MX2015004736A - Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma. - Google Patents

Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma.

Info

Publication number
MX2015004736A
MX2015004736A MX2015004736A MX2015004736A MX2015004736A MX 2015004736 A MX2015004736 A MX 2015004736A MX 2015004736 A MX2015004736 A MX 2015004736A MX 2015004736 A MX2015004736 A MX 2015004736A MX 2015004736 A MX2015004736 A MX 2015004736A
Authority
MX
Mexico
Prior art keywords
steel sheet
dip galvanized
alloyed hot
galvanized steel
mass
Prior art date
Application number
MX2015004736A
Other languages
English (en)
Other versions
MX362505B (es
Inventor
Shintaro Yamanaka
Soshi Fujita
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2015004736A publication Critical patent/MX2015004736A/es
Publication of MX362505B publication Critical patent/MX362505B/es

Abstract

Una lámina de acero galvanizada por inmersión en caliente aleada en la que utiliza una lámina de acero matriz que contiene una cantidad prescrita de C, Si, Mn, etc., donde una capa chapada de zinc galvanizada por inmersión en caliente aleada que de 3 a 30 micras de espesor y que contiene de 5 a 15% en masa de Fe se aplica a la superficie de la chapa de acero matriz, la chapa de acero galvanizada por inmersión en caliente aleada que tiene una capa (A) que está dispuesta directamente debajo de la superficie de la chapa de acero matriz y se extiende hasta un espesor de 2 a 20 micras de la superficie de la chapa de acero matriz y en la chapa de acero matriz, la capa (A) que contiene al menos 50% en volumen de una estructura de ferrita, al menos 90% en masa de Fe en forma que no es óxido, no más de 10% en masa en total de óxidos de Fe, Si, Mn, P, S, y al, y menos de 0.05% en masa de C.
MX2015004736A 2012-11-06 2013-11-05 Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma. MX362505B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012244274 2012-11-06
PCT/JP2013/079858 WO2014073520A1 (ja) 2012-11-06 2013-11-05 合金化溶融亜鉛めっき鋼板とその製造方法

Publications (2)

Publication Number Publication Date
MX2015004736A true MX2015004736A (es) 2016-02-05
MX362505B MX362505B (es) 2019-01-22

Family

ID=50684623

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2015004736A MX362505B (es) 2012-11-06 2013-11-05 Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma.

Country Status (14)

Country Link
US (2) US10167541B2 (es)
EP (1) EP2918696B1 (es)
JP (1) JP5708884B2 (es)
KR (1) KR101699644B1 (es)
CN (1) CN104769146B (es)
BR (1) BR112015008396B1 (es)
CA (1) CA2888738C (es)
ES (1) ES2773302T3 (es)
MX (1) MX362505B (es)
PL (1) PL2918696T3 (es)
RU (1) RU2635499C2 (es)
TW (1) TWI494442B (es)
WO (1) WO2014073520A1 (es)
ZA (1) ZA201503075B (es)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101561008B1 (ko) * 2014-12-19 2015-10-16 주식회사 포스코 구멍확장능이 우수한 용융아연도금강판, 합금화 용융아연도금강판 및 그 제조방법
BR112017025389A2 (pt) 2015-06-11 2018-08-07 Nippon Steel & Sumitomo Metal Corporation chapa de aço galvanizada e método para fabricar a mesma
EP3342893A4 (en) * 2015-08-24 2019-01-16 Nippon Steel & Sumitomo Metal Corporation ALLOY-FILLED ZINC PLATED STEEL SHEET AND METHOD FOR MANUFACTURING SAME
JP6460053B2 (ja) 2016-06-27 2019-01-30 Ｊｆｅスチール株式会社 高強度合金化溶融亜鉛めっき鋼板およびその製造方法
KR101853767B1 (ko) * 2016-12-05 2018-05-02 주식회사 포스코 강의 제조 방법 및 이를 이용하여 제조된 강
KR101967959B1 (ko) 2016-12-19 2019-04-10 주식회사 포스코 굽힘 가공성이 우수한 초고강도 강판 및 이의 제조방법
US11447848B2 (en) 2018-03-30 2022-09-20 Nippon Steel Corporation Steel sheet and manufacturing method of therefor
TWI651417B (zh) * 2018-08-09 2019-02-21 中國鋼鐵股份有限公司 熱浸鍍鋅鋼材及其製造方法
EP3715490B1 (en) * 2019-03-29 2023-08-23 Bayerische Motoren Werke Aktiengesellschaft Method of casting steel alloy component and cast component
DE102019108457B4 (de) * 2019-04-01 2021-02-04 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Stahlbandes mit verbesserter Haftung metallischer Schmelztauchüberzüge
DE102019108459B4 (de) * 2019-04-01 2021-02-18 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Stahlbandes mit verbesserter Haftung metallischer Schmelztauchüberzüge
JP7468823B2 (ja) 2022-03-25 2024-04-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP7477065B1 (ja) 2023-03-31 2024-05-01 Ｊｆｅスチール株式会社 めっき鋼板の製造方法

