Miembro de lamina de acero formada en caliente de alta resistencia.

Info

Publication number
MX2016012380A
MX2016012380A MX2016012380A MX2016012380A MX2016012380A MX 2016012380 A MX2016012380 A MX 2016012380A MX 2016012380 A MX2016012380 A MX 2016012380A MX 2016012380 A MX2016012380 A MX 2016012380A MX 2016012380 A MX2016012380 A MX 2016012380A
Authority
MX
Mexico
Prior art keywords
equal
less
strength hot
sheet member
steel sheet
Prior art date
Application number
MX2016012380A
Other languages
English (en)
Inventor
Hikida Kazuo
Kojima Nobusato
Tabata Shinichiro
Moriki Takahiro
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2016012380A publication Critical patent/MX2016012380A/es

Abstract

Un miembro de lámina de acero formada en caliente de alta resistencia que exhibe tanto una dureza consistente como resistencia a la fractura retardada, y se caracteriza porque: el miembro de lámina de acero formada en caliente de alta resistencia tiene una composición química prescrita; el grado de segregación de Mn a (=[Máxima concentración de Mn (% en masa) en el centro de lámina en la dirección del grosor] / concentración de Mn promedio (% en masa) a una profundidad de 1/4 del grosor total de la lámina desde la superficie]) es menor que o igual a 1.6; el valor de pureza de acero tal como se define en JIS G 0555 (2003) es menor que o igual a 0.08%; el tamaño de grano promedio de los granos ? anteriores es menor que o igual a 10 µm; y la densidad numérica de los carburos residuales es menor que o igual a 4x103 partículas/mm2.
MX2016012380A 2014-03-26 2015-03-26 Miembro de lamina de acero formada en caliente de alta resistencia. MX2016012380A (es)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2014063941 2014-03-26
JP2014063944 2014-03-26
PCT/JP2015/059491 WO2015147216A1 (ja) 2014-03-26 2015-03-26 高強度熱間成形鋼板部材

Publications (1)

Publication Number Publication Date
MX2016012380A true MX2016012380A (es) 2016-12-02

Family

ID=54195720

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016012380A MX2016012380A (es) 2014-03-26 2015-03-26 Miembro de lamina de acero formada en caliente de alta resistencia.

Country Status (10)

Country Link
US (1) US10060005B2 (es)
EP (1) EP3124637B9 (es)
JP (1) JP6237884B2 (es)
KR (1) KR101837883B1 (es)
CN (1) CN106103782B (es)
BR (1) BR112016021766A2 (es)
ES (1) ES2749437T3 (es)
MX (1) MX2016012380A (es)
PL (1) PL3124637T3 (es)
WO (1) WO2015147216A1 (es)

Families Citing this family (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20170075046A (ko) * 2015-12-22 2017-07-03 주식회사 포스코 내식성이 우수한 열간 프레스 성형품 및 그 제조방법
JP6493285B2 (ja) * 2016-04-19 2019-04-03 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
WO2017183059A1 (ja) * 2016-04-19 2017-10-26 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
JP6493284B2 (ja) * 2016-04-19 2019-04-03 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
JP6493286B2 (ja) * 2016-04-19 2019-04-03 Ｊｆｅスチール株式会社 耐摩耗鋼板および耐摩耗鋼板の製造方法
CA3017282C (en) * 2016-04-19 2021-01-05 Jfe Steel Corporation Abrasion-resistant steel plate and method of producing abrasion-resistant steel plate
EP3447156B1 (en) * 2016-04-19 2019-11-06 JFE Steel Corporation Abrasion-resistant steel sheet and method for producing abrasion-resistant steel sheet
US11035018B2 (en) 2016-04-19 2021-06-15 Jfe Steel Corporation Abrasion-resistant steel plate and method of producing abrasion-resistant steel plate
KR101795247B1 (ko) 2016-04-22 2017-11-08 현대자동차주식회사 핫스탬핑용 강재
CN106191678B (zh) * 2016-08-24 2018-06-26 武汉钢铁有限公司 用中薄板坯直接轧制的抗拉强度≥1700MPa热成形钢及生产方法
JP6347864B1 (ja) * 2017-03-24 2018-06-27 日新製鋼株式会社 オーステナイト系ステンレス鋼スラブの製造方法
CN107099748B (zh) * 2017-04-28 2019-03-26 武汉钢铁有限公司 高温成型用超高强锌铝镁镀层钢板及其制造方法
WO2019003449A1 (ja) * 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
WO2019003448A1 (ja) 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
WO2019003451A1 (ja) * 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
WO2019003447A1 (ja) * 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
MX2020009592A (es) * 2018-03-29 2020-10-05 Nippon Steel Corp Articulo estampado en caliente.
KR102450162B1 (ko) 2018-03-29 2022-10-04 닛폰세이테츠 가부시키가이샤 핫 스탬프용 강판
KR102460598B1 (ko) * 2018-03-29 2022-10-31 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형체
CN111655884B (zh) * 2018-03-29 2021-11-09 日本制铁株式会社 热冲压成型体
WO2020158285A1 (ja) * 2019-01-31 2020-08-06 Ｊｆｅスチール株式会社 熱間プレス部材、熱間プレス部材用冷延鋼板、およびそれらの製造方法
JP6966023B2 (ja) * 2019-03-20 2021-11-10 日本製鉄株式会社 ホットスタンプ成形体
KR102279900B1 (ko) * 2019-09-03 2021-07-22 주식회사 포스코 열간 성형용 강판, 열간 성형 부재 및 그 제조방법
KR20220084382A (ko) 2019-11-26 2022-06-21 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형품 및 핫 스탬프용 강판
US20220410239A1 (en) * 2019-11-26 2022-12-29 Magna International Inc. Hot stamp tooling assembly and method of forming a part with tailored temper properties
CN112877592B (zh) * 2019-11-29 2022-06-28 宝山钢铁股份有限公司 具有优异漆膜附着力的热成形部件及其制造方法
CN112276030B (zh) * 2020-10-13 2021-11-19 攀钢集团攀枝花钢铁研究院有限公司 一种高强抗延迟断裂热轧钢轨及其制备方法

