MX377677B - Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma. - Google Patents

Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma.

Info

Publication number
MX377677B
MX377677B MX2016010667A MX2016010667A MX377677B MX 377677 B MX377677 B MX 377677B MX 2016010667 A MX2016010667 A MX 2016010667A MX 2016010667 A MX2016010667 A MX 2016010667A MX 377677 B MX377677 B MX 377677B
Authority
MX
Mexico
Prior art keywords
steel plate
annealing
temperature
inclusive
condition
Prior art date
Application number
MX2016010667A
Other languages
English (en)
Other versions
MX2016010667A (es
Inventor
Yoshiyasu Kawasaki
Yusuke Fushiwaki
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2016010667A publication Critical patent/MX2016010667A/es
Publication of MX377677B publication Critical patent/MX377677B/es

Abstract

Se describe una lámina de acero galvanizada por inmersión en caliente de alta resistencia producida a partir de una lámina de acero que contiene Si y Mn como un material base y excelente en aspecto del recubrimiento, resistencia a la corrosión, resistencia al deslaminado del recubrimiento durante conformación severa, y conformabilidad durante conformación severa. También se describe un método para la producción de la lámina de acero galvanizada por inmersión en caliente de alta resistencia. En un proceso de calentamiento para recocido, se utilizan las siguientes (Condición 1) a (Condición 3). (Condición 1) En el proceso de calentamiento para recocido, la velocidad de aumento de temperatura cuando la temperatura en el interior de un horno de recocido está en un intervalo de temperatura de 450 °C a A °C inclusive (donde A es un valor arbitrario seleccionado en un intervalo de 500 = A) es de 7 °C/seg o más. (Condición 2) La temperatura máxima de lámina de acero alcanzada durante el recocido es de 600 °C o superior y 750 °C o inferior. (Condición 3) Cuando la temperatura de la lámina de acero está en un intervalo de temperatura de 600 °C a 750 °C inclusive durante el recocido, el tiempo de tránsito de la lámina de acero en el intervalo de temperatura de 600 °C a 750 °C inclusive es de 30 segundos o mayor y 10 minutos o menor, y el punto de rocío de una atmósfera es de -45 °C o inferior.
MX2016010667A 2014-02-18 2015-02-06 Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma. MX377677B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014028693A JP5884196B2 (ja) 2014-02-18 2014-02-18 高強度溶融亜鉛めっき鋼板の製造方法
PCT/JP2015/000536 WO2015125433A1 (ja) 2014-02-18 2015-02-06 高強度溶融亜鉛めっき鋼板およびその製造方法

Publications (2)

Publication Number Publication Date
MX2016010667A MX2016010667A (es) 2016-11-08
MX377677B true MX377677B (es) 2025-03-11

Family

ID=53877957

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016010667A MX377677B (es) 2014-02-18 2015-02-06 Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma.

Country Status (7)

Country Link
US (1) US10301701B2 (es)
EP (1) EP3109338B1 (es)
JP (1) JP5884196B2 (es)
KR (1) KR101864655B1 (es)
CN (1) CN106029934B (es)
MX (1) MX377677B (es)
WO (1) WO2015125433A1 (es)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108495941B (zh) * 2016-01-28 2019-10-22 杰富意钢铁株式会社 钢板的温度控制装置及温度控制方法
CN105908079B (zh) * 2016-06-20 2018-06-12 首钢集团有限公司 一种高强度钢的处理方法
JP6460053B2 (ja) 2016-06-27 2019-01-30 Ｊｆｅスチール株式会社 高強度合金化溶融亜鉛めっき鋼板およびその製造方法
WO2019092467A1 (en) 2017-11-08 2019-05-16 Arcelormittal A galvannealed steel sheet
JP2021014605A (ja) * 2019-07-10 2021-02-12 株式会社神戸製鋼所 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
CN115613030B (zh) * 2022-05-05 2024-10-18 首钢集团有限公司 一种具有优良表面质量的汽车用含磷镀锌钢的生产方法
DE102022118249A1 (de) 2022-07-21 2024-02-01 Thyssenkrupp Steel Europe Ag Verfahren zur Einstellung einer Ofenatmosphäre in einem Wärmebehandlungsofen
DE102023105147A1 (de) 2023-03-02 2024-09-05 Thyssenkrupp Steel Europe Ag Verfahren zur Wärmebehandlung eines Stahls
EP4545672A1 (de) 2023-10-25 2025-04-30 ThyssenKrupp Steel Europe AG Verfahren zum schmelztauchbeschichten eines stahlflachprodukts sowie schmelztauchbeschichtungsanlage

