MX2019000576A - Lámina de acero y lámina de acero chapada. - Google Patents
Lámina de acero y lámina de acero chapada.Info
- Publication number
- MX2019000576A MX2019000576A MX2019000576A MX2019000576A MX2019000576A MX 2019000576 A MX2019000576 A MX 2019000576A MX 2019000576 A MX2019000576 A MX 2019000576A MX 2019000576 A MX2019000576 A MX 2019000576A MX 2019000576 A MX2019000576 A MX 2019000576A
- Authority
- MX
- Mexico
- Prior art keywords
- steel sheet
- crystal grains
- carbides
- terms
- larger
- Prior art date
Abstract
Una lámina de acero tiene una composición química específica y tiene una estructura representada por, por área, ferrita: 30 a 95 % y bainita: 5 a 70 %. Cuando una región que está rodeada por un límite de grano que tiene desorientación de 15 ° o más y tiene un diámetro de círculo equivalente de 0.3 µm o más se define como un grano de cristal, la proporción de granos de cristal que cada uno tienen una desorientación intragranular de 5 a 14 ° a todos los granos de cristal es de 20 a 100% por proporción de área. Una relación de aspecto promedio de elipse equivalente a los granos de cristal es 5 o menos. Una densidad de distribución promedio del total de carburos basados en Ti y carburos basados en Nb, cada uno con un tamaño de grano de 20 nm o más en los límites de grano de ferrita es de 10 carburos/µm o menos.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016155100 | 2016-08-05 | ||
PCT/JP2017/028477 WO2018026014A1 (ja) | 2016-08-05 | 2017-08-04 | 鋼板及びめっき鋼板 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2019000576A true MX2019000576A (es) | 2019-09-02 |
Family
ID=61073647
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2019000576A MX2019000576A (es) | 2016-08-05 | 2017-08-04 | Lámina de acero y lámina de acero chapada. |
Country Status (9)
Country | Link |
---|---|
US (1) | US11236412B2 (es) |
EP (1) | EP3495528A4 (es) |
JP (1) | JP6358407B2 (es) |
KR (1) | KR102186320B1 (es) |
CN (1) | CN109563580A (es) |
BR (1) | BR112019000766B8 (es) |
MX (1) | MX2019000576A (es) |
TW (1) | TWI629369B (es) |
WO (1) | WO2018026014A1 (es) |
Families Citing this family (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016132549A1 (ja) | 2015-02-20 | 2016-08-25 | 新日鐵住金株式会社 | 熱延鋼板 |
PL3260565T3 (pl) | 2015-02-20 | 2019-12-31 | Nippon Steel Corporation | Blacha stalowa cienka walcowana na gorąco |
WO2016135898A1 (ja) | 2015-02-25 | 2016-09-01 | 新日鐵住金株式会社 | 熱延鋼板 |
ES2769224T3 (es) * | 2015-02-25 | 2020-06-25 | Nippon Steel Corp | Chapa de acero laminada en caliente |
EP3495528A4 (en) | 2016-08-05 | 2020-01-01 | Nippon Steel Corporation | STEEL SHEET, AND PLATED STEEL SHEET |
