MX2017005571A - Lamina de acero de alta resistencia y metodo para la fabricacion de la misma. - Google Patents

Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.

Info

Publication number
MX2017005571A
MX2017005571A MX2017005571A MX2017005571A MX2017005571A MX 2017005571 A MX2017005571 A MX 2017005571A MX 2017005571 A MX2017005571 A MX 2017005571A MX 2017005571 A MX2017005571 A MX 2017005571A MX 2017005571 A MX2017005571 A MX 2017005571A
Authority
MX
Mexico
Prior art keywords
less
residual austenite
polygonal ferrite
steel sheet
martensite
Prior art date
Application number
MX2017005571A
Other languages
English (en)
Inventor
Yokota Takeshi
Seto Kazuhiro
Matsuda Hiroshi
Kawasaki Yoshiyasu
Yamashita Takako
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2017005571A publication Critical patent/MX2017005571A/es

Abstract

Se describe una lámina de acero que tiene una composición química predeterminada y una microestructura de acero que contiene, en relación de área, 35% o más y 80% o menos de ferrita poligonal y 5% o más y 25% o menos de martensita, y que contiene, en fracción en volumen, 8% o más de austenita retenida, en la cual la ferrita poligonal, la martensita, y la austenita retenida tienen un tamaño de grano promedio de 6 µm o menos, 3 µm o menos, y 3 µm o menos, respectivamente, y cada una tienen una relación de aspecto de grano promedio de 2.0 o menos, y en la cual un valor obtenido al dividir un contenido de Mn en la austenita retenida en % en masa entre un contenido de Mn en la ferrita poligonal en % en masa es igual a 2.0 o más.
MX2017005571A 2014-10-30 2015-10-29 Lamina de acero de alta resistencia y metodo para la fabricacion de la misma. MX2017005571A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014221903 2014-10-30
PCT/JP2015/005459 WO2016067625A1 (ja) 2014-10-30 2015-10-29 高強度鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2017005571A true MX2017005571A (es) 2017-06-23

Family

ID=55856989

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017005571A MX2017005571A (es) 2014-10-30 2015-10-29 Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.

Country Status (7)

Country Link
US (1) US10954578B2 (es)
EP (1) EP3214197B1 (es)
JP (1) JP6179676B2 (es)
KR (1) KR101949627B1 (es)
CN (1) CN107075644B (es)
MX (1) MX2017005571A (es)
WO (1) WO2016067625A1 (es)

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6179676B2 (ja) 2014-10-30 2017-08-16 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP6172404B1 (ja) * 2015-09-04 2017-08-02 Ｊｆｅスチール株式会社 高強度薄鋼板およびその製造方法
US11560606B2 (en) * 2016-05-10 2023-01-24 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
US11993823B2 (en) 2016-05-10 2024-05-28 United States Steel Corporation High strength annealed steel products and annealing processes for making the same
US11142805B2 (en) 2016-09-30 2021-10-12 Jfe Steel Corporation High-strength coated steel sheet and method for manufacturing the same
EP3543364B1 (en) * 2016-11-16 2020-11-11 JFE Steel Corporation High-strength steel sheet and method for producing same
EP3543365B1 (en) 2016-11-16 2021-01-20 JFE Steel Corporation High-strength steel sheet and method for producing same
JP6699711B2 (ja) * 2017-11-28 2020-05-27 Ｊｆｅスチール株式会社 高強度鋼帯の製造方法
CN111788323B (zh) * 2018-02-19 2022-07-01 杰富意钢铁株式会社 高强度钢板及其制造方法
JP6954211B2 (ja) * 2018-03-30 2021-10-27 日本製鉄株式会社 金属成形板、塗装金属成形板および成形方法
MX2020010313A (es) 2018-03-30 2020-10-22 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para su produccion.
JP6705560B2 (ja) * 2018-03-30 2020-06-03 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP6705562B2 (ja) 2018-03-30 2020-06-03 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN113454244B (zh) * 2019-02-25 2023-03-03 杰富意钢铁株式会社 高强度钢板及其制造方法
MX2022004669A (es) * 2019-10-23 2022-05-25 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para fabricar la misma.
US20230059951A1 (en) * 2020-01-14 2023-02-23 Nippon Steel Corporation Steel sheet and manufacturing method thereof
RU2749411C1 (ru) * 2020-07-08 2021-06-09 Публичное акционерное общество "Северсталь" (ПАО "Северсталь") Способ производства холоднокатаного горячеоцинкованного проката из стали с двухфазной феррито-мартенситной структурой
KR102373222B1 (ko) * 2020-08-28 2022-03-11 현대제철 주식회사 우수한 홀확장성과 굽힘성을 가지는 고강도 냉연강재 및 그 제조방법
CN112375991A (zh) * 2020-11-11 2021-02-19 安徽金亿新材料股份有限公司 一种高热传导耐磨气门导管材料及其制备方法
CN114032457A (zh) * 2021-10-18 2022-02-11 首钢集团有限公司 一种连续热浸镀锌高强钢板及其制造方法