Family Cites Families (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5849619B2 (ja) 1979-04-28 1983-11-05 住友金属工業株式会社 化成処理性にすぐれた高張力冷延鋼板の製造方法
JPH05320952A (ja) 1992-05-25 1993-12-07 Nkk Corp 塗装後の耐食性に優れた高強度冷延鋼板
JP2951480B2 (ja) 1992-06-24 1999-09-20 川崎製鉄株式会社 化成処理性ならびに成形性に優れる高張力冷延鋼板及びその製造方法
JP3514837B2 (ja) 1994-09-12 2004-03-31 日新製鋼株式会社 熱延鋼板の溶融めっき方法
JP2001140021A (ja) 1999-11-18 2001-05-22 Kawasaki Steel Corp めっき密着性に優れた高強度溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
JP3857939B2 (ja) 2001-08-20 2006-12-13 株式会社神戸製鋼所 局部延性に優れた高強度高延性鋼および鋼板並びにその鋼板の製造方法
JP3840392B2 (ja) 2001-10-09 2006-11-01 株式会社神戸製鋼所 りん酸塩処理性に優れた鋼板
JP4718782B2 (ja) 2003-02-06 2011-07-06 新日本製鐵株式会社 合金化溶融亜鉛めっき鋼板、およびその製造方法
JP4464720B2 (ja) 2003-04-10 2010-05-19 新日本製鐵株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP4319559B2 (ja) 2003-04-10 2009-08-26 株式会社神戸製鋼所 化成処理性に優れる高強度冷延鋼板
JP4315844B2 (ja) 2004-03-05 2009-08-19 株式会社神戸製鋼所 塗膜密着性に優れた高強度冷延鋼板
JP4843982B2 (ja) * 2004-03-31 2011-12-21 Ｊｆｅスチール株式会社 高剛性高強度薄鋼板およびその製造方法
EP2700730A3 (en) 2004-07-27 2017-08-09 Nippon Steel & Sumitomo Metal Corporation Steel sheet having high Young's modulus, hot-dip galvanized steel sheet using the same, alloyed hot-dip galvanized steel sheet, steel pipe having high Young's modulus, and methods for manufacturing these
JP4576921B2 (ja) 2004-08-04 2010-11-10 Ｊｆｅスチール株式会社 冷延鋼板の製造方法
JP4634915B2 (ja) 2004-11-15 2011-02-16 新日本製鐵株式会社 高ヤング率鋼板、それを用いた溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、高ヤング率鋼管、高ヤング率溶融亜鉛めっき鋼管、及び高ヤング率合金化溶融亜鉛めっき鋼管、並びにそれらの製造方法
JP4741376B2 (ja) 2005-01-31 2011-08-03 新日本製鐵株式会社 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備
WO2006109489A1 (ja) 2005-03-31 2006-10-19 Kabushiki Kaisha Kobe Seiko Sho 塗膜密着性、加工性及び耐水素脆化特性に優れた高強度冷延鋼板並びに自動車用鋼部品
WO2007067014A1 (en) 2005-12-09 2007-06-14 Posco Tole d'acier laminee a froid de haute resistance possedant une excellente propriete de formabilite et de revetement, tole d'acier plaquee de metal a base de zinc fabriquee a partir de cette tole et procece de fabrication de celle-ci
JP4882447B2 (ja) 2006-03-28 2012-02-22 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法
JP4932363B2 (ja) 2006-07-20 2012-05-16 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板及びその製造方法
JP5092507B2 (ja) 2007-04-06 2012-12-05 住友金属工業株式会社 高張力合金化溶融亜鉛めっき鋼板とその製造方法
KR101027250B1 (ko) 2008-05-20 2011-04-06 주식회사 포스코 고연성 및 내지연파괴 특성이 우수한 고강도 냉연강판,용융아연 도금강판 및 그 제조방법
KR100985298B1 (ko) 2008-05-27 2010-10-04 주식회사 포스코 리징 저항성이 우수한 저비중 고강도 열연 강판, 냉연강판, 아연도금 강판 및 이들의 제조방법
JP2010126757A (ja) 2008-11-27 2010-06-10 Jfe Steel Corp 高強度溶融亜鉛めっき鋼板およびその製造方法
KR101079472B1 (ko) * 2008-12-23 2011-11-03 주식회사 포스코 도금표면품질이 우수한 고망간강의 용융아연도금강판의 제조방법
JP5370244B2 (ja) 2009-03-31 2013-12-18 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP5552864B2 (ja) * 2009-03-31 2014-07-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5206705B2 (ja) 2009-03-31 2013-06-12 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
BRPI1014674A2 (pt) 2009-03-31 2019-04-16 Jfe Steel Corp chapa de aço galvanizada de alta resistência e método de produção da mesma
JP5552863B2 (ja) 2009-03-31 2014-07-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5552862B2 (ja) 2009-03-31 2014-07-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5712542B2 (ja) 2010-09-29 2015-05-07 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5760361B2 (ja) 2010-09-29 2015-08-12 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
KR20130049820A (ko) 2010-09-30 2013-05-14 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
JP5856002B2 (ja) 2011-05-12 2016-02-09 Ｊｆｅスチール株式会社 衝突エネルギー吸収能に優れた自動車用衝突エネルギー吸収部材およびその製造方法
JP5834869B2 (ja) * 2011-12-14 2015-12-24 Ｊｆｅスチール株式会社 化成処理性に優れた高強度鋼板およびその製造方法
JP5811841B2 (ja) * 2011-12-28 2015-11-11 新日鐵住金株式会社 Ｓｉ含有高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5505430B2 (ja) 2012-01-17 2014-05-28 Ｊｆｅスチール株式会社 鋼帯の連続焼鈍炉及び連続焼鈍方法
JP5982905B2 (ja) 2012-03-19 2016-08-31 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP5888267B2 (ja) 2012-06-15 2016-03-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板
JP5888268B2 (ja) * 2012-06-15 2016-03-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法および高強度溶融亜鉛めっき鋼板
JP5962541B2 (ja) 2012-07-23 2016-08-03 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
EP2940176B1 (en) * 2013-03-04 2019-03-27 JFE Steel Corporation High-strength steel sheet, method for manufacturing same, high-strength molten-zinc-plated steel sheet, and method for manufacturing same