CN113637923B (zh) * | 2016-08-05 | 2022-08-30 | 日本制铁株式会社 | 钢板及镀覆钢板 |
TWI629367B (zh) * | 2016-08-05 | 2018-07-11 | 日商新日鐵住金股份有限公司 | Steel plate and plated steel |
MX2019000577A (es) * | 2016-08-05 | 2019-07-04 | Nippon Steel Corp | Lamina de acero y lamina de acero enchapada. |
KR102131527B1 (ko) * | 2018-11-26 | 2020-07-08 | 주식회사 포스코 | 내구성이 우수한 고강도 강재 및 이의 제조방법 |
US20220042147A1 (en) * | 2019-03-11 | 2022-02-10 | Nippon Steel Corporation | Hot-rolled steel sheet |
CN113366127B (zh) * | 2019-03-11 | 2023-01-17 | 日本制铁株式会社 | 热轧钢板 |
US20220170128A1 (en) * | 2019-05-31 | 2022-06-02 | Nippon Steel Corporation | Steel sheet for hot stamping |
JP7381842B2 (ja) | 2019-08-20 | 2023-11-16 | 日本製鉄株式会社 | 厚鋼板 |
KR102307928B1 (ko) | 2019-12-02 | 2021-09-30 | 주식회사 포스코 | 내구성이 우수한 후물 복합조직강 및 그 제조방법 |
KR20220138402A (ko) * | 2020-03-19 | 2022-10-12 | 닛폰세이테츠 가부시키가이샤 | 강판 |
KR102326688B1 (ko) * | 2020-05-15 | 2021-11-15 | 히타치 긴조쿠 가부시키가이샤 | 핸들링성이 우수한 금속박판 |
Family Cites Families (122)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5770257A (en) | 1980-10-17 | 1982-04-30 | Kobe Steel Ltd | High strength steel plate |
US4501626A (en) | 1980-10-17 | 1985-02-26 | Kabushiki Kaisha Kobe Seiko Sho | High strength steel plate and method for manufacturing same |
JPS5842726A (ja) | 1981-09-04 | 1983-03-12 | Kobe Steel Ltd | 高強度熱延鋼板の製造方法 |
JPS61217529A (ja) | 1985-03-22 | 1986-09-27 | Nippon Steel Corp | 延性のすぐれた高強度鋼板の製造方法 |
JPH02149646A (ja) | 1988-11-30 | 1990-06-08 | Kobe Steel Ltd | 加工性、溶接性に優れた高強度熱延鋼板とその製造方法 |
JP2609732B2 (ja) | 1989-12-09 | 1997-05-14 | 新日本製鐵株式会社 | 加工性とスポット溶接性に優れた熱延高強度鋼板とその製造方法 |
JP2840479B2 (ja) | 1991-05-10 | 1998-12-24 | 株式会社神戸製鋼所 | 疲労強度と疲労亀裂伝播抵抗の優れた高強度熱延鋼板の製造方法 |
JP2601581B2 (ja) | 1991-09-03 | 1997-04-16 | 新日本製鐵株式会社 | 加工性に優れた高強度複合組織冷延鋼板の製造方法 |
JP2548654B2 (ja) | 1991-12-13 | 1996-10-30 | 新日本製鐵株式会社 | 複合組織鋼材のエッチング液およびエッチング方法 |
JP3037855B2 (ja) | 1993-09-13 | 2000-05-08 | 新日本製鐵株式会社 | 耐疲労亀裂進展特性の良好な鋼板およびその製造方法 |
JPH0949026A (ja) | 1995-08-07 | 1997-02-18 | Kobe Steel Ltd | 強度−伸びバランス及び伸びフランジ性にすぐれる高強度熱延鋼板の製造方法 |
JP3333414B2 (ja) | 1996-12-27 | 2002-10-15 | 株式会社神戸製鋼所 | 伸びフランジ性に優れる加熱硬化用高強度熱延鋼板及びその製造方法 |
DZ2530A1 (fr) | 1997-12-19 | 2003-02-01 | Exxon Production Research Co | Procédé de préparation d'une tôle d'acier cette tôle d'acier et procédé pour renforcer la resistanceà la propagation des fissures d'une tôle d'acier. |
US6254698B1 (en) | 1997-12-19 | 2001-07-03 | Exxonmobile Upstream Research Company | Ultra-high strength ausaged steels with excellent cryogenic temperature toughness and method of making thereof |