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001011575A (ja) * 1999-06-30 2001-01-16 Nippon Steel Corp 冷間加工性に優れた機械構造用棒鋼・鋼線及びその製造方法
JP3389562B2 (ja) 2000-07-28 2003-03-24 アイシン高丘株式会社 車輌用衝突補強材の製造方法
WO2002044435A1 (fr) * 2000-12-01 2002-06-06 Aichi Steel Corporation Acier destiné à une carburation et appareillage carburé
JP4267367B2 (ja) * 2002-06-19 2009-05-27 新日本製鐵株式会社 原油油槽用鋼およびその製造方法、原油油槽およびその防食方法
JP4427465B2 (ja) 2005-02-02 2010-03-10 新日本製鐵株式会社 生産性に優れたホットプレス高強度鋼製部材の製造方法
JP4733522B2 (ja) * 2006-01-06 2011-07-27 新日本製鐵株式会社 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法
CN101484601B (zh) * 2006-05-10 2012-07-25 住友金属工业株式会社 热挤压成形钢板构件及其制造方法
JP4725415B2 (ja) * 2006-05-23 2011-07-13 住友金属工業株式会社 熱間プレス用鋼板および熱間プレス鋼板部材ならびにそれらの製造方法
JP5385554B2 (ja) 2008-06-19 2014-01-08 株式会社神戸製鋼所 熱処理用鋼
WO2011158818A1 (ja) 2010-06-14 2011-12-22 新日本製鐵株式会社 ホットスタンプ成形体、ホットスタンプ用鋼板の製造方法及びホットスタンプ成形体の製造方法
JP5652321B2 (ja) * 2011-05-13 2015-01-14 新日鐵住金株式会社 熱間複合成形性及び打抜き部の耐遅れ破壊特性に優れたホットスタンプ用鋼板とその製造方法
TWI481730B (zh) 2012-08-28 2015-04-21 Nippon Steel & Sumitomo Metal Corp 鋼板
CN106661685B (zh) * 2014-05-15 2018-04-20 新日铁住金株式会社 热成形钢板构件
BR112017020004A2 (pt) * 2015-04-08 2018-06-19 Nippon Steel & Sumitomo Metal Corporation folha de aço para tratamento térmico

Also Published As

Publication number Publication date
JP6237884B2 (ja) 2017-11-29
US10060005B2 (en) 2018-08-28
EP3124637B9 (en) 2019-12-04
EP3124637A4 (en) 2017-08-30
ES2749437T3 (es) 2020-03-20
PL3124637T3 (pl) 2020-03-31
US20170096724A1 (en) 2017-04-06
WO2015147216A1 (ja) 2015-10-01
KR101837883B1 (ko) 2018-03-12
CN106103782B (zh) 2018-06-01
EP3124637A1 (en) 2017-02-01
JPWO2015147216A1 (ja) 2017-04-13
KR20160123372A (ko) 2016-10-25
EP3124637B1 (en) 2019-07-31
CN106103782A (zh) 2016-11-09
BR112016021766A2 (pt) 2017-08-15

Similar Documents

Publication Publication Date Title
MX2016012380A (es) Miembro de lamina de acero formada en caliente de alta resistencia.
MX2017005569A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2017005571A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2014009471A (es) Plancha de acero laminada en frio de alta resistencia y proceso para fabricar la misma.
MX2017005568A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para la fabricacion de las mismas.
MY191191A (en) High-strength steel sheet and method for manufacturing the same
MX2017010598A (es) Hoja de acero laminada en caliente.
MX2016005086A (es) Lamina de acero laminada en caliente que tiene excelente dureza de superficie despues de tratamiento termico carburizante y excelente capacidad de estiramiento.
UA115791C2 (uk) Спосіб виготовлення деформаційно-зміцнених сталевих деталей з покриттям та листи з попередньо нанесеним покриттям для виготовлення цих деталей
MX2018016223A (es) Lamina de acero y lamina de acero enchapada.
MX2017005567A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas.
MX2017010537A (es) Chapa de acero laminada en caliente.
MX2022012560A (es) Lamina de acero de alta resistencia y proceso para producir la misma.
MX2016008809A (es) Miembro formado en caliente y proceso para manufacturar el mismo.
MX2020006865A (es) Composiciones y metodos de extraccion, respetuosos con el medio ambiente, de minerales y metales de la mena.
MX2018002854A (es) Lamina de acero y producto esmaltado.
MX2016012674A (es) Material de acero estampado en caliente.
MX2017003396A (es) Hoja de acero laminada en caliente.
MX2017009930A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2016015397A (es) Hoja de acero laminada en caliente y metodo de produccion de esta.
MX2018002142A (es) Lamina de acero.
PH12017500200B1 (en) Steel sheets for cans and methods for manufacturing the same
MX2016008330A (es) Placa de acero para conformacion en caliente y metodo de elaboracion de miembro de acero conformado por presion en caliente.
MX2019002804A (es) Composiciones de carbonato y metodos para utilizarlas.
MX2016002690A (es) Hoja de acero laminada en caliente que tiene excelente procesabilidad en frio y excelentes propiedades superficiales y dureza despues del procesamiento.

Legal Events

Date Code Title Description
HC Change of company name or juridical status

Owner name: NISSAN MOTOR CO., LTD.

FG Grant or registration