Also Published As

Publication number Publication date
WO2015125433A1 (ja) 2015-08-27
EP3109338A1 (en) 2016-12-28
EP3109338B1 (en) 2018-12-12
EP3109338A4 (en) 2017-03-01
US10301701B2 (en) 2019-05-28
US20170166990A1 (en) 2017-06-15
CN106029934A (zh) 2016-10-12
JP2015151606A (ja) 2015-08-24
MX2016010667A (es) 2016-11-08
JP5884196B2 (ja) 2016-03-15
KR20160122255A (ko) 2016-10-21
CN106029934B (zh) 2018-11-30
KR101864655B1 (ko) 2018-06-05

Similar Documents

Publication Publication Date Title
MX377677B (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma.
MX2017002974A (es) Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia.
MX2018006419A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia.
MX2017001106A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia.
MX2017002797A (es) Producto plano de acero con un recubrimiento de ai, procedimiento para su fabricacion, elemento constructivo de acero y procedimiento para su fabricacion.
MX2017010574A (es) Metodo de produccion de una pieza fosfatable a partir de una hoja recubierta con un recubrimiento a base de aluminio y un recubrimiento de zinc.
MX2016013771A (es) Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia.
MX374164B (es) Procedimiento de fabricacion de un componente de acero provisto de un revestimiento metalico de proteccion contra la corrosion.
MX376279B (es) Método para la fabricación de una lámina de acero galvanizada de alta resistencia.
UA115745C2 (uk) Спосіб виготовлення високоміцного сталевого листа з покриттям або без покриття і одержаний лист
RU2016151385A (ru) Способ производства высокопрочного стального листа с покрытием, обладающего высокой прочностью, пластичностью и формуемостью
MX376277B (es) Lámina de acero de alta resistencia y método para la producción de la misma y lámina de acero galvanizada de alta resistencia y método para la producción de la misma.
MX380408B (es) Metodo de produccion de lamina de acero galvano-recocida.
MX386346B (es) Método para la producción de láminas de acero recocidas después de galvanizadas de alta resistencia.
WO2016014424A3 (en) System and method for producing a hardened and tempered structural member
MX382046B (es) Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de lamina de acero recocida despues de galvanizada de alta resistencia.
MX2021013782A (es) Acero recubierto con zinc para aplicaciones de conformado en caliente y metodo de produccion.
MX376280B (es) Método para la fabricación de una lámina de acero recocida después de galvanizada de alta resistencia.
TR201820853T4 (tr) Alümine edilmiş bir ambalaj çeliğinin üretilmesi için yöntem.
MX380199B (es) Método para producir una hoja de acero de alta resistencia que tiene capacidad de formación mejorada y hoja obtenida por dicho método.
MX2016010665A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX380705B (es) Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma.
MX2016010669A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la lamina de acero de alta resistencia.
MX390428B (es) Método de producción de lámina de acero revestida de alta resistencia con resistencia y conformabilidad mejoradas.
MX388783B (es) Método para la producción de lámina de acero galvanizada de alta resistencia.

Legal Events

Date Code Title Description
FG Grant or registration