WO2001023625A1 (fr) | 1999-09-29 | 2001-04-05 | Nkk Corporation | Tole d'acier et son procede de fabrication |
FR2801061B1 (fr) | 1999-11-12 | 2001-12-14 | Lorraine Laminage | Procede de realisation d'une bande de tole laminere a chaud a tres haute resistance, utilisable pour la mise en forme et notamment pour l'emboutissage |
JP4258934B2 (ja) | 2000-01-17 | 2009-04-30 | Jfeスチール株式会社 | 加工性と疲労特性に優れた高強度熱延鋼板およびその製造方法 |
JP4306076B2 (ja) | 2000-02-02 | 2009-07-29 | Jfeスチール株式会社 | 伸びフランジ性に優れた高延性熱延鋼板およびその製造方法 |
JP4445095B2 (ja) | 2000-04-21 | 2010-04-07 | 新日本製鐵株式会社 | バーリング加工性に優れる複合組織鋼板およびその製造方法 |
EP1201780B1 (en) | 2000-04-21 | 2005-03-23 | Nippon Steel Corporation | Steel plate having excellent burring workability together with high fatigue strength, and method for producing the same |
JP3790135B2 (ja) | 2000-07-24 | 2006-06-28 | 株式会社神戸製鋼所 | 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法 |
EP1176217B1 (en) | 2000-07-24 | 2011-12-21 | KABUSHIKI KAISHA KOBE SEIKO SHO also known as Kobe Steel Ltd. | High-strength hot-rolled steel sheet superior in strech flange formability and method for production thereof |
ES2690275T3 (es) | 2000-10-31 | 2018-11-20 | Jfe Steel Corporation | Chapa de acero laminado en caliente de alta resistencia y método para la fabricación de la misma |
JP3882577B2 (ja) | 2000-10-31 | 2007-02-21 | Jfeスチール株式会社 | 伸びおよび伸びフランジ性に優れた高張力熱延鋼板ならびにその製造方法および加工方法 |
JP3888128B2 (ja) | 2000-10-31 | 2007-02-28 | Jfeスチール株式会社 | 材質均一性に優れた高成形性高張力熱延鋼板ならびにその製造方法および加工方法 |
JP4205853B2 (ja) | 2000-11-24 | 2009-01-07 | 新日本製鐵株式会社 | バーリング加工性と疲労特性に優れた熱延鋼板およびその製造方法 |
JP2002226943A (ja) | 2001-02-01 | 2002-08-14 | Kawasaki Steel Corp | 加工性に優れた高降伏比型高張力熱延鋼板およびその製造方法 |
JP2002317246A (ja) | 2001-04-19 | 2002-10-31 | Nippon Steel Corp | 切り欠き疲労強度とバーリング加工性に優れる自動車用薄鋼板およびその製造方法 |
JP4062118B2 (ja) * | 2002-03-22 | 2008-03-19 | Jfeスチール株式会社 | 伸び特性および伸びフランジ特性に優れた高張力熱延鋼板とその製造方法 |
JP4205893B2 (ja) | 2002-05-23 | 2009-01-07 | 新日本製鐵株式会社 | プレス成形性と打抜き加工性に優れた高強度熱延鋼板及びその製造方法 |
CA2511661C (en) | 2002-12-24 | 2010-01-26 | Nippon Steel Corporation | High burring, high strength steel sheet excellent in softening resistance of weld heat affected zone and method of production of same |
JP4288146B2 (ja) | 2002-12-24 | 2009-07-01 | 新日本製鐵株式会社 | 溶接熱影響部の耐軟化性に優れたバーリング性高強度鋼板の製造方法 |
JP4116901B2 (ja) | 2003-02-20 | 2008-07-09 | 新日本製鐵株式会社 | バーリング性高強度薄鋼板およびその製造方法 |
JP2004315857A (ja) | 2003-04-14 | 2004-11-11 | Nippon Steel Corp | 打ち抜き加工性に優れた高強度熱延鋼板及びその製造方法 |
JP4580157B2 (ja) | 2003-09-05 | 2010-11-10 | 新日本製鐵株式会社 | Bh性と伸びフランジ性を兼ね備えた熱延鋼板およびその製造方法 |