Family Cites Families (36)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61157625A (ja) 1984-12-29 1986-07-17 Nippon Steel Corp 高強度鋼板の製造方法
JP2588420B2 (ja) 1988-04-11 1997-03-05 日新製鋼株式会社 延性の良好な超高強度鋼材の製造方法
JP3857939B2 (ja) 2001-08-20 2006-12-13 株式会社神戸製鋼所 局部延性に優れた高強度高延性鋼および鋼板並びにその鋼板の製造方法
JP2003277884A (ja) 2002-01-21 2003-10-02 Kobe Steel Ltd 加工性及び焼付硬化性に優れた高強度鋼板
JP4374196B2 (ja) * 2002-02-19 2009-12-02 新日本製鐵株式会社 加工性、めっき性および靱性に優れた微細組織を有する高強度鋼板及びその製造方法
JP4677714B2 (ja) * 2003-05-15 2011-04-27 住友金属工業株式会社 海浜耐候性に優れた橋梁用鋼材およびそれを用いた構造物
EP1512760B1 (en) * 2003-08-29 2011-09-28 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High tensile strength steel sheet excellent in processibility and process for manufacturing the same
JP4408386B2 (ja) * 2004-04-19 2010-02-03 新日本製鐵株式会社 結晶粒の微細な複合組織高張力鋼
JP4681290B2 (ja) * 2004-12-03 2011-05-11 本田技研工業株式会社 高強度鋼板及びその製造方法
DE102005046459B4 (de) * 2005-09-21 2013-11-28 MHP Mannesmann Präzisrohr GmbH Verfahren zur Herstellung von kaltgefertigten Präzisionsstahlrohren
JP4692259B2 (ja) * 2005-12-07 2011-06-01 Ｊｆｅスチール株式会社 成形性および形状凍結性に優れる高強度鋼板
CN104775071A (zh) 2007-03-05 2015-07-15 新日铁住金株式会社 冷轧钢板和合金化熔融镀锌钢板以及它们的制造方法
JP5194878B2 (ja) * 2007-04-13 2013-05-08 Ｊｆｅスチール株式会社 加工性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP4949124B2 (ja) * 2007-05-22 2012-06-06 新日鐵住金ステンレス株式会社 形状凍結性に優れた高強度複相ステンレス鋼板及びその製造方法
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4894863B2 (ja) 2008-02-08 2012-03-14 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4998756B2 (ja) * 2009-02-25 2012-08-15 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4962594B2 (ja) * 2010-04-22 2012-06-27 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
CN103597106B (zh) * 2011-06-10 2016-03-02 株式会社神户制钢所 热压成形品、其制造方法和热压成形用薄钢板
JP5648597B2 (ja) 2011-07-06 2015-01-07 新日鐵住金株式会社 冷延鋼板の製造方法
MX363038B (es) 2011-07-06 2019-03-01 Nippon Steel & Sumitomo Metal Corp Metodo para producir hoja de acero laminada en frio.
JP5440672B2 (ja) 2011-09-16 2014-03-12 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板およびその製造方法
CA2850332C (en) * 2011-09-30 2016-06-21 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet and high-strength alloyed hot-dip galvanized steel sheet excellent in mechanical cutting property, and manufacturing method thereof
JP5454745B2 (ja) * 2011-10-04 2014-03-26 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
KR20140099544A (ko) * 2011-12-26 2014-08-12 제이에프이 스틸 가부시키가이샤 고강도 박강판 및 그의 제조 방법
JP5860308B2 (ja) 2012-02-29 2016-02-16 株式会社神戸製鋼所 温間成形性に優れた高強度鋼板およびその製造方法
JP5348268B2 (ja) * 2012-03-07 2013-11-20 Ｊｆｅスチール株式会社 成形性に優れる高強度冷延鋼板およびその製造方法
KR102060522B1 (ko) * 2012-03-30 2019-12-30 뵈스트알파인 스탈 게엠베하 고강도 냉연 강판 및 그의 제조 방법
JP5860354B2 (ja) * 2012-07-12 2016-02-16 株式会社神戸製鋼所 降伏強度と成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
WO2014020640A1 (ja) * 2012-07-31 2014-02-06 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
CA2923585A1 (en) * 2013-09-10 2015-03-19 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Hot-pressing steel plate, press-molded article, and method for manufacturing press-molded article
JP6068314B2 (ja) * 2013-10-22 2017-01-25 株式会社神戸製鋼所 冷間加工性と浸炭熱処理後の表面硬さに優れる熱延鋼板
WO2016067624A1 (ja) 2014-10-30 2016-05-06 Ｊｆｅスチール株式会社 高強度鋼板、高強度溶融亜鉛めっき鋼板、高強度溶融アルミニウムめっき鋼板および高強度電気亜鉛めっき鋼板、ならびに、それらの製造方法
JP6179676B2 (ja) 2014-10-30 2017-08-16 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
US20190276907A1 (en) 2016-04-19 2019-09-12 Jfe Steel Corporation Steel sheet, coated steel sheet, and methods for manufacturing same