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS55122865A (en) 1979-03-12 1980-09-20 Nippon Steel Corp Molten zinc plating method for difficult plating steel sheet
JPS59219473A (ja) 1983-05-26 1984-12-10 Nippon Steel Corp カラ−エツチング液及びエツチング方法
JP3606102B2 (ja) 1999-04-20 2005-01-05 Ｊｆｅスチール株式会社 熱延鋼板、溶融めっき熱延鋼板およびそれらの製造方法
TW504519B (en) * 1999-11-08 2002-10-01 Kawasaki Steel Co Hot dip galvanized steel plate excellent in balance of strength and ductility and in adhesiveness between steel and plating layer, and method for producing the same
JP2001200352A (ja) 2000-01-20 2001-07-24 Nkk Corp 耐パウダリング性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法
JP4283408B2 (ja) 2000-02-14 2009-06-24 新日本製鐵株式会社 成形性の優れた溶融亜鉛メッキ高強度薄鋼板とその製造方法
JP2001279412A (ja) 2000-03-29 2001-10-10 Nippon Steel Corp 耐食性の良好なＳｉ含有高強度合金化溶融亜鉛めっき鋼板とその製造方法
JP2001323355A (ja) 2000-05-11 2001-11-22 Nippon Steel Corp めっき密着性と塗装後耐食性の良好なＳｉ含有高強度溶融亜鉛めっき鋼板と塗装鋼板およびその製造方法
JP4331915B2 (ja) 2001-07-12 2009-09-16 新日本製鐵株式会社 疲労耐久性および耐食性に優れた高強度高延性溶融Ｚｎめっき鋼板及びその製造方法
BR0210265B1 (pt) 2001-06-06 2013-04-09 folha de aÇo galvanizado ou galvanelado com imersço a quente.
JP4275424B2 (ja) 2002-02-12 2009-06-10 Ｊｆｅスチール株式会社 高張力溶融亜鉛めっき鋼板及びその製造方法、並びに高張力合金化溶融亜鉛めっき鋼板及びその製造方法
CA2520814C (en) * 2003-03-31 2009-09-15 Nippon Steel Corporation Alloyed molten zinc plated steel sheet and process of production of same
DE602004027475D1 (de) 2003-04-10 2010-07-15 Arcelor France Ein herstellungsverfahren für feuerverzinktes stahlblech mit hoher festigkeit
JP4192051B2 (ja) * 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
JP4837459B2 (ja) 2006-06-30 2011-12-14 新日本製鐵株式会社 外観が良好な耐食性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP4589880B2 (ja) * 2006-02-08 2010-12-01 新日本製鐵株式会社 成形性と穴拡げ性に優れた高強度溶融亜鉛めっき鋼板と高強度合金化溶融亜鉛めっき鋼板及び高強度溶融亜鉛めっき鋼板の製造方法並びに高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5223360B2 (ja) 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5338087B2 (ja) 2008-03-03 2013-11-13 Ｊｆｅスチール株式会社 めっき性に優れる溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき設備
DE112009001685B4 (de) 2008-07-09 2015-09-03 Suzuki Motor Corp. Laserüberlappschweißverfahren
JP2010018874A (ja) * 2008-07-14 2010-01-28 Kobe Steel Ltd 合金化溶融亜鉛めっき鋼板と合金化溶融亜鉛めっき鋼板の製造方法
JP2010126757A (ja) 2008-11-27 2010-06-10 Jfe Steel Corp 高強度溶融亜鉛めっき鋼板およびその製造方法
KR101402503B1 (ko) 2009-08-31 2014-06-03 신닛테츠스미킨 카부시키카이샤 고강도 용융 아연 도금 강판 및 그 제조 방법
JP2011153349A (ja) * 2010-01-27 2011-08-11 Sumitomo Metal Ind Ltd 外観特性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法
JP5636727B2 (ja) * 2010-04-27 2014-12-10 新日鐵住金株式会社 溶融亜鉛めっき鋼板およびその製造方法
JP5434960B2 (ja) 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5545077B2 (ja) 2010-06-30 2014-07-09 新日鐵住金株式会社 合金化溶融亜鉛めっき鋼板の製造方法
JP2012012683A (ja) 2010-07-02 2012-01-19 Sumitomo Metal Ind Ltd 溶融亜鉛めっき鋼板の製造方法
PL2762601T3 (pl) * 2011-09-30 2018-11-30 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka mająca warstwę cynkowaną ogniowo i wykazująca doskonalą zwilżalność powłoki galwanicznej i przyczepność powłoki galwanicznej oraz sposób jej wytwarzania