EP1553202A1 (en) | 2004-01-09 | 2005-07-13 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | Ultra-high strength steel sheet having excellent hydrogen embrittlement resistance, and method for manufacturing the same |
JP4412727B2 (ja) | 2004-01-09 | 2010-02-10 | 株式会社神戸製鋼所 | 耐水素脆化特性に優れた超高強度鋼板及びその製造方法 |
JP4333379B2 (ja) | 2004-01-29 | 2009-09-16 | Jfeスチール株式会社 | 加工性、表面性状および板平坦度に優れた高強度薄鋼板の製造方法 |
JP4470701B2 (ja) | 2004-01-29 | 2010-06-02 | Jfeスチール株式会社 | 加工性および表面性状に優れた高強度薄鋼板およびその製造方法 |
JP2005256115A (ja) | 2004-03-12 | 2005-09-22 | Nippon Steel Corp | 伸びフランジ性と疲労特性に優れた高強度熱延鋼板 |
JP4926406B2 (ja) | 2004-04-08 | 2012-05-09 | 新日本製鐵株式会社 | 疲労き裂伝播特性に優れた鋼板 |
JP4460343B2 (ja) | 2004-04-13 | 2010-05-12 | 新日本製鐵株式会社 | 打ち抜き加工性に優れた高強度熱延鋼板及びその製造方法 |
KR100942088B1 (ko) | 2005-03-28 | 2010-02-12 | 가부시키가이샤 고베 세이코쇼 | 확공 가공성이 우수한 고강도 열연 강판 및 그의 제조방법 |
JP3889766B2 (ja) | 2005-03-28 | 2007-03-07 | 株式会社神戸製鋼所 | 穴拡げ加工性に優れた高強度熱延鋼板およびその製造方法 |
JP5070732B2 (ja) | 2005-05-30 | 2012-11-14 | Jfeスチール株式会社 | 伸び特性、伸びフランジ特性および引張疲労特性に優れた高強度熱延鋼板およびその製造方法 |
DE102005051052A1 (de) | 2005-10-25 | 2007-04-26 | Sms Demag Ag | Verfahren zur Herstellung von Warmband mit Mehrphasengefüge |
JP4840567B2 (ja) | 2005-11-17 | 2011-12-21 | Jfeスチール株式会社 | 高強度薄鋼板の製造方法 |
JP4854333B2 (ja) | 2006-03-03 | 2012-01-18 | 株式会社中山製鋼所 | 高強度鋼板、未焼鈍高強度鋼板およびそれらの製造方法 |
JP4575893B2 (ja) | 2006-03-20 | 2010-11-04 | 新日本製鐵株式会社 | 強度延性バランスに優れた高強度鋼板 |
JP4528275B2 (ja) | 2006-03-20 | 2010-08-18 | 新日本製鐵株式会社 | 伸びフランジ性に優れた高強度熱延鋼板 |
CA2652821C (en) * | 2006-05-16 | 2015-11-24 | Jfe Steel Corporation | Hot-rollled high strength steel sheet having excellent ductility, stretch-flangeability, and tensile fatigue properties and method for producing the same |
JP4969915B2 (ja) | 2006-05-24 | 2012-07-04 | 新日本製鐵株式会社 | 耐歪時効性に優れた高強度ラインパイプ用鋼管及び高強度ラインパイプ用鋼板並びにそれらの製造方法 |
JP5228447B2 (ja) | 2006-11-07 | 2013-07-03 | 新日鐵住金株式会社 | 高ヤング率鋼板及びその製造方法 |
US8157933B2 (en) | 2007-03-27 | 2012-04-17 | Nippon Steel Corporation | High-strength hot rolled steel sheet being free from peeling and excellent in surface properties and burring properties, and method for manufacturing the same |
JP5339765B2 (ja) | 2007-04-17 | 2013-11-13 | 株式会社中山製鋼所 | 高強度熱延鋼板およびその製造方法 |
JP5087980B2 (ja) | 2007-04-20 | 2012-12-05 | 新日本製鐵株式会社 | 打ち抜き加工性に優れた高強度熱延鋼板及びその製造方法 |
JP5037415B2 (ja) | 2007-06-12 | 2012-09-26 | 新日本製鐵株式会社 | 穴広げ性に優れた高ヤング率鋼板及びその製造方法 |
JP4980163B2 (ja) | 2007-07-20 | 2012-07-18 | 新日本製鐵株式会社 | 成形性に優れる複合組織鋼板およびその製造方法 |
PL2221287T3 (pl) | 2007-11-14 | 2015-12-31 | Hitachi Metals Ltd | Ceramiczna struktura typu plastra miodu, oparta na tytanianie glinu, sposób jej wytwarzania i sproszkowany materiał wyjściowy do jej wytwarzania |
