MX2017009935A - Lamina de acero de alta resistencia y metodo de produccion para la misma. - Google Patents

Lamina de acero de alta resistencia y metodo de produccion para la misma.

Info

Publication number
MX2017009935A
MX2017009935A MX2017009935A MX2017009935A MX2017009935A MX 2017009935 A MX2017009935 A MX 2017009935A MX 2017009935 A MX2017009935 A MX 2017009935A MX 2017009935 A MX2017009935 A MX 2017009935A MX 2017009935 A MX2017009935 A MX 2017009935A
Authority
MX
Mexico
Prior art keywords
steel sheet
production method
strength steel
method therefor
ferrite
Prior art date
Application number
MX2017009935A
Other languages
English (en)
Inventor
Yokota Takeshi
Seto Kazuhiro
Kaneko Shinjiro
Minami Hidekazu
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2017009935A publication Critical patent/MX2017009935A/es

Abstract

Una lámina de acero tiene una microestructura que contiene ferrita en una relación de área de 20% o más, martensita en una relación de área de 5% o más, y martensita revenida en una relación de área de 5% o más. La ferrita tiene un tamaño de grano medio de 20.0 µm o menos. Una relación de intensidad inversa de fibra-? con respecto a fibra-a en la ferrita es de 1.00 o más y una relación de intensidad inversa de fibra-? con respecto a fibra-a en la martensita y la martensita revenida es de 1.00 o más.
MX2017009935A 2015-02-03 2016-01-27 Lamina de acero de alta resistencia y metodo de produccion para la misma. MX2017009935A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015019562A JP6032298B2 (ja) 2015-02-03 2015-02-03 高強度冷延鋼板、高強度めっき鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
PCT/JP2016/000407 WO2016125461A1 (ja) 2015-02-03 2016-01-27 高強度鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2017009935A true MX2017009935A (es) 2017-12-07

Family

ID=56563816

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017009935A MX2017009935A (es) 2015-02-03 2016-01-27 Lamina de acero de alta resistencia y metodo de produccion para la misma.

Country Status (7)

Country Link
US (1) US10472697B2 (es)
EP (1) EP3255162B1 (es)
JP (1) JP6032298B2 (es)
KR (1) KR101986595B1 (es)
CN (1) CN107208226B (es)
MX (1) MX2017009935A (es)
WO (1) WO2016125461A1 (es)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6032299B2 (ja) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板、高強度めっき鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
JP6032300B2 (ja) * 2015-02-03 2016-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板、高強度めっき鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
MX2019002337A (es) 2016-08-31 2019-05-16 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para su fabricacion.
JP6315044B2 (ja) 2016-08-31 2018-04-25 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
KR101889181B1 (ko) 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
KR102178677B1 (ko) * 2019-05-20 2020-11-13 주식회사 포스코 구멍확장성이 우수한 고강도 강판 및 이의 제조방법
MX2022012277A (es) 2020-04-07 2022-10-27 Nippon Steel Corp Hoja de acero.
CN114293111B (zh) * 2021-12-08 2022-10-11 北京科技大学 一种1.1GPa级片层相间的马氏体-铁素体双相钢及其制备方法
CN114672739B (zh) * 2022-04-20 2023-08-29 攀钢集团攀枝花钢铁研究院有限公司 一种逆相变钒微合金化轻质高强钢及其生产方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4407449B2 (ja) 2003-09-26 2010-02-03 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
AU2005227556B2 (en) * 2004-03-31 2008-02-14 Jfe Steel Corporation High-rigidity high-strength thin steel sheet and method for producing same
JP4867256B2 (ja) 2005-09-29 2012-02-01 Ｊｆｅスチール株式会社 剛性に優れた高強度薄鋼板およびその製造方法
JP5223360B2 (ja) 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5233142B2 (ja) 2007-03-28 2013-07-10 Ｊｆｅスチール株式会社 穴拡げ性に優れた高剛性高強度鋼板およびその製造方法
JP5157215B2 (ja) 2007-03-28 2013-03-06 Ｊｆｅスチール株式会社 加工性に優れた高剛性高強度鋼板およびその製造方法
WO2010114131A1 (ja) 2009-04-03 2010-10-07 株式会社神戸製鋼所 冷延鋼板およびその製造方法
JP4977185B2 (ja) 2009-04-03 2012-07-18 株式会社神戸製鋼所 伸びと伸びフランジ性のバランスに優れた高強度冷延鋼板およびその製造方法
JP5786319B2 (ja) 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 耐バリ性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5825481B2 (ja) * 2010-11-05 2015-12-02 Ｊｆｅスチール株式会社 深絞り性および焼付硬化性に優れる高強度冷延鋼板とその製造方法
JP5958038B2 (ja) * 2011-04-21 2016-07-27 Ｊｆｅスチール株式会社 外圧に対する缶胴部の座屈強度が高く、成形性および成形後の表面性状に優れた缶用鋼板およびその製造方法
US9512508B2 (en) * 2011-07-27 2016-12-06 Nippon Steel and Sumitomo Metal Corporation High-strength cold-rolled steel sheet having excellent stretch flangeability and precision punchability and manufacturing method thereof
US20150027594A1 (en) 2011-11-15 2015-01-29 Jfe Steel Corporation Thin steel sheet and process for producing the same
JP5884714B2 (ja) 2012-01-31 2016-03-15 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板およびその製造方法
EP2881483B1 (en) * 2012-07-31 2019-09-25 Nippon Steel Corporation Cold-rolled steel sheet, electrolytic zinc-coated cold-rolled steel sheet, hot-dip zinc-coated cold-rolled steel sheet, alloyed hot-dip zinc-coated cold-rolled steel sheet, and methods for producing said steel sheets
WO2015008454A1 (ja) * 2013-07-17 2015-01-22 Ｊｆｅスチール株式会社 缶用鋼板およびその製造方法
KR101753511B1 (ko) * 2013-08-02 2017-07-19 제이에프이 스틸 가부시키가이샤 고강도 고영률 강판 및 그 제조 방법
EP2998415B1 (en) * 2013-08-02 2017-09-06 JFE Steel Corporation High-strength, high-young's modulus steel plate, and manufacturing method thereof