Also Published As

Publication number Publication date
PL2918696T3 (pl) 2020-07-13
KR101699644B1 (ko) 2017-01-24
EP2918696A4 (en) 2016-07-20
CN104769146A (zh) 2015-07-08
BR112015008396A2 (pt) 2017-07-04
ZA201503075B (en) 2016-01-27
ES2773302T3 (es) 2020-07-10
MX362505B (es) 2019-01-22
JPWO2014073520A1 (ja) 2016-09-08
US10167541B2 (en) 2019-01-01
CA2888738C (en) 2018-02-06
JP5708884B2 (ja) 2015-04-30
US10711336B2 (en) 2020-07-14
EP2918696B1 (en) 2020-01-01
CA2888738A1 (en) 2014-05-15
WO2014073520A1 (ja) 2014-05-15
TWI494442B (zh) 2015-08-01
BR112015008396B1 (pt) 2019-12-03
US20190078190A1 (en) 2019-03-14
TW201432057A (zh) 2014-08-16
CN104769146B (zh) 2016-08-24
RU2015121407A (ru) 2016-12-27
RU2635499C2 (ru) 2017-11-13
KR20150060974A (ko) 2015-06-03
EP2918696A1 (en) 2015-09-16
US20150275345A1 (en) 2015-10-01

Similar Documents

Publication Publication Date Title
MX2015004736A (es) Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma.
MX2016002449A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX355496B (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
IN2014DN07662A (es)
MX369428B (es) Láminas de acero de alta resistencia, galvanizadas por inmersión en caliente y proceso para producir las mismas.
TR201904325T4 (tr) Sıcak baskıda kullanım için alaşımlı sıcak daldırma galvanize çelik levha ve çelik parça üretimi için yöntem.
MX2017005505A (es) Lamina de acero galvanizado por inmersion en caliente.
MX2014003713A (es) Placa de acero galvanizado, y metodo para fabricarla.
MX355495B (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX366222B (es) Laminas de acero de alta resistencia y laminas de acero galvanizadas de alta resistencia con capacidad de fijacion de forma excelente, y metodo para la fabricacion de las mismas.
MY166781A (en) High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof
MX2013011863A (es) Hoja de acero laminada en caliente de alta resistencia que tiene excelente capacidad de deformacion local y metodo para fabricar la misma.
MX2015001687A (es) Plancha de acero chapada con zinc para moldeo a presion en caliente.
EP2644729A3 (en) Steel plate with excellent hydrogen induced cracking resistance, and manufacturing method of the same
MX344422B (es) Lamina de acero para prensado en caliente y procedimiento para la fabricación de un miembro prensado en caliente utilizando la lamina de acero.
MX366702B (es) Hoja de acero revestida con aleación de zinc por inmersión en caliente excelente en adherencia de revestimiento, y método para producir la misma.
MY177836A (en) Low yield ratio high-strength hot-dip galvanized steel sheet, low yield ratio high-strength hot-dip galvannealed steel sheet, method for manufacturing low yield ratio highstrength hot-dip galvanized steel sheet, and method for manufacturing low yield ratio high-strength hot-dip galvannealed steel sheet
MX2015001071A (es) Plancha de acero laminada en frio, plancha de acero laminada en frio electrogalvanizada, plancha de acero laminada en frio galvanizada por inmersion en caliente, plancha de acero laminada en frio galvanizada por inmersion en caliente aleada, y metodos de fabricacion de las mismas.
MX2016010001A (es) Lamina de acero galvano-recocida y metodo para la produccion de la misma.
MX2015016367A (es) Placa de acero laminada en frio, placa de acero laminada en frio galvanizada, y metodo para manufacturar las placas.
IN2014MN00819A (es)
MX2017003396A (es) Hoja de acero laminada en caliente.
WO2012053871A3 (ko) 금속코팅강판, 용융아연도금강판 및 이들의 제조방법
MX2016008330A (es) Placa de acero para conformacion en caliente y metodo de elaboracion de miembro de acero conformado por presion en caliente.
MX2015015064A (es) Lamina de acero galvanizado y metodo para producir el mismo.

Legal Events

Date Code Title Description
FG Grant or registration