JP5359296B2 (ja) * | 2008-01-17 | 2013-12-04 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5194858B2 (ja) * | 2008-02-08 | 2013-05-08 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
EP2267175B1 (en) | 2008-03-26 | 2013-02-13 | Nippon Steel & Sumitomo Metal Corporation | Hot rolled steel sheet possessing excellent fatigue properties and stretch-flange ability and process for producing the hot rolled steel sheet |
CN101999007B (zh) | 2008-04-10 | 2012-12-12 | 新日本制铁株式会社 | 扩孔性和延展性的平衡极良好、疲劳耐久性也优异的高强度钢板和镀锌钢板以及这些钢板的制造方法 |
JP5200653B2 (ja) | 2008-05-09 | 2013-06-05 | 新日鐵住金株式会社 | 熱間圧延鋼板およびその製造方法 |
JP5042914B2 (ja) | 2008-05-12 | 2012-10-03 | 新日本製鐵株式会社 | 高強度鋼およびその製造方法 |
JP5438302B2 (ja) | 2008-10-30 | 2014-03-12 | 株式会社神戸製鋼所 | 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法 |
JP2010168651A (ja) | 2008-12-26 | 2010-08-05 | Nakayama Steel Works Ltd | 高強度熱延鋼板およびその製造方法 |
JP4853575B2 (ja) | 2009-02-06 | 2012-01-11 | Jfeスチール株式会社 | 耐座屈性能及び溶接熱影響部靭性に優れた低温用高強度鋼管およびその製造方法 |
JP4977184B2 (ja) | 2009-04-03 | 2012-07-18 | 株式会社神戸製鋼所 | 伸びと伸びフランジ性のバランスに優れた高強度冷延鋼板およびその製造方法 |
EP2415891A4 (en) | 2009-04-03 | 2014-11-19 | Kobe Steel Ltd | COLD-ROLLED STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF |
JP5240037B2 (ja) | 2009-04-20 | 2013-07-17 | 新日鐵住金株式会社 | 鋼板およびその製造方法 |
JP4917186B2 (ja) * | 2009-05-11 | 2012-04-18 | 新日本製鐵株式会社 | 打抜き加工性と疲労特性に優れた熱延鋼板、溶融亜鉛めっき鋼板、およびそれらの製造方法 |
JP4772927B2 (ja) * | 2009-05-27 | 2011-09-14 | 新日本製鐵株式会社 | 疲労特性と伸び及び衝突特性に優れた高強度鋼板、溶融めっき鋼板、合金化溶融めっき鋼板およびそれらの製造方法 |
JP5423191B2 (ja) * | 2009-07-10 | 2014-02-19 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5482204B2 (ja) | 2010-01-05 | 2014-05-07 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
EP2530180B1 (en) | 2010-01-29 | 2018-11-14 | Nippon Steel & Sumitomo Metal Corporation | Steel sheet and method for manufacturing the steel sheet |
JP4842413B2 (ja) | 2010-03-10 | 2011-12-21 | 新日本製鐵株式会社 | 高強度熱延鋼板及びその製造方法 |
JP5510025B2 (ja) | 2010-04-20 | 2014-06-04 | 新日鐵住金株式会社 | 伸びと局部延性に優れた高強度薄鋼板およびその製造方法 |
JP5765080B2 (ja) | 2010-06-25 | 2015-08-19 | Jfeスチール株式会社 | 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法 |
MX342629B (es) * | 2010-07-28 | 2016-10-07 | Nippon Steel & Sumitomo Metal Corp | Lamina de acero enrollada en caliente, lamina de acero enrollada en frio, lamina de acero galvanizada y metodos para fabricar los mismos. |
JP5719545B2 (ja) | 2010-08-13 | 2015-05-20 | 新日鐵住金株式会社 | 伸びとプレス成形安定性に優れた高強度薄鋼板 |
JP5126326B2 (ja) | 2010-09-17 | 2013-01-23 | Jfeスチール株式会社 | 耐疲労特性に優れた高強度熱延鋼板およびその製造方法 |
EP2439290B1 (de) | 2010-10-05 | 2013-11-27 | ThyssenKrupp Steel Europe AG | Mehrphasenstahl, aus einem solchen Mehrphasenstahl hergestelltes kaltgewalztes Flachprodukt und Verfahren zu dessen Herstellung |