Also Published As

Publication number Publication date
CN107208226B (zh) 2019-03-05
EP3255162A4 (en) 2017-12-27
KR101986595B1 (ko) 2019-09-30
JP6032298B2 (ja) 2016-11-24
KR20170106457A (ko) 2017-09-20
US20180023161A1 (en) 2018-01-25
EP3255162B1 (en) 2019-08-14
WO2016125461A1 (ja) 2016-08-11
US10472697B2 (en) 2019-11-12
CN107208226A (zh) 2017-09-26
JP2016141857A (ja) 2016-08-08
EP3255162A1 (en) 2017-12-13

Similar Documents

Publication Publication Date Title
MX2017009931A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2017009935A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2017009930A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2017005569A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2017005571A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
EP3636788A4 (en) HIGH STRENGTH STEEL SHEET AND ITS PRODUCTION PROCESS
MX2017005568A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para la fabricacion de las mismas.
MX2015014099A (es) Hoja de acero laminada en caliente y metodo de fabricacion de la misma.
MX2017015333A (es) Lamina de acero rolada en frio de alta resistencia, lamina de acero recubierta de alta resistencia, metodo para fabricar lamina de acero rolada en frio de alta resistencia, y metodo para fabricar lamina de acero recubierta de alta resistencia.
MX2017010754A (es) Hoja de acero laminada en frio, metodo para fabricar la misma.
EP3415653A4 (en) HIGHLESS GALVANIZED STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF
MX2017010910A (es) Lamina de acero laminada en frio de alta resistencia y metodo para fabricar la misma.
EP3633058A4 (en) HIGH STRENGTH STEEL SHEET AND METHOD FOR ITS MANUFACTURING
EP3561119A4 (en) HARDENED MARTENSITIC STEEL WITH A LOW STRETCHING RATIO AND EXCELLENT EQUIVALENT STRENGTH AND METHOD OF MANUFACTURING THEREOF
MX2017005567A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas.
MX2017010537A (es) Chapa de acero laminada en caliente.
MX2017008622A (es) Hoja de acero laminada en caliente.
MX2016008809A (es) Miembro formado en caliente y proceso para manufacturar el mismo.
MX2020010211A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
EP3395993A4 (en) High yield ratio type high-strength cold-rolled steel sheet and manufacturing method thereof
MX2019005637A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
EP3778975A4 (en) HIGH STRENGTH STEEL SHEET AND MANUFACTURING METHOD FOR IT
MX2017006374A (es) Acero multifase ultra resistente de endurecimiento al aire teniendo propiedades excelentes de procesamiento y metodo para produccion de cinta del acero referido.
MX2017002579A (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para fabricar la misma.
EP3409807A4 (en) HIGH-RESISTANCE GALVANIZED STEEL SHEET WITH HIGH ELASTICITY RATIO AND METHOD FOR PRODUCING SAME