановления не ниже 0,35
37. Способ по п.36, дополнительно включающий расплавление стекольной шихты.
38. Способ по п.36, включающий образование селеносодержащей стекольной шихты с коэффициентом окисления-восстановления около 0,35-0,60.
39. Состав стекла по п.1, при котором коэффициент окисления-восстановления составляет не менее 0,35.
40. Состав нейтрального серого стекла для автомобильных обзорных панелей со сниженными характеристиками сдвига пропускаемого цвета, базовая часть у которого включает следующие компоненты, вес.%:
а основные красители по существу состоящие из
при котором стекло имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, при этом коэффициент окисления-восстановления составляет 0,2-0,675, TSET составляет менее или равное 65%, а стандартный сдвиг пропускаемого цвета составляет менее 4.
41. Состав нейтрального серого стекла для автомобильных обзорных панелей со сниженными характеристиками сдвига пропускаемого цвета, базовая часть у которого включает следующие компоненты, вес.%:
а основные красители содержат
при котором стекло имеет световую проницаемость, по меньшей мере, 65% при толщине 3,9 мм, при этом коэффициент окисления-восстановления составляет 0,2-0,675, TSET составляет менее или равное 65%, а стандартный сдвиг пропускаемого цвета составляет менее 6.