RU2543590C2 (ru) * | 2010-10-18 | 2015-03-10 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Горячекатаный, холоднокатаный и плакированный стальной лист, имеющий улучшенную равномерную и локальную пластичность при высокой скорости деформации |
JP5776398B2 (ja) | 2011-02-24 | 2015-09-09 | Jfeスチール株式会社 | 低温靭性に優れた低降伏比高強度熱延鋼板およびその製造方法 |
JP5667471B2 (ja) | 2011-03-02 | 2015-02-12 | 株式会社神戸製鋼所 | 温間での深絞り性に優れた高強度鋼板およびその温間加工方法 |
MX338997B (es) | 2011-03-28 | 2016-05-09 | Nippon Steel & Sumitomo Metal Corp | Placa de acero laminada en frio y metodo de produccion de la misma. |
CN103443320B (zh) | 2011-03-31 | 2015-09-23 | 新日铁住金株式会社 | 各向同性加工性优良的含贝氏体型高强度热轧钢板及其制造方法 |
CA2832890C (en) | 2011-04-13 | 2016-03-29 | Nippon Steel & Sumitomo Metal Corporation | Hot-rolled steel sheet for gas nitrocarburizing and manufacturing method thereof |
CA2831551C (en) | 2011-04-13 | 2016-03-08 | Nippon Steel & Sumitomo Metal Corporation | Hot-rolled steel sheet and method of producing the same |
BR112013029839B1 (pt) | 2011-05-25 | 2019-06-25 | Nippon Steel & Sumitomo Metal Corporation | Chapa de aço laminada a quente e método para produção da mesma |
JP5640898B2 (ja) | 2011-06-02 | 2014-12-17 | 新日鐵住金株式会社 | 熱延鋼板 |
JP5780210B2 (ja) | 2011-06-14 | 2015-09-16 | 新日鐵住金株式会社 | 伸びと穴広げ性に優れた高強度熱延鋼板およびその製造方法 |
CN103732781B (zh) | 2011-07-29 | 2016-07-06 | 新日铁住金株式会社 | 合金化热浸镀锌层和具有该层的钢板以及其制造方法 |
RU2567960C1 (ru) | 2011-09-30 | 2015-11-10 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Высокопрочный гальванизированный горячим погружением стальной лист |
CN103874776B (zh) | 2011-09-30 | 2016-05-18 | 新日铁住金株式会社 | 机械切断特性优良的高强度热浸镀锌钢板、高强度合金化热浸镀锌钢板以及它们的制造方法 |
US9534271B2 (en) | 2011-12-27 | 2017-01-03 | Jfe Steel Corporation | Hot rolled steel sheet and method for manufacturing the same |
JP5447741B1 (ja) | 2012-02-17 | 2014-03-19 | 新日鐵住金株式会社 | 鋼板、めっき鋼板、及びそれらの製造方法 |
TWI463018B (zh) | 2012-04-06 | 2014-12-01 | Nippon Steel & Sumitomo Metal Corp | 具優異裂縫阻滯性之高強度厚鋼板 |
EP2843075B1 (en) | 2012-04-26 | 2018-03-21 | JFE Steel Corporation | High-strength hot-rolled steel sheet having excellent ductility, stretch flangeability and uniformity and method for manufacturing the same |
CN104395490B (zh) * | 2012-06-26 | 2017-03-08 | 新日铁住金株式会社 | 高强度热轧钢板及其制造方法 |
IN2014DN08577A (es) * | 2012-07-20 | 2015-05-22 | Nippon Steel & Sumitomo Metal Corp | |
ES2608036T3 (es) | 2012-08-03 | 2017-04-05 | Tata Steel Ijmuiden Bv | Un proceso para producir tiras de acero laminado en caliente y una tira de acero producida con este |
JP5825225B2 (ja) | 2012-08-20 | 2015-12-02 | 新日鐵住金株式会社 | 熱延鋼板の製造方法 |