Also Published As

Publication number Publication date
KR20170072322A (ko) 2017-06-26
CN107075644B (zh) 2019-03-29
JPWO2016067625A1 (ja) 2017-04-27
US10954578B2 (en) 2021-03-23
EP3214197B1 (en) 2019-01-09
JP6179676B2 (ja) 2017-08-16
EP3214197A1 (en) 2017-09-06
US20180127847A9 (en) 2018-05-10
WO2016067625A1 (ja) 2016-05-06
KR101949627B1 (ko) 2019-02-18
EP3214197A4 (en) 2017-11-22
CN107075644A (zh) 2017-08-18
US20170314091A1 (en) 2017-11-02

Similar Documents

Publication Publication Date Title
MX2017005571A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2017005569A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
WO2016067624A8 (ja) 高強度鋼板、高強度溶融亜鉛めっき鋼板、高強度溶融アルミニウムめっき鋼板および高強度電気亜鉛めっき鋼板、ならびに、それらの製造方法
MX2017005567A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas.
MX2020010210A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2017010598A (es) Hoja de acero laminada en caliente.
MX2017009931A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2017001689A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2017001720A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2017010754A (es) Hoja de acero laminada en frio, metodo para fabricar la misma.
MX2016008809A (es) Miembro formado en caliente y proceso para manufacturar el mismo.
MX2017010532A (es) Lamina o placa de acero laminada en caliente.
MX2017010537A (es) Chapa de acero laminada en caliente.
MX2017001688A (es) Lamina de acero de alta resistencia, metodo de produccion para la misma y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2017008622A (es) Hoja de acero laminada en caliente.
MX2017001529A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2020010211A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2017009935A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
EP3719157A4 (en) HIGH STRENGTH GALVANIZED STEEL SHEET AND METHOD FOR MANUFACTURING IT
MX2019005637A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2017009930A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2016016330A (es) Acero para forjado en frio.
MX2016008808A (es) Miembro formado en caliente y proceso para fabricar el mismo.
MX2017005945A (es) Barra de acero laminada o material de alambre laminada para componente forjado en frio.
MX2017003396A (es) Hoja de acero laminada en caliente.