RU2605014C2 (ru) | 2012-09-26 | 2016-12-20 | Ниппон Стил Энд Сумитомо Метал Корпорейшн | Лист двухфазной стали и способ его изготовления |
KR101654492B1 (ko) | 2012-09-27 | 2016-09-05 | 신닛테츠스미킨 카부시키카이샤 | 열연 강판 및 그 제조 방법 |
CN104870676B (zh) | 2012-12-18 | 2017-12-05 | 杰富意钢铁株式会社 | 低屈服比高强度冷轧钢板及其制造方法 |
JP5821861B2 (ja) | 2013-01-23 | 2015-11-24 | 新日鐵住金株式会社 | 外観に優れ、伸びと穴拡げ性のバランスに優れた高強度熱延鋼板及びその製造方法 |
BR112015024840B1 (pt) * | 2013-04-15 | 2020-03-31 | Nippon Steel Corporation | Chapa de aço laminada a quente |
JP6241274B2 (ja) | 2013-12-26 | 2017-12-06 | 新日鐵住金株式会社 | 熱延鋼板の製造方法 |
KR101863486B1 (ko) * | 2014-04-23 | 2018-05-31 | 신닛테츠스미킨 카부시키카이샤 | 테일러드 롤드 블랭크용 열연 강판, 테일러드 롤드 블랭크 및 그들의 제조 방법 |
JP6292022B2 (ja) | 2014-05-15 | 2018-03-14 | 新日鐵住金株式会社 | 高強度熱延鋼板及びその製造方法 |
JP6390273B2 (ja) | 2014-08-29 | 2018-09-19 | 新日鐵住金株式会社 | 熱延鋼板の製造方法 |
KR101981876B1 (ko) | 2015-02-20 | 2019-05-23 | 닛폰세이테츠 가부시키가이샤 | 열연 강판 |
PL3260565T3 (pl) | 2015-02-20 | 2019-12-31 | Nippon Steel Corporation | Blacha stalowa cienka walcowana na gorąco |
WO2016132549A1 (ja) | 2015-02-20 | 2016-08-25 | 新日鐵住金株式会社 | 熱延鋼板 |
WO2016135898A1 (ja) | 2015-02-25 | 2016-09-01 | 新日鐵住金株式会社 | 熱延鋼板 |
ES2769224T3 (es) * | 2015-02-25 | 2020-06-25 | Nippon Steel Corp | Chapa de acero laminada en caliente |
MX2019000577A (es) * | 2016-08-05 | 2019-07-04 | Nippon Steel Corp | Lamina de acero y lamina de acero enchapada. |
TWI629367B (zh) | 2016-08-05 | 2018-07-11 | 日商新日鐵住金股份有限公司 | Steel plate and plated steel |
EP3495528A4 (en) | 2016-08-05 | 2020-01-01 | Nippon Steel Corporation | STEEL SHEET, AND PLATED STEEL SHEET |
CN113637923B (zh) * | 2016-08-05 | 2022-08-30 | 日本制铁株式会社 | 钢板及镀覆钢板 |
-
2017
- 2017-08-04 EP EP17837115.9A patent/EP3495528A4/en not_active Withdrawn
- 2017-08-04 WO PCT/JP2017/028477 patent/WO2018026014A1/ja unknown
- 2017-08-04 KR KR1020197000254A patent/KR102186320B1/ko active IP Right Grant
- 2017-08-04 MX MX2019000576A patent/MX2019000576A/es unknown
- 2017-08-04 BR BR112019000766A patent/BR112019000766B8/pt active Search and Examination
- 2017-08-04 TW TW106126479A patent/TWI629369B/zh not_active IP Right Cessation
- 2017-08-04 CN CN201780046261.9A patent/CN109563580A/zh active Pending
- 2017-08-04 JP JP2017562090A patent/JP6358407B2/ja active Active
- 2017-08-04 US US16/315,120 patent/US11236412B2/en active Active
Also Published As
Publication number | Publication date |
---|---|
CN109563580A (zh) | 2019-04-02 |
EP3495528A1 (en) | 2019-06-12 |
US20190226061A1 (en) | 2019-07-25 |
JPWO2018026014A1 (ja) | 2018-08-02 |
WO2018026014A1 (ja) | 2018-02-08 |
KR102186320B1 (ko) | 2020-12-03 |
US11236412B2 (en) | 2022-02-01 |
JP6358407B2 (ja) | 2018-07-18 |
TWI629369B (zh) | 2018-07-11 |
KR20190014077A (ko) | 2019-02-11 |
EP3495528A4 (en) | 2020-01-01 |
BR112019000766B8 (pt) | 2023-03-14 |
BR112019000766B1 (pt) | 2023-01-10 |
BR112019000766A2 (pt) | 2019-04-24 |
TW201809313A (zh) | 2018-03-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2019000576A (es) | Lámina de acero y lámina de acero chapada. | |
MX2018016223A (es) | Lamina de acero y lamina de acero enchapada. | |
MX2019000577A (es) | Lamina de acero y lamina de acero enchapada. | |
MX2019000051A (es) | Lamina de acero y lamina de acero chapada. | |
MX2017010598A (es) | Hoja de acero laminada en caliente. | |
MX2017014938A (es) | Lamina de acero y metodo de produccion de la misma. | |
MX336096B (es) | Lamina de cero laminada en caliente y metodo para producir la misma. | |
MX2017010537A (es) | Chapa de acero laminada en caliente. | |
MX2020006507A (es) | Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma. | |
MX360510B (es) | Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia a la fractura retardada, y metodo para producir la misma. | |
MX2016012380A (es) | Miembro de lamina de acero formada en caliente de alta resistencia. | |
MX2017005569A (es) | Lamina de acero de alta resistencia y metodo para la fabricacion de la misma. | |
MX2018016000A (es) | Lamina de acero. | |
MX2019001045A (es) | Lamina de acero y metodo para la produccion de la misma. | |
MX2019012250A (es) | Lamina de acero y metodo de fabricacion asociado. | |
MX2017005571A (es) | Lamina de acero de alta resistencia y metodo para la fabricacion de la misma. | |
UA115491C2 (uk) | Магнітні або намагнічувані частинки пігменту та шари з оптичним ефектом | |
MX357963B (es) | Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, con excelentes caracteristicas mecanicas de corte, lamina de acero galvanizado por inmersion en caliente, aleada, de alta resistencia y metodo para producir dichas laminas. | |
UA118036C2 (uk) | Високоміцна сталь та спосіб виготовлення | |
MX352397B (es) | Lamina de acero de alta resistencia y lamina de acero galvanizada de alta resistencia excelentes en moldeabilidad y metodos de produccion de las mismas. | |
MX2017001689A (es) | Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia. | |
ATE516322T1 (de) | Dispersionen von wachsen und anorganischen nanopartikeln sowie deren verwendung | |
MX2019001600A (es) | Lamina de acero, y metodo de produccion para la misma. | |
MX2020010211A (es) | Lamina de acero de alta resistencia y metodo para fabricar la misma. | |
MX2018012680A (es) | Lamina de acero galvanizada por inmersion en